Surface Mount Technology

job:LAY00 page:1 colour:1 black–text SMT Soldering Handbook job:LAY00 page:2 colour:1 mmmm black–text job:LAY00 ...

Author: Rudolf Strauss

80 downloads 1526 Views 3MB Size Report

This content was uploaded by our users and we assume good faith they have the permission to share this book. If you own the copyright to this book and it is wrongfully on our website, we offer a simple DMCA procedure to remove your content from our site. Start by pressing the button below!

Report copyright / DMCA form

DOWNLOAD PDF

job:LAY00 page:1 colour:1

black–text

SMT Soldering Handbook

job:LAY00 page:2 colour:1

mmmm

black–text

job:LAY00 page:3 colour:1

black–text

SMT Soldering Handbook

Rudolf Strauss, Dr.Ing., FIM

job:LAY00 page:4 colour:1

black–text

Newnes An imprint of Butterworth-Heinemann Linacre House, Jordan Hill, Oxford OX2 8DP 225 Wildwood Ave, Woburn, MA 01801-2041 A division of Reed Educational and Professional Publishing Ltd A member of the Reed Elsevier plc group oxford boston johannesburg melbourne new delhi singapore First published 1994 as Surface Mount Technology Second edition 1998 © Rudolf Strauss 1994, 1998 All rights reserved. No part of this publication may be reproduced in any material form (including photocopying or storing in any medium by electronic means and whether or not transiently or incidentally to some other use of this publication) without the written permission of the copyright holder except in accordance with the provisions of the Copyright, Designs and Patents Act 1988 or under the terms of a licence issued by the Copyright Licensing Agency Ltd, 90 Tottenham Court Road, London, England W1P 9HE. Applications for the copyright holder’s written permission to reproduce any part of this publication should be addressed to the publishers.

British Library Cataloguing in Publication Data Strauss, Rudolf Surface Mount Technology I. Title 621.3815 ISBN 0 7506 35894 Library of Congress Cataloguing in Publication Data Strauss, Rudolf. Surface mount technology Rudolf Strauss. p. cm. Includes bibliographical references and index. ISBN 0 7506 1862 0 1. Surface mount technology. 2. Printed circuits–Design and construction. I. Title. TK7870.15.S63 93–44368 621.381531–dc20 CIP Typeset by Vision Typesetting, Manchester Printed and bound in Great Britain by Biddles Ltd of Guildford and King’s Lynn

job:LAY00 page:5 colour:1

black–text

Contents

Preface to the ﬁrst edition Preface to the second edition Glossary 1 Why SMDs? References

xii xiv xvi 1 5

2 The SMD family 2.1 Shapes, sizes and construction 2.1.1 Melfs and chips 2.1.2 LCCCs 2.1.3 SOs and PLCCs 2.2 High-pincount components 2.2.1 TABs 2.2.2 Flip-chips and BGAs 2.3 Multichip modules 2.4 The solderable surfaces of SMDs 2.4.1 Melfs and chips 2.4.2 Components with legs 2.5 SMD shapes and wavesoldering behaviour 2.6 The popcorn eﬀect 2.7 References

6 6 6 8 9 9 10 11 13 14 14 15 16 16 18

3 Soldering 3.1 The nature of soldering and of the soldered joint 3.1.1 The roles of solder, ﬂux and heat

20 20 20

job:LAY00 page:6 colour:1

black–text

vi Contents

3.2

3.3

3.4

3.5 3.6

3.7

3.1.2 Soldering methods 3.1.3 Soldering success The solder 3.2.1 Constituents, melting behaviour and mechanical properties 3.2.2 Composition of solders for use in electronics 3.2.3 Lead-free solders 3.2.4 Solder impurities The soldered joint 3.3.1 Soldering as a surface reaction between a molten and a solid metal 3.3.2 Structure and characteristics of the soldered joint 3.3.3 Mechanical properties of soldered joints 3.3.4 Soldering on surfaces other than copper 3.3.5 Long-term behaviour of soldered joints 3.3.6 Long-term reliability of soldered joints The ﬂux 3.4.1 Tasks and action of the soldering ﬂux 3.4.2 Wetting and interfacial tension 3.4.3 Properties required in a ﬂux 3.4.4 Rosin ﬂuxes 3.4.5 Low-solids and no-clean ﬂuxes 3.4.6 Watersoluble ﬂuxes 3.4.7 Solvents used in ﬂuxes 3.4.8 Flux standards 3.4.9 Testing soldering ﬂuxes Soldering heat 3.5.1 Heat requirements and heat ﬂow 3.5.2 Heating options Solderability 3.6.1 Wetting and dewetting 3.6.2 Capillarity and its eﬀects 3.6.3 Capillarity and joint conﬁguration 3.6.4 The importance of solderability 3.6.5 Oxide layers 3.6.6 Solderability-enhancing surface coatings 3.6.7 Leaching eﬀect of molten solder 3.6.8 Measuring solderability References

21 24 24 24 27 29 31 36 36 37 40 41 43 44 45 45 47 48 50 52 53 54 54 57 60 60 61 63 63 65 65 69 69 71 73 74 81

job:LAY00 page:7 colour:1

black–text

Contents vii

84 84 84 85 87 87 96 98 98 100 102 103 103 104

4 Wavesoldering 4.1 The wave concept 4.1.1 Wavesoldering before SMDs 4.1.2 Wavesoldering after SMDs 4.2 Applying the ﬂux 4.2.1 Types of ﬂuxer 4.2.2 Monitoring and controlling ﬂux quality 4.3 Preheating the board 4.3.1 Heat requirements 4.3.2 Heat emitters and their characteristics 4.3.3 Temperature control 4.4 The solderwave 4.4.1 Construction of the soldering unit 4.4.2 Thermal role of the solderwave 4.4.3 Interaction between molten solder and the circuit board 4.4.4 Chipwaves 4.4.5 Formation and control of dross 4.5 Wavesoldering in an oxygen-free atmosphere 4.5.1 Origins and development 4.5.2 Wavesoldering in nitrogen 4.6 Board conveyor systems 4.6.1 Functional requirements 4.6.2 Board-handling systems 4.7 Wavesoldering practice 4.7.1 Operating parameters and their role 4.7.2 Choosing and monitoring operating parameters 4.7.3 Optimizing machine parameters 4.7.4 Machine maintenance 4.7.5 Check-analysis of the solderbath 4.7.6 Dealing with dross 4.7.7 Hygiene and safety 4.8 The role of adhesives in wavesoldering 4.8.1 Demands on the adhesive and the glued joint 4.8.2 Storage and handling behaviour of adhesives 4.8.3 Applying the adhesive 4.8.4 Curing the adhesive joint 4.8.5 The glass transition temperature 4.9 References

105 110 114 118 118 119 126 126 126 130 130 131 136 137 138 138 139 141 141 141 143 145 146 147

5 Reﬂowsoldering 5.1 The reﬂow concept

148 148

job:LAY00 page:8 colour:1

black–text

viii Contents

5.2

5.3

5.4

5.5

5.6

5.7

5.8

5.1.1 SMDs and reﬂowsoldering 5.1.2 Reﬂowsoldering versus wavesoldering Solder paste 5.2.1 Operational requirements 5.2.2 Standard speciﬁcations 5.2.3 Solderpowder 5.2.4 The ﬂux and its residue 5.2.5 Printing and dispensing properties 5.2.6 The solderball test Putting the solder paste on the board 5.3.1 Single-spot dispensing 5.3.2 Stencilling and screen printing 5.3.3 Depots of solid solder Vapourphase soldering 5.4.1 The basic concept 5.4.2 Vapourphase working ﬂuids 5.4.3 The physics of vapourphase soldering 5.4.4 Vapourphase soldering equipment 5.4.5 ‘New-generation’ vapourphase soldering systems Infrared soldering 5.5.1 Working principle 5.5.2 The physics of heat transfer by radiation 5.5.3 The physics of heat transfer by convection 5.5.4 Operation of infrared ovens 5.5.5 Oven design 5.5.6 Infrared soldering in a controlled atmosphere Reﬂowsoldering with hot air or gas 5.6.1 Convection versus radiation 5.6.2 The physics of convection reﬂowsoldering 5.6.3 Convection reﬂow ovens 5.6.4 Development potential of convection reﬂowsoldering 5.6.5 Convection soldering of single components Laser soldering 5.7.1 How a laser works 5.7.2 Nd: YAG and CO lasers 5.7.3 Laser soldering in practice 5.7.4 Laser-soldering equipment Impulse soldering 5.8.1 Operating principle 5.8.2 The solder depot

148 154 158 158 159 160 164 165 167 169 169 171 178 179 179 180 180 184 186 189 189 191 200 201 203 208 209 209 210 210 212 214 217 218 218 220 221 223 223 224

job:LAY00 page:9 colour:1

black–text

Contents

5.8.3 The thermode and its heating cycle 5.8.4 Impulse-soldering equipment 5.9 SMD soldering methods – A survey 5.10 References

ix

225 227 228 232

6 The circuit board 6.1 The beginnings 6.2 SMD-speciﬁc demands on a circuit board 6.3 Thermal management 6.3.1 Thermal expansion mismatch 6.3.2 Eﬀects of temperature diﬀerences between components and board 6.4 Solderable surfaces 6.4.1 Galvanic coatings 6.4.2 Hot tinning 6.4.3 Organic coatings 6.4.4 Flat solder depots 6.5 The soldermask 6.6 Layout 6.6.1 Layout for wavesoldering 6.6.2 Layout for reﬂowsoldering 6.7 References

234 234 234 236 237

7 Component placement 7.1 The task 7.2 Reliability of placement 7.3 Placement options 7.3.1 Fully manual placement 7.3.2 Semi-automatic placement 7.3.3 Fully automatic sequential systems 7.3.4 Simultaneous placement systems 7.4 The practice of automatic component placement 7.4.1 The range of choice 7.4.2 Classes of placement machines 7.5 Reference

250 250 251 253 253 255 256 257 258 258 259 260

8 Cleaning after soldering 8.1 Basic considerations 8.1.1 Reasons for cleaning 8.1.2 Designing for cleanability 8.1.3 What must be removed? 8.2 The theory of cleaning

261 261 263 266 267 269

237 238 239 239 241 242 244 244 244 247 249

job:LAY00 page:10 colour:1

black–text

x Contents

8.2.1 The physics of cleaning 8.2.2 The chemistry of cleaning 8.3 The practice of solvent cleaning 8.3.1 Organic solvents 8.3.2 Solvent-cleaning installations 8.3.3 In-line cleaning plants 8.3.4 Halogenated solvents: safety and health 8.3.5 The three environmental threats 8.3.6 Restrictions on solvent usage 8.3.7 Non-ﬂammable organic solvents with reduced environmental risks 8.3.8 Flammable solvents 8.4 Cleaning with water 8.4.1 Chemical and physical aspects 8.4.2 Water quality 8.4.3 Water recycling and eﬄuent problems 8.4.4 Removal of residue from watersoluble ﬂuxes 8.4.5 Removal of residue from resinous ﬂuxes 8.4.6 Water washing installations 8.5 Semi-aqueous cleaning 8.5.1 The concept 8.5.2 The cleaning solvents 8.5.3 Semi-aqueous washing installations for water-immiscible solvents 8.5.4 Semi-aqueous washing installations for water-miscible solvents 8.6 Testing for cleanliness 8.6.1 The meaning of cleanliness 8.6.2 Measuring ionic contamination (MIL test) 8.6.3 Measuring surface insulation resistance (SIR) 8.7 The future of cleaning and of ﬂuxing 8.8 References 9 Quality control and inspection 9.1 The meaning of ‘quality’ 9.1.1 Product quality and product reliability 9.1.2 Classiﬁcation according to reliability requirements 9.2 Soldering success and soldering perfection 9.2.1 Soldering success and soldering faults 9.2.2 Soldering perfection and soldering imperfections 9.3 Practical examples of soldering faults 9.4 The ideal and the imperfect joint

