From Bulk to Nano: The Many Sides of Magnetism (Springer Series in Materials Science)

Springer Series in materials science 117 Springer Series in materials science Editors: R. Hull R. M. Osgood, Jr. ...

Author: Carmen-Gabriela Stefanita

27 downloads 498 Views 3MB Size Report

This content was uploaded by our users and we assume good faith they have the permission to share this book. If you own the copyright to this book and it is wrongfully on our website, we offer a simple DMCA procedure to remove your content from our site. Start by pressing the button below!

Report copyright / DMCA form

DOWNLOAD PDF

Springer Series in

materials science

117

Springer Series in

materials science Editors: R. Hull

R. M. Osgood, Jr.

J. Parisi

H. Warlimont

The Springer Series in Materials Science covers the complete spectrum of materials physics, including fundamental principles, physical properties, materials theory and design. Recognizing the increasing importance of materials science in future device technologies, the book titles in this series ref lect the state-of-the-art in understanding and controlling the structure and properties of all important classes of materials. 99 Self-Organized Morphology in Nanostructured Materials Editors: K. Al-Shamery and J. Parisi 100 Self Healing Materials An Alternative Approach to 20 Centuries of Materials Science Editor: S. van der Zwaag 101 New Organic Nanostructures for Next Generation Devices Editors: K. Al-Shamery, H.-G. Rubahn, and H. Sitter 102 Photonic Crystal Fibers Properties and Applications By F. Poli, A. Cucinotta, and S. Selleri 103 Polarons in Advanced Materials Editor: A.S. Alexandrov 104 Transparent Conductive Zinc Oxide Basics and Applications in Thin Film Solar Cells Editors: K. Ellmer, A. Klein, and B. Rech 105 Dilute III-V Nitride Semiconductors and Material Systems Physics and Technology Editor: A. Erol 106 Into The Nano Era Moore’s Law Beyond Planar Silicon CMOS Editor: H.R. Huff 107 Organic Semiconductors in Sensor Applications Editors: D.A. Bernards, R.M. Ownes, and G.G. Malliaras

109 Reactive Sputter Deposition Editors: D. Depla and S. Mahieu 110 The Physics of Organic Superconductors and Conductors Editor: A. Lebed 111 Molecular Catalysts for Energy Conversion Editors: T. Okada and M. Kaneko 112 Atomistic and Continuum Modeling of Nanocrystalline Materials Deformation Mechanisms and Scale Transition By M. Cherkaoui and L. Capolungo 113 Crystallography and the World of Symmetry By S.K. Chatterjee 114 Piezoelectricity Evolution and Future of a Technology Editors: W. Heywang, K. Lubitz, and W. Wersing 115 Defects, Photorefraction and Ferroelectric Switching in Lithium Niobate By T. Volk and M. W¨ohlecke 116 Einstein Relation in Compound Semiconductors and Their Nanostructures By K.P. Ghatak, S. Bhattacharya, and D. De 117 From Bulk to Nano The Many Sides of Magnetism By C.-G. Stefanita

108 Evolution of Thin-Film Morphology Modeling and Simulations By M. Pelliccione and T.-M. Lu

Volumes 50–98 are listed at the end of the book.

Carmen-Gabriela Stefanita

From Bulk to Nano The Many Sides of Magnetism

With 53 Figures

123

Dr. Carmen-Gabriela Stefanita NanoDotTek Burlington, MA 01803, USA E-mail: [email protected]

Series Editors:

Professor Robert Hull

Professor Jürgen Parisi

University of Virginia Dept. of Materials Science and Engineering Thornton Hall Charlottesville, VA 22903-2442, USA

Universit¨at Oldenburg, Fachbereich Physik Abt. Energie- und Halbleiterforschung Carl-von-Ossietzky-Strasse 9–11 26129 Oldenburg, Germany

Professor R. M. Osgood, Jr.

Professor Hans Warlimont

Microelectronics Science Laboratory Department of Electrical Engineering Columbia University Seeley W. Mudd Building New York, NY 10027, USA

Institut f¨ur Festk¨orperund Werkstofforschung, Helmholtzstrasse 20 01069 Dresden, Germany

Springer Series in Materials Science ISSN 0933-033X ISBN 978-3-540-70547-5

e-ISBN 978-3-540-70548-2

Library of Congress Control Number: 2008931053 © Springer-Verlag Berlin Heidelberg 2008 This work is subject to copyright. All rights are reserved, whether the whole or part of the material is concerned, specif ically the rights of translation, reprinting, reuse of illustrations, recitation, broadcasting, reproduction on microf ilm or in any other way, and storage in data banks. Duplication of this publication or parts thereof is permitted only under the provisions of the German Copyright Law of September 9, 1965, in its current version, and permission for use must always be obtained from Springer-Verlag. Violations are liable to prosecution under the German Copyright Law. The use of general descriptive names, registered names, trademarks, etc. in this publication does not imply, even in the absence of a specif ic statement, that such names are exempt from the relevant protective laws and regulations and therefore free for general use. Typesetting: Data prepared by SPi using a Springer TEX macro package Cover concept: eStudio Calamar Steinen Cover production: WMX Design GmbH, Heidelberg SPIN: 12255337 57/3180/SPi Printed on acid-free paper 987654321 springer.com

In memory of my grandparents, whose lifelong dedication made it all possible

Preface

The inspiration for this book can be traced back many years to two major works that inﬂuenced the author’s outlook on applied physics: Ferromagnetismus by R. Becker, W. D¨oring (Springer, Berlin 1939), and Ferromagnetism by R.M. Bozorth (IEEE Press, New York 1951). The former work is a collection of lectures held in the 1930s for ‘technicians’ attending a technical college. The German language in which the work was originally written was extremely convenient for the author of this present book, as it was for a long time the only comfortable technical language in an English speaking environment. Later on, upon encountering the work by Bozorth, it was a relief to see the clarity and eloquence of the subjects presented in English, despite the impressive thickness of the book. Bozorth’s work still constitutes a practical review for anyone in a multidisciplinary industry who comes across the various manifestations of magnetism. The popularity of both works is so enduring that they are regarded as highly academic, and yet extremely readable, a reference in their own right, still attracting many readers these days in industry and academia. The ﬁeld of magnetism progressed immensely in the twentieth century, and shows no signs of slowing down in the present one. It has become so vast that it is quite often viewed only in its parts, rather than as a whole. In today’s myriad of applications, especially on a nanoscale, and their changeable implications mostly on a macroscale, it often seems that diﬀerent aspects of reported work on magnetism are scattered and unrelated. Furthermore, the many atomic theories found in all major books on magnetism employ complex mathematical language that makes it less obvious how a theoretical description involving, e.g. spin can be associated with actual experimental observations. The diverse expressions of magnetic phenomena on more than one scale, and the apparent confusion created by the overwhelming literature that treats disparate accounts of magnetism individually without placing them in a broader context, have led to the writing of this book. Based on the author’s own struggle and experience in sifting through and organizing the vast amount

VIII

Preface

of information, this work addresses the relationship between individual topics in magnetism, trying to make the connection between magnetic phenomena on various scales more understandable. Nevertheless, the author makes no claims that the book comes even close to the work of the masters mentioned earlier. The intention of this author is only to show how the diﬀerent sides of magnetism come together. For this reason, the focus of the book is only on a few selected topics that the author believes are more representative of the broader subject. The book has an introductory chapter on some basic concepts in magnetism. A few of these are later ‘picked up’ in subsequent chapters, while others are not mentioned again. Nevertheless, just highlighting them once draws the reader’s attention to their existence and hints of their usefulness. The second chapter is an underpinning of magnetic nondestructive techniques, in particular magnetic Barkhausen noise, regarded by many as merely a laboratory nondestructive evaluation method. In any case, the valuable results and understanding gained through it have proved useful to more industrial nondestructive techniques such as Magnetic Flux Leakage and Remote Field Eddy Current. In the third chapter, the author takes a closer look at combined phenomena with wide industrial applications. The simple fact that optics and magnetism or piezoelectricity and magnetostriction can coexist has amazing consequences in many multidisciplinary areas. Furthermore, these subjects may recur in other established ﬁelds of magnetism, as implied in subsequent chapters. The fourth chapter goes deeper into the origins of ferromagnetism, showing that these constitute the foundation of emerging semiconductor electronics spin-oﬀs (Chap. 5), as well as the recording heads in our everyday computers. The controversial and yet extremely promising ﬁeld of spintronics is brieﬂy described in Chap. 5, while some trends in magnetic recording media are tackled in Chap. 6. Magnetism is used across many disciplines because of its rich implications in physics, chemistry, biochemistry, and the various areas of engineering. The author has undertaken to illustrate the various subﬁelds in magnetism in a manner that anyone with a basic familiarity with modern physics can follow, regardless of their specialty. By no means is this book intended to be a comprehensive inclusion of all aspects of magnetism, nor does it have any claims that it treats the various areas in an exhaustive manner. On the contrary, this work is primarily intended to link the diﬀerent areas of magnetism by showing how various phenomena ﬁt into a broader picture. Its goal is to bring together a broad ﬁeld in such a way that it provides a starting point for a graduate student or an experienced researcher for tackling a complex issue with maximum eﬃciency. Collecting many sides of magnetism into a single volume had to be unavoidably selective; it is just an attempt at trying to spark an interest in this extended subject while keeping it together. Sometimes, this work has attempted to clarify the nature of macroscopic magnetic phenomena and how, in some cases, they can be traced back to a nanoscale. These days, the

Preface

IX

popularity of nanotechnology may overshadow macro phenomena, although they are closely connected. Nanotechnology deals with the manipulation of materials on an atomic or molecular scale measured in billionths of a meter, while having manifestations on an every day scale. At other times, the spotlight of the book has been on explaining the physical nature of some basic magnetic phenomena, while illustrating the connection with real applications or contemporary research. It is a pleasure to acknowledge the support and encouragement I have received from colleagues and friends without whom I may have never written this book. My thanks go to Profs. L. Clapham and D.L. Atherton, as well as Drs. J.-K. Yi and T. Krause who may have long have forgotten how it all started. More recently, Prof. S. Bandyopadhyay, and my collaborators Drs. M. Namkung, F. Yun, and S. Pramanik have left their intellectual imprint on this work, therefore my gratitude extends to them. I apologize to all those who have not been named. Rest assured your inﬂuence has played a tremendous role in shaping this book, and the many subjects tackled are a tribute to your work. Lastly, it should be stated that the author does not endorse any of the commercial products discussed in this book. The products were only mentioned for historical reasons, or to illustrate a principle and explain some magnetics concepts. Burlington, MA, July 2008

Carmen-Gabriela Stefanita

Contents

Symbols . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . XVII 1

Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.1 Review of Certain Historic Magnetic Concepts . . . . . . . . . . . . . . 1.1.1 Magnetic Susceptibility . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.1.2 Classiﬁcation of Magnetic Materials . . . . . . . . . . . . . . . . . 1.1.3 The Concept of Magnetic Pole . . . . . . . . . . . . . . . . . . . . . . 1.1.4 Magnetic Dipoles . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.2 Origins of Magnetism on an Atomic Scale . . . . . . . . . . . . . . . . . . 1.2.1 The Importance of Angular Momentum . . . . . . . . . . . . . . 1.2.2 Magnetic Moment of a Sample of N Atoms . . . . . . . . . . . 1.2.3 Crystal Field vs. Spin–Orbit Coupling . . . . . . . . . . . . . . . 1.2.4 Magnetocrystalline Anisotropy . . . . . . . . . . . . . . . . . . . . . . 1.2.5 Magnetostriction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.3 Structure-Dependent Micromagnetism . . . . . . . . . . . . . . . . . . . . . 1.3.1 Division into Magnetic Domains . . . . . . . . . . . . . . . . . . . . . 1.3.2 Formation of Domain Walls . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.3 Types of Domain Walls . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.4 Signiﬁcance of Magnetic Domains and Domain Walls . . 1.4 Towards Technological Advancements . . . . . . . . . . . . . . . . . . . . . . 1.4.1 Design of New Magnetic Materials . . . . . . . . . . . . . . . . . . . 1.4.2 Magnetic Quantum Dots . . . . . . . . . . . . . . . . . . . . . . . . . . . References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

1 2 2 3 5 6 6 7 8 9 10 10 11 12 12 13 14 15 15 15 16

2

Barkhausen Noise as a Magnetic Nondestructive Testing Technique . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.1 Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.2 A Basic Deﬁnition of Magnetic Barkhausen Noise . . . . . . . . . . . . 2.2.1 Types of MBN Experiments . . . . . . . . . . . . . . . . . . . . . . . . 2.2.2 Where does MBN Originate? . . . . . . . . . . . . . . . . . . . . . . . 2.2.3 Formation of Magnetic Domains . . . . . . . . . . . . . . . . . . . . . 2.2.4 MBN and 180◦ Domain Walls . . . . . . . . . . . . . . . . . . . . . . .

19 19 20 20 21 22 23

XII

3

Contents

2.3 Stress Eﬀects . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.1 Elastic Stress Causes Changes in Bulk Magnetization . . 2.3.2 Magnetic Domains Respond to Stress . . . . . . . . . . . . . . . . 2.3.3 Magnetic Anisotropy and MBN . . . . . . . . . . . . . . . . . . . . . 2.3.4 Some Parameters Used in MBN Analysis . . . . . . . . . . . . . 2.3.5 Elastic Stress Inﬂuences on Magnetic Anisotropy . . . . . . 2.3.6 Plastic Deformation and Magnetic Anisotropy . . . . . . . . 2.3.7 Eﬀects of Residual Stresses . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.8 Inﬂuence of Dislocations . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.9 Selective Wall Energy Increases at Pinning Sites . . . . . . . 2.3.10 Roll Magnetic Anisotropy . . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.11 Limits in MBN Signal Increase with Plastic Stress . . . . . 2.4 Eﬀects of Microstructure on MBN . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.1 Variations in Grain Size . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.2 Compositional and Phase Inﬂuences . . . . . . . . . . . . . . . . . 2.4.3 MBN Behavior in Diﬀerent Materials . . . . . . . . . . . . . . . . 2.5 Competitiveness of MBN in Nondestructive Evaluation . . . . . . . 2.5.1 Usefulness of MBN for MFL . . . . . . . . . . . . . . . . . . . . . . . . 2.5.2 Need for Calibration of MBN as NDT . . . . . . . . . . . . . . . . References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

24 24 24 25 25 27 27 28 30 30 31 32 33 33 34 34 36 36 37 38

Combined Phenomena in Novel Materials . . . . . . . . . . . . . . . . . 3.1 The Interest in Magneto-optical Media . . . . . . . . . . . . . . . . . . . . . 3.1.1 Conventional vs. Continuous Media . . . . . . . . . . . . . . . . . . 3.1.2 The Basis of Magneto-optical Eﬀects . . . . . . . . . . . . . . . . . 3.1.3 Composite Films Used in Magneto-optical Recording . . 3.1.4 Magnetic Recording and Optical Readout . . . . . . . . . . . . 3.1.5 Quality of Magnetic Recording . . . . . . . . . . . . . . . . . . . . . . 3.1.6 Overcoming Noise Problems . . . . . . . . . . . . . . . . . . . . . . . . 3.1.7 The MO Sony Disk . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.1.8 Magnetically Induced Super Resolution . . . . . . . . . . . . . . 3.1.9 Nondestructive Optical Readout . . . . . . . . . . . . . . . . . . . . . 3.1.10 Double and Multilayer MO Disks . . . . . . . . . . . . . . . . . . . . 3.1.11 Domain Wall Displacement Detection . . . . . . . . . . . . . . . . 3.1.12 Magnetic Bubble Domains . . . . . . . . . . . . . . . . . . . . . . . . . . 3.1.13 Generation of a Bubble Bit of Memory . . . . . . . . . . . . . . . 3.1.14 Driving Force for Wall Displacement . . . . . . . . . . . . . . . . . 3.2 Magnetoelectric Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.1 The Magnetoelectric Eﬀect . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.2 Oxides, Boracites, Phosphates, etc. . . . . . . . . . . . . . . . . . . 3.2.3 Layered Composite Materials . . . . . . . . . . . . . . . . . . . . . . . 3.2.4 Product, Sum and Combination Properties . . . . . . . . . . . 3.2.5 PZT and Magnetostrictive Materials . . . . . . . . . . . . . . . . . 3.2.6 Avoiding Ferrites . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.7 Undesired Eﬀects of Sintering . . . . . . . . . . . . . . . . . . . . . . .

41 41 42 43 43 44 44 45 46 47 47 48 49 50 50 50 51 51 52 52 53 53 54 54

Contents

3.2.8 3.2.9 3.2.10 3.2.11 3.2.12 3.2.13 3.2.14 3.2.15 3.2.16 3.2.17 3.2.18 3.2.19 3.2.20 References 4

XIII

Variations in Signal Due to Mechanical Coupling . . . . . . Laminated Composites . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Voltage Coeﬃcient α . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Obtaining Improved Voltage Coeﬃcients . . . . . . . . . . . . . ME and Nanostructures . . . . . . . . . . . . . . . . . . . . . . . . . . . . Eﬀects on a Nanoscale . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Residual Stresses and Strains in Nanostructures . . . . . . . Multiferroics . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Using Terfenol-D . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Multiferroic Transformers . . . . . . . . . . . . . . . . . . . . . . . . . . Multiferroic Sensors for Vortex Magnetic Fields . . . . . . . Enhancing Multiferroicity through Material Design . . . . Identifying Multiferroics . . . . . . . . . . . . . . . . . . . . . . . . . . . . ..................................................

55 55 56 57 57 58 60 61 61 61 63 63 64 64

Magnetoresistance and Spin Valves . . . . . . . . . . . . . . . . . . . . . . . . 4.1 Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.2 A Simple Way of Quantifying Magnetoresistance . . . . . . . . . . . . 4.3 What is Responsible for GMR? . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.4 Deskstar 16 GP . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.5 “Spin-down” vs. “Spin-up” Scattering: Magnetic Impurities . . . 4.6 Fabrication of GMR Multilayers: Thin Films and Nanostructures . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.7 Spin Valves . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.8 The Role of Exchange Bias . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.9 Ni–Fe Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.10 Ternary Alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.11 Ni–Fe Alloys with Higher Fe Content . . . . . . . . . . . . . . . . . . . . . . 4.12 Basic Principles of Storing Information Magnetically . . . . . . . . . 4.13 Materials for spin valve Sensors . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.14 The Need for Proper Sensor Design . . . . . . . . . . . . . . . . . . . . . . . . 4.15 Magnetic Tunnel Junctions . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.16 Anisotropic Magnetoresistive Sensors . . . . . . . . . . . . . . . . . . . . . . 4.17 Extraordinary Magnetoresistance . . . . . . . . . . . . . . . . . . . . . . . . . . 4.18 GMR Sensors with CPP Geometry . . . . . . . . . . . . . . . . . . . . . . . . 4.19 Dual Spin Valves . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.20 Some GMR Multilayer Material Combinations . . . . . . . . . . . . . . 4.21 Ferromagnetic/Nonmagnetic Interfaces . . . . . . . . . . . . . . . . . . . . . 4.22 The Nonmagnetic Spacer . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.23 Magnetic Tunneling . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.24 The Magnetic Tunnel Transistor . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.25 Some Special Types of Ferromagnets . . . . . . . . . . . . . . . . . . . . . . . 4.26 Colossal Magnetoresistance . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.27 CPP Geometry Preferred in Sensors . . . . . . . . . . . . . . . . . . . . . . . 4.28 Spin Valves in Commercial Applications . . . . . . . . . . . . . . . . . . . . References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

71 71 72 72 73 73 74 75 75 76 77 77 78 80 81 82 82 83 83 84 85 86 86 87 87 88 89 90 91 93

XIV

5

Contents

Some Basic Spintronics Concepts . . . . . . . . . . . . . . . . . . . . . . . . . . 99 5.1 Encoding Information: Emergence of Spintronics . . . . . . . . . . . . 99 5.2 Spin Injection . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 100 5.2.1 Minority vs. Majority Spin Carriers . . . . . . . . . . . . . . . . . . 100 5.2.2 Spin Injection Rate . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 100 5.2.3 Spin Polarization and Spin Transfer . . . . . . . . . . . . . . . . . 101 5.2.4 CPP vs. CIP Geometry . . . . . . . . . . . . . . . . . . . . . . . . . . . . 102 5.2.5 Spin Accumulation, Spin Relaxation, and Spin Diﬀusion Length . . . . . . . . . . . . . . . . . . . . . . . . . . 103 5.2.6 No Spin Accumulation in CIP Geometry . . . . . . . . . . . . . 103 5.2.7 Half-Metallic Ferromagnets . . . . . . . . . . . . . . . . . . . . . . . . . 104 5.2.8 Some Epitaxial Growth Techniques . . . . . . . . . . . . . . . . . . 104 5.2.9 ME Materials and Spintronics . . . . . . . . . . . . . . . . . . . . . . . 105 5.2.10 Spontaneous Band Splitting . . . . . . . . . . . . . . . . . . . . . . . . 106 5.2.11 Spin Valves . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 106 5.2.12 Poor Injection Eﬃciency . . . . . . . . . . . . . . . . . . . . . . . . . . . 107 5.2.13 Additional Layer Between Ferromagnet and Spacer . . . . 107 5.2.14 III–V Magnetic Semiconductors . . . . . . . . . . . . . . . . . . . . . 107 5.2.15 Obtaining Spin-Polarized Magnetic Semiconductors . . . . 108 5.2.16 Light vs. Electric-Field-Induced Carrier Enhancement . . 108 5.2.17 Giant Planar Hall Eﬀect . . . . . . . . . . . . . . . . . . . . . . . . . . . 109 5.2.18 Maintaining Spin Polarization . . . . . . . . . . . . . . . . . . . . . . . 109 5.2.19 The Future of Spin Injection . . . . . . . . . . . . . . . . . . . . . . . . 111 5.3 Control of Spin Transport . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 111 5.3.1 The Need for Long Spin Relaxation Times . . . . . . . . . . . . 111 5.3.2 Organic Semiconductor Spacers . . . . . . . . . . . . . . . . . . . . . 112 5.3.3 Spin Transport in Organic Semiconductor Spin Valves . 113 5.3.4 Nanoscale Eﬀects at Ferromagnet/Organic Semiconductor Interface . . . . . . . . . . . . . . . . . . . . . . . . . . . . 113 5.3.5 Carbon Nanotubes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 114 5.3.6 GMR vs. TMR . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 114 5.3.7 The Parallel Resistor Model . . . . . . . . . . . . . . . . . . . . . . . . 116 5.3.8 Eﬀects at Adjacent Interfaces in GMR . . . . . . . . . . . . . . . 116 5.3.9 Scattering at Bloch Walls . . . . . . . . . . . . . . . . . . . . . . . . . . 117 5.3.10 Importance of Materials Choice . . . . . . . . . . . . . . . . . . . . . 118 5.3.11 Spin Control Through Electric Fields . . . . . . . . . . . . . . . . 118 5.4 Spin Selective Detection . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 119 5.4.1 Detecting Single Spins . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 119 5.4.2 Detecting Spin Polarization of an Ensemble of Spins . . . 119 5.4.3 The Datta and Das Spin Field Eﬀect Transistor . . . . . . . 121 5.4.4 The Future of Spintronics Devices . . . . . . . . . . . . . . . . . . . 121 References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 121

Contents

XV

6

Trends in Magnetic Recording Media . . . . . . . . . . . . . . . . . . . . . . 129 6.1 The Popularity of Magnetic Tapes . . . . . . . . . . . . . . . . . . . . . . . . . 129 6.1.1 Quality of Magnetic Tapes . . . . . . . . . . . . . . . . . . . . . . . . . . 130 6.1.2 The Pressure for Higher Capacity Magnetic Tapes . . . . . 131 6.1.3 Constraints Imposed by Thermal Stability . . . . . . . . . . . . 131 6.1.4 Forming a Bit . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 132 6.1.5 Inﬂuence of Magnetic Anisotropy . . . . . . . . . . . . . . . . . . . . 133 6.1.6 Choice of Materials . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 133 6.2 Bit Patterned Magnetic Media . . . . . . . . . . . . . . . . . . . . . . . . . . . . 134 6.2.1 Bit-Cells . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 134 6.2.2 Minimizing Errors . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 135 6.2.3 Some Disadvantages of Patterned Bits . . . . . . . . . . . . . . . 136 6.2.4 Solutions for Patterning Bits Eﬃciently . . . . . . . . . . . . . . 136 6.2.5 Materials for Bit Patterned Magnetic Media . . . . . . . . . . 137 6.2.6 Maintaining Competitiveness . . . . . . . . . . . . . . . . . . . . . . . 138 6.2.7 Going Nano and Beyond . . . . . . . . . . . . . . . . . . . . . . . . . . . 138 6.3 Self-assembly and Magnetic Media . . . . . . . . . . . . . . . . . . . . . . . . . 139 6.3.1 Alumina Templates . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 139 6.3.2 Guided Self-assembly as a Solution to Long-Range Ordering . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 142 6.3.3 Chemically vs. Topographically Guided Self-assembly . . 144 6.3.4 Biological Self-assembled Templates . . . . . . . . . . . . . . . . . . 144 6.3.5 The Versatility of Block Copolymers . . . . . . . . . . . . . . . . . 144 6.3.6 Inorganic Templates May Still Be Competitive . . . . . . . . 145 6.4 Present Alternatives for Discrete Media Production . . . . . . . . . . 145 6.4.1 Patterning with Stampers and Masks . . . . . . . . . . . . . . . . 145 6.4.2 Cleanliness Concerns . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 146 6.4.3 Obtaining High Aspect Ratios . . . . . . . . . . . . . . . . . . . . . . 147 6.4.4 Types of Nanopatterning Processes . . . . . . . . . . . . . . . . . . 147 6.4.5 Emerging Fabrication Techniques . . . . . . . . . . . . . . . . . . . . 148 6.4.6 Discrete Track Media . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 149 6.4.7 Identifying Track Locations . . . . . . . . . . . . . . . . . . . . . . . . . 149 6.4.8 Parallel Writing of Data . . . . . . . . . . . . . . . . . . . . . . . . . . . . 150 6.4.9 Magnetic Lithography for Mass Data Replication . . . . . . 150 6.4.10 Magnetic Disk Drives vs. Semiconductor Processing . . . . 151 6.4.11 Head Performance . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 151 6.4.12 Spin Valves and Giant Magnetoresistive Heads . . . . . . . . 152 6.4.13 Looking Back and into the Future . . . . . . . . . . . . . . . . . . . 152 References . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 153

7

Concluding Remarks . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 161 Reference . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 161

Index . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 163

Symbols

BJ bcc c d d dV e E Eexchange Em Emagnetocrystalline Emagneotelastic Emagnetostatic Ewall F g g g0 G↑ G↓ Gtot ↑ Gtot ↓ H H H ˆ H H0 Hcw

Brillouin function Body centered cubic Crystallographic axis Diameter of ﬁrst Airy ring nm Displacement of the magnetic wall nm Unit volume cm3 Electron charge 1.602176487 × 10−19 C Induced electric ﬁeld (intensity) V cm−1 Exchange energy (density) J cm−3 ˆ (also known as magnetic energy) J Eigenvalues of H Magnetocrystalline (anisotropic) energy (density) J cm−3 Magnetoelastic energy (density) J cm−3 Magnetostatic energy (density) J cm−3 Energy (density) per unit surface area and unit wall thickness J cm−3 Magnetic force N Electron spin g−factor Land´e g-factor Free electron g-factor, g0 = 2.0023 “Spin-up” conductance S “Spin-down” conductance S Total “spin-up” conductance S Total “pin-down” conductance S Reduced Planck constant J s or N m s Applied magnetic ﬁeld (intensity) A m−1 or Oe External magnetic ﬁeld (intensity) Oe Magnetic ﬁeld intensity Oe Hamiltonian Applied magnetic ﬁeld intensity A m−1 or Oe Magnetic wall coercivity Oe

XVIII Symbols

Hext HM Hσ hcp I je jM J Jz Jz kT l lsd L L L m mJ M M M MY MBNenergy MR n n n n0 N NA NA p p p p P r R(0) R(H) s S S

External magnetic ﬁeld (intensity) Oe Demagnetizing ﬁeld (intensity) Oe Magnetic ﬁeld (intensity) due to Bloch wall energy gradient Oe Hexagonal closed packed Sensing current A Net electric current (density) A cm−3 Net magnetization current (density) A cm−3 Total atomic angular momentum units of z component of J units of Expectation value of Jz units of Thermal activation energy J Length of bar magnet cm Spin diﬀusion length nm Torque N m Minimum mark length nm Total orbital angular momentum units of Magnetic moment A m2 Eigenvalues of Jz Magnetization A m−1 or Wb m; 1 Wb m = 1/4π ×1010 gauss cm3 Maximum moment reached before unloading kg m2 Specimen magnetization T Moment of yield at outer surface kg m2 See text for description mV2 s Magnetoresistance % Density of states for majority (↑) and minority (↓) spin-polarized electrons cm−3 or J−1 Number of electrons in an atom Spin density at distance x from the interface cm −3 or J−1 Spin density at the interface cm −3 or J−1 Number of atoms in the sample (e.g. Avogadro number) Numerical aperture of the objective lens System numerical aperture Direction of polarization (German: parallel) Magnetic pole strength Wb Pattern period nm Recording wavelength for magnetic mark nm Spin polarization of the ferromagnetic layer % Distance between magnetic poles cm Resistance at zero magnetic ﬁeld Ω Resistance at a magnetic ﬁeld value H Ω Direction of polarization (German: senkrecht) Electron spin Total spin angular momentum units of

Symbols

t T T2 T↑ T↓ U ν νF νw V x x x X z Z

XIX

Sample thickness mm Absolute temperature K Transverse relaxation time ns “Spin-up” transmission probability “Spin-down” transmission probability Potential energy J Linear velocity of the rotating disk m s−1 Fermi velocity m s−1 Linear velocity of the magnetic wall m s−1 Detected voltage V Distance from the interface nm Domain wall position nm Ratio of magnetic and thermal energies Magnetic susceptibility H m−1 Axis in the x, y, z Cartesian system Partition function

Greeks α α α β β ηM ηM ΘN θ θ θ κα λ λ λ λ λs λ100 λ111 µ0 µB µJ µJz µw

Energy (density) contribution responsible for an easy axis J cm−3 Magnetoelectric voltage coeﬃcient V cm−1 Oe−1 Parameter measuring spin transport asymmetry Energy (density) contribution from the isotropic background J cm−3 |e| Bohr magneton 2mc = 10−24 J T−1 Spin injection eﬃciency for a single heterojunction Spin injection eﬃciency for a double heterojunction N´eel temperature K Angle between the directions of magnetic ﬁeld and bar magnet magnetization Angle at which a magnetic ﬁeld is applied Half-angle between the two beams in interference lithography Magnetic anisotropy constant J cm−3 Magnetostriction Light wavelength used in lithography nm Mean free path nm Readout light wavelength nm Isotropic saturation magnetostriction Saturation longitudinal magnetostriction along [100] Saturation longitudinal magnetostriction along [111] Permeability of vacuum µ0 = 4π × 10−7 H m−1 Bohr magneton µB = 9.27400949(80) × 10−24 J T−1 Component of µ parallel to J Bohr magnetons Projection of µJ along z Bohr magnetons Wall mobility cm2 V−1 s

XX

µJz µL µS µ ρ τ τ↑↓ υ ϕ χ0 χ

Symbols

expectation value of the magnetic moment µJz Bohr magnetons Magnetic moment associated with L Bohr magnetons Magnetic moment associated with S Bohr magnetons Total magnetic moment Bohr magnetons Resistivity corresponding to “spin-down” and “spin-up” electrons Ω cm Wall displacement time ns Spin-ﬂip time ns Magnetic switching volume cm3 Easy axis direction Relative susceptibility Magnetic susceptibility

1 Introduction

Summary. The reader is introduced to some historical concepts in magnetism discovered over half a century ago, but of signiﬁcant usefulness nowadays. Some magnetic nondestructive testing techniques, as well as magnetic tapes are based on a few of these concepts. Furthermore, many modern applications of magnetism rely on atomic scale magnetic phenomena that reach macroscopic values even at a few nanometers. With the advent of nanotechnology and its widespread implications, these concepts are the foundation for understanding a few of those that rely on magnetic properties. Nevertheless, the ﬁrst chapter does not discuss all magnetic concepts or magnetic phenomena on which applications such as nanomechanical devices, spin valves, or quantum computing are based. On the contrary, the whole purpose of this book is to gradually entice the reader to discover the many sides of this discipline termed magnetism. As the book progresses, more and more magnetic concepts are being revealed and placed in a contemporary application context. Most people are not aware that a signiﬁcant number of modern conveniences are based on magnetic properties. Hence, the book aims at clarifying these facts.

Magnetism has stimulated the interest of humans for a few thousand years, oﬀering the possibility for imaginative exploitation of magnetic properties. From the compass needle to magnetic storage media, the overwhelming variety of magnetic discoveries has covered a colossal range of applications [1]. Whether by incorporating naturally occurring magnetic materials, or fabricating advanced artiﬁcial magnetic structures, the human intellect has been tireless in the pursuit of novel technologies [2]. Many magnetic phenomena were discovered over half a century ago [1]. They are gaining recognition now because manipulating magnetic structures is leading to signiﬁcant technological advancements, such as nanomechanical devices, spin valves [3], and quantum computing [4, 5]. Many people are not aware of the fact that a signiﬁcant number of modern conveniences are based on magnetic phenomena [6]. Furthermore, many of the magnetic properties encountered, whether intrinsic or induced, have atomic origins, but become fulﬂedged on length scales of the order of a few nanometers [7]. From there,

2

1 Introduction

they become macroscopically observable [4]. This recurrent fact, explicit or implied, should be kept constantly in mind as it represents the foundation for the topics depicted throughout this book.

1.1 Review of Certain Historic Magnetic Concepts The mineral called magnetite (Fe3 O4 ), the ﬁrst magnetic material discovered, takes its name after Magnesia, a region in Turkey. A pointed piece of magnetite turns approximately north–south if it is supported in air or on the surface of water [8]. Alternatively, a pivoted iron needle becomes magnetic if rubbed with magnetite, and hence positions itself north–south. The word lodestone is derived from this directional property of magnetite or magnetized iron, as it means, in old English, a stone that leads the way (or lode). However, not all magnetite can become lodestones. A certain composition and crystal structure are required, as well as a strong magnetic ﬁeld such as the transient ﬁeld produced by lightning. The beginnings of magnetism are covered in many books, among which Still’s [8] or Guimar˜ aes’ [9] oﬀer a captivating account on the properties and history of lodestone, as well as other permanent magnets. 1.1.1 Magnetic Susceptibility The most common way of classifying magnetic properties of materials is by their response to an applied magnetic ﬁeld. Materials that are magnetized to a certain extent by a magnetic ﬁeld are called magnetic [10]. In particular, it is the quantity termed magnetic susceptibility χ that characterizes the magnetic response through the relationship M = χH 0 ,

(1.1)

where M is the magnetization, also known as the magnetic moment per unit volume, and H 0 is the applied magnetic ﬁeld intensity [11]. Magnetic susceptibility is usually a tensor and a function of both ﬁeld H 0 and magnetization M . For a magnetically isotropic material, M is parallel to H 0 , and χ is reduced to a scalar quantity. The unit for the permeability of vacuum µ0 is the same as for χ [12]. Hence, it is possible to measure χ in units of µ0 . In this case, the measured dimensionless quantity is called relative susceptibility and is denoted by χ0 χ χ0 = . (1.2) µ0 Values for relative susceptibilities range from 10−5 [12] (very weak) to 106 (very strong magnetism). In some cases, the relative susceptibility is negative. Or, the relationship between M and H is not linear, so that χ0 depends on H . The behavior of χ0 leads to various types of magnetism [2]. The origins of magnetism can be traced back to the orbital motion and to the spin of electrons that obey the Pauli exclusion principle, which will be brieﬂy reviewed in subsequent sections.

1.1 Review of Certain Historic Magnetic Concepts

3

1.1.2 Classiﬁcation of Magnetic Materials Ferromagnetic materials contain spontaneously magnetized magnetic domains where an individual domain’s magnetization is oriented diﬀerently with respect to the magnetization of neighboring domains [2]. The spontaneous domain magnetization is a result of unpaired electron spins from partially ﬁlled shells, spins aligned parallel to each other due to a strong exchange interaction. The arrangement of spins depends on temperature and so does the spontaneous domain magnetization [2]. When the total resultant magnetization for all magnetic domains is zero, the ferromagnetic material is said to be demagnetized. However, an applied magnetic ﬁeld changes the total resultant magnetization from zero to a saturation value [2]. When the magnetic ﬁeld is decreased and reverses in sign, the magnetization of a ferromagnetic material does not retrace its original path of values, the material exhibiting so-called hysteresis [2]. A strong ferromagnet exhibits a relative susceptibility of 106 [12]. In contrast to ferromagnetism, a weak form of magnetism termed diamagnetism is attributed mainly to the orbital motion of electrons viewed classically as a “current loop,” creating a magnetic moment [11]. An external magnetic ﬁeld induces a magnetic ﬂux in the diamagnetic material which counters the change in the external ﬁeld. Diamagnetic materials exhibit an antiparallel magnetization with respect to the direction of the applied magnetic ﬁeld, opposing the latter according to Lenz’s law. Thus, the magnetization of a diamagnetic material is proportional to the applied magnetic ﬁeld as seen in Fig. 1.1. Diamagnets have a negative and very weak relative susceptibility, of the order 10−5 [12]. Consequently, if a few magnetic atoms exist in the material, their inﬂuence overshadows the diamagnetism. Nonmagnetic atoms may become spin polarized by neighboring ferromagnetic atoms. Similar to ferromagnetism, paramagnetism is also attributed to unpaired electron spins. However, due to a diﬀerent electron conﬁguration, these spins are free to change their direction. Therefore, at certain temperatures they assume random orientations as a consequence of thermal agitation [11].

M

H

Fig. 1.1. Linear relationship between magnetization and applied magnetic ﬁeld (intensity) in a diamagnetic material

4

1 Introduction

An example of paramagnetism is the conﬁguration of the electrons in the conduction band of metals [12]. When an external magnetic ﬁeld is applied, a weak induced magnetization is produced parallel to the ﬁeld. The induced magnetization is proportional to the external ﬁeld, nevertheless stays positive, unlike in diamagnets. On the other hand, the susceptibility is inversely proportional to absolute temperature T , a fact also known as the Curie–Weiss law [11] (Fig. 1.2). For paramagnets, the relative susceptibility is a positive [12] 10−3 to 10−5 . Analogous to paramagnetism, antiferromagnetism also exhibits a small positive relative susceptibility that varies with temperature [11]. However, this dependence diﬀers signiﬁcantly not only in the shape of the curve but also in the fact that in an antiferromagnetic material it displays a change at the so-called [11] N´eel temperature ΘN (Fig. 1.3). Below this temperature, the electron spins are arranged antiparallel so that they cancel each other and an external magnetic ﬁeld is faced with a strong opposition due to the interaction between these spins. Consequently, the susceptibility decreases as 1/χ

T

Fig. 1.2. Curie–Weiss law of paramagnetism, where the susceptibility is inversely proportional to absolute temperature

1/χ

0

ΘN

T

Fig. 1.3. Variation of susceptibility with temperature for an antiferromagnetic material

1.1 Review of Certain Historic Magnetic Concepts

5

the temperature decreases, in contrast to paramagnetic behavior. However, above the N´eel temperature the spins become randomly oriented while the susceptibility decreases as the temperature is raised [11]. Ferrites exhibit a kind of magnetism known as ferrimagnetism, in some ways similar to ferromagnetism [2]. However, in ferrimagnetic materials magnetic ions are placed on two diﬀerent types of lattice sites, so that spins on one site type are oppositely oriented to spins on the other lattice site type [12]. The result is a total nonzero magnetization that is spontaneous. Nevertheless, an increase in temperature brings about a disturbance in the spin arrangement that culminates in completely random orientation of spins at the Curie temperature. At this temperature, the ferrimagnet loses its spontaneous magnetization and becomes paramagnetic. Ferromagnetic materials also have a Curie point above which they exhibit paramagnetic behavior [10, 13]. 1.1.3 The Concept of Magnetic Pole Quite often, the treatment of magnetism is similar to that of electrostatics [13, 14]. The fundamental magnetic phenomenon is viewed as an interaction between magnetic poles of strengths p1 and p2 separated by a distance r, analogous to the Coulomb interaction between electrically charged particles [12, 13]: p1 p2 , (1.3) F = 4πµ0 r2 where F is the force acting on a magnetic pole and µ0 is the permeability of vacuum mentioned above. Alternatively, an electric current will also exert a force on a magnetic pole. Whether it is another magnetic pole or the electric current producing a magnetic ﬁeld, the force F acting on a magnetic pole of strength p is [12, 13] F = pH 0 ,

(1.4)

where H 0 is the applied magnetic ﬁeld. Magnetic poles occur in pairs. When a magnet is cut into pieces, each piece will have a pair of poles [11, 13]. Equation (1.4) implies that if a magnetic material is brought near a magnet, the magnetic ﬁeld of the magnet will magnetize the material [12, 13]. Consequently, the magnetic ﬁeld is sometimes called a magnetizing force. Furthermore, it is customary to represent the magnetic ﬁeld by lines, also called lines of force (Fig. 1.4) to which a compass needle would be a tangent [11, 13]. As seen in Fig. 1.4, the magnetic ﬁeld lines outside the magnet radiate outward from the north pole. They leave the north pole and return at the south pole, reentering the magnet [12]. If a bar magnet of length l which has magnetic poles p and −p at its ends is placed in a uniform magnetic ﬁeld, the couple of magnetic force gives rise to a torque [13] L L = −plH sin θ, (1.5)

6

1 Introduction

S

N

Fig. 1.4. Magnetic ﬁeld representation outside a magnet or magnetized material

where θ is the angle between the direction of the magnetic ﬁeld H and the direction of the magnetization M of the bar magnet [11]. The product pl is the magnetization M of the bar [13]. The work done by the torque gives rise to a potential energy U in the absence of frictional forces [11, 13] U = −M H cos θ.

(1.6)

This equation is particularly important in the discussion of magnetic domains and the realignment of their magnetization when an external magnetic ﬁeld is applied [12]. The potential energy has a minimum value when [11, 13] θ = 0. 1.1.4 Magnetic Dipoles If the bar length l tends to zero value, while simultaneously the strength of the magnetic poles p approaches inﬁnity, the system thus produced is called a magnetic dipole [11, 12]. Alternatively, a magnetic dipole can also be deﬁned by a circular electric current of inﬁnite intensity spanning an area of zero dimension [12, 13]. No matter how we look at it, the magnetic dipole is only a mathematical concept, useful for the deﬁnition of some magnetic quantities. The magnetic moment m of the magnetic dipole is [13] m = M dV,

(1.7)

where M is the magnetization mentioned earlier, and dV is the unit volume. This equation was considered in earlier books as the deﬁnition [13] for M . If the magnetization is constant throughout the magnetized body, the latter is considered homogeneous from a magnetic point of view [12].

1.2 Origins of Magnetism on an Atomic Scale The magnetic moment of atoms originates from electrons in partly ﬁlled electron shells, and is determined by a fundamental property known as the angular momentum [15]. Each individual electron has an angular momentum associated with its orbital motion, and an intrinsic, or spin angular momentum [15]. Hence, there are two sources of the atomic magnetic moment: currents associated with the orbital motion of the electrons, and the electron spin [13].

1.2 Origins of Magnetism on an Atomic Scale

7

1.2.1 The Importance of Angular Momentum For an n-electron atom, these 2n angular momenta couple together to give a total angular momentum whose exact properties depend on the details of the coupling parameters [16]. The individual atomic orbital angular momenta couple together to give a total orbital angular momentum L, and the individual atomic spin angular momenta couple together to give a total spin angular momentum S . Finally, L and S couple together, to give a total atomic angular momentum [16] J . The orbital and spin angular momenta each have a magnetic moment associated with them µL = −βL,

µS = −2βS,

(1.8)

where β is the Bohr magneton. The total magnetic moment µ is then µ = −β(L + 2S).

(1.9)

A system consisting of N identical magnetic atoms will have a total angular momentum J and magnetic moment µ. L, S , and µ precess about J . The component of µ perpendicular to J averages to zero over a time significantly larger than the precession period [16]. When a ﬁeld is applied, only the component of µ parallel to J is sensed. That parallel component will be denoted µJ . The angular momentum state of an atom is characterized by eigenvalues of J [2], that is J(J +1). Using the properties of angular momentum operators and the law of cosines, we have µ2J = g 2 J(J + 1)β 2 .

(1.10)

Choosing the z component of J , that is Jz with eigenvalues mj = J, J − 1, . . ., −J, the magnetic moment along z is µJz = −gβJz ,

(1.11)

where g, the Land´e g-factor or spectroscopic splitting factor is given by∗ g =1+

J(J + 1) + S(S + 1) − L(L + 1) . 2J(J + 1)

(1.12)

Nevertheless, the Land´e g-factor results from the calculation of the ﬁrst-order perturbation of the energy of an atom when a weak external magnetic ﬁeld acts on the sample [15,16]. Normally, the quantum states of electrons in atomic orbitals are degenerate in energy, thereby the degenerate states all share the same angular momentum. However, if the atom is placed in a weak magnetic ﬁeld, the degeneracy is lifted [17]. Furthermore, this dimensionless g-factor relates the observed magnetic moment µJz of an atom to the angular momentum quantum number mj and the fundamental quantum unit of magnetism, that is the Bohr magneton [15, 16]. ∗

For a rigorous derivation of above results, please see any introduction to quantum mechanics [15, 16], or more specialized books on electric and magnetic susceptibilities [17].

8

1 Introduction

1.2.2 Magnetic Moment of a Sample of N Atoms In a simple paramagnet, the atoms do not interact with each other, and the ˆ come from their interaction with the only contributions to the Hamiltonian H applied magnetic ﬁeld H 0 . As the atoms are identical, only the Hamiltonian for a single atom needs to be considered [15–17] ˆ = −µJ · H 0 . H

(1.13)

Choosing H 0 to be along the z-axis, we can write [15, 16] ˆ = −µJ H 0 . H z

(1.14)

The eigenvalues of H are then [15–17] Em = −gβmj H 0 . The partition function Z is deﬁned by [15–17] ˆ Z= exp (−Em /kT ) = Tr exp −H/kT

(1.15)

(1.16)

n

or, in our case [15–17], ZJ =

J

exp (gβmj H 0 /kT ).

(1.17)

mj =−J

The partition function is an important quantity when dealing with multiparticle structures, as it encompasses the statistical properties of the entire system [15–17]. It depends on a number of factors, such as the system’s temperature, the angular momentum quantum number, external magnetic ﬁeld, etc. Furthermore, it is a sum over all states while determining how the probabilities are divided among the various states composing the system, based on their individual energies [15–17]. The magnetic and the thermal energies can be expressed in terms of the partition function. Denoting by x the ratio of magnetic and thermal energies [15–17] gβJH 0 , (1.18) x= kT the partition function becomes J sinh 2J+1 x 2J 1 . exp(mj x/J) = ZJ (x) = (1.19) sinh 2J x m =−J j

The partition function allows calculation of the expectation value of the magnetic moment µJz , a quantity observed experimentally [15–17].

1.2 Origins of Magnetism on an Atomic Scale

9

The magnetization of the sample of N atoms is given by [15, 16] M = N µJz = N gβ Jz , where

ˆ Tr Jz e−H/kT . Jz = ˆ Tr e−H/kT

Consequently, M = N gβ

ˆ Tr Jz eH/kT ZJ (x)

.

(1.20)

(1.21)

(1.22)

This expression can be reduced to the useful form [15, 16] M = N gβJBJ (x),

(1.23)

where BJ is called the Brillouin function [15, 16]. This function describes the dependency of the magnetization on the applied magnetic ﬁeld, temperature, and the total angular momentum quantum number; hence it is a useful concept. It is used to derive important laws of magnetism, such as the Curie–Weiss law mentioned earlier [12]. 1.2.3 Crystal Field vs. Spin–Orbit Coupling The magnetic moment of atoms in magnetic materials, such as the iron-series transition-metal atoms in ferromagnetic metals (e.g., Fe, Co, Ni, YCo5 ), and ferrimagnetic nonmetals (e.g., Fe3 O4 , NiO) is largely given by the spin, rather than orbital motion [10]. In this case, the spin moment µS is equal to the number of unpaired electron spins. On the other hand, the orbital moment µL is very small, typically of the order of 0.1 β, because the orbital motion of electrons is “quenched” by something called the crystal ﬁeld [17]. Each atomic moment is acted on by the crystal ﬁeld, proportional to the magnetization of its environment [12]. If an atomic moment were to be removed from its environment, it would leave behind a magnetic ﬁeld. The ﬁeld is produced by the surrounding spins, and is a manifestation of the local symmetry of the crystal. Crystal structure is a determining factor for intrinsic magnetic properties, such as saturation magnetization or magnetocrystalline anisotropy [2]. For example, the saturation magnetization of α-Fe (2.15 T) is associated with the bcc structure of elemental iron [13]. The competition between the electrostatic crystal ﬁeld interaction and spin–orbit coupling is responsible for the alignment of atomic magnetic moments [13], giving rise to magnetocrystalline anisotropy.

10

1 Introduction

1.2.4 Magnetocrystalline Anisotropy Magnetocrystalline anisotropy is in eﬀect a variation of magnetic properties with crystallographic orientation [2]. In iron, 100 is the preferred crystallographic direction along which magnetic moments from magnetic domains tend to align [2]. The anisotropy of most magnetic materials is of magnetocrystalline origin [13]. Permanent magnets, such as SmCo5 , or Nd2 Fe14 B need a high magnetic anisotropy to keep the domain magnetization in a desired direction [13]. This is achieved due to the electronic conﬁguration in these materials which results in a particular interaction between the crystal ﬁeld and the spin–orbit coupling, as explained below. The crystal ﬁeld acts on the orbits of the inner shell d and f electrons. Concurrently, as a relativistic phenomenon spin–orbit coupling is most pronounced for inner-shell electrons in heavy elements, such as rare-earth 4f electrons [13, 15, 16]. This results in a rigid coupling between spin and orbital moment in heavy elements [18]. On the other hand, the magnitude of the magnetocrystalline anisotropy depends on the ratio of crystal ﬁeld energy and spin–orbit coupling [19]. It should be emphasized that for Fe, Ni, and Co, the magnetocrystalline anisotropy is due to 3d electron spins, in contrast to the magnetocrystalline anisotropy for rare earths that originates in the 4f shells [18]. In fact, the strong magnetocrystalline anisotropy in permanent magnets is given by the comparatively small electrostatic interaction of the unquenched 4f charge clouds with the crystal ﬁeld [13, 17, 18]. The absence of quenching means that typical single ion anisotropies (rare earth ions) are much larger than 3d anisotropies [18, 19]. This strong magnetocrystalline anisotropy is exploited in advanced permanent magnets, where it leads to very high coercivities, such as 4.4 T in Sm3 Fe17 N3 -based magnets [13, 17, 18]. Therefore, a large number of magnetic applications are based on rare earth metal alloys [18]. 1.2.5 Magnetostriction Aside from spontaneous magnetization and magnetocrystalline anisotropy, other intrinsic magnetic properties such as magnetostriction, or exchange stiﬀness also have origins in atomic scale magnetism [20]. Although they manifest themselves on length scales of a few angstroms, they reach bulk values even [11] at ∼1 nm. Under the inﬂuence of a magnetic ﬁeld, the shape of a ferromagnetic object changes due to a magnetic property termed magnetostriction [11] (noted λ). However, this type of deformation is very small, only of the order ∼10−5 –10−6 [12], or even smaller in weakly magnetic materials. Magnetostriction was discovered in 1842 by Joule [11] who noticed a change in length when an iron rod was magnetized in a weak magnetic ﬁeld, similar to the schematic illustration in Fig. 1.5.

1.3 Structure-Dependent Micromagnetism

11

transverse magnetostriction

longitudinal magnetostriction

H Fig. 1.5. Elongation of a ferromagnetic object in the direction of an applied magnetic ﬁeld

Nevertheless, when a specimen elongates under an applied magnetic ﬁeld, its volume remains constant. This means that a transverse magnetostriction exists, about half the value of the longitudinal magnetostriction, and of opposite sign [11]. Magnetostriction is believed to be due to spin–orbit coupling of valence electrons in ferromagnets [12]. Because electron orbits are coupled to spins, when the latter change direction to align with domain magnetization, the orbits change shape to conserve angular momentum. Since electron orbits are coupled to the crystal lattice, the lattice inside a magnetic domain (see below) deforms spontaneously in the direction of domain magnetization [12]. Iron single crystals magnetized to saturation in the [100] direction, increase in that direction due to magnetostriction. The strain due to magnetostriction increases with magnetic ﬁeld, until it reaches a saturation value. This value can be positive, negative, or in some alloys, zero [11]. Furthermore, magnetostriction saturates along a speciﬁc crystallographic axis, for example, λ100 = 19.5 × 10−6 and λ111 = −18.8 × 10−6 in a single cubic crystal. λ100 and λ111 are the saturation values of the longitudinal magnetostriction in the directions [100] and [111], respectively [21]. Quite often, an “isotropic saturation magnetostriction” λs = λ100 = λ111 = −7 × 10−6 is assumed [21], although it is not representative of experimental results [22].

1.3 Structure-Dependent Micromagnetism Micromagnetic properties are usually structure dependent, and therefore responsible for a quite unique behavior of ferromagnetic materials under an applied magnetic ﬁeld [2]. Some nondestructive evaluation techniques exploit micromagnetic properties to detect ﬂaws and strains on the surface of engineering components [1]. Several aspects of nondestructive evaluation based on structure-dependent micromagnetism are discussed in more detail in Chap. 2.

12

1 Introduction

Nevertheless, its basis is the fact that strongly magnetic materials divide spontaneously into magnetic domains [13] as a consequence of the minimization contest of ﬁve diﬀerent energies, a process described brieﬂy below. 1.3.1 Division into Magnetic Domains In ferromagnetic materials, individual atomic magnetic moments tend to stay parallel to one another, keeping the exchange energy at a low value [13]. Such an alignment increases the magnetostatic energy by creating a large external magnetic ﬁeld [11], as shown in Fig. 1.6. Therefore within the material, several magnetic domains are created, where within each domain individual magnetic moments add up to a total domain magnetization [1]. Furthermore, the domain magnetizations of neighboring domains are antiparallel [11] (Fig. 1.7). In this conﬁguration, the exchange energy is somewhat increased, however the magnetostatic energy is lowered [11]. Domain walls are formed between magnetic domains [1]. 1.3.2 Formation of Domain Walls Further division into magnetic domains decreases magnetostatic energy even more, however the domain wall formed between domains with antiparallel magnetizations (Fig. 1.7) introduces an energy associated with the wall [11].

Fig. 1.6. Alignment of individual atomic moments increases magnetostatic energy by creating a large external magnetic ﬁeld

Fig. 1.7. Division into magnetic domains with antiparallel domain magnetizations decreases magnetostatic energy. A domain wall is formed between domains

1.3 Structure-Dependent Micromagnetism

13

domain wall

Fig. 1.8. Magnetic domain wall containing atomic magnetic moments of gradually varying orientation, ensuring a smoother transition to opposite domain magnetization

This wall increases the exchange energy which is highest at the wall [11]. Fortunately, the exchange force acts only over one or two atomic distances, having larger values in the wall vicinity. If the transition from one magnetization direction to another is sharp, as is the case with antiparallel domain magnetizations, the exchange energy will be too high to keep this domain conﬁguration in equilibrium [11]. Exchange energy [23] arises from the Pauli exclusion principle, and is a quantummechanical eﬀect based on the degree of wavefunction overlap [15, 16]. A domain wall of a certain width, encompassing atomic magnetic moments of gradually varying orientation (Fig. 1.8), ensures a smoother transition opposite to domain magnetization direction, decreasing the exchange energy [11]. The width of the transition layer is determined, and thereby limited by the magnetocrystalline energy, which in order to maintain a minimum, tends to keep atomic magnetic moments aligned along one of the easy directions of the crystal axes [11]. 1.3.3 Types of Domain Walls The transition layer known as a domain wall can be of two types: Bloch wall [24] where the atomic magnetic moments rotate outside of the plane of the magnetic moments, and N´eel wall [25] where atomic moments remain in plane while the rotation occurs [11]. Since domain magnetizations tend to align with preferred crystallographic axes, domain walls separating domains of diﬀerent orientations can be classiﬁed as 180◦ , 90◦ (iron) or 109◦ , 71◦ (nickel), depending on the angles these crystallographic axes make in a speciﬁc lattice [11]. It should be noted that some of these walls of diﬀerent orientation occur in closure domains [13]. The latter are created when the material divides into magnetic domains to allow more of the magnetic ﬂux to stay within the material, minimizing magnetostatic energy [11, 13] (Fig. 1.9). To monitor magnetostatic ﬁelds and domain conﬁgurations, colloidal suspensions termed [26] ferroﬂuids are usually employed. Ferroﬂuids, for instance

14

1 Introduction closure domains

Fig. 1.9. Formation of 90◦ closure domains in iron. The closure domains are perpendicular to the 180◦ domains, illustrated here with vertical domain magnetizations

Fe3 O4 or BaFe12 O19 are stable substances, typically 10 nm particles immersed in hydrocarbons or other organic liquids, as water-based ferroﬂuids are more diﬃcult to produce. They can also be used as liquids in bearings. 1.3.4 Signiﬁcance of Magnetic Domains and Domain Walls Magnetic domains and their walls are responsible for extrinsic magnetic properties, such as remanence and coercivity. They are also the reason for the hysteresis observed in ferromagnetic materials [27]. Magnetic domain conﬁgurations change with an applied magnetic ﬁeld or stress through the displacement of domain walls. Therefore magnetic domains and in particular domain wall pinning by obstacles are magnetic microstructures exploited in some technological applications based on magnetic Barkhausen noise, or thickness dependent domain wall and coercive phenomena in thin ﬁlms. On the other hand, in some cases such as magnetic recording, energetic losses created in the material because of these microstructures need to be minimized [28]. Particle size determines domain conﬁgurations and the mechanism of magnetization reversal within magnetic domains [29]. For instance, clusters are single-domain magnets and their large surface-to-volume ratio leads to strong diameter dependence of intrinsic properties such as anisotropy and magnetization [30]. Clusters tend to be superparamagnetic, particularly at high temperatures [31]. These aspects are important in magnetic recording. Thin-ﬁlm magnetism was initially also related to micromagnetic structures such as domains and domain walls [32]. Nowadays, it has developed into a separate branch of condensed matter physics [32] because nanostructured thin-ﬁlms with intermediate or high coercivities are used in permanent magnets or magnetic recording [33], both strong and independent areas of magnetism.