269 274 276 277 282 288 291 293 297 298 299 302 302 303 305 306 306 307 310 310 311 313 315 318 318 319 321 322 323 325 325 325 326 327 327 330 332 332

job:LAY00 page:11 colour:1

black–text

Contents

9.5 Inspection 9.5.1 When to inspect 9.5.2 Visual inspection 9.5.3 Automated opto-electronic inspection 9.5.4 X-ray inspection 9.5.5 Electronic inspection 9.5.6 Thermographic inspection 9.6 References

xi

332 335 337 338 338 340 340 340

10 Rework 10.1 The unavoidability of rework 10.1.1 Rework in the production process 10.1.2 Desoldering and resoldering 10.2 Basic considerations 10.2.1 Metallurgical and mechanical consequences of rework 10.2.2 The cost of rework 10.2.3 Lessons to be learned 10.3 Rework equipment 10.3.1 Heat sources 10.3.2 Rework stations 10.4 Rework tasks and procedures 10.4.1 Removing bridges and solderballs 10.4.2 Desoldering SMDs 10.4.3 Filling empty joints 10.4.4 Resoldering SMDs 10.4.5 Cleaning after rework 10.4.6 Semi-mechanized work stations 10.5 Integrating rework into the production process 10.5.1 Rework personnel 10.5.2 Closed-loop soldering 10.6 References

342 342 342 343 343

Index

363

343 344 344 345 345 347 348 348 348 353 356 358 359 360 360 361 361

job:LAY00 page:12 colour:1

black–text

Preface to the first edition

This book has been written for all those who have to solder surface mounted devices to circuit boards, and it should therefore be of interest to practitioners of soldering in all its various forms. Apart from them, people concerned with inspection and quality control, or with the choice and acquisition of equipment, may ﬁnd some sections of the book useful. I have tried to cover all the practicalities of soldering in electronic manufacture in such a way and such language, that it can be read and, I hope, understood by those in direct charge of assembling circuit boards by soldering. Temperatures are given in degrees Centigrade and Fahrenheit; as a rule, operating temperatures are rounded up or down to the nearest round ﬁgure, unless they relate to physical constants such as melting or boiling points. Dimensions are given both in metric and imperial units. Since it is in the ﬁrst place about soldering, the book covers all aspects of the soldering process itself, which include principally solders, ﬂuxes, soldering heat and solderability. Because it deals with the soldering of SMDs, it describes the dimensions and features of these components as far as they are relevant to soldering. What goes on inside an SMD is of no concern here. All practical and, as far as is necessary, the theoretical aspects of wavesoldering and of the various methods of reﬂowsoldering are comprehensively treated. Features of the circuit board and of component placement are considered as far as they are relevant to the soldering process. Cleaning after soldering is treated in detail. The text is based on the state of the art, which this quickly evolving technology had reached by the middle of 1993. The restrictions on the use of cleaning media and methods, which the book mentions, are those which were in force or anticipated at that point in time. Practitioners of soldering need to know what constitutes a ‘good’ joint, and how to correct soldering defects. Therefore, quality control and inspec-

job:LAY00 page:13 colour:1

black–text

Preface to the first edition xiii

tion are discussed in detail, as is corrective soldering. Some readers may ﬁnd the contents of these sections of the book provocative or controversial. This was diﬃcult to avoid, because I hold strong views in these matters, many of them based on practical experience. My own interest and involvement in soldering go back a long time. Having studied experimental physics, as it was then called, in Germany in the mid-thirties, I joined and later managed the research department of a leading smelter of alloys of lead, tin and copper, when I came to London in 1939. During the war, which broke out soon after, I was involved in the development of the new technologies and materials which it demanded, many of them related to soldering. In the mid-1950s, I was closely associated with the invention and introduction by my company of wavesoldering of printed circuit boards, which themselves had been invented during the war by Paul Eisler in London. My involvement with electronic soldering continued until my retirement in the mid-seventies. My engagement in consultancy, lecturing, and writing, still on that same subject, continues. A large number of friends and former colleagues have given me much help, advice and support in writing this book, and I have drawn on the published work of several of them. My thanks are due to them all. They are too numerous to mention individually, but I must single out Dr Wallace Rubin of Multicore Solders Ltd for guiding me through the maze of the standard speciﬁcations of solders and ﬂuxes, and Russ Wood, formerly of Dage (GB) Ltd, and Gordon Littleford, formerly of Kerry Ultrasonics Ltd, who have put me right on the ﬁner points of today’s cleaning technology. Finally, my special thanks are due to Dr Colin Lea of the National Physical Laboratory in Teddington, who never hesitated to let me draw on his and his colleagues’ wide fund of scientiﬁc knowledge. Rudolf Strauss

job:LAY00 page:14 colour:1

black–text

Preface to the second edition

There have been drastic changes in the various technologies covered in this book since its ﬁrst edition appeared some three years ago. The growth of the market in electronic products has not slackened and its global monetary value is expected to overtake that of the automotive industry before the year 2000. Driven by market forces, electronic assemblies have become progressively smaller; 30 per cent of all electronic products, such as mobile telephones, camcorders, lap-top computers and electronic notebooks are now ‘handheld’; the universal use of electronic ‘smart cards’ is imminent. The result is miniaturization, the crowding of an ever increasing data storage and handling capacity into devices which ﬁt into a pocket or the palm of a hand. Soldering is still the dominant joining technology, but soldered joints are moving ever closer together. Wavesoldering has reached the limits of its capabilities, and reﬂowsoldering has become the leading technique. Another eﬀect of the pressure of the marketplace is the shortened life expectancy of many electronic products. The demand for constant innovation in the ﬁelds of video and audio products, communication, oﬃce and car electronics and many other areas such as military, means that any given item may become obsolete well before the end of its natural lifespan. Interest in the long-term behaviour of soldered joints has therefore noticeably slackened. Instead, the mounting bulk of scrapped electronic equipment is beginning to worry the environmentalists, who are the driving force behind the search for lead-free solders. This second edition takes account of these changes. Like the ﬁrst one, it aims to present the practical problems, which the practitioner of soldering has to face and solve, in simple terms and plain language, free from technical jargon. Once again, I have to thank many of my friends and former colleagues for their help and advice. Dr Wallace Rubin, and Dr Malcolm Warwick of

job:LAY00 page:15 colour:1

black–text

Preface to the second edition xv

Multicore have brought me up to date on much of current industrial practice, and on the present state of American and European standard speciﬁcations relating to solder alloys and soldering ﬂuxes. The staﬀ of ITRI Ltd (formerly the International Tin Research Institute) have been most helpful in guiding me on my way in the world of lead-free solders. My special thanks go to Professor Theodore L. Bergman, of the University of Connecticut USA, who pointed out a serious misconception of mine in the ﬁrst edition of this book, relating to the absorption of infrared radiation in the atmosphere of a reﬂowsoldering oven. This error has been corrected in this second edition. Rudolf Strauss

job:LAY00 page:16 colour:1

black–text

Glossary

As is characteristic of any upwardly mobile technology, its practitioners are continuously coining new technical terms and abbreviations, which are given a more or less agreed meaning. It will be useful to provide a necessarily limited list of them at this point. ASICIO Application-speciﬁc integrated circuit I/O, BGA Ballgrid array: a plastic or ceramic body containing an IC, with its IOs, in the form of solder bumps, located on its underside CC Chip-carrier: a square-bodied, plastic or ceramic SMD, with an IC inside Chip The term ‘chip’ has acquired several meanings, among them the following: an IC on a ceramic substrate; an SMD which contains an IC; a resistor or ceramic capacitor, encased in a rectangular ceramic body. Unless expressly stated, the term ‘chip’ will always have this last meaning in this book COB Chip-on-board: a bare chip, glued to a board and connected to its circuitry by wirebonding CSP Chip-size package: an SMD with a plastic or ceramic body which is not much larger than the chip which it contains DCA Direct chip attach (an alternative name for ﬂip chip) DIL ‘Dual-in-line’: a through-mounted device (TMD) containing an integrated circuit with two parallel lines of legs FP Flip chip: a bare chip with solder-bumps on its underside. Like a BGA, it can be reﬂowsoldered directly to a circuit board IC Integrated circuit: an electronic circuit carried on the surface of a silicon wafer I/O, IO In/out: the solderable connectors or leads of an SMD

job:LAY00 page:17 colour:1

black–text

Glossary xvii

MCM Melf PCB PLCC QFP SMD SO SOIC SOT TMD VSOIC

Multi-chip module: an array of interconnected ICs, mounted on a common substrate, such as a multilayer PCB, or a silicon, ceramic or glass wafer, to be soldered to a circuit board A ‘metal electrode face-bonded’ component: a resistor or a diode, encased in a cylindrical ceramic body with metallized solderable ends Printed circuit board Plastic leaded chip carrier: a CC with a body made of plastic, with J-shaped legs on all four sides Quad ﬂatpack: a plastic body containing an IC, with gull-wing legs on all four sides A surface-mounted device ‘Small outline’: an SMD, with a plastic body, carrying gull-wing legs on opposite sides An SO, with an IC (usually with a 1.25 mm/50 mil pitch) An SO transistor Through-mounted device: a component with connecting wires or legs, which are inserted into the through-plated holes of a circuit board ‘Very small outline’: a ﬁne-pitch SOIC

job:LAY00 page:18 colour:1

mmmm

black–text

job:LAY01 page:1 colour:1

black–text

1 Why SMDs?

The relationship between the manufacturers of electronic components and the assemblers of electronic circuitry resembles that between two diﬀerent orders of living beings, for example insects and plants: they need one another to be able to exist, and for that reason there are close links between the evolutionary paths of both. The shapes and the dimensions of their bodies, or respectively their functions, must match one another, so that whatever is needed to ensure the survival of either species can be properly performed. Any mistakes or mismatches are punished by extinction. Here the similarity ends: the evolutionary paths of plants and animals started to go their diﬀerent ways over three hundred million years ago. The evolutionary periods in the world of electronics are measured in units smaller than decades, sometimes years. Also, bees and ﬂowers cannot talk to one another; the designers and makers of components and the designers and makers of electronic assemblies can and should. Sometimes, in the past, maybe not often enough, but now very close cooperation is the rule. Unless this communication develops into a continuing, orderly and purposeful dialogue, extinction of isolated species with insuﬃcient evolutionary mobility continues to be a threat. At the other end of the mobility scale, a few large manufacturing houses have managed to bring three orders of electronic species together into one closely-knit symbiosis: components, component-placement equipment, and electronic assemblies are all designed, made, used and marketed by one single vertically-structured organization. The particular branch of electrical engineering, which from about 1905 onwards was called ‘electronics’, could be said to have begun with the transmission of the ﬁrst Morse signal across the Atlantic by Marconi, on 12 December 1901. Then, as now, one of the principal uses of electronics was the creation and transmission of signals. Then, as now, the basic constructional elements of electronic apparatus were of two kinds, components and the conducting links between them. On the one hand there were active devices such as spark-gaps, later on thermionic valves and passive components like inductive tuning and coupling coils, capacitors, and resistors. On the other hand there was a tangle of wires which connected these devices with one another. Judging by contemporary drawings and photographs, the style of these installations, whether landbased or on board a ship, was that of a rather untidy

job:LAY01 page:2 colour:1

black–text

2 Why SMDs?

laboratory. The terminals of the various electronic devices were usually screw connectors. After the First World War, radio started to develop as a vehicle for the transmission of news and entertainment to the public at large. To begin with, most receivers were assembled by domestic amateurs, who soldered connecting wires to a set of components supplied by their makers, complete with the necessary wiring diagrams. Industrial manufacture of domestic receivers and electronic apparatus in general began in the early twenties. Soldering was the universal method of joining the connecting wires to the component terminals. An electronic apparatus was a three-dimensional assembly: the valves, coils, and resistances were all fairly large, measuring several inches across and in height, and their terminals were not always close together or in one plane. Soon they began to be assembled together on a common chassis, and the connecting wires were prefabricated as a three-dimensional wiring loom. Teams of skilled operators, mainly girls, handsoldered the wire ends to the component terminals, which themselves were either short wires or soldering lugs. They worked with electric soldering irons and solderwire with a rosin-ﬂux core. Soldering quality on the whole was excellent, because every operator was his (or her) own quality inspector: she would not lift the iron oﬀ a joint until she had seen the solder ﬂow into it. Making a wrong connection was the main danger. The three-dimensional nature of electronic assemblies had two consequences: they did not lend themselves to mechanized mass production (though some attempts were made) and post-assembly inspection was almost impossible. Testing was functional, and the location of faults was a skill, not a science. Paul Eisler’s invention of the printed circuit in 1943 (Section 6.1) changed all that: he replaced the three-dimensional wiring loom with a two-dimensional pattern of thin strips of copper foil, carried on one side of an insulating phenolic paper board. Wherever a conductor had to be soldered to the terminal of a component, a hole was drilled into the board, and surrounded by a ring of conductor foil, the ‘land’. The components, which at that time were axial resistors, axial or radial capacitors, sockets for thermionic valves and, increasingly, threelegged transistors, were placed on the other side of the board with their terminal wires pushed through their appropriate holes in the board. Their protruding ends were crimped over the lands, which surrounded the holes, and soldered to them, one by one (Figure 1.1). Again, teams of girls inserted the components, crimped the

Figure 1.1 Component on a single-sided circuit board

job:LAY01 page:3 colour:1

black–text

Why SMDs? 3

wire ends and handsoldered them to the lands on the board. Rules were established for what a good joint should look like, and some of these rules persist to this day (Chapter 9). Because all the joints of the assembly were in one plane, soldering all of them in one operation was the obvious next step. This was made possible by the invention of wavesoldering in 1956 (Section 4.1). From then on, the forward march of the printed circuit board became unstoppable, and it soon conquered the world. However, the assembly itself was still three-dimensional. Though the circuit pattern was in two dimensions, the thermionic valves, later the transistors, and all the resistors and capacitors were sitting on it like houses on a ﬂat piece of ground, with their terminal sticking through it. Surface-mounted resistors stuck to circuit boards had been described in 1952, but the ﬁrst mention of a device with its terminals in contact with conductors on a circuit board occurs in a British patent in 1960.

In the mid sixties, the growth of hybrid technology provided the incentive to design surface-mounted devices which had no connecting wires. Thick-ﬁlm circuitry, carried on ceramic wafers, provided a rugged basis for electronic assemblies for use in demanding environments. Because it was impracticable to provide the wafers with holes, the components had to be surface mountable by necessity. To begin with, some of them were simply wired components with their legs cut oﬀ, like melfs. Others were already purpose-designed for mounting on ceramics, like chips. SOs with their angled legs came soon after chips and melfs, followed by PLCCs. They were the direct descendants of the DILs, and the pitch of their legs is still 1.27 mm/50 mil, like that of the DILs. All of them are decidedly three-dimensional, and obviously originally conceived for handsoldering. The component manufacturers issued detailed soldering advice, but left it to the makers and users of wavesoldering machines to cope with the problems caused by the three-dimensional nature of the components (Section 4.1.2). In spite of these problems, and the initial reluctance of the assembling industry to cope with them, the advance of SMDs was as unstoppable as that of the printed circuit board twenty years earlier. With the arrival of integrated circuits and their multiple functions, the number of component legs – their pincount – began to grow beyond the 68 legs which were manageable with the old 1.27 mm/50 mil pitch, and this signalled the approaching end of the species of inserted components with their legs or wires stuck into holes drilled in a board. Surface-mounting technology (SMT) began to take over. At the same time, components became ﬂatter, and approached the two-dimensionality of the boards on which they sit. The designers of soldering equipment and of SMDs had started to work together. TABs are a typical example of the beneﬁts of this cooperation. Today, a number of driving forces, which are pushing SMT further forward, can be discerned: 1. Related to the individual component: large-scale integration of chips and high switching rates demand short leads of roughly equal lengths. This requirement can only be met with the close-pitch design of QFPs (quad ﬂat packages) and TABs (tape automated bonding packages) (Figure 1.2).

job:LAY01 page:4 colour:1

black–text

4 Why SMDs?

Figure 1.2 DIL and PLCC. (a) 64–lead DIL, 2.54 mm/100 mil pitch; (b) 68–lead PLCC, 1.27 mm/50 mil pitch (Philips)

2. Related to the assembly as a whole: the number of functions per component, and consequently per assembly, has grown almost exponentially over the years since the introduction of SM technology. A ﬁne-pitchtechnology board is many times smaller than a board with the same functions but populated with inserted components only. Electronic devices like the controls for a camcorder, the circuitry of a mobile telephone, or a pacemaker, are unthinkable without SMT. 3. Related to circuit manufacture: automatic insertion of ﬁne-pitch wired components, even if they did exist, would pose insurmountable diﬃculties. The use of SMDs is still growing steadily, having overtaken inserted components in 1992. The forecast from which Figure 1.3 is reproduced predicted a strong growth of the chip-on-board technique, by which bare chips are placed on the circuit board

job:LAY01 page:5 colour:1

black–text

Why SMDs? 5

Figure 1.3 Forecast of electronic component usage (from Surface Mount Technology, BPA Ltd, Dorking RH4 1DF, UK Feb. 1989)

and their IOs are connected with their footprints by wirebonding (COB = chip-onboard). This technique has meanwhile been overtaken by BGAs and ﬂip–chips, for reasons explained in Section 2.2. Since this book is devoted entirely to surfacemounting by soft soldering, surface attachment methods such as wirebonding and using conducting adhesives are outside its scope. As of now, almost all SMDs are connected to the conductor pattern of the board on which they sit by soldering. Alternative joining techniques, such as wirebonding in the case of COB constructions, or joining with a conductive, adhesive polymer, or even elastomer, have established a toehold in SMD technology, which will almost certainly grow in the future. This present book, however, is conﬁned to soldering as the method of joining components to the conductor pattern on the circuit board.

References 1. Anon. (1952) Adhesive Resistors, Circuit World (UK), Feb. 1952, p. 70. 2. Brit. Patent 853 987, Nov. 1960. 3. Kirby, P. L. and Pagan, I. D. (1987) The Origins of Surface Mounting. Proc. Europ. Microelectron. Conf., Bournemouth, UK, June 1987. 4. Slyman, D. A. (1996) Anisotropic Conductive Adhesives. Productronic 10/96, pp. 30–36.

job:LAY02 page:2 colour:1

black–text

2 The SMD family

Like all electronic components, surface-mounted devices (SMDs) can be classiﬁed according to their function. Passive components include resistors, capacitors and inductors, all of them bipolar devices. Active components have three or more terminals, apart from diodes which have two. Basically, active devices contain switches or gates. These can number from the one of a single transistor with its three leads up to 25 000 for gate arrays with three hundred leads, or 250 000 for memories with about thirty leads.

A detailed discussion of the function and internal construction of SMDs is outside the framework of this book, which is concerned with the problem of soldering SMDs to circuit boards. Therefore, it is the shapes and the solderable surfaces of these SMDs which are our main interest. Components for direct attachment techniques like ‘naked’ chips for ‘chip on board’ mounting, are also outside the scope of this present book because they are connected to the circuit board not by soldering but by a wirebonding technique.

2.1 Shapes, sizes and construction SMDs come in three basic shapes: short cylinders, rectangular blocks and ﬂat slabs. Table 2.1 lists them, together with their main characteristics, and sketches their main features. The names by which they have become known have emerged as they were developed, and for this reason they do not follow any logical scheme.

2.1.1 Melfs and chips Cylindrical SMDs, made solderable by thick-ﬁlm metallization or metallic caps at either end of their ceramic or glass bodies, are known as melfs (Metal Electrode Faced components). A small proportion of melfs are bipolar diodes with glass bodies, metal endcaps, and markings indicating their polarity. To ensure correct placement, diodes are packed in blistertape. SMDs with small square ceramic bodies are called chips. Their endfaces are metallized by thick-ﬁlm metallic deposit.

job:LAY02 page:3 colour:1

black–text

The SMD family 7

Table 2.1 The SMD family Shape

Nature, name

Number of IOs

Pitch mm/inch

Passive Melf

2

—

Mini melf Micro melf Active SOD

2

—

2

—

Passive chips

2

—

3–4

—

SO, SOIC

6–28

1.27/ 0.050

4.0 ; 5.0/ 16 ; 0.2 to 7.6 ; 18/ 0.3 ; 0.72

W,R

VSO

40–56

0.75/ 0.030

up to 11 ; 21/ 0.44 ; 0.85

W,R

SOJ, PLCC

20–84

1.27/ 0.050

up to 29.4 ; 29.4/ 1.16 ; 1.16

W,R

Active SOT

2

Body, size mm/inch Ceramic 5.0 ; 2.22 dia./ 0.2 ; 0.08 dia. 3.6 ; 1.4 dia./ 0.14 ; 0.06 dia. 2.0 ; 1.1 dia./ 0.08 ; 0.04 dia. Glass 3.5 ; 1.6 dia./ 0.14 ; 0.64 dia. to 5.0 ; 2.3 dia./ 0.2 ; 0.09 dia. 1.25 ; 2.0/ 0.05 ; 0.08 to 5.7 ; 5.0/ 0.23 ; 0.2 Plastic 3.0 ; 1.3/ 0.12 ; 0.05

Soldering method W,R W,R W,R W,R

W,R

W,R

job:LAY02 page:4 colour:1

black–text

8 The SMD family

Table 2.1 (continued) Shape

Nature, name

Number of IOs

Pitch mm/inch

Body, size mm/inch

Soldering method

QFP

44–370

0.5/0.02

Plastic; 30 ; 30/ 1.2 ; 1.2

R

TAB

up to 400 72–1089

Film; 8, 16, 35/ 0.32, 0.64, 1.4 Plastic, up to 25 ; 25/ 1.0 ; 1.0

Impulse

BGA

down to 0.35/ 0.014 1.27, 1.5/ 0.05, 0.06

R

W: Wavesolderable; R: Reﬂowsolderable; Impulse: Impulse solderable

Resistors and capacitors, being passive components without polarity, can be mounted either way on their footprints. Therefore they can be picked from bulk feeders. Of the 170 ; 10 passive SMDs which were used worldwide in 1990, 57% were resistors, 42% were ceramic condensers, with tantalum and electrolytic condensers forming the rest.