1.4 Towards Technological Advancements

15

1.4 Towards Technological Advancements Magnetism is at present a very diversiﬁed discipline. Many magnetic structures, whether naturally occurring or artiﬁcially created have opened new possibilities for scientiﬁc and technological developments [34]. However, improving performance of existing magnetic materials is merely one of the many challenges of contemporary research [35]. Ultimately, new applications become feasible pushing not only nature, but also the human imagination, to its unexplored boundaries. A few of these topics will be discussed in subsequent chapters. 1.4.1 Design of New Magnetic Materials Apart from natural magnets, most magnetic materials are not really known to the public at large. If faced with the option of drawing up a list of materials exhibiting magnetic properties, very few people can name more than three. To complicate matters even further, a new “materials design” approach is implemented these days in a few areas of magnetism. One method is to nanoengineer structures to the extent that entirely new materials are fabricated. This creates artiﬁcial “metamaterials” relying on combined magnetic phenomena not observable in the original individual compounds. For instance, by introducing soft phases into hard ones, or incorporating a soft phase into an amorphous matrix, a completely diﬀerent magnetic material can be created [36]. It is no wonder that we read reports of embedded magnetic clusters, or granular polymer materials displaying shape anisotropy [37]. Whatever the case may be, it shows that magnetic properties are realized on comparatively small length scales [38]. It also justiﬁes why multiphase structures imitate the coexistence of independent magnetic properties [32]. Nevertheless, interesting magnetic systems have been produced by mechanical alloying and chemical reactions, with many possible applications: advanced magnetic recording media [39], materials for microwave applications, or even electroluminescent display devices [40]. 1.4.2 Magnetic Quantum Dots The search for ever-increasing storage densities in magnetic recording has led to the fabrication of two-dimensional arrays of nanodots. These are in essence very small structures where quantum-mechanical eﬀects are no longer negligible, therefore coining the term quantum dots [41, 42]. Concepts such as quantum well states and spin degrees of freedom come into play, expanding the areas of applications for quantum dots to quantum computing and spin electronics [43]. Several methods for producing quantum dots are currently being investigated, and some are reviewed later in this book. From more traditional ones,

16

1 Introduction

such as nanolithography, molecular beam epitaxy, or chemical vapor deposition, to emerging self-assembly techniques, whether DNA-assisted or chemically induced, complex arrays of quantum dots are presently being developed all over the world [4]. However, their long term survival will ultimately be determined by their ability to be implemented in large scale fabrication with minimum costs. Until then, these techniques are conﬁned to the laboratory. In the following chapters, a closer look will also be taken at other types of nanostructures, and their feasibility examined. The present book examines the fascinating realm of magnetic phenomena from a variety of angles, emphasizing current interests, as well as emerging trends in the ever-progressing technological miniaturization. Of course, the book is not all inclusive, however it opens the door for a sequence of topics that may be discussed in the future.

References 1. D.C. Jiles, Introduction to Magnetism and Magnetic Materials (Chapman and Hall, New York, 1991) 2. R.M. Bozorth, Ferromagnetism (IEEE Press, New York, 1951) 3. S. Mørup, C. Frandsen, Phys. Rev. Lett. 92(21), 217201 (2004) 4. R. Skomski, J. Phys.: Condens. Matter 15, R841 (2003) 5. E. Svoboda, IEEE Spectrum. 15 (2007) 6. R.B. Cowburn, A.O. Adeyeye, M.E. Welland, Phys. Rev. Lett. 81(24), 5414 (1998) 7. J. Fidler, T. Schreﬂ, J. Phys. D: Appl. Phys. 33, R135 (2000) 8. A. Still Soul of Lodestone: The Background of Magnetical Science (Murray Hill Books, New York, 1946) 9. A.P. Guimar˜ aes, From Lodestone to Supermagnets: Understanding Magnetic Phenomena (Wiley, New York, 2005) 10. M.E. Schabes, J. Magn. Magn. Mater. 95, 249 (1991) 11. B.D. Cullity, Introduction to Magnetic Materials, 2nd edn. (Addison-Wesley, New York, 1972) 12. S. Chikazumi, Physics of Magnetism (Wiley, New York, 1964) 13. R. Becker, W. D¨ oring, Ferromagnetismus, (Springer, Berlin, 1939) 14. F.T. Ulaby, Fundamentals of Applied Electromagnetics (Prentice Hall, New Jersey, 1999) 15. D.J. Griﬃths, Introduction to Quantum Mechanics (Prentice Hall, New Jersey, 1995) 16. W. Greiner, Quantum Mechanics, an Introduction, 2nd edn. (Springer, Berlin, 1994) 17. Van Vleck, Theory of Electric and Magnetic Susceptibilities (Oxford University Press, Oxford, 1965) 18. J.M.D. Coey (ed.), Rare-Earth Iron Permanent Magnets (Oxford University Press, Oxford, 1996) 19. A. Aharoni, Introduction to the Theory of Ferromagnetism (Oxford University Press, Oxford, 1996)

References

17

20. J.S. Smart, Eﬀective Field Theories of Magnetism (Saunders, Philadelphia, 1966) 21. C. Kittel, J.K. Galt, Solid State Phys. 3, 437 (1956) 22. M.J. Sablik, G.L. Burkhardt, H. Kwun, D.C. Jiles, J. Appl. Phys. 63(8), 3930 (1988) 23. W. Heisenberg, Z. Physik 49, 619 (1928) 24. F. Bloch, Z. Physik 57, 545 (1929) 25. L. N´eel, Ann. Geophys. 5, 99 (1949) 26. W.-L. Luo, S.R. Nagel, T.F. Rosenbaum, R.E. Rosenzweig, Phys. Rev. Lett. 67, 2721 (1991) 27. W.F. Brown, Micromagnetics (Wiley, New York, 1963) 28. J.A.C. Bland, B. Heinrich (eds.), Ultrathin Magnetic Structures, vol. 1 (Springer, Berlin, 1994) 29. T. Schreﬂ, J. Fidler, K.J. Kirk, J.N. Chapman, J. Magn. Magn. Mater. 175, 193 (1997) 30. S.E. Apsel, J.W. Emmert, J. Deng, L.A. Bloomﬁeld, Phys. Rev. Lett. 76, 1441 (1996) 31. C.P. Bean, J.D. Livingston, J. Appl. Phys. 30, 120S (1959) 32. D.J. Sellmeyer, C.P. Luo, Y. Qiang, J.P. Liu, Handbook of Thin Film Materials, ed. by H.S. Nalwa, vol. 5 (Academic, San Diego, CA, 2002) 33. R.A. McCurrie, Ferromagnetic Materials. Structure and Properties (Academic, London, 1994) 34. R.M.H. New, R.F.W. Pease, R.L. White, J. Magn. Magn. Mater. 155, 140 (1996) 35. R.W. Chantrell, D. Weller, T.J. Klemmer, S. Sun, E.E. Fullerton, J. Appl. Phys. 91, 6866 (2002) 36. U. Gradmann, Handbook of Magnetic Materials, ed. by K.H.J. Buschow, vol. 7 (Elsevier, Amsterdam, 1993) 37. S.W. Charles, Studies of Magnetic Properties of Fine Particles and Their Relevance to Materials Science, ed. by J.L. Dormann, D. Fiorani (Elsevier, Amsterdam, 1992) 38. R. Skomski, J.M.D. Coey, Permanent Magnetism (Institute of Physics, Bristol, 1999) 39. I.A. Al-Omari, D.J. Sellmeyer, Phys. Rev. B 52, 3441 (1995) 40. J.E. Evetts (ed.), Concise Encyclopedia of Magnetic and Superconducting Materials (Pergamon Press, Oxford, 1992) 41. A.V. Khaetskii, Y.V. Nazarov, Phys. Rev. B 64, 125316 (2001) 42. H. Zeng, R. Skomski, L. Menon, Y. Liu, S. Bandyopadhyay, D.J. Sellmeyer, Phys. Rev. B 65, 134426 (2002) 43. X.-D. Hu, S. Das Sarma, Phys. Rev. A. 61, 062301 (2000)

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

Summary. In a large part of the hysteresis cycle of a ferromagnetic material, the magnetization process takes place through a random sequence of discontinuous movements of magnetic domain walls, giving rise to what is termed magnetic Barkhausen noise (MBN). This noise phenomenon can give information on the interaction between domain walls and stress conﬁgurations, or compositional microstructure. It is also a complementary nondestructive testing technique to eddy-current probe sensors as well as magnetic ﬂux leakage (MFL), both established in the nondestructive evaluation industry. This chapter takes a closer look at the inﬂuence of stress on magnetic domain conﬁguration, and how this is reﬂected in the MBN signal. The latter can be analyzed by using a variety of parameters, and some of these are introduced during the discussion. Apart from domain conﬁguration, stress also aﬀects magnetic anisotropy which can reveal further details on the stress state present in the material. Concurrently, residual stresses and dislocations play a signiﬁcant role in the MBN investigation, completing the analysis and adding to the competitiveness of MBN as a nondestructive testing technique for ferromagnetic materials.

2.1 Introduction In a large part of the hysteresis cycle of a ferromagnetic material, the magnetization process takes place through a random sequence of discontinuous movements of magnetic domain walls, giving rise to what is termed magnetic Barkhausen noise (MBN) [1,2]. This noise phenomenon is investigated statistically through the detection of the random voltage observed on a pick up coil during the magnetization of the material [3]. Analysis of MBN can give information on the interaction between domain walls and stress conﬁgurations, or compositional microstructure [4]. It is also a complementary nondestructive testing technique to eddy-current probe sensors [5–7] as well as magnetic ﬂux leakage (MFL) [8], both more established in the nondestructive evaluation industry.

20

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

2.2 A Basic Deﬁnition of Magnetic Barkhausen Noise As mentioned above, during the action of a smoothly varying alternating magnetic ﬁeld of intermediate intensity, abrupt irreversible changes in the form of MBN emissions (Fig. 2.1) are observed in the magnetization of a ferromagnetic material [3]. These irreversible changes occur in the steep part of the magnetization curve, and they account for magnetic hysteresis in ferromagnetic materials [9]. MBN is named after its discoverer [10], and is called “noise” due to the sound heard in the loudspeaker used in the original experiment. It is termed “magnetic” to distinguish it from acoustic Barkhausen noise, the latter being based on magnetoacoustic emission [11, 12]. 2.2.1 Types of MBN Experiments There are two types of Barkhausen noise experiments that are usually performed. If the detection coil is placed on the surface of the specimen, the emissions are termed surface Barkhausen noise, whereas a coil wrapped around the specimen detects encircling Barkhausen noise [13, 14] (Fig. 2.2). According to M

magnetic Barkhausen noise

H

Fig. 2.1. Irreversible discontinuities in magnetization M as the ac magnetic ﬁeld H is varied are termed magnetic Barkhausen noise

specimen

specimen coil

coil

Fig. 2.2. Surface (left) vs. encircling (right) Barkhausen noise detection

2.2 A Basic Deﬁnition of Magnetic Barkhausen Noise

21

Excitation electromagnet

DC

Search Coil

Bipolar power amplifier Specimen Waveform generator

Applied moment

Amplifier 0.5kHz high pass filter

PC Supplementary amplifier & filter Two channel ADC

Fig. 2.3. A typical MBN measurement apparatus (reprinted from [16] (copyright 2004) with permission from Elsevier)

skin depth considerations [15], the estimated depth for minimum penetration of the magnetizing ﬁeld is roughly 1 mm, whereas the depth from which the MBN signal originates is ∼30 µm. A typical MBN experimental setup [16] is sketched in Fig. 2.3. The MBN signal is detected by a search coil with a large number of turns of insulated copper wire wound around a ferrite cylinder. The output of the search coil is ampliﬁed and ﬁltered [16]. 2.2.2 Where does MBN Originate? A ferromagnetic material that has not been magnetized consists of a large number of magnetic domains with random magnetic orientation, so that the bulk net magnetization is zero [3, 17] (Fig. 2.4). An external magnetic ﬁeld tends to align the individual magnetic moments of the domains. Those domains with moments aligned most closely with the applied ﬁeld will increase in volume at the expense of the other domains [9] (Fig. 2.5). The specimen becomes magnetized, as the walls move between adjacent domains [17]. When the external magnetic ﬁeld is removed, the domains do not necessarily revert back to their original conﬁguration [9]. This is because domain walls may have encountered pinning sites while moving, and to overcome these energy was expended [3, 9]. Once the wall has made it over the pinning site, there is no return path when the ﬁeld is no longer acting. MBN is the irreversible “jump” of domain walls over local obstacles acting as pinning sites, such as grain boundaries, dislocations, inhomogeneities or other imperfections (Fig. 2.6). All lattice irregularities are likely to cause delays in domain wall movement, leading to uneven and discontinuous changes in magnetization [9, 18].

22

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

Fig. 2.4. Sketch of magnetic domains with random magnetic orientation in a polycrystalline ferromagnetic material, in the absence of an external magnetic ﬁeld or stress. The dark curves represent grain boundaries (reprinted from [20]) domain wall displacement under the influence of a magnetic field

applied H

domain wall position in the absence of a magnetic field

Fig. 2.5. Under the inﬂuence of an applied magnetic ﬁeld, magnetic domains grow through wall displacement. Domains with moments aligned most closely with the applied ﬁeld will increase in volume at the expense of the other domains. Dashed lines show wall positions in the absence of the ﬁeld (reprinted from [20])

2.2.3 Formation of Magnetic Domains Formation of magnetic domains occurs because of a minimization contest of the ﬁve basic energies involved in ferromagnetism: E = Eexchange + Emagnetostatic + Emagnetocrystalline + Emagnetoelastic + Ewall . (2.1) The exchange energy Eexchange originates in quantum mechanical exchange forces or spin–spin interactions that are responsible for ferromagnetism [19]. A minimum in exchange energy is obtained when the spins of unpaired

2.2 A Basic Deﬁnition of Magnetic Barkhausen Noise

23

domain wall energy domain wall jump

0

x0x1

x2

x3

x wall position

Fig. 2.6. Irreversible Barkhausen transitions. Domain walls overcome pinning sites and settle at energetically more favorable positions (reprinted from [20])

electrons are parallel, which is not possible in the same phase space. The magnetostatic energy Emagnetostatic reaches a minimum when the magnetization of a magnetic domain is parallel to the external magnetic ﬁeld [3, 9]. Crystal symmetry gives rise to a magnetocrystalline (anisotropic) energy Emagnetocrystalline that becomes minimum when the magnetization of a magnetic domain is aligned with a preferred crystallographic direction, such as 100 in iron [15]. These directions are also termed axes of easy magnetization [3]. The crystal lattice strain is related to the direction of domain magnetization through the magnetoelastic energy Emagneotelastic [9]. It is a minimum when the lattice is deformed such that the domain is elongated or contracted in the direction of domain magnetization [9]. The ﬁfth energy is related to the fact that domain walls have certain energy per unit area of surface and unit thickness of wall Ewall because atomic moments are not parallel to each other, or to an easy axis. Increases and decreases in these ﬁve energies have consequences for the equilibrium of the crystalline lattice in the material such that not all energies can be minimum at the same time. Formation of a certain magnetic domain conﬁguration is the outcome of the sum of the ﬁve basic energies being minimized, although the energies themselves may not be at their minimum [20]. 2.2.4 MBN and 180◦ Domain Walls Domain walls separating regions of opposite magnetic moment are called 180◦ walls, whereas walls lying at 90◦ to each other are appropriately termed 90◦ walls [3, 15]. Nickel has 109◦ and 71◦ domain walls [3, 15]. It is believed that MBN is primarily due to 180◦ domain wall motion [3,9,21]. The 90◦ domain walls have stress ﬁelds associated with them, as their magnetizations lie at right angles on either side of the wall, causing lattice

24

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

spacings to be slightly larger in the direction of magnetization. The resulting strain impedes with 90◦ domain wall motion, making them less competitive than 180◦ domain walls that have a higher velocity [22].

2.3 Stress Eﬀects Due to its high sensitivity to stress, MBN can be used as an independent nondestructive technique (NDT) for the evaluation of elastic stresses and strains [23], as well as plastic deformation and its consequences [20, 24]. 2.3.1 Elastic Stress Causes Changes in Bulk Magnetization A ferromagnetic material subjected to stress will cause changes to its bulk magnetization, even if no applied ﬁeld is present [3]. This is because magnetic domains are inﬂuenced by stress and the resulting strain inside the material. Magnetic domains undergo stress-induced volume changes just like they would under an external magnetic ﬁeld. As the internal elastic stress increases, the ﬁeld required to move a domain wall across a pinning site, as well as the wall energy gradient increase, too [3]. The pinning sites themselves are also inﬂuenced by stress [25]. In fact, elastic strain eﬀects are more inﬂuential on Barkhausen noise than plastic strain eﬀects [25]. To gain a better idea of how stress inﬂuences MBN, a closer look at magnetic domains under the inﬂuence of stress is necessary. 2.3.2 Magnetic Domains Respond to Stress An applied stress, just like an applied magnetic ﬁeld, destroys the balance of the ﬁve energies. They have to readjust to minimize their sum [20]. If no external ﬁeld is acting, the magnetostatic energy is zero. On the other hand, the magnetocrystalline and magnetoelastic energy are the dominant players [9, 15]. Under stress, both magnetocrystalline and magnetoelastic energy compete to determine the direction of the domain magnetization. Nevertheless, stresses in excess of 1,700 MPa are needed to counterbalance the eﬀect of the magnetocrystalline energy, and change the direction of domain magnetization [26]. Therefore, the domain magnetization remains parallel to the crystallographic easy axis of the material, even under an applied stress. Since realignment of magnetization with stress is not easily attained, the domain conﬁguration minimizes its energy through movement of domain boundaries. A new energy conﬁguration is achieved when domains lying closest to the direction of applied uniaxial tensile stress grow at the expense of domains with perpendicular domain magnetization. In contrast, under a compressive stress the domains with magnetic moments perpendicular to the axis of applied stress become energetically favorable [21]. In this manner, the magnetoelastic energy is decreased [15, 26].

2.3 Stress Eﬀects

25

There is another mechanism through which magnetic domains respond to an applied stress. In general under stress, there is an increase in the 180◦ domain wall population in the stress direction if the stress is tensile, with an opposite eﬀect for compressive stress. Since MBN is associated with the pinning of magnetic domain walls, a higher signal is obtained along the direction of tensile stress, and a lower for compressive stress [27]. 2.3.3 Magnetic Anisotropy and MBN Magnetic properties of a material depend on the direction in which they are measured, and this phenomenon is known as magnetic anisotropy [3]. Only the magnetocrystalline anisotropy which is directly related to crystal symmetry is an intrinsic property of the material, while all other magnetic anisotropies are induced [15]. Quite often, design of commercial ferromagnetic materials is dependent on their magnetic anisotropy [23]. MBN is a suitable technique for detecting magnetic anisotropy in a ferromagnetic material, without regard to its origin. An MBN signal is detected at particular angles with respect to the specimen’s axis, and after mathematical modeling it is plotted on a polar graph. The shape of the graph reveals the direction of the magnetic easy axis or magnetic anisotropy, because the MBN signal is large in that particular direction, as will be seen in subsequent sections. 2.3.4 Some Parameters Used in MBN Analysis When modeling the MBN signal, two contributions are taken into account (1) that from domains responsible for an easy axis, also known as α and (2) a contribution from isotropically oriented domains represented by β [28]. The two contributions α and β are incorporated as ﬁtting parameters into a mathematical expression describing a so-called MBNenergy MBNenergy = α cos2 (θ − φ) + β,

(2.2)

where θ is the angle at which a magnetic ﬁeld is applied, and ϕ is the easy axis direction [28]. The parameter α is obtained by subtracting β from the maximum “MBNenergy ,” due to β being a minimum in MBNenergy . α represents contributions from domains responsible for a magnetic easy axis, whereas β takes into account contributions from isotropically oriented domains [20]. The signiﬁcance of the MBNenergy is related to the change in magnetic ﬂux under the inﬂuence of the magnetic ﬁeld component parallel to a particular domain wall [20]. The latter will move if its coercivity is overcome by the ﬁeld component parallel to the wall [28]. MBN measurements are taken at 10◦ intervals covering the entire 360◦ circle of an angular scan. The angle is with respect to the sweep ﬁeld direction of the MBN sensor [20]. Equation (2.2) is ﬁt to the measured MBN data, while

26

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique direction of applied load 200 150 100 50 MBNenergy (mV2s)

200

150

100

50

0 0

50

100 150

200

50 100 150 200 0.03% 0%

Fig. 2.7. Typical MBNenergy polar plot revealing a magnetic easy axis (or magnetic anisotropy) under the inﬂuence of an applied uniaxial tensile load. The plot is elongated in the direction of magnetic anisotropy which in the case of the 0.03% deformation is also the direction of the applied uniaxial tensile stress. The plot at 0% deformation is not a perfect circle, indicating that a magnetic anisotropy is present in the as is material due to prior processing which resulted in trapped residual stresses. The magnetic anisotropy of the as is material is in a direction diﬀerent from the one along which the load will be subsequently applied (reprinted from [41])

the resulting calculated MBNenergy is plotted on a polar graph. Figure 2.7 shows a typical polar graph for the MBNenergy when magnetic anisotropy is present. In the absence of magnetic anisotropy, the MBNenergy plot is a perfect circle. If magnetic anisotropy is present such as for instance due to an applied uniaxial tensile load, the circle is elongated in the direction of the magnetic anisotropy which is also the direction of the uniaxial tensile load, transforming the plot from a circle into an ellipse [20]. Apart from MBNenergy , another parameter termed pulse height distribution is also used to characterize the MBN signal [20]. This is because the MBN signal consists of a collection of voltage pulses or “events” of varying amplitude that carry information about the magnetic state of the material. Usually, only voltage pulses above and below a certain threshold are considered in order to maintain integrity of the analysis. A positive slope between two consecutive measurements crossing the positive voltage threshold deﬁnes the onset of an event, while a similar positive slope crossing the negative voltage threshold the end of it.

2.3 Stress Eﬀects

27

The occurrence of events of diﬀerent amplitude is represented in a graph termed a pulse height distribution where the absolute values of the event amplitudes are examined by height [20]. Actually, the MBNenergy is obtained by calculating for each event the area between the time axis and the squared voltage pulse, and summing over all measured events. 2.3.5 Elastic Stress Inﬂuences on Magnetic Anisotropy Angular MBN scans are very sensitive to stress-induced changes; therefore, they are a good indicator of the stress condition present in a ferromagnetic material at the time of the investigation. A large number of studies have conclusively demonstrated a high magnetic response in steel to applied elastic tensile or compressive stress, with an easy axis development along the direction of the tensile (Table 2.1a), and away from the compressive stress direction [27, 29–33]. Domain magnetization vectors are aligned with [100] crystallographic directions closest to the direction of principal stress [20]. An applied elastic tensile stress increases MBNenergy while creating a strong magnetic easy axis in the stress direction. The magnetic easy axis develops further with increased elastic stress, sometimes modifying its orientation while keeping up with directional variations in stress. Conversely, an applied compressive elastic stress decreases the MBNenergy in the compression direction [34], and creates a magnetic easy axis perpendicular to applied stress [29]. A magnetic easy axis becomes even more pronounced with plastic deformation, while MBNenergy values experience only a slight variation in the plastic regime, as opposed to the large increases observed during elastic deformation [25]. 2.3.6 Plastic Deformation and Magnetic Anisotropy A notable fact is that the magnetic easy axis continues to be present and become further pronounced in the plastic range of deformation [25] (Table 2.1c, e). Additionally, complex stress distributions left behind after mechanical processing such as cold rolling can also be characterized using MBN measured at diﬀerent stages of rolling [20,35] (Table 2.1b, d, f). Table 2.1 gives an overview of what can be detected using MBN, simultaneously showing some of the inﬂuence of elastic and plastic deformation on magnetic domains. The latter are best represented by changes in pulse height distributions, especially noticeable along directions of maximum shearing stress [20] (Table 2.1c, left). Plastic deformation distorts the crystalline lattice permanently by slipping when the critical-resolved shear stress is reached on a slip plane. Between slipped and unslipped portions dislocations form that alter the interplanar spacing, creating strain ﬁelds and thereby volume changes in magnetic domains. While dislocation strain ﬁelds contribute to the redistribution of strain within a grain, they also alter the magnetic texture of the material.

28

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

Table 2.1. Elastic vs. plastic deformation eﬀects on MBNenergy , pulse height distribution, as well as magnetic domains (a) A magnetic easy axis develops under an elastic stress, becoming more pronounced in (c) and (e) under plastic deformation. Changes in pulse height distribution become apparent in (c, left) at an angle of 45◦ with respect to the principal stress, along the direction of maximum shearing stress. Cold rolling reveals a complex stress distribution in (b), (d), and (f) [35]

Therefore, it is no surprise that plastic stress-induced eﬀects are reﬂected in the measured MBN signal which depends so strongly on changes in magnetic domain conﬁguration [25]. While elastic strain has been noticed to signiﬁcantly alter the magnetic anisotropy α in the specimen, it has little inﬂuence on the isotropic background signal β. On the other hand, plastic deformation has the opposite eﬀect, in as much as it changes β, but leaves α almost unaltered [25]. 2.3.7 Eﬀects of Residual Stresses When using angular MBN scans to characterize samples that have reached the plastic regime and have been unloaded, it is noticed that the easy axis becomes less pronounced, nevertheless is still present [35]. Furthermore, interestingly the curve described by (2.2) does not ﬁt experimental data. Higher

2.3 Stress Eﬀects

29

MBNenergy values are revealed in both axial and transverse directions to the previously applied tension, indicative of residual stresses trapped by plastic strains [20]. Residual stresses in welded T-section samples of SAE 1020 steel have been successfully detected in the past [13]. Signiﬁcant increases in MBN signal have been observed in areas surrounding the weld before the sample underwent stress relief treatment. The latter involves annealing, a process known to reduce magnetoelastic energy [36]. Residual stresses are elastic in nature; however, they can be surrounded by nonuniform microstructural changes in the specimen [16]. This is because grains within a polycrystalline sample deform diﬀerently depending on their crystallographic orientation with respect to the direction of applied stress. While deforming, grains can lock in elastic intergranular stresses [37], and their inﬂuence is visible in the MBN signal [13, 25]. Figure 2.8 shows a correlation

200 Residual stress (MPa) 100

−2

−1

0 0

1

2

−100

(a)

−200 2

Relative peak height

1 Peak A

(b) −2

Peak B −1

0 0

1

2

n M / MY

Fig. 2.8. Residual stress and relative MBN peak height in the unloaded state, correlated with the moment applied prior to unloading. (a) Residual stress determined by X-ray diﬀraction; (b) Normalized peak height from MBN proﬁle. M/MY is the ratio between the maximum moment applied to a specimen before unloading, and the moment at which the stress reaches the yield point at the outer surface, while n is the sign of stress on the surface (positive for tension, and negative for compression) (reprinted from [16] (copyright 2004) with permission from Elsevier)

30

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

between residual stresses detected using X-ray diﬀraction and MBN peak height in unloaded specimens [16]. The same pattern is observed for both residual stresses and MBN peak height, proving that the two correlate very well. 2.3.8 Inﬂuence of Dislocations Elastic stresses between grains adjust while dislocations appear in grain boundary regions [38], reducing stress concentration. Dislocations start to form even before the macroscopic elastic limit has been reached [39, 40]. The eﬀect that dislocations have on the magnetic domain conﬁguration can be witnessed through the abrupt and complex changes in MBNenergy as well as pulse height distribution, changes characteristic of early stages of plastic deformation termed microyielding [40, 41]. The latter occurs as dislocation formation is initiated in some grains, while others remain intact [40]. The created strain ﬁelds result in increases in magnetic domains located in grain boundary regions. Their MBN signal is likely to be greater than the one of smaller size domains in the grain interior. A certain MBN response is obtained, dependent on how many grains develop dislocations. Not all grains undergo plastic deformation at the same time or at the same stress level. This is because of their diﬀerent orientation with respect to the direction of applied stress. As deformation progresses reaching the plastic stress regime, massive dislocations are generated forming dislocation tangles as they move through the lattice. Also, more strain ﬁelds appear inside grains, as the bulk of the grain becomes aﬀected by stress. New stress distributions emerge leaving their imprint on the MBN signal. 2.3.9 Selective Wall Energy Increases at Pinning Sites Unequal size increases between magnetic domains, evidenced in the plastic stress regime, result in diﬀerences in the energetic level of domains. Furthermore, with enhanced dislocation density extending to more and more grains, domain wall energy gradient increases selectively at pinning sites [25]. Although single dislocations are too small to pin domain walls, dislocation tangles are believed to act as pinning sites to domain wall movement [42]. Figure 2.9 shows a possible domain wall energy redistribution at local pinning sites where walls experience a Barkhausen jump. When stress enters the plastic regime, some sites experience a signiﬁcant energy increase, while simultaneously leaving other sites unchanged. Therefore, the Barkhausen transition is expected to occur from one high energy site to an even higher energy site, skipping sites with lower energy. Previous studies show that these unusual transitions are revealed in the detected MBN signal, in particular the pulse height distributions [20, 25].

2.3 Stress Eﬀects

31

domain wall jump without stress domain wall jump with plastic stress

domain wall energy

3 2 1

0

x0x1

x2

x3

x wall position

Fig. 2.9. Domain wall energy distribution at pinning sites with and without the inﬂuence of plastic stress. Dashed lines indicate changes that occur because of plastic stress, such as nonuniform increases in domain wall energy at some pinning sites and domain wall jumps that skip lower energy sites

2.3.10 Roll Magnetic Anisotropy Variations in magnetic anisotropy are not only due to residual stresses or dislocations that alter magnetic domain conﬁguration but also due to other factors such as crystallographic texture and various microstructural inhomogeneities [35,43]. These leave their imprint on MBN signals because they, too, determine domain wall dynamics. MBN pulse height distributions are particularly indicative of such inﬂuences, as there are visible diﬀerences in their occurrence at various stages of plastic deformation. For instance, in the case of some typical nuclear reactor pressure vessel steel specimens subjected to varying levels of cold rolling, it was noticed that along the rolling direction the number of large MBN voltage pulses has diminished at reduction ratios of ∼25%, increasing again at ∼60% reduction ratios [35]. These pulse height distribution observations correlate well with the detected variations in the magnetic anisotropy of the nuclear reactor pressure vessel steel specimens, as the preexisting anisotropy direction was destroyed at ∼25% reduction ratio, increasing again and aligning with the rolling direction while deformation progressed to ∼60% reduction ratio [35]. It is known that a {100}(110) texture develops in severely deformed steel, detectable after 20–30% deformation [44], therefore crystallographic texture development is one of the reasons magnetic anisotropy experiences changes. However, there is signiﬁcant scatter about the “ideal” texture until higher levels of deformation (80–90%) are reached when texture formation is complete [44]. Nevertheless, texture cannot be the only factor responsible for roll induced changes in magnetic anisotropy, at least judging by the direction of the

32

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

latter displayed at diﬀerent deformation levels. Stress levels are so high that inhomogeneous deformation is unavoidable, as internal elastic stresses become trapped in some parts of the material. These residual stresses, whether axially compressive due to the rolling process, or built up at grain boundaries or between crystallographic planes, bring their own contribution to the magnetic anisotropy of the cold rolled specimens. The type of anisotropy described above is attributed to the cold rolling process itself, and has therefore been termed roll magnetic anisotropy [43,45,46]. It is believed to be due to complex metallurgical changes resulting in competing eﬀects between crystallographic texture, as well as anisotropic microscopic and macroscopic residual stresses. In some cases, such as for nickel–cobalt alloys, a roll magnetic anisotropy has been observed along two directions, rather than a single one [46]. 2.3.11 Limits in MBN Signal Increase with Plastic Stress An applied stress that acts simultaneously on grains with diﬀerent crystallographic orientations leads to longitudinal or shear incompatibility at grain boundaries [47]. The relative orientation of grains with respect to each other determines the type of incompatibility. Crystallographic orientations such as [100] and [111] experience longitudinal incompatibility [48], which means that one grain is in tension, while its neighbor is in compression. The stress at grain boundaries induced by longitudinal incompatibility is almost three times higher than the critical-resolved shear stress within a grain [49]. Therefore, dislocations are more likely generated at grain boundaries before they can form in the interior of the grain. Also, the interplanar spacing is altered in the vicinity of the actual dislocation, giving rise to what is termed strain ﬁeld of the dislocation [47]. The formation of these dislocation induced strain ﬁelds results in local variations in interplanar distance along a certain crystallographic direction within a grain. Nevertheless, these can only accommodate so much elastic strain before slip systems are activated and plastic ﬂow initiates, leading to work hardening. The latter will increase slightly the threshold for plastic ﬂow, allowing some elastic strain to continue to build up, but this build up will eventually reach its limits. Mughrabi [50] advanced the idea of hard mechanical regions consisting of dislocation tangles in and near grain boundaries, surrounded by a softer matrix. The hard regions are built of small volumes assumed to be under tensile stress, while separated by larger volumes (soft regions) under compressive stress [50]. Thus, plastic deformation introduces permanent lattice distortion with different consequences for each particular domain conﬁguration. Irregular stress distributions aﬀect the volume of magnetic domains, especially for those in grain boundary regions that experience increases in volume before their neighbors in the grain interior. But every magnetic domain size modiﬁcation implies wall movement, hence variations in MBN signal. Nevertheless, these

2.4 Eﬀects of Microstructure on MBN

33

volume changes can only extend so far, as the resulting additional strain ﬁelds attributed to massive plastic deformation will ultimately put restrictions in domain size increase, as well as impede the simultaneous motion of domain walls. These limitations lead to a slow down in MBN signal increase, fact evidenced in measurements performed at very high levels of deformation that show only a small rise in signal [41]. Some authors consider this eﬀect a “magnetic degradation” [51, 52].

2.4 Eﬀects of Microstructure on MBN 2.4.1 Variations in Grain Size Bertotti et al. [53] investigated the eﬀect of grain size on MBN, observing that the boundaries of grains are likely sources for domain wall pinning. Ng et al. [54] conﬁrmed that a large number of grain boundaries result in more intense Barkhausen noise emissions. The large number of boundaries is found in samples with smaller grains that have been annealed at lower temperatures. Small grain samples have larger MBN signals because the boundaries act as pinning sites, and since their fractional volume is larger, more pinning sites need to be overcome when the walls move. Krause et al. [27] suggested that the number of 180◦ domain walls increases in the presence of applied tensile stress, and derived an expression for the change in magnetoelastic energy under these circumstances. From this expression, they calculated a threshold stress that would be necessary to add another domain wall to the conﬁguration. This threshold stress depends on the grain size and it increases with the number of existing domain walls. Hence, MBN activity is strongly linked to grain size and grain boundaries. Ng et al. [54] advanced the idea that the interaction between the domain walls and dislocation tangles leads to diﬀerent MBN proﬁles than the interaction between the walls and grain boundaries. They used this argument to explain secondary peaks observed in some of the MBN signals. This is because the physical nature of the pin is assumed to dictate the restoring force acting on the wall. Grain size inﬂuences the number of defects in the specimen and hence its magnetic properties [55]. Ranjan et al. [56] substantiated these ﬁndings by showing that the number of MBN pulses varies inversely with grain size in annealed nickel. Large number of pulses means smaller grains, therefore more pinning sites, and possibly more defects. Gatelier-Rothea et al. [57] reported a decrease in MBN signal when the grain size in iron samples increased. That grain size is inversely proportional to the detected MBN signal was also noticed by Tiito et al. [58] who investigated the magnetic behavior of steel specimens of varying grain size. However, precipitates and segregation of phosphorus at grain boundaries can act as additional pinning sites for domain walls, increasing the number of MBN pulses even in large grained specimens, as observed experimentally in decarburized steel [56].

34

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

2.4.2 Compositional and Phase Inﬂuences Compositional variations can bring their own contribution to signals, rendering the MBN analysis more complicated. Plain carbon steels were studied by Kameda et al. [59], who found that variations in MBN signal are obtained because of phase changes such as carbide precipitation or intergranular impurity segregation left behind after heat treatment. Jiles [60] investigated plain carbon steels of the AISI 10xx series, documenting how MBN changes with carbon content due to increased pinning of domain walls by carbide particles. When the latter built networks of lamella carbide, they provided stronger pinning, as opposed to the spheroidized carbides that impeded less the movement of domain walls. Heat treatment of carbon steel AISI 4130 produces pearlite, bainite, and martensite, each with its distinct MBN signature [60]. Blaow et al. [61] compared MBN signal proﬁles in cementite, pearlite, and martensite specimens with and without compressive strain. When the specimens were undeformed, MBN signals were more pronounced in the magnetically soft spheroidized cementite, however reduced in pearlite or the magnetically hard martensite specimen tempered at 400◦ C. The latter also displayed multiple MBN peaks with strain, whereas pearlite and a martensite specimen tempered at 180◦ C showed only a single peak. However, that peak increased systematically with strain. It should be noted that the MBN parameters employed in these studies are quite diﬀerent from the ones described above in earlier sections. Instead, magnetization curves were recorded, and it is on these curves that one or more peaks were noticed. The most signiﬁcant change with strain in MBN signal proﬁles in the Blaow et al. [61] study was observed in the spheroidized cementite specimens. A single peak in the undeformed state was followed by peak broadening with three overlapping peaks. It is assumed that cementite lamellas provide strong directional pinning to domain wall motion, as previous reports indicate [62,63]. All MBN signal changes were reversible when loads were removed while still in the elastic stage of deformation [61]. 2.4.3 MBN Behavior in Diﬀerent Materials Three peak MBN proﬁles were also observed in the magnetization curves of unstrained mild steel [64] and were attributed to spike (or residual) domains. These are usually nucleated and annihilated in the knee region of the hysteresis loop, but some are retained in the specimen upon saturation. Because some spike domains are retained, reversal of the ﬁeld causes abrupt nucleation of new domains when the knee region is reached again [64]. Around saturation, the incomplete annihilation of these spike domains causes some MBN activity, as Ng et al. [54] pointed out when they observed a second peak at higher ﬁelds in the magnetization curve of low carbon steel. Buttle et al. [65] investigated the magnetization of quite diﬀerent material types and observed a single peak in a cold-worked Ni sample, however noticed

2.4 Eﬀects of Microstructure on MBN

35

a three peak MBN proﬁle in an Fe sample. Interestingly, Thompson et al. [66] and Lo et al. [67] reported double peak MBN signals in ferritic–pearlitic steel with higher volume fraction. A second peak in the MBN signal was also noticed by Kleber et al. [68] who applied a compressive elastic and later plastic stress to mild steel as well as Armco iron specimens. Nevertheless, Armco iron displayed diﬀerent MBN behavior than mild steel. In the experiment of Kleber et al. [68] an increase in MBN signal was detected with tensile as well as compressive plastic stress in Armco iron specimens [68]. The magnetic behavior seen in Armco iron was ascribed to dislocation tangles and their interaction with magnetic domain walls [68]. On the other hand, mild steel displayed a decrease in MBN with tensile plastic stress, and almost no change in compression, contrary to earlier reports by other groups [25]. Kleber et al. [68] concluded that residual internal stresses play a diﬀerent role in inﬂuencing MBN behavior in tensile vs. compressive deformation in mild steel. By this argument, they attributed the changes in MBN observed in the mild steel specimens to residual stresses. In contrast, dislocation eﬀects on MBN were assumed to be independent of the sign of plastic strain. Nevertheless, the overall objective of the Kleber et al. study [68] was to separate the eﬀect of dislocations from that of residual internal stresses in the plastic regime, hence two materials with diﬀerent yield strengths were chosen. A somewhat related goal was targeted by Moorthy et al. [69] in their work on the eﬀects of fatigue and overstressing on the MBN response of casecarburized En36 steel. Given the type of steel and its mechanical processing, these specimens had a sharp change in microhardness with depth level, so that a crack initiated at the surface propagated very fast into the material. Furthermore, dislocations had a small chance to form prior to crack formation, as smaller stress levels did not allow dislocation initiation, while crack formation preceded larger stresses necessary for developing dislocations. Of course, the magnetic behavior was observed to also vary under these circumstances. In Moorthy et al.’s study [69], MBN peak height increased in the vicinity of the crack, hence this technique was able to detect the crack location. Nevertheless, crack growth represented only a small fraction in the fatigue life of the case-carburized steel, with specimens failing soon after crack initiation. On the other hand, detection of residual stresses proved to be a more useful indicator of impending failure, since the MBN technique was able to better assess the maximum level of bending stress prior to crack initiation. Alerting users before cracks have a chance to form is deﬁnitely a more favorable alternative to ﬁnding out that the component is about to fail as soon as a crack is detected [69]. The MBN response of nonoriented (3 wt.%) Si–Fe was investigated by V.E. Iordache et al. [70] who subjected the steel specimens to uniaxial tensile stress beyond the macroscopic elastic limit, unloaded the specimens, and performed MBN measurements again during a second reloading. The study allowed a comparison of the diﬀerent aspects of tensile deformation, from elastic strain

36

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

EBN (mV2s)

500

450

e P = 1.75% e P = 6% e P = 11.6%

400

0

100 200 300 400 500 Reloaded stress 0 reload (MPa)

Fig. 2.10. Barkhausen noise energy vs. reloaded stresses (open marks) compared with values under initial applied stress (full marks) for three nonoriented (3 wt.%) Si–Fe specimens (reprinted from [51] (copyright 2003) with permission from Elsevier)

to microyielding, plastic yielding, and strain hardening. The measurements performed in situ during reloading (Fig. 2.10) revealed some similarities to previous studies of the magnetic behavior of steel, even though the latter were not performed after loading for a second time [20,25]. It should be noted that loading, unloading, and reloading again increases MBN values measured at the same level of stress as during the ﬁrst loading [71].

2.5 Competitiveness of MBN in Nondestructive Evaluation 2.5.1 Usefulness of MBN for MFL MFL is an eﬀective inspection method for evaluating corrosion and defect impact on pipelines while they are still in service [72]. It is based on inducing a magnetic ﬂux into the walls of a pipeline, using strong permanent magnets. The ﬂux will “leak out” if metal loss exists, such as when the walls contain defects. A Hall sensor detects the leaking ﬂux that depends on defect geometry, as well as any associated stresses [73]. Given the complexity of the factors inﬂuencing the MFL signal, MBN can be of assistance in giving a correct interpretation, provided results from both techniques are compared to establish a common pattern under similar circumstances [73]. Quite often, simulation tools relying on ﬁnite element analysis have been employed to model magnetic ﬂux patterns around corrosion defects [74]. Results from MFL studies [73] indicate that ﬂux signals around the defect, in particular dents, are sensitive to elastic residual stresses, but not to plastic deformation. This is in agreement with MBN studies on elastic vs. plastic

2.5 Competitiveness of MBN in Nondestructive Evaluation

37

Bz (T)

40

0.018 0.017

y (mm)

30

0.016 0.012

20

0.008 0

0.004

0

0

0

10

20 x (mm)

0.016

0.008

0

- 0.004

0.008

10

- 0.008 - 0.012

30

40

Fig. 2.11. Simulated MFL contour maps obtained 0.5 mm underneath a dented steel plate. The maps show the combined eﬀect of dent geometry and stresses (reprinted from [75] (copyright 2005) with permission from Elsevier)

deformation eﬀects, which also indicate that elastic stress has a more pronounced inﬂuence on magnetic behavior than plastic stress [20, 25]. A recent MFL study [73] revealed that the radial signal is most determined by compressive stress conﬁgurations perpendicular to the ﬂux path, lowering steel permeability and forcing ﬂux out of the pipe [73]. Figure 2.11 shows the simulated magnetic ﬁeld contour maps on the bottom side of a steel plate containing a dent, illustrating the eﬀect of both dent geometry and stress conﬁgurations on the MFL signal. It seems that geometry is the dominant factor, and not stress distributions around the dent, except for a very pronounced peak in the lower part of the ﬁgure. The peak is attributed to stress and correlates well with previous ﬁndings of MBN studies [20, 25, 75]. The MFL simulation results [73] were correlated with experimental magnetic ﬂux patterns determined using the MFL technique. Specimens were subjected to a residual stress removal treatment before a dent was applied, to ensure that only stress conﬁgurations associated with the dent itself were present. Experimental results matched very closely those obtained by simulation [73]. The knowledge gained through prior MBN studies on stress conﬁgurations and magnetic behavior assisted in obtaining a more complete interpretation of MFL signals [73]. 2.5.2 Need for Calibration of MBN as NDT The main advantage of magnetic Barkhausen noise as a nondestructive technique is that it reveals complex changes in materials structure that originate in microstructural properties, as well as stress conﬁgurations, together

38

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique

leaving their imprint on the material. How the latter responds depends on multiple factors, each with a speciﬁc inﬂuence on magnetic behavior. Nevertheless, these factors are diﬃcult to dissociate and treat individually, requiring an experienced user to give the appropriate interpretation to the measured MBN data. For instance, magnetic domains of neighboring grains of the same crystallographic orientation could become simultaneously active. In this case, an enhanced MBN signal is likely to be obtained, however this large signal may not be entirely because of crystallographic texture. Furthermore, reorientation of grains that can occur with plastic deformation is likely to cause redistribution of internal stresses, potentially destroying the eﬀects of other factors such as residual stresses. Fortunately, crystallographic reorientation only happens at high deformation levels, usually associated with mechanical processing [44]. User knowledge and experience are extremely important in MBN data analysis. Nevertheless, because MBN depends on so many inﬂuential variables, it is still necessary to resort to comparative studies, and ultimately calibrate measurements. An undeformed specimen or a known microstructural state needs to act as a standard for a particular type of alloy. In spite of commonalities, one should not directly compare MBN results for diﬀerent types of plain carbon steels. Their prior magnetic history, processing treatment and ultimately type of steel will determine their MBN response.

References 1. R.M. Bozorth, Ferromagnetism (IEEE Press, New York, 1951) 2. W.A. Theiner, H.H. Williams, Determination of Microstructural Parameters by Magnetic and Ultrasonic Quantitative NDE, in Nondestructive Methods Material Property Determination (Plenum Press, New York, 1984), p. 249 3. S. Chikazumi, Physics of Magnetism (Wiley, New York, 1964) 4. V.N. Shah, P.E. MacDonald, Residual Life Assessment of Major Light Water Reactor Components, vol. 1 (Idaho National Engineering Laboratory, Seattle, 1987), p. 144 5. S. Nath, B. Wincheski, J.P. Fulton, M. Namkung, IEEE Trans. Magn. 30(6), 4644 (1994) 6. R.A. Wincheski, M. Namkung, Aerospace Am. 36(3), 27 (1998) 7. B. Wincheski, J.P. Fulton, S. Nath, M. Namkung, J.W. Simpson, Mat. Eval. 52(1), 22 (1994) 8. V. Babbar, B. Shiari, L. Clapham, IEEE Trans. Mag. 40(1), 43 (2004) 9. R. Becker, W. D¨ oring, Ferromagnetismus (Springer Verlag, Berlin, 1939) 10. H. Barkhausen, Physik. Z. 20, 401 (1919) 11. A.E. Lord, in Acoustic Emission, ed. by W.P. Mason, R.N. Thurston. Physics Acoustics, vol. 9 (Academic Press, New York, 1975) 12. M. Namkung, S.G. Allison, J.S. Heyman, IEEE Trans. Ultrasonics Ferroelectrics Freq. Control 33(1), 108 (1986) 13. K. Tiito, in Nondestructive Evaluation: Application to Materials Processing, ed. by O. Buck, S.M. Wolf (ASM, Materials Park, Ohio, 1984), p. 161

References

39

14. X. Kleber, A. Vincent, NDT&E Int. 37, 439 (2004) 15. B.D. Cullity, Introduction to Magnetic Materials, 2nd edn. (Addison-Wesley, New York, 1972) 16. M. Blaow, J.T. Evans, B. Shaw, Mater. Sci. Eng. A386, 74 (2004) 17. D.C. Jiles, Introduction to Magnetism and Magnetic Materials (Chapman and Hall, New York, 1991) 18. J.C. McClure, Jr., K. Schr¨ oder, CRC Crit. Rev. Solid State Sci. 6, 45 (1976) 19. W. Heisenberg, Z. Physik 49, 619 (1928) 20. C-G. Stefanita, Ph.D. Thesis, Department of Physics, Queen’s University, Kingston, Ontario, Canada, 1999 21. D. Utrata, M. Namkung, Rev. Progr. Quant. Nondestr. Eval. 2, 1585 (1987) 22. R.S. Tebble, Proc. Phys. Soc. Lond. B 68, 1017 (1955) 23. J-K. Yi, Nondestructive Evaluation of Degraded Structural Materials by Micromagnetic Technique, Ph.D. Thesis, Department of Nuclear Engineering, Korea Advanced Institute of Science and Technology, Taejon, Korea (1993) 24. H. Kwun, G.I. Burkhardt, Electromagnetic Techniques for Residual Stress Measurement, 9th edn. Metals Handbook, vol. 17 (ASM International, Materials Park, 1989), p. 159 25. C-G. Stefanita, D.L. Atherton, L. Clapham, Acta Mater. 48, 3545 (2000) 26. C. Kittel, J.K. Galt, Solid State Phys. 3, 437 (1956) 27. T.W. Krause, L. Clapham, A. Pattantyus, D.L. Atherton, J. Appl. Phys. 79(8), 4242 (1996) 28. T.W. Krause, L. Clapham, D.L. Atherton, J. Appl. Phys. 75(12), 7983 (1994) 29. C. Jagadish, L. Clapham, D.L. Atherton, IEEE Trans. Magn. 25(5), 3452 (1989) 30. C. Jagadish, L. Clapham, D.L. Atherton, NDT Int. 22(5), 297 (1989) 31. C. Jagadish, L. Clapham, D.L. Atherton, J. Phys. D: Appl. Phys. 23, 443 (1990) 32. C. Jagadish, L. Clapham, D.L. Atherton, IEEE Trans. Magn. 26(1), 262 (1990) 33. T.W. Krause, K. Mandal, C. Hauge, P. Weyman, B. Sijgers, D.L. Atherton, J. Magn. Magn. Mater. 169, 207 (1997) 34. H. Kwun, G.L. Burkhardt, NDT Int. 20, 167 (1987) 35. C.-G. Stefanita, L. Clapham, J.-K. Yi, D.L. Atherton, J. Mater. Sci. 36, 2795 (2001) 36. R.L. Pasley, Mater. Eval. 28, 157 (1970) 37. L.E. Murr, Met. Trans. 6A, 427 (1975) 38. K. Tangri, T. Malis, Surface Sci. 31, 101 (1972) 39. R.M. Douthwaite, T. Evans, Acta Met. 21, 525 (1973) 40. V. Moorthy, S. Vaidyanathan, T. Jayakumar, B. Raj, B.P. Kashyap, Acta Mater. 47, 1869 (1999) 41. C.-G. Stefanita, L. Clapham, D.L. Atherton, J. Mater. Sci. 35, 2675 (2000) 42. A.J. Birkett, W.D. Corner, B.K. Tanner, S.M. Thompson, J. Phys. D: Appl. Phys. 22, 1240 (1989) 43. W. Six, J.I. Snoek, W.G. Burgers, De Ingenier 49E, 195 (1934) 44. G.E. Dieter, Mechanical Metallurgy (McGraw Hill, New York, 1961) 45. S. Chikazumi, K. Suzuki, H. Iwata, J. Phys. Soc. Jpn. 15(2), 250 (1960) 46. N. Tamagawa, Y. Nakagawa, S. Chikazumi, J. Phys. Soc. Jpn. 17(8), 1256 (1962) 47. J.P. Hirth, Met. Trans. 3, 3047 (1972) 48. M.A. Meyers, K.K. Chawla, Mechanical Metallurgy: Principles and Applications (Prentice Hall, New Jersey, 1984) 49. M.A. Meyers, E. Ashworth, Phil. Mag. A 46(5), 737 (1982)

40 50. 51. 52. 53. 54. 55. 56. 57. 58. 59. 60. 61. 62. 63. 64. 65. 66. 67. 68. 69. 70. 71. 72. 73. 74. 75.

2 Barkhausen Noise as a Magnetic Nondestructive Testing Technique H. Mughrabi, Acta Metall. Mater. 31, 1367 (1983) V.E. Iordache, E. Hug, N. Buiron, Mater. Sci. Eng. A359, 62 (2003) K. Kashiwaya, Jpn. J. Appl. Phys. 31, 237 (1992) G. Bertotti, F. Fiorillo, A. Montorsi, J. Appl. Phys. 67(9), 5574 (1990) D.H.L. Ng, K.S. Cho, M.L. Wong, S.L.I. Chan, X-Y. Ma, C.C.H. Lo, Mat. Sci. Eng. A358, 186 (2003) H. Sakamoto, M. Okada, M. Homma, IEEE Trans. Magn. 23, 2236 (1987) R. Ranjan, D.C. Jiles, O. Buck, R.B. Thompson, J. Appl. Phys. 61(8), 3199 (1987) C. Gatelier-Rothea, J. Chicois, R. Fougeres, P. Fleischmann, Acta Mater. 46, 4873 (1998) S. Tiito, M. Otala, S. S¨ ayn¨ aj¨ akangas, NDT Int. 9, 117 (1976) J. Kameda, R. Ranjan, Acta Metall. 35, 1515 (1987) D.C. Jiles, J. Phys. D 21, 1186 (1988) M. Blaow, J.T. Evans, B.A. Shaw, Acta Mater. 53, 279 (2005) M.G. Hetherington, J.P. Jakubovics, J. Szpunar, B.K. Tanner, Philos. Mag. B 56, 561 (1987) L.J. Dijkstra, C. Wert, Phys. Rev. 79, 979 (1950) D.G. Hwang, H.C. Kim, J. Phys. D: Appl. Phys. 21, 1807 (1988) D.J. Buttle, C.B. Scruby, J.P. Jakubovics, C.A.D. Briggs, Philos. Mag. A 55, 717 (1986) S.M. Thompson, B.K. Tanner, J. Magn. Magn. Mater. 123, 283 (1993) C.C.H. Lo, C.B. Scruby, J. Appl. Phys. 85, 5193 (1999) X. Kleber, A. Vincent, NDT&E Int. 37, 439 (2004) V. Moorthy, B.A. Shaw, P. Hopkins, NDT&E Int. 38, 159 (2005) V.E. Iordache, E. Hug, N. Buiron, Mater. Sci. Eng. A359, 62 (2003) M. Lindgren, T. Lepist¨ o, NDT&E Int. 34, 337 (2001) W. Mao, C. Mandache, L. Clapham, D.L. Atherton, Insight 43(10), 688 (2001) V. Babbar, L. Clapham, J. Nondestr. Eval. 22(4), 117 (2003) N. Ida, W. Lord, IEEE Trans. Magn. 19(5), 2260 (1983) V. Babbar, J. Bryne, L. Clapham, NDT&E Int. 38, 471 (2005)

3 Combined Phenomena in Novel Materials

Summary. This chapter is divided into two parts: magneto-optical media and magnetoelectric materials. The ﬁrst part deals with magnetic recording and optical readout, a branch of magnetism that tends to be under-appreciated, especially nowadays when new developments have entered the recording market. Therefore, the objective is to draw attention to the signiﬁcance of continuous media and its impressive stability. These media are not limited by thermal reversal eﬀects of singledomain particles. However, they encounter their own challenges to high quality recording or accurate optical readout. Even Barkhausen noise can aﬀect the latter in a negative way. In the second part, materials are presented where magnetic properties are intertwined with electric phenomena, creating a unique environment for imaginative applications. Some substances exhibit naturally a unique combination of properties, while others can be engineered to display eﬀects not normally found in individual constituents. The range of applications for metamaterials is expanding every year, including magnetoelectric sensors and transducers, read/write devices, or even microwave dielectrics. Nevertheless, the ongoing problem of how to improve the design of magnetoelectric materials with a strong magnetization–polarization correlation remains, requiring a better understanding of the mechanisms leading to the generation of these eﬀects.