Chips have been given a four-digit number code which indicates their approximate size in hundredths of an inch. The ﬁrst two give their length, the second their width. Thus a 0805 chip is about 2 mm/0.08 in long and 1.25 mm/0.05 in wide. On the other hand, the designation of melfs gives their approximate size in millimetres. An 0102 micromelf has a diameter of 1.1 mm/0.04 in and is 2.2 mm/0.09 in long. The main feature of melfs and chips is their tendency to get smaller and smaller. At present, a limit seems to have been reached with 0805 chips and 0102 micromelfs. The makers of automatic component placement equipment had to face and solve the formidable task of handling these small components and placing them with the required speed and precision (Chapter 7).

2.1.2 LCCCs Until recently, there was a class of integrated circuits, housed in ﬂat, square ceramic bodies, in sizes of up to and above 25.4 ; 25.4 mm/1 ; 1 in. Each of the four sides carried a row of thick-ﬁlm solderable patches, usually of gold or a gold–platinum alloy, at a pitch of 1.27 mm/50 mil as connectors. These were known as leadless ceramic chip carriers (LCCCs). They had originally been designed to be soldered to the ceramic substrate of hybrid circuits. In the context of printed circuit board assemblies, they became extinct because of the problems caused by the thermal expansion mismatch between them and the FR4 circuit boards to which they had to be soldered (Section 6.2).

job:LAY02 page:5 colour:1

black–text

The SMD family 9

2.1.3 SOs and PLCCs Most SMDs have moulded plastic bodies, which contain semiconductor devices, and which do not suﬀer from the thermal expansion mismatch problem. Their solderable connectors, if located on the periphery of the body, have the form of angled legs numbering from three up to 400 or more, depending on the number and complexity of their functions. The devices which they contain may be single transistors, integrated circuits (ICs), or application-speciﬁc integrated circuits (ASICs) such as gate arrays, microprocessors, or random access memories (RAMs). The ‘small-outline’ SMDs (SOs) are the direct descendants of insertiontechnique components with ﬂat push-through legs, spaced at a centre distance (pitch) of 1.27 mm/50 mil. Their bodies can be up to 10 mm/0.4 in high, and they include SOTs (small-outline transistors), and SOICs (small-outline integrated circuits). Their solderable legs are angled downwards (‘gullwing’ shape), raising the underside of the housing oﬀ the board surface (‘stand-oﬀ’, Section 8.1.1). SO legs are relatively thick, from 0.1 mm/4 mil to 0.3 mm/12 mil, and therefore somewhat rigid. This lack of ‘compliance’, which can cause stresses on the soldered joints in the case of a temperature diﬀerence between component and board, can be a problem (Section 3.1). The gullwing legs of ‘very-small-outline’ SMDs (VSOs) also have gullwing legs, with a pitch of 0.75 mm/30 mil. PLCCs (plastic leadless chip carriers) are SOs with their J-shaped legs tucked underneath the edge of the component body instead of pointing outwards, in order to save space. The price which the board assembler may have to pay for this gain in real estate is the problem of skipped wavesoldered joints, especially with closely set PLCCs (Section 6.4.1), or of ‘wicking’ when they are reﬂowsoldered (Section 9.3). For impulse soldering with a thermode (Section 5.7), PLCCs require a special thermode which heats the sides of the J-legs, since the footprints are not directly accessible. Equally, visual inspection demands special optics for oblique viewing, because the ends of the J-legs are out of the line of sight when viewed vertically.

2.2 High-pincount components The crowding of ever more functions into a single chip demands more and more IOs (Figure 2.1). Chips with up to 1000 IOs have been forecast for the end of the century, if not before. If the IOs are placed along the four sides of the component (peripheral IOs), the number which can be accommodated on a given package is limited by the minimum distance or pitch between them, which present soldering techniques can handle. Wavesoldering under nitrogen reaches its limits with IO pitches down to 0.5 mm/20 mil (Section 4.5.2), and reﬂowsoldering with 0.3 mm/7.5 mil. At this point, even the best ﬁne-pitch solder pastes and the most precise screenprinting equipment (Sections 5.2.5 and 5.3.2) are operating at the limits of their capabilities. Also, at these pitches, component leads get very thin and easily damaged on

job:LAY02 page:6 colour:1

black–text

10 The SMD family

Figure 2.1 Maximum lead count trends (after E. J. Vardaman ¸4 ). General trend: +60 leads/year (courtesy Techsearch International Inc., Austin, Texas, USA)

high-speed placement machines. Unavoidably, with a technology operating near the limits of its capability, reject rates and rework costs begin to rise steeply.

2.2.1 TABs In the late 1970s, TABs provided an answer (‘TAB’ stands for ‘tape-automated bonding’). A TAB carries a chip which is no longer enclosed in a moulded plastic body, but covered by a thin glass wafer, with its copper leads bonded to a polyimide tape, which has the form of a standard cine-ﬁlm, from super-8 up to 35 mm or more (Figure 2.2). These tapes are robust, and lend themselves to automatic placement and soldering on purpose-designed equipment, which by now has become well developed and widely available. The inner ends of the leads are soldered to the pads of the IC by the manufacturer of the TAB by a solder-bump technique (inner-lead bonding, ILB). The outer ends, with a pitch of down to 300 m/12 mil, can be impulse-soldered with a thermode (outer-lead-bonding, OLB). Hot-air thermode (HAT) techniques, which can also work with hot nitrogen, and laser techniques for OLB have been developed. One of the advantages of TABs is the ease with which each can be tested by the manufacturer, using as test pads ends of the outer leads. The footprints to which the TAB leads are to be soldered are given a solder coating of about 15 m/0.6 mil. For details of the required soldering techniques, see Section 5.8. TABs are approximately 0.2 mm/8 mil thick. Therefore, they lend themselves to being stacked, one on top of the other, on the same set of footprints. In this way, a large number of possible functions can be crowded into a very small board area, for applications such as camcorders and photographic equipment. Because they are so

job:LAY02 page:7 colour:1

black–text

The SMD family 11

Figure 2.2 The TAB

thin, TABs are used in ‘smart’ mutifunction cards (such as telephone cards), which at present have a standard thickness of 0.825 mm/33 mil.

2.2.2 Flip-chips and BGAs TABs have severe limitations: they cannot be soldered to a board by wave- or reﬂowsoldering, the two dominating in-line assembly techniques for circuit boards, but are designed for impulse soldering (Section 5.8), a one-by-one operation using dedicated equipment, which interrupts the continuity of a production line. Also, a TAB is wasteful of board area, considering the size of the chip which it carries in the centre of the long-legged spider of its leads. For these reasons, TABs have not swept the board in the way they had been expected to some years ago. It has been forecast that by the year 2000 packages with peripheral IOs will no longer be able to handle the number of functions demanded from them.

Putting the IOs on the underside of an IC or of its package (array technique) instead of along its edges (peripheral technique) radically solves the ﬁne-pitch problem: A 25 mm/1 in square package will accommodate about 300 peripheral IOs at a pitch of 0.3 mm/7.5 mil. An area array accommodates the same number of IOs on the underside of the same chip with the much wider pitch of 1.27 mm/ 50 mil. An added bonus of the area array is the shortened and more uniform signal path between the IC gates and the IOs. The array concept itself is not new. An early embodiment was the pin-grid array, where the IOs took the form of straight pins, arranged in rows on the underside of the component. They could either be inserted into a matching pattern of holes in the circuit board and wavesoldered, or placed on a matching pattern of footprints on the board and reﬂowsoldered. IOs in the form of an array of hemispherical solder bumps instead of pins proved to be more successful than pins. They were ﬁrst used on the ‘ﬂip-chip’, introduced in the 1970s by IBM for in-house use. Since the mid-1990s, the use of ﬂip-chips and BGAs, both of which carry solder bumps, has grown rapidly (Figure 2.3). With a ﬂip-chip, the array of solder bumps sits on the underside of the ceramic

job:LAY02 page:8 colour:1

black–text

12 The SMD family

body or die of a bare chip. Not being covered by a plastic package, a ﬂip-chip must be protected, after having been soldered to a circuit board. A top-cover, inelegantly called ‘glob top’, mostly a thermosetting polymer, is applied to the upper surface of the chip. An ‘underﬁll’, a similar low-viscosity thermosetting ﬁller, is dispensed along one edge or two adjacent edges of the chip. It penetrates the gap between the chip and the board by capillarity, protecting the IOs against moisture, and assisting the soldered joints to withstand the stresses caused by the thermal expansion mismatch between the ceramic body of the chip and the board laminate. The underﬁll also locks in the ﬂux residues left after soldering, which must therefore be strictly non-corrosive and non-conductive. Finally, once cured it makes corrective removal and resoldering of a ﬂip-chip impossible. Flip-chips are mainly used where component height is at a premium, as for example in ‘smart cards’. Where height is less restricted, the robust and easily handled BGAs dominate the ﬁeld. Their array of bumps can take the form of a square or a staggered grid, the former being the more usual one (Figure 2.3). The bumps are normally spaced at a pitch of 1.5 mm/60 mil or 1.27 mm/25 mil, their diameter varying between 0.5 mm/20 mil and 0.625 mm/25 mil. Being hemispherical, their height is roughly half their diameter. Solder bumps are usually formed from either eutectic solder (63% Sn, 37% Pb, melting point 183 °C/361 °F) or silver-containing eutectic (62% Sn, 2% Ag, 36% Pb, melting point 178 °C/352 °F, see Section 3.2.2 and Table 3.2). These bumps will be fully molten at the usual reﬂow temperatures of 215 °C/420 °F–230 °C/ 445 °F used in a normal reﬂow oven, allowing the BGA to settle down close to the board after reﬂow. Alternatively, the bumps may consist of an alloy of 3% Sn/97% Pb, with a melting range from 315 °C/595 °F to 320 °C/608 °F. These ‘controlled-collapse’ bumps do not melt completely during normal reﬂow temperatures, but form a stubby column between the BGA and the board. Such columns are better able to absorb lateral stresses which can arise from the thermal expansion mismatch between the board and the BGA. In any case, the thermal expansion mismatch between the polymer body of a BGA and the circuit board is less than that between the ceramic body of a ﬂip-chip and the board. BGAs need no underﬁll and can be desoldered and replaced if necessary. Nevertheless, with large BGAs thermal stresses caused by temperature ﬂuctuations, can pose a problem. BGAs ﬁt readily into the standard in-line reﬂow techniques along with the other SMDs. Because of their low stand-oﬀ height, cleaning after soldering is problematical (see Section 8.3.9). It is certainly advisable to use a no-clean paste (see Section 5.2.4) and to reﬂowsolder in a nitrogen atmosphere (see Section 5.6.4). Vapourphase soldering (Section 5.4) with its heat-input evenly shared between the components and the board on which they sit, is decidedly attractive in the context of soldering boards which carry BGAs. BGAs oﬀer a number of advantages: they are robust and easy to handle. Coplanarity of the ends of the gull-wing leads, the bane of ﬁne-pitch components, is no longer a problem. Accuracy of placement is much less critical than with ﬁne-pitch components, because of their wide pitch and their ability to self-align during the reﬂow-process: if misplaced by even half a pitch, the surface tension of the molten

job:LAY02 page:9 colour:1

black–text

The SMD family 13

Figure 2.3 Ball-grid array

solder centres all the IOs of the BGA on to their lands (see Figure 3.18a, Section 3.6.3). Finally, there are no longer any worries about the solderability of the terminations. Because of all this, users of BGAs report greatly improved assembly yields, and a consequent saving in cost.