3.1 The Interest in Magneto-optical Media Materials with intermediate values for magnetic anisotropies have traditionally been employed as magnetic recording media. For instance, magnetic tapes made use of ferromagnetic solid solutions such as γ-Fe2 O3 –Fe3 O4 in the form of acicular particles [1]. The uniaxial magnetic anisotropy due to their shape gave them good coercivity [2] which also depended strongly on the ratio of ferrous to ferric ions. Higher coercivity values were obtained when Fe2+ /Fe3+ was greater than 0.04, however the type of binder in which the particles were dispersed (e.g., paraﬃn or epoxy resin) appeared to have a contribution as well [3]. The inﬂuence on the coercivity was seemingly because of the stress

42

3 Combined Phenomena in Novel Materials

applied to the powder particles by the surrounding material, especially when the temperature varied, as there is a diﬀerence in thermal expansion coeﬃcients of the magnetic particles and the binder [4]. 3.1.1 Conventional vs. Continuous Media In conventional magnetic recording, the magnetic grains forming a bit (Fig. 3.1) are separated from each other because of exchange coupling [5] which plays a tremendous role in the properties of the media, and ultimately the recording process. Also, the thermal stability of conventional magnetic recording media depends on the magnetization reversal of single-domain particles under thermal activation [6]. However, the magnetic properties of magneto-optical (MO) media are continuous, so that signiﬁcant diﬀerences exist between magneto-optical and conventional tapes. For MO media, marks are recorded as magnetic domains between which a magnetic wall exists (Fig. 3.2). With an estimated wall width of 8 nm, and a mark width of 170 nm (corresponding to an areal density 100 Gbits in−2 ), the energy barrier for the wall motion is 320 times larger than the thermal activation energy kT , implying that the thermal stability of the magnetic walls in MO media is higher than that of magnetic perpendicular recording media [7]. Nevertheless, it is possible to obtain discrete entities for MO data storage as demonstrated successfully using two versatile techniques: X-ray lithography and ion beam etching [8]. Using these, regular micrometer-sized square lattices of round dots were patterned on Au/Co/Au (111) thin ﬁlms with perpendicular easy magnetization axes. Co layers were sandwiched between a 5 nm thick Au capping layer and a 25 nm thick (111) Au buﬀer layer deposited on a

Fig. 3.1. A sketch of a bit cell formed of single-domain particles separated from each other because of exchange coupling. Bit cells are constituents of conventional recording media domain 1

domain wall

domain 2

Fig. 3.2. In MO media, marks are recorded as magnetic domains between which a domain wall exists. A domain wall denotes a transition layer which separates two adjacent domains in diﬀerent directions

3.1 The Interest in Magneto-optical Media

43

thermally oxidized Si substrate. The magnetic dots were obtained through a mask using X-ray lithography, where the unprotected parts of the ﬁlm were then removed by ion beam etching [9]. The MO Kerr rotation measured on the ﬁlm showed a strong dependence on the direction of light polarization, and the ratio of ﬁlm to background reﬂectance. Single magnetic dots displayed magnetization reversals [10]. 3.1.2 The Basis of Magneto-optical Eﬀects The Faraday eﬀect or Faraday rotation is a MO phenomenon where the plane of polarization of incident light is rotated proportional to the intensity of the component of the magnetic ﬁeld in the direction of the beam of light, as the light passes through a material (Fig. 3.3). The eﬀect is observed in transmission through a medium, mostly in optically transparent dielectric materials. It was discovered by Michael Faraday in 1845 and is an experimental evidence of the interaction between light and a magnetic ﬁeld. The magneto-optic Kerr eﬀect is similar to the Faraday eﬀect, however it describes changes in polarization of light that is reﬂected from a magnetized material. This eﬀect takes its name after John Kerr who reported it in 1875 [11]. 3.1.3 Composite Films Used in Magneto-optical Recording Intermetallic compounds, such as MnBi, were among the ﬁrst materials used for magnetic recording and optical readout by the Faraday–Kerr eﬀect. MnBi has a hexagonal nickel arsenide crystal structure with a very high magnetic anisotropy constant [12]. The direction of easy magnetization is along the c angle of rotation

magnetic field polarization

polarization direction of light propagation material through which light passes

Fig. 3.3. Sketch of the Faraday eﬀect. The plane of polarization of incident light rotates proportionally to the intensity of the magnetic ﬁeld component aligned with the direction of light propagation. The eﬀect is observed in transmission through a medium

44

3 Combined Phenomena in Novel Materials

axis. Initially, the Faraday–Kerr eﬀect was used to study magnetic domains in MnBi ﬁlms [13]. However, once it was noticed that the optical setup can be made such that domains of either polarity appear signiﬁcantly dark, while those of opposite polarity remained noticeably light; the idea of using this high contrast for magnetic recording and optical readout was born. In fact, the ﬁrstreported MO recording was in 1957 [14]. That experiment was based on MnBi magnetic ﬁlms made by vapor depositing on a glass substrate a layer of Mn, followed by a layer of Bi. The composite ﬁlm was baked in successive steps at temperatures above 200◦ C, and sealed oﬀ at a pressure of 1.5 × 10−7 mmHg. Over the next 3 days, the ﬁlm was further baked at temperatures ranging from 225 to 350◦ C. Even though the ﬁlms were not perfectly uniform or continuous, areas of approximately an inch square were crystallographically arranged with the c axis normal to the surface, which was also the bulk uniaxial direction of easy magnetization with a spread of only 15◦ . This detail was particularly important for the optical reading process, as the domain magnetization vectors needed to have components along the direction of propagation of light. Dominant in-plane magnetization vectors would have required oblique illumination. Actually, some previous magnetic domain observation experiments carried out on single crystals of silicon iron and evaporated ﬁlms of NiFe (80% Ni) used oblique illumination [15,16]. If the ﬁlms were thinner and more transparent, magnetic domain observation was made with the transmitted light inclined at an angle of 45◦ to the surface of the ﬁlm [17]. However in the experiment of Williams et al., the fact that the easy axis of magnetization was normal to the surface allowed optical readout to occur by shining polarized light perpendicularly on the ﬁlm. 3.1.4 Magnetic Recording and Optical Readout During optical readout, the light was reﬂected back by the surface of the ﬁlm, and the plane of polarization was rotated either clockwise or counterclockwise depending on the magnetic polarity of the reﬂecting domain areas. By rotating an analyzer, the light from the domains of one polarity was extinguished while the light from those of the opposite polarity was not. This made the former domains appear dark while the latter were light. A Kerr–Faraday rotation of approximately 5◦ was obtained, giving a good visual contrast. For writing on the ﬁlm, an electropolished magnetic probe tip with tapered ends was used as shown in Fig. 3.4. One end of the probe wrote dark, whereas the other end wrote light, depending on which direction was magnetized in the local area. If the analyzer is rotated to the other position of maximum contrast, the light and dark areas are reversed, as shown in Fig. 3.4a, b. 3.1.5 Quality of Magnetic Recording The grey background was due to many ﬁne magnetic domains that appeared either dark or light. They ranged in size from approximately 3,000–6,000 ˚ A,

3.1 The Interest in Magneto-optical Media

45

Fig. 3.4. Magnetic writing on a ﬁlm of MnBi. The numbers 1 and 2 were written with one end of a magnetic probe, and 3 with the other end. Analyzer setting: (a) +5◦ and (b) −5◦ (reprinted from [14] (copyright 1957) with permission from the American Institute of Physics)

and this was also the width of the domain boundaries, revealing a very ﬁne domain structure of adjacent boundaries. It was estimated that 106 bits could be recorded on 1 cm2 of ﬁlm, an assessment based on the above observations, and the width of the ﬁnest line which was 0.001 cm. Nevertheless, the limited capabilities of the read/write equipment would have been an impediment as well. The writing was erased by either saturating or demagnetizing the ﬁlm perpendicular to the surface. Although the Faraday–Kerr angle of rotation was fairly large, this MO recording method using MnBi ﬁlms had the disadvantage of large media noise due to the grain boundaries in the crystallite. In spite of its shortcomings, a better understanding of the MO eﬀect in MnBi was still being sought decades later through theoretical studies of the spin–orbit interaction and exchange splitting of the electronic structure [18]. 3.1.6 Overcoming Noise Problems In the 1970s, other media for MO recording were introduced that displayed drastically reduced noise [19]. Among these, amorphous GdCo ﬁlms [20] were used because they had no grain boundaries. At the same time, it was determined that amorphous rare-earth transition metals [21] are good candidates for erasable and nonvolatile MO disks for which thermomagnetic methods are utilized. However, with the advent of semiconductor lasers as well as improved tracking and focusing servo-techniques, MO disk drives were developed in the 1980s based on amorphous TbFe [22] and GdFeCo as the MO recording medium [23]. By the end of the decade, 130 mm MO disks with a (two side) capacity of 650MB were commercially available. At the beginning of the 1990s, single-sided 90 mm MO disks of 128MB for data recording, and 64 mm rewritable Mini Disks for digital audio recording were put on the market [24].

46

3 Combined Phenomena in Novel Materials

3.1.7 The MO Sony Disk A cross-sectional view of a MO disk produced by Sony in the 1990s is schematically shown in Fig. 3.5. Marks are recorded on land areas tracked using grooves, obtained on a polycarbonate substrate using a Ni stamper [25]. Also on the substrate, the four layers are deposited by sputtering, with TbFeCo constituting the magnetic layer of about 20 nm thickness. Two dielectric layers, typically Si3 N4 , are deposited on either side of the magnetic layer to protect it against corrosion [26]. The choice for TbFeCo is based on its good properties such as reasonably high perpendicular magnetic anisotropy, large coercivity (800 kA m−1 ), low noise, and a moderate Kerr rotation angle. Writing onto the disk is obtained by shining a 10 mW light pulse on a 1 µm diameter area on the magnetic layer, raising the temperature within the light spot by heat absorption. When the raised temperature reaches a critical point (170◦ C for TbFeCo) where the coercivity is equal to an applied magnetic ﬁeld for writing, a mark is recorded while the magnetization within the light spot is redirected upwards [27]. Readout from the disk is done through the MO eﬀect originating in the magnetic layer, by shining a 1.5 mW light, weak enough to raise the temperature only slightly, much lower than the critical temperature for recording [28]. For linearly polarized light, the polarization of the reﬂected light rotates in opposite directions for oppositely directed spins. In conventional detection, these Kerr rotation angles are picked up by a beam splitter that divides them into s-polarized and p-polarized light before entering two detectors. Thus, recorded marks that advance while the disk is rotating are read out by the light beam focused on the media [29]. The limit of this detection method is given by the recording wavelength p of the marks (Fig. 3.6) which needs to be longer than the optical limit λ/(2NA) where λ is the readout light wavelength and NA is the numerical aperture of the objective lens.

Poly-Carbonate Substrate groove land protective layer magnetic layer protective layer

Si3N4 TbFeCo Si3N4

reflective layer

Al

track pitch 1.6 µm

Fig. 3.5. Cross-sectional view of a MO disk from the 1990s (reprinted from [39] (copyright 1994) with permission from the IEEE)

3.1 The Interest in Magneto-optical Media

47

recorded mark

P d

light spot

Fig. 3.6. Limit of conventional detection. Recording wavelength p is greater than the optical limit λ/(2NA). The ﬁrst Airy ring has diameter d (reprinted from [39] (copyright 1994) with permission from the IEEE)

3.1.8 Magnetically Induced Super Resolution To increase the resolution of the optical readout process, the microscope can be equipped with an optical system containing a pinhole smaller than the spot size shining on the object, enabling detection of an object smaller than the limit imposed by conventional detection [30]. However this method, too, has its limitations that can be overcome by having the pinhole produced right in the media. The pinholes are created at the intersection of the readout light spot with a heated area that is produced by a laser (∼10 mW). Thus, a portion of the focused spot is optically masked [31] leaving an eﬀective aperture much smaller than the focused spot. The signal is optically detected within the eﬀective aperture when a magnetic ﬁeld higher than the coercivity of the heated region is applied during readout [32]. The magnetization of the heated region aligns with the ﬁeld, corresponding to erasure [33]. The remaining area apertures the light spot, increasing the resolving power [34] similar to decreasing the light wavelength or increasing the numerical aperture of an objective in conventional detection. This method which expands the readout resolution limit of the MO disk is termed magnetically induced super resolution (MSR) [35]. There are two types of detection by MSR: front aperture detection (FAD) [36] and rear aperture detection (RAD) [37], as shown in Fig. 3.7 [38]. The readout resolution obtained by MSR exceeds the conventional optical limit without the need for a shorter wavelength or a larger numerical aperture of the objective lens [39]. 3.1.9 Nondestructive Optical Readout The increased resolution obtained in the MSR method described above is destructive, as it results in erasing the recorded mark after readout [40]. A nondestructive alternative also developed by Sony was to use an exchange-coupled magnetic triple layer ﬁlm with a readout, switching and recording layer [41].

48

3 Combined Phenomena in Novel Materials aperture area

masked area

masked area

Front Aperture Detection (FAD)

aperture area

Rear Aperture Detection (RAD)

Fig. 3.7. Two types of detection in the MSR method (reprinted from [38] (copyright 1992) with permission from the IEEE)

The readout layer has a low coercivity [42], as opposed to the high coercivity recording layer [43]. When the magnetic layers cool down after the recorded mark in the readout layer is erased by the applied ﬁeld in the heated area, the information is still retained in the recording layer [44]. This information is subsequently copied onto the readout layer due to the exchange coupling between the readout and recording layers [45], enabling recorded marks to be read out several times [46]. Marks with a recording wavelength of 0.76 mm are resolved for a heating power of 2.5 mW, which is called a resolving power [39]. 3.1.10 Double and Multilayer MO Disks A comparative MO recording study also performed in the mid 1990s at Sony involving Pt/Co multilayer [47] and GdFeCo/TbFeCo double-layer [48] disks using a high power green laser revealed better signal to noise ratios and areal densities three times higher than other MO disks available at the time [49]. The shorter wavelength of the green laser (532 nm), as opposed to the previously used 780 nm laser [50], oﬀered promise of increased densities in these MO disks due to higher coercivities and Kerr rotation angles obtainable in these layers. In the past, TbFe with its large coercivity had proved to be a good choice for the writing layer [51], while GdFe displayed a high Kerr rotation angle very suitable for a readout layer [52]. These exchange-coupled magnetic double layers showed improved carrier levels [53], encouraging further exploration and subsequent development of MO disks with slightly diﬀerent element combinations: GdFeCo and TbFeCo. The new ﬁlms had a combined coercivity higher than 10 kOe. The layers were successively deposited by sputtering on photo-polymerized glass substrates [54] while a specially prepared stamper left sharp grooves with a track pitch of 0.9 µm on the substrate. Scanning tunneling microscopy investigations revealed improved surface smoothness and sharper boundaries between lands and grooves leading to reduced disk noise. The thickness of the layers was optimized for the green laser wavelength. Simultaneous investigations were also performed on Pt/Co multilayers successively deposited by sputtering on

3.1 The Interest in Magneto-optical Media

49

the same kind of substrate. The Pt/Co ﬁlms displayed a relatively high Curie temperature of 400◦ C and a lower coercivity (1 kOe). Through layer thickness optimization it was possible to obtain at least as good MO properties in these Pt/Co as in the GdFeCo/TbFeCo ﬁlms. 3.1.11 Domain Wall Displacement Detection An optical readout technique based on domain wall displacement detection (DWDD) [55] also uses a magnetic triple layer ﬁlm embedded in a magnetooptical disk [56] (Fig. 3.8). Its strength lies in the fact that its resolving power is not determined by an optical limit but by the driving force of the wall displacement, the latter being temperature dependent [57]. The magnetic triple layer ﬁlm is exchange coupled so that information recorded on the memory layer is copied onto the displacement layer for readout [58]. However, the exchange coupling is cut oﬀ when the switching layer reaches the critical temperature which is almost its Curie temperature. The magnetic domain wall is displaced to the maximum temperature point when the wall passes through a critical temperature contour, also known as the front line (Fig. 3.8). When the leading edge of the recorded mark passes the front line, a waveform of the signal rises steeply and falls down rapidly as the trailing edge passes the line. The annealed areas on both sides of the track ensure that no side magnetic walls are present [59], a characteristic that is in sharp contrast to the size dependence of magnetic bubble domains whose walls are circumferential [60]. Thus in DWDD, the gradient of the Bloch wall energy, basically independent of domain size, acts as a driving force and is responsible for wall displacement.

Fig. 3.8. Domain wall displacement detection (DWDD) where light is incident from the substrate (not shown); (a) marks recorded by magnetic ﬁeld modulation (top view ); (b) cross-sectional view of the magnetic triple layer ﬁlm. The memory layer is TbFeCo, the switching layer is TbFe, and the displacement layer is GdFe (reprinted from [56] (copyright 1999) with permission from the IEEE)

50

3 Combined Phenomena in Novel Materials

3.1.12 Magnetic Bubble Domains Magnetic bubble domains are generated in certain materials when the coercivity is lowered under the inﬂuence of a laser beam [61]. The coercivity needs to be low compared to the bias ﬁeld which is necessary for the maintenance of the magnetic bubbles that constitute the written bits [62]. However, when no laser light is shining the coercivity needs to be higher than the bias ﬁeld to render the material nonvolatile [63]. Only a few milliwatts of power are necessary for writing on a ﬁlm with low coercivity [64]. In order for the writing to be stable, the bubbles have to nucleate only at the center of the irradiating beam, in the region where the temperature is higher. Thus, bubble formation should be more favorable at higher temperatures because if bubbles were to form in the cooler area of the beam, they would escape the center and writing would become unstable. Materials that satisfy these requirements are Bi containing liquid phase epitaxial garnet ﬁlms that have a high Faraday rotation angle so that a written bit or magnetic bubble can be read out with a high contrast ratio [65]. These days, Bi substituted garnets are still being studied in detail for technological applications of the MO eﬀect, in particular in optical storage devices [66]. Enhanced Faraday rotation angles obtained in these materials are attributed to diﬀerent eﬀects, such as mixing of the 3d Fe3+ orbitals with the 6p Bi3+ orbitals [67], or the large splitting of the excited state induced by the large spin–orbit coupling of the Bi3+ ions [68]. 3.1.13 Generation of a Bubble Bit of Memory A bubble or a bit of memory is generated at a corner of a square formed on the ﬁlm by etching or ion implantation. Another bubble called a “cue bubble” is also generated to move the bit bubble to the opposite corner. This is done by having the cue bubble follow the movement of the light beam. Due to their low coercivity (typically less than 1 Oe), magnetic bubbles move along the temperature gradient to the region heated by the light beam. As the light beam approaches the bit bubble so does the cue bubble. The bit bubble is repelled by the interbubble repulsive force and is subsequently stabilized at the opposite corner of the square [60]. The size of the written bit is the size of the magnetic bubble domain, and it depends only on the bias ﬁeld, regardless of the light beam intensity, pulse width, or beam diameter. The bit is circular in shape, irrespective of the shape of the light beam [69]. 3.1.14 Driving Force for Wall Displacement To get an idea about the driving force for wall displacement in DWDD, consider the velocity of the wall. The linear velocity νw of the magnetic wall can be calculated according to the formula νw = µw (Hσ + HM + Hext − Hcw ),

(3.1)

3.2 Magnetoelectric Materials

51

where µw is the wall mobility, Hσ is the magnetic ﬁeld caused by the gradient of Bloch wall energy, HM is the demagnetizing ﬁeld from the magnetic triple layers, Hext is the external magnetic ﬁeld, and Hcw is the wall coercivity [56]. The latter has a small value for GdFe in the displacement layer when there is no exchange force. Also, the external magnetic ﬁeld Hext of about 300 Oe is only applied to cancel a ghost signal observed when a longer mark (> 0.25 µm) passes the rear line. On the basis of the above equation, and using some additional theoretical considerations [70, 71] as well as experimental data [72], the velocity of the wall displacement was estimated to be 17 m s−1 which compares reasonably well with the experimental value of 28 m s−1 obtained in the experiment of Fig. 3.7. The magnetic wall velocity νw determines the available data transfer rate because the minimum mark length L that can be read out by DWDD is given by the relationship d L >τ= , (3.2) ν νw where ν is the linear velocity of the rotating disk (∼1.5 m s−1 ), and d is the displacement of the wall. Equation (3.2) means that the wall displacement time τ has to be shorter than the time L/ν for the magnetic wall to reach the terminal, before the next wall reaches the front line. Since ν/L gives the data transfer rate, it indicates that the latter is limited by the linear velocity νw of the magnetic wall. In this DWDD experiment, the maximum data transfer rate was calculated to be 100MB s−1 [56]. At the same time, an estimate of the minimum mark length that can be read out by DWDD was ντ = 50 nm [73]. It should also be noted that a large wall displacement time τ results in a large jitter, where the jitter in nanometers is given by the jitter in nanoseconds times the disk velocity. The jitter in the time domain is inversely proportional to the maximum slope of a signal wave. But the slope is determined by the wall velocity which becomes a quality factor for the jitter. However, the main reason for the jitter in DWDD remains the ﬂuctuation of the front line.

3.2 Magnetoelectric Materials 3.2.1 The Magnetoelectric Eﬀect From Maxwell’s equations it becomes apparent that electric and magnetic ﬁelds are interrelated [74]. A time-varying magnetic ﬂux produces an electric ﬁeld, and hence a potential drop in a stationary loop. A moving loop with a time-varying area in a stationary magnetic ﬁeld generates a voltage also known as a motional electromotive force (Faraday’s law). Conversely, a steady electric current generates a magnetic ﬁeld (Biot–Savart law) [75]. These combined electric and magnetic phenomena have resulted in a variety

52

3 Combined Phenomena in Novel Materials

of applications of major technological importance, from traditional electromagnets to the manipulation of magnetic domains by ways other than magnetic ﬁelds [76]. In particular, there is an eﬀect that has witnessed a signiﬁcant revival in recent years. The linear magnetoelectric (ME) eﬀect is the induction of a magnetization by an electric ﬁeld or the induction of an electric polarization by a magnetic ﬁeld [77]. In essence, in its most general deﬁnition, the magnetoelectric eﬀect is the coupling between magnetic and electric ﬁelds in matter [78], leading to consequential changes in permeability or permittivity, quite often simultaneously observed with the main eﬀect. The most important requirement for the ME eﬀect to be observed is the simultaneous presence of long-range ordering of magnetic moments and electric dipoles. 3.2.2 Oxides, Boracites, Phosphates, etc. The ME eﬀect was ﬁrst predicted by Curie in 1894 [79] and coined as a term by Debye in 1926 [80]. Nevertheless, it was not conﬁrmed until the 1960s when Russian scientists obtained experimental conﬁrmation of an electric ﬁeldinduced magnetization [81,82] and a magnetic ﬁeld-induced polarization [83,84] in antiferromagnetic Cr2 O3 . ME materials that caught researchers’ attention early on were Ti2 O3 [85], GaFeO3 [86], garnet ﬁlms [87], solid solutions such as PbFe0.5 Nb0.5 O3 [88], boracites [89], and phosphates [90]. These materials must be ordered and have a ferroelectric/ferrielectric/antiferroelectric structure that can undergo a transition to a paraelectric state. Crystal structure plays a signiﬁcant role in determining the dielectric properties of paraelectric compounds [91]. Conversely, the ferromagnetic/ferrimagnetic/antiferromagnetic state must change to a paramagnetic state. About 80 single-phase materials display the eﬀect [92], yet it is too weak for developing useful applications [93], notwithstanding early predictions [94]. Even with enhanced ME responses observed in some phosphates such as LiCoPO4 [95] and TbPO4 [96] or yttrium iron garnet ﬁlms [97], microscopic mechanisms are hindering larger induced magnetizations or polarizations in these materials [98], especially at room temperature where ME coupling is small. Additionally, mathematical considerations reveal inherent weaknesses in the ME response [99–101]. Presently, no single-phase material is known that has a high coupling between magnetization and polarization [102], in spite of ongoing research in this area and some progress. For instance, it was noticed that Ti substitution in BiFeO3 renders the compound magnetoelectric, while also reﬁning microstructure and reducing grain size. This eﬀect is attributed to an increase in volume fraction of grain boundaries, leading to an enhanced interfacial polarization [103]. However, improvements in these materials are not signiﬁcant enough to meet industrial expectations. 3.2.3 Layered Composite Materials To obtain better results, the solution is to design composite materials formed by two [104] or three [105] constituents such that the ME response would

3.2 Magnetoelectric Materials

53

exceed the response observed in single-phase materials [106], thereby advancing the prospects for applications [107]. Tellegen was the ﬁrst to formulate the idea of such a composite material, although his suggestion was not practically realizable at the time [108]. A composite material is made of layers of magnetostrictive (or piezomagnetic) and piezoelectric constituents [109], in order that a strain produced by a magnetic ﬁeld applied to the magnetostrictive (or piezomagnetic) material is passed along to the piezoelectric part where it induces a polarization. Most ferromagnetic materials display the magnetostrictive eﬀect. In piezomagnetic materials, the strain induced by a magnetic ﬁeld is linearly proportional to the ﬁeld strength, in contrast to magnetostrictive materials where it is proportional to the square of the ﬁeld strength [110]. Because the layers of the composite material are stress coupled, when the magnetostrictive (or piezomagnetic) part is strained under a magnetic ﬁeld, an electric ﬁeld is induced across the piezoelectric part. In magnetostrictivepiezoelectric composites, the ME eﬀect is nonlinear. Although ferrites such as Cr2 O3 (or a compound containing Cr2 O3 ) are not piezomagnetic, a magnetostriction induced in an AC magnetic ﬁeld gives rise to pseudopiezomagnetic eﬀects, and a ME eﬀect is still observed [111]. The respective thickness and number of layers of the individual phases play an important role in determining the magnitude of the ME response [112], since the compressive stress is higher in thinner piezoelectric layers [113]. Piezocrystals with large piezoelectric voltage coeﬃcients and large elastic compliances give rise to enhanced ME signals. In addition, the volume fraction of the piezoelectric phase needs to be suﬃciently high, the piezoelectric coupling coeﬃcient has to be large, and the magnetic phase must have a small saturation magnetization and a high magnetostriction [114]. 3.2.4 Product, Sum and Combination Properties The magnetostrictive and piezoelectric materials in themselves do not always exhibit a ME eﬀect, though a composite made of these materials may [115]. According to the classiﬁcation given in [116], such a ME composite displays product properties, where the ME eﬀect is absent in either of the initial phases. Alternatively, the ME eﬀect in a composite may be due to sum properties if it is a result of the weighted contribution of each material, and is proportional to the volume of weight fractions of the magnetostrictive and piezoelectric phases [117]. Similarly, the end compound may display scaling or combination properties if the ME response is higher in the composite than in one or more of the constituents [118]. 3.2.5 PZT and Magnetostrictive Materials A commercially available and intensely used piezoelectric material is PbZr1−x Tix O3 (PZT) that is often combined with magnetostrictive constituents such as manganites, LiFe5 O8 , Permendur and YIG [119]. Nevertheless, the most familiar choice is the ferrite NiFe2 O4 or the doped version

54

3 Combined Phenomena in Novel Materials

Ni0.8 Zn0.2 Fe2 O4 , as well as compounds where Ni is substituted with Co such as in CoFe2 O4 [120]. Composites with magnetically hard CoFe2 O4 show a weaker ME coupling, in spite of the high magnetostriction observed in CoFe2 O4 . This is in contrast to the better coupling obtained in compounds that contain the softer NiFe2 O4 that has a much smaller anisotropy and magnetostriction [121]. Substituting Ni or Co with Zn in diﬀerent percentages increases the ME response because Zn releases lattice strain, increases permeability, and lowers magnetic anisotropy [122]. An applied magnetic ﬁeld results in domain wall motion and spin rotation within the magnetic domains; therefore, a high initial permeability or unobstructed domain motion is essential for good ME coupling between the magnetostrictive and piezoelectric phases [123]. 3.2.6 Avoiding Ferrites The low resistivity of ferrites produces leakage currents in the sample, resulting in reduced ME behavior in composite materials. One way to increase the resistivity of the ferrite constituent is to decrease the sintering temperature during the fabrication process [124]. Alternatively, the magnetostrictive behavior observed in La0.7 Sr0.3 MnO3 , La0.7 Ca0.3 MnO3 [125], or Tb1−x Dyx Fe2 alloys (Terfenol-D) [126] makes them popular substitutes for ferrites as constituents in ME composite materials. Additionally, the ME properties of composites containing a magnetostrictive rare-earth-iron alloy such as Terfenol-D combined with piezoelectric ceramics like polyvinylidine-ﬂuoride (PVDF) have been calculated using the Green’s function technique and found likely to exhibit a giant ME eﬀect [127]. Other materials for the piezoelectric part that showed promising results were Bi4 Ti3 O12 , PbMg1/3 V2/3 O3 , PbMg1/3 Nb2/3 O3 –PbTiO3 , or PbZn1/3 Nb2/3 O3 –PbTiO3 [128]. Pioneering experiments with these materials [129] revealed that many parameters needed to be tuned to take advantage of the properties of the individual constituents, just as the interactions between them had to be considered to ensure a maximized ME response. By combining ferroelectric piezoelectric materials, such as BaTiO3 , BiFeO3 , or BiFe1−x Tix O3 , and ferromagnetic piezomagnetic CoFe2 O4 , researchers were able to obtain a new composite material with an enhanced ME response strongly dependent on the fabrication conditions, usually involving sintering [130]. During this process, solid state reactions take place among the constituent oxides, for instance in the case of BaCO3 , Co3 O4 , Fe2 O3 , or TiO2 when they are heated below their melting point, particles adhere to each other. 3.2.7 Undesired Eﬀects of Sintering After fabrication, the obtained composite is heated above the ferroelectric transition temperature, and then poled during cooling under an applied electric ﬁeld. The magnetic poling is done at room temperature under a constant DC magnetic ﬁeld, usually by keeping the composite samples between the

3.2 Magnetoelectric Materials

55

poles of an electromagnet [131]. Sintered composites are less expensive to prepare than unidirectionally solidiﬁed in situ materials, in spite of the fact that the ME signal is higher in the latter category. The molar ratio of phases in sintered composites, the grain size of each phase, and the sintering temperature are easily controllable. However, with sintered composites a variety of problems surface, such as the diﬃculty in passing on the mechanical stress between the magnetostrictive and piezoelectric materials without losses [132] or the reduction in the ME response due to leakage currents in low resistivity magnetostrictive phases. Microcracks due to thermal expansion mismatch between constituents, impurities or undesired phases are also noticed to reduce the ME signal [133]. 3.2.8 Variations in Signal Due to Mechanical Coupling Some variations in ME behavior are observed because of the amount of mechanical coupling between the magnetostrictive and piezoelectric phases [134]. Certain constituents such as La0.7 Sr0.3 MnO3 , La0.7 Ca0.3 MnO3 or CoFe2 O4 are joined only weakly to PZT [135], while NiFe2 O4 has superior interface coupling to PZT [136]. Additionally, mechanical defects such as pores or microscopic cracks form because of lattice strain, limiting the mechanical bond between the particles of the diﬀerent components [137]. It was observed that the ME signal increases with higher sintering temperatures for PZT and Ni-ferrites with Fe ions dissolving into the PZT, or the latter diﬀusing into the ferrite matrix. Doping the Ni-ferrite with Co, Cu, and Mn leads to enhanced values for the magnetostriction, magnetomechanical coupling, and electric resistivity. It should be noted that the dielectric transition temperature in these composites is close to the original dielectric Curie temperature of pure PZT [138]. 3.2.9 Laminated Composites Further improved results were obtained when the magnetostrictive and piezoelectric constituents were assembled from particulate materials [139] or by hot molding, the latter producing interfaces that can no longer be resolved by SEM [140] (Fig. 3.9). Mixtures of PZT/PVDF or Terfenol-D/PVDF are set in molds and subsequently hot pressed [141]. Instead of sintering the constituents, researchers use laminated layers, and indeed enhanced ME responses are observed [142]. An example of a laminated composite is obtained by sandwiching a PZT layer between two Terfenol-D plates and bonding using a conductive epoxy resin, followed by curing the compound at 80◦ C for 3–4 h under load [143]. The large ME responses given by laminated composites can be attributed to the lack of chemical reactions between independently prepared constituents, unlike in sintered granular composites or unidirectionally solidiﬁed composites where the temperature of processing is too high to avoid any chemical reaction of the phases [144]. In spite of the obstacles encountered in experiments with composite materials, the obtained ME response exceeds the largest values observed in single-phase compounds [145].

56

3 Combined Phenomena in Novel Materials

Fig. 3.9. SEM cross sectional micrograph of a trilayer structure obtained by hot pressing of three laminated layers of mixtures at 180◦ C and 10 MPa for 30 min. No obvious interfaces can be observed between these three layers (reprinted with permission from [140], copyright 2003 by the American Physical Society, URL: http://link.aps.org/abstract/PRB/v68/e224103; doi:10.1103/PhysRevB.68.224103)

3.2.10 Voltage Coeﬃcient α ME behavior is usually determined by using a voltage coeﬃcient α, measured in V cm−1 Oe−1 and expressed as ∂E α= , (3.3) ∂H where ∂E is the electric ﬁeld produced by an applied AC magnetic ﬁeld ∂H. The produced electric ﬁeld is measured via the voltage ∂V detected across the sample thickness t. One of the ﬁrst studies on composites done at Philips Laboratories in the Netherlands resulted in a ME composite obtained by unidirectional solidiﬁcation of a eutectic composition of the quinary system Fe–Co–Ti–Ba–O. Through critical control over the composition, especially when one of the components is oxygen, the eutectic liquid decomposes into alternate layers of perovskite and spinel phases during the unidirectional solidiﬁcation process. For the researchers at Philips, an excess of TiO2 (1.5 wt%) in their composites gave a high ME voltage coeﬃcient of 50 mV cm−1 Oe−1 [146]. In subsequent work on BaTiO3 –CoFe2 O4 , a ME voltage coeﬃcient as high as 130 mV cm−1 Oe−1 was obtained [147]. These values are in contrast to the 20 mV cm−1 Oe−1 voltage coeﬃcient obtained earlier by the Philips researchers in Cr2 O3 single crystals. Since then, much higher values were obtained for the ME voltage coeﬃcient.

3.2 Magnetoelectric Materials

57

3.2.11 Obtaining Improved Voltage Coeﬃcients As noted earlier, the relationship between the applied magnetic ﬁeld and the voltage induced in the detection circuit is not linear in compounds made of several constituents [148], as it would be for single-phase materials [149]. To obtain linearity in a composite material, the weak AC magnetic ﬁeld (up to 10 Oe) needs to be superimposed on a large (up to 10 kOe) DC bias ﬁeld [150], so that the ME eﬀect over a short range around this bias can be approximated as a linear eﬀect, and the voltage coeﬃcient α varies linearly with the DC bias ﬁeld [151]. For an enhanced response, the modulation frequency of the applied ﬁeld needs to coincide with the magnetic [152], electrical [153], or mechanical eigenmodes [154] of the system. If the AC magnetic ﬁeld is tuned to electromechanical resonance, a signiﬁcant increase in the ME voltage coeﬃcient α is obtained [155]. Observations show that α displays a strong frequency dependence in the microwave range [156, 157]. In addition to frequency considerations, the orientation of the DC magnetic ﬁeld and AC probe ﬁeld, as well as the direction of the induced signal with respect to the former two, determines the magnitude of the ME signal [158]. A longitudinal ME response is obtained when both AC and DC applied ﬁelds, as well as the induced signal are parallel to each other [159]. Conversely, a transverse ME response is obtained when the induced electric ﬁeld is perpendicular to the applied DC and AC magnetic ﬁelds [160], which need to be parallel to one another for maximum eﬀect [161]. Ultimately, the ME response depends on the relative orientation of the constituents [162]. Enhanced ME responses in laminated plate composites with transverse polarization and longitudinal magnetization with respect to the applied ﬁeld were obtained by some researchers [163]. Studies were also done for laminate designs with longitudinally magnetized and longitudinally polarized constituents [164]. Their ﬁndings depended on the direction of maximum magnetostrictive strain. Considering that magnetostrictive strain is anisotropic, the ME eﬀect is less pronounced for a direction with reduced magnetostriction. ME coupling is increased when a small increase in the magnetic ﬁeld results in a signiﬁcant increase in magnetostriction, since a key requirement for a strong ME coupling is a large magnetostriction. At the same time, the ME coupling between the piezoelectric and magnetostrictive phases vanishes when the magnetostriction attains saturation [165]. Therefore, any dependence of the ME eﬀect on ﬁeld orientation results from the magnetostriction. 3.2.12 ME and Nanostructures Lately, magnetoelectric compounds have been obtained by self-assembly on a nanoscale, a technique which shows promising results in terms of phenomena that can be exploited through nanotechnology. In an interesting study, hexagonal CoFe2 O4 nanopillars embedded in a BaTiO3 matrix were grown

58

3 Combined Phenomena in Novel Materials

perpendicular to a single-crystal SrTiO3 substrate [166]. The average spacing between the nanopillars was 20–30 nm, and the whole composite, nanopillars and matrix materials, was grown with a high degree of crystallographic orientation. In this ME compound, the (quasi)unidirectional conﬁnement of the nanopillars led to strains in the magnetostrictive CoFe2 O4 lattice, deformation that was further enhanced due to structural distortions it created in the ferroelectric BaTiO3 matrix. Good connectivity among the constituents was revealed when temperature-dependent magnetization measurements showed signiﬁcant coupling between the magnetic and electric phases, coupling that dropped at the ferroelectric Curie temperature of 390 K. In an alternative experiment, ferromagnetic NiFe2 O4 (NFO) nanoparticles were dispersed with their crystal orientations aligned in a ferroelectric Pb(Zr0.52 Ti0.48 )O3 (PZT) matrix [167]. The NFO-PZT nanocomposite was fabricated as a thin ﬁlm on (001) oriented 0.5% Nb-doped SrTiO3 (Nb:STO) substrates using pulsed laser deposition. The advantage of having nanoparticles rather than nanopillars is that the geometry of the former reduces possible leakage current paths through the ferromagnetic phase. In the end, measured ME parameters, such as remnant polarization, saturation polarization, coercive electric ﬁeld, and their magnetic counterparts, were in good agreement with reported values for bulk composites [168, 169]. Furthermore, the magnetoelectric voltage coeﬃcient α displayed hysteresis and remanence in its magnetic ﬁeld dependence, similar to bulk composites [170]. 3.2.13 Eﬀects on a Nanoscale Previous theoretical methods such as Green’s function technique [171], ﬁnite element method, [172] or the constitutive equations [173] have been developed only for the calculation of ME responses of bulk composites, considering no inﬂuence of residual strain. Even fewer theoretical approaches exist for nanostructured ME compounds [174]. Aside from quantum mechanical phenomena revealed on a nanoscale [175], the magnetic, dielectric, magnetostrictive, and piezoelectric properties are also strongly dependent on mechanical boundary conditions, or mechanical constraints caused by lattice misﬁt between ﬁlm and substrate. Choosing appropriate ferroelectric and magnetic materials for an epitaxial nanocomposite requires consideration of lattice match and elastic properties, solid solubility, as well as chemical compatibility. Growing CoFe2 O4 at elevated temperatures surrounded by ferroelectric BaTiO3 leads to self-assembly of the former into columnar nanostructures due to reduced solid solubility of the two phases (Fig. 3.10a, b). As a result of the lattice match between BaTiO3 –CoFe2 O4 and the substrate, good epitaxial alignment is obtained along the ﬁlm’s normal (Fig. 3.10c). Furthermore, magnetism and ferroelectricity coexist in the thin ﬁlm, as proved by the magnetic force microscopy (MFM) images shown in Fig. 3.11, and piezoelectric force microscopy experiments. These scans were repeated after every electrical poling or magnetizing process. Consequently, it was determined that

3.2 Magnetoelectric Materials

59

Fig. 3.10. (a) Sketch of the self-assembled BaTiO3 –CoFe2 O4 heterostructure on a (001) SrTiO3 substrate with a thick SrRuO3 electrode. (b) Plan-view TEM image of the CoFe2 O4 nanopillars surrounded by the BaTiO3 matrix. The bar is 30 nm. (c) High resolution plan-view TEM image of the BaTiO3 –CoFe2 O4 interface taken in the area marked by a rectangle in (b). The bar is 3 nm (reprinted from [176] (copyright 2005) with permission from the American Chemical Society)

an applied electric ﬁeld can switch the magnetization between two stable states in the CoFe2 O4 columns. Similar results were obtained for the polarization in the BaTiO3 matrix under an applied magnetic ﬁeld, proving that there is a strong elastic strain-mediated ME coupling between the two ferroic components of the nanocomposite. Through calculations it was shown that the piezoelectric elastic energy density (∼0.6 × 105 J m−3 ) is of the same order of magnitude as the magnetoelastic energy density (∼0.9 × 105 J m−3 ) that needs to be overcome to enable a temporary change in the magnetic anisotropy [176].

60

3 Combined Phenomena in Novel Materials

Fig. 3.11. Magnetic force microscopy image after magnetizing the BaTiO3 –CoFe2 O4 ﬁlm perpendicular to the surface in a magnetic ﬁeld of 20 kOe. The magnetic anisotropy in the columnar CoFe2 O4 is perpendicular to the surface. The bar is 2 µm (reprinted from [176] (copyright 2005) with permission from the American Chemical Society)

3.2.14 Residual Stresses and Strains in Nanostructures Further experimentation [177] determined that the coupling interaction in a nanostructured multiferroic BaTiO3 –CoFe2 O4 ﬁlm is diﬀerent from that in bulk composites due to large longitudinal residual stresses and strains created by the CoFe2 O4 nanopillars embedded in the BaTiO3 matrix. These results were backed up by theoretical models based on constitutive equations for piezoelectric and piezomagnetic materials, equations modiﬁed on purpose for nanomaterials. The ME parameters calculated from the theoretical models for nanostructured systems agree well with the experimentally measured values, thereby verifying the residual strain induced variations in the ME ﬁlms. Hence, nanostructured ME compounds can act as a transducer between magnetic and electric ﬁeld signals, proving that ME materials can be obtained by nanofabrication, while intensifying the anticipation of revolutionary changes in miniaturization, integration, and length-scale reduction in instrumentation and electronics. Newly developed nanomaterials may ﬁnally bring the ME eﬀect to practical levels for signiﬁcant advances in technologies that have undergone promising developments since the 1990s: magnetic–electric sensors and transducers, read/write devices, or even spintronics [178]. Nevertheless, the ongoing problem of how to improve the design of ME materials with a strong magnetization–polarization correlation remains, and it naturally requires a better understanding of the mechanisms leading to the generation of the ME eﬀect.

3.2 Magnetoelectric Materials

61

3.2.15 Multiferroics Extensive research over the last decade has shown that enhanced signals are obtained in materials with existing or induced long-range magnetic or electric ordering that can in their turn, generate magnetic or electric ﬁelds. It was noticed that tuning of ME performance can be achieved in boracites with clamped switching of electrical and magnetic domains, in orthorhombic manganites where a ferroelectric restructuring can be brought about by an applied magnetic ﬁeld, or in hexagonal manganites with electric ﬁeld-induced ferromagnetic ordering [179]. These observations led to a new classiﬁcation for these compounds. They are called ferroics and are mainly characterized by the fact that switchable ferromagnetic or ferroelectric domains are formed, and ferromagnetic or ferroelectric ordering can be induced by an applied (or sometimes intrinsic) electric or magnetic ﬁeld [180]. Furthermore, if these compounds are fabricated such that ferromagnetic and ferroelectric phases are made to coexist, then manipulating the ferromagnetic phase implies that setting or reading of a magnetic state can be obtained by means of a coexisting ferroelectric state, both within the same material [181]. Compounds with two or more phases are known as multiferroics [182], since they combine two or more primary ferroic properties. 3.2.16 Using Terfenol-D Within multiferroic materials, multiple types of domains are present and there is a cross correlation between coexisting forms of ordering. A simple illustration of a three phase ferroic is the Terfenol-D/PZT/PVDF composite obtained by molding and pressing at 10 MPa and 190◦ C, containing distinct particles of the blended parts as shown in Fig. 3.12. The PZT/PVDF particles constitute the ferroelectric part, while Terfenol-D is the ferromagnetic constituent. Terfenol-D particles display a low resistance, and hence it is required that they are well dispersed in the PZT/PVDF matrix to maintain the electrically insulating property of the composite. Otherwise, the low resistance path created by the Terfenol-D particles will cause the polarization charges to leak via this path. A magnetostrictive change in the Terfenol-D particles is transmitted to the PZT/PVDF matrix inducing polarization charges, giving rise to a ME response [183]. 3.2.17 Multiferroic Transformers The combination of magnetostrictive Terfenol-D and piezoelectric PZT may oﬀer applications in miniature transformers [184]. In such studies, a laminated composite of ring-type geometry containing circumferentially magnetized Terfenol-D and circumferentially polarized PZT was found to display a large ME voltage gain. The design of the transformer is based on the piezoelectric and piezomagnetic equations of state in a radial symmetric-mode vibration, and consists of a four-segment piezoelectric ring layer placed between two

62

3 Combined Phenomena in Novel Materials

Fig. 3.12. Cross-sectional micrograph of three-phase Terfenol-D/PZT/PVDF composite. The particles above 10 µm are Terfenol-D, the 5 µm particles are PZT, and the irregular phase is polyvinylidine ﬂuoride PVDF (reprinted from [183] (copyright 2003) with permission from the American Institute of Physics)

Fig. 3.13. Ring-type ME laminate composite for transformer applications where the voltage gain is deﬁned as Vout /Vin (reprinted from [184] (copyright 2004) with permission from the American Institute of Physics)

magnetostrictive ring layers. Unwanted eddy-currents are minimized or eliminated when the conductive magnetostrictive layers are made very thin. The ﬁelds are applied circumferentially, giving rise to strains in the circumferential direction. A sketch of the transformer design is shown in Fig. 3.13. The AC magnetic excitation ﬁeld is applied via a current in a toroidal coil that embraces the three ring layers. Hence, the vortex magnetic ﬁeld is contained circumferentially within the rings, causing the magnetostrictive rings

3.2 Magnetoelectric Materials

63

to shrink/expand. As a result, the piezoelectric ring strains radially, producing an output voltage from each of the four segments of the ring. When the frequency of the excitation ﬁeld is equal to the resonance frequency of the ring and the device functions in resonance drive, the strong ME coupling allows the output voltage to be much higher than the input, exhibiting a large voltage gain. The latter is dependent on the DC magnetic ﬁeld, and has a value of ∼25 at its maximum, for a resonance frequency of 53.3 kHz. Considering these recent advances in ME materials, as exempliﬁed by this transformer that does not require secondary coils with a high-turn ratio, traditional electromagnets may soon be replaced by a solid-state device with a totally diﬀerent geometry. 3.2.18 Multiferroic Sensors for Vortex Magnetic Fields Another possible application of ring-shaped laminates of Terfenol-D and PZT is that of sensors for AC rotating or vortex magnetic ﬁelds, as described by the same group of researchers mentioned earlier [185]. On the basis of similar construction and design, a vortex magnetic ﬁeld applied to the Terfenol-D rings gives rise to a strain in the circumferential direction that puts the piezoelectric PZT ring in a radial vibration mode. Detection of the magnetic ﬁeld occurs with a high sensitivity of 10−8 T. Other geometries where, for instance, the magnetic ﬁeld is parallel, and the electric ﬁeld is perpendicular to the principal strain direction [186] allow only detection of magnetic ﬁelds of constant direction. However, in some cases such as in power-integrated circuits [187] or superconducting ﬁlms [188] it is the vortex magnetic ﬁelds that may require detection. 3.2.19 Enhancing Multiferroicity through Material Design Multiferroicity can be enhanced or even acquired through proper material design. PbFe1/2 Nb1/2 O1/3 [189] displays a ME eﬀect when transition-metal ions are partly replaced by paramagnetic ions [190]. In a subgroup of hexagonal manganites (e.g. doped perovskite manganites), a magnetic ﬁeld induces displacement of the Mn3+ ions along the hexagonal axis and the subsequent geometric charge ordering generates a ferroelectric polarization, and hence a ME eﬀect [191]. A static magnetic ﬁeld applied to Pr1−x Cax MnO3 (0.3 < x < 0.7) produces an insulator–metal transition that leads to a transformation from an antiferromagnetic insulating to a ferromagnetic metallic state accompanied by changes in dielectric properties [192]. Rare-earth manganites RMnO3 where R can be Ho, Er, Tm, or Yb can trigger phase transitions and considerably high ME signals. An applied magnetic ﬁeld induces an antiferromagnetic reorientation of the Mn3+ moments and ferromagnetic ordering of the rareearth sublattices [193]. Sometimes, ME interactions can be strengthened by lowering the porosity and increasing the resistivity in a ferroic compound. Similarly, hot pressing can contribute to controlling key ME parameters that depend on grain size and density, by increasing the initial permeability and strengthening the electromechanical coupling [194].

64

3 Combined Phenomena in Novel Materials

3.2.20 Identifying Multiferroics The designation of ferroic depends on nanoscale eﬀects within the material, eﬀects that can ultimately allow the formation of switchable domains, as in ferroelectric or ferromagnetic ordering. The latter are inﬂuenced largely by symmetry operations which take place in the crystal when either the polarization or magnetization, or both, rotate. For example, in Ni3 B7 O13 I where the polarization and a weak magnetization are coupled, an electric ﬁeld-induced 180◦ reversal of the polarization leads to a 90◦ rotation of the magnetization [195]. This is a symmetry operation of the paramagnetic dielectric phase that leads to a transformation between diﬀerent domains of the ordered compound. However, it does not further reduce the symmetry of the crystal [196]. On the other hand, a mere rotation of magnetization is not a symmetry operation of the parent phase, and therefore reduces the magnetic energy and increases the free energy of the crystal. Consequently, coupling between polarization and magnetization in a compound conserves the symmetry and makes it possible to obtain a large ME response [197]. It was also demonstrated that in some antiferromagnetic materials spin-rotation domains are generated that supplement the existing spin-reversal domains. In these materials, the piezomagnetic interaction of the strain induced by the ferroelectric domain walls reduces the free energy of the crystal [198], giving rise to ME behavior even if the global symmetry of the crystal forbids the eﬀect. The presence of an external ﬁeld is usually necessary for bringing about a ME magnetization or polarization. Still, a spontaneous ME eﬀect is possible when an intrinsic polarization causes a weak permanent magnetization [199]. Equally, the magnetic order in some modiﬁed perovskite compounds such as TbMnO3 [200] or DyMnO3 [201] can lead to the emergence of polarization giving rise to a ME eﬀect. Attempts to combine magnetic and electric ordering in the same phase have proved unsuccessful so far, owing to the mutually exclusive nature of atomic-level mechanisms responsible for ferromagnetism or ferroelectricity. On the other hand, the variety of mechanisms responsible for ME behavior in multiphase ferroics clearly indicates that more research is necessary to obtain a comprehensive representation of the sources of the ME eﬀect if better design for these materials is sought.

References 1. 2. 3. 4. 5. 6. 7.