Nevertheless, there are some points on the debit side: boards which have to accommodate BGAs will most likely require more layers than they would need otherwise, and therefore they will be more expensive (see Section 6.2). The main problem is that the joints underneath a BGA cannot be visually inspected. It is certainly advisable to check the paste printdown on the board for empty lands before placement, and the BGAs for their full complement of bumps, which can be done automatically ‘on the ﬂy’ by many placement machines (see Section 9.5.3 and 9.5.4). Post-soldering inspection, if required, demands an X-ray technique (see Section 9.5.4).

2.3 Multichip modules Apart from the growing number of functions crowded into an individual chip, the functional complexity of electronic circuits themselves, especially in the ﬁelds of automobile electronics, telecommunications, laptop and palmtop computers and industrial and medical sensor and control technology is growing at an estimated annual rate of 15–20 per cent. In this context, the term ‘complexity’ includes the number of components and soldered joints per board, the signal frequency to be handled, and the thermal load to be dissipated .

job:LAY02 page:10 colour:1

black–text

14 The SMD family

Multichip modules (MCMs) are a means to hive oﬀ some of the complexity of a board into compact, selfcontained subassemblies which are mounted on the board after its SMDs have been soldered to it. MCMs are small hermetically sealed units, containing a number of closely packed ICs which are wirebonded to a substrate such as an organic multilayer laminate, a thick-ﬁlm ceramic or a thin-ﬁlm glass circuit. They are often protected by a hermetically sealed cover, and if required they can be ﬁtted with external cooling ﬁns to dissipate the heat generated in the circuitry. Their outer leads can either be soldered to the main board, or mechanically connected with it with edge-connectors. Multichip modules are mentioned in this survey, because they are subassemblies, which contain a number of SMDs, though not being SMDs by themselves. The production of MCMs often requires specialized manufacturing technologies, such as clean-room techniques. They are therefore mostly produced, often also designed and functionally tested, by specialist ﬁrms, to the requirements of the board assembler. At present, they are mainly used in subsystems in mainframes, military applications and telecom switching systems.

2.4 The solderable surfaces of SMDs Obviously, the solderable surfaces and the leads of SMDs must maintain a consistently high solderability, without demanding strong ﬂuxes, and their shelf-life under normal storage conditions should be at least a year. Their design and metallurgical structure are governed by these requirements, and by the nature of the component body and the soldering methods which are likely to be used.

2.4.1 Melfs and chips Melfs and chips carry solderable, metallic surfaces at two opposing ends of their ceramic bodies. The ends of the cylindrical melf resistors are normally in the form of small caps, pressed from steel sheet. Next to the steel comes an electroless deposited nickel/ phosphorus layer, which in turn carries a thin copper layer, covered by another nickel layer, about 5 m/0.2 mil thick. It is ﬁnally topped by an up to 10 m/0.4 mil thick tin coating. The ﬁrst nickel coating ensures a good, diﬀusion-free bond between the iron and the copper, while the second one acts as a ‘diﬀusion barrier’, which prevents the formation of the tin/copper intermetallic ‘eta’ () compound (Section 3.2). Once the layer diﬀuses through the outer tin cover to the surface, it oxidizes and spoils the solderability of the component. The end faces of chips are covered by a sintered thick-ﬁlm metallic deposit. Such deposits consist of solderable metallic particles, embedded in a frit of low-melting glass. The particles on the surface represent the solderable face of the chip. They consist mostly of 80% to 90% silver, the balance being palladium, which has the function of slowing down the otherwise rapid dissolution of the silver particles during reﬂowsoldering (Section 3.6.4). Once they have been leached away by the molten solder, only the unsolderable glass frit remains on the surface.

job:LAY02 page:11 colour:1

black–text

The SMD family 15

Alternatively, and more recently, a thick-ﬁlm layer of plain silver is covered with a diﬀusion barrier of nickel, and a top coat of up to 10 m of tin for solderability.

2.4.2 Components with legs SOs and PLCCs The legs of most SOs and PLCCs are stamped from a 42% nickel/58% iron (Alloy 42) sheet, which has a low coeﬃcient of thermal expansion. They are between 0.2 mm/8 mil and 0.3 mm/12 mil thick, which means that they are suﬃciently sturdy not to get bent during normal handling, which ensures their ‘coplanarity’. The trade-oﬀ is their lack of compliance, when a temperature diﬀerence between the component and the circuit board puts a stress on their soldered joints (Section 6.2). Coplanarity in an SMD means that the ends of all its legs are in one plane, so that each one of them is in ﬁrm contact with its footprint when placed on the board. A leg which has been bent upwards may cause an open joint. One or more legs which are bent downwards may lift their neighbours oﬀ their footprints. Normally, coplanarity of multilead components is expected to be within 0.2 mm/8 mil. However, with ﬁne-pitch technology, the thickness of the solder paste printdown on the footprints may drop below that ﬁgure, which means that with today’s multilead components, coplanarity must be nearer to 0.1 mm/4 mil. Many automatic component placement machines are designed to check the coplanarity of multilead components between collecting them from the feeder magazine and putting them down on their footprints (Section 7.3). Naturally, coplanarity only matters with wavesoldering or an infrared, hot air or vapourphase reﬂow process, where the component legs rest freely on their footprints. With impulse soldering, a hot soldering tool (thermode) presses them against their footprints and, within reasonable limits, lack of coplanarity becomes irrelevant (Section 5.7). The solderability of the legs of SOs and PLCCs is ensured by a galvanic, reﬂowed coating of 60%Sn/40%Pb, which may have an undercoating of 1–5 m copper to ensure adhesion. Alternatively the topcoat may be hot-tinned with 60/40 tin–lead solder (up to 15 m/0.6 mil thick). Alternatively, and more recently, legs of SOs and PLCCs are stamped from sheet rolled from an alloy consisting of 98%Cu/2%Fe, which has very good mechanical and electrical properties. The solderable topcoat is the same as with the legs made from Alloy 42.

QFPs and TABs QFP legs are mostly made from an alloy 89/Cu/9%Ni2/Sn with a galvanic and reﬂowed, or hot-tinned, topcoat of 60Sn/40Pb. TAB legs are made either from tinned plain copper or 98%Cu/2%Fe alloy sheet. They are produced by an etching technique, using a photomechanically produced etch resist pattern. QFP and TAB legs are thin and slender. They may be as thin as 0.1 mm/4 mil, and their width depends on the pitch at which they are spaced. With a pitch of

job:LAY02 page:12 colour:1

black–text

16 The SMD family

0.5 mm/20 mil for example, footprints are 0.25 mm/10 mil wide, and the component legs are narrower still. This means that they are easily deformed, causing the above-mentioned problem of coplanarity. It is one of the several virtues of TABs that they possess built-in coplanarity: the outer ends of their legs are ﬁxed to the frame of the carrier ﬁlm, from which they are cut free as they are being placed. Furthermore, they are mostly soldered to their footprints with a thermode, which presses them down on the board, and only rarely by a non-contact reﬂow process. The metallurgical data of the solderable component surfaces and legs are summarized in Chapter 3, Table 3.7.

2.5 SMD shapes and wavesoldering behaviour As has been said already, SMDs were originally conceived for hybrid technology in the early seventies, for handsoldering to their ceramic substrate or reﬂowsoldering on a hotplate. The latter was no problem, considering the single-sided construction of the circuit and the stability and good heat conductivity of the ceramic. The soldering problems began when SMDs had to be wavesoldered to printed circuit boards. Their design did not turn out to be particularly user-friendly, especially as far as the SOs and PLCCs were concerned. This diﬃculty is due to the contours which their designers gave them: the ends of their legs, which have to be soldered to the footprints, are too close to the relatively high bodies which enclose their semiconductor circuitry. Thus, the ‘angle of aspect’, which is formed between the upper edge of the component body and the end of the solderable leg, is between 60° for SOs and 90° for PLCCs (Figure 2.4). The solderwave ﬁnds it diﬃcult to penetrate into these corners, because of the surface tension of the molten solder (Shadow eﬀect, Section 4.4.3). These diﬃculties were the reason for the development of the ‘chip-wave’ technology. As chips acquired ever more functions, and the number of their leads increased beyond the 84 legs of the PLCCs, their plastic housings became larger and ﬂatter. QFPs are not much above 2 mm/8 mil in height, and their soldering terminals are more readily accessible to the solderwave. The even ﬂatter TABs would be even easier to wavesolder if their ﬁne pitch did not make wavesoldering very diﬃcult, if not impossible, because of the close setting of their legs and the consequent danger of bridging. However, recent reﬁnements of wavesoldering under nitrogen have pushed the limit of wavesolderability without bridging back to a pitch of 0.6 mm/24 mil, and eﬀorts are being made to extend this down to 0.4 mm/16 mil.

2.6 The popcorn effect Under some circumstances, the plastic bodies of large, ﬂat SMDs like PLCCs and QFPs can develop cracks if they are soldered in a solderwave, by vapourphase soldering or in an infrared or hot-air convection oven. In all these cases, the whole

job:LAY02 page:13 colour:1

black–text

The SMD family 17

Figure 2.4 The contours of SOs, PLCCs and QFPs.

component is heated to well above the melting point of the solder (183 °C/361 °F). These cracks are caused by the so-called ‘popcorn eﬀect’, which is due to the following mechanism. The bodies of SOs, PLCCs and QFPs, being made from plastic, are capable of absorbing moisture if they are manufactured or stored under humid conditions. The moisture not only accumulates in the body itself, but can also penetrate into the inner cavity of the SMD. During soldering, it turns to steam. As a consequence, pressure of several atmospheres can build up in the interior of the component, which causes the housing to ‘balloon’ and crack (Figure 2.5). Naturally, the popcorn eﬀect does not arise with soldering methods where only the leads are

job:LAY02 page:14 colour:1

black–text

18 The SMD family

Figure 2.5 The popcorn effect

heated while the body of the SMD remains cool. These methods include impulse soldering with a thermode, and laser soldering. The popcorn eﬀect can be prevented by the manufacturer of the SMD, if the components are moulded in a strictly dry environment, or dried out by a heating process, and packed in moisture-impermeable metal foil. Alternatively, the user can carry out the heat treatment himself (48 hours at 125 °C/260 °F or 100 hours at 100 °C/215 F). For this purpose, the components must of course be removed from their magazine trays. Afterwards, they are sealed in polythene bags, together with a desiccating compound, and used as soon as possible. It is another virtue of TABs that, since they are enclosed in a glass cover, they do not suﬀer from this problem.