P.J. Flanders, IEEE Trans. Magn. 12, 348 (1976) P.J. Flanders, IEEE Trans. Magn. 10, 1050 (1974) M. Kaneko, IEEE Trans. Magn. 16, 1319 (1980) S. Ogawa, C. Handa, S. Ishida, H. Soma, IEEE Trans. Magn. 13, 1394 (1977) L.R. Bickford Jr., J. Pappis, J.L. Stull, Phys. Rev. 99, 1210 (1955) H.J. Richter, IEEE Trans. Magn. 35, 2790 (1999) M. Kaneko, S. Yoshimura, G. Fujita, S. Kobayashi, IEEE Trans. Magn. 36, 2266 (2000)

References

65

8. C. Cesari, J.P. Faure, J. Nihoul, K. Ledang, P. Veillet, D. Renard, J. Magn. Magn. Mater. 78(2), 296 (1989) 9. F. Rousseaux, A.M. Haghirigosnet, B. Kebabi, Y. Chen, H. Launois, Microelectr. Eng. 17(1–4), 157 (1992) 10. O. Geoﬀroy, D. Givord, Y. Otani, B. Pannetier, A.D. Santos, M. Schlenker, Y. Souche, J. Magn. Magn. Mater. 121(1–3), 516 (1993) 11. A. Yariv, Optical Electronics, 3rd ed. (Holt, New York, 1985) 12. C. Guillaud, Thesis, Univ. of Strasbourg, Strasbourg, France, 1943 13. B.W. Roberts, C.P. Bean, Phys. Rev. 96, 1494 (1954) 14. H.J. Williams, R.C. Sherwood, F.G. Foster, E.M. Kelley, J. Appl. Phys. 28 (10), 1181 (1957) 15. C.A. Fowler Jr., E.M. Fryer, Phys. Rev. 86, 426 (1952) 16. C.A. Fowler Jr., E.M. Fryer, Phys. Rev. 100, 746 (1955) 17. C.A. Fowler Jr., E.M. Fryer, Phys. Rev. 104, 552 (1956) 18. D.K. Misemer, J. Magn. Mater. 72, 267 (1988) 19. A. Ashkin, J.M. Dziedzic, Appl. Phys. Lett. 21, 253 (1972) 20. Y. Togami, IEEE Trans. Magn. 18(6), 1233 (1982) 21. P. Chaudhari, J.J. Cuomo, R.J. Gambino, Appl. Phys. Lett. 22(7), 337 (1973) 22. Y. Mimura, N. Imamura, Appl. Phys. Lett. 28(12), 746 (1976) 23. N. Imamura, C. Ota, Jpn. J. Appl. Phys. 19, L731 (1980) 24. E. Ikeda, T. Tanaka, T. Chiba, H. Yoshimura, J. Magn. Soc. Jpn. 17(S1), 335 (1993) 25. M. Kaneko, K. Aratani, Y. Mutoh, A. Nakaoki, K. Watanabe, H. Makino, Jpn. J. Appl. Phys. 28(28), 27 (1989) 26. M. Kaneko, IEEE Trans. Magn. 28(5), 2494 (1992) 27. A. Okamuro, J. Saito, T. Hosokawa, H. Matsumoto, H. Akasaka, J. Magn. Soc. Jpn. 15(S1), 447 (1991) 28. Y. Mutoh, T. Shimouma, A. Nakaoki, K. Suzuki, M. Kaneko, J. Magn. Soc. Jpn. 15(S1), 311 (1991) 29. J. Saito, M. Sato, H. Matsumoto, H. Akasaka, Jpn. J. Appl. Phys. 26(4), 155 (1987) 30. M. Kaneko, K. Aratani, M. Ohta, Jpn. J. Appl. Phys. 31(1), 568 (1992) 31. M. Ohta, A. Fukumoto, K. Aratani, M. Kaneko, K. Watanabe, J. Magn. Soc. Jpn. 15(S1), 319 (1991) 32. A. Fukumoto, S. Kubota, Jpn. J. Appl. Phys. 31(1), 529 (1992) 33. G. Bouwhuis, J.H.M. Spruit, Appl. Opt. 29, 3766 (1990) 34. A. Fukumoto, S. Yoshimura, Proc. SPIE 1663, 216 (1992) 35. S. Yoshimura, A. Fukumoto, M. Kaneko, H. Owa, Jpn. J. Appl. Phys. 31(1), 576 (1992) 36. F. Maeda, M. Arai, H. Owa, H. Takahashi, M. Kaneko, Proc. SPIE 1499, 62 (1991) 37. A. Fukumoto, K. Aratani, S. Yoshimura, T. Udagawa, M. Ohta, M. Kaneko, Proc. SPIE 1499, 216 (1991) 38. S. Yoshimura, I. Nakao, A. Fukumoto, M. Kaneko, H. Owa, IEEE Trans. Consum. Electr. 38(3), 660 (1992) 39. M. Kaneko, K. Aratani, A. Fukumoto, S. Miyaoka, Proc. IEEE 82 (4), 543 (1994) 40. A. Fukumoto, S. Yoshimura, T. Udagawa, K. Aratani, M. Ohta, M. Kaneko, Proc. SPIE 1499, 216 (1991)

66

3 Combined Phenomena in Novel Materials

41. K. Aratani, M. Kaneko, Y. Muto, K. Watanabe, H. Makino, Proc. SPIE 1078, 258 (1989) 42. A. Nakaoki, S. Tanaka, T. Shimouma, M. Kaneko, Jpn. J. Appl. Phys. 31(1), 596 (1992) 43. K. Aratani, A. Fukumoto, M. Ohta, M. Kaneko, K. Watanabe, Proc. SPIE 1499, 209 (1991) 44. A. Nakaoki, Y. Mutoh, S. Tanaka, T. Shimouma, K. Asano, K. Aratani, M. Kaneko, K. Watanabe, Proc. SPIE 1316, 292 (1990) 45. T. Fukami, Y. Nakaki, T. Tokunaga, M. Taguchi, K. Tsutsumi, J. Appl. Phys. 67, 4415 (1990) 46. S. Tanaka, T. Shimouma, A. Nakaoki, K. Aratani, M. Kaneko, J. Magn. Soc. Jpn. 15(S1), 331 (1991) 47. S. Hashimoto, A. Maesaka, Y. Ochiai, J. Appl. Phys. 70, 5133 (1991) 48. W.B. Zeper, A.P.J. Jongenelis, A.J. Jacobs, H.W. van Kesteren, P.F. Garcia, IEEE Trans. Magn. 28, 2503 (1912) 49. M. Kaneko, Y. Sabi, I. Ichimura, S. Hashimoto, IEEE Trans. Magn. 29(6), 3766 (1993) 50. M. Takahashi, J. Nakamura, M. Ojima, K. Tatsuno, Proc. SPIE 1663, 250 (1992) 51. Y. Mimura, N. Imamura, Appl. Phys. Lett. 28(12), 746 (1976) 52. S. Tsunashima, H. Tsuji, T. Kobayashi, S. Uchiyama, IEEE Trans. Magn. 17, 2840 (1981) 53. T. Kobayashi, H. Tsuji, S. Tsunashima, S. Uchiyama, Jpn. J. Appl. Phys. 20, 2089 (1981) 54. S. Hashimoto, Y. Ochiai, J. Magn. Magn. Mat. 88, 211 (1990) 55. T. Shiratori, E. Fujii, Y. Miyaoka, Y. Hozumi, J. Magn. Soc. Jpn. 22(S2), 47 (1998) 56. M. Kaneko, T. Sakamoto, A. Nakaoki, IEEE Trans. Magn. 35(5), 3112 (1999) 57. T. Shiratori, E. Fujii, Y. Miyaoka, Y. Hozumi, Digest Int. Symp. Optical Memory (Tsukuba, Japan, 1998), p. 46 58. T. Shiratori, E. Fujii, Y. Miyaoka, Y. Hozumi, J. Magn. Soc. Jpn. 23, 145 (1999) 59. S. Kobayashi, S. Senshu, S. Iwaasa, S. Igarashi, S. Wachi, T. Funahashi, M. Ogawa, Proc. SPIE 1663, 15 (1992) 60. M. Kaneko, T. Okamoto, H. Tamada, Y. Tamada, IEEE Trans. Magn. 22(1), 2 (1986) 61. J.P. Krumme, H.J. Schmitt, IEEE Trans. Magn. 11(5), 1097 (1972) 62. Y.S. Liu, G.S. Almasi, G.E. Keefe, IEEE Trans. Magn. 13(6), 1744 (1977) 63. H. Callen, R.M. Josephs, J. Appl. Phys. 42(5), 1977 (1971) 64. A.H. Bobeck, R.F. Fischer, A.J. Perneski, J.P. Remeika, L.G. van Uitert, IEEE Trans. Magn. 5(3), 544 (1969) 65. W.F. Druyvesteyn, J.Appl. Phys. 46(3), 1342 (1975) 66. J. Yang, Y. Xu, F. Zhang, M. Guillot, J. Phys: Condens. Matter 18, 9287 (2006) 67. K. Matsumoto, S. Sasaki, K. Haraga, K. Yamaguchi, T. Fujii, IEEE Trans. Magn. 28, 2895 (1992) 68. G.F. Dionne, G.A. Allen, J. Appl. Phys. 75, 6372 (1994) 69. M. Kaneko, T. Okamoto, H. Tamada, T. Yamada, IEEE Trans. Magn. 19(5), 1763 (1983)

References

67

70. O.W. Shih, J. Appl. Phys. 75, 4382 (1994) 71. E. Schloemann, J. Appl. Phys. 44, 1837 (1973) 72. M. Tabata, T. Kobayashi, S. Shiomi, M. Masuda, Jpn. J. Appl. Phys. 36, 7177 (1997) 73. J.C. Slonczewski, J. Appl. Phys. 44, 1759 (1973) 74. J.D. Jackson, Classical Electrodynamics, 2nd ed. (Wiley, New York, 1975) 75. F.T. Ulaby Fundamentals of Applied Electromagnetics (Prentice Hall, Upper Saddle River, NJ, 1999) 76. P. Smole, W. Ruile, C. Korden, A. Ludwig, E. Quandt, S. Krassnitzer, P. Pongratz, in Proc. IEEE International Frequency Control Symposium, Tampa, 2003, p. 903 77. E. Ascher, in Magnetoelectric Interaction Phenomena in Crystals, ed. by A.J. Freeman, H. Schmid (Gordon and Breach, London, 1975) 78. K. Aizu, Phys. Rev. B 2, 754 (1970) 79. P. Curie, J. Phys. 3, 393 (1894) 80. P. Debye, Z. Phys. 36, 300 (1926) 81. D.N. Astrov, Sov. Phys.- JETP 11, 708 (1960) 82. D.N. Astrov, Sov. Phys.- JETP 13, 729 (1961) 83. G.T. Rado, V.J. Folen, Phys. Rev. Lett. 7, 310 (1961) 84. V.J. Folen, G.T. Rado, E.W. Stalder, Phys. Rev. Lett. 6, 607 (1961) 85. B.I. Al’Shin, D.N. Astrov, Sov. Phys.- JETP 17, 809 (1963) 86. G.T. Rado, Phys. Rev. Lett. 13, 335 (1964) 87. T.H. O’Dell, Phil. Mag. 16, 487 (1967) 88. T. Watanabe, K. Kohn, Phase Trans. 15, 57 (1989) 89. E. Ascher, H. Rieder, H. Schmid, H. St¨ ossel, J. Appl. Phys. 37, 1404 (1966) 90. R.P. Santoro, D.J. Segal, R.E. Newnham, J. Phys. Chem. Solids 27, 1192 (1966) 91. R. Ranjan, A. Agrawal, A. Senyshyn, H. Boysen, J. Phys.: Condens. Matter 18, L515 (2006) 92. B.B. Krichevtsov, V.V. Pavlov, R.V. Pisarev, A.G. Selitsky, Ferroelectrics 161, 65 (1993) 93. J.P. Rivera, Ferroelectrics 161, 165 (1994) 94. V.E. Wood, A.E. Austin, Int. J. Magn. 5, 303 (1974) 95. J.P. Rivera, Ferroelectrics 161, 147 (1993) 96. G.T. Rado, J.M. Ferrari, W.G. Maisch, Phys. Rev. B 29, 4041 (1984) 97. B.B. Krichevtsov, V.V. Pavlov, R.V. Pisarev, JETP Lett. 49, 535 (1989) 98. C.W. Nan, F.-S. Jin, Phys. Rev. B 48, 8578 (1993) 99. W.F. Brown Jr., R.M. Hornreich, S. Shtrikman, Phys. Rev. 168, 574 (1968) 100. R.M. Hornreich, S. Shtrikman, Phys. Rev. 161, 506 (1967) 101. G.A. Gehring, Ferroelectrics 161, 275 (1994) 102. S. Dong, J. Li, D. Viehland, Appl. Phys. Lett. 83, 2265 (2003) 103. M. Kumar, K.L. Yadav, J Phys.: Condens. Matter 18, L503 (2006) 104. C.W. Nan, M. Li, X. Feng, S. Yu, Appl. Phys. Lett. 78, 2527 (2001) 105. C.W. Nan, L. Liu, N. Cai, J. Zhai, Y. Ye, Y.H. Lin, L.J. Dong, C.X. Xiong, Appl. Phys. Lett. 81 (20), 3831 (2002) 106. S. Lopatin, I. Lopatina, I. Lisnevskaya, Ferroelectrics 161-162, 63 (1994) 107. C.W. Nan, Phys. Rev. B 50, 6082 (1994) 108. B.D.H. Tellegen, Philips Res. Rep. 3, 81 (1948) 109. C.W. Nan, G.J. Weng, Phys. Rev. B 60, 6723 (1999)

68

3 Combined Phenomena in Novel Materials

110. Proc. 3rd Int. Conf. Magnetoelectric Interaction Phen. Cryst. (MEIPIC-3), Ferroelectrics 204, 356 (1997) 111. K.K. Patankar, S.A. Patil, K.V. Sivakumar, R.P. Mahajan, Y.D. Kolekar, M.B. Kothale, Mat. Chem. Phys. 65, 97 (2000) 112. G. Srinivasan, E.T. Rasmussen, J. Gallegos, R. Srinivasan, Y.I. Bokhan, V.M. Laletin, Phys. Rev. B 64, 214408 (2001) 113. A.V. Virkar, J.L. Huang, R.A. Cutler, J. Am. Ceram. Soc. 70, 164 (1987) 114. S. Shastry, G. Srinivasan, M.I. Bichurin, V.M. Petrov, A.S. Tatarenko, Phys. Rev. B 70, 064416 (2004) 115. C.W. Nan, M. Li, X. Feng, S. Yu, Appl. Phys. Lett. 78, 2527 (2001) 116. J. Ryu, S. Priya, K. Uchino, H.E. Kim, J. Electroceram. 8, 107 (2002) 117. K. Mori, M. Wuttig, Appl. Phys. Lett. 81, 100 (2002) 118. C.W. Nan, M. Li, J.H. Huang, Phys. Rev. B 63, 144415 (2001) 119. Proc. 4th Int. Conf. Magnetoelectric Interaction Phen. Cryst. (MEIPIC-4), Ferroelectrics 282, 1 (2002) 120. M.I. Bichurin, I.A. Kornev, V.M. Petrov, A.S. Tatarenko, Y.V. Kiliba, G. Srinivasan, Phys. Rev. B 64, 094409 (2001) 121. M. Avellaneda, G. Harshe, J. Intell. Mater. Syst. Struct. 5, 501 (1994) 122. G. Srinivasan, R. Hayes, M.I. Bichurin, Solid State Comm. 128, 261 (2003) 123. Landolt-Bornstein, in Numerical Data and Functional Relationships in Science and Technology, Group III, Crystal and Solid State Physics, vol. 4(b), Magnetic and Other Properties of Oxides, ed. by K.-H. Hellwege, A.M. Hellwege (Springer, New York, 1970) 124. K.K. Patankar, R.P. Nipankar, V.L. Mathe, R.P. Mahajan, S.A. Patil, Ceramics Int. 27, 853 (2001) 125. A.P. Ramirez, J. Phys.: Condens. Matter 9, 8171 (1997) 126. G. Engdahl, Handbook of Giant Magnetostrictive Materials (Academic Press, New York, 2000) 127. C.W. Nan, J. Appl. Phys. 76, 1155 (1994) 128. M.I. Bichurin, V.M. Petrov, Ferroelectrics 162, 33 (1994) 129. J van Suchtelen, Philips Res. Rep. 27, 28 (1972) 130. J. van den Boomgard, R.A.J. Born, J. Mat. Sci. 13, 1538 (1978) 131. S. Mazumder, G.S. Bhattacharyya, Ceramics Int. 30, 389 (2004) 132. J. Ryu, A.V. Carazo, K. Uchino, H.E. Kim, Jpn. J. Appl. Phys. 40, 4948 (2001) 133. S.W. Or, N. Nersessian, G.P. Carman, J. Magn. Magn. Mater. 262, L181 (2003) 134. N. Nersessian, S.W. Or, G.P. Carman, J. Magn. Magn. Mater. 263, 101 (2003) 135. M.I. Bichurin, I.A. Kornev, V.M. Petrov, I. Lisnevskaya, Ferroelectrics 204, 289 (1997) 136. A.M.J.G. van Run, D.R. Terrell, J.H. Scholing, J. Mater. Sci. 9, 1710 (1974) 137. J. Ryu, S. Priya, A.V. Carazo, K. Uchino, H.E. Kim, J. Am. Ceram. Soc. 84, 2905 (2001) 138. J. Ryu, A.V. Carazo, K. Uchino, H-E Kim, J. Electroceramics 7, 17 (2001) 139. G. Srinivasan, C.P. DeVreugd, C.S. Flattery, V.M. Laletsin, N. Paddubnaya, Appl. Phys. Lett. 85(13), 2550 (2004) 140. N. Cai, J. Zhai, C-W. Nan, Y. Lin, Z. Shi, Phys. Rev. B 68, 224103 (2003) 141. N. Cai, C.W. Nan, J. Zhai, Y. Lin, Appl. Phys. Lett. 84, 18 (2004) 142. N. Nersessian, S.W. Or, G.P. Carman, IEEE Trans. Magn. 40(4), 2646 (2004) 143. S. Dong, J. Li, D. Viehland, J. Appl. Phys. 95(5), 2625 (2004) 144. S.W. Or, N. Nersessian, G.P. Carman, IEEE Trans. Magn. 40, 1 (2004)

References

69

145. H. Schmid, Int. J. Magn. 4, 337 (1973) 146. J. van den Boomgard, A.M.J.G. van Run, J. van Suchtelen, Ferroelectrics 14, 727 (1976) 147. J. van den Boomgard, D.R. Terrell, R.A.J. Born, H.F.J.I. Giller, J. Mat. Sci. 9, 1705 (1974) 148. K.-H. Chew, L.H. Ong, D.R. Tilley, Appl. Phys. Lett. 77, 2755 (2000) 149. G. Harshe, J.P. Dougherty, R.E. Newnham, Int. J. Appl. Electromagn. Mater. 4, 145 (1993) 150. L.H. Ong, J. Osman, D.R. Tilley, Phys. Rev. B 65, 134108 (2002) 151. J. Zhai, N. Cai, Z. Shi, Y. Lin, C.W. Nan, J. Appl. Phys. 95(10), 5685 (2004) 152. M.I. Bichurin, V.M. Petrov, O.V. Ryabkov, S.V. Averkin, G. Srinivasan, Phys. Rev. B 72, 060408(R) (2005) 153. M.I. Bichurin, V.M. Petrov, Y.V. Kiliba, G. Srinivasan, Phys. Rev. B 66, 134404 (2002) 154. T.R. Tilley, J.F. Scott, Phys. Rev. B 25, 3251 (1982) 155. S. Dong, J. Cheng, J.F. Li, D. Viehland, Appl. Phys. Lett. 83, 4812 (2003) 156. K.S. Chang, M. Aronova, O. Famodu, I. Takeuchi, S.E. Loﬂand, J. HattrickSimpers, H. Chang, Appl. Phys. Lett. 79(26), 4411 (2001) 157. H. Schmid et al. (ed), Ferroelectrics 161-162, 748 (1994) 158. J.F. Scott, JETP Lett. 49(4), 233 (1989) 159. M.I. Bichurin, D.A. Filippov, V.M. Petrov, V.M. Laletsin, N. Paddubnaya, G. Srinivasan, Phys. Rev. B 68, 132408 (2003) 160. G. Srinivasan, E.T. Rasmussen, R. Hayes, Phys. Rev. B 67, 014418 (2003) 161. Y.N. Venevtsev, V.V. Gagulin, Inorg. Mat. 31(7), 797 (1995) 162. P. Saintgregoire, Key Eng. Mat. 101, 237 (1995) 163. M.I. Bichurin, V.M. Petrov, G. Srinivasan, Phys. Rev. B 68, 054402 (2003) 164. G. Srinivasan, V.M. Laletsin, R. Hayes, N. Paddubnaya, E.T. Rasmussen, D.J. Fekel, Solid State Commun. 124, 373 (2002) 165. G. Harshe, J.O. Dougherty, R.E. Newnham, Int. J. Appl. Electromagn. Mater. 4, 145 (1993) 166. H. Zheng, J. Wang, S.E. Loﬂand, Z. Ma, L. Mohaddes-Ardabili, T. Zhao, L. Salamanca-Riba, S.R. Shinde, S.B. Ogale, F. Bai, D. Viehland, Y. Jia, D.G. Schlom, M. Wuttig, A. Roytburd, R. Ramesh, Science 303, 661 (2004) 167. H. Ryu, P. Murugavel, J.H. Lee, S.C. Chae, T.W. Noh, Y.S. Oh, H.J. Kim, K.H. Kim, J.H. Jang, M. Kim, C. Bae, J.-G. Park, Appl. Phys. Lett. 89, 102907 (2006) 168. I. Kanno, H. Kotera, K. Wasa, T. Matsunaga, T. Kamada, R. Takayama, J. Appl. Phys. 92, 4091 (2003) 169. P. Samarasekara, F.J. Cadieu, Jpn. J. Appl. Phys. 40(1), 3176 (2001) 170. G. Srinivasan, E.T. Rasmussen, B.J. Levin, R. Hayes, Phys. Rev. B 65, 134402 (2002) 171. C.W. Nan, L. Liu, Y.H. Lin, Appl. Phys. Lett. 83, 4266 (2003) 172. G. Liu, C.W. Nan, N. Cai, Y.H. Lin, J. Appl. Phys. 95, 2660 (2004) 173. G. Harshe, PhD Thesis, The Pennsylvania University (1991) 174. C.W. Nan, G. Liu, Y.H. Lin, H. Chen, Phys. Rev. Lett. 94, 197203 (2005) 175. P. Bruno, V.K. Dugaev, Phys. Rev. B 72, 241302(R) (2005) 176. F. Zavaliche, H. Zheng, L. Mohaddes-Ardabili, S.Y. Yang, Q. Zhan, P. Shafer, E. Reilly, R. Chopdekar, Y. Jia, P. Wright, D.G. Schlom, Y. Suzuki, R. Ramesh, NanoLett. 5(9), 1793 (2005)

70

3 Combined Phenomena in Novel Materials

177. G. Liu, C.W. Nan, J. Sun, Acta Mat. 54, 917 (2006) 178. M. Fiebig, J. Phys. D: Appl. Phys. 38, R123 (2005) 179. H. Schmid, Magnetoelectric Interaction Phenomena in Crystals (Kluwer, Dordrecht, 2004) 180. T. Lonkai, D. Hohlwein, J. Ihringer, W. Prandl, Appl. Phys. A 74, S843 (2002) 181. T.K. Soboleva, Ferroelectrics 162, 287 (1994) 182. H. Schmid, Ferroelectrics 162, 317 (1994) 183. C.W. Nan, N. Cai, L. Liu, J. Zhai, Y. Ye, Y.H. Lin, J. Appl. Phys. 94(9), 5930 (2003) 184. S. Dong, J.F. Li, D. Viehland, Appl. Phys. Lett. 84(21), 4188 (2004) 185. S. Dong, J.F. Li, D. Viehland, J. Appl. Phys. 96(6), 3382 (2004) 186. S. Dong, F. Bai, J.F. Li, D. Viehland, IEEE Trans. Ultrason. Ferroelectr. Freq. Control 50, 10 (2003) 187. G. Busatto, R.L. Capruccia, F. Ianmuzzo, F. Velardi, R. Roncella, Microelectron. Reliab. 43, 577 (2003) 188. K. Senapati, S. Chakrabati, L.K. Sahoo, R.C. Budhani, Rev. Sci. Instrum. 75(1), 141 (2004) 189. G.A. Smolenskii, A.I. Agranovskaya, V.A. Isupov, Sov. Phys. – Solid State 1, 149 (1959) 190. G.A. Smolenskii, I.E. Chupis, Sov. Phys. – Usp. 25, 475 (1982) 191. C. Ederer, N.A. Spaldin, Nat. Mater. 3, 849 (2004) 192. Y. Tomioka, A. Asamitsu, H. Kuwahara, Y. Morimoto, Y. Tokura, Phys. Rev. B 53, R1689 (1996) 193. M. Fiebig, Th. Lottermoser, M.K. Kneip, M. Bayer, J. Appl. Phys. 99, 08E302 (2006) 194. V.K. Babbar, R.K. Puri, J. Appl. Phys. 79, 6515 (1996) 195. H. Schmid, Bull. Mater. Sci. 17, 1411 (1994) 196. V. Janovec, L.A. Shuvalov, in Magnetoelectric Interaction Phenomena in Crystals, ed. by A.J. Freeman, H. Schmid (Gordon and Breach, London, 1975) 197. S.M. Skinner, IEEE Trans. Parts, Mater. Packaging 6, 68 (1970) 198. A.V. Goltsev, R.V. Pisarev, T. Lottermoser, M. Fiebig, Phys. Rev. Lett 90, 177204 (2003) 199. D.L. Fox, J.F. Scott, J. Phys. C 10, L329 (1977) 200. T. Kimura, T. Goto, H. Shintani, K. Ishizaka, T. Arima, Y. Tokura, Nature 426, 55 (2003) 201. T. Goto, T. Kimura, G. Lawes, A.P. Ramirez, Y. Tokura, Phys. Rev. Lett. 92, 257201 (2004)

4 Magnetoresistance and Spin Valves

Summary. The prospects of uncovering spin dominated transport in structural geometries containing various combinations of magnetic metals/semiconductors/ organics have led to a separate and fast-growing research area. While signatures of an eﬀect known as giant magnetoresistance (GMR) have been seen in many cases at various temperatures, there is still a fair amount of debate about the origin of the observed results. Additionally, the term spin valve has entered mainstream while being applied liberally and interchangeably with GMR, which is strictly speaking not correct. Since magnetic sensors enjoy an increasing popularity in ultra-high density recording applications, it is worth looking at what this is all about. Considering their technological importance and to insure their appropriate employment in a device, magnetic sensors and their underlying structural geometries require an in-depth understanding of the mechanisms triggering resistance changes, as well as the role of accompanying eﬀects such as exchange bias. Not all cases seem to be valid GMR or spin valve structures, nor are all changes in electrical resistance due to spin transport, much less spin ﬁltering. What locks spins at an interface, which electrons pass and which do not are just a few questions not easily answered. For all these reasons and many more, this chapter undertakes to examine closer some of the challenging phenomena that take place in those devices accountable for one of the innovations of today’s computer culture: massive information storage.

4.1 Introduction Interesting eﬀects are unveiled when electron transport is combined with magnetoresistance, in particular when the former occurs through certain coupled multilayer structures composed of magnetic and nonmagnetic metals, semiconductors or even organic materials. Among these eﬀects is the giant magnetoresistance (GMR) for which observations date back to the late 1980s when the ﬁrst groups [1,2] of scientists to discover GMR did measurements on molecular beam epitaxy (MBE) assembled multilayers. In a varying magnetic ﬁeld, GMR structures experience changes in electrical resistance when the ﬁeld overcomes the coupling in their ferromagnetic/nonmagnetic/ferromagnetic conﬁguration.

72

4 Magnetoresistance and Spin Valves

In a more simpliﬁed view, when the applied magnetic ﬁeld reaches the coercivity of one of the ferromagnetic layers, the magnetization of that layer aligns parallel to the applied ﬁeld. The magnetoresistance of the system increases or decreases depending on the direction of magnetization in the second ferromagnetic layer. If the magnetizations in the two ferromagnetic layers are parallel to each other the resistance decreases, while the converse is true for antiparallel layers. Upon reaching the coercivity of the second ferromagnetic layer, the magnetization in that layer aligns with the applied ﬁeld as well, and the magnetoresistance of the system changes again.

4.2 A Simple Way of Quantifying Magnetoresistance Magnetoresistance (MR) is deﬁned as MR =

R(0) − R(H) × 100%, R(0)

where R(0) is the resistance at zero magnetic ﬁeld and R(H) is the resistance at a magnetic ﬁeld value H. Depending on the shape of the magnetoresistance curve, the system is said to have positive magnetoresistance (i.e., “holds water”) or in the converse case, negative magnetoresistance. In the 1988 experiment of Baibich et al. [1], the multilayer structures (∼30 layers or more) were formed from (001)Fe/(001)Cr superlattices on (001) GaAs substrates. The same type of ferromagnet existed on both sides of the Cr spacer, and yet GMR was observed. Furthermore, the highest GMR (∼two times resistivity decrease at 4.2 K) was seen in structures with Cr layers only 9 ˚ A thin. Previously, it had been established that (100)Fe/Cr/Fe structures are antiferromagnetically coupled for Cr layer thicknesses of 9 ˚ A, displaying antiparallel magnetizations even in zero ﬁeld [3]. The fact that GMR is observed for these thin Cr layers is due precisely to this antiferromagnetic coupling between adjacent Fe layers that occurs at Cr layer thicknesses below 30 ˚ A. Nevertheless, there is a limit for how thin these spacer layers can be before oscillatory interlayer exchange coupling sets in and reduces the GMR response [4]. Remarkably, in the Baibich et al. [1] experiment the GMR eﬀect was still observable at room temperature.

4.3 What is Responsible for GMR? Baibich et al. [1] recognized that spin-dependent transmission of conduction electrons between Fe layers through the thin Cr layers is responsible for GMR, and that the orientation of the magnetization in the Fe layers with respect to the external ﬁeld plays a role in obtaining GMR. The concept that spin scattering by interface roughness has a noteworthy inﬂuence on magnetoresistance with diﬀerences in scattering for “spin-up” or “spin-down” electrons was discussed in 1988, acknowledging agreement with earlier experiments [5]. Having a paramagnetic layer with the thickness of a few lattice spacings between

4.5 “Spin-down” vs. “Spin-up” Scattering: Magnetic Impurities

73

two ferromagnetic layers can result in antiferromagnetic behavior of the overall system [6]. Early on [7], IBM introduced a design for GMR sensors in magnetic disk drives consisting of an “artiﬁcial” antiferromagnetic structure comprising two ferromagnetic layers antiferromagnetically coupled by means of a Ru layer of only ∼3 ˚ A. Because of its thinness, the Ru layer displayed a relatively high interlayer oscillatory exchange energy. Although it ensured a strong exchange coupling, it required a magnetic ﬁeld of many Tesla to overcome the antiferromagnetic coupling [7].

4.4 Deskstar 16 GP Multilayer GMR sensors were introduced commercially by IBM in November 1997 as magnetic recording read heads in disk drive products designated [8] Deskstar 16 GP. By using these read heads, extremely small magnetic bits at an areal density of 2.69 Gb in−2 could be read. In the initial design of GMR sensors, the current ﬂowed parallel to the layers in the device in a currentin-plane (CIP) geometry requiring the sensor to be electrically insulated from the conducting magnetic shields [9]. This would not have been so undesirable if the insulation between the shields would not have occupied space, thereby limiting the recording density of the sensors. When determining the capacity of these early hard disk drives not only the areal density needs to be taken into account, but also the size and number of disks or platters within the drive. Deskstar 16 GP contained 95-mm-diameter disks, each with a storage capacity of more than 3.2 GB, resulting in a total data storage capacity [10] of 16.8 GB.

4.5 “Spin-down” vs. “Spin-up” Scattering: Magnetic Impurities A magnetic material for which the conductivity depends on spin orientation is likely to contribute to magnetoresistance eﬀects, due to the lower resistivity experienced by one of the spin components. In GMR structures built with these materials, the magnetization vectors in the layers have to be ferromagnetically aligned at some point, so that the spin component with the preferred spin polarization can pass through the layers. Furthermore, impurities need to be present at the interfaces, as they are considered responsible for asymmetric spin scattering [11]. For instance, it was observed that changes in magnetoresistance due to “spin-down” → “spin-down” scattering in Cr impurities in bulk Fe are roughly six times smaller than for “spin-up” → “spin-up” scattering. Because the Fe layers are considerably thicker than the Cr layers, the Cr atoms in the layer of only three lattice constant thickness can be regarded as Cr impurities in bulk Fe. This implies a weak interface scattering and a high transmission for the “spin-down” electrons carrying current with a low

74

4 Magnetoresistance and Spin Valves

resistivity. At zero ﬁeld, both Cr and Fe atoms (of the layer with antiparallel magnetization) correspond to scattering centers for the mixed “spin-up” and “spin-down” electrons, reducing transmission of electrons through the layers [1]. Similar concepts were introduced also in 1988 by Johnson and Silsbee for spin injection from a ferromagnet [12]. Additionally, theoretical calculations based on the Boltzmann transport equation validated that (Mn, V) impurities achieve comparable scattering eﬀects to Cr impurities in Fe, whereas (Al, Ir) impurities lead to a rapid degradation of GMR [13]. Further experiments in which ultrathin layers of a variety of third elements (V, Mn, Ge, Ir, Al) were deposited between Fe and Cr layers conﬁrmed the importance of spin dependent scattering from impurities at the interfaces [14]. A parameter α = ρ↓ /ρ↑ = 1 meant to measure the asymmetry in spin transport through the interface was used for comparison between samples containing diﬀerent elements. The resistivity ρ corresponded to “spin-down” and “spin-up” electrons, where the arrows were used to distinguish between the two orientations. It was found that a correlation existed between α and the magnitude of the GMR response [15].

4.6 Fabrication of GMR Multilayers: Thin Films and Nanostructures After 1988, multilayer experiments started to ﬂourish and researchers observed increased GMR values, partly due to other fabrication methods employed for these structures such as magnetron sputtering [16]. In a 1996 experiment [17], a cluster beam deposition process [18] was used to produce high quality Fe/Cu granular ﬁlms whose GMR was compared to those obtained by a conventional co-evaporation method. The process of cluster beam deposition entails the formation of small metallic clusters by adiabatic expansion of vaporized atoms through a crucible’s nozzle in vacuum. An electron beam ionizes the clusters, and a bias voltage is applied between the source and the substrate to propel the clusters onto the substrate while enhancing surface migration of adatoms. To preserve the clusters, an alternative method involves deposition of neutral clusters that are softly landed without ionization or acceleration [17]. In any case, the granular nature of the clusters led to suppressed GMR values, as opposed to the chemically and magnetically homogeneous co-evaporated ﬁlms. This was because GMR is highly sensitive to nanoscale heterogeneity, and the magnetic state at the interface between the clusters and the host matrix. Easier magnetization switching, and hence enhanced GMR values have been reported [19] for magnetic layers that are magnetically textured displaying a preferred direction of magnetization. This is the case for layers containing nanowire arrays where the strong shape anisotropy of the latter has proved to be advantageous. It was observed [19] that multilayered

4.8 The Role of Exchange Bias

75

ﬁlms of Fe/Ni80 Fe20 /Co/Cu/Co with a nanowire arrangement display larger GMR values than similar ﬁlms without nanowires. The researchers attributed this improved response to the shape-induced easy axis of magnetization that allowed straightforward switching of magnetic moments without signiﬁcant hindrance from the domain structure.

4.7 Spin Valves The actual variation in magnetoresistance occurs when the ﬁeld changes the relative orientations of magnetizations in two adjacent magnetic regions. While these magnetizations are parallel to each other pointing in a common direction, electrons with spins oriented in the same direction (for instance, “spin-down”) pass easily from one layer to another. Electrons with antiparallel spins (for instance, “spin-up”) are strongly scattered, leading to low resistivity for electrons with parallel spins. On the other hand, if adjacent regions have antiparallel magnetizations, both “spin-down” and “spin-up” electrons are strongly scattered, and the resistivity is high for all electrons. This spinﬁltering property [20] has led to the term spin valve. A spin valve structure can encompass many layers, however the latter can be divided into three possible categories: (1) a soft ferromagnet, appropriately called a free layer due to the ease with which the direction of magnetization can be changed; (2) a spacer layer, usually a paramagnet; and (3) a hard ferromagnet consisting of a pinned layer exchange coupled [21] to an antiferromagnetic pinning layer, often formed by three layers [22]. Exchange coupling implies that the exchange interaction between magnetic moments is such that the magnetization within the pinned layer cannot change directions easily [23]. The eﬀect was ﬁrst documented [24] in the 1950s, and has been used in the magnetic recording industry for stabilizing the magnetization within the sensing layer with one of the goals being that of reducing [25] Barkhausen noise.

4.8 The Role of Exchange Bias Research [26,27] indicates that the exchange bias eﬀect originates from uncompensated interfacial spins locked in the antiferromagnet. Thus, the hysteresis loop of the antiferromagnetic layer is asymmetrical, also said to be shifted horizontally [28]. The spins are therefore “pinned,” and do not follow the external ﬁeld [29]. Speciﬁcally, when the bilayer formed by the ferromagnetic and antiferromagnetic layers is cooled below the ordering temperature of the latter, the spins in the antiferromagnetic layer are blocked in antiferromagnetic domains with uncompensated net moments in the direction of the ferromagnetic layer, giving rise to a net magnetic bias ﬁeld [30].

76

4 Magnetoresistance and Spin Valves

Studies performed on NiO/Co, IrMn/Co, and PtMn/Co90 Fe10 using high sensitivity X-ray magnetic circular dichroism spectroscopy in total electron yield detection identiﬁed uncompensated Ni or Mn spins located at the antiferromagnetic–ferromagnetic interfaces [31]. The 1/e probing depth makes this method responsive to the interfacial surface [32]. By measuring the Ni or Co hysteresis loops, the team [31] was able to identify that roughly only 4% of the ferromagnetic monolayer is tightly pinned to the antiferromagnet, therefore not rotating in an external ﬁeld. Furthermore, they found that there is a quantitative correlation between the size of the pinned interfacial magnetization and the macroscopic magnetic exchange bias ﬁeld.

4.9 Ni–Fe Alloys Generally, Ni–Fe alloys are weak magnetoresistive at room temperature, therefore their study requires low temperatures and ﬁelds in excess of 20 kOe. These conditions are disadvantageous in the magnetic recording industry, as it is desirable to have magnetic sensors that detect small ﬁelds at room temperature. With the invention of electroplating baths and improved fabrication processes for the heads at IBM, a plated inductive permalloy head [33] was employed in the early days of magnetic recording. This electroplated permalloy was the only selected material for this purpose, as it could meet the strict requirements for both reading and writing processes. With a saturation ﬂux density [34] of 1 T, negligible magnetostriction and corrosion resistance, it was easily plated into ﬁlms. Its soft magnetic properties made it employable as both read and write element [35]. As the areal density of drives increased, Ni45 Fe55 started to gain ground. Although its soft magnetic properties were not as good as in permalloy, the increased magnetic moment due to the higher Fe content allowed writing in higher coercivity media. The fact that the magnetic moment for binary NiFe alloys increases monotonically with Fe content up to a composition [34] of 65% Fe, and the better corrosion properties than Co-based high moment alloys led to further exploration of this Ni–Fe alloy. However, trying to optimize the material to improve the writeability process was deteriorating readability, and vice versa. This is because inductive writing usually requires a better magnetic anisotropy, a smaller coercivity and a very low magnetostriction. The problem was solved with the introduction of the magnetoresistive read sensor [36] that was used in conjunction with the inductive write head [37], but with a physical separation between the writer and reader. Once the physical separation between the processes became possible permitting individual optimization of writing and reading, the soft magnetic property requirements of the inductive writer material became less stringent. The head design was improved to handle the positive magnetostriction. After much work leading to serious improvements, Ni45 Fe55 was accepted as a standard in the thin ﬁlm head industry after permalloy [38].

4.11 Ni–Fe Alloys with Higher Fe Content

77

4.10 Ternary Alloys To achieve increased recording densities, higher magnetic moments were needed. Soft magnetic ternary alloys such as CoFeCu with high cobalt content (>75%), low magnetostriction, reduced internal stress and saturation ﬂux densities as high as 2 T were developed by IBM to be used as write heads [39], following permalloy and Ni45 Fe55 . Adding Cu reduced the Barkhausen noise, reﬁned the grain size improving domain conﬁguration, and broadened the range of compositions for which the coercivity is low. Deposition of CoFeCu ternary alloys with uniform composition from a bath containing a reduced concentration of a diﬀusion-controlled element such as Cu posed challenges during the fabrication process. Adding to the problematic fabrication conditions, the weak corrosion resistance made CoFeCu ternary alloys impracticable in magnetic recording. Furthermore, they did not display a visible advantage over Ni45 Fe55 in terms of head performance, therefore they were not implemented in magnetic recording. Preferably, a magnetic recording head should have a high moment, low coercivity, no magnetostriction, large electrical resistance, no internal stress and high corrosion resistance. None of this is achievable in one single material, and compromises need to be made. IBM considered other soft magnetic ternary alloys such as CoNiFe instead of [40] CoFeCu. When electrodeposited galvanostatically from a sulfate/chloride bath similar to the plating bath used for the fabrication of Ni45 Fe55 , the CoNiFe ﬁlms displayed a magnetic ﬂux density higher than 2 T. More than 250 alloy compositions were obtained by changing the Ni2+ , Fe2+ , and Co2+ concentrations and varying the current density for a given bath composition. However, this CoNiFe plating system was not consistently reproducible in the high moment region of the ternary diagram. More reliable data were obtained for samples with compositions around Co44 Ni27 Fe29 displaying a slightly lower magnetic ﬂux density (∼2 T), a coercivity of 1.2 Oe, and a low internal stress (115 MPa). Most samples underwent thermal annealing treatments without damage to their structure [40].

4.11 Ni–Fe Alloys with Higher Fe Content IBM reexamined higher-iron NiFe binary alloys [41]. Magnetic properties of bulk alloys diﬀer from their electrodeposited counterparts, especially if annealed at high temperatures. Therefore, electrodeposition of NiFe with compositions ranging from Ni35 Fe65 to Ni15 Fe85 was performed in sulfate/chloride baths containing boric acid, saccharin, and a surfactant in magnetic ﬁelds of ∼800 Oe, at temperatures varying between 15 and 30◦ C according to a patented recipe [42]. Thermal annealing followed at 225◦ C for 8 h. As a result [43], the ﬁlms displayed higher values of internal stress and magnetostriction than CoFeNi, nevertheless they were more corrosion resistant and easier to manufacture.

78

4 Magnetoresistance and Spin Valves

Following further investigations, Ni32 Fe68 and Ni20 Fe80 with saturation ﬂux densities of 2 T and 2.2 T, respectively, were adopted [44] by IBM who also investigated the CoFe group of iron alloys. The latter were plated in a galvanostatic bath with a proprietary additive that led to magnetic ﬂux densities of 2.4 T for a 50–70 wt% Fe composition [45]. During the process, bath composition and plating conditions were optimized by investigating the eﬀect of the bath components on the surface pH during plating, as well as current density [46]. These plated alloys with such a high magnetic ﬂux density exhibited a large positive magnetostriction (+45 ppm) and high internal stresses of up to [47] 850 MPa. From permalloy to CoFe alloys, IBM brought signiﬁcant improvements to magnetic recording heads by developing innovative methods of electrodepositing soft magnetic alloys with magnetic ﬂux densities from 1 to 2.4 T.

4.12 Basic Principles of Storing Information Magnetically In magnetic recording, information is stored as magnetized regions within thin magnetic layers that have been deposited on glass or aluminum substrates. The ﬂux emanating from the transitions between magnetized regions is detected by a magnetic read head (Fig. 4.1). The strength of the magnetic ﬁeld at the read head is only a few tenths of Oe, therefore GMR sensors capable of detecting such small ﬁelds are important for hard disk drive read head applications [48]. To ensure sensitivity to small magnetic ﬁelds, one of the ferromagnets in the GMR structure is magnetically hardened, such that its magnetization is ﬁxed and will not rotate while in the range of ﬁelds it is subjected to. Hardening can be achieved by coupling that ferromagnetic layer to a thin antiferromagnetic layer via exchange biasing, as mentioned earlier. If the layer is pinned, it has a shifted hysteresis loop, due to the exchange bias of the adjacent antiferromagnetic layer. In contrast, the hysteresis loop of the free layer is centered, displaying reduced coercivity. In the end, the strength of the exchange coupling in the reading head needs to be such that the soft ferromagnetic layer can still rotate its magnetization in the presence of a magnetic ﬁeld, as given for instance by the transition regions in the magnetic tape. As a result, only the free layer magnetization is switched in the low ﬁelds created by the bit transitions previously written on the magnetic disk. When the magnetizations of the pinned and free layer change direction from parallel to antiparallel, the magnetoresistance increases due to increased spindependent scattering. These changes in magnetoresistance are used to detect transitions between magnetic bits, allowing recovery of stored magnetic data. The spacer layer thickness of the free layer in spin valves having for instance Co90 Fe10 /Cu/Co90 Fe10 pinned/spacer/free layer structures has a

4.12 Basic Principles of Storing Information Magnetically

79

Fig. 4.1. Basic principles of magnetic recording. (a) Information is stored as magnetized regions within thin magnetic layers. The ﬂux emanating from the transitions is detected by a magnetic read head while the disk is rotating underneath. The read element scales down in size with the area of the magnetized regions. (b) The read sensor is part of a read/write head mounted on a ceramic slider that is ﬂown above a rapidly spinning disk. The hard drive unit typically contains a stack of several head-disk assemblies plus control electronics (reprinted from [48] (copyright 2003) with permission from the IEEE)

noteworthy impact on the interlayer coupling ﬁelds [49]. This is because coupling ﬁelds depend on the shape of the Fermi surface of the spacer layer, as well as the degree of conﬁnement of the magnetic carriers in the spacer quantum well. In the weak conﬁning system Co90 Fe10 /Cu/Co90 Fe10 pinned/spacer/free layer, the minority spin electrons in the spacer layer are conﬁned close to the

80

4 Magnetoresistance and Spin Valves

top of a ﬁnite quantum well, inﬂuencing considerably the temperature dependence of the oscillatory interlayer coupling constant. Particularly, for PtMnpinned Co90 Fe10 layers, Maat [49] et al. found two coupling mechanisms to contribute to the coupling ﬁeld: the magnetostatic N´eel coupling originating from the correlated roughness at the Co90 Fe10 /Cu and Cu/Co90 Fe10 interfaces, and the oscillatory interlayer coupling.

4.13 Materials for spin valve Sensors On the basis of various complexities displayed by prototype materials incorporated into magnetic read heads, IBM and later Hitachi GST investigated a variety of materials and material combinations for their suitability as layers part of the their spin-valve sensors. Among these, cobalt ferrite CoFe2 O4 thin ﬁlms were under consideration as exchange-spring pinning layers [50]. Their magnetic properties are highly dependent on their microstructure which is determined by the fabrication process, in this case, reactive sputtering from a CoFe2 target. Oxide pinning layers are preferred due to their increased corrosion resistance. Although other oxide materials have been considered, such as α-Fe2 O3 [51], rare earth orthoferrites [52], and Nix Co1−x O [53], it is still CoFe2 O4 that has the highest anisotropy constant. Furthermore, orthoferrites are not easily manufactured at room temperature and α-Fe2 O3 requires thick layers before suﬃcient pinning is achieved, not to mention they display a low exchange ﬁeld. For the spin valve with the CoFe2 O4 pinning layer [54], changes in magnetoresistance of 12.8% and pinning ﬁelds of 1,500 Oe have been observed, while the soft magnetic properties of the free layer were maintained. As expected, the spin valve formed of glass/CoFe2 O4 /Co/Cu/Co/NiFe/Ru layers displays asymmetric hysteresis loops, as the cobalt ferrite layer is not fully reversed. This is similar to PtMn or NiMn pinning layers, where the coercivity is approximately half of the pinning ﬁeld value and the CoFe2 O4 /Co acts like an exchange spring magnet with saturation ﬁelds for CoFe2 O4 exceeding 15 kOe. Nevertheless, the loops become symmetric again for cycles of ±18 kOe, when the CoFe2 O4 layer experiences full magnetization reversal [54]. If the pinned layer has a too high coercivity it can be hysteretic at moderate ﬁelds, and therefore easily demagnetized after several cycles. Additionally, the interactions between the free and pinned layer can render a too high free layer coercivity. Cobalt ferrite spin valves seem to evade these diﬃculties, as the pinned layer displays no hysteresis, and the coercivity of the pinned layer is similar to the one of antiferromagnetically pinned spin valves. Further improvements can be made by adding an insulating cobalt oxide (CoO or Co3 O4 ) underlayer that pins without shunting current. Aside from its electric insulating properties, this underlayer provides a template for better crystalline growth, maintaining a higher coercivity and thermal stability. Also, free layer properties are preserved, comparable to PtMn based sensors

4.14 The Need for Proper Sensor Design

81

of similar thickness. The insulating layer can be made part of the insulating gap, reducing the thickness of the cobalt ferrite layer to only [55] ∼3 nm. Although the total cobalt oxide/cobalt ferrite thickness is ∼17 nm, it is still under the 40 nm thickness of cobalt ferrite layers that is usually stable. Thus, the spin valve can ﬁt into a 50 nm gap, as required for recording densities of >100 Gbit in−2 .

4.14 The Need for Proper Sensor Design CoFe2 O4 ﬁlms have a more homogeneous magnetic structure, as compared to hard magnetic materials such as CoPtCr that have a high magnetic anisotropy. The latter apparently leads to fringing ﬁelds aﬀecting the free layer, thereby increasing its coercivity. Nevertheless, further studies of CoPt18 hard magnet pinning layers (50 ˚ A) on Cr seed layers (>20 ˚ A) fabricated by the IBM team [56], later under Hitachi GST found that free layer softness is not compromised after all if the spacer layer is relatively thick. That, and the reduced critical thickness of the CoPt pinning layer renders the latter a viable alternative to IrMn or PtMn antiferromagnets for small gap sensors in high density magnetic recording. PtMn needs a minimum thickness of 150 ˚ A to become antiferromagnetically ordered upon annealing, while minimum 80 ˚ A are required for IrMn to obtain optimum exchange bias. The CoPt layers are deposited at room temperature by dc magnetron sputtering in an argon pressure of 2 mTorr using two separate Co and Pt targets. Composition changes are obtained by varying the sputtering power of the Pt source. After using vibrating sample magnetometry and magneto-optical polar Kerr rotation in magnetic ﬁeld scans up to ±18 kOe, the CoPt magnetization was found to be in-plane, while there was no out-of-plane remanence observed. Furthermore, the in-plane hysteresis loops are alike in any in-plane direction, indicating that the ﬁlm is magnetically isotropic in plane. For pinning applications in spin valves it is required for the magnetic moment of the CoPt pinning layer to balance the magnetic moment of the reference layer, CoFe. In this study, it was found that the moment of 50 ˚ A of CoPt18 equals the moment of ∼38 ˚ A of CoFe10 . The coercivity and coupling ﬁeld values of the free soft layer were measured at 5–10 Oe, and the coercivity of the CoPt18 layers was found to be ∼1.5 kOe for Pt concentrations 16–22 at.%. The resistivity was measured at only 31 µΩ cm, implying a low parasitic resistance, which is especially important since a pinning layer does not usually contribute to GMR, but rather decreases the overall signal. Its resistance can be similar or greater than the total resistance of the actual spin valve structure. PtMn resistivities between 193 and 227 µΩ cm were recorded, actual values dependent on annealing conditions. Similar resistivity values were obtained [56] for IrMn, 150–162 µΩ cm. In related investigations by Maat et al. [57] ultrastrong Ir-coupled antiparallel self-pinned layers were used for the stabilization of the thick reference

82

4 Magnetoresistance and Spin Valves

layer. High coupling constants had been previously measured in Ir-coupled layers [58]. The extremely high coupling energies >3 ergs cm−2 permit increased layer thicknesses to >100 ˚ A for both pinned and reference layers. The antiparallel pinned structure was balanced in terms of magnetic moments, and high saturation ﬁelds were maintained, as required for the stability of the read sensor. The strong coupling was retained even when patterned into nanopillars of 50–200 nm. However, the Ir-coupled spin valves do not display thermal stability, as observed after annealing for 4 h at 255◦ C.

4.15 Magnetic Tunnel Junctions Magnetic tunnel junctions (MTJ) have been considered for magnetic recording due to some similarities to spin valve devices. While the sense current is passed not in plane, but perpendicularly through the device, the spacer layer is replaced by a very thin insulating tunnel barrier. Tunneling magnetoresistance responses as high as 50% at room temperature have been reported in devices with alumina tunnel barriers [59]. An anisotropic magnetoresistance arises when the magnetization throughout the device is rotated uniformly so as to change the angle between the direction of current ﬂow and the magnetic moment. The anisotropic magnetoresistance increases signiﬁcantly when the contact cross section is narrowed to nanoscale, where the point contacts enter the tunneling regime. The magnetic moments of the two contacts rotate together, while remaining parallel to each other [60].

4.16 Anisotropic Magnetoresistive Sensors Artifacts can arise in MTJs due to magnetostriction eﬀects and magnetostatic forces that can alter the geometry of nanoscale junctions as the magnetic ﬁeld is varied [61]. These challenges can be overcome by ﬁrmly attaching the contacts to a nonmagnetic silicon substrate and performing measurements exclusively at low temperatures, to suppress thermally driven surface diﬀusion of metal atoms [62]. Nevertheless from a fabrication perspective, a perpendicular current ﬂow is an advantage in magnetic recording, because the sensor can be directly attached to the magnetic shields that can also be used as electrical contacts. Prior to GMR read heads, the magnetic recording industry employed anisotropic magnetoresistive sensors made of two thick, soft magnetic layers shielding a sensing layer in the middle [63]. The spatial resolution of the anisotropic magnetoresistive read head was determined by the thickness of the sensing layer and the separation of the two shields, leading to predictions of maximum areal densities of only ∼5 Gb in−2 [48]. The anisotropic magnetoresistive heads achieved a low performance of merely a few percent variation in magnetoresistance at room temperature. This was due to the fact that anisotropic magnetoresistance is attributed

4.18 GMR Sensors with CPP Geometry

83

to bulk scattering within a ferromagnetic metal, with changes in resistance strongly dependent on the angle between an applied external ﬁeld and the direction of current ﬂow. On the other hand, GMR is predominantly inﬂuenced by interface scattering, therefore leading to responses of 65% (at 295 K) and 115% (at 4.2 K) in Co/Cu multilayers in the early [64] 1990s. In some instances, bulk scattering can inﬂuence GMR due to the existence of spinindependent imperfections such as lattice distortions, structural disorders or heterogeneity of the material, aﬀecting the mean free path and causing resistance variations under an applied magnetic ﬁeld even at low temperatures [65]. In particular, ferromagnetic alloys containing permalloy display a random distribution of magnetic atoms causing spin-dependent bulk scattering [66, 67]. However, the latter has a relatively small impact [68] on GMR, as compared to spin-dependent interface scattering.

4.17 Extraordinary Magnetoresistance In some experimental devices based on a diﬀerent type of magnetoresistance eﬀect, the so-called extraordinary magnetoresistance (EMR), some problems due to the in-plane ﬁeld sensitivity are avoided, as the geometry of EMR results in sensitivity to magnetic ﬁelds perpendicular to the wafer plane. The EMR is modulated by the Lorentz force that acts on the electrons that form a current between two adjacent conduction channels formed by a high mobility semiconductor bar and a low-resistance metallic shunt, both nonmagnetic. EMR devices may be taken into consideration for sensors integrated into planar recording head conﬁgurations [69].

4.18 GMR Sensors with CPP Geometry Meanwhile, GMR sensors with current-perpendicular-to-plane (CPP) geometry are used in the magnetic recording industry. In these, the current travels between the two magnetic shields (Fig. 4.2) perpendicular to the plane of the layers in the spin valve, parallel to the air-bearing surface of the sensor [70]. The spacing between the two shields determines the downtrack resolution of the recorded bits. The overall width of the sensor is responsible for the crosstrack resolution, while the sensor height needs to scale with the track width for good magnetic stability [71]. Increases in GMR can be achieved by partially oxidizing layers within the structure [71,72]. The total sensor electrical resistance is usually kept low to ∼100 Ω, allowing a high sensor bandwidth and a high signal-to-noise ratio. The CPP sensor resistance is characterized by the product: sensor electrical resistance × track width × sensor height (in Ω µm2 ), which needs to be kept low. For instance, serial product resistance values (due to the antiferromagnet and excluding underlayers) of only 34 Ω µm2 for a PtMn-pinned spin valve, and 13 Ω µm2 for an IrMn-pinned spin valve

84

4 Magnetoresistance and Spin Valves

Shield 2 Hard bias

Hard bias

Insulator

Insulator 40 nm

Shield 1

Fig. 4.2. Air-bearing surface view in an SEM micrograph of an all-metal CPP-GMR head with 40 nm reader width (reprinted from [70] (copyright 2006) with permission from the IEEE)

have been obtained [56]. This low product makes CPP GMR sensors more compatible with high density recording heads than MTJ devices that display a too high resistance to be employed in high data rate disk drives [73]. However, parasitic resistance from underlayers, antiferromagnets, cap layers, and other inactive layers reduce the measured GMR.

4.19 Dual Spin Valves To improve GMR sensor performance, Childress et al. [70, 74] from Hitachi GST investigated a dual spin valve composed of a multilayer stack: underlayer/IrMn[pinned layer/Ru/reference layer]Cu/free layer/Cu/[reference layer/Ru/pinned layer]IrMn/cap (Fig. 4.3)). Thin IrMn (6–7 nm) are preferred to thicker (13–15 nm) PtMn layers, due to the requirement of reduced stack height that inﬂuences the head resolution along the recorded track through the total read gap. The Ru layer facilitated the antiferromagnetic coupling between the pinned layer and the reference layer, creating the actual spin valve, and minimizing the magnetostatic coupling to the free layer. Having a dual spin valve represents a challenge from a magnetic perspective, as the stability of the sensor depends signiﬁcantly on having the top and bottom pinned layers well pinned. Nevertheless, some diﬀerence in pinning strength is expected for the top and bottom pinning layers because of growth conditions, crystallographic and magnetic texture development, and roughness eﬀects. The ﬁlms were deposited by dc magnetron sputtering onto Si and glass wafers at room temperature [74] or alternatively, on a chemically mechanically polished NiFe shield surface that had been previously electrodeposited onto alumina-TiC substrates [70]. In the latter case, the ﬁlms were annealed for 5 h at 245◦ C, then cooled in a 13 kOe magnetic ﬁeld to set the pinning direction in IrMn. The total stack height of the sensor was kept just

4.20 Some GMR Multilayer Material Combinations

85

Cap layers

IrMn 70Å PLtop RLtop FL RLbot PLbot

See text Ru 8Å See text Cu 35Å CoFe166Å NiFe1625Å CoFe166Å Cu 35Å

Dual

See text Ru 8Å CoFe1630Å

Single

IrMn 80Å Underlayers

Fig. 4.3. Multilayer stack for single and dual spin valves. The single spin valves are obtained by terminating the structure with a cap after the free layer FL (reprinted from [74] (copyright 2006) with permission from the American Institute of Physics)

under 50 nm [70]. The free layer coercivity of ∼9 Oe and the high coupling ﬁeld of 45 Oe obtained for the dual spin valve design indicated suitability for magnetic recording [74]. Furthermore, this design resulted in stabilized transfer curves in applied ﬁelds of ±500 Oe, lower spin torque-induced noise, reduced parasitic resistance and higher GMR values, making them promising candidates for ultra-high density head sensors for recording applications at >300 Gbit in−2 .

4.20 Some GMR Multilayer Material Combinations Ferromagnetic Co layers separated by thin Cu layers were noticed to exhibit GMR of over 110% even at room temperature, compared to only 80% displayed by Fe/Cr structures [75]. Generally, GMR can be observed in a variety of transition metal magnetic multilayers, while the eﬀect ﬂuctuates as the thickness of the spacer layer is varied. Additionally, the shape of the magnetoresistance curve changes with spacer layer thickness [76], as well as due to the fact that the resistance of these materials is strongly temperature dependent. Nevertheless, diﬀerent thicknesses cause the interlayer exchange coupling to alternate between antiferromagnetic and ferromagnetic, such that the magnetizations of successive ferromagnetic layers are either parallel or antiparallel. Only antiferromagnetic coupling leads to noteworthy GMR [77]. Subtle structural modiﬁcations of magnetic layers can also result in considerably altered properties and ultimately no GMR or enhanced GMR response [78]. In some cases, changes in the magnetic phase can be obtained using light, such as in [79] (Cd,Mn)Te/(Cd,Zn,Mg)Te or [80] (In,Mn)As/(Al,Ga)Sb. To obtain GMR, the electrical resistance needs to be signiﬁcantly reduced by a magnetic ﬁeld that induces parallel magnetization alignment in multilayers

86

4 Magnetoresistance and Spin Valves

that would otherwise contain randomly oriented magnetization vectors or be spontaneously antiferromagnetic. It was observed that in layered structures of permalloy and Cu, the intermixing of the two at the interface reduces GMR [81]. On the other hand, an inverse GMR eﬀect was detected in Fe/Cu and Cr multilayer structures [82], with thin Cr layers intercalated into Fe.

4.21 Ferromagnetic/Nonmagnetic Interfaces Spin-dependent conductivity in GMR multilayers is signiﬁcantly inﬂuenced by scattering at the interfaces between ferromagnetic and nonmagnetic layers, as predicted by ab initio calculations based on spin-dependent energy bands [83], and through a variety of experiments. This fact is not surprising given the dissipative nature of an eﬀect based on selective passage for one spin component of the electronic current density. Less scattering and therefore less dissipation of energy occurs when the magnetization vectors of the layers are aligned, allowing the favored spin component to carry electric current with lower resistivity, shunting out the more strongly scattered component. Additionally, magnetoresistance is always reduced by spin-ﬂip scattering of both “spin-down” and “spin-up” electrons. For the spin-carrying electron to make it through a layer without spin-ﬂip scattering, the thickness of the layer must be smaller than the mean free path for spin-ﬂip. Demagnetizing ﬁelds associated with the magnetic moments of the ferromagnetic layers become more signiﬁcant as the volume is increased, fact that adds to the necessity of keeping the layers thin. However, progressive reduction of size for the devices containing such ferromagnetic layers increases the magnetic ﬁeld requirements for changing their magnetic state. This will eventually limit the smallest ﬁelds that can be detected with these devices, as well as the packing density of neighboring devices.

4.22 The Nonmagnetic Spacer The oscillation of the GMR eﬀect is usually observed in systems where the spacer layer is a nonmagnetic 3d, 4d, or 5d transition metal. Electrons are the principal charge carriers in transition metals, and according to Mott’s model [84] conduction is not by d electrons, but rather due to transitions into empty d states at the Fermi level. The high density of states and low d electron velocity make it easier for the highly mobile valence sp electrons to make the transition. The eﬀective masses of sp electrons are small compared to d electrons, resulting in a current primarily due to valence sp electrons. In Fe the d band is exchange split, making the density of states diﬀerent for “spin-up” and “spin-down” electrons at the Fermi level. In contrast to ferromagnetic Fe, in nonmagnetic Cu the d bands are fully occupied and not exchange split. The valence sp bands have low density of states and high velocity electrons,

4.24 The Magnetic Tunnel Transistor

87

resulting in a low probability of scattering and a long mean free path, making Cu a more suitable spacer layer than Fe. When the conduction electrons leave the nonmagnetic spacer layer and enter the ferromagnetic layer, they are scattered dependent on spin. Scattering in ferromagnets is spin-selective, causing the mean free path of minority spin electrons to diﬀer from that of majority spin electrons. Thus in ferromagnetic materials, two largely independent conduction channels exist, corresponding to “spin-up” and “spin-down” electrons. Because GMR is based on spin-dependent scattering of electrons at the Fermi energy, it is an eﬀect that can be exploited in spintronic devices [85].

4.23 Magnetic Tunneling Magnetic tunneling may also be a candidate for spintronic devices, as it involves the generation, manipulation and detection of spin polarized current. Spin polarization can be expressed simply as P =

n↑ − n↓ , n↑ + n↓

where n is the density of states for majority (↑) and minority (↓) spin-polarized electrons. Julli`ere [86] proposed this relationship for the magnetoresistance: MR =

2P1 P2 , P1 + P 2

where P1 and P2 are the polarizations of the two ferromagnetic layers. Clearly, the higher MR is obtained for larger spin polarizations. In practice, techniques that measure the spin polarization of the ferromagnet’s electronic states may not give results that agree, as each technique is related to the polarization in diﬀerent ways, not allowing direct comparison to each other. Although the Julli`ere model is for tunneling MR, it is often applied to GMR structures. This is because in both cases, the ferromagnetic/spacer (barrier) layer interface electronic states inﬂuence the degree of spin polarization. It should be noted in passing that, in GMR spin valves and in MTJ electron transport occurs near the Fermi level, however it is possible for electron transport to occur at much higher energies. These are the so-called hot electrons, and they are utilized in spin valve transistors made of a spin valve base with two semiconductor substrates constituting the emitter and collector.

4.24 The Magnetic Tunnel Transistor The alignment of the magnetic moments within the spin valve base determines the collector current, therefore the base is sensitive to large magnetic ﬁelds. Nevertheless, the energy of the hot electrons is limited to about 0.9 eV due

88

4 Magnetoresistance and Spin Valves

to the emitter Schottky barrier height, restricting the value of the collector current to [87] ∼20 nA. On the other hand, in the magnetic tunnel transistor the energy of the hot electrons can be adjusted by varying the bias voltage between the emitter and base across the tunnel barrier. This allows the magnetic tunnel transistor to operate over a wide energy range while obtaining high collector currents through large voltage bias [88]. The transmission of hot electrons injected into the empty states above the Fermi level is possible because of the longer attenuation lengths of majority spin hot electrons, as there is a spin dependence of the number of states available for inelastic scattering by electron–hole pair excitation [89]. Due to the nonequilibrium nature of tunneling magnetic phenomena, when the spin-polarized hot electrons are injected into the states above the Fermi level of one ferromagnetic electrode, holes are simultaneously injected into the states below the Fermi level of the counterelectrode, also by a tunneling process. The nonequilibrium holes scatter quasielastically in the ﬁrst few nanometers of the material due to spin-wave emission, while at larger depth into the layer the attenuation is dominated by inelastic scattering by electron– hole pair excitations, but with opposite spin-asymmetry. In a p-type magnetic tunnel transistor, after spin-dependent transmission through the ferromagnetic base, holes are collected in the valence band of the p-type semiconductor, provided their energy and momentum allow them to overcome the Schottky barrier [90]. For hot holes, a spin valve eﬀect of 130% and attenuation lengths as short as 0.6 nm have been reported [91].

4.25 Some Special Types of Ferromagnets Recording of information can be done using electron spin, whereas traditionally, information processing and communication rely on electron charge. The question arises whether charge and spin of electrons can both be utilized at the same time to broaden device applications. Nonmagnetic materials, such as GaAs or similar III–V semiconductors, are currently employed in devices that use charge. Apparently, they can be made magnetic if high concentrations of magnetic elements are introduced [92], although this is sometimes being disputed at magnetic semiconductor conferences. Semiconductors are particularly preferred for these types of experiments, as they have the ability to be doped with impurities and thereby change their properties [93]. If these impurities are magnetic, molecular beam epitaxial growth is employed under low temperature equilibrium conditions to enhance their solubility [94]. The result is a diluted magnetic semiconductor, for instance Ga0.947 Mn0.053 that has a high magnetic transition temperature (∼110 K) which corresponds well with the calculated transition temperature based on the Ruderman–Kittel– Kasuya–Yosida (RKKY) interaction [95]. The advantage of diluted magnetic semiconductor materials is that ferromagnetism and semiconducting characteristics coexist [96]. Many eﬀects are

4.26 Colossal Magnetoresistance

89

attributed to the exchange interaction between itinerant holes and magnetic spins [97, 98]. For (Ga,Mn)As it is assumed that holes play a critical role in the magnetic coupling between ferromagnetic semiconductors/nonmagnetic layered structures [99], whereas exchange interactions between the electrons in the semiconducting band and the localized electrons at the magnetic ions lead to interesting electronic, optical and magnetic properties [100]. Furthermore, computations show that strain has a strong inﬂuence on the valence subbands [100], therefore it may be possible to use strain engineering to control the magnetic properties resulting from the hole-mediated exchange. In (Ga,Mn)As, the ferromagnetic double exchange between nearby pairs of Mn ions is stronger than the antiferromagnetic superexchange. Conversely, the latter remains signiﬁcant in p-(Zn,Mn)Te due to the lack of electrical participation of Mn atoms in II–VI compounds [100]. Also, (Ga,Mn)As ﬁlms display a considerable magnetic anisotropy because of the interaction between spin and orbital degrees of freedom of the magnetic electrons [100]. In the case of (Ga,Mn)Sb with a few percent of Mn, a pronounced anomalous Hall eﬀect and a negative magnetoresistance below 50 K are obtained, indicating the formation of a ferromagnetic semiconductor where the Mn atoms are incorporated into the GaSb host [101]. On the other hand, p-type (Ga,Mn)N is supposed to have a Curie temperature above room temperature [102], which would add more capabilities to GaN-based structures, already in use in photonics and high power electronics. According to theoretical [103] and experimental [104, 105] investigations, the n-type (Ga,Mn)N does not display ferromagnetism above 1 K.

4.26 Colossal Magnetoresistance Half-metallic ferromagnets are promising materials that show potential for GMR structures, as they have an absence of either majority or minority states at the Fermi energy, so that the current shows a high degree of spin polarization. For example, Fe3 O4 with its high Curie temperature [106] (858K), [107] CrO2 , Heusler alloys, and manganites are considered to be half-metallic ferromagnets. Doped manganite perovskites such as for instance, La1−x Ax MnO3 have also been under study in recent years owing to the fact that they display an eﬀect termed colossal magnetoresistance (CMR). CMR is quite diﬀerent from the GMR of magnetic multilayers, nevertheless the origin of the eﬀect is still being debated. A variety of mechanisms have been proposed as an explanation, such as electron–phonon coupling [108], double exchange [109], electron–magnon interactions [110], or phase- and charge-segregation [111]. The fact remains that signiﬁcant changes in the magnetoresistance of the manganite perovskites are observed at very large ﬁelds and low temperatures. Below 140 K, the parent compound LaMnO3 displays an antiferromagnetic structure, while the magnetic coupling between the Mn3+ ions is mediated by superexchange interactions.

90

4 Magnetoresistance and Spin Valves

Particularly interesting properties are obtained when the hole doping is increased by cationic species, resulting in compounds such as La0.8 A0.2 MnO3 (A = Ca, Na, Sr) which show extreme magnetoresistance values at room temperature and a high, controllable insulator–metal transition temperature well over the paramagnetic–ferromagnetic transition temperature [112]. Introducing Sr at Ca-sites sharpens the transition from metal to insulator [113], whereas hole doping with [114] Pb leads to a completely stable ferromagnetic character. On the other hand, Ho-doping with only 1 mol% raises the metal–insulator transition temperature [115]. These changes in structure and transport properties are a result of the creation of mobile Mn4+ species on the Mn sites [116]. If additionally, a compound such as La0.7 Pb0.3 MnO3 is doped with transition metals (e.g., Fe), the latter enters the samples as Fe3+ , giving rise to an antiferromagnetic coupling between Fe and Mn, and ﬁne-tuning the double exchange mechanism [117]. A signiﬁcant challenge for manganite perovskites remains the fabrication of qualitatively good materials for applications, as researchers ﬁnd diﬀerences between single crystal and polycrystalline specimens [118, 119]. The microstructure is to some extent responsible for these diﬀerences [120], leading to freezing of magnetic domains in partially melted samples [121], or to variations in CMR depending on the connectivity between grains [122]. Strain induced by lattice mismatch between ﬁlms and substrate has an eﬀect on the electronic phase separation [123], inﬂuencing the charged ordered state [124]. Adding metal ions improves physical properties, especially around room temperature [125]. By changing the doping level (La/Ba ratio) and adding metal ions such as Ag in La1−x Bax MnO3 thin ﬁlms grown by pulsed-laser deposition, remarkably sharp metal–insulator transitions can be obtained [126]. Sintering and partial melting seem to open up new percolating conduction channels between grains, helping the ordering of Mn spins and restoring the ferromagnetic state at elevated temperatures [127].

4.27 CPP Geometry Preferred in Sensors A variety of studies [128–131] have come to the conclusion that the CPP geometry is the most advantageous for magnetic spin valves, leading to maximum GMR performance. This is because in the CPP geometry the current ﬂows perpendicular to the multilayers and electrons experience spin-dependent scattering at the interfaces [132]. A quantity termed spin diﬀusion length plays a crucial role in perpendicular spin transport. A short spin diﬀusion length results in reduced GMR [133]. The Valet–Fert model [134, 135] uses the spin diﬀusion length to describe CPP GMR transport in metallic ferromagnetic– normal metal–ferromagnetic multilayers. The model takes into account dissimilar scattering rates for majority and minority spins in the two channels displaying diﬀerent resistivities.

4.28 Spin Valves in Commercial Applications

91

When the spins ﬂip from “up” to “down” and conversely, an electrochemical potential diﬀerence arises, similar to the charge accumulation eﬀect at the interface between a normal metal and a superconductor. Thus, a spin accumulation builds up at the interface while a perpendicular current ﬂows through it. Johnson was the ﬁrst to calculate the spin accumulation in ferromagnetic– normal metal–ferromagnetic conﬁgurations where the thickness of the nonmagnetic metal was much longer than the spin-diﬀusion length [136]. On the other hand, when the spacer layer is thin and the spin diﬀusion length longer than the thickness of the ferromagnetic layer, the Valet–Fert model is reduced to the “two-current representation” [137]. In this simpliﬁed version, the GMR of the CPP spin valve with antiparallel coupled pinned and reference ferromagnetic layers increases with the thickness of the latter. However, too much thickness can be detrimentary to the saturation ﬁeld value that needs to be suﬃciently high for sensor stability. A challenge for measuring GMR in the CPP geometry is the small resistance of the samples making them diﬃcult to characterize. The samples must have a surface area large enough for the magnetic layers to retain the properties characteristic for large thin ﬁlms. A solution is to fabricate the layers in the form of nanowires, in an alternating magnetic and nonmagnetic layer pattern such as Co/Cu [138,139]. The large aspect ratios of nanowire length vs. diameter allow for easy magnetotransport measurements. However, ill deﬁned current directions can lead to small GMR values of for instance [140], only 6% at room temperature reaching 12% at 5 K. In the CIP geometry, due to the current ﬂowing in the sample plane and hence through the spacer or individual magnetic layers [141], the GMR response is even more reduced. Therefore, the CPP geometry is still preferred where improved designs can lead to low resistance-area products for the spin valves, combined with high GMR values [142, 143], making it feasible to fabricate low-resistance, nanometer-sized devices for high data rate magnetic recording applications.

4.28 Spin Valves in Commercial Applications The sensing heads in disk drives based on GMR can detect much smaller magnetic ﬁelds than earlier generation technologies. Not only can the density of bits of information on the disk be increased, but also reading the information is now faster. Other interesting applications of spin valves, such as the bipolar spin switch [144], the micromagnetometer [145], or the micro-SQUID [146], have also emerged in the previous decade, and still more are yet to come. For instance, vibrations of several tens of ˚ A of microelectromechanical systems microbridges have been successfully measured using a 10 × 2 µm2 spin valve sensor displaying a 6.5% GMR [147]. The spin valve sensor is made out of a top-pinned spin valve structure Ta/NiFe/CoFe/Cu/CoFe/MnIr/Ta using ion beam deposition on a glass substrate. Prepatterning is done by photolithography and ion-beam milling.

92

4 Magnetoresistance and Spin Valves

Fig. 4.4. (a) An integrated spin valve sensor and MEMS bridge with micromagnet. (b) The gate, spin valve sensor, and lead environment (reprinted from [147] (copyright 2002) with permission from the IEEE)

In this design, the sensor is placed 3 µm away and 2.6 µm below the central point of a Si:H/Al bridge with a 1 µm air gap (Fig. 4.4)), while it detects the fringe ﬁeld (30–40 Oe) created by an rf-magnetron sputtered Co78 Pt22 micromagnet deposited on top of the bridge. Magnet saturation occurs transverse to the bridge length, creating a transverse fringe ﬁeld in the sensor. The movement of the bridge is controlled by an applied voltage on the gate. Further improvements in the design and experimental conditions led to reported bridge deﬂections up to [148] 0.23 µm. The whole device could be part of a membrane/microbridge/cantilever system, considering that microcantilevers are increasingly being used in biochip applications as detectors or actuators. The deﬂection of these microbridges can be determined with nanometer resolution due to the extraordinary sensitivity of spin valves to changes in magnetic ﬁelds. From rotational speed control devices (for ABS systems) [149], to high current monitoring devices for power lines [150, 151] or positioning control devices in robotic systems [152], spin valves have been incorporated reliably wherever sensitivity to magnetic ﬁelds needs to be quantiﬁed.

References

93

References 1. M.N. Baibich, J.M. Broto, A. Fert, F. Nguyen van Dau, F. Petroﬀ, Phys. Rev. Lett. 61(21), 2472 (1988) 2. G. Binasch, P. Grunberg, F. Saurenbach, W. Zinn, Phys. Rev. B 39, 4828 (1989) 3. P. Gr¨ unberg, R. Schreiber, Y. Pang, M.B. Brodsky, H. Sowers, Phys. Rev. Lett. 57(19), 2442 (1986) 4. S.S.P. Parkin, in Ultrathin Magnetic Structures, ed. by B. Heinrich, J.A.C. Bland, vol. II (Springer, Berlin, 1994) p. 148 5. A. Fert, I.A. Campbell, J. Phys. F 6, 849 (1976) 6. V.S. Gornakov, V.I. Nikitenko, W.F. Egelhoﬀ, R.D. McMichael, A.J. Shapiro, R.D. Shull, J. Appl. Phys. 91(10), 8272 (2002) 7. S.S.P. Parkin, D. Mauri, Phys. Rev. B 44, 7131 (1991) 8. L. Geppert (ed.), A Giant Leap for Disk Drives, IEEE Spectrum 3, 24 (1998) 9. R. Dill, R.E. Fontana, S.S.P. Parkin, C. Tsang, US Patent 5,898,548, 1999 10. S.S.P. Parkin, IBM J. Res. Develop. 42(1), 3 (1998) 11. Z.-G. Zhu, G. Su, B. Jin, Q.-R. Zheng, Int. J. Modern Phys. B 16(19), 2857 (2002) 12. M. Johnson, R.H. Silsbee, Phys. Rev. B 37, 3312 (1988) 13. B.L. Johnson, R.E. Camley, Phys. Rev. B 44(18), 9997 (1991) 14. P. Baumgart, B. Gurney, D. Wilhoit, T. Nguyen, B. Dieny, V. Speriosu, J. Appl. Phys. 69, 4792 (1991) 15. P. Baumgart, B.A. Gurney, D.R. Wilhoit, T. Nguyen, B. Dieny, V.S. Speriosu, J. Appl. Phys. 69(8), 4792 (1991) 16. S.S.P. Parkin, N. Morc, K.P. Roche, Phys. Rev. Lett. 64, 2304 (1990) 17. K. Wakoh, T. Hihara, T.J. Konno, K. Sumiyama, K. Suzuki, Mat. Sci. Eng. A217/218, 326 (1996) 18. W.L. Brown, M.F. Jarrold, R.L. McEachern, M. Sosnowski, G. Takaoka, H. Usui, I. Yamada, Nucl. Instrum. Method. B59/60, 182 (1991) 19. A. Maeda, T. Tanuma, M. Kume, Mater. Sci. Eng. A217, 203 (1996) 20. R.D. Shull, A.J. Shapiro, V.S. Gornakov, V.I. Nikitenko, J.S. Jiang, H. Kaper, G. Leaf, S.D. Bader, IEEE Trans. Magn. 37(4), 2576 (2001) 21. J.S. Jiang, E.E. Fullerton, C.H. Sowers, A. Inomata, S.D. Bader, IEEE Trans. Magn. 35(5), 3229 (1999) 22. A.J. Shapiro, V.S. Gornakov, V.I. Nikitenko, R.D. McMichael, W.F. Egelhoﬀ, Y.W. Tahk, R.D. Shull, L. Gan, J. Magn. Magn. Mat. 240, 70 (2002) 23. E.E. Fullerton, J.S. Jiang, M. Grimsditch, C.H. Sowers, S.D. Bader, Phys. Rev. B 58(18), 12193 (1998) 24. W.H. Meiklejohn, C.P. Bean, Phys. Rev. B 102, 1413 (1956) 25. C. Tsang, J. Appl. Phys. 55, 2226 (1984) 26. J. Nogu´es, I.K. Schuller, J. Magn. Magn. Mater. 192, 203 (1999) 27. A.E. Berkowitz, K. Takano, J. Magn. Magn. Mater. 200, 552 (1999) 28. W.H. Meiklejohn, J. Appl. Phys. 33, 1328 (1962) 29. V.S. Gornakov, V.I. Nikitenko, A.J. Shapiro, R.D. Shull, J.S. Jiang, S.D. Bader, J. Magn. Magn. Mater. 246, 80 (2002) 30. W. Zhu, L. Seve, R. Sears, B. Sinkovic, S.S.P. Parkin, Phys. Rev. Lett. 86, 5389 (2001) 31. H. Ohldag, A. Scholl, F. Nolting, E. Arenholz, S. Maat, A.T. Young, M. Carey, J. St¨ ohr, Phys. Rev. Lett. 91(1), 017203 (2003)

94 32. 33. 34. 35. 36. 37. 38. 39. 40.

41. 42. 43. 44.

45. 46. 47. 48. 49. 50. 51. 52.

53. 54. 55. 56. 57. 58. 59. 60. 61.

4 Magnetoresistance and Spin Valves W.J. Antel, F. Perjeru, G.R. Harp, Phys. Rev. Lett. 83, 1439 (1999) L.T. Romankiw, D.A. Thompson, US Patent 4,295,173, 13 October 1981 R. Bozorth, Ferromagnetism (Van Nostrand, Princeton, NJ, 1951) P.C. Andricacos, L.T. Romankiw, Advances in Electrochemical Science and Engineering, ed. by H. Gerischer, C. Tobias, vol. 3 (VCH, New York, 1994) D.A. Thompson, Proc. AIP Conf. Magn. Magn. Mat. 24, 528 (1975) L.T. Romankiw, US Patent 3,908,194, 23 Sept. 1975 L.T. Romankiw, Electrochem. Soc. Proc. PV90-8, 39 (1990) J-W. Chang, P.C. Andricacos, B. Petek, P.L. Trouilloud, L.T. Romankiw, Electrochem. Soc. Proc. PV98-20, 488 (1999) E.I. Cooper, C. Bonhˆ ote, J. Heidmann, Y. Hsu, P. Kern, J.W. Lam, M. Ramasubramanian, N. Robertson, L.T. Romankiw, H. Xu, IBM J. Res. Develop. 49(1), 103 (2005) N. Robertson, H.L. Hu, C. Tsang, IEEE Trans. Magn. 33(5), 2818 (1997) J.V. Powers, L.T. Romankiw, US Patent 3,652,442, 28 March 1972 T. Osaka, M. Takai, K. Hayashi, Y. Sogawa, K. Ohashi, Y. Yasue, M. Saito, K. Yamada, IEEE Trans. Magn. 34, 1432 (1994) M. Ramasubramanian, J. Lam, A. Hixson-Goldsmith, A. Medina, T. Dinan, N. Robertson, T. Harris, S. Yuan, Electrochem. Soc. Proc. PV2002-27, 298 (2003) C. Bonhˆ ote, H. Xu, E.I. Cooper, L.T. Romankiw, Electrochem. Soc. Proc. PV2002-27, 319 (2003) P. Kern, C. Bonhˆ ote, L.T. Romankiw, Electrochem. Soc. Proc. PV2002-27, 328 (2003) H. Xu, J. Heidmann, Y. Hsu, Electrochem. Soc. Proc. PV2002-27, 307 (2003) S. Parkin, X. Jiang, C. Kaiser, A. Panchula, K. Roche, M. Samant, Proc. IEEE 91(5), 661 (2003) S. Maat, A. Zeltser, J. Li, L. Nix, B.A. Gurney, Phys. Rev. B 70, 014434 (2004) K.V. O’Donovan, J.A. Borchers, S. Maat, M.J. Carey, B.A. Gurney, J. Appl. Phys. 95(11), 7507 (2004) W.C. Cain, W.H. Meiklejohn, M.H. Kryder, J. Appl. Phys. 61, 4170 (1982) A. Scholl, J. Stohr, J. Luning, J.W. Seo, J. Fompeyrine, H. Siegwart, J.P. Locquet, F. Nolting, S. Anders, E.E. Fullerton, M.R. Scheinfein, H.A. Padmore, Science 287, 1014 (2000) M.J. Carey, A.E. Berkowitz, Appl. Phys. Lett. 60, 3060 (1991) M.J. Carey, S. Maat, P. Rice, R.F.C. Farrow, R.F. Marks, A. Kellock, P. Nguyen, B.A. Gurney, Appl. Phys. Lett. 81(6), 1044 (2002) S. Maat, M.J. Carey, E.E. Fullerton, T.X. Le, P.M. Rice, B.A. Gurney, Appl. Phys. Lett. 81(3), 520 (2002) S. Maat, J. Checkelsky, M.J. Carey, J.A. Katine, J.R. Childress, J. Appl. Phys. 98, 113907 (2005) S. Maat, M.J. Carey, J.A. Katine, J.R. Childress, J. Appl. Phys. 98, 073905 (2005) S. Colins, A. Dinia, J. Appl. Phys. 91, 5268 (2002) J.S. Moodera, L.R. Kinder, T.M. Wong, R. Meservey, Phys. Rev. Lett. 74, 3273 (1995) K.I. Bolotin, F. Kuemmeth, D.C. Ralph, Phys. Rev. Lett. 97, 127202 (2006) W.F. Egelhoﬀ Jr., L. Gan, H. Ettedgui, Y. Kadmon, C.J. Powell, P.J. Chen, A.J. Shapiro, R.D. McMichael, J.J. Mallett, T.P. Moﬀat, M.D. Stiles, E.B. Svedberg, J. Magn. Magn. Mater. 287, 496 (2005)

References

95

62. Z.K. Keane, L.H. Yu, D. Natelson, Appl. Phys. Lett. 88, 062514 (2006) 63. T. Ozue, M. Kondo, Y. Soda, S. Fukuda, S. Onodera, T. Kawana, IEEE Trans. Magn. 38(1), 136 (2002) 64. S.S.P. Parkin, Z.G. Li, D.J. Smith, Appl. Phys. Lett. 58, 2710 (1991) 65. J. Inoue, J. Magn. Magn. Mat. 164, 273 (1996) 66. B. Dieny, Europhys. Lett. 17, 261 (1992) 67. D.M. Edwards, R.B. Muniz, J. Mathon, IEEE Trans. Magn. 27, 3548 (1991) 68. B.A. Gurney, V.S. Speriosu, J.P. Nozieres, H. Lefakis, D.R. Wilhoit, O.U. Need, Phys. Rev. Lett. 71, 4023 (1993) 69. T.D. Boone, L. Folks, J.A. Katine, S. Maat, E. Marinero, S. Nicoletti, M. Field, G.J. Sullivan, A. Ikhlassi, B. Brar, B.A. Gurney, IEEE Trans. Magn. 42(10), 3270 (2006) 70. J.R. Childress, M.J. Carey, M-C. Cyrille, K. Carey, N. Smith, J.A. Katine, T.D. Boone, A.A.G. Driskill-Smith, S. Maat, K. Mackay, C.H. Tsang, IEEE Trans. Magn. 42(10), 2444 (2006) 71. A. Tanaka, Y. Shimizu, Y. Seyama, K. Nagasaka, R. Kondo, H. Oshima, S. Eguchi, H. Kanai, IEEE Trans. Magn. 38(1), 84 (2002) 72. K. Nagasaka, Y. Seyama, L. Varga, Y. Shimizu, A. Tanaka, J. Appl. Phys. 89, 6943 (2001) 73. O. Wunnicke, N. Papanikolaou, P.H. Dederichs, V. Drchal, J. Kudrnovsky, Phys. Rev. B 65, 064425 (2002) 74. J.R. Childress, M.J. Carey, S.I. Kiselev, J.A. Katine, S. Maat, N. Smith, J. Appl. Phys. 99, 08S305 (2006) 75. S.S.P. Parkin, Z.G. Li, D.J. Smith, Appl. Phys. Lett. 58, 2710 (1991) 76. K. Liu, S.M. Zhou, C.L. Chien, V.I. Nikitenko, V.S. Gornakov, A.J. Shapiro, R.D. Shull, J. Appl. Phys. 87(9), 5052 (2000) 77. S.S.P. Parkin, Phys. Rev. Lett. 67, 3598 (1991) 78. F.J. Himpsel, T.A. Jung, P.F. Seidler, IBM J. Res. Develop. 42(10), 33 (1998) 79. A. Haury, A. Wasiela, A. Arnoult, J. Cibert, S. Tatarenko, T. Dietl, Y. Merle d’Aubign´e, Phys. Rev. Lett. 79, 511 (1997) 80. S. Koshihara, A. Oiwa, M. Hirasawa, S. Katsumoto, Y. Iye, C. Urano, H. Takagi, H. Munekata, Phys. Rev. Lett. 78, 4617 (1997) 81. V.S. Speriosu, J.P. Nozieres, B.A. Gurney, B. Dieny, T.C. Huang, H. Lefakis, Phys. Rev. B 47, 11579 (1993) 82. J.M. George, L.G. Pereira, A. Barth´el´emy, F. Petroﬀ, L. Steren, J.L. Duvail, A. Fert, R. Loloee, P. Holody, P.A. Schroeder, Phys. Rev. Lett. 72, 408 (1994) 83. R.K. Nesbet, IBM J. Res. Develop. 42(1), 53 (1998) 84. N.F. Mott, Proc. R. Soc. Lond. Ser. A 156, 368 (1936) 85. J.F. Gregg, I. Petej, E. Jouguelet, C. Dennis, J. Phys. D: Appl. Phys. 35, R121 (2002) 86. M. Julli`ere, Phys. Lett. 54, 225 (1975) 87. D.J. Monsma, R. Vlutters, J.C. Lodder, Science 281, 407 (1998) 88. S. van Dijken, X. Jiang, S.S.P. Parkin, Appl. Phys. Lett. 80, 3364 (2002) 89. R. Jansen, J. Phys. D: Appl. Phys. 36, R289 (2003) 90. B.G. Park, T. Banerjee, J.C. Lodder, R. Jansen, Phys. Rev. Lett. 97, 137205 (2006) 91. T. Banerjee, E. Hag, M.H. Siekman, J.C. Lodder, R. Jansen, Phys. Rev. Lett. 94, 027204 (2005) 92. H. Ohno, Science 281(5379), 951 (1998)

96

4 Magnetoresistance and Spin Valves

93. H. Ohno, H. Munekata, T. Penny, S. von Moln´ ar, L.L. Chang, Phys. Rev. Lett. 68, 2664 (1992) 94. A. Oiwa, A. Endo, S. Katsumoto, Y. Iye, H. Ohno, H. Munekata, Phys. Rev. B 59, 5826 (1999) 95. F. Matsukura, H. Ohno, A. Shen, Y. Sugawara, Phys. Rev. B 57(4), R2037 (1998) 96. H. Munekata, A. Zaslavsky, P. Fumagalli, R.J. Gambino, Appl. Phys. Lett. 63, 2929 (1999) 97. T. Adhikari, S. Basu, Jpn. J. Appl. Phys. 33(1), 4581 (1994) 98. H. Ohno, A. Shen, F. Matsukura, A. Oiwa, A. Endo, S. Katsumoto, Y. Iye, Appl. Phys. Lett. 69, 363 (1996) 99. T. Dietl, H. Ohno, F. Matsukura, Phys. Rev. B 63, 195205 (2001) 100. S. Koshihara, A. Oiwa, S. Katsumoto, Y. Iye, C. Urano, H. Takagi, H. Munekata, Phys. Rev. Lett. 78, 4617 (1997) 101. F. Matsukura, E. Abe, H. Ohno, J. Appl. Phys. 87(9), 6442 (2000) 102. M.L. Reed, N.A. El-Masry, H.H. Stadelmaier, M.K. Ritums, M.J. Reed, C.A. Parker, J.C. Roberts, S.M. Bedair, Appl. Phys. Lett. 79(21), 3473 (2001) 103. T. Dietl, A. Haury, Y. Merle d’Aubign´e, Phys. Rev. B 55, R3347 (1997) 104. S. von Moln´ ar, H. Munekata, H. Ohno, L.L. Chang, J. Magn. Magn. Mater. 93, 356 (1991) 105. Y. Satoh, D. Okazawa, A. Nagashima, J. Yoshino, Physica E 10, 196 (2001) 106. A. Yanase, K. Siratori, J. Phys. Soc. Jpn. 53, 312 (1984) 107. K.P. K¨ amper, W. Schmitt, G. G¨ untherodt, R.J. Gambino, R. Ruf, Phys. Rev. Lett. 59, 2788 (1987) 108. A.J. Milli, P.B. Littlewood, B.I. Shraiman, Phys. Rev. Lett. 74, 5144 (1995) 109. K. Kubo, N. Ohata, J. Phys. Soc. Jpn. 33, 21 (1972) 110. E.L. Nagaev, Phys. Rev. 346, 387 (2001) 111. A. Moreo, S. Yuunoki, E. Dagotto, Science 283, 2034 (1999) 112. X. Zhu, Y. Sun, J. Dai, W. Song, J. Phys. D: Appl. Phys. 39, 2654 (2006) 113. A.K. Pradhan, Y. Feng, B.K. Roul, D.R. Sahu, Appl. Phys. Lett. 79(4), 506 (2001) 114. C.W. Searle, S.T. Wang, Can. J. Phys. 48, 2023 (1969) 115. A.K. Pradhan, B.K. Roul, Y. Feng, Y. Wu, S. Mohanty, D.R. Sahu, P. Dutta, Appl. Phys. Lett. 78(11), 1598 (2001) 116. J. Gutierrez, F.J. Bermejo, N. Veglio, J.M. Barandiaran, P. Romano, C. Mondelli, M.A. Gonz´ alez, A.P. Murani, J. Phys.: Condens. Matter 18, 9951 (2006) 117. J. Gutierrez, A. Pe˜ na, J.M. Barandiaran, T. Hernandez, L. Lezama, M. Insausti, T. Rojo, Phys. Rev. B 61, 9028 (2000) 118. H.Y. Hwang, S.-W. Cheong, N.P. Ong, B. Batlogg, Phys. Rev. Lett. 77, 2041 (1996) 119. K.M. Krishnan, A.R. Modak, C.A. Lucas, R. Michel, H.B. Cherry, J. Appl. Phys. 79, 5169 (1996) 120. R. Shreekala, M. Rajeswari, K. Ghosh, A. Goyal, J.Y. Gu, C. Kwon, Z. Trajanovic, T. Boettcher, R.L. Greene, R. Ramesh, T. Venkatesan, Appl. Phys. Lett. 71, 282 (1997) 121. X.L. Wang, J. Horvat, H.K. Liu, S.X. Dou, Solid State Commun. 108, 661 (1998) 122. A. de Andr´es, M. Garc´ıa-Hern´ andez, J.L. M´ artinez, C. Prieto, Appl. Phys. Lett. 73, 999 (1998)

References

97

123. M. Uehara, S. Mori, C.H. Chen, S.-W. Cheong, Nature 399, 560 (1999) 124. Y. Ogimoto, M. Izumi, T. Manako, T. Kimura, Y. Tomioka, M. Kawasaki, Y. Tokura, Appl. Phys. Lett. 78, 3505 (2001) 125. R. Shreekala, M. Rajeswari, S.P. Pai, S.E. Loﬂand, S.B. Ogale, S.M. Bhagat, M.J. Downes, R.L. Greene, R. Ramesh, T. Venkatesan, Appl. Phys. Lett. 74, 2857 (1999) 126. A.K. Pradhan, D.R. Sahu, B.K. Roul, Y. Feng, Appl. Phys. Lett. 81(19), 3597 (2002) 127. A.K. Pradhan, B.K. Roul, J.G. Wen, Z.F. Ren, M. Muralidhar, P. Dutta, D.R. Sahu, S. Mohanty, P.K. Patro, Appl. Phys. Lett. 76(6), 763 (2000) 128. H.E. Camblong, S. Zhang, P. Levy, Phys. Rev. B 47, 4735 (1993) 129. M.A.M. Gijs, G.E. Bauer, Adv. Phys. 46, 285 (1997) 130. W.P. Pratt Jr., S.F. Lee, J.M. Slaughter, R. Loloee, P.A. Schroeder, J. Bass, Phys. Rev. Lett. 66, 3060 (1991) 131. S.D. Steenwyck, S.Y. Hsu, R. Loloee, J. Bass, W.P. Pratt Jr., J. Magn. Magn. Mater. 170, L1 (1997) 132. J.-Ph. Ansermet, J. Phys.: Condens. Matter. 10, 6027 (1998) 133. A. Azizi, S.M. Thompson, K. Ounadjela, J. Gregg, P. Vennegues, A. Dinia, J. Arabski, C. Fermon, J. Magn. Magn. Mater. 148, 313 (1995) 134. T. Valet, A. Fert, Phys. Rev. B 48, 7099 (1993) 135. A. Fert, S. Lee, Phys. Rev. B 53, 6554 (1996) 136. M. Johnson, Phys. Rev. Lett. 70, 2142 (1993) 137. Q. Yang, P. Holody, S.F. Lee, L.L. Henry, R. Loloee, P.A. Schroeder, W.P. Pratt, J. Bass, Phys. Rev. Lett. 72, 3274 (1994) 138. A. Blondel, J.Ph. Meier, B. Doudin, J.-Ph. Ansermet, Appl. Phys. Lett. 66, 3019 (1994) 139. L. Piraux, J.M. George, J.F. Despres, C. Leroy, E. Ferain, R. Legras, K. Ounadjela, A. Fert, Appl. Phys. Lett. 65(19), 2484 (1994) 140. A. Chalastaras, L.M. Malkinski, J.-S. Jung, S.-L. Oh, J.-K. Lee, C.A. Ventrice Jr., V. Golub, G. Taylor, IEEE Trans. Magn. 40(4), 2257 (2004) 141. B. Dieny, V.S. Speriosu, S.S.P. Parkin, B.A. Gurney, D.R. Wilhoit, D. Mauri, Phys. Rev. B 43(1), 1297 (1991) 142. W.P. Pratt, S.F. Lee, P. Holody, Q. Yang, R. Loloee, J. Bass, P.A. Schroeder, Phys. Rev. B 51, 3226 (1995) 143. S.D. Steenwyck, S.Y. Hsu, R. Loloee, J. Bass, W.P. Pratt, J. Magn. Magn. Mater. 170, L1 (1997) 144. M. Johnson, Mater. Sci. Eng. B 31, 199 (1995) 145. V. Cros, S.F. Lee, G. Faini, A. Cornette, A. Hamzic, A. Fert, J. Magn. Magn. Mater. 165, 512 (1997) 146. C. Chapelier, M. El Khatib, P. Perrier, A. Benoit, D. Mailly, in Superconducting Devices and Their Applications, ed. by H. Koch, H. Lubbig (Springer, Berlin, 1991), p. 286 147. H. Li, J. Gaspar, P.P. Freitas, V. Chu, J.P. Conde, IEEE Trans. Magn. 38(5), 3371 (2002) 148. H. Li, M. Boucinha, P.P. Freitas, J. Gaspar, V. Chu, J.P. Conde, J. Appl. Phys. 91(10), 7774 (2002) 149. J. Daughton, J. Brown, E. Shen, R. Beech, A. Pohm, W. Kud, IEEE Trans. Magn. 30, 4608 (1994)

98

4 Magnetoresistance and Spin Valves

150. J.K. Spong, V.S. Speriosu, R.E. Fontana, M.M. Dovek, T.L. Hylton, IEEE Trans. Magn. 32(2), 366 (1996) 151. N. Sugawara, M. Takiguchi, T. Yaoi, N. Negoro, K. Kagawa, A. Okabe, K. Hayashi, H. Kano, Appl. Phys. Lett. 70(4), 523 (1997) 152. P.P. Freitas, F. Silva, N.J. Oliveira, L.V. Melo, L. Costa, N. Almeida, Sens. Actuators 81, 2 (2000)

5 Some Basic Spintronics Concepts

Summary. New and intriguing devices for more eﬃcient information processing have emerged in the ﬁrst decade of the new millenium. An elusive property of electrons known as spin may just be the next entity for data encoding. This connection between electron transport and spin plays a major role in information transport through the device. Since spin is usually associated with quantum mechanics, any devices relying on it are termed quantum devices. In the present chapter, a new area of electronics is discussed, an area that has seen various degrees of experimental success in proving that information can indeed be encoded, transported and stored using both electron charge and spin. When dealing with spin it is expected that tiny length scales within the device come into play, and that phenomena not generally encountered in bulk materials come to light. Furthermore, for information to be reliably encoded and transported from one part of the device to another using the spin associated with electrons, certain conditions need to be met. Aside from examining some of these key conditions, this chapter also highlights what has been done to eliminate challenges encountered in spin injection, transport and detection, as well as a few developments where the majority of research seems to be concentrated nowadays.

5.1 Encoding Information: Emergence of Spintronics Spin allows for the diﬀerentiation between electrons [1] grouping them into two types, “spin-up” and “spin-down” depending on their ±1/2 spin projection onto a given quantization axis. In ferromagnetic metals, there is an imbalance at the Fermi level in the number of “spin-up” and “spin-down” electrons [2]. Because of this imbalance, electrons traveling from one metal ferromagnet to another through a nonmagnetic spacer carry information about the magnetization of the ﬁrst ferromagnet [3]. The spin of a single electron is considered a suitable entity to encode a qubit [4], a coherent superposition of “spin-up” and “spin-down” states. Thus, information can be encoded via electron spin, and transported from one part of the device to another using electron current [5], if certain conditions are

100

5 Some Basic Spintronics Concepts

met for the phase coherence to be maintained. The coding can be changed by remagnetizing the metal ferromagnet containing the information. Also, the transport of information only takes place provided the device is built on a short length scale for the quantum mechanical phase coherence of the electronic wave function to be preserved [6]. The quantum mechanical phase coherence is measured by the transverse relaxation time T2 [7]. Spin coherence times signiﬁcantly exceed charge coherence times, making spin based quantum devices more robust and fault tolerant than their charge based counterparts [8]. Control of spin-polarized electrical conduction while maintaining phase coherence is likely to have a great impact on quantum information technology [9]. It is not surprising that a promising ﬁeld termed spin electronics or spintronics has emerged [10], dealing with the active control and manipulation of spin degrees of freedom in condensed matter structures. Spintronics is based on three factors [11]: spin injection, control of spin transport, and spin selective detection, however to generate the properties that are important for these three factors certain mesomagnetic length scales need to be considered, typically [12] tens to thousands of Angstroms. Nanotechnology can nowadays construct devices on these scales [13].

5.2 Spin Injection 5.2.1 Minority vs. Majority Spin Carriers The injection of spin from a ferromagnet into an otherwise nonmagnetic material is one of the prerequisites for any spintronic device [14]. But how do we get to these spins? According to Mott’s model [15] from the 1930s, “spin-up” and “spin-down” electrons exist in two diﬀerent channels (or subbands) in a ferromagnetic material. Although spin-ﬂip scattering occurs between the two channels resulting in spins losing their initial orientation, it is often neglected given the short time scales of all other processes in the system [14]. Nonetheless, the density of states in the two spin channels is diﬀerent, and the electrical current is primarily due to electrons with a lower density of states at the Fermi level. These are also known as “minority spin carriers” [16], as opposed to “majority spin carriers” corresponding to those with a higher density of states. Minority spin carriers constitute a good supply of spins when the current passes from a ferromagnet to a nonmagnetic material. 5.2.2 Spin Injection Rate The spin injection rate at a single ferromagnetic/semiconductor heterojunction is given by the ratio of the net magnetization current jM to electric current je passing through the interface under an applied voltage [17]: jM µB , = ηM je e

(5.1)

5.2 Spin Injection

101

where µB is the Bohr magneton. The relationship is valid under the assumption that no spin-ﬂip scattering or no spin precession takes place at the interface [17, 18]. The degree of spin polarization of the net electron ﬂux through the interface is described by the interfacial transport parameter [14] (or spin injection eﬃciency) ηM . The latter is connected to the “spin-up” and “spindown” conductances G↑ and G↓ through [14] ηM =

G↑ − G↓ . G↑ + G↓

(5.2)

For a double ferromagnetic/semiconductor/ferromagnetic heterojunction, the spin injection eﬃciency η M is deﬁned similarly in terms of the total spin conductances [14] G↑ tot and G↓ tot ηM =

tot Gtot ↑ − G↓ tot . Gtot ↑ + G↓

(5.3)

The elastic multiple scattering at the interfaces leads to “spin-up” and “spindown” transmission probabilities T↑ and T↓ that result [14] in spin injection eﬃciency ηM T↑ − T↓ ηM = . (5.4) T↑ + T↓ − T↑ T↓ A net spin current ﬂows through the two interfaces when T↑ = T↓ [14]. Spin injection can be experimentally tested using a spin valve conﬁguration, as reviewed brieﬂy further below. 5.2.3 Spin Polarization and Spin Transfer In low dimensional systems, a spin polarization of electrons can exist even in zero magnetic ﬁeld [19]. For metals, the spin–orbit eﬀect can result in an energy separation of a few mV between the spin bands. Nevertheless for low electron densities, electron–electron interactions can cause a 2D homogeneous system to become unstable to spontaneous spin polarization as a result of exchange [20]. Reports of an enhanced g-factor and anomalous spin susceptibility have indicated that spontaneous spin polarization does exist when the disorder is low [21]. Spin-polarized current can transfer the angular momentum from carriers to a ferromagnet where it can change the direction of magnetization, even though no external ﬁeld is acting. This eﬀect is equivalent to a spin transfer torque [22, 23]. The spin torque is driven by a spin-polarized current [24], and is a reaction to a common process termed spin ﬁltering [25], because spin-polarized electrons interact with the ferromagnet. Spin ﬁltering means that incoming electrons with spin components perpendicular to the magnetic moment in the ferromagnet are being ﬁltered out. Consequently, this perpendicular spin is transferred as a torque exerted on the moment due to conservation laws

102

5 Some Basic Spintronics Concepts

that have to take place. Hence, the mechanism for spin transfer implies a spin ﬁltering process without which the transfer would not take place. Nevertheless, the ferromagnet needs to be thin, as the conditions for this eﬀect to occur are not realized in bulk materials [26]. Furthermore, when a phenomenon termed spin transmission resonance [26] takes place, the magnetic moment in the ferromagnet remains unaltered, and no spin transfer occurs. Thus, there is more than one way to control the injection of spin. 5.2.4 CPP vs. CIP Geometry To study spin injection and detection, the so-called polarize/analyze experiments [27] are used where the ﬁrst ferromagnet serves as a “polarizer,” and the second as an “analyzer.” A voltage jump is detected when the magnetizations change from a parallel to an antiparallel orientation. Julli´ere’s experiment [28] reported in 1975 was the ﬁrst demonstration of spin ﬁltering without superconductors, as he employed an Fe/Ge/Co structure (at 4.2 K). In principle, in a “polarize/analyze” experiment two ferromagnets are used in two geometries while separated by a nonmagnetic spacer layer (see also Chap. 4). The currentperpendicular-to-plane (CPP) geometry (Fig. 5.1, bottom) is more frequently utilized, and most mathematical treatments refer to it [29]. On the other hand, the current-in-plane (CIP) geometry (Fig. 5.1 top) was historically employed ﬁrst because it is easier to realize [30].

+I +V

−V −I

+I

+V

−V

−I

Fig. 5.1. Top: Current-in-plane (CIP); bottom: current-perpendicular-to-plane (CPP) geometry (reprinted from [38] (copyright 2002) with permission from the Institute of Physics)

5.2 Spin Injection

103

5.2.5 Spin Accumulation, Spin Relaxation, and Spin Diﬀusion Length In some cases, to generate spin polarization and thereby a nonequilibrium spin population [31], optical techniques have been employed involving circularly polarized photons that transfer their angular momentum to electrons [32, 33]. For actual spintronics devices, electrical spin injection is preferred [34], where a magnetic electrode is connected to a specimen. A current from the electrode drives spin-polarized electrons to the sample, creating a nonequilibrium spin accumulation in the latter [35]. To restore equilibrium, a process of spin relaxation occurs, giving rise to an exponential spin accumulation decay from the interface. Spin relaxation ranges from picoseconds to microseconds [36,37], and takes place over a distance termed spin diﬀusion length. The spin diﬀusion length lsd is estimated to be [38] νF τ↑↓ λ , (5.5) lsd = 3 where νF is the Fermi velocity, τ↑↓ is the spin-ﬂip time, and λ is the mean free path. If any spin accumulation is to be achieved, the spin relaxation needs to be counterbalanced by a certain spin accumulation rate [39]. The latter can be given in terms of the spin density n at distance x from the interface [38] n = n0 e−x/lsd ,

(5.6)

where n0 is the spin density at the interface. After integrating to obtain the total number of spins in the accumulation, the spin accumulation rate is found to be n0 lsd /τ↑↓ . In the end, a total spin density of 1022 m−3 is estimated, compared to a total electron density of about 1028 m−3 [38]. This shows that the spin density asymmetry represents only about one part in a million of the total electron density, making it diﬃcult to measure. Impurities shorten the mean free path and the spin-ﬂip time, thereby reducing the spin diﬀusion length. 5.2.6 No Spin Accumulation in CIP Geometry Spin accumulation cannot be achieved in a CIP geometry [38], therefore the critical length scale is in this case the mean free path. Nevertheless, a drop in resistance is observed even in a CIP sample when the magnetizations are aligned in the two ferromagnetic layers. This drop is attributed to diﬀerent mobilities for the “spin-up” and “spin-down” electrons, and not to spin accumulation. If the nonmagnetic layer is suﬃciently thin for the electrons to experience successive momentum scattering events when they reach either one of the ferromagnetic layers, a diﬀerence in “spin-up” and “spin-down” electron scattering will lead to resistance changes. Therefore, while the magnetizations in the ferromagnets are aligned one spin type is heavily scattered

104

5 Some Basic Spintronics Concepts

in both layers, leaving the other spin type relatively unscattered [29]. On the other hand, if the layers have antiparallel magnetization, neither spin type has high mobility due to heavy scattering in one ferromagnet or the other. For giant magnetoresistance [40] (GMR) to occur in CIP samples, the thickness of the spacer layer has to be less than the mean free path (20–30 ˚ A). 5.2.7 Half-Metallic Ferromagnets In a half-metallic ferromagnet [41], even in the absence of a magnetic ﬁeld [42] only one spin channel has available states at the Fermi surface, making up the “majority spin carriers” [43]. The other spin band is either completely full or completely empty, while its energy level is diﬀerent from that of the Fermi level [44]. This group of ferromagnets contains Heusler alloys [45], ferromagnetic oxides [46, 47], and some diluted magnetic semiconductors (DMS) [14]. Heusler alloys are cubic materials with four interpenetrating fcc sublattices. They are thought to include Co2 MnSi [48], NiMnSb [49], Co2 MnGe [50], and Co2 FeSi [51]. Group IV magnetic semiconductors are of particular interest due to their potential compatibility with Si-based processing technologies. However, their diﬃcult fabrication requirements such as high doping levels and high growth temperatures may pose some challenges. When unwanted phase separations occur, the materials obtained are disordered and inhomogeneous. Usually, doping with several elements is preferred over single ones, as the dopants alter the local kinetic and strain conditions [52]. X-ray diﬀraction investigations revealed that strains in the ﬁlm depend linearly on Co and Mn concentrations. While Co in Ge contracts the lattice, doping with Mn expands it [53]. At the same time, strain stabilizes growth in Co-rich samples due to the small lattice mismatch. There may exist an optimum doping concentration for which the lattices may no longer be mismatched. Furthermore, electric and magnetic properties of Co-rich (Coa Mnb )x Ge1−x epitaxial ﬁlms are controlled by the doping concentration, therefore the latter is a key factor in the fabrication of these materials. There is also a possibility that both electrons and holes are spin polarized, thereby opening new avenues for heterojunction applications [53]. Half-metallic ferromagnetic oxides consist of compounds that have itinerant electrons such as CrO2 and Sr2 FeMoO6 , or compounds with localized electrons as is the case for Fe3 O4 . The discovery of unexpected properties in ferromagnetic oxides has sparked a general interest in these materials all over the world [53]. Of course, the type of fabrication technique is the most important factor in inﬂuencing what properties a certain compound may have. 5.2.8 Some Epitaxial Growth Techniques Oxygen-plasma-assisted-molecular-beam-epitaxy-grown Cox Ti1−x O2−x usually results in a high concentration of oxygen vacancies that permit thermally driven redox reactions to take place. This in turn leads to Ti being fully

5.2 Spin Injection

105

oxidized at the expense of Co, and the formation of Co nanoparticles. Furthermore, spectroscopic investigations reveal that O vacancies are eﬀectively bound to substitutional Co to maintain its +2 oxidation state. Nevertheless, this material has great thermal stability as it does not change its magnetic properties when annealed in vacuum at 825 K, as opposed to pulsed-laserdeposition-grown Co : TiO2 [54]. Recently, an advanced technique termed combinatorial-laser-molecularbeam-epitaxy [53] has been developed for the synthesis of a large number of samples with diﬀerent compositions in a short amount of time. Compositional variations are easily implemented into high-throughput synthesis methods followed by a rapid characterization of structural, electrical, and magnetic properties. This approach allows an eﬃcient search for advanced functional materials and identiﬁcation of structure–composition–property relationships. For instance, it was applied to the investigation of new magnetic oxide semiconductors such as ZnO and TiO2 doped with 3d transition metals. Generally, anatase TiO2 is unstable and very sensitive to the choice of substrate relative to the rutile mineral phase that is easier to grow. Also, to obtain speciﬁc properties for the compound to be grown, the oxygen partial pressure and growth temperature need to be carefully chosen to better control the valence states of various transition metals. The combinatorial-laser-molecular-beam-epitaxy approach found that none of the 3d transition metals doped into ZnO ﬁlms resulted in ferromagnetic behavior, at least within the experimental error. On the other hand, some experimenters observed that Co-doped ZnO grown on sapphire substrates is slightly ferromagnetic up to [55] ∼350 K. In this case, oxygen vacancies were noted to lead to n-type conductivity, while Co mole fractions of up to 0.35 were obtained. Co(II) was found to substitute for Zn(II) in the ZnO lattice. As far as Co-doped TiO2 is concerned, it was observed to display the highest saturation and remanent magnetization, as well as the highest Curie temperature (∼700 K) among all half-metallic ferromagnetic oxides [54]. Furthermore, a Co0.06 Ti0.94 O2 ﬁlm was noticed to be transparent in the visible and near-infrared regions. 5.2.9 ME Materials and Spintronics Some magnetoelectric (ME) materials [56, 57] such as Cr2 O3 , GaFeO3 , Ni3 B7 O13 I, LiMnPO4 , and Y3 Fe5 O12 may be useful in spintronics applications. These materials display a coexistence of spontaneous ferromagnetic (or antiferromagnetic) and ferroelectric order, where the coupling between magnetization and polarization gives rise to a ME response [58]. Antiferromagnetic order is only slightly aﬀected by magnetic ﬁelds, however exerts a strong control of the magnetic conﬁguration due to the exchange coupling to adjacent ferromagnetic ﬁlms. This coupling can be tuned by electric ﬁelds via the ME eﬀect. The ME inﬂuence on GMR has been demonstrated experimentally in CrO2 /Cr2 O3 /CrO2 junctions, where the Cr2 O3 ﬁlm grows

106

5 Some Basic Spintronics Concepts

naturally between CrO2 crystallites [59]. Similarly, the same research group proposes using an antiferromagnetic ME thin ﬁlm as a dielectric tunnel junction between two ferromagnetic metallic layers, one soft and one hard. The ME tunnel barrier could sustain high electric ﬁelds of dielectric breakdown value while simultaneously giving rise to a signiﬁcant net magnetization that would shift the magnetization curves of both ferromagnetic layers, allowing the resistance value of the device to be determined by the electric ﬁeld in the ME layer [59]. 5.2.10 Spontaneous Band Splitting In DMS such as the ferromagnetic phase of (Ga,Mn)As [60] or (In,Mn)As [61], the valence band splits spontaneously into “spin-up” and “spin-down” subbands [62]. The DMS are nonmagnetic semiconductors doped with a few percent of magnetic impurities. Depending on the percentage of the dopant and the complex chemistry involved, these materials can exhibit ferromagnetism at and above room temperature. Nevertheless, what is sometimes interpreted as ferromagnetism in a DMS is actually just an eﬀect due to a secondary magnetic impurity phase. 5.2.11 Spin Valves For a simplistic explanation of what happens in a CPP sample, it can be assumed that the two ferromagnets are half metallic. Furthermore, it is assumed that the metals are similar, in the sense that the spin polarizations are of the same sign. In view of the density of states spin asymmetry, the ﬁrst ferromagnet would supply a current with only one type of spins that accumulate in the spacer layer. If the thickness of the latter is less than the spin diﬀusion length, the spins will make it across the spacer into the second ferromagnet provided the magnetizations in the two ferromagnets are aligned. This is because the second ferromagnet, also a half-metal has density of states for only one spin type. Hence, spin ﬁltering occurs. In case the magnetizations are antiparallel, the second ferromagnet will not accept the other type of spins. If the two ferromagnets in the above example are of opposite polarization, the majority spins in one ferromagnet are not a majority in the other ferromagnet. Therefore, a parallel alignment of magnetizations will lead to an increase in resistance, while the converse is true for antiparallel orientation. The overall GMR response of the system is in this case negative. Several design and fabrication techniques [63] have been employed [64] to obtain dissimilar switching of the magnetizations in the two ferromagnetic layers [65,66], a practice common to spin valve [14] heads in magnetic recording. Spin valves are essentially based on how the spins scatter depending on the alignment of magnetizations, and the layer coercivities. Some aspects are also discussed in Chaps. 4 and 6.