2.7 References 1. Reiner, M. (1985) VLSI Packaging, Hybrid Circuits, No. 6, pp. 9–13. 2. BPA Ltd (1989) Surface Mount Technology, A Critical Analysis, BPA Ltd, Dorking RH4 1DF, UK, pp. 146–147. 3. Anon. (19934) Surface Mount Technology (Germany), p. 68. 4. Vardaman, E. J. (1992) New TAB Developments and Applications, Proc. Nepcon West, pp. 590–594. 5. Vardaman, E. J. (1996) Worldwide Packaging Roadmaps. Soft Soldering, Research and Practice 1996, Proc. Academic Colloquium Munich, 19/20.11.96, DVS Report 182. pp. 14–18. 6. Willis, B. (1996) SMART Group Electronic Production Year Book, pp. 15–18. 7. Palmer, M. J. (1991) HAT Tool for Fluxless OLB and TAB. Electronic Components and Technology Conf., pp. 507–510.

job:LAY02 page:15 colour:1

black–text

The SMD family 19

8. Wolski, G. B. (1993) Impulses from SMT Production. EPP (Leinfelden, Germany), June 1993, pp. 15–21 (in German). 9. Burgess, T., McCall, G. and Poulter, S. (1993) New Trends in IC Packaging, Electronics Manufacture and Test (UK), June 1993, pp. 14–15. 10. Gordon, S. F., Huﬀman, W. D., Prough, S., Sandkuhle, R. and Yee, M. (1987) Moisture Eﬀect on Susceptibility to Package Cracking in Plastic SMDs. IPC Techn. Rev., 29, 2, pp. 18–20. 11. Smernos, S. (1996) Multichip-Module Architectures. Soft Soldering, Research and Practice 1996. Proc. Academic Colloquium Munich, 19/20.11.96, DVS Report 182, pp. 18–25.

job:LAY03 page:2 colour:1

black–text

3 Soldering

3.1 The nature of soldering and of the soldered joint Soldering, together with welding, is one of the oldest techniques of joining two pieces of metal together. Today, we distinguish between three ‘metallurgical’ joining methods: welding, hard soldering (or brazing) and soft soldering. The term ‘metallurgical’ implies that at and near to the joint interface, the microstructure has been altered by the joining process: what has happened has made one single piece of metal out of the two joint members, so that electric current can ﬂow and mechanical forces can be transmitted from one to the other. With both hard and soft soldering, the joint gap is ﬁlled with a molten alloy (an alloy is a mixture of two or more pure metals) which has a lower melting point than the joint members themselves, but which is capable of wetting them and, on solidifying, of forming a ﬁrm and permanent bond between them. The basis of most hard solders is copper, with additions of zinc, tin and silver. Most hard solders do not begin to melt below 600 °C/1100 °F, which rules them out for making conductive joints in electronic assemblies. Soft solders for making joints on electronic assemblies were by tradition, until recently, alloys of lead and tin, which begin to melt at 183 °C/361 °F. This comparatively modest temperature makes them suitable for use in the assembly of electronic circuits, provided heat-sensitive components are adequately protected against overheating. With some of the lead-free solders which have now entered the ﬁeld (see Section 3.2.3) soldering temperatures might have to be either higher or lower.

3.1.1 The roles of solder, flux and heat Soft soldering (from here on to be simply called ‘soldering’) is based on a surface reaction between the metal which is to be soldered (the substrate) and the molten solder. This reaction is of fundamental importance; unless it can take place, solder and substrate cannot unite, and no joint can be formed. The reaction itself is ‘exothermic’, which means that it requires no energy input

job:LAY03 page:3 colour:1

black–text

Soldering 21

to proceed, once it has started. Soldering heat is needed to melt the solder, because solid solder can neither react with the substrate (or only very slowly), nor ﬂow into a joint. The reaction between solder and substrate is of crucial importance for both the process of soldering, and for the resultant soldered joint. With a normal tin–lead solder, only the tin takes part in the reaction. With lead-free solders, other alloying components such as silver or indium may be involved as well. The reaction products are so-called intermetallic compounds, hard and brittle crystals, which form on the interface between the solid substrate and the molten solder. The bulk of them stay where they have formed. They constitute the so-called ‘intermetallic layer’ or ‘diﬀusion zone’, which has a profound eﬀect on the mechanical properties of the soldered joint and on its behaviour during its service life. Any non-metallic surface layer on the substrate, such as an oxide or sulﬁde, however thin, or any contamination whatever, prevents this reaction, and by implication prevents soldering. Unless the contamination is removed, the reaction cannot occur. Unfortunately, under normal circumstances all metal surfaces, with the exception of gold and platinum, carry a layer of oxide or sulﬁde, however clean they look. The soldering ﬂux has to remove this layer, and must prevent it from forming again during soldering. Naturally, the surface of the molten solder is also one of the surfaces which must be considered here, because an oxide skin would prevent its mobility. Clean solder can ﬂow freely across the clean substrate, and ‘tin’ it. (The expression ‘tinning’ derives from the fact that solder is often called ‘tin’ by the craftsmen who use it, and not from the fact that tin is one of its constituents.) It is important at this point to make it quite clear that the ﬂux only has to enable the reaction between substrate and molten solder to take place. It does in no way take part in the reaction once it has arranged the encounter between the two reaction partners. Hence it follows that the nature and strength of the bond between solder and substrate do not depend on the nature or quality of the ﬂux. What does depend on the quality of the ﬂux is the quality of the joint which it has helped (or failed to help) to make. For example, if the ﬂux did not remove all of the surface contamination from the joint faces, the solder will not have been able to penetrate fully into the joint gap, and a weak or open joint will result. Thus there are three basic things which are required to make a soldered joint: 1. Flux, to clean the joint surfaces so that the solder can tin them. 2. Solder, to ﬁll the joint. 3. Heat, to melt the solder, so that it can tin the joint surfaces and ﬁll the joint.

3.1.2 Soldering methods Handsoldering The various soldering methods which are used with electronic assemblies diﬀer in the sequence in which solder, ﬂux, and heat are brought to the joint, and in the way in which the soldering heat is brought to the joint or joints.

job:LAY03 page:4 colour:1

black–text

22 Soldering

With handsoldering, the heat source is the tip of a soldering iron, which is heated to 300–350 °C/570–660 °F. A small amount of ﬂux may have been applied to the joint members before they are placed together. The assembled joint is heated by placing the tip of the soldering iron on it or close to it. Solder and ﬂux are then applied together, in the form of a hollow solderwire, which carries a core of ﬂux, commonly based on rosin. The end of the cored wire is placed against the entry into the joint gap. As soon as its temperature has reached about 100 °C/200 °F, the rosin melts and ﬂows out of the solderwire into the joint. Soon afterwards, the joint temperature will have risen above 183 °C/361 °F; the solder begins to melt too, and follows the ﬂux into the joint gap (Figure 3.1). As soon as the joint is satisfactorily ﬁlled, the soldering iron is lifted clear, and the joint is allowed to solidify. Thus, with handsoldering, the sequence of requirements is as follows: 1. Sometimes, a small amount of ﬂux. 2. Heat, transmitted by conduction. 3. Solder, together with the bulk of the ﬂux. Clearly, this operation requires skill, a sure hand, and an experienced eye. On the other hand, it carries an in-built quality assurance: until the operator has seen the solder ﬂow into a joint and neatly ﬁll it, he – or more frequently she – will not lift the soldering iron and proceed to the next joint. Before the advent of the circuit board in the late forties and of mechanized wavesoldering in the mid ﬁfties, this was the only method for putting electronic assemblies together. Uncounted millions of good and reliable joints were made in this way. Handsoldering is of course still practised daily in the reworking of faulty joints (Section 10.3). Mechanized versions of handsoldering in the form of soldering robots have become established to cope with situations, where single joints have to be made in locations other than on a ﬂat circuit board, and which therefore do not ﬁt into a wavesoldering or paste-printing routine (see Section 6.2). These robots apply a

Figure 3.1 The principle of handsoldering

job:LAY03 page:5 colour:1

black–text

Soldering 23

soldering iron together with a metered amount of ﬂux-cored solderwire to joints on three-dimensional assemblies, which because of their geometry do not lend themselves to wavesoldering nor to the printing down of solder paste. Naturally, soldering with a robot demands either a precise spatial reproducibility of the location of the joints, or else complex vision and guidance systems, to target the soldering iron on to the joints.

Wavesoldering With wavesoldering (Figure 3.2) the following sequence applies: 1. Flux is applied to all the joints on a board. 2. Preheating the board to about 100 °C/210 °F supplies part of the soldering heat by radiation. 3. Molten solder (250 °C/480 °F) is applied in the form of a wave, which also supplies the bulk of the heat to the joints by conduction.

Reflowsoldering With reﬂowsoldering (Figure 3.3), the possible sequences are: 1. A mixture of solder and ﬂux (solder paste) is applied to every joint before assembly. 2. Heat is applied by radiation, convection or conduction. Or 1. Solder is preplaced in solid form on one of the surfaces of every joint. 2. Flux is applied to the preplaced solder. 3. Heat is applied by radiation, convection or conduction. Both wavesoldering and reﬂowsoldering are highly developed methods of quantity production. Being mechanized and automated, they demand integrated systems of controlling and monitoring their various operating parameters.

Figure 3.2 The principle of wavesoldering

job:LAY03 page:6 colour:1

black–text

24 Soldering

Figure 3.3 The reﬂowsoldering principle

3.1.3 Soldering success Whether a completed soldering operation has been successful or not can be unequivocally decided by answering the following three questions by either ‘Yes’ or ‘No’: 1. Has the solder reached, and remained in, every single place where its presence is required for the functioning of the completed assembly? In other words, are there no open joints? 2. Has any solder remained in a place where its presence prevents (or endangers) the functioning of the completed assembly? In other words, are there no bridges (or solder balls)? 3. Is every SMD where it was placed before soldering started? In other words, did any SMDs swim away in the wave, or during reﬂow, or are there any tombstones? What matters here is that the answer to each question is in the nature of an objective verdict, not a subjective judgement of compliance with an arbitrary deﬁnition of quality. This distinction between soldering success and soldering quality has an important bearing on the whole area of quality control. It means that two separate inspectors, including any automatic functional test or opto-electronic inspection method, must arrive at the same verdict. This argument is pursued further in Section 9.3.