5.2 Spin Injection

107

5.2.12 Poor Injection Eﬃciency When high eﬃciency spin injection is hindered, it is usually because of a loss of spin polarization at the interface due to spin ﬂipping [29]. Even if the two materials are closely lattice matched, the interface is still nonideal [67]. It takes only a very small amount of ferromagnetic atoms to diﬀuse into the nonmagnetic side of the interface, and scatter electrons between the two spin channels [68]. This is because these diﬀused atoms will likely carry a local magnetic moment oriented randomly with respect to the magnetization direction, moment which interacts with that of the electrons crossing the interface [69]. Spin ﬂipping is more pronounced if the nonmagnetic spacer has a small density of states [70]. A possible scenario for avoiding spin ﬂipping may be the employment of a half-metallic ferromagnet due to the absence of ﬁnal states for ﬂipping [71]. Rashba [72] suggested using spin tunnel injection to circumvent the boundary condition problems related to electrochemical potential continuity at metal/semiconductor interfaces. A tunnel contact between a ferromagnet and a semiconductor is spin selective due to the spin polarization of the density of states. The barrier will lead to spin polarization of the tunnel current, and thereby support the diﬀerence in chemical potential between the “spin-up” and “spin-down” bands at the interface. However, in this case a very thin or discontinuous tunnel barrier may worsen injection eﬃciency. 5.2.13 Additional Layer Between Ferromagnet and Spacer Direct injection from a “normal” ferromagnet may still be better provided that somehow spin polarization is maintained upon injection. This may be achievable if another layer of some material is introduced between the ferromagnet and the spacer. The role of this intermediate layer would be to take over the spin polarization and deliver it mostly unchanged to the spacer layer. The intermediate layer may be a magnetic or nonmagnetic tunneling barrier, or a Schottky barrier whose depletion zone is the actual intermediate layer. If the Schottky barrier is suﬃciently extended, it mediates the diﬀerence in electrochemical potentials between the metal and semiconductor, improving spin injection eﬃciency. In case of a nonmagnetic tunneling barrier, the voltage drop across the barrier would be very large and totally control the injected current and its polarization. However, in spite of spin ﬂipping still occurring, the injected polarization is in this case independent of the diﬀusion constants [73]. 5.2.14 III–V Magnetic Semiconductors High spin polarization is assumed to exist in manganite perovskites [74], and III–V ferromagnetic semiconductors like (Ga,Mn)As [75]. Mn ions are electrically neutral in II–VI compounds, but act as an acceptor in III–V semiconductors due to the large density of states in the valence band [76]. Ferromagnetic

108

5 Some Basic Spintronics Concepts

interactions between the localized spins in (Ga,Mn)As are believed to be due to holes originating from these Mn acceptors [77, 78]. In spite of the lower mobilities and shorter lifetimes as compared to electrons, holes can still provide a successful spin injection [79]. TMR values as high as 70% have been observed at 8 K for 1.6 nm AlAs barriers in GaMnAs/AlAs/GaMnAs structures [80]. Usually, III–V semiconductors are easier doped with electrically active impurities, in contrast to the II–VI compounds that can sustain greater concentrations of transition metals [81]. The magnitude of spontaneous magnetization increases with the concentration of the dopant, reaching 100% in the metallic phase [76, 82]. 5.2.15 Obtaining Spin-Polarized Magnetic Semiconductors Turning nonmagnetic semiconductors into spin-polarized ferromagnets is more diﬃcult than it may seem at ﬁrst glance, requiring among other things a certain well determined amount of magnetic elements [83]. This is because the solubility of the magnetic elements in III–V semiconductors is quite low, only ∼1018 cm−3 [84]. Techniques such as molecular beam epitaxy or laser ablation have been used below room temperature to introduce transition metals into a semiconductor matrix without the formation of undesired phases, as for instance MnAs [85]. Some researchers found high-temperature ferromagnetism in (Ga,Mn)N [86, 87] with conclusive proof that the ferromagnetic properties are not a result of secondary magnetic phases. The GaN ﬁlms were produced by metalorganic chemical vapor deposition on (0001) sapphire substrates, and doped after growth with Mn using solid state diﬀusion [86]. Theoretical models describing ferromagnetic behavior of Mn doped p-type semiconductors have sustained experimental ﬁndings by predicting a Curie temperature above room temperature for (Ga,Mn)N [88]. This material became of interest in photonics and high power electronics, as well as integrated systems that contain both processing of information and data storage in one unit. To gain further insight into the properties of (Ga,Mn)As, studies related to the asymmetric scattering of spin-polarized carriers have been carried out using anomalous Hall eﬀect data [84]. These show that all-semiconductor (Ga,Mn)As/(Al,Ga)As/(Ga,Mn)As trilayers display spin dependent scattering and GMR in a CPP or CIP conﬁguration [89, 90] as well as a tunneling magnetoresistance (TMR) over 70% [80]. Spin injection has also been observed in spin-LEDs containing (Ga,Mn)As as an emitter [91], while a (Ga,Mn)As emitter has been employed in resonant tunneling structures [92]. 5.2.16 Light vs. Electric-Field-Induced Carrier Enhancement Ferromagnetic order in III–V diluted magnetic semiconductor heterostructures such as (In,Mn)As/GaSb was found to be induced by light [93, 94] through the enhancement of carrier-mediated ferromagnetic interactions between Mn ions. Light generates excess holes in the (In,Mn)As layer

5.2 Spin Injection

109

rendering it p-type. Their n-type counterparts can be paramagnetic [95]. Alternatively, it was observed that the hole concentration and ferromagnetic interactions in (In,Mn)As can be controlled by applied electric ﬁelds, a unique aspect of ferromagnetism in III–V and II–VI systems. By applying electric ﬁelds, researchers [96] managed to vary reversibly the transition temperature of hole-induced ferromagnetism in an (In,Mn)As channel part of an insulatinggate ﬁeld-eﬀect transistor. The transition temperature of (In,Mn)As is usually ∼30 K or below [97]. Nevertheless, by varying the hole concentration through applied electric ﬁelds, the ferromagnetic exchange interaction among localized Mn spins can be controlled, thereby reversibly altering ferromagnetic properties such as transition temperature. These results may be applicable to the integration of ferromagnetic semiconductors with nonmagnetic III–V semiconductor devices such as lasers. 5.2.17 Giant Planar Hall Eﬀect The large spin polarization of holes in (Ga,Mn)As combines its eﬀects with the strong spin–orbit coupling in the valence band giving rise to unusual properties. Among these, researchers [98] noticed the development of a spontaneous transverse voltage in response to a longitudinal current ﬂow in the absence of an applied ﬁeld. In single domain high-quality ferromagnetic semiconductors, this eﬀect can be ∼4 orders of magnitude stronger than in metallic ferromagnets. Furthermore, a giant planar Hall eﬀect is observed in epitaxial (Ga,Mn)As thin ﬁlms in response to an applied in plane magnetic ﬁeld (Fig. 5.2). Two abrupt jumps are registered in the planar Hall resistance at distinct magnetic ﬁeld values, while the longitudinal resistance also experiences small jumps. These jumps appear to be independent of sample size or geometry. Nevertheless, the smaller specimens display Barkhausen jumps (Fig. 5.2f), as the propagation of domain walls is limited by specimen geometry [99]. 5.2.18 Maintaining Spin Polarization As seen earlier, some of the problems in spintronics revolve around how to interface diﬀerent materials so that spin injection is achieved, and how to maintain spin polarization at room temperature [100]. The idea of growing magnetic III–V/II–VI semiconductor material superlattices has been suggested with the intent of raising the Curie temperature [101]. Employing semiconductors is expected given that they can be processed to high purity, the equilibrium carrier densities can be varied through doping, and electronic properties are tunable by gate potentials. Furthermore, certain semiconductor features such as depletion zones, voltage blocking, diﬀusion currents, the tunnel eﬀect, as well as conduction in two-dimensional electron gases [102] (2DEG) can sometimes be exploited in the design of spintronic devices.

110

5 Some Basic Spintronics Concepts

Fig. 5.2. (a–c) Planar Hall resistance in three specimens of diﬀerent size obtained at 4.2 K as a function of an in-plane magnetic ﬁeld at 20◦ ﬁxed orientation; (d) ﬁelddependent sheet resistance of the 100 µm wide Hall specimen; (e) relative orientations of sensing current I, external ﬁeld H, and magnetization M. An SEM image of the 6 µm specimen is also shown; (f) Barkhausen jumps observable in the 6 m specimen near the resistance transitions (reprinted from [98] (copyright 2003) with permission from the American Physical Society. URL: http://link.aps.org/abstract/ PRL/v90/e107201; doi:10.1103/PhysRevLett.90.107201)

In 2DEG, conduction occurs along a channel in a thin sheet of charge. 2DEGs are of interest in spintronics because they are “ballistic,” as opposed to “diﬀusive” [103], therefore have better chances of maintaining spin polarization. However, it is unfortunate that there does not seem to be a conclusive demonstration of electrical spin injection in ohmic all-electrical ferromagnetic/semiconductor 2DEG devices [27]. The two main obstacles appear to be the local Hall eﬀect, and the conductivity mismatch, as stated earlier [27,103]. The latter is severe for ohmic contacts between ferromagnetic metals and nonmagnetic semiconductors [104]. As already mentioned, one alternative for bypassing the problem was suggested by Rashba and consists of employing relatively high impedance magnetic tunnel junctions [72]. Nonetheless, we know that these are in a class of their own and require extensive study, as the physics of spin injection and detection with ferromagnetic/nonmagnetic tunnel junctions is rather diﬀerent from that of clean ohmic ferromagnetic/nonmagnetic junctions. Due to recent advances in high-quality magnetic semiconductors [105], and in the optimization of interfaces [106], semiconductor materials are increasingly preferred over metals. When spin-polarized carriers are injected from a magnetic semiconductor into a “normal” semiconductor, the polarization of the injected carriers depends on the magnetization direction in the magnetic

5.3 Control of Spin Transport

111

semiconductor [106]. Higher percentages in injection [107] may be achieved by injection from a semiconductor, than by direct injection from metals. Nevertheless, if interface scattering is absent, the spin accumulation density may be too small in the semiconductor [108], and hence the spin-polarized current through the interface may also be too small. 5.2.19 The Future of Spin Injection Spin injection in semiconductors diﬀers from that in metals [109], as there is a much greater spin relaxation lifetime in semiconductors [33]. In an innovative experiment, a so-called “spin aligner” fabricated from a doped II–VI semiconductor was used to interface with a III–V compound [107]. The result was that injection eﬃciencies of 90% spin-polarized current were achieved, while injection took place into the nonmagnetic semiconductor device GaAs/AlGaAs used as a light-emitting diode. Spin polarization was conﬁrmed through the circular polarization state of the emitted light [107]. In a quite diﬀerent study but not of lesser signiﬁcance, a ballistic pure spin current was injected and controlled in GaAs/AlGaAs quantum wells [110]. The current was termed pure, as it was not accompanied by a net charge current, but rather consisted only of orthogonally polarized “spin-up” and “spin-down” photons, demonstrating an alternative type of spin current. Despite challenges posed by materials problems, the least of them being the limited functionality given by low operating temperatures, it is believed that magnetic semiconductors will play a signiﬁcant role as spin injectors in the near future [62, 83]. The fact that ferromagnetism can be induced using Mn doping in zinc-blende III–V compounds or II–VI semiconductors has opened up new areas for exploration [111]. Novel physical phenomena have been discovered [112], launching the development of previously unknown spin injection devices [113].

5.3 Control of Spin Transport Various spin decoherence mechanisms inﬂuence spin transport [114] because unlike charge, spin is a nonconserved quantity [11]. Spin-polarized electrons (or holes) maintain their polarization as long as they do not come across a magnetic impurity [115] or interact with the lattice via spin–orbit coupling. Collisions with magnons cause momentum transfer between spin channels, a process often referred to as spin mixing [29]. To maintain spin polarization, the interaction between spin and the transport environment needs to be controlled [116, 117]. 5.3.1 The Need for Long Spin Relaxation Times One of the challenges in spin transport is extending spin transmission over longer distances, so that spin can be more eﬃciently manipulated during the

112

5 Some Basic Spintronics Concepts

transfer process. Metals and inorganic semiconductors have momentum scattering lengths shorter than spin scattering lengths, leading to unwanted diffusive electron transport [118]. For this reason, organic semiconductors have recently been under increased scrutiny [119, 120] as potential replacements for metal and inorganic semiconductor spacers. It was observed that organic semiconductors display unique optical as well as spintronic properties, showing promise for a whole range of signal processing and communication applications [121]. Particularly appealing to spintronics is the weak spin–orbit interaction in organics, leading to long spin relaxation times [120]. Additionally, the reduced size, which can be obtained for devices incorporating organic semiconductors, allows integration into opto-spintronic chips [122]. 5.3.2 Organic Semiconductor Spacers These properties unique to organic semiconductors may be attributed to the strong intramolecular rather than intermolecular interactions. This is due to the fact that conjugated polymers are quasi-one-dimensional systems resulting in weakly screened electron–electron interactions. On the other hand, electrons and the lattice are strongly coupled; therefore, charge carriers in these materials are positive and negative polarons, rather than holes and electrons [123]. Spin valve structures with organic semiconductor spacers have been constructed in thin ﬁlm [119] or nanowire form [124]. The resistance of a spin valve depends on the state of the electron spins, being controllable by an external magnetic ﬁeld. Figure 5.3 depicts a hysteresis curve for Ni/Alq3 /Co trilayer Ni-Alq3-co

300 10−6

magnetic moment (emu)

200 10−6

Hc = 800 Oe

100 10−6 0 100 −100 10−6 1.9 K

−200 10−6

magnetic field parallel to nanowires −6

−300 10 −1.2 104 −8000

−4000

0

4000

8000

1.2 104

magnetic field (Oe)

Fig. 5.3. Hysteresis curve for Ni/Alq3 /Co trilayer nanowires obtained at 1.9 K using a Physical Parameter Measurement System (Quantum Design). The trilayer nanowires were fabricated in porous alumina obtained by anodization

5.3 Control of Spin Transport

113

nanowires obtained at 1.9 K, showing that these structures are responsive to magnetic ﬁelds. When in thin ﬁlm form, spin valves with organic semiconductor spacers have displayed a GMR as high as 40% at low temperatures [119]. These encouraging results may be due in part to the La0.67 Sr0.33 MnO3 that is believed to be a half-metallic ferromagnet [125]. As already mentioned, halfmetallic ferromagnets are appealing for spintronics, as they hold promise as superior spin injectors with near-100% spin polarization [126]. 5.3.3 Spin Transport in Organic Semiconductor Spin Valves Charge injection into organic semiconductors occurs mainly through tunneling [127], thereby avoiding the conductivity mismatch problem common to ferromagnetic/inorganic semiconductor interfaces [128]. At these interfaces, spins can switch from “spin-up” to “spin-down” and conversely, giving rise to an electrochemical potential and thereby variations in conductivity [129,130]. A recent experiment [124] with spin valves composed of nanowires with organic semiconductor spacers suggested that the primary spin relaxation mechanism in the organic material is the Elliott–Yafet mode [131] for which carrier scattering and velocity changes result in spin relaxation. These results were observed in trilayer nanowire spin valves consisting of cobalt, Alq3 (tris(8-hydroxy-quinolinolato) aluminum), and nickel, fabricated in 50 nm alumina pores. The fabrication process of the trilayers involves alumina pores obtained by anodizing an electropolished 0.1 mm thick aluminum foil in 0.3 M oxalic acid using a 40 V dc voltage [132]. Pore diameter size is ﬂexible, ultimately dependent on anodization conditions including the type of acid employed. Also, the height of the pores is adjusted by varying the anodization time, or by subsequent etching using dilute phosphoric acid [133]. The spin valve eﬀect is noticeable on a magnetoresistance curve when the magnetoresistance reaches a high point at certain ﬁeld values. For an applied magnetic ﬁeld parallel to the nanowires, the measured magnetoresistance curves revealed such points between 800 and 1,800 Oe where the coercivities of nickel and cobalt are expected. The eﬀect was visible in the nanowires only up to ∼100 K. 5.3.4 Nanoscale Eﬀects at Ferromagnet/Organic Semiconductor Interface Because of the “proximity eﬀect” [119], a spin polarization exists at the interface between Alq3 and the injecting ferromagnet. The spin polarization extends over a few lattice constants. Additionally, a small Schottky barrier is formed at the organic/ferromagnet interface. Therefore, the spin-polarized carriers tunnel and diﬀuse through the ﬁrst interface into the organic material while their spin polarization decays exponentially. They ﬁnally reach the second interface through which they also tunnel, causing a current that is detected in the second ferromagnet. The change in magnetoresistance is given

114

5 Some Basic Spintronics Concepts

by the Julli´ere formula [28], which takes into account spin polarization at the injecting and detecting contacts. With spin polarizations in nickel and cobalt at their Fermi energies of [134] 33% and 42%, respectively, and an Alq3 layer thickness of 33 nm, the spin diﬀusion length was estimated to be ∼4 nm, fairly independent of the Alq3 layer thickness. This value is almost an order of magnitude smaller than the spin diﬀusion length reported for thin ﬁlm layers [119]. This implies that the spin relaxation occurs at a higher rate in nanowires. Furthermore, carrier mobility is reduced in the Alq3 layer because of the additional Coulomb scattering caused by the charged surface states [135]. All things considered, the Elliott–Yafet [131] spin relaxation mechanism is suggested as being dominant in the Alq3 nanowires, giving rise to long [124] spin relaxation times that range from a few milliseconds to over 1 s at 1.9 K. 5.3.5 Carbon Nanotubes With the advent of carbon nanotubes new possibilities open up for spin transmission, especially since carbon nanotubes display extremely long electron and phase scattering lengths [136]. These unique properties are partly due to the construction of carbon nanotubes. A single walled nanotube (SWNT) consists of only one graphene sheet wrapped around to form a 1–3 nm diameter cylinder. On the other hand, multiwalled nanotubes contain several concentric cylinders reaching diameters of up to 80 nm. The chirality of the wrapping in a SWNT determines whether it behaves as a semiconductor or a metal. The lightness of the carbon atom is an advantage, as it provides for reduced spin-ﬂip scattering. Carbon nanotubes have been incorporated in spintronic devices with the intent of studying their spin transport properties. For instance, a MWNT was grown on a Si substrate containing a thin SiO2 layer and ferromagnetically contacted (Fig. 5.4). In spite of the long channel nanotube length of 250 nm, the injected spin remained polarized, judging by the 9% resistance change obtained at 4.2 K [137]. Spins maintained their coherence during transport through the nanotube and inﬂuenced the value of the magnetoresistance [137]. 5.3.6 GMR vs. TMR The eﬀective resistance of the whole multilayer or trilayer structure is dependent on magnetic changes, therefore GMR [138,139] and TMR [140,141] eﬀects play a key role in spintronics. By varying the spacer layer composition and the measurement conﬁguration, GMR and TMR devices can be built. An example of a GMR response is shown in Fig. 5.5, where a surprisingly large spin diﬀusion length was measured in a 40 nm MWNT with Co contacts [142]. In TMR, an electrical current passes by quantum mechanical tunneling through an insulating tunnel barrier between two ferromagnetic layers [143]. Two-terminal spin tunneling junctions have been built exhibiting large changes in tunnel resistance, depending on the relative orientations of the magnetizations in the ferromagnetic layers [27]. The TMR eﬀect is usually explained based on Julli´ere’s model [28], where the rate of tunneling is

5.3 Control of Spin Transport

115

Fig. 5.4. Scanning electron microscopy image of a Co contacted MWNT. The diameter of the nanotube is 30 nm and the conducting channel length is 250 nm (reprinted from [137] (copyright 2001) with permission from the American Institute of Physics)

Fig. 5.5. An example of a GMR response in a 40 nm Co-contacted MWNT with a spin diﬀusion length of 130 nm (reprinted from [142] (copyright 2000) with permission from Elsevier)

proportional to the product of the electron densities of states at that particular energy on each side of the barrier. Electrons with majority spins tunnel if the two half-metallic ferromagnets have aligned magnetizations, rendering a low resistance for the device. During antiparallel orientation of magnetizations, the product of the initial and ﬁnal densities of states is zero for either spin type, therefore no current ﬂows [144].

116

a

5 Some Basic Spintronics Concepts

Current flow

b

Current flow

Fig. 5.6. Two resistor model provides a simple explanation for the low (a) and high (b) resistance conﬁgurations of magnetic multilayers. (a) The layers have parallel magnetizations allowing spins in one channel to pass through with no scattering, whereas spins in the other channel experience scattering while traversing the layers. (b) The magnetizations of adjacent layers are antiparallel, and spins in both channels are scattered. The resistors in each path represent the resistances the spins experience in each layer (reprinted from [38] (copyright 2002) with permission from the Institute of Physics)

5.3.7 The Parallel Resistor Model Although crude, a parallel resistor model (Fig. 5.6) can give further insight into the mechanics of high and low resistance magnetic layer conﬁgurations [38]. As shown in Fig. 5.6, the ﬁve series resistors represent the resistances of each layer. The high and low resistances correspond to the two spin channels. With arbitrarily assigned values of 1 and 10 Ω, the parallel and antiparallel magnetization conﬁgurations have total resistances of 4.5 Ω and 13 Ω, respectively. Thus, a minimum resistance state is obtained for a parallel magnetization conﬁguration, while antiparallel alignment results in a higher resistance. Of course, the model fails to explain what occurs at adjacent interfaces, and does not take into account spin accumulation, diﬀusion or relaxation. 5.3.8 Eﬀects at Adjacent Interfaces in GMR Some concepts have been adapted from TMR and applied to GMR because of the similarities exhibited by the two eﬀects. To gain some insight into this issue, a very simplistic approach can be taken for GMR where spin transport is considered in a ferromagnetic multilayer stack. A spin splitting of

5.3 Control of Spin Transport

117

the Fermi level is presumed in the ferromagnetic metals, causing an unequal distribution of “spin-up” and “spin-down” electron states. Additionally, if an “ohmic” nontunneling CPP conﬁguration is assumed where Mott’s model applies, then spins in one channel pass through with no scattering, while spins in the other channel are scattered at interfaces [145] when the magnetizations in all layers are parallel. Conversely, spins experience maximum scattering for the antiparallel alignment of magnetizations of neighboring magnetic layers, because spins in both channels are scattered while traversing the layers [27]. Generally, a current sourced through a ferromagnet acquires a spin polarization due to the remnant magnetization of that ferromagnet. When the current is injected into the spacer layer it induces a net polarization. The latter decays spatially with a characteristic length, the spin diﬀusion length mentioned earlier. Spin-polarized holes relax quickly, whereas spin-polarized electrons persist for long times [38]. If the separation between the ﬁrst ferromagnet and the second is smaller than the spin diﬀusion length, a voltage is induced. The origin of this spin-induced voltage is the increase in “spindown” population and decrease in “spin-up” population in the nonmagnetic spacer layer. The two spin channels are oﬀset because of the diﬀerence experienced in their electrochemical potentials [27]. As a result, the “spin-down” electrochemical potential of the second ferromagnet must rise to match that of the “spin-downs” in the spacer layer. There is a resulting nonequilibrium magnetization in the spacer layer that depends on the partial polarization at the Fermi level, diﬀerences in Fermi velocities, and partial or ineﬃcient spin transfer across the interface [27]. 5.3.9 Scattering at Bloch Walls Within the magnetic layers spin scattering can also occur at Bloch walls, resulting in decoherence of the electrons and wall nucleation, wich decreases the resistivity [146]. This is due to the fact that when the electron passes through the Bloch wall, the exchange ﬁeld acting on the electron spin changes its orientation, an eﬀect known in magnetic resonance spectroscopy as “adiabatic passage.” The passage can be “fast” if the spin precession about the applied ﬁeld is fast in comparison to the angular velocity of the rotation of the magnetic ﬁeld, meaning that the spin precession follows the magnetic ﬁeld in its rotation. Nevertheless, the spin precession does not quite follow the exchange ﬁeld as the electron traverses the wall, so that the spins experience a potential barrier. Furthermore, if the electron passes through magnetic multilayers, or a tunnel barrier, the eﬀect is called “sudden passage,” because the electron is suddenly subjected to another magnetic ﬁeld [147]. Scattering at Bloch walls was suspected of being responsible for colossal magnetoresistance (CMR) in manganate perovskites [148].

118

5 Some Basic Spintronics Concepts

5.3.10 Importance of Materials Choice Both GMR and TMR depend on the comprising materials [149,150]. The combination ferromagnet/spacer (or insulator) is a determining factor in obtaining a certain GMR or TMR value [151]. It is not just up to the ferromagnet to control the spin polarization, magnetoresistance or tunneling process. Therefore, proper understanding of spintronics is only possible by taking into account the electronic structure of both ferromagnetic and nonmagnetic spacer layers, and how they interface. For instance, the Fermi surfaces of Co and Cu match well for the majority spin electrons in Co, while the match is not good for the minority spins [152]. Because of this unequal alignment of subband structures in the Co/Cu system, a spin asymmetry of the tunneling current has been observed for both layered and granular structures [153]. Although large TMR can be achieved, this system is very sensitive to the interface conditions between Co and Cu requiring smooth and sharp interfaces between the magnetic and nonmagnetic layers [154]. Poor surface quality leads to “hot spots” or “pinholes.” In the former case, electrons tunnel preferentially through localized regions of low barrier thickness, whereas the latter scenario implies direct contact between the ferromagnets [155]. TMR depends on the type of insulator material, as well as on the barrier height and width [156]. Additionally, TMR varies with barrier impurities, temperature, and bias voltage [157]. This is because spin-ﬂip scattering increases with the content of magnetic impurities in the barrier, and it is assumed that it also increases with temperature, as it is an inelastic process [158]. On the other hand, some opinions [159, 160] suggest that increases in temperature bring about a reduction in the overall magnetization in the ferromagnet because of excitations of magnons. The latter eﬀect increases electron–magnon scattering due to the fact that magnons are spin 1 quasiparticles, leading to electron spin ﬂipping [161], and hence a reduced TMR response. 5.3.11 Spin Control Through Electric Fields One additional issue that should be addressed is the one of spin control through an external ﬁeld. So far, most methods proposed for manipulating electron spin involve time-dependent magnetic ﬁelds. However, electric ﬁelds would be more useful from an application point of view, and this may not be so intangible. Rashba et al. suggested that while in a semiconductor quantum well electron spins couple to an electric ﬁeld because of the spin–orbit interaction [162, 163]. In this case, an external in-plane electric ﬁeld as small as 0.6 V cm−1 could be used to eﬃciently manipulate electron spin. Furthermore, this coupling would be by far stronger than the coupling to an ac magnetic ﬁeld [163]. Future applications will put these ideas to the test.

5.4 Spin Selective Detection

119

5.4 Spin Selective Detection Spin S can be detected by its magnetic moment – gµB S, where g is the electron g-factor, diﬀerent from the free electron value g0 = 2.0023, and µB is the Bohr magneton [164]. With today’s electron spin resonance microscopy capability, the smallest volume element that can be imaged must contain 107 electron spins [165]. This does not sound encouraging for single-spin detection. Fortunately, there is another technique with much improved sensitivity. Magnetic resonance force microscopy (MRFM) has proved to have the ability to detect an individual electron spin [166], because MRFM is based on detecting a magnetic force between the spins in the sample and a ferromagnetic tip. However, the force from an electron spin is only a few attonewtons, roughly 106 times smaller than the forces detected by atomic force microscopy (AFM) [166]. 5.4.1 Detecting Single Spins To measure unpaired electron spins, experiments involving a custom fabricated mass-loaded silicon cantilever have been performed on silicon dioxide specimens. These ultrasensitive cantilever-based force sensors are the newest development in MRFM, and are made for the purpose of facilitating singlespin detection [167]. The custom fabricated mass-loaded silicon cantilever employed in the single-spin experiment [166] had an attached 150 nm-wide SmCo magnetic tip used to sense the force from the electron spin. For the spin measurement to occur, the vitreous silica specimens had to be irradiated with Co gamma rays. This procedure resulted in silicon dangling bonds containing unpaired electron spins. Figure 5.7 shows the conﬁguration of the single-spin MRFM experiment. At points in the specimen where the condition for magnetic resonance is satisﬁed, cyclic adiabatic inversion of the spin takes place causing a slight shift of the cantilever frequency. The shift is due to the magnetic force exerted by the spin on the tip. Unfortunately, low temperatures (1.6 K) are required to minimize force noise and reduce the spin relaxation rate [166]. Nevertheless, the MRFM technique allows imaging of spins as deep as 100 nm below the surface. 5.4.2 Detecting Spin Polarization of an Ensemble of Spins Several methods have been developed for measuring spin polarization, including spin-polarized photoemission spectroscopy [168], or Andreev reﬂection [169]. The latter makes use of a superconductor connected to a spin asymmetric material. A small applied bias voltage leads to electron tunneling from the normal metal to the superconductor, and the formation of Cooper pairs which have zero spin. This is because electrons with given momentum and spin couple with electrons of opposite momentum and spin, so that when the latter

120

5 Some Basic Spintronics Concepts Cantilever Microwave coil

Interferometer

Magnetic tip

Resonant slice

Spin

z

y

x

Fig. 5.7. Experimental conﬁguration of a single-spin MRFM measurement involving an ultrasensitive silicon cantilever with a SmCo magnetic tip positioned ∼125 nm above a silica specimen containing a low density of unpaired electron spins. The “resonant slice” marks the region in the specimen where the ﬁeld from the magnetic tip (plus an externally applied ﬁeld) matches the condition for magnetic resonance (reprinted from [166] (copyright 2004) with permission from Nature Publishing Group)

leaves a hole is created. If the normal metal is half metallic, the necessary hole density of states is absent, therefore the Andreev reﬂection is suppressed. The spin polarization in the normal metal is related to the conductivity of the contact, allowing determination of the spin polarization [169]. Spin polarization can also be determined by using a reference electrode with 100% spin polarization [170]. The material under investigation constitutes the ﬁrst electrode from which tunneling currents ﬂow towards the reference electrode. Because spin polarization in the reference electrode depends not only on the electrode material itself, but also on the accompanying insulator, it is important to maintain the same magnetic metal/insulator combination in each experiment. Furthermore, good material quality and minimizing defects at interfaces can prevent spin-ﬂip events and therefore randomization of spin orientation that could otherwise compromise the integrity of the experiment. In practical devices, not the spins themselves need to be detected, but rather changes in the spin states that lead to changes in the measured signals [171, 172].

References

121

5.4.3 The Datta and Das Spin Field Eﬀect Transistor In 1990, Datta and Das [173] developed the concept of a spin ﬁeld eﬀect transistor consisting of two ferromagnets as source (spin injector) and drain (spin detector) with parallel magnetic moments. The device was not realized experimentally, but is still useful as it illustrates some of the principles on which spintronic devices are supposed to work. The Datta and Das transistor makes use of the Rashba eﬀect where a stationary electric ﬁeld present in the material looks partially magnetic to a relativistic traveler. This is because carrier velocities in devices are of the order of ∼106 m s−1 , and the magnetic component of the local ﬁelds in the depletion layer, or of the crystal ﬁelds is capable of inﬂuencing the transport of the relativistic carriers. In case of the transistor, the gate voltage generates an eﬀective magnetic ﬁeld that causes the spins to precess about a precession vector due to the spin–orbit coupling. The magnetic ﬁeld is tunable by the gate voltage at the top of the channel. By controlling the voltage, the precession is modiﬁed so that it leads to parallel or antiparallel spins while in transit through the channel. A large current is obtained when the spins are parallel to the magnetizations in the source and drain. The situation corresponds to the “on” state of the transistor. In the reverse situation, when the spins are antiparallel to the magnetizations in the ferromagnets, the spins are scattered and the transistor is in the “oﬀ” state. 5.4.4 The Future of Spintronics Devices The Datta and Das [173] spin ﬁeld eﬀect transistor is an example of a device where the population and the phase of the spin of an ensemble of electrons can be controlled. Nevertheless, the prerequisites for a successful experimental implementation of spin transistors remain: (1) injection of spin-polarized current [33], (2) spin coherent propagation [174], (3) induction of controlled spin precession [175], and (4) spin selective collection [31]. In spite of these diﬃculties, progress is being made in all ﬁelds of spintronic devices [176, 177]. The range of potential spintronic devices is starting to expand only now, and goes beyond spin ﬁeld eﬀect transistors. There still remain many challenges to be overcome before successfully fabricating commercial devices. Future developments in spintronic devices will be largely driven by advances in spintronic materials. In the end, all-semiconductor structures are expected to take over hybrid designs with metallic ferromagnets. But this will depend on the ability of producing high-quality interfaces with nonmagnetic materials.

References 1. H.C. Ohanian, Am. J. Phys. 54(6), 500 (1986) 2. O. Pietzsch, S. Okatov, A. Kubetzka, M. Bode, S. Heinze, A. Liechtenstein, R. Wiesendanger, Phys. Rev. Lett. 96, 237203 (2006) ˇ 3. S. Das Sarma, J. Fabian, X. Hu, I. Zuti, Superlatt. Microstruct. 27, 289 (2000)

122

5 Some Basic Spintronics Concepts

4. V. Privman, I.D. Wagner, G. Kventsel, Phys. Lett. A 239, 141 (1998) 5. S. Bandyopadhyay, Phys. Rev. B 61, 13813 (2000) 6. T. Calarco, A. Datta, P. Fedichev, E. Pazy, P. Zoller, Phys. Rev. A 68, 012310 (2003) 7. B.E. Kane, Nature 393, 133 (1998) 8. S. Bandyopadhyay, V.P. Roychowdhury, Superlatt. Microstruct. 22, 411 (1997) 9. J.M. Daughton, A.V. Pohm, R.T. Fayﬁeld, C.H. Smith, J. Phys. D 32, R169 (1999) 10. S. Das Sarma, Am. Sci. 89, 516 (2001) 11. S.A. Chambers, Y.K. Yoo, Mater. Res. Soc. Bull. 28, 706 (2003) 12. A. Steane, Rep. Prog. Phys. 61, 117 (1998) 13. C.-G. Stefanita, F. Yun, M. Namkung, H. Morkoc, S. Bandyopadhyay, in Electrochemical Self-Assembly as a Route to Nanodevice Processing, ed. by H.S. Nalwa. Handbook of Electrochemical Nanotechnology (American Scientiﬁc, Los Angeles 2006) 14. F. Mireles, G. Kirczenow, Europhys. Lett. 59(1), 107 (2002) 15. N.F. Mott, Proc. R. Soc. Lond. Ser. A 156, 368 (1936) 16. A. Barthelemy, A. Fert, Phys. Rev. B 43, 13124 (1991) 17. M. Johnson, R.H. Silsbee, Phys. Rev. B 37, 5326 (1988) 18. M. Johnson, Phys. Rev. B 58, 9635 (1998) 19. A. Ghosh, C.J.B. Ford, M. Pepper, H.E. Beere, D.A. Ritchie, Phys. Rev. Lett. 92, 116601 (2004) 20. D. Varsano, S. Moroni, G. Senatore, Europhys. Lett. 53, 348 (2001) 21. E. Tutuc, S. Melinte, M. Shayegan, Phys. Rev. Lett. 88, 036805 (2002) 22. X. Waintal, E.B. Myers, P.W. Brouwer, D.C. Ralph, Phys. Rev. B 62, 12317 (2000) 23. M.D. Stiles, A. Zangwill, Phys. Rev. B 66, 014407 (2002) 24. J.C. Slonczewski, J. Magn. Magn. Mater. 159, L1 (1996) 25. L. Berger, Phys. Rev. B 54, 9353 (1996) 26. W. Kim, F. Marsiglio, Phys. Rev. B 69, 212406 (2004) 27. D.D. Awschalom, D. Loss, N. Samarth (eds.), Semiconductor Spintronics and Quantum Computation (Springer, Berlin, 2002) 28. M. Julli´ere, Phys. Lett. 54, 225 (1975) 29. J.-Ph. Ansermet, J. Phys.: Condens. Matter 10, 6027 (1998) 30. B. Dieny, V.S. Speriosu, S.S.P. Parkin, B.A. Gurney, D.R. Wilhoit, D. Mauri, Phys. Rev. B 43, 1297 (1991) 31. D. Hagele, M. Oestreich, W.W. Ruhle, N. Nestle, K. Ebert, Appl. Phys. Lett. 73, 1580 (1998) 32. D.D. Awschalom, J.M. Kikkawa, Phys. Today 52(6), 33 (1999) 33. J.M. Kikkawa, D.D. Awschalom, Nature 397, 139 (1999) 34. M. Johnson, R.H. Silsbee, Phys. Rev. Lett. 55, 1790 (1985) 35. D. Chiba, M. Yamanouchi, F. Matsukura, H. Ohno, Science 301, 943 (2003) 36. F.X. Bronold, I. Martin, A. Saxena, D.L. Smith, Phys. Rev. B 66, 233206 (2002) 37. R.S. Britton, T. Grevatt, A. Malinowski, R.T. Harley, P. Perozzo, A.R. Cameron, A. Miller, Appl. Phys. Lett. 73, 2140 (1998) 38. J.F. Gregg, I. Petej, E. Jouguelet, C. Dennis, J. Phys. D: Appl. Phys. 35, R121 (2002) 39. R. de Sousa, S. Das Sarma, Phys. Rev. B 68, 155330 (2003)

References

123

40. M.N. Baibich, J.M. Broto, A. Fert, F. Nguyen Van Dau, F. Petroﬀ, Phys. Rev. Lett. 61(21), 2472 (1988) 41. R.A. de Groot, F.M. Mueller, P.G. van Engen, K.H.J. Buschow, Phys. Rev. Lett. 50, 2024 (1983) 42. W.E. Pickett, J.S. Moodera, Phys. Today 54(5), 39 (2001) 43. R.A. de Groot, F.M. Mueller, P.G. van Engen, K.H.J. Buschow, J. Appl. Phys. 55, 2151 (1984) 44. Y.K. Yoo, F.W. Duewer, H. Yang, Y. Dong, X.-D. Xiang, Nature 406, 704 (2000) 45. C. Palmstr¨ om, Mater. Res. Soc. Bull. 28, 725 (2003) 46. T. Dietl, H. Ohno, F. Matsukura, J. Cibert, D. Ferrand, Science 287, 1019 (2000) 47. K. Sato, H. Katayama-Yoshida, Jpn. J. Appl. Phys. 39(2), L555 (2000) 48. I. Galanakis, P.H. Dederichs, N. Papanikolau, Phys. Rev. B 66, 174429 (2002) 49. R. de Groot, F. Mueller, P. van Engen, K. Buschow, Phys. Rev. Lett. 50, 2024 (1983) 50. S. Ishida, S. Fujii, S. Kashiwagi, S. Asano, J. Phys.: Condens. Matter 2, 8583 (1990) 51. M. Hashimoto, J. Herfort, H-P. Sch¨ onherr, K.H. Ploog, J. Phys.: Condens. Matter 18, 6101 (2006) 52. F. Tsui, L. He, D. Lorang, A. Fuller, Y.S. Chu, A. Tkachuk, S. Vogt, Appl. Surf. Sci. 252(7), 2512 (2006) 53. Y. Matsumoto, H. Koinuma, T. Hasegawa, I. Takeuchi, F. Tsui, Y.K. Yoo, Mater. Res. Bull. 28, 734 (2003) 54. S.A. Chambers, R.F.C. Farrow, Mat. Res. Bull. 28, 729 (2003) 55. K. Ueda, H. Tabata, T. Kawai, Appl. Phys. Lett. 79, 988 (2001) 56. I.E. Dzyaloshinskii, Sov. Phys. – JETP 10, 628 (1960) 57. T. Katsufuji, S. Mori, M. Masaki, Y. Moritomo, N. Yamamoto, H. Takagi, Phys. Rev. B 64, 104419 (2001) 58. T. Kimura, S. Kawamoto, I. Yamada, M. Azuma, M. Takano, Y. Tokura, Phys. Rev. B 67, 180401 (2003) 59. Ch. Binek, B. Doudin, J. Phys.: Condens. Matter 17, L39 (2005) 60. S.J. Potashnik, K.C. Ku, S.H. Chun, J.J. Berry, N. Samarth, P. Schiﬀer, Appl. Phys. Lett. 79, 1495 (2001) 61. T. Omiya, F. Matsukura, T. Dietl, Y. Ohno, T. Sakon, M. Motokawa, H. Ohno, Physica E 7, 976 (2000) 62. T. Dietl, H. Ohno, Mater. Res. Soc. Bull. 28, 714 (2003) 63. A.J. Shapiro, V.S. Gornakov, V.I. Nikitenko, R.D. McMichael, W.F. Egelhoﬀ, Y.W. Tahk, R.D. Shull, L. Gan, J. Magn. Magn. Mat. 240, 70 (2002) 64. E.E. Fullerton, J.S. Jiang, M. Grimsditch, C.H. Sowers, S.D. Bader, Phys. Rev. B 58(18), 12193 (1998) 65. R.D. Shull, A.J. Shapiro, V.S. Gornakov, V.I. Nikitenko, J.S. Jiang, H. Kaper, G. Leaf, S. D. Bader, IEEE Trans. Mag. 37(4), 2576 (2001) 66. V.S. Gornakov, V.I. Nikitenko, W.F. Egelhoﬀ, R.D. McMichael, A.J. Shapiro, R.D. Shull, J. Appl. Phys. 91(10), 8272 (2002) 67. B.T. Jonker, Proc. IEEE 91, 727 (2003) 68. P.M. Levy, Adv. Res. Appl. 47, 367 (1994) 69. P.B. Allen, Solid State Commun. 102, 127 (1997) 70. M.A.M. Gijs, E.W. Bauer, Adv. Phys. 46, 285 (1997)

124

5 Some Basic Spintronics Concepts

71. P.C. van Son, H. van Kempen, P. Wyder, Phys. Rev. Lett. 58, 2271 (1987) 72. E.I. Rashba, Phys. Rev. B 62, R16267 (2000) 73. B.T. Jonker, S.C. Erwin, A. Petrou, A.G. Petukhov, Mater. Res. Soc. Bull. 28, 740 (2003) 74. J.-H. Park, E. Vescovo, H.-J. Kim, C. Kwon, R. Ramesh, T. Venkatesan, Phys. Rev. Lett. 81, 1953 (1998) 75. J.G. Braden, J.S. Parker, P. Xiong, S.H. Chun, N. Samarth, Phys. Rev. Lett. 91, 056602 (2003) 76. T. Dietl, Physica E 10, 120 (2001) 77. H. Akai, Phys. Rev. Lett. 81, 3002 (1998) 78. T. Dietl, H. Ohno, F. Matsukura, Phys. Rev. 63, 195205 (2001) 79. E. Johnston-Halperin, D. Lofgreen, R.K. Kawakami, D.K. Young, L. Coldren, A.C. Gossard, D.D. Awschalom, Phys. Rev. B 65, 041306(R) (2002) 80. M. Tanaka, Y. Higo, Phys. Rev. Lett. 87, 026602 (2001) 81. T. Dietl, H. Ohno, Physica E 9, 185 (2001) 82. D. Ferrand, J. Cibert, A. Wasiela, C. Bourgognon, S. Tatarenko, G. Fishman, T. Andrearczyk, J. Jaroszynski, S. Kolesnik, T. Dietl, B. Barbara, D. Dufeu, Phys. Rev. B 63, 085201 (2001) 83. H. Ohno, Science 281, 951 (1998) 84. H. Ohno, H. Munekata, T. Penny, S. von Moln´ ar, L.L. Chang, Phys. Rev. Lett. 68, 2664 (1992) 85. H. Ohno, A. Shen, F. Matsukura, A. Oiwa, A. Endo, S. Katsumoto, Y. Iye, Appl. Phys. Lett. 69, 363 (1996) 86. M.L. Reed, N.A. El-Masry, H.H. Stadelmaier, M.K. Ritums, M.J. Reed, C.A. Parker, J.C. Roberts, S.M. Bedair, Appl. Phys. Lett. 79, 3473 (2001) 87. H. Hori, S. Sonoda, T. Sasaki, Y. Yamamoto, S. Shimizu, K. Suga, K. Kindo, Physica B, Condens. Matter 324 (1-4), 142 (2002) 88. T. Dietl, F. Matsukura, H. Ohno, Phys. Rev. B 66, 033203 (2002) 89. F. Matsukura, D. Chiba, Y. Ohno, T. Dietl, H. Ohno, Physica E 16, 104 (2003) 90. D. Chiba, N. Akiba, F. Matsukura, Y. Ohno, H. Ohno, Appl. Phys. Lett. 77, 1873 (2000) 91. M. Kohda, Y. Ohno, K. Takamura, F. Matsukura, H. Ohno, Jpn. J. Appl. Phys. 40, L1274 (2001) 92. H. Ohno, N. Akiba, F. Matsukura, A. Shen, K. Ohtani, Y. Ohno, Appl. Phys. Lett. 73, 363 (1998) 93. H. Munekata, T. Abe, S. Koshihara, A. Oiwa, M. Hirasawa, S. Katsumoto, Y. Iye, C. Urano, H. Takagi, J. Appl. Phys. 81(8), 4862 (1997) 94. S. Koshihara, A. Oiwa, M. Hirasawa, S. Katsumoto, Y. Iye, C. Urano, H. Takagi, Phys. Rev. Lett. 78(24), 4617 (1997) 95. S. von Moln´ ar, H. Munekata, H. Ohno, L.L. Chang, J. Magn. Magn. Mater. 93, 356 (1991) 96. H. Ohno, D. Chiba, F. Matsukura, T. Omyia, E. Abe, T. Dietl, Y. Ohno, K. Ohtani, Nature 408, 944 (2000) 97. H. Munekata, A. Zaslavsky, P. Fumagalli, R.J. Gambino, Appl. Phys. Lett. 63, 2929 (1993) 98. H.X. Tang, R.K. Kawakami, D.D. Awschalom, M.L. Roukes, Phys. Rev. Lett. 90, 107201 (2003) 99. T. Ono, H. Miyajima, K. Shigeto, K. Mibu, N. Hosoito, T. Shinjo, Science 284 (5413), 468 (1999)

References

125

100. A. Shen, H. Ohno, F. Matsukura, Y. Sugawara, Y. Ohno, N. Akiba, T. Kuroiwa, Jpn. J. Appl. Phys. 36, L73 (1997) 101. F. Matsukura, H. Ohno, A. Shen, Y. Sugawara, Phys. Rev. B 57, R2037 (1998) 102. N. Biyikli, J. Xie, Y.-T. Moon, F. Yun, C.-G. Stefanita, S. Bandyopadhyay, H. Morko¸c, I. Vurgaftman, J.R. Meyer, Appl. Phys. Lett. 88, 142106 (2006) 103. J.M. Kikkawa, I.P. Smorchkova, N. Samarth, D.D. Awschalom, Science 277 (5330), 1284 (1997) 104. G. Schmidt, D. Ferrand, L.W. Molenkamp, A.T. Filip, B.J. van Wees, Phys. Rev. B 62(8), R4790 (2000) 105. Y. Ohno, D.K. Young, B. Beschoten, F. Matsukura, H. Ohno, D.D. Awschalom, Nature 402, 790 (1999) 106. B.T. Jonker, Y.D. Park, B.R. Bennett, H.D. Cheong, G. Kioseoglou, A. Petrou, Phys. Rev. B 62(12), 8180 (2000) 107. R. Fiederling, M. Keim, G. Reuscher, W. Ossau, G. Schmidt, A. Waag, L.W. Molenkamp, Nature 402, 787 (1999) 108. R.P. Borges, C. Dennis, J.F. Gregg, E. Jouguelet, K. Ounadjela, I. Petej, S.M. Thompson, M.J. Thornton, J. Phys. D 35, 186 (2002) 109. S.A. Wolf, D.D. Awschalom, R.A. Buhrman, J.M. Daughton, S. von Moln´ ar, M.L. Roukes, A.Y. Chtchelkanova, D.M. Treger, Science 294, 1488 (2001) 110. M.J. Stevens, A.L. Smirl, R.D.R. Bhat, A. Najmaie, J.E. Sipe, H.M. van Driel, Phys. Rev. Lett. 90(13), 136603 (2003) 111. D.K. Young, E. Johnston-Halperin, D.D. Awschalom, Y. Ohno, H. Ohno, Appl. Phys. Lett. 80, 1598 (2002) 112. H. Boukari, P. Kossacki, M. Bertolini, D. Ferrand, J. Cibert, S. Tatarenko, A. Wasiela, J.A. Gaj, T. Dietl, Phys. Rev. Lett. 88, 207204 (2002) 113. M. Kohda, Y. Ohno, K. Takamura, F. Matsukura, H. Ohno, Jpn. J. Appl. Phys. 40(2), L1274 (2001) 114. D.D. Awschalom, Physica E 10, 1 (2001) 115. J. Korringa, Can. J. Phys. 34, 1290 (1956) 116. G. Bastard, R. Ferreira, Surf. Sci. 267, 335 (1992) 117. G. Burkhard, H.A. Engel, D. Loss, Fortschr. Phys. 48, 965 (2000) 118. G. Schmidt, D. Ferrand, L.W. Molenkamp, A.T. Filip, B.J. van Wees, Phys. Rev. B 62, R4790 (2000) 119. Z.H. Xiong, D. Wu, Z.V. Vardeny, J. Shi, Nature 427, 821 (2004) 120. V. Dediu, M. Murgia, F.C. Matacotta, C. Taliani, S. Barbanera, Solid State Commun. 122, 181 (2002) 121. S. Forrest, P. Burrows, M. Thompson, IEEE Spectr. 37, 29 (2000) 122. C.D. Dimitrakopoulos, P.R.L. Malenfant, Adv. Mater. 14, 99 (2002) 123. M. Wohlgenannt, Z.V. Vardeny, J. Shi, T.L. Francis, X.M. Jiang, O. Mermer, G. Veeraraghavan, D. Wu, Z.H. Ziong, IEE Proc. Circuits Devices Syst. 152(4), 385 (2005) 124. S. Pramanik, C.-G. Stefanita, S. Patibandla, S. Bandyopadhyay, K. Garre, N. Harth, M. Cahay, Nat. Nanotechnol. 2, 216 (2007) 125. H.Y. Hwang, S.W. Cheong, N.P. Ong, B. Batlogg, Phys. Rev. Lett. 77, 2041 (1996) 126. A.P. Ramirez, J. Phys.: Condens. Matter 9, 8171 (1997) 127. H. Bassler, Polym. Adv. Technol. 9, 402 (1998) 128. G. Schmidt, D. Ferrand, L.W. Molenkamp, A.T. Filip, B.J. van Wees, Phys. Rev. B: Condens. Matter 62, R4790 (2000)

126 129. 130. 131. 132.

133. 134. 135.

136. 137. 138. 139. 140. 141. 142. 143. 144. 145. 146. 147. 148. 149. 150. 151. 152. 153. 154. 155. 156. 157. 158. 159.

5 Some Basic Spintronics Concepts P.C. van Son, H. van Kempen, P. Wider, Phys. Rev. Lett. 58, 2271 (1987) M. Johnson, R.J. Silsbee, Phys. Rev. B 35, 4959 (1987) R.J. Elliott, Phys. Rev. 96, 266 (1954) C.-G. Stefanita, F. Yun, H. Morkoc, S. Bandyopadhyay, Self-assembled Quantum Structures Using Porous Alumina on Silicon Substrates, in Recent Res. Develop. Phys. vol. 5, p. 703, ISBN 81-7895-126-6, Transworld Research Network 37/661(2), Trivandrum-695 023, Kerala, India, 2004 C.-G. Stefanita, S. Pramanik, A. Banerjee, M. Sievert, A.A. Baski, S. Bandyopadhyay, J. Crystal Growth 268(3–4), 342 (2004) E.Y. Tsymbal, O.N. Mryasov, P.R. LeClair, J. Phys. Condens. Matter 15, R109 (2003) V. Pokalyakin, S. Tereshin, A. Varfolomeev, D. Zaretsky, A. Baranov, A. Banerjee, Y. Wang, S. Ramanathan, S. Bandyopadhyay, J. Appl. Phys. 97, 124306 (2005) R. Saito, G. Dresselhaus, M.S. Dresselhaus, Physical Properties of Carbon Nanotubes (Imperial College, Singapore, 1998) B.W. Alphenaar, K. Tsukagoshi, M. Wagner, J. Appl. Phys. 89(11), 6864 (2001) M.A.M. Gijs, G.E.W. Bauer, Adv. Phys. 46, 285 (1997) E. Hirota, H. Sakakima, K. Inomata, Giant Magneto-resistance Devices (Springer, Berlin, 2002) T. Miyazaki, N. Tezuka, J. Magn. Magn. Mater. 139, L231 (1995) J. Mathon, A. Umerski, Phys. Rev. B 63, 220403 (2001) B.W. Alphenaar, K. Tsukagoshi, H. Ago, Physica E 6, 848 (2000) P.M. Tedrov, R. Merservey, Phys. Rev. Lett. 26, 192 (1971) S. Maekawa, U. Gafvert, IEEE Trans. Magn. 18, 707 (1982) G. Binasch, P. Gr¨ unberg, F. Saurenbach, W. Zinn, Phys. Rev. B 39, 4828 (1989) G. Tatara, H. Fukuyama, Phys. Rev. Lett. 78, 3773 (1997) J.F. Gregg, W. Allen, S.M. Thompson, M.L. Watson, G.A. Gehring, J. Appl. Phys. 79, 5593 (1996) S.F. Zhang, Z. Yang, J. Appl. Phys. 79, 7398 (1996) S. Maekawa, S. Takahashi, H. Imamura, Mater. Sci. Eng. B 84, 44 (2001) N. Garcia, M. Munoz, Y.-W. Zhao, Phys. Rev. Lett. 82, 2923 (1999) J.M. De Teresa, A. Barthelemy, A. Fert, J-P. Contour, F. Montaigne, P. Seneor, Science 286, 507 (1999) J.E. Ortega, F.J. Himpsel, G.J. Mankey, R.F. Willis, Phys. Rev. B 47, 1540 (1993) J. Mathon, M. Villeret, R.B. Muniz, J. d’Albuquerque e Castro, D.M. Edwards, Phys. Rev. Lett. 74, 3696 (1995) P. Segovia, E.G. Michel, J.E. Ortega, Phys. Rev. Lett. 77, 3455 (1996) T. Dimopulos, V. Da-Costa, C. Tiusan, K. Ounadjela, H.A.M. van den Berg, J. Appl. Phys. 89, 7371 (2001) J.S. Moodera, L.R. Kinder, T.M. Wong, R. Meservey, Phys. Rev. Lett. 74, 3273 (1995) S.T. Chui, Phys. Rev. B 55, 5600 (1997) J. Inoue, S. Maekawa, J. Magn. Magn. Mater. 198, 167 (1999) J.S. Moodera, J. Nowak, R.J.M. van de Veerdonk, Phys. Rev. Lett. 80, 2941 (1998)

References

127

160. A.H. MacDonald, T. Jungwirth, M. Kasner, Phys. Rev. Lett. 81, 705 (1998) 161. S. Zhang, P.M. Levy, A.C. Marley, S.S.P. Parkin, Phys. Rev. Lett. 79, 3744 (1997) 162. A. Bychkov, E.I. Rashba, J. Phys. C 17, 6039 (1984) 163. E.I. Rashba, Al. L. Efros, Appl. Phys. Lett. 83(25), 5295 (2003) 164. F. Beuneu, P. Monod, Phys. Rev. B 18, 2422 (1978) 165. A. Blank, C.R. Dunnam, P.P. Borbat, J.H. Freed, J. Magn. Reson. 165, 116 (2003) 166. D. Rugar, R. Budakian, H.J. Mamin, B.W. Chui, Nature 430, 329 (2004) 167. T.D. Stowe, K. Yasumura, T.W. Kenny, D. Botkin, K. Wago, D. Rugar, Appl. Phys. Lett. 71, 288 (1997) 168. J-H. Park, E. Vescovo, H-J. Kim, C. Kwon, R. Ramesh, T. Venkatesan, Nature 392, 794 (1998) 169. R.J. Soulen Jr., J.M. Byers, Science 282 (5386), 85 (1998) 170. J.M. de Teresa, A. Barthelemy, A. Fert, J.P. Contour, F. Montaigne, P. Seneor, Science 286, 507 (1999) 171. R.D.R. Bhat, J.E. Sipe, Phys. Rev. Lett. 85, 5432 (2000) 172. B.T. Jonker, US Patent No. 5,874,749, 23 February 1999 173. S. Datta, B. Das, Appl. Phys. Lett. 56, 665 (1990) 174. J. Nitta, F. Meijer, Y. Narita, H. Takayanagi, Physica E 6, 318 (2000) 175. A.F. Morpurgo, J.P. Heida, T.M. Klapwijk, B.J. van Wees, G. Borghs, Phys. Rev. Lett. 80, 1050 (1998) 176. R.I. Dzhioev, K.V. Kavokin, V.L. Korenev, M.V. Lazarev, B.Ya. Meltser, M.N. Stepanova, B.P. Zakharchenya, D. Gammon, D.S. Katzer, Phys. Rev. B 66, 245204 (2002) 177. T. Hayashi, M. Tanaka, A. Asamitsu, J. Appl. Phys. 87, 4673 (2000)

6 Trends in Magnetic Recording Media

Summary. Magnetic tapes have been popular for nonvolatile information storage for a long time, however the past decade has seen a signiﬁcant growth of new types of memory. This is because of increasing demands for higher data storage densities that have pressured manufacturers to produce storage systems with higher capacity. To meet these demands, the granular ﬁlms of the Co-based alloy were reduced in thickness and grain size, however grain size reduction below ∼10 nm posed problems. This is due to thermal ﬂuctuations becoming uncontrollable, therefore leading to loss of information. The present chapter discusses the latest developments aimed at overcoming these challenges. As such, the capabilities and limitations encountered by magnetic tapes as recording media are reviewed. Additionally, new tendencies in magnetic recording media are uncovered, by examining closer discrete bit media. The latter have proven so far to have several distinct advantages over continuous media. This is in part due to their discrete bit-cells being able of maintaining a thermally stable single domain remanent state. For this reason, it appears that bit patterning the magnetic medium may be the key for next generation magnetic data storage solutions if certain challenges are overcome. As an alternative route, self-assembly may constitute the means of manufacturing future magnetic media, therefore a brief look is taken at this option.

6.1 The Popularity of Magnetic Tapes Magnetic tapes are economical because of their reduced per-bit cost and high reliability. It is therefore not surprising that they have constituted for decades an adequate medium for archival data storage. Traditionally, magnetic recording media are made of magnetically hard layers such as hcp Co-based alloys containing Pt, Cr, Ta, and B sputter deposited onto an NiP-coated aluminum or glass substrate [1]. Of course, the magnetic easy axis of Co coincides with its hcp c-axis. Moreover, the magnetic layer itself consists of a single sheet of ﬁne, single-domain grains [2]. Usually, the magnetic easy axis of the grains is in the plane of the ﬁlm; however, a perpendicular easy axis is preferred for the

130

6 Trends in Magnetic Recording Media

reason of increased data storage capabilities. If the grains are longitudinally oriented, the bulk (or resultant) magnetization of a group of grains forming a bit-cell is either oriented to the left or right. In perpendicular media, this orientation is up or down. A protective coating made of carbon covers the ﬁlm stack, which also includes various underlayers below the magnetic ﬁlm [3]. Nevertheless, due to the fabrication process the magnetic grains have random crystallographic orientation and are of irregular size. If the substrate is crystallographically textured, it inﬂuences the direction of the easy axis of the magnetic layer, making reorientation possible along some preferred direction [4]. 6.1.1 Quality of Magnetic Tapes Studies performed on longitudinal magnetic media containing CoCrPt in an SiO2 matrix have shown that the deposition rate is a key element for the quality of the tape. High deposition rates of, for instance, 10 nm s−1 are very desirable; nevertheless, they result in faulty microstructure and harmful heating of the substrate. The SiO2 matrix was earlier proved to reduce magnetic grain coupling, thereby lowering media noise without any further heating, annealing, or some other processing [5]. In the CoCrPt studies, diﬀerences in microstructure grain size and orientation were examined with bright ﬁeld and dark ﬁeld transmission electron microscopy (TEM) for varying deposition rates (Figs. 6.1 and 6.2). A slower deposition rate produced a better deﬁned SiO2 network that minimized coupling between the magnetic grains, results conﬁrmed by a similar experiment [6]. The nonmagnetic phase of SiO2 separated the grains well, given that boundary segregation of oxides had been reported by other researchers [7, 8] to be an important factor in fabricating well-isolated Co grains. Moreover, oxidation conditions were responsible for the isolation between Co grains and their increased coercivity [9], while media noise performance depended on the oxide type [10].

Fig. 6.1. (a) Bright ﬁeld and (b) dark ﬁeld TEM images of magnetic media produced with a deposition rate of 0.28 nm s−1 (reprinted from [42] (copyright 2006) with permission from the IEEE)

6.1 The Popularity of Magnetic Tapes

131

Fig. 6.2. (a) Bright ﬁeld and (b) dark ﬁeld TEM images of magnetic media produced with a deposition rate of 0.05 nm s−1 (reprinted from [42] (copyright 2006) with permission from the IEEE)

The thickness of the magnetic layer is expected to result in dissimilarities in the degree of Co grain isolation and grain size, in addition to diﬀerences in exchange coupling [11]. Yet, no particular trend was observed for a given thickness as far as crystallographic and magnetic c-axis orientations were concerned [12]. Even so, an optimum signal-to-noise ratio and best possible media writability require a compromise in layer thickness, coercivity, and grain microstructure [13]. Additionally, concessions have to be made in the choice of materials including the intermediate layer [14] between the granular recording ﬁlm and the soft magnetic underlayer [15]. 6.1.2 The Pressure for Higher Capacity Magnetic Tapes Demands for increased data storage densities have placed more pressure on manufacturers to produce magnetic tape systems with higher capacity. Not long ago, areal recording densities for ﬂexible media had reached 3 Gbits in.−2 for metal particulate media [16], and about 11.5 Gbits in.−2 for metal evaporated media [17]. To further increase data storage of conventional magnetic tapes, the granular ﬁlm of the Co-based alloy is reduced in thickness and grain size, allowing larger coercivities [18]. Each grain behaves as a single magnetic particle displaying a certain degree of exchange coupling to its neighbors [19]. 6.1.3 Constraints Imposed by Thermal Stability When the grain size is reduced below ∼10 nm, thermal ﬂuctuations become uncontrollable, and a spontaneous reversal of grain magnetization cannot be prevented [20]. The magnetic energy per grain becomes too small to avoid such thermally activated reversals. This is known as the superparamagnetic eﬀect, and it leads to the loss of information [21]. If κα is the magnetic anisotropy constant, υ is the magnetic switching volume, and kT is the thermal activation energy, then the thermal stability factor κα ν/kT needs to stay larger

132

6 Trends in Magnetic Recording Media

than 60 to keep the thermally activated reversal manageable for conventional longitudinal recording media [22]. To maintain a suﬃcient signal-to-noise ratio for these types of media, the number of grains per bit should not be reduced. Thus, only the grain volume υ can be made smaller. At the same time, κα cannot be increased limitless, as the required magnetic ﬁeld for writing a bit would also need to be enhanced, and with existing head designs only ﬁelds that do not exceed 15 kOe can be produced [23]. With these constraints, magnetic heads can currently write only on ∼8 nm diameter magnetic grains [24]. Longitudinal granular media have a distribution of small grain diameters that leads to increased thermal activation reversals, predominantly at densities higher than [25] 100 Gbits in.−2 . For perpendicular recording, the instability of the magnetization due to the onset of superparamagnetism sets the limit to densities of 0.5–1.0 Tbits in.−2 [26]. In fact, single domains are expected to form below a certain size due to lesser energy demands for the formation of a domain wall, as compared to those required to create a two-domain state [27]. If the latter were divided by a domain wall, the magnetic island would not be in a stable state [28]. The magnetization would reverse or domains would nucleate when the domain wall would move rapidly [29]. For high-quality recording, the magnetic islands must not reverse magnetization under thermal activation and become superparamagnetic [27]. 6.1.4 Forming a Bit A suﬃciently strong external magnetic ﬁeld can switch the magnetization of individual magnetic grains. Assuming the grains remain stable, if information is recorded on the randomly oriented granular medium, contributions from several hundred grains need to be averaged to form a bit which can be read with suﬃciently high signal-to-noise ratio. To improve the latter, it is best to use magnetically textured media where the easy magnetization axes are preferentially oriented along the track [30]. However, if the magnetic tape contains metal particles and they are being reduced in size, it becomes diﬃcult to sustain suﬃcient coercivity. Therefore, other types of ﬁne particles with large coercivity such as iron nitride [31] and Ba ferrite [32] have been suggested as an alternative. A magnetic tape containing 21 nm (plate diameter) Ba ferrite particles produced using an advanced precision coating process was recently studied [33] for its improved magnetic recording properties. The volume of the particles was roughly 36% smaller than that of metal particles of 45 nm length. Despite their smaller volume, the coercivity of 160 kA m−1 was nearly equal to that of metal particles, and the thermal stability factor was estimated at 65, high enough to ensure stability. Furthermore, the stack of layers was similar to the one used in actual magnetic recording, as it comprised the magnetic layer, an underlayer, a substrate of polyethylene naphthalate base ﬁlm, and a back coat layer.

6.1 The Popularity of Magnetic Tapes

133

A reduction in magnetic layer thickness to 65 nm with less than 10% thickness variation was possible due to the advanced precision coating process. The main result of the study was the enhanced signal-to-noise ratio of the Ba ferrite particles, a value of 23.5 dB compared to 14.5 dB for the metal particulate tape. It should be mentioned that the signal-to-noise ratio for magnetic tapes is roughly proportional to the number of magnetic grains per bit. Therefore, increasing bit areal density without sacriﬁcing signal-to-noise ratio requires reducing the average grain volume in the magnetic medium. The tapes were evaluated using a metal-in-gap write head with a gap length of 0.2 µm and a track width of 20 µm, as well as a giant magnetoresistive read head with a track width of 1.5 µm and a shield-to-shield length of 0.16 µm. In a typical magnetic recording head, there is an inductive write element, and a magnetoresistive read element. The head is mounted on an air-bearing slider while ﬂying along the data track at nanometer size heights. During the ﬂight along the track, the head stores a sequence of 1 and 0 (i.e., magnetic data) on the magnetic medium by magnetizing into two possible magnetization directions. The information is read back by the read sensor that detects the varying magnetic ﬂux emanating from the magnetized pattern on the track. 6.1.5 Inﬂuence of Magnetic Anisotropy Studies performed in pure and Co/Ti-doped Ba ferrite particles (of hexagonal crystallographic structure) uncovered interesting facts in the role played by the magnetocrystalline and shape anisotropy constants. As expected, the former dominates the latter at all temperatures if the Ba ferrite particles are undoped, giving rise to a uniaxial anisotropy along the c-axis. However, the dominance is reversed for the doped particles where the magnetocrystalline anisotropy is weakened by the ionic substitutions, especially at lower temperatures. This happens in spite of the temperature dependence of both anisotropy constants, where the decrease in temperature should have enhanced the magnetocrystalline anisotropy. With the shape anisotropy becoming larger, the overall magnetic anisotropy is no longer uniaxial, presenting multiple preferred directions for the magnetization. To validate comparison with conventional longitudinal particulate recording media, the particles were assembled with aligned c-axis in the deposition plane [34]. 6.1.6 Choice of Materials Co/Pd [35] and CoCrPt [36] alloys, particularly if prepatterned, are more likely to respond favorably to the thermal stability problem. This is because the entire volume of the magnetic islands is the eﬀective switching unit, yet only for densities below [37] 10 Tbits in.−2 . Barium ferrite particles display characteristics that also make them viable candidates for superior magnetic media, because they meet some of the above requirements while oﬀering a

134

6 Trends in Magnetic Recording Media

chemical stability common to oxide compounds [38]. Lately, areal recording densities of 17.5 Gbits in.−2 [39] have been demonstrated for Ba ferrite particulate media by using a giant magnetoresistive head for reading. These results were partly possible because of the advanced fabrication process employed for the magnetic medium. Due to the use of high dispersion technologies for ﬁne Ba ferrite particles, a smooth surface and uniform particle distribution were obtained in an 80-nm-thick magnetic layer. A high signal-to-noise ratio (∼19 dB) and increased resolution were observed as well. Further observations conﬁrmed these ﬁndings by achieving the same areal recording density of 17.5 Gbits in.−2 in Ba ferrite particulate media, and 31 Gbits in.−2 in CoCrPt–SiO2 sputtered media by a diﬀerent group of researchers [40].

6.2 Bit Patterned Magnetic Media 6.2.1 Bit-Cells These days, bit patterning the magnetic medium is highly favored for next generation magnetic data storage solutions [41]. Discrete bit media have several distinct advantages over continuous media [42], partly because the discrete bitcells are more capable of maintaining a thermally stable single domain remanent state [43]. The latter is characterized by a common and well-deﬁned easy axis of constant orientation with respect to the head read/write elements [44]. Additionally, the anisotropy and hence the coercivity agree with the existing write ﬁeld, while the saturation magnetization can be adjusted to optimize recording [45]. Each bit-cell stores 1 bit of information, resulting in ordered arrays of discrete magnetic entities containing data [46]. Considering that in conventional magnetic media several randomly oriented grains are contained in 1 bit, this contrasts signiﬁcantly with the fact that a bit of patterned media is formed from one single prepatterned grain (Fig. 6.3). Additionally, superparamagnetic behavior in magnetic grains is avoided in media with patterned bits [47]. By employing a previously deﬁned magnetic entity per bit, larger volume magnetic bit-cells became possible. This reduces the number of magnetic switching volumes per bit to one entity, without the statistical averaging over several grains [48]. As a result, the constraints imposed on the magnetic grains of conventional media are avoided, allowing about 1012 prepatterned magnetic bit-cells per surface to be obtained in patterned media. It is estimated that the size and periodicity of the bit-cells are 25 and 35 nm, respectively, assuming an initial recording density of 500 Gbits in.−2 [49]. The bit size determines the switching volume, making bit-cells thermally stable, and yet still reversible by the head technology [50]. At the same time, transitions across and down the track are deﬁned by the bit pattern, and no longer by the magnetic ﬁeld of the head [51].

6.2 Bit Patterned Magnetic Media

135

Fig. 6.3. Conventional (left) and patterned (right) magnetic media. The main difference lies in the fact that for conventional perpendicular media, several randomly oriented grains are contained in 1 bit, whereas the bits of patterned media consist of one single grain that has been prepatterned (reprinted from [49] (copyright 2006) with permission from Solid State Technology and Microlithography World)

6.2.2 Minimizing Errors The magnetic easy axis of each bit and that of the recording head have the same relative orientation with respect to each other, in contrast to the randomly oriented axes of the grains in the plane of the ﬁlm in conventional recording media [52]. However, there is a problem with written-in errors that diﬀer from the usual signal-to-noise ratios. The former are due to statistical ﬂuctuations of the magnetic properties and the locations of the individual dots [53]. The size and shape of the patterned magnetic islands as well as their position may vary from one data cell to another, because of lithography or self-assembly errors in nanoparticle size distribution [54]. Therefore, a magnetoresistive playback head of a certain design must be chosen to maximize playback signal resolution and to minimize sensitivity to noise due to these patterning imperfections. Additionally, the playback signal amplitude experiences a linear loss with ﬁlling ratio or packing density, which represents a percentage of the bit area ﬁlled with magnetic material. It was observed that diﬀerential readers exhibited enhanced performance with respect to spatial resolution and sensitivity to medium imperfections due to their ability to compare bits [55].

136

6 Trends in Magnetic Recording Media

6.2.3 Some Disadvantages of Patterned Bits Patterned bits cannot be easily accommodated due to the geometry of the recording media. Circumferential magnetic texturing [56] is required in patterned longitudinal media which is diﬃcult to achieve using polycrystalline ﬁlms and substrates [57]. A partial solution is to orient the magnetic easy axis normal to the ﬁlm surface to form a perpendicular recording medium. Magnetic force microscopy (MFM) was initially used to observe the magnetization states of these patterned bits [58], and shortly after it was observed that the tip itself can be used to switch the magnetization of a bit [59]. Nevertheless, an MFM can only be used as a laboratory technique for studying magnetization reversals and domain conﬁgurations of patterned media. Otherwise, bits can be reversed inadvertently, as it is only the tip scan height that sets the diﬀerence between reading and writing [60]. To better control writing the bits, local heating can be applied, in addition to the tip ﬁeld [61]. If a current passes between the tip and the island to be written, or an additional ﬁeld is applied, some of the bit reversal can be prevented [62]. Patterned bits must be organized in a circular conﬁguration, so that the head can remain on a single track of units as it goes over a given area. In addition, servo marks need to be deﬁned on the disks to keep the head on a given path. In conventional recording, these servo marks are written on a plain continuous medium with a recording head, but without predetermined track locations. In patterned media, the locations are predeﬁned which requires the servo marks to be patterned. Because of the circular symmetry of magnetic patterns, Cartesian e-beam lithography developed for mask production in the integrated circuit industry cannot be employed eﬃciently. 6.2.4 Solutions for Patterning Bits Eﬃciently A mechanical rotary stage and a ﬁxed e-beam column ensure patterning of a master mold dot-by-dot while the e-beam resist covered master is rotating. After exposure, the resist is developed and reactive ion etching (RIE) is used to transfer the pattern into the master mold substrate. A disk substrate is coated with liquid nanoimprint resist, and the previously obtained master mold is pressed against this disk substrate. The liquid resist reﬂows until the master topography is copied onto the resist and ultraviolet (UV) light is applied to cure the resist and create a solid replica. The resist pattern is afterwards transferred into the disk substrate using RIE. Pillars on the replica correspond to holes on the master mold. After resist stripping and disk substrate cleaning, a magnetic medium (Co/Pt [63] or Co/Pd [64] multilayers) is sputter deposited over the patterned disk substrate. Bit patterned media oﬀer the possibility of increased recording densities, if certain challenges are overcome. For instance, imperfections in bit spacings, size, thickness, and shape, as well as ﬂuctuations in saturation magnetization result in a signal-to-noise ratio similar to that of conventional recording media [65]. In recent years, perpendicular discrete bit media have received

6.2 Bit Patterned Magnetic Media

137

progressively more attention as they display a higher density potential due to larger head write ﬁelds, and enhanced thermal stability of single domain islands. The latter have the advantage of eliminating the jitter noise of conventional media, which usually arises due to grain irregularities in the transitions. Nevertheless, the major diﬀerence between discrete bit and conventional media is the necessity of synchronizing the head position with the predeﬁned island locations [66]. As mentioned, the main source of noise is likely to originate in bit size and bit pitch variations [67, 68]. Therefore, the write ﬁeld has to be well placed to write on the desired bit and not on adjacent bits [46]. Cleanliness and smoothness are also issues, as they can interfere with the ability of the head to ﬂy at the required sub-10 nm ﬂy height [69]. Additionally, the thickness of the medium needs to be of the order of the bit spacing to prevent the head from inadvertently writing neighboring areas with the fringes of the head ﬁeld gradient. Stray ﬁelds from adjacent bits scale with saturation magnetization, and so does the contribution of the shape anisotropy to the total uniaxial anisotropy [70]. 6.2.5 Materials for Bit Patterned Magnetic Media The most likely candidate materials for perpendicular discrete bit media are those with interfacial anisotropy such as Co/Pt [71] or Co/Pd [72] multilayers, as well as CoPtCr alloys [73] grown with the c-axis normal to the surface. High exchange coupling between the individual entities is needed if single domain areas are to be achieved, in contrast to the low exchange that is important in conventional magnetic recording [74]. Patterned bit media do not demand a magnetically soft underlayer as previously used for continuous ﬁlms to channel ﬂux between a small write pole and a large ﬂux return pole. This underlayer would add unneeded complexity to the patterning of the bits, however, it may become again necessary if densities in excess of 1 Tbit in.−2 are envisioned. FePt is a material that instead of being magnetic in the chemically ordered state, it is magnetic in the disordered state [75]. However, it has the advantage that nanoparticles as small as 4 nm diameter have suﬃcient magnetocrystalline anisotropy to remain magnetically stable at these small volumes, avoiding superparamagnetism [76]. Lately in a series of experiments, FePt nanoparticles were fabricated through solution chemistry and seized precipitation [77], the process resulting in a suspension of surfactant coated particles [78]. A substrate dipped into the suspension became covered with FePt nanoparticles that formed self-assembled nanolayers [79]. The FePt nanoparticles were oriented at random [80] and were in a disordered fcc crystallographic phase in which they were magnetic [81]. In some cases, annealing at temperatures higher than 600◦ C was required to induce a phase transformation [82] with the nanoparticles displaying a shared magnetic easy axis [83]. Nevertheless, this latter step can lead to the undesired consequence of particle agglomeration [84, 85]. Alternatively, this eﬀect can

138

6 Trends in Magnetic Recording Media

potentially be eliminated by surfactant chemistry optimization [86], or by hardening the organic matrix with ion beam irradiation [87]. In any case, it is not desirable that some nanoparticles should remain in a disordered fcc phase while others attain some degree of ordering. Therefore, it is necessary to prevent a large scale spreading of anisotropy in the medium [88]. Some studies suggest that ordering depends on particle size [89]. At the same time, there is a chance that alloying with a metallic element may also lead to ordering [90]. In a recent experiment involving chemically ordered antiferromagnetic FePt3 nanoparticles, ion beam irradiation with 700 keV N+ ions at a dose of 1 × 106 ions cm−2 destroyed the chemical order and induced ferromagnetism [91]. Concurrently, it was also observed that this method preserved ﬁlm crystallinity, therefore showing potential to be used for patterning magnetic ﬁlms. 6.2.6 Maintaining Competitiveness Any new nanopatterning methods that are expected to be competitive in the recording media market need to satisfy the four criteria: inexpensive fabrication, capability to produce circular symmetry patterns, have the potential of sub-50 nm resolution, and result in a clean surface for the head to ﬂy over. Lithography processes may meet these requirements; however, they all have their limitations. Optical lithography has a resolution given by λ/(2NA), where λ is the light wavelength used and NA is the system numerical aperture. Various resolution enhancement techniques can be employed, so that a wavelength of 193 nm can achieve 90 nm line widths, with possible reductions to 45 nm using immersion lithography, nevertheless still not suﬃcient for patterning the recording medium. Only extreme UV light or X-rays can achieve the required resolution, however, these techniques are not commercially available due to their prohibitive costs. 6.2.7 Going Nano and Beyond Interference lithography has been proposed as an alternative for disk patterning [92]. Among its accomplishments are magnetic Co nanodots [93], and Co or Ni nanopillars [94] that seem to be studied often [95]. Interference lithography is maskless, as the patterning is done by interference fringes produced by two optical beams giving rise to a pattern period p = λ/2 sin θ, where θ is the half-angle between the two beams. Patterned dots have been obtained through successive 90◦ rotations of the sample between exposures, resulting in patterned areas whose size depends on the power of the laser beam. Consequently, centimeter scale arrays of magnetic nanodots [96] have been successfully fabricated using interference lithography. In addition, the technique can be used for producing a master for nanoimprinting [97], or for local annealing of previously deposited ﬁlms [98].

6.3 Self-assembly and Magnetic Media

139

Due to the limitations imposed by the λ/2 minimum period even at short wavelengths, the sub-50 nm resolution required for discrete bit recording is diﬃcult to achieve by interference lithography. By using a series of diﬀraction gratings for producing interference minima and maxima, achromatic interference is obtained that can overcome the wavelength limit of monochromatic interference. Magnetic nanodots have been patterned this way while the fringe pitch was 100 nm [99]. Another advantage oﬀered by diﬀraction gratings is that they can create circular beams not otherwise accessible due to the linear fringes of conventional interference lithography. Thus, patterns with circular symmetry have been demonstrated [100]. Magnetic nanostructures of sub-100 nm size have been successfully obtained using ion beam bombardment [101] or electron beam (e-beam) lithography [102], although both are expensive and slow writing processes. The resolution is not determined only by the e-beam diameter, but also by resist properties responsible for proximity inﬂuences of the overlapping low level exposures. These occur due to electron scattering in the resist and substrate [103]. In spite of its shortcomings, e-beam lithography should not be dismissed as a viable technique for the fabrication of masks used in master/replication methods. X-ray lithography, in particular that using soft rays (1–10 nm wavelength), also uses a mask fabricated using e-beam lithography, and since X-ray lithography is a parallel process [104], an area as large as the mask can be patterned in a single exposure. Nanoscale features such as 88 nm permalloy dots [105] or 200 nm Co dots [106] have been patterned. Nevertheless, X-ray lithography requires a high intensity X-ray synchrotron. Cost and accessibility remain issues with lithographic processes currently employed in patterned bit media production. While continuous media disks cost only a few dollars, nanopatterning can make disk fabrication economically unacceptable. In addition, patterned features on a nanoscale are challenging to create even at higher costs. A bit areal density of 300 Gbits in.−2 necessitates a 30 nm bit-cell, and under the same prerequisite 1,500 Gbits in.−2 will require a 14 nm cell [144]. Thermally assisted recording [107] or lithography technologies for such feature sizes are not probable to be accessible or cost eﬀective soon enough for the hard drive industry to maintain the current compound annual rate of areal density growth.

6.3 Self-assembly and Magnetic Media 6.3.1 Alumina Templates Self-assembled templates formed through a natural process such as selfordering oﬀer an appealing alternative to expensive lithography methods not only because of cost, but also because of their versatility. Among the favored materials is anodic alumina due to its ease of production where only variables such as voltage [108], current, [109] and pH of the employed acid [110] control

140

6 Trends in Magnetic Recording Media

Fig. 6.4. Scanning electron microscopy (SEM) image of an alumina mask/ membrane self-assembled through a simple anodization process. The alumina membrane displays throughout its thickness a hexagonal array of nanopores similar to a honeycomb structure (C.-G. Stefanita and S. Bandyopadhyay, unpublished)

the fabrication process. Regular hexagonal arrays of nanometer sized pores (most commonly 10–100 nm [111]) can be formed on the surface of aluminum (Fig. 6.4). While the pores reach through the whole layer of anodized aluminum, there is a thin Al2 O3 (alumina) barrier at the bottom of the pores forming an impediment to electrodeposition [112] or evaporation of any material that is supposed to ﬁll the pores [113]. The barrier can be conveniently removed through etching under a reverse dc current and low voltage in a diluted acidic solution [114]. Furthermore, the whole alumina layer, now a template containing the regularly arranged pores [115], can be removed and placed on a diﬀerent substrate. Prior to transfer, the alumina layer can be thinned (Fig. 6.5) to allow e-beam evaporation of a material of choice. Figure 6.6 shows an example of e-beam evaporation of a metal such as Zn, forming a quasiregular array of nanodots. The versatility of alumina templates is also demonstrated in Fig. 6.7 where RIE has been used to replicate the hexagonal pattern on a GaN substrate. If the pores are ﬁlled by ac or dc electrodeposition, depending on pore diameter

6.3 Self-assembly and Magnetic Media

141

Fig. 6.5. SEM image of a cross section of a thinned alumina template displaying regularly spaced nanopores reaching through the thickness of the template (C.-G. Stefanita, F. Yun, and S. Bandyopadhyay, unpublished)

Fig. 6.6. SEM image of quasiordered Zn nanodots obtained by e-beam evaporation through a self-assembled alumina mask. If an electron beam of a heated material strikes the nanopores of an alumina mask, it will deposit minute quantities of that particular material, if the mask is thin enough to allow the beam to penetrate through the pores. The mask is removed after the evaporation and an array of nanodots is obtained on the substrate on which the mask has been placed (C.-G. Stefanita and S. Bandyopadhyay, unpublished)

142

6 Trends in Magnetic Recording Media 5.00

2.50

0

2.50

0 5.00 µm

Fig. 6.7. The regular hexagonal pattern of the alumina mask can be etched onto a substrate, as seen in this atomic force microscopy (AFM) image of a duplicated honeycomb nanopattern on GaN. In general, substrates can be etched on a nanoscale using reactive ion etching and an alumina mask that has been appropriately thinned (C.-G. Stefanita and S. Bandyopadhyay, unpublished)

and template thickness, nanowires of a wide range of diameter and height can be obtained (Fig. 6.8). On the other hand, etching the alumina template in a dilute acidic solution for a well-deﬁned time, just before the template dissolves completely, leaves a collection of hollow alumina nanorods behind (Fig. 6.9). 6.3.2 Guided Self-assembly as a Solution to Long-Range Ordering Given their versatility, self-assembled templates may be the key to obtaining storage densities in excess of 1 Tbit in.−2 that require sub-14 nm resolution, as well as new shapes and proﬁles. When used as a mask, self-assembled templates [116] can be used for etching or depositing just like an exposed resist. The ordered regions can be over 100 µm in size, similar to grains in conventional magnetic recording. Furthermore, the length scales of self-ordering can be increased by templating the surface before further processing using ion beam exposure [117] or interference lithography [118]. The idea of combining lithographic processes with natural templates in what is known as guided

6.3 Self-assembly and Magnetic Media

143

Fig. 6.8. The alumina membrane can be used to selectively electrodeposit under ac or dc conditions metals, semiconductors or organic materials into the nanopores, as seen in this transmission electron microscopy (TEM) image of ZnO nanowires. Arrays of nanowires can be fabricated by electrodeposition in templates that are subsequently removed by etching (C.-G. Stefanita and S. Bandyopadhyay, unpublished)

Fig. 6.9. SEM image of hollow alumina nanorods obtained after etching an alumina template just for enough time to recover the pores without completing removing their surroundings (C.-G. Stefanita and S. Bandyopadhyay, unpublished)

self-assembly is one possible solution to the problem of coherent long-range ordering. There are two categories of techniques that qualify as guided selfassembly: chemical where the surface chemistry is selectively modiﬁed to allow

144

6 Trends in Magnetic Recording Media

formation of nanostructures in some areas [119–121], and topographical where the surface geometry is altered [122]. 6.3.3 Chemically vs. Topographically Guided Self-assembly In chemically guided self-assembly, the surface of the substrate is selectively functionalized (using, e.g., polydimethylsiloxane) so that self-assembled monolayers (SAM) develop, aiding the formation of patterned structures [123]. Conversely, a topographically modiﬁed substrate requires employment of a combination of masks, stamps, and etching to achieve the desired prepatterning. As an example of topographically guided self-assembly, a sputtered perpendicular Co74 Cr6 Pt20 40 nm thick medium was resist-coated and imprinted with an Ni stamp. Additionally, a bit pattern was created in the resist grooves using a polystyrene PMMA block copolymer. After annealing the PMMA, the spheres that formed were selectively removed using an oxygen plasma treatment. Consequently, holes formed in the polystyrene matrix were ﬁlled with spin-on-glass. The matrix was subsequently removed by ion milling, and so was the excess magnetic medium, leaving tracks of magnetic nanodots protected by the spin-on-glass [124]. Packing densities of 450 Gbits in.−2 have been reported for magnetic nanodots fabricated in self-assembled templates [125]. In an opposite type of experiment, thin ﬁlms were deposited on top of alumina masks, giving rise to regular arrays of holes in the ﬁlm, termed “antidots” [126]. 6.3.4 Biological Self-assembled Templates Biological self-assembled templates have also been considered as possible alternatives for data storage media [127]. In particular, the protein ferritin oﬀers promises for magnetic particle growth due to its capability of self-assembling into a hollow sphere with an ∼8 nm cavity. Inside the cavity, FePt or CoPt nanoparticles can be grown in an hcp structure with an arrangement period inﬂuenced only by the ferritin dimensions and not the particle within the ferritin cavity. However, the easy axes of the particles are not easy to orient, and the packing fraction is less than that for conventional recording media [128]. 6.3.5 The Versatility of Block Copolymers As already mentioned, block copolymers are versatile compounds used frequently to generate template surfaces through guided self-assembly. They consist of a polymer chain with two distinct monomers bound together [129]. Because of their ﬂexibility, block copolymers can be used as masks to prepare the substrate prior to the deposition of a magnetic thin ﬁlm. They are usually spun onto a surface, previously prepatterned by interference lithography or RIE. The copolymer migrates to the grooves, leaving the top of the patterned

6.4 Present Alternatives for Discrete Media Production

145

lines free of polymer material. Through subsequent treatment, the block copolymer phase separates producing periodicities of 200–1,500 nm [130], or even ﬁner such as 10–200 nm [131]. The obtained geometry of the periodicities (whether spheres or lamellae) depends on the ratio of the two monomers and the surface energy of the substrate [132]. These periodicities are then utilized as templates for the growth of magnetic nanodots [133], however, sometimes the nanodots themselves are employed as an etch mask, for instance, in the case of a previously deposited Co ﬁlm with W/SiOx caps [134]. In a similar copolymer experiment, it is the gap between the 200 nm hexagonally packed polystyrene spheres that is used for the deposition of Co/Pt multilayers forming a reverse structure [135]. It was also observed that the curvature of the sides of polystyrene spheres can be exploited to alter the properties of Co/Pd ﬁlms [136] deposited in the form of multilayers, and thereby displaying a perpendicular anisotropy, highly desired in magnetic recording [137]. 6.3.6 Inorganic Templates May Still Be Competitive As a substitute for polymer templates, inorganic particles are still used frequently, being capable of forming close-packed arrays on certain types of functionalized surfaces (thereby chemically guided for self-assembly). For example, amorphous SiO2 was turned into spheres on which Co was deposited and oxidized on the walls of the spheres, creating isolated Co nanodots [138]. However, the geometry of the recording medium, in particular, the rotating disk layout imposes the added constraint of tracks with circular symmetry [139] and nanostructure ordering over large areas [140].

6.4 Present Alternatives for Discrete Media Production No matter what fabrication technique is utilized or what type of substrate is chosen, there are still challenges that need to be overcome before selfassembled templates can be reliably employed in discrete bit media production. In the meantime, the magnetic recording community is using master fabrication and inexpensive replication to manufacture CD-ROMs. The master is produced using a laser writer, a rather costly process. Even so, the mass manufacture of CD-ROMs by injection molding from the master is economical and reliable at present. 6.4.1 Patterning with Stampers and Masks At least for now, nanoimprinting oﬀers a viable alternative to expensive fabrication by using a rigid or ﬂexible mold/stamper [141] to emboss a relief pattern into a thermosetting or photocuring polymer resist layer [142]. After the resist

146

6 Trends in Magnetic Recording Media

is patterned with the stamper, the former is used as an etch mask to further transmit the pattern onto the underlying layer [143]. The patterned resist layer acting as an etch mask can be a PMMA layer that was heated above its glass transition temperature and onto which the stamper was pressed. Commonly employed materials for the stamper are Si or SiO2 if the stamper is rigid [144]. Self-assembly can be utilized to pattern the mold or stamper, however, e-beam lithography is routinely employed. Additionally, the primary stamper can be duplicated using nanoimprinting, and the ensuing replica can be used to produce more molds/stampers, such that the duplicated stampers become more economically viable [145]. The patterned layer has to be thick enough to shield the unexposed areas underneath, at least as thick as the necessary etch depth. Trilayers and complex processes which utilize windows are sometimes the answer for better feature depth control [146]. The substrate below the SiO2 ﬁlm to be patterned by RIE is typically a silicon wafer with a thin metal layer on top. The role of the metal layer is to ensure adhesion of the SiO2 ﬁlm above it. Ni or Co pillars with perpendicular anisotropy are usually electroplated in the patterned openings, after which the surface is chemically or mechanically polished to achieve a certain smoothness [147]. In an alternative approach, the pillars can be formed by lift-oﬀ after depositing a Ni or Co ﬁlm onto a nanoimprinted PMMA mask [148]. 6.4.2 Cleanliness Concerns Patterned media require much less severe lithography constraints than silicon processing where exact alignments, transfers, and repeat exposures add several important steps to fabrication. There is, however, the issue of exterior smoothness in disk drive applications, as the recording head is supported by an air bearing of sub-10 nm size while ﬂying above the surface at velocities greater than 40 m s−1 . For this reason, the surface needs to be free of contamination such as resist residue. The cleanliness and smoothness of the surface are key elements in hard disk drive operation; therefore rigorous requirements are enforced during the fabrication process of patterned media [149]. Even the smallest resist contamination can cause a serious collapse in head performance due to the breakdown in the aerodynamic air bearing above the disk surface. The sub-10 nm head disk spacing supporting the head leaves very little room for error while the magnetic recording head is ﬂying above the surface of the disk [150]. Only about 0.2–0.4 nm rms surface roughness are allowed, posing a challenge to fabrication techniques that necessitate a thorough cleaning process without damaging the magnetic ﬁlm [151]. The latter is usually prone to corrosion, and quite often too soft to support a ﬂying head. A hard protective layer such as carbon is typically employed, with the additional requirement of edge protection when patterned elements are involved.

6.4 Present Alternatives for Discrete Media Production

147

6.4.3 Obtaining High Aspect Ratios In discrete bit and equally in discrete track media, it seems that a good compromise for maintaining such small head disk distances is to pattern the substrate rather than the magnetic ﬁlm [152]. By creating deep islands and channels in the disk, the side walls of these etched depressions serve to decouple neighbors from each other [153]. Thereby, the magnetic ﬂux emanating from the channels is greatly reduced when it reaches the read element, without interfering with that of the islands [154]. The disk can be easily cleaned after patterning without disturbing the magnetic ﬁlm, as it does not experience any of the etching processes. However, some protective coating is recommended. It is diﬃcult to use RIE on magnetic layers, in particular when nanoimprinting is employed for resist patterning, as the high aspect ratio necessary for obtaining nanopillars is hard to achieve. Even if this impediment is overcome, releasing the mask is not trivial considering that the adhesion force is high in the increased pillar contact areas. One possible solution is to put an SiO2 layer onto a plating base, etch it and subsequently deposit a magnetic ﬁlm onto the imprinted layer, followed by lift-oﬀ to expose the nanodots [155]. Or, as mentioned before, etch the substrate thereby patterning it and then deposit a magnetic ﬁlm while the side walls of the trenches provide the necessary domain isolation [156]. Imprint patterning and etching the substrate have produced 30 nm Co/Pt nanodots with perpendicular anisotropy [157], and discrete tracks in NiP-coated Al disks on which CoPtCr ﬁlms were deposited [158]. 6.4.4 Types of Nanopatterning Processes Above procedures can be regarded as additive processes for nanopatterning, as the nanopattern is ﬁrst created and then the magnetic ﬁlm is deposited. Generally, the resist or some other layer is patterned into an array of holes, after which the latter are ﬁlled with a magnetic material by using evaporation or sputtering. If using resist, it needs to be removed at the end through lift-oﬀ where the patterned resist is dissolved in a solvent. The deposited ﬁlm on top of the resist is removed along with the resist. In contrast to additive nanopatterning, subtractive processes involve magnetic ﬁlms contained underneath layers meant to serve as masks, and any etching that is done to these layers aﬀects the magnetic ﬁlm as well. The patterned layer turned etch mask ensures that excess magnetic ﬁlm is removed by ion milling, sputter etching, or wet chemical etching, considering that magnetic materials are diﬃcult to etch using RIE. Ion milling is not a greatly selective process, and while diﬀerent materials have similar etch rates, thick polymer masks or hard masks made of metallic ﬁlms have to be employed. For these processes etch masks obtained by self-assembly can be used as an economical alternative to more expensive masks [159].

148

6 Trends in Magnetic Recording Media

6.4.5 Emerging Fabrication Techniques In spite of the diﬃculty of directly patterning the magnetic structures, several prototype techniques have been utilized, among them focused ion beam (FIB) using Ga+ ions [160]. Patterned servo marks [161] or 100 nm patterned bits [162] have been etched in conventional longitudinal recording media using FIB. Irradiation with light ions such as He+ [163] or Ar+ [164] has been employed for spatially modulating the anisotropy of several magnetic systems. Initially ordered ﬁlms of FePt can be disordered to some degree if ion irradiation is combined with thermal annealing, resulting in areas with higher anisotropy [165]. Additionally, it was noticed that Ga+ implantation in CoPtCr ﬁlms resulted in single domain remanent states if the islands were smaller than 70 nm in diameter [166], or that the interfacial anisotropy of Co/Pt multilayers is reduced by FIB [167]. Nevertheless looking on the plus side, the disk surface was suﬃciently clean to ﬂy a recording head above it and permit comparison of readback waveforms from patterned and conventionally written bits. Contact and proximity masks have been used to pattern exposures of light ions. For He+ ions of 30 keV resist masks of 600 nm are necessary, whereas tungsten masks need to only be 200 nm thick [168]. A viable alternative may be oﬀered by selectively blocking ion exposures via contact resist or masks placed directly on the ﬁlms, such as membrane masks made of etched silicon [169]. A few hundred nanometer thick Si membranes are suﬃcient for stopping light ions of tens of kiloelectronvolts [170]. Fabricating membranes for 2.5 in. diameter disks with the sub-50 nm size requirements for discrete bit recording are quite demanding. Projection ion beam lithography may help to reduce the feature size in the masks used in FIB, as the diﬀraction limit of ions does not limit the achievable resolution. With ion wavelengths of the order of 10−5 nm, the diﬀraction limit is only a few nm. An optimistic resolution limit for SiO2 masks was reported to be 14 nm [171], which is higher than the magnetic resolution. The latter is limited by the exchange coupling in the magnetic ﬁlm, nonetheless highly desirable if single domains are to be formed. Magnetic domain walls may propagate from low anisotropy to high anisotropy regions, resulting in poorly deﬁned boundaries and less stability [172]. Nevertheless, it is the dense magnetic feature concern, and the fact that projection systems would require masks ten times larger than the disk diameter if patterning is to be done in one exposure, that have so far limited the use of these techniques [173]. Even more unusual for nanopatterning magnetic ﬁlms is using a conventional AFM tip coated with a barium ferrite solution. The technique is known as dip-pen nanolithography, as the AFM tip is brought into contact with a suitably prepared substrate, resulting in sub-100 nm size features [174]. Although these laboratory tools involving direct writing or etching using focused ions, or some other resourceful idea have been successful at fabricating

6.4 Present Alternatives for Discrete Media Production

149

structures over small areas [175], they lack the high throughput necessary for the industrial fabrication of patterned media. 6.4.6 Discrete Track Media Some proposals advance the idea that discrete track media can be regarded as an eﬃcient way to increase areal densities. For instance, using an e-beam deﬁned resist mask a Co containing magnetic ﬁlm can be etched, thereby patterning the surface of the ﬁlm into tracks [176]. Thus, magnetic properties of discrete track media are comparable, yet only up to a point to those of continuous thin ﬁlms. What they have in common is the similar manner of writing transitions into the tracks. The transition width between adjacent bits, and consequently the linear recording density depend on the size and uniformity of the grains. However, write fringing, erase band, and track-edge noise limit the feasible track density [177]. If the tracks are physically deﬁned, a greater signal-to-noise ratio may be achievable, although writing resolution at the track edges remains a critical challenge. Even if magnetic isolation of grains improves the write resolution at the track edges, with narrow track recording of ∼100 nm or less expected for densities of 1.0 Tbits in.−2 and beyond [178, 179], track edge irregularities are likely to contribute to the track-edge noise. Therefore, at these track widths e-beam lithography is unavoidable, making the additional processing not cost eﬀective. Maybe embossing or nanoimprinting shows more promise, as they involve patterning the substrate prior to thin ﬁlm deposition [180]. Grooves can be ﬁrst etched into a layer covering the disk, and then a magnetic ﬁlm can be deposited on top of the patterned ﬁlm. If the grooves are deep enough, there is reduced likelihood of a readback amplitude. With fabrication issues remaining the main problem, it is up to techniques that have industrial suitability to demonstrate that discrete track patterning has potential. 6.4.7 Identifying Track Locations The role of a magnetic servo pattern is to deﬁne the track positions in order for the magnetic head to repeatably write and read the data bits. During the writing process, the head is ﬂown over the entire disk surface while the servo marks are being recorded, track by track. The recorded servo marks identify the track locations, while the write ﬁeld from the recording head delineates the bit length along the track and the bit width across the track. This process is both slow and expensive, in contrast to the stamping or injection molding of optical media such as CDs and DVDs. There can be a problem of misregistration of the head to the track location after each revolution, due to mechanical vibrations and imperfect head positioning. By patterning the tracks and hence physically making out

150

6 Trends in Magnetic Recording Media

the track locations on the disk, the errors in head tracing can be reduced. Regions between tracks should be nonmagnetic or at a lower level than the head, to prevent the read element from sensing any magnetic response from them. Largely, the read element can be manufactured of comparable width with the write element without concern for side reading, thereby improving fabrication yield and lessening requirements on head tolerances. The track width is still lithographically deﬁned; however, the down track bit transitions are determined by the ﬁeld gradient from the write head, making material requirements for discrete track media similar to those of continuous media [181]. Granular CoPtCr-based ﬁlms [182] deposited onto either prepatterned glass or NiP substrates make it common place to employ conventional magnetic recording materials for discrete track media [183]. 6.4.8 Parallel Writing of Data Initially, preembossed rigid magnetic disks (PERMs) were used for parallel magnetic data recording, where the data were recorded on the lands of a land/groove structure, while the embossed pattern contained track following marks [184]. The whole idea was to write equal information on several disks simultaneously, and that included formatting the media, such as inscribing sector headers or position marks. The PERM disks were manufactured by embossing and etching a land/groove pattern into a glass disk. A magnetoresistive element detected an error signal representative of the track following on these large grooves. Feed forward compensation, achieved by mounting a prepatterned disk onto a spindle, was used for track eccentricity. 6.4.9 Magnetic Lithography for Mass Data Replication To improve the patterning of servo information or for more eﬃcient mass replication of content onto magnetic disk media, several fabrication techniques have been developed, among them magnetic lithography [185]. Using a master or a mask, the magnetic pattern is transferred onto a substrate referred to as a slave. The latter is ﬁrst magnetized uniformly in one direction by an external magnetic ﬁeld, after which the mask is placed in closed contact with the disk, and the direction of the external magnetic ﬁeld is reversed. During this process, the magnetic mask selectively shields the slave disk from the external ﬁeld while the magnetic pattern is transferred onto the disk [186]. Magnetic patterns can be transferred via rigid masks with air channel and vacuum [187], or rigid Si masks with ﬂexible disks such as metal tape [188]. Alternatively, a magnetic pattern can also be transferred by creating a master while etching a substrate and coating the surface with a soft magnetic ﬁlm, covering the grooves and lands. The gap where the substrate is etched prevents magnetic shielding from the grooves, and the pattern can be transferred [189]. Masters employed in magnetic lithography can be used over one million times

6.4 Present Alternatives for Discrete Media Production

151

to print disks [190]. Even perpendicular recording media with coercivities as high as 10 kOe have beneﬁted from the printing technique [191]. Nevertheless, transferring patterns by magnetic lithography is not likely to reach the tens of nanometers resolution required for high density recording. 6.4.10 Magnetic Disk Drives vs. Semiconductor Processing DRAM or semiconductor memory was sold for $100 per GB in 2005, whereas magnetic disk drives were only $1 per GB, in spite of their mechanical complexity [192]. This discrepancy is due to the 1010 features usually necessary on a semiconductor memory wafer, as compared to only 105 typically encountered on 5-in.-diameter wafers of magnetic heads (∼40,000 heads). Magnetic recording heads are fabricated with fewer processing steps than semiconductor-based memories. It is only the track width that needs to be lithographically deﬁned at the minimum size (∼120 nm, half the track pitch in 40 Gbits in.−2 disks), in contrast to the down track spacings between transitions that are deﬁned by the thin ﬁlm deposition process. In this case, a single head and disk may be able to address 30 GB of data [193]. 6.4.11 Head Performance Head performance is typically evaluated as a function of an external variable such as pressure that translates into a determination of spacing. It was argued that perpendicular recording is less sensitive to head spacing than conventional longitudinal recording due to the soft underlayer [194]. However, recent experiments have demonstrated that the two recording techniques have similar sensitivities. To prove this, the projects involved using drives with the same air-bearing design that allowed the drives to respond with a similar change in spacing when the ambient pressure varied. Speciﬁcally, the longitudinal write heads incorporated a dual layer eight turn coil, a 15 µm yoke, and a physical write width of 215 nm. Conversely, the perpendicular write heads contained a single pole, while the physical write width was 150 nm. In both types of drives, the read heads were giant magnetoresistive spin valve sensors with a Co–Fe–Ni–Fe free layer and a physical read width of 115 nm. The drives were placed in a pressure chamber where variations either above or below atmospheric pressure raised or lowered the nominal ﬂying height. The performance of the drives was assessed based on the raw uncorrected bit error rate, or soft error rate [195]. The magnetic ﬁeld dynamics and spatial distribution under the recording pole control the perpendicular recording process. Nonuniform pole footprints accompanied by cross- and down-track degradation of media saturation and overwrite were observed occasionally [196]. Consequently, measurement techniques were developed to assess the stability of perpendicular recording heads. Heads with well-saturated uniform media saturation under the recording pole result in a symmetrical cross-track overwrite proﬁle, whereas heads

152

6 Trends in Magnetic Recording Media

with nonuniform footprints generate asymmetrical cross-track overwrite distribution [197]. The head keeper spacing is the head air-bearing surface to soft underlayer surface, and is one of the critical parameters that aﬀect the writer ﬁeld strength [198] and the playback process [199]. A nondestructive method for determining the head keeper spacing from the playback waveform of a speciﬁc recording pattern was developed for this purpose [200]. 6.4.12 Spin Valves and Giant Magnetoresistive Heads Given their low intrinsic impedances, all-metallic giant magnetoresistive heads in a current-perpendicular-to-plane geometry are appealing for future high density recording sensors. Nevertheless, these impedances are increasing when the cross sectional area of the sensor is reduced, a necessary aspect in keeping up with rising recording densities. To solve the problem, magnetic heads have been redesigned by employing a dual spin valve sensor stack with thin IrMn antiferromagnetic top and bottom pinned layers, as shown in a recent study by Hitachi GST researchers [201]. In a diﬀerent study, corrosion resistant spin valve ﬁlms made of Ta/NiFe/CoNiFe/CuAu/CoNiFe/PtMn/Ta built into conventional shieldtype giant magnetoresistive heads, and tested using a helical-scan tape drive showed a preservation of magnetic properties over 20 days. This occurred despite being exposed to corrosive gas [202], an estimated equivalent of environmental pollution a personal computer experiences over 10 years [203]. Further obstacles need to be overcome in the design of giant magnetoresistive heads, among them an increased signal-to-noise ratio and better resolution, if these heads are to be employed as future recording sensors. 6.4.13 Looking Back and into the Future Since 1956 when IBM launched in the market the ﬁrst magnetic hard disk drive capable of storing about 4.4 MB, the storage density (measured in bits in.−2 ) has increased more than 2 × 107 times [204]. This has been achieved primarily by scaling the components of the disk drive to smaller dimensions so that the head moves closer to the disk, enhancing the write and read resolution [205]. Improvements in head design have increased their performance [206], which means that high coercivity media can be written at high data rates. Yet, bit areal density growth has slowed down from 100% per year experienced over a decade or so to 40% per year in recent years, due to remaining challenges encountered in recording head design, as well as magnetic media fabrication [49]. There seems to be an agreement in the magnetic recording industry that giving up the requirement for multiple grains per bit may settle the thermal stability issue. This leads to the necessity of adopting alternative fabrication and magnetic recording technologies to achieve even higher densities. While

References

153

more traditional magnetic recording approaches start to encounter physical limitations set by the thermal stability of the recorded bits, nanofabrication is oﬀering new solutions for increased data densities [207]. Self-assembled arrays of high anisotropy magnetic nanoparticles may oﬀer a replacement for thin ﬁlm magnetic media, especially if they can be produced extremely small in size [208]. It seems that new doors for higher storage densities and novel disk drives not attainable by scaling current technologies may open if lithography or self-assembly are used for disk patterning [209]. It is currently envisioned that magnetic nanostructures will be the basic units for future patterned media.