3.2 The solder 3.2.1 Constituents, melting behaviour and mechanical properties Solidification and microstructure Soft solders are alloys of lead and tin. Lead, a soft, heavy metal, melts at 327 °C/ 621 °F. Tin, a slightly harder metal of a white colour, melts at 232 °C/450 °F. Lead

job:LAY03 page:7 colour:1

black–text

Soldering 25

by itself is hardly ever used for normal soldering in electronics, because it has a high melting point and needs a strong, corrosive ﬂux or a strongly reducing atmosphere in order to tin copper. Tin takes readily to most substrates, and can be used with mild ﬂuxes, but it too is rarely used by itself, for several reasons: it is expensive, and its melting point is inconveniently high for electronic soldering. The series of tin–lead alloys form a so-called eutectic system: both alloy partners, added to one another, lower the melting point of the resultant mixture; the two descending melting-point curves meet not far from the middle, at the eutectic composition of 63% tin/37% lead, which melts sharply at the eutectic temperature of 183 °C/361 °F. To either side of the eutectic composition, all the tin–lead alloys, which have a tin content between 19.2% and 97.5%, begin to melt at that eutectic temperature when heated from the solid. They also set completely solid at that temperature when cooled down from the molten state. There is a further feature: to either side of the eutectic, the alloys have no sharp melting point, but a melting range, which gets wider as the composition moves away from the eutectic. The lower end of the melting range is always 183 °C/361 °F (called the eutectic temperature), but the top end rises towards the melting points of tin and lead respectively (Figure 3.4). Towards both ends of the melting point diagram certain complications arise, which can be disregarded in the present context. This melting behaviour is reﬂected in the microstructure of the solidiﬁed alloys: seen under the microscope, the eutectic itself forms a ﬁnely interlaced pattern of thin layers of tin and lead. Solders of eutectic composition have the lowest melting point within the whole range and they, as well as their close neighbours, solidify

Figure 3.4 Melting-point diagram and microstructure of the tin–lead alloys

job:LAY03 page:8 colour:1

black–text

26 Soldering

with a smooth, bright surface. On the tinny side of the eutectic, small crystals of nearly pure tin are embedded in its microstructure; lead-rich crystals are embedded on the leady side. On heating, the eutectic always melts at the eutectic temperature, called the solidus, but the tin- or lead-rich crystals do not melt until the temperature has reached the top end of the melting range, called the liquidus (Figure 3.4).

Mechanical strength Alloys are almost always mechanically stronger than their individual constituents. The tin/lead alloys conﬁrm this rule, as Table 3.1 shows. This table lists the tensile behaviour at room temperature (20 °C/68 °F) of lead, tin and eutectic solder, with and without a small addition of silver. As a constructional engineering material, solder is not impressive: Tensile strength of rolled copper sheet: 12 tons/sq. in Tensile strength of rolled brass sheet: 21 tons/sq. in Tensile strength of cast solder 64Sn/37Pb: 4 tons/sq. in These ﬁgures teach us an important lesson: there are only three legitimate functions which a soldered joint should be asked to fulﬁl. They are the following: 1. To conduct electricity. 2. To conduct heat. 3. To make a liquid- or gas-tight seal. No soldered joint ought to be required to transmit any constructional loads or forces unless it is mechanically strengthened, e.g. by forming a double-locked seam. The design of a soldered electronic assembly in which joints are used not only as elements of conduction of electricity or heat, but also of construction, should be carefully examined and possibly reconsidered. This of course begs a question: anchoring reﬂowsoldered SMDs to a board is undeniably a constructional function. However, as long as the mass of an SMD is below 10 g, say half an ounce, the soldered joints between its leads and the footprints should be well able to hold the SMD where it belongs. If the soldered assembly has to survive extreme accelerations (e.g. in military or rocketry hardware) or vibraTable 3.1 The mechanical strength of solder

Metal

Tensile strength at 20 °C/68 °F tons/sq. in N/sq. mm

Elongation %

Tin Lead 63% Sn/37% Pb 3% Sn/2% Ag/35% Pb

1.1 1.0 4.0 4.2

70 45 50 40

17.0 15.5 62 65

At elevated temperatures, tin, lead, and tin/lead solders lose strength progressively: at 100 °C/212 °F about 20 per cent of the room-temperature strength are lost, while at 140 °C/284 °F between 40 and 50 per cent are lost.

job:LAY03 page:9 colour:1

black–text

Soldering 27

tions, the joints should be relieved of the resulting loads by suitable means such as brackets or encapsulation. The loads which are placed on joints between SMDs and their footprints by reason of the thermal expansion mismatch between component and board will be dealt with in Section 3.3.5. As the temperature rises, the strength ﬁgures of solders fall oﬀ, at ﬁrst slowly, and then above 100 °C/212 °F rather more quickly, dropping of course to zero at the melting point of the metal concerned. The reason is that, in terms of absolute temperature (absolute zero is located at −273.2 °C = 0 K, see Section 5.5.2), at room temperature a solder is already within 35% of its melting point.

3.2.2 Composition of solders for use in electronics The preferred composition of solders chosen for the soldering of electronic assemblies is at or near the eutectic, for obvious reasons (Figure 3.5). This choice holds good for all forms of solder: ingot solder for wavesoldering machines, solder wire for handsoldering, and solder powder for solder pastes. Solder pastes and solderwire for the handsoldering of SMDs often contain a small addition of silver, which provides several advantages (Section 5.2.3):

Figure 3.5 Electronic solders and their melting behaviour

job:LAY03 page:10 colour:1

black–text

28 Soldering

1. It improves the strength and fatigue resistance of the soldered joints. 2. It reduces the leach-out of silver from silverbased substrates, such as the metallized faces of certain chips. Tin and lead form a ‘binary’ eutectic, at near enough 63% Sn (61.9% according to the last critical study, with a melting point of 183.0 °C/361.4 °F. Tin, lead and silver form a ‘ternary’ eutectic, with a composition of 62.5% Sn and 1.35% Ag, the balance being lead. This would be the metallurgically correct composition of a silver-containing electronic solder. Some standard speciﬁcations, and consequently some silver-containing solders and solder pastes which are being marketed, have somewhat higher silver contents. The eﬀect which such an excess of silver may have on the joint is discussed in more detail in Section 5.2.3.

Relevant standard specifications The standard speciﬁcations of the major industrial countries list large numbers of solder compositions which meet the needs of all the various joining technologies. Since the early 1990s, much progress has been made in eliminating some of the discrepancies between these standards, both within Europe and between Europe and the USA. Only a few of them are relevant to the soldering of electronic assemblies. Table 3.2 gives the compositions of the solders for use in electronics, as laid down in the International Standard Speciﬁcation ISO 9453 (1990). This standard has now replaced the various national European standards, which had previously been in force. In the USA, the ISO standards are regarded as purely European documents. Since QQ-S-571 was withdrawn, industry in the States is using speciﬁcation ANSI JSTD-006, which overlaps the ISO speciﬁcation (see Table 3.2). It is inadvisable to choose a solder with a tin content below 60%, or an antimonycontaining solder. The former needs higher soldering temperatures, which can be Table 3.2 Composition of solders normally used for electronic soldering Designation

%Sn

%Sb

%Ag

%Pb

ISO 9453 S-Sn63Pb37 E-Sn63Pb37 E-Sn62Pb36Ag2

62.5–63.5 62.5–63.5 61.5–62.5

0.12 0.05 0.05

– – 1.8–2.2

remainder remainder remainder

ANSI JSTD-006 Sn63Pb37C Sn62Pb36Ag02C

63.0 62.0

0.05 0.05

– 2.0

remainder remainder

The ISO preﬁx ‘E’ and the ANSI variation letter ‘C’ indicate that these solders are nominally antimony-free. They are preferred for the soldering of electronic assemblies, because antimony is suspected of aﬀecting the wetting power of a solder on copper and some other substrates.

job:LAY03 page:11 colour:1

black–text

Soldering 29

an important factor when a soldering technique is pushed to its limits, as is the case with wavesoldering of boards which are densely populated with SMDs, or which carry ﬁne-pitch ICs. Also, lower tin-content solders give less attractive joints, of a dull appearance. Antimonial solders are suspected of a lower wetting power on copper and its alloys, especially brass. The material cost of the solder forms a minute part to the total cost of soldering; an attempt to save money by buying a cheaper alloy carries an unjustiﬁable risk. Many solder vendors oﬀer a special solder quality for wavesoldering, with claims for a drastically reduced dross formation in the machine. Their composition conforms to the relevant standard speciﬁcations, but their purity exceeds the requirements laid down in these standards. Several have been manufactured by special processes which aim to improve the behaviour of these solders in the wavemachine still further. With the advent of wavesoldering in an oxygen-free atmosphere, which drastically reduces the formation of dross by removing its cause, these solders may have lost some of their relevance. On the other hand, here too any attempt to save material costs is counterproductive: a cent saved by the purchasing department may cost many dollars spent on rework after soldering.

Alternative solders Circumstances can arise where solders which are not based on lead and tin become attractive. During the mid eighties, it was thought that the malfunctioning of ICs after soldering was to a large extent due to their exposure to the hot solderwave. It could be shown that wavesoldering at temperatures between 180 °C/356 °F and 200 °C/390 °F, using the tin–bismuth eutectic (43% Sn, 57% Bi, melting point 139 °C/282 °F) as a solder gave good results and strong, reliable joints, provided a ﬂux was used which was suﬃciently active at these low temperatures.

However, the quality of ICs improved at about the same time, and lowtemperature wavesoldering never took oﬀ. Under some exceptional circumstances, it can become attractive to carry out a number of reﬂow operations one after the other, each at a lower temperature than the preceding one (sequential soldering). Solder pastes with melting points ranging from 139 °C/282 °F up to 302 °C/576 °F can be supplied by most paste vendors for sequential soldering (Section 5.2.3).

3.2.3 Lead-free solders Lead has long been recognized as a potentially poisonous substance. Nevertheless, its presence in solder as a major constituent has been accepted without protest since the beginning of soldering; this in turn has led to a number of commonsense precautionary rules. As far as they relate to the handling of solder and of solder dross, they are fully discussed in Section 4.7.7. However, since the early 1990s, the presence of lead-containing solder in the ever increasing volume of scrapped and dumped electronic products, which adds up to a very large annual tonnage, has been recognized as a threat to the environment.

job:LAY03 page:12 colour:1

black–text

30 Soldering

Since 1990, the awareness of this environmental problem has led, amongst other things, to the introduction of several bills in the US Congress, which propose to restrict or tax the use of lead-containing solders. This sparked oﬀ an intense search by a number of research organizations and industrial corporations for alternative, lead-free solders. The result is a steadily growing number of patent applications and published papers, not only in the western world, but also in Japan. ITRI Ltd, the former International Tin Research Institute, of Uxbridge, Middlesex, UK, have been particularly active in organizing surveys of up-to-date industrial experience with lead-free solders and coatings, of published literature, and of the steadily growing number of patents relating to lead-free solders and their application.