References 1. J.G. Zhu, IEEE Trans. Magn. 28, 3267 (1992) 2. K.M. Tako, T. Schreﬂ, M.A. Wongsam, R.W. Chantrell, J. Appl. Phys. 81, 4082 (1997) 3. J.O. Oti, IEEE Trans. Magn. 29, 1265 (1993) 4. J.J. Miles, B.K. Middleton, IEEE Trans. Magn. 26, 2137 (1990) 5. T. Oikawa, M. Nakamura, H. Uwazumi, T. Shimats, H. Muraoka, Y. Nakamura, IEEE Trans. Magn. 38(5), 1976 (2002) 6. L. Wang, H.-S. Lee, Y. Qin, J.A. Bain, D.E. Laughlin, IEEE Trans. Magn. 42(10), 2306 (1006) 7. T. Chiba, J. Ariake, N. Honda, J. Magn. Magn. Mater. 287, 167 (2005) 8. N. Supper, D.T. Margulies, T. Olson, Y. Ikeda, A. Moser, B. Lengsﬁeld, A. Berger, IEEE Trans. Magn. 42(10), 2333 (2006) 9. J. Ariake, T. Chiba, N. Honda, IEEE Trans. Magn. 41, 3142 (2005) 10. G. Choe, A. Roy, Z. Yang, B.R. Acharya, E.N. Abarra, IEEE Trans. Magn. 42(10), 2327 (2006) 11. J. Chen, H.J. Richter, D.Q. Chen, C. Chang, R. Ranjan, J.L. Lee, IEEE Trans. Magn. 40(2), 489 (2004) 12. T. Shimatsu, T. Oikawa, Y. Inaba, H. Sato, I. Watanabe, H. Aoi, H. Muraoka, Y. Nakamura, IEEE Trans. Magn. 40(4), 2461 (2004) 13. U. Kwon, H.S. Jung, M. Kuo, E.M.T. Velu, S.S. Malhotra, W. Jiang, G. Bertero, R. Sinclair, IEEE Trans. Magn. 42(10), 2330 (2006) 14. H. Nemoto, R. Araki, Y. Hosoe, IEEE Trans. Magn. 42(10), 2336 (2006) 15. K. Shintaku, IEEE Trans. Magn. 42(10), 2339 (2006) 16. N. Segikuchi, K. Kawakami, T. Ozue, M. Yamaga, S. Onodera, IEEE Trans. Magn. 41(10), 3235 (2005) 17. T. Ozue, M. Kondo, Y. Soda, S. Fukuda, S. Onodera, T. Kawana, IEEE Trans. Magn. 38(1), 136 (2002) 18. J.C. Mallinson, IEEE Trans. Magn. 32, 599 (1996); H.J. Richter, J. Phys. D: Appl. Phys. 32, R147 (1999) 19. S.H. Charap, P.L. Lu, Y.J. He, IEEE Trans. Magn. 33, 978 (1997) 20. Y. Nakatani, Y. Uesaka, N. Hayashi, Jpn. J. Appl. Phys. 28, 2485 (1989) 21. X. Wang, J.F.d. Castro, K. Gao, Z. Jin, IEEE Trans. Magn. 42(10), 2294 (2006) 22. D. Weller, A. Moser, IEEE Trans. Magn. 35, 4423 (1999)

154

6 Trends in Magnetic Recording Media

23. K.R. Coﬀey, T. Thomson, J-U. Thiele, J. Appl. Phys. 93(10), 8471 (2003) 24. D. Weller, A. Moser, L. Folks, M.E. Best, W. Lee, M.F. Toney, M. Schwickert, J.-U. Thiele, M.F. Doerner, IEEE Trans. Magn. 36, 10 (2000) 25. U. Nowak, D. Hinzke, J. Appl. Phys. 85, 4337 (1999) 26. M.H. Kryder, R.W. Gustafson, J. Magn. Magn. Mater. 287, 449 (2005) 27. J. Fidler, T. Schreﬂ, J. Phys. D: Appl. Phys. 33, R135 (2000) 28. T. Schreﬂ, J. Fidler, J. Magn. Magn. Mater. 111, 105 (1992) 29. E.C. Stoner, E.P. Wohlfarth, IEEE Trans. Magn. 27, 3475 (1991) 30. A. Moser, K. Takano, D.T. Margulies, M. Albrecht, Y. Sonobe, Y. Ikeda, S.H. Sun, E.E. Fullerton, J. Phys. D: Appl. Phys. 35, R157 (2002) 31. Y. Sasaki, N. Usuki, K. Matsuo, M. Kishimoto, IEEE Trans. Magn. 41(10), 3241 (2005) 32. S. Saito, H. Noguchi, Y. Endo, K. Ejiri, T. Mandai, T. Sugizaki, Fujiﬁlm Res. Develop. 48, 71 (2003) 33. T. Nagata, T. Harasawa, M. Oyanagi, N. Abe, S. Saito, IEEE Trans. Magn. 42(10), 2312 (2006) 34. G. Bottoni, IEEE Trans. Magn. 42(10), 2309 (2006) 35. P.F. Carcia, A.D. Meinhaldt, A. Suna, Appl. Phys. Lett. 47(2), 178 (1985) 36. J.H. Judy, J. Magn. Magn. Mater. 287, 16 (2005) 37. E. Miyashita, K. Kuga, R. Taguchi, T. Tamaki, H. Okuda, J. Magn. Magn. Mater. 235, 413 (2001) 38. S. Saitoh, R. Inaba, A. Kashiwagi, IEEE Trans. Magn. 31(6), 2859 (1995) 39. A. Matsumoto, Y. Endo, H. Noguchi, IEEE Trans. Magn. 42(10), 2315 (2006) 40. R.M. Palmer, M.D. Thornley, H. Noguchi, K. Usuki, IEEE Trans. Magn. 42(10), 2318 (2006) 41. C.T. Rettner, M.E. Best, B.D. Terris, IEEE Trans. Magn. 37(4), 1649 (2001) 42. G. Herzer, IEEE Trans. Magn. 25, 3327 (1989) 43. A. Lyberatos, D.V. Berkov, R.W. Chantrell, J. Phys.: Condens. Matter. 5, 8911 (1993) 44. R. Skomski, J. Phys.: Condens. Matter. 15, R841 (2003) 45. W. Wernsdorfer, Adv. Chem. Phys. 118, 99 (2001) 46. G.F. Hughes, IEEE Trans. Magn. 36(2), 521 (2000) 47. T. Schreﬂ, J. Fidler, K.J. Kirk, J.N. Chapman, J. Magn. Magn. Mater. 175, 193 (1997) 48. J. Lohau, A. Moser, C.T. Rettner, M.E. Best, B.D. Terris, Appl. Phys. Lett. 78, 990 (2001) 49. Z.Z. Bandic, E.A. Dobisz, T.-W. Wu, T.R. Albrecht, Solid State Technol. S7 (2006) 50. M. Ichida, K. Yoshida, IEEE Trans. Magn. 42(10), 2291 (2006) 51. A.F. Torabi, D. Bai, P. Luo, J. Wang, M. Novid, IEEE Trans. Magn. 42(10), 2288 (2006) 52. B. Yang, D.R. Fredkin, IEEE Trans. Magn. 43, 3842 (1998) 53. B. Yang, D.R. Fredkin, J. Appl. Phys. 79, 5755 (1996) 54. R. Fischer, T. Leineweber, H. Kronm¨ uller, Phys. Rev. B 57(10), 723 (1998) 55. D. Smith, E. Chunsheng, S. Khizroev, D. Litvinov, IEEE Trans. Magn. 42(10), 2285 (2006) 56. R.M.H. New, R.F.W. Pease, R.L. White, R.M. Osgood, K. Babcock, J. Appl. Phys. 79, 5851 (1996) 57. M. Albrecht, S. Ganesan, C.T. Rettner, A. Moser, M.E. Best, R.L. White, B.D. Terris, IEEE Trans. Magn. 39, 2323 (2003)

References

155

58. G.A. Gibson, S. Schultz, J. Appl. Phys. 73, 4516 (1993) 59. M. Kleiber, F. Kummerlen, M. Lohndorf, A. Wadas, D. Weiss, R. Wiesendanger, Phys. Rev. B 58, 5563 (1998) 60. C.A. Ross, H.I. Smith, T. Savas, M. Schattenburg, M. Farhoud, M. Hwang, M. Walsh, M.C. Abraham, R.J. Ram, J. Vac. Sci. Technol. B 17, 3168 (1999) 61. M. Lohndorf, A. Wadas, G. Lutjering, D. Weiss, R. Wiesendanger, Z. Phys. B: Condens. Matter. 101, 1 (1996) 62. C. Haginoya, K. Koike, Y. Hirayama, J. Yamamoto, M. Ishibashi, O. Kitakami, Y. Shimada, Appl. Phys. Lett. 75, 3159 (1999) 63. T. Suzuki, Scripta Met. Mat. 33(10–11), 1609 (1995) 64. T.C. Ulbrich, D. Makarov, G. Hu, I.L. Guhr, D. Suess, T. Schreﬂ, M. Albrecht, Phys. Rev. Lett. 96, 077202 (2006) 65. H.J. Richter, A.Y. Dobin, O. Heinonen, K.Z. Gao, R.J.M. v.d. Veerdonk, R.T. Lynch, J. Xue, D. Weller, P. Asselin, M.F. Erden, R.M. Brockie, IEEE Trans. Magn. 42(10), 2255 (2006) 66. R.L. White, R.M.H. New, R.F.W. Pease, IEEE Trans. Magn. 33, 990 (1997) 67. S.K. Nair, R.M.H. New, IEEE Trans. Magn. 34, 1916 (1998) 68. M.M. Aziz, B. Middleton, C.D. Wright, IEE Proc. Sci. Meas. Technol. 150, 232 (2003) 69. S.Y. Yamamoto, S. Schultz, Appl. Phys. Lett. 69, 3263 (1996) 70. G.F. Hughes, IEEE Trans. Magn. 35, 2310 (1999) 71. O. Hellwig, S. Maat, J.B. Kortright, E.E. Fullerton, Phys. Rev. B 65, 144418 (2002) 72. S. Maat, K. Takano, S.S.P. Parkin, E.E. Fullerton, Phys. Rev. Lett. 87(8), 087202-1 (2001) 73. B.D. Terris, M. Albrecht, G. Hu, T. Thomson, C.T. Rettner, IEEE Trans. Magn. 41(10), 2822 (2005) 74. I. Navarro, E. Pulido, P. Crespo, A. Hernando, J. Appl. Phys. 73, 6525 (1993) 75. Y.K. Takahashi, K. Hono, S. Okamoto, O. Kitakami, J. Appl. Phys. 100, 074305 (2006) 76. J.W. Harrell, S. Wang, D.E. Nikles, M. Chen, Appl. Phys. Lett. 79, 4393 (2001) 77. S.H. Sun, C.B. Murray, D. Weller, L. Folks, A. Moser, Science 287, 1989 (2000) 78. J.A. Christodoulides, M.J. Bonder, Y. Huang, Y. Zhang, S. Stoyanov, G.C. Hadjipanayis, A. Simopoulos, D. Weller, Phys. Rev. B 68, 054428 (2003) 79. T. Hyeon, Chem. Commun. 8, 927 (2003) 80. T. Thomson, M.F. Toney, S. Raoux, S.L. Lee, S. Sun, C.B. Murray, B.D. Terris, J. Appl. Phys. 96, 1197 (2004) 81. H. Kodama, S. Momose, N. Ihara, T. Uzumaki, A. Tanaka, Appl. Phys. Lett. 83, 5253 (2003) 82. Z.R. Dai, S.H. Sun, Z.L. Wang, Nano Lett. 1, 443 (2001) 83. Y. Ding, S. Yamamuro, D. Farrell, S.A. Majetich, J. Appl. Phys. 93, 7411 (2003) 84. A.C.C. Yu, M. Mizuno, Y. Sasaki, M. Inoue, H. Kondo, I. Ohta, D. Djayaprawira, M. Takahashi, Appl. Phys. Lett. 82, 4352 (2003) 85. S.M. Momose, H. Kodama, N. Ihara, T. Uzumaki, A. Tanaka, Jpn. J. Appl. Phys. 42, L1252 (2003) 86. T. Thomson, B.D. Terris, M.F. Toney, S. Raoux, J.E.E. Baglin, S.L. Lee, S. Sun, J. Appl. Phys. 95, 6738 (2004) 87. J.E.E. Baglin, S. Sun, A.J. Kellock, T. Thomson, M.F. Toney, B.D. Terris, C.B. Murray, Mater. Res. Soc. Symp. Proc. 777, T6.5.1 (2003)

156

6 Trends in Magnetic Recording Media

88. H. Sakuma, T. Taniyama, Y. Kitamoto, Y. Yamazaki, H. Nishio, H. Yamamoto, J. Appl. Phys. 95, 7261 (2004) 89. Y.K. Takahashi, T. Ohkubo, M. Ohnuma, K. Hono, J. Appl. Phys. 93, 7166 (2003) 90. S.S. Kang, D.E. Nikles, J.W. Harrell, X.W. Wu, J. Magn. Magn. Mater. 266, 49 (2003) 91. S. Maat, A.J. Kellock, D. Weller, J.E.E. Baglin, Eric E. Fullerton, J. Magn. Magn. Mater. 265, 1 (2003) 92. B. Vogeli, H.I. Smith, F.J. Castano, S. Haratani, Y. Hao, C.A. Ross, J. Vac. Sci. Technol. B B19, 2753 (2001) 93. A. Fernandez, P.J. Bedrossian, S.L. Baker, S.P. Vernon, D.R. Kania, IEEE Trans. Magn. 32, 4472 (1996) 94. M. Farhoud, J. Ferrera, A.J. Lochtefeld, T.E. Murphy, M.L. Schattenburg, J. Carter, C.A. Ross, H.I. Smith, J. Vac. Sci. Technol. B 17, 3182 (1999) 95. Y. Hao, F.J. Casta˜ no, C.A. Ross, B. V¨ ogeli, M.E. Walsh, H.I. Smith, J. Appl. Phys. 91(10), 7989 (2002) 96. A. Carl, S. Kirsch, J. Lohau, H. Weinforth, E.F. Wassermann, IEEE Trans. Magn. 35, 3106 (1999) 97. W. Wu, B. Cui, X.Y. Sun, W. Zhang, L. Zhuang, L.S. Kong, S.Y. Chou, J. Vac. Sci. Technol. B 16, 3825 (1998) 98. L. Gao, S.H. Liou, M. Zheng, R. Skomski, M.L. Yan, D.J. Sellmyer, N. Polushkin, J. Appl. Phys. 91, 7311 (2002) 99. T.A. Savas, M. Farhoud, H.I. Smith, M. Hwang, C.A. Ross, J. Appl. Phys. 85, 6160 (1999) 100. H.H. Solak, C. David, J. Vac. Sci. Technol. B 21, 2883 (2003) 101. Y.J. Chen, J.P. Wang, E.W. Soo, L. Wu, T.C. Chong, J. Appl. Phys. 91(10), 7323 (2002) 102. C.A. Ross, Annu. Rev. Mater. Sci. 31, 203 (2001) 103. J.C. Lodder, J. Magn. Magn. Mater. 272–276, 1692 (2004) 104. H.I. Smith, J. Vac. Sci. Technol. B 13, 2323 (1995) 105. C. Miramond, C. Fermon, F. Rousseaux, D. Decanini, F. Carcenac, J. Magn. Magn. Mater. 165, 500 (1997) 106. F. Rousseaux, D. Decanini, F. Carcenac, E. Cambril, M.F. Ravet, C. Chappert, N. Bardou, B. Bartenlian, P. Veillet, J. Vac. Sci. Technol. B 13, 2787 (1995) 107. J.U. Thiele, S. Maat, J.L. Robertson, E.E. Fullerton, IEEE Trans. Magn. 40(4), 2537 (2004) 108. S. Pramanik, C.-G. Stefanita, S. Bandyopadhyay, J. Nanosci. Nanotechnol. 6(7), 1973 (2006) 109. R.M. Metzger, V.V. Konovalov, M. Sun, T. Xu, G. Zangari, B. Xu, M. Benakli, W.D. Doyle, IEEE Trans. Magn. 36, 30 (2000) 110. P. Aranda, J.M. Garcia, J. Magn. Magn. Mater. 249, 214 (2002) 111. C.-G. Stefanita, F. Yun, M. Namkung, H. Morkoc, S. Bandyopadhyay, Electrochemical Self-assembly as a Route to Nanodevice Processing, ed. by H.S. Nalwa. in Handbook of Electrochemical Nanotechnology (American Scientiﬁc, Stevenson Ranch, 2006) 112. M. Sun, G. Zangari, M. Shamsuzzoha, R.M. Metzger, Appl. Phys. Lett. 78, 2964 (2001) 113. C.-G. Stefanita, F. Yun, H. Morkoc, S. Bandyopadhyay, Self-assembled Quantum Structures Using Porous Alumina on Silicon Substrates, in Recent Res. Devel. Physics 5: 703, Transworld Research Network 37/661 (2), Trivandrum695 023, Kerala, India (2004), ISBN 81-7895-126-6

References

157

114. C.-G. Stefanita, S. Pramanik, A. Banerjee, M. Sievert, A.A. Baski, S. Bandyopadhyay, J. Cryst. Growth 268(3–4), 342 (2004) 115. K. Liu, J. Nogues, C. Leighton, H. Masuda, K. Nishio, I.V. Roshchin, I.K. Schuller, Appl. Phys. Lett. 81, 4434 (2001) 116. R. Zhu, Y.T. Pang, Y.S. Feng, G.H. Fu, Y. Li, L.D. Zhang, Chem. Phys. Lett. 368, 696 (2003) 117. N.W. Liu, A. Datta, C.Y. Liu, Y.L. Wang, Appl. Phys. Lett. 82, 1281 (2003) 118. Z.J. Sun, H.K. Kim, Appl. Phys. Lett. 81, 3458 (2002) 119. S.O. Kim, H.H. Solak, M.P. Stoykovich, N.J. Ferrier, J.J. de Pablo, P.F. Nealey, Nature 424, 411 (2003) 120. M. Kimura, M.J. Misner, T. Xu, S.H. Kim, T.P. Russell, Langmuir 19, 9910 (2003) 121. L. Rockford, S.G.J. Mochrie, T.P. Russell, Macromolecules 34, 1487 (2001) 122. A.A. Zhukov, M.A. Ghanem, A. Goncharov, P.A.J. de Groot, I.S. El-Hallag, P.N. Bartlett, R. Boardman, H. Fangohr, J. Magn. Magn. Mater. 272–276, 1621 (2004) 123. S. Palacin, P.C. Hidber, J.P. Bourgoin, C. Miramond, C. Fermon, G.M. Whitesides, Chem. Mater. 8, 1316 (1996) 124. K. Naito, H. Hieda, M. Sakurai, Y. Kamata, K. Asakawa, IEEE Trans. Magn. 38, 1949 (2002) 125. Z.B. Zhang, D. Gekhtman, M.S. Dresselhaus, J.Y. Ying, Chem. Mater. 11, 1659 (1999) 126. Z.L. Xiao, Appl. Phys. Lett. 81, 2869 (2002) 127. B.D. Reiss, C.B. Mao, D.J. Solis, K.S. Ryan, T. Thomson, A.M. Belcher, Nano Lett. 4, 1127 (2004) 128. E. Mayes, A. Bewick, D. Gleeson, J. Hoinville, R. Jones, O. Kasyutich, A. Nartowski, B. Warne, J. Wiggins, K.K.W. Wong, IEEE Trans. Magn. 39, 624 (2003) 129. I.W. Hamley, Nanotechnology 14, R39 (2003) 130. J.Y. Cheng, C.A. Ross, E.L. Thomas, H.I. Smith, G.J. Vancso, Appl. Phys. Lett. 81, 3657 (2002) 131. C. Harrison, J.A. Dagata, D.H. Adamson, in Developments in Block Copolymer Science and Technology, ed. by I.W. Hamley (Wiley, New York, 2003) 132. Y. Kamata, A. Kikitsu, H. Hieda, M. Sakurai, K. Naito, J. Appl. Phys. 95, 6705 (2004) 133. X.M. Yang, C. Liu, J. Ahner, J. Yu, T. Klemmer, E. Johns, D. Weller, J. Vac. Sci. Technol. B 22, 31 (2004) 134. J.Y. Cheng, C.A. Ross, V.Z.H. Chan, E.L. Thomas, R.G.H. Lammertink, G.J. Vancso, Adv. Mater. 13, 1174 (2001) 135. P.W. Nutter, H. Du, V. Vorithitikul, D. Edmundson, E.W. Hill, J.J. Miles, C.D. Wright, IEE Proc. Sci. Meas. Technol. 150, 227 (2003) 136. D.G. Stinson, S-C. Shin, J. Appl. Phys. 67(9), 4459 (1990) 137. M. Albrecht, G. Hu, I.L. Guhr, T.C. Ulbrich, J. Boneberg, P. Leiderer, G. Schatz, Nature Mater. 4, 203 (2005) 138. S.P. Li, W.S. Lew, Y.B. Xu, A. Hirohata, A. Samad, F. Baker, J.A. Bland, Appl. Phys. Lett. 76, 748 (2000) 139. C. Harrison, D.H. Adamson, Z.D. Cheng, J.M. Sebastian, S. Sethuraman, D.A. Huse, R.A. Register, P.M. Chaikin, Science 290, 1558 (2000) 140. R.A. Segalman, H. Yokoyama, E.J. Kramer, Adv. Mater. 13, 1152 (2001)

158

6 Trends in Magnetic Recording Media

141. M. Colburn, A. Grot, B.J. Choi, M. Amistoso, T. Bailey, S.V. Sreenivasan, J.G. Ekerdt, C.G. Willson, J. Vac. Sci. Technol. B 19, 2162 (2001) 142. S.Y. Chou, P.R. Krauss, W. Zhang, L.J. Guo, L. Zhuang, J. Vac. Sci. Technol. B 15, 2897 (1997) 143. S.Y. Chou, P.R. Krauss, L.S. Kong, J. Appl. Phys. 79, 6101 (1996) 144. S.Y. Chou, P.R. Krauss, P.J. Renstrom, J. Vac. Sci. Technol. B 14, 4129 (1996) 145. G.M. McClelland, M.W. Hart, C.T. Rettner, M.E. Best, K.R. Carter, B.D. Terris, Appl. Phys. Lett. 81, 1483 (2002) 146. M. Natali, A. Lebib, E. Cambril, Y. Chen, I.L. Prejbeanu, K. Ounadjela, J. Vac. Sci. Technol. B 19, 2779 (2001) 147. S.Y. Chou, Proc. IEEE 85, 652 (1997) 148. L.S. Kong, L. Zhuang, S.Y. Chou, IEEE Trans. Magn. 33, 3019 (1997) 149. Y. Soeno, M. Moriya, K. Ito, K. Hattori, A. Kaizu, T. Aoyama, M. Matsuzaki, H. Sakai, IEEE Trans. Magn. 39, 1967 (2003) 150. N. Tagawa, A. Mori, Microsyst. Technol., Micro-Nanosyst. Inf. Storage Proc. Syst. 9, 362 (2003) 151. N. Tagawa, T. Hayashi, A. Mori, J. Tribol.-Trans. ASME 123, 151 (2001) 152. S. Landis, B. Rodmacq, B. Dieny, Phys. Rev. B 62, 12271 (2000) 153. S. Landis, B. Rodmacq, B. Dieny, B. Dal’Zotto, S. Tedesco, M. Heitzmann, J. Magn. Magn. Mater. 226, 1708 (2001) 154. G. Hu, T. Thomson, M. Albrecht, M.E. Best, B.D. Terris, C.T. Rettner, S. Raoux, G.M. McClelland, M.W. Hart, J. Appl. Phys. 95, 7013 (2004) 155. L.S. Kong, L. Zhuang, M.T. Li, B. Cui, S.Y. Chou, Jpn. J. Appl. Phys. 37, 5973 (1998) 156. J. Moritz, B. Dieny, J.P. Nozieres, S. Landis, A. Lebib, Y. Chen, J. Appl. Phys. 91, 7314 (2002) 157. J. Moritz, S. Landis, J.C. Toussaint, P. Bayle-Guillemaud, B. Rodmacq, G. Casali, A. Lebib, Y. Chen, J.P. Nozieres, B. Dieny, IEEE Trans. Magn. 38, 1731 (2002) 158. D. Wachenschwanz, W. Jiang, E. Roddick, A. Homola, P. Dorsey, B. Harper, D. Treves, C. Bajorek, IEEE Trans. Magn. 41, 670 (2005) 159. C. Ross, Annu. Rev. Mater. Res. 31, 203 (2001) 160. C.T. Rettner, M.E. Best, B.D. Terris, IEEE Trans. Magn. 37, 1649 (2001) 161. X.D. Lin, J.G. Zhu, W. Messner, IEEE Trans. Magn. 36, 2999 (2000) 162. J.G. Zhu, X.D. Lin, L.J. Guan, W. Messner, IEEE Trans. Magn. 36, 23 (2000) 163. W.H. Bruenger, C. Dzionk, R. Berger, H. Grimm, A. Dietzel, F. Letzkus, R. Springer, Microelectron. Eng. 61–62, 295 (2002) 164. A. Dietzel, R. Berger, H. Loeschner, E. Platzgummer, G. Stengl, W.H. Bruenger, F. Letzkus, Adv. Mater. 15, 1152 (2003) 165. D. Ravelosona, T. Devolder, H. Bernas, C. Chappert, V. Mathet, D. Halley, Y. Samson, B. Gilles, A. Marty, IEEE Trans. Magn. 37, 1643 (2001) 166. C.T. Rettner, S. Anders, T. Thomson, M. Albrecht, Y. Ikeda, M.E. Best, B.D. Terris, IEEE Trans. Magn. 38, 1725 (2002) 167. C.T. Rettner, S. Anders, J.E.E. Baglin, T. Thomson, B.D. Terris, Appl. Phys. Lett. 80, 279 (2002) 168. J. Fassbender, D. Ravelosona, A. Samson, J. Phys. D.: Appl. Phys. 37, R179 (2004) 169. P. Warin, R. Hyndman, J. Glerak, J.N. Chapman, J. Ferre, J.P. Jamet, V. Mathet, C. Chappert, J. Appl. Phys. 90, 3850 (2001)

References

159

170. B.D. Terris, D. Weller, L. Folks, J.E.E. Baglin, A.J. Kellock, H. Rothuizen, P. Vettiger, J. Appl. Phys. 87, 7004 (2000) 171. T. Devolder, C. Chappert, Y. Chen, E. Cambril, H. Bernas, J.P. Jamet, J. Ferre, Appl. Phys. Lett. 74, 3383 (1999) 172. J.G. Kusinski, K.M. Krishnan, G. Denbeaux, G. Thomas, B.D. Terris, D. Weller, Appl. Phys. Lett. 79, 2211 (2001) 173. J. Melngailis, A.A. Mondelli, I.L. Berry, R. Mohondro, J. Vac. Sci. Technol. B 16, 927 (1998) 174. F. Lu, X.G. Liu, Y. Zhang, V.P. Dravid, C.A. Mirkin, Nano Lett. 3, 757 (2003) 175. B.D. Terris, L. Folks, D. Weller, J.E.E. Baglin, A.J. Kellock, H. Rothuizen, P. Vettiger, Appl. Phys. Lett. 75, 403 (1999) 176. S.E. Lambert, I.L. Sanders, A.M. Patlach, M.T. Krounbi, IEEE Trans. Magn. 23, 3690 (1987) 177. K. Miura, D. Sudo, M. Hashimoto, H. Muraoka, H. Aoi, Y. Nakamura, IEEE Trans. Magn. 42(10), 2261 (2006) 178. R. Wood, IEEE Trans. Magn. 36(1), 36 (2000) 179. M. Mallary, A. Torabi, M. Benaki, IEEE Trans. Magn. 38(4), 1719 (2002) 180. T. Ishida, O. Morita, M. Noda, S. Seko, S. Tanaka, H. Ishioka, IEEE Trans. Fund. Electron. Commun. Comput. Sci. E76A, 1161 (1993) 181. H.N. Bertram, Theory of Magnetic Recording (Cambridge University Press, Cambridge, 1994) 182. H.J. Richter, IEEE Trans. Magn. 35, 2790 (1999) 183. D. Weller, M.F. Doerner, Annu. Rev. Mater. Sci. 30, 611 (2000) 184. K. Watanabe, T. Takeda, K. Okada, H. Takino, IEEE Trans. Magn. 29, 4030 (1993) 185. S.A. Nikitov, L. Presmanes, P. Tailhades, D.E. Balabanov, J. Magn. Magn. Mater. 241, 124 (2002) 186. Z.Z. Bandic, H. Xu, Y.M. Hsu, T.R. Albrecht, IEEE Trans. Magn. 39, 2231 (2003) 187. T. Ishida, K. Miyata, T. Hamada, H. Hashi, Y.S. Ban, K. Taniguchi, A. Saito, IEEE Trans. Magn. 39, 628 (2003) 188. R. Sugita, O. Saito, T. Muranoi, M. Nishikawa, M. Nagao, J. Appl. Phys. 91, 8694 (2002) 189. R. Sugita, T. Muranoi, M. Nishikawa, M. Nagao, J. Appl. Phys. 93, 7008 (2003) 190. T. Ishida, K. Miyata, T. Hamada, K. Tohma, IEEE Trans. Magn. 37, 1875 (2001) 191. A. Saito, T. Ono, S.J. Takenoiri, IEEE Trans. Magn. 39, 2234 (2003) 192. http://www.reed-electronics.com/semiconductor 193. M. Plummer et al. (ed.), The Physics of High Density Recording (Springer, Berlin, 2001) 194. Y. Tanaka, J. Magn. Magn. Mater. 287, 468 (2005) 195. S. Gebredingle, S. Gider, R. Wood, IEEE Trans. Magn. IEEE Trans. Magn. 42(10), 2273 (2006) 196. A. Taratorin, K.B. Klaassen, IEEE Trans. Magn. 42(2), 157 (2006) 197. A. Taratorin, K.B. Klaassen, IEEE Trans. Magn. 42(10), 2267 (2006) 198. I.D. Mayergoyz, P. McAvoy, C. Tse, C. Kraﬀt, C. Tseng, IEEE Trans. Magn. 42(10), 2282 (2006) 199. Z.J. Liu, J.T. Li, K.S. Chai, L. Wang, IEEE Trans. Magn. 42(10), 2279 (2006) 200. Z. Jin, C. Fu, X. Wang, Y. Zhou, J. F.d.Castro, IEEE Trans. Magn. 42(10), 2270 (2006)

160

6 Trends in Magnetic Recording Media

201. J.R. Childress, M.J. Carey, M.-C. Cyrille, K. Carey, N. Smith, J.A. Katine, T.D. Boone, A.A.G. Driskell-Smith, S. Maat, K. Mackay, C.H. Tsang, IEEE Trans. Magn. 42(10), 2444 (2006) 202. M. Sekine, T. Watanabe, Y. Tamakawa, T. Shibata, Y. Soda, IEEE Trans. Magn. 42(10), 2321 (2006) 203. D.W.D. Williams, IEEE Trans. Compon., Hybrids Manuf. Technol. 11(10), 36 (1988) 204. L. Gomes, Talking Tech, The Wall Street Journal (August 22, 2006) 205. E. Grochowski, D.A. Thompson, IEEE Trans. Magn. 30, 3797 (1994) 206. W. Scholz, S. Batra, IEEE Trans. Magn. 42(10), 2264 (2006) 207. http://public.itrs.net 208. X.W. Wu, K.Y. Guslienko, R.W. Chantrell, D. Weller, Appl. Phys. Lett. 82, 3475 (2003) 209. S.Y. Chou, IEEE Trans. Magn. 85, 652 (1997)

7 Concluding Remarks

Materials research and nanomagnetic phenomena are intertwined ﬁelds that inevitably lead to rapid developments of future technologies of increased performance. The interest in nanomagnetics is not just a fashionable trend in today’s science and engineering, but rather a natural consequence of technological progress. Novel physical phenomena are uncovered when magnetic systems are reduced to nanoscale. For instance, semiconductor electronics is traditionally based on the manipulation of charge, nevertheless it is expected that reduction in device dimensions as seen by Moore’s law will reach its fundamental limits by 2010 [1]. Since electrons carry both spin and charge, they oﬀer the possibility of combining the two and thereby adding a new degree of freedom to modern devices. An encoder can write information using spin polarization in one part of a spintronic device, while itinerant electrons convey this information to a physically diﬀerent part where it is decoded. These processes occur in nanodevices, as the spin diﬀusion length is in that length scale. Similarly, perpendicular recording media and the challenges posed in magnetic recording by superparamagnetism have their origin in the size of magnetic domains or the width of the domain walls, as well as exchange length, all of them governed by a balance of energy terms at the nanoscale. Nevertheless, magnetism at small length scales has developed in recent years to encompass a wealth of information, solving many of the problems once thought insurmountable. The most intriguing discoveries in magnetics are yet to come. Depending on future developments, new directions in the many aspects of magnetism will be uncovered, adding to the complexity of this ﬁeld. These will shape our preferences for certain areas, perhaps rendering others obsolete. Be that as it may, the magnetism ﬁeld itself can only be enriched as the human mind strives to conquer new realms of knowledge.

Reference 1. H.S.P. Wong, D.J. Frank, P.M. Solomon, C.H.J. Wann, J.J. Welser, Proc. IEEE 87, 537 (1999)

Index

[100], 11 [111], 11 ‘artiﬁcial’ antiferromagnetic structure, 73 2DEG, 109 absolute temperature, 3–5, 8 dielectric transition temperature, 55 sintering temperature, 54 adiabatic passage, 117 air bearing, 146 Airy ring, 47 alumina membrane, 143 analyzer, 44, 45 Andreev reﬂection, 119, 120 angle, 6 angular, 6 angular momentum, 7, 11 angular momentum operators, 7 angular momentum quantum number, 8 individual atomic orbital, 7 total angular momentum quantum number, 9 anisotropic magnetoresistance, 82 anisotropic magnetoresistive sensors, 82 anisotropy, 10, 134 magnetocrystalline anisotropy, 10, 25, 137 annealing, 29, 33, 49, 77, 82, 130, 137, 138, 148 anodic alumina, 139 anodization, 113 anomalous Hall eﬀect, 89, 108

antiferromagnetic coupling, 72, 73, 84 antiferromagnetic order, 81, 105 antiferromagnetism, 4 antiferroelectric, 52 antiferromagnetic, 52 antiferromagnetic material, 4 atomic magnetic moment, 23 axis of easy magnetization, 13, 23, 25–28, 42–44, 132, 136, 137 crystallographic easy axis, 24 shape-induced easy axis of magnetization, 75 uniaxial direction of easy magnetization, 44 bainite, 34 ballistic, 110 ballistic pure spin current, 111 Barkhausen jumps, 109 Barkhausen noise encircling Barkhausen noise, 20 bcc, 9 Biot-Savart law, 51 bipolar spin switch, 91 bit, 42, 50, 73, 83, 91, 132, 133, 135 bit error rate, 151 bit pitch, 137 bit transitions, 78 Patterned, 136 bit patterning, 134, 144 bit reversal, 136 bit-cell, 42, 130, 134 Bloch wall, 13, 117 Bohr magneton, 7, 101

164

Index

Boltzmann transport equation, 74 bridge, 92 bridge deﬂections, 92 microbridges, 92 Brillouin function, 9 bulk magnetization, 130 bulk scattering, 83 spin-dependent bulk scattering, 83 carbide precipitation, 34 carbon nanotubes, 114 cationic species, 90 cementite, 34 chemical vapor deposition, 16 chemically guided self-assembly, 145 CIP, 103 clamped switching, 61 cluster beam deposition process, 74 cobalt, 85 Co, 10 coercivity, 10, 14, 25, 41, 46–50, 72, 76, 77, 80, 81, 85, 132, 134 coercive, 14 wall coercivity, 51 cold rolling, 27, 28, 31 colloidal suspensions, 13 colossal magnetoresistance, 89, 90 compliance, 53 conduction band of metals, 4 conductivity mismatch, 110, 113 controlled spin precession, 121 Cooper pairs, 119 corrosion, 36, 46, 76, 80, 152 corrosion defects, 36 Coulomb interaction, 5 couple of forces, 5 coupled multilayer structures, 71 coupling ﬁeld, 79, 80 CPP, 90, 91 crack formation, 35 critical length scale, 103 cross-track, 152 crystal, 11, 23 crystal lattice, 11 crystal symmetry, 23, 25, 64 cubic, 11 single-crystal, 58 crystal ﬁeld, 9, 10 crystal structure, 9, 43

crystallographic axis, 11, 13 preferred, 13 crystallographic direction, 10, 23, 27 preferred, 10 crystallographic orientation, 29, 32, 38, 58, 130 crystallographic texture, 31, 32, 38, 130 Curie, 52 Curie point, 49, 105, 109 Curie temperature, 5, 89 dielectric Curie temperature, 55 ferroelectric Curie temperature, 58 Curie–Weiss law, 4, 9 current loop, 3, 51 current-in-plane, 102 current-perpendicular-to-plane, 83, 102 data storage densities, 129, 131 Datta and Das transistor, 121 Debye, 52 deformation, 33, 58 elastic deformation, 27, 28 plastic deformation, 24, 27, 28, 30, 31 degenerate energy, 7 degenerate states, 7 demagnetized, 3 demagnetizing ﬁeld, 86 density of states spin asymmetry, 106 diamagnetism diamagnetic material, 3 diamagnets, 4 diluted magnetic seimiconductor, 88 dip-pen nanolithography, 148 discrete bit recording, 139 dislocations, 21, 27, 30, 31 DMS, 106 domain conﬁguration, 24 domain magnetization, 3, 12, 27 direction of domain magnetization, 23 domain wall, 12–14, 21, 24 domain wall displacement, 14 N´eel wall, 13 pinning, 14 domain wall motion, 23 dual spin valve, 84, 85, 152 e-beam evaporation, 140 e-beam lithography, 136, 139

Index eﬀective aperture, 47 eigenvalues, 7, 8 electric-ﬁeld-induced ordering, 61 electrical spin injection, 103 electrochemical potential, 91 electrodeposition, 140 electromagnet, 52 electron-hole pair excitation, 88 electron-magnon interactions, 89 electron-phonon coupling, 89 Elliott-Yafet, 113, 114 energy, 12, 22, 30, 31 Bloch wall, 51 domain wall energy, 31 energy conﬁguration, 24 energy density, 59 exchange energy, 13, 22 magnetic, 8 magnetocrystalline, 24 magnetocrystalline (anisotropic) energy, 23 magnetocrystalline energy, 13, 24 magnetoelastic, 24 magnetoelastic energy, 23, 29, 33 magnetoelastic energy density, 59 magnetostatic energy, 12, 13, 23, 24 thermal, 8 wall energy, 30 evaporated media, 129 exchange bias, 75, 78, 81 exchange coupling, 42, 48, 49, 105, 131, 137, 148 exchange energy, 12, 13 exchange interaction, 3, 75, 89 exchange split, 86 exchange spring magnet, 80 exchange-spring pinning layers, 80 expectation value, 8 extraordinary magnetoresistance, 83 Faraday rotation, 43, 50 fatigue, 35 Fermi level, 87–89, 99, 100, 104, 117, 118 ferrimagnetism, 5, 55 ferrielectric, 52 ferrimagnetic, 9 ferrimagnetic material, 5 ferrites, 5, 53, 54

165

ferrite ferrite cylinder, 21 ferritin, 144 ferroelectric order, 105 ferroﬂuids, 13, 14 ferroics, 61, 64 ferromagnetic metallic state, 63 ferromagnetic ordering, 63, 64 ferromagnetic oxides, 104 ferromagnetism, 3, 5, 22, 58, 88 ferromagnetic, 10, 12, 14, 52 ferromagnetic material, 19–22, 24, 25, 27 ﬁnite element analysis, 36 ﬁnite element method, 58 ﬁrst-order perturbation, 7 ﬂexible media, 131 focused ion beam, 148 force, 5 driving force, 49 exchange force, 13, 22, 51 interbubble repulsive force, 50 magnetizing force, 5 restoring force, 33 free energy of crystal, 64 free layer, 75, 81 g-factor, 101 giant magnetoresistance, 71, 104 giant planar Hall eﬀect, 109 GMR, 85, 91, 105, 113, 114, 116, 118 GMR head, 133 guided self-assembly, 143 half-metallic ferromagnet, 89, 104, 107, 113 half-metallic ferromagnetic oxides, 105 Hamiltonian, 8 head, 132, 134, 136–138, 151, 152 giant magnetoresistive head, 152 hard disk drive read head, 78 head design, 76 high density recording head, 84 inductive write head, 76 magnetic read head, 78 magnetoresistive playback head, 135 metal-in-gap write head, 133 planar recording head, 83 recording head, 136

166

Index

sensing head, 91 write head, 77 head resolution, 84 head tracing, 150 Heusler alloys, 89, 104 hexagonal arrays, 140 hot electrons, 87 hot holes, 88 hysteresis, 3, 14, 20, 58, 75, 78, 81, 112 asymmetric hysteresis, 80 hysteresis cycle, 19 in-plane ﬁeld sensitivity, 83 injection eﬃciency, 107 injection molding, 149 insulating tunnel barrier, 82 insulator-metal transition temperature, 90 interface scattering, 73, 83, 111 spin-dependent interface scattering, 83 interference lithography, 138, 144 intergranular impurity segregation, 34 interlayer exchange coupling, 85 interlayer oscillatory exchange energy, 73 inverse GMR, 86 ion beam deposition, 91 ion beam etching, 42, 43 ion milling, 147 ion-beam milling, 91 iron, 10, 11, 13, 14, 23, 75–78 Armco iron, 35 Fe, 10 silicon iron, 44 itinerant holes, 89 Joule, 10 Julli`ere, 87, 114 Kerr rotation, 43, 46, 48, 81 lamella carbide, 34 laminated composite, 61 lamination, 55, 57 Land´e g-factor, 7 lattice, 5, 11, 13, 23, 30, 54, 55, 58 crystalline lattice, 23, 27 lattice distortion, 32, 83

lattice irregularities, 21 lattice match, 58, 107 lattice misﬁt, 58 lattice spacings, 24 lattice mismatch, 90, 104 law of cosines, 7 Lenz’s law, 3 lift-oﬀ, 147 load, 26 reloading, 36 uniaxial tensile load, 26 unloaded specimens, 30 unloaded state, 29 unloading, 29 local Hall eﬀect, 110 localized spins, 108 lodestone, 2 long-range ordering, 61, 142 longitudinal recording media, 132 Lorentz force, 83 macroscopic elastic limit, 30 magnet single-domain magnets, 14 magnetic oxide semiconductors, 105 magnetic anisotropy, 10, 14, 19, 25–27, 31, 41, 46, 54, 59, 60, 76, 81, 89 induced, 25 interfacial anisotropy, 137 magnetic anisotropy constant, 43, 131 magnetocrystalline anisotropy, 9, 10, 133 perpendicular anisotropy, 146 roll magnetic anisotropy, 31, 32 shape anisotropy, 15, 74, 133, 137 uniaxial anisotropy, 133, 137 uniaxial magnetic anisotropy, 41 magnetic Barkhausen noise, 14, 19, 24, 25, 41, 75, 77 acoustic Barkhausen noise, 20 Barkhausen jump, 30 Barkhausen noise emissions, 33 Barkhausen transition, 30 dislocation tangles, 30, 33 grain boundary, 21, 22, 30 inhomogeneities, 21 Irreversible discontinuities, 20 irreversible jump, 21

Index local obstacles, 21 magnetoacoustic emission, 20 pinning, 25 Pinning Sites, 21, 24, 30, 31 surface Barkhausen noise, 20 magnetic cluster, 14, 15 magnetic dipole, 6 magnetic domain, 3, 6, 11–14, 21, 24, 27, 30, 33, 35, 38, 44 adjacent domain, 21 closure domain, 13, 14 cue bubble, 50 domain boundary, 24 domain wall displacement detection, 49 domain wall jumps, 31 domain wall motion, 24, 54 domain wall pinning, 33 DWDD, 51 Magnetic bubble domain, 49, 50 magnetic domain conﬁguration, 19, 23, 28, 30, 31 magnetic domain wall, 19, 23, 25, 42, 50 motion of domain wall, 33 original conﬁguration, 21 spike (or residual) domain, 34 wall mobility, 51 magnetic domain wall, 19, 23, 25, 132 domain wall population, 25 wall displacement, 21, 22, 30 magnetic easy axis, 129 magnetic ﬁeld, 11, 12, 21 magnetic ﬁeld density, 57 magnetic ﬁeld intensity, 2–8, 14, 20, 22–24, 43, 46, 51, 53, 56, 59 bias ﬁeld, 50 magnetic ﬁeld, 47 magnetizing ﬁeld, 21 static magnetic ﬁeld, 63 vortex magnetic ﬁeld, 63 magnetic ﬁeld lines, 5 magnetic ﬂux density, 3, 13, 25, 37, 51, 77 magnetic ﬂux leakage, 19, 36 magnetic force microscopy, 58, 60, 136 magnetic hardening, 78 magnetic lithography, 150

167

magnetic moment, 2, 3, 6, 8–10, 52, 82, 86 atomic magnetic, 9 atomic magnetic moment, 6, 9, 13 orbital moment, 9 spin moment, 9 magnetic nanodot, 138, 144 magnetic order, 64 magnetic pattern, 150 magnetic permeability, 37 permeability of vacuum, 2, 5, 52, 54 magnetic phase hard magnetic phase, 15 soft magnetic phase, 15 magnetic polarity, 44 magnetic pole strength, 6 magnetic poles, 5 magnetic quantum dots, 15 magnetic recording read head, 73, 133 magnetic resolution, 148 magnetic resonance, 119 magnetic semiconductors, 110 magnetic shield, 83 magnetic susceptibility, 2, 5 relative, 2, 3 magnetic tape, 129–132 magnetic texture, 27, 84, 132, 136 magnetic tunnel junctions, 110 magnetic tunnel transistor, 88 magnetic tunneling, 87 magnetic writing, 45, 46, 48, 50 magnetically homogeneous, 6 magnetically isotropic, 2, 81 magnetite, 2 magnetization, 2, 5, 6, 9, 13, 14, 46, 47, 52, 72, 136 bulk magnetization, 24 bulk net magnetization, 21 discontinuous changes, 21 domain magnetization, 10, 11, 13, 14, 24, 44 electric ﬁeld-induced magnetization, 52 free layer magnetization, 78 induced, 4 magnetization curve, 20 magnetization process, 19

168

Index

magnetization realignment, 24 reversal, 14, 42, 80 magnetization direction, 6, 24 magnetic orientation, 21 random magnetic orientation, 22 magnetization rotation, 64 magneto-optical, 49 magneto-optical media, 41 magnetoelectric, 41, 51–55, 105 magnetostatic N´eel coupling, 80 magnetostriction, 10, 11, 53–55, 57, 76, 82 isotropic saturation magnetostriction, 11 longitudinal magnetostriction, 11 magnetostrictive, 53 positive magnetostriction, 78 magnetotransport, 91 magnetron sputtering, 74, 81, 84 majority or minority states, 89 manganite perovskites, 89, 107, 117 mark, 46–49, 51 servo mark, 136 martensite, 34 master, 136, 138, 145 mean free path, 87, 103, 104 media, 138 conventional longitudinal particulate recording media, 133 Discrete bit media, 134 particulate media, 129, 134 perpendicular discrete bit media, 136 plain continuous medium, 136 recording media, 135 sputtered media, 134 metal evaporated media, 131 metalorganic chemical vapor deposition, 108 metamaterials, 15 micro-SQUID, 91 microcantilever, 92 micromagnetism, 11 Micromagnetic, 11 micromagnetometer, 91 microyielding, 30, 36 minority spin electrons, 79, 87 molecular beam epitaxy, 16, 71, 108 momentum scattering, 112 Mott’s model, 86, 100, 117

MRFM, 119 multiferroics, 61 multilayer structure, 86 MWNT, 114 N´eel temperature, 4, 5 nanocomposite, 58, 59 nanodot, 140 nanofabrication, 153 nanoimprinting, 138, 149 nanolithography, 16 nanopatterning, 147 nanopillar, 57–59, 82, 138 nanorods, 142 nanostructure, 14, 16, 58, 60 nanostructure ordering, 145 nanowire arrays, 74 negative GMR, 106 negative magnetoresistance, 72 net magnetization current, 100 nickel, 13, 75–77 annealed nickel, 33 cold-worked Ni, 34 Ni, 10 Ni stamper, 46 nickel-iron iron, 44 nondestructive evaluation, 11, 19, 37 nondestructive testing, 19, 24 nonmagnetic spacer layer, 86, 87, 102 numerical aperture, 138 optical lithography, 138 optical readout, 43, 44, 46–49 orbital moment, 10 orbital motion, 2, 3, 6, 9 organic semiconductor spacers, 112, 113 organic semiconductors, 112 oscillatory interlayer exchange coupling, 72, 80 parallel resistor model, 116 paramagnetic-ferromagnetic transition temperature, 90 paramagnetism, 3, 4 paramagnet, 4, 8 paramagnetic, 5, 52 paramagnetic ions, 63 partially ﬁlled, 3

Index partition function, 8 partly ﬁlled electron shells, 6 patterned bit, 136 patterned bit media, 139 patterned media, 134, 136 Pauli exclusion principle, 2, 13 permalloy, 76, 77, 83, 86, 139 permanent magnet, 2, 5, 6, 10, 14, 15, 36 PERMs, 150 perovskite, 64 phase scattering length, 114 phase space, 23 piezoelectric force microscopy, 58 piezomagnetic, 53 pseudopiezomagnetic, 53 pinned layer, 75 pinning, 80 pinning layer, 75, 81 plastic yielding, 36 polar graph, 25, 26 polarize/analyze experiments, 102 pole, 5 north, 5 south, 5 porous alumina, 112 positive and negative polarons, 112 positive magnetoresistance, 72 potential energy, 6 precession, 7 preferred directions of magnetization, 133 prepatterned magnetic bit-cells, 134 projection ion beam lithography, 148 pulse height distribution, 26–28, 30, 31 pulsed laser deposition, 58, 90 PZT, 53, 55, 58, 61, 63 quantum computing, 15 quantum dots, 16 quantum mechanical phase coherence, 100 quantum states, 7 quenching, 9, 10 random orientations, 3 rare-earth transition metals, 10, 45, 54, 63 Rashba, 118, 121

169

reactive ion etching, 136 recorded track, 84 recording head, 146, 148 recording medium, 145 reference layer, 84 remanence, 14, 58 replication, 145 resolution, 47, 134, 135, 138, 149 crosstrack resolution, 83 downtrack resolution, 83 super resolution, 47 resonance, 57 rf magnetron sputtering, 92 RIE, 140, 144, 146, 147 RKKY interaction, 88 saturation, 3, 11, 45, 53, 57, 82, 105, 134, 137 saturation magnetization, 9 saturation ﬂux density, 76 scaling, 152 Schottky barrier, 88, 107, 113 selective electrodeposition, 143 self-assembled arrays, 153 self-assembled monolayers, 144 self-assembly, 16, 57, 135, 137, 139, 142 chemical, 143 topographical, 144 self-ordering, 139 self-pinning, 81 SEM, 141 sensing layer, 75, 82 sensor, 152 cantilever-based force sensors, 119 CPP GMR sensor, 84 CPP sensor, 83 density recording sensor, 152 detection coil, 20 eddy-current probe sensor, 19 GMR sensor, 73, 78, 83 Hall sensor, 36 magnetic sensor, 76 magnetic–electric sensor, 41, 60 magnetoresistive read sensor, 76 MBN sensor, 25 multiferroic sensor, 63 read sensor, 82, 133 search coil, 21 small gap sensor, 81

170

Index

spin valve sensor, 80, 91 ultra-high density head sensor, 85 valve sensor, 151 sintering, 54, 55, 90 skin depth, 21 slip plane, 27 slipping, 27 spacer layer, 75, 91, 104 spatial resolution, 82 spectroscopic splitting factor, 7 spheroidized carbide, 34 spin, 2–6, 9–11, 46 spin rotation, 54 spin–spin interactions, 22 unpaired, 22 spin accumulation, 91, 103, 111 spin accumulation rate, 103 spin aligner, 111 spin angular momentum, 6 individual atomic, 7 spin band, 101 spin channels, 100, 107, 111, 116 spin coherent propagation, 121 spin conductance, 101 spin density, 103 spin dependent scattering, 74 spin detector, 121 spin diﬀusion length, 90, 103, 106, 114 spin electronics or spintronics, 15 spin ﬁeld eﬀect transistor, 121 spin ﬁltering, 101, 102, 106 spin ﬂipping, 107 spin injection, 108 spin injection eﬃciency, 101, 107 spin injector, 113, 121 spin mixing, 111 spin polarization, 3, 87, 101, 104, 106, 110, 114, 119 spin relaxation, 103, 111–114 spin scattering, 72, 73, 112 spin torque, 85 spin transfer, 101, 102 spin transfer torque, 101 spin transmission resonance, 102 spin transport asymmetry, 74 spin valve, 75, 78, 80, 81, 83, 90–92, 106, 112 nanowire spin valves, 113 spin valve transistors, 87

spin–orbit, 9 spin–orbit coupling, 10, 121 spin-dependent scattering, 90 spin-dependent transmission, 72 spin-diﬀusion length, 91 spin-down, 72–75, 86, 100, 103, 106 spin-ﬂip scattering, 86, 100, 114 spin-ﬂip time, 103 spin-orbit eﬀect, 101 spin-polarized hot electrons, 88 spin-reversal domain, 64 spin-rotation domain, 64 spin-selective scattering, 87 spin-up, 72–75, 86, 100, 103, 106 spin-up and spin-down photons, 111 spintronic devices, 87 spintronics, 105 spontaneous magnetization, 10, 12, 108 spontaneous magnetization reversal, 129, 131 spontaneous spin polarization, 101 spontaneously magnetized, 3, 5 sputtering, 147 stamper, 48, 146 steel, 29, 31, 35 decarburized steel, 33 ferritic–pearlitic steel, 35 low carbon steel, 34 mild steel, 35 plain carbon steels, 34, 38 steel plate, 37 unstrained mild steel, 34 strain, 11, 23, 24, 53–55, 58, 60, 89, 104 elastic strain, 28 magnetostrictive strain, 57 plastic strain, 24, 29 principal strain direction, 63 residual strain, 58, 60 strain ﬁeld of the dislocation, 32 strain ﬁelds, 27, 30, 33 strain hardening, 36 strengths, 5 stress, 14, 19, 22, 24, 29, 30, 32, 53 anisotropic stress, 32 applied stress, 24, 29 applied tensile stress, 33 applied uniaxial tensile stress, 24

Index bending stress, 35 compression and compresive stress, 29, 32, 35, 53 compressive elastic, 35 compressive elastic stress, 27 compressive plastic, 35 compressive stress, 24, 25, 27 compressive stress conﬁgurations, 37 critical-resolved shear stress, 27, 32 elastic intergranular stresses, 29 elastic stress, 24, 27, 28, 30, 37 elastic tensile, 27 internal elastic stress, 24 internal stress, 38, 77, 78 longitudinal residual stresses, 60 macroscopic stress, 32 maximum shearing stress, 27, 28 mechanical stress, 55 microscopic stress, 32 plastic stress, 31, 35, 37 plastic stress regime, 30 principal stress, 27, 28 residual stress, 19, 26, 28–32, 35, 38, 60 stress concentration, 30 stress conﬁgurations, 19 stress direction, 25 stress distributions, 30 stress ﬁelds, 23 stress relief, 29 stress state, 19 stress-induced, 24, 27 tensile plastic stress, 35 tensile stress, 25 tension, 29 threshold stress, 33 uniaxial tensile stress, 26, 35 sudden passage, 117 superparamagnetic eﬀect, 129, 131 superparamagnetism, 132, 134, 137 switchable domain, 61, 64 SWNT, 114 symmetry operation, 64

171

TEM, 130, 143 temperature absolute temperature, 9 Terfenol-D, 54, 55, 61, 63 thermal activation energy, 131 thermal activation reversal, 132 thermal agitation, 3 thermal expansion coeﬃcient, 42 thermal ﬂuctuations, 129, 131 thermal reversal, 41 thermal stability, 133, 137 thermal stability factor, 131, 132 thermally assisted recording, 139 TMR, 114, 118 topographically modiﬁed substrate, 144 torque, 5, 6 total resultant magnetization, 3 track, 48, 49, 132, 149 pitch, 48 track width, 133 track-edge, 149 transmission probability, 101 transverse magnetostriction magnetostriction, 11 transverse relaxation time T2 , 100 trilayer, 113 tunnel barrier, 106 tunnel contact, 107 tunnel junction, 106 tunneling magnetoresistance, 82, 108 two-current representation, 91 uncompensated interfacial spins, 75 unpaired electron spins, 3, 9 Valet-Fert model, 90, 91 vibrating sample magnetometry, 81 voltage coeﬃcient, 56, 57 work hardening, 32 X-ray diﬀraction, 29, 30, 104 X-ray lithography, 42, 43, 139 yield point, 29 yield strength, 35

Springer Series in

materials science Editors: R. Hull

R. M. Osgood, Jr.

50 High-Resolution Imaging and Spectrometry of Materials Editors: F. Ernst and M. R¨uhle 51 Point Defects in Semiconductors and Insulators Determination of Atomic and Electronic Structure from Paramagnetic Hyperﬁne Interactions By J.-M. Spaeth and H. Overhof 52 Polymer Films with Embedded Metal Nanoparticles By A. Heilmann 53 Nanocrystalline Ceramics Synthesis and Structure By M. Winterer 54 Electronic Structure and Magnetism of Complex Materials Editors: D.J. Singh and D. A. Papaconstantopoulos 55 Quasicrystals An Introduction to Structure, Physical Properties and Applications Editors: J.-B. Suck, M. Schreiber, and P. H¨aussler 56 SiO2 in Si Microdevices By M. Itsumi 57 Radiation Effects in Advanced Semiconductor Materials and Devices By C. Claeys and E. Simoen 58 Functional Thin Films and Functional Materials New Concepts and Technologies Editor: D. Shi 59 Dielectric Properties of Porous Media By S.O. Gladkov 60 Organic Photovoltaics Concepts and Realization Editors: C. Brabec, V. Dyakonov, J. Parisi and N. Sariciftci 61 Fatigue in Ferroelectric Ceramics and Related Issues By D.C. Lupascu

J. Parisi

H. Warlimont

62 Epitaxy Physical Principles and Technical Implementation By M.A. Herman, W. Richter, and H. Sitter 63 Fundamentals of Ion-Irradiated Polymers By D. Fink 64 Morphology Control of Materials and Nanoparticles Advanced Materials Processing and Characterization Editors: Y. Waseda and A. Muramatsu 65 Transport Processes in Ion-Irradiated Polymers By D. Fink 66 Multiphased Ceramic Materials Processing and Potential Editors: W.-H. Tuan and J.-K. Guo 67 Nondestructive Materials Characterization With Applications to Aerospace Materials Editors: N.G.H. Meyendorf, P.B. Nagy, and S.I. Rokhlin 68 Diffraction Analysis of the Microstructure of Materials Editors: E.J. Mittemeijer and P. Scardi 69 Chemical–Mechanical Planarization of Semiconductor Materials Editor: M.R. Oliver 70 Applications of the Isotopic Effect in Solids By V.G. Plekhanov 71 Dissipative Phenomena in Condensed Matter Some Applications By S. Dattagupta and S. Puri 72 Predictive Simulation of Semiconductor Processing Status and Challenges Editors: J. Dabrowski and E.R. Weber 73 SiC Power Materials Devices and Applications Editor: Z.C. Feng

Springer Series in

materials science Editors: R. Hull

R. M. Osgood, Jr.

74 Plastic Deformation in Nanocrystalline Materials By M.Yu. Gutkin and I.A. Ovid’ko 75 Wafer Bonding Applications and Technology Editors: M. Alexe and U. G¨osele 76 Spirally Anisotropic Composites By G.E. Freger, V.N. Kestelman, and D.G. Freger 77 Impurities Conﬁned in Quantum Structures By P.O. Holtz and Q.X. Zhao

J. Parisi

H. Warlimont

86 Wide-Gap Chalcopyrites Editors: S. Siebentritt and U. Rau 87 Micro- and Nanostructured Glasses By D. H¨ulsenberg and A. Harnisch 88 Introduction to Wave Scattering, Localization and Mesoscopic Phenomena By P. Sheng 89 Magneto-Science Magnetic Field Effects on Materials: Fundamentals and Applications Editors: M. Yamaguchi and Y. Tanimoto

78 Macromolecular Nanostructured Materials Editors: N. Ueyama and A. Harada

90 Internal Friction in Metallic Materials A Handbook By M.S. Blanter, I.S. Golovin, H. Neuh¨auser, and H.-R. Sinning

79 Magnetism and Structure in Functional Materials Editors: A. Planes, L. Ma˜nosa, and A. Saxena

91 Time-dependent Mechanical Properties of Solid Bodies By W. Gr¨afe

80 Micro- and Macro-Properties of Solids Thermal, Mechanical and Dielectric Properties By D.B. Sirdeshmukh, L. Sirdeshmukh, and K.G. Subhadra 81 Metallopolymer Nanocomposites By A.D. Pomogailo and V.N. Kestelman 82 Plastics for Corrosion Inhibition By V.A. Goldade, L.S. Pinchuk, A.V. Makarevich and V.N. Kestelman 83 Spectroscopic Properties of Rare Earths in Optical Materials Editors: G. Liu and B. Jacquier 84 Hartree–Fock–Slater Method for Materials Science The DV–X Alpha Method for Design and Characterization of Materials Editors: H. Adachi, T. Mukoyama, and J. Kawai 85 Lifetime Spectroscopy A Method of Defect Characterization in Silicon for Photovoltaic Applications By S. Rein

92 Solder Joint Technology Materials, Properties, and Reliability By K.-N. Tu 93 Materials for Tomorrow Theory, Experiments and Modelling Editors: S. Gemming, M. Schreiber and J.-B. Suck 94 Magnetic Nanostructures Editors: B. Aktas, L. Tagirov, and F. Mikailov 95 Nanocrystals and Their Mesoscopic Organization By C.N.R. Rao, P.J. Thomas and G.U. Kulkarni 96 Gallium Nitride Electronics By R. Quay 97 Multifunctional Barriers for Flexible Structure Textile, Leather and Paper Editors: S. Duquesne, C. Magniez, and G. Camino 98 Physics of Negative Refraction and Negative Index Materials Optical and Electronic Aspects and Diversiﬁed Approaches Editors: C.M. Krowne and Y. Zhang

From Bulk to Nano: The Many Sides of Magnetism (Springer Series in Materials Science)