In practical terms, a price has to be paid for eliminating lead from soldering: with almost all lead-free solders, tin is still the main constituent, the rest being metals such as silver, copper, indium, or bismuth. Most lead-free solders have either higher or lower melting points than normal solder, some of them wet copper less readily, and most of them are more expensive. The soldering behaviour of the principal lead-free solders has by now been well established; determining the long-term properties of joints made with them still needs a great deal of protracted work, though much has been done already. The solders listed in Table 3.3 have been known and used for purposes other than soldering electronic assemblies for a long time. Their melting points are either about 40–50 °C/70–90 °F above or below those of standard lead-containing solders. More complex solders, many of them of a proprietary composition, with melting points closer to those of conventional tin–lead solders have been developed, and these too are commercially available, at a cost. In terms of electronic soldering, a solder with a melting point above or below 183 °C/361 °F needs diﬀerent working parameters and often a diﬀerent ﬂux as well. With wavesoldering, these changes can be accommodated without undue diﬃculty. Reﬂowsoldering poses more serious problems: the ﬂuxes in solder pastes need to be modiﬁed, and for many of the lead-free solders this has been done. Most of the major vendors can now oﬀer solder pastes based on one or more lead-free solders. Reﬂowsoldering equipment presents a more diﬃcult problem: most of the existing reﬂow ovens are designed to produce temperature proﬁles suitable for solders with a melting point of 183 °C/361 °F (Sections 5.5 and 5.6). Working a reﬂow oven with a lower-melting solder is perhaps not too diﬃcult, but changing to a higher-melting one may pose serious problems and most likely requires the Table 3.3 Some lead-free solders already in use Composition

Melting point or range

Comment

1. 3.5% Ag, bal.Sn

221 °C/430 °F

2. 5% Sb, bal.Sn

232 °C–240 °C 450 °F–464 °F 138 °C/280 °F

Strong joints; tins very well Strong joints; tins well Good joints; tins well

3. 58% Bi, bal.Sn

job:LAY03 page:13 colour:1

black–text

Soldering 31

acquisition of a specially adapted oven. Vapourphase soldering with lead-free solders is probably less problematical, since working ﬂuids with diﬀerent boiling points are available (Section 5.4). Generally speaking, changes in working parameters can be costly and may narrow existing process windows. Finally, BGAs with their integral solder-bumps, which are made from lead-containing solder, are just getting into their stride (Section 2.2); a change-over to a lead-free technology would come at an inopportune time. At the time of writing (1997), the electronic manufacturing industry has adopted a ‘wait and see’ attitude towards using lead-free solders. There is a feeling, especially in Japan, that converting a production line to alternative solders will be very costly. It has been stated that some Japanese electronics manufacturers ‘ﬁgure it would be cheaper to pay the proposed US tax (on Pb-containing solder) than to switch to a lead-free technology’.

Meanwhile, organizing the collection, sorting and treatment of scrapped electronic components and equipment, together with the recovery of valuable as well as noxious metals from them, is well advanced. It would certainly seem to be a simpler, more sensible and much less costly approach to the lead-in-solder problem than adjusting the whole technology of soldering in electronic production to lead-free solders.

3.2.4 Solder impurities Impurity limits Impurities in solder merit discussion mainly in the context of wavesoldering, because the initially pure solder bath is liable to become contaminated during use. Solder paste and solderwire are always used in the form and with the degree of purity in which they are received from the vendor. Provided the vendor is experienced and reliable (and nobody should be tempted to buy from any other source) the purity of the solder can be taken as granted, given the present state of the art. Furthermore, the normal buyer is in no position to check the chemical composition of the purchased solder product, and he must of necessity turn to the vendor or to an independent laboratory for a chemical analysis (Section 4.8.5). The impurity limits which ISO 9453 and ANSI J-STD-006 prescribe for the vendor are given in Table 3.4. These ﬁgures are obviously based on international agreement, as would be expected. They must be regarded with one proviso, however: general soldering practice, but particularly wavesoldering practice, shows that with some of these impurities, like iron, aluminium and cadmium, limits tolerable in practical production are lower than those allowed in some standards, as Table 3.5 shows. It should also be added that the purity of the solder supplied by the experienced and reliable vendors mentioned above does indeed keep well within these strict limits.

job:LAY03 page:14 colour:1

black–text

32 Soldering

Table 3.4 Impurity limits according to European and American standards ISO 9453 Cu 0.05% Al 0.001% Cd 0.002% Zn 0.001% Bi 0.10% Fe 0.02% As 0.03% Sb – Ag – Ni – In – Total impurities (not counting Sb, Bi, and Cu) not to exceed 0.08%

ANSI/JSTD-006 0.08% 0.005% 0.002% 0.003% 0.10% 0.02% 0.03% 0.5% 0.05% 0.01% 0.10 –

Table 3.5 Impurity limits according to actual practice

Element

Tolerable practical limit in wavesoldering

Actual analysis of a solder bath after six months’ running

% Cu % Al % Cd % Zn % Bi % Sb % Fe % Ni % Ag % Au % As

0.35 0.0005 0.002 0.001 0.25 0.1 0.005 0.005 1.35 0.5 0.03

0.227 0.001 0.001 0.001 0.015 0.018 0.001 0.001 0.025 0.001 0.01

In a wavesoldering bath, the copper content may rise well above the limit set by the various standard speciﬁcations. A more precise analysis requires a specially prepared sample, not available in this instance. Bi is sometimes added intentionally in amounts up to 2% in order to give a dull, nonreﬂective ﬁnish to the soldered joints. This makes visual inspection easier, without harming the performance of the solder or the quality of the joints. In a wavesoldering bath, both Ag and Au may safely rise above the limits set for them under the general heading ‘all others’, without aﬀecting the performance of the solder or the quality of the joints.

job:LAY03 page:15 colour:1

black–text

Soldering 33

Harmful impurities What matters most is the eﬀect of an excess of a given impurity on the behaviour of the solder in its molten state. If it is acceptable under that heading, the impurity will certainly not harm the ﬁnished joint after it has solidiﬁed. The behaviour of a contaminated solder in a wavesoldering machine is the best yardstick of the eﬀect which a given impurity will produce. These damaging eﬀects are conveniently considered under two headings:

1. Impurities which make the molten solder ‘gritty’ Copper If the copper content of a solder rises above the solubility limit of copper at the temperature at which the solder is being used, small, needle-shaped crystals of an intermetallic copper–tin compound (Cu Sn ) form in the melt (we will encounter them again in every solder joint made on a copper substrate; Section 3.3.1). These crystals reduce the mobility of the molten solder, and can lead to incomplete ﬁlling of narrow joints. They give the joints a rough, ‘sandy’ appearance, and increase the formation of dross. In reﬂowsoldering, the eﬀect of any copper contamination is much less serious, and in any case copper is not a likely impurity in any solder depot which has been reﬂowed unless this reﬂow process has been excessively prolonged. The solubility of copper in molten solder depends on both its temperature and its tin content (Figure 3.6). In a 63% tin solder bath, running at 250 °C/480 °F, the

Figure 3.6 Solubility of copper in non-antimonial solder (author’s measurements)

job:LAY03 page:16 colour:1

black–text

34 Soldering

crystals will appear when the copper content exceeds 0.43%. To make sure that none form in some cooler parts of a wavesoldering bath, it is wise to set the upper copper limit for any wavesoldering bath at 0.35%. In actual wavesoldering practice, copper will hardly ever rise above that point unless something has gone wrong, such as a circuit board having become stuck in the solderwave, or the solder temperature having drifted upwards. Normally, the copper content of a solderbath will settle down between 0.20% and 0.25% after some time, without approaching the solubility limit. As the copper content of the solder rises, its rate of attack on copper slows down, so that the solubility limit is never reached, taking the drag-out of solder on the joints and its replenishment with fresh solder into account. The general use of soldermasks, which leave only the footprints uncovered, has drastically reduced the occurrence of copper contamination. Up to 0.2% of copper are soluble in solid 63% tin solder before the copper–tin crystals appear. Because such solder, when molten, erodes copper soldering bits much more slowly, some vendors market solderwire with this deliberate copper addition. Such solders are of course outside the provisions of the relevant standard speciﬁcation. Should the copper contamination have risen above the danger limit, the simplest way of dealing with it is to empty part of the solderbath and replenish it with fresh solder. The drawn-oﬀ coppery solder will normally be taken back and credited by the vendor, after deducting a charge for reﬁning. Iron Iron is much less soluble in solder than copper: its solubility limit in 63% tin solder at 250 °C/482 °F is 0.017% (author’s measurement). Above that percentage, iron forms small, globular crystals of Fe Sn. They too give the soldered joints a gritty appearance. Iron contamination can occur when ﬁlling the solderbath of a new, carelessly prepared soldering machine: iron ﬁlings, loose nuts, etc., which have been left behind may start to dissolve in the molten solder. Immediate and excessive formation of dross, as soon as the solder pump is switched on, may be a sign of this kind of trouble. Immediate skimming, repeated at frequent intervals, can be a simple remedy. Another cause of iron pick-up by the solder may be local attack by the molten solder on a mild steel or cast iron solderbath. This can happen if a sharp inorganic ﬂux, such as zinc chloride, has erroneously been put on the bath surface. In this case too, excessive dross formation is an indicator. Under normal conditions though, an iron solderbath can be run during the whole useful life of the machine without the slightest iron pick-up in the bath. Fresh solder from any reliable source carries no more than 0.003–0.005% of iron. If a control analysis shows an iron content of 0.01% or more, it is a sign that something must have gone wrong. In this case, the bath ought to be emptied and examined for any signs of tinning by the solder. Any aﬀected spots should be cleaned by grinding, and the exposed iron surface must be oxidized with a blowﬂame, before the container is reﬁlled with clean solder. The contaminated solder is best returned to the vendor.

job:LAY03 page:17 colour:1

black–text

Soldering 35

2. Impurities which produce a skin on molten solder Impurities in this class cause the formation of a tough oxide skin on the solder surface. In appearance it is similar to the skin formed on hot milk. Even repeated skimming will not remove it. Skinny solder causes bridging, ‘icicles’, and the formation of solder adhesions on the substrate, often called ‘snails’ trails’. It is important to realize, however, that there may be another cause for these troubles, related to deﬁcient ﬂuxing (Section 4.2). Before jumping to any conclusion, ﬁrst check whether there is a skin on the solder surface which cannot be skimmed oﬀ. There is no remedy against skin-forming impurities once one of them has entered the solderbath. The solder container must be emptied, and most carefully cleaned of any remaining solder, before it is reﬁlled with fresh solder. These considerations do not apply to wavesoldering in a controlled, oxygen-free atmosphere. Zinc Zinc causes skinning when present in amounts above 0.001%. It can occasionally get into a solderbath by mistake: immersing any galvanized steel implement in the molten solder is enough to ruin it. The diecasting alloy Mazak is based on zinc, but fortunately it is diﬃcult to tin. A diecast item which has fallen into the bath will not immediately cause any harm if it is retrieved within a reasonable time, say a few hours. Brass too contains zinc, but there is no record of any zinc pick-up by a solder bath, even if brass screw heads or rivets pass regularly through the solderwave and are tinned in the process. Cadmium Cadmium acts like zinc, if present in amounts above 0.002%. Before cadmium was outlawed as a poison, cadmium-plated ﬁttings on circuit boards were a frequent cause of cadmium contamination. Today, cadmium can be disregarded as a skinformer in wavesoldering operations. Before its threat to health was recognized, eutectic lead–tin solders, laced with up to 1 per cent of cadmium, were often used for reﬂowsoldering or ‘sweatsoldering’ silver-coated ceramic insulators to condenser lids or similar metal parts. Cadmium in solder slows down the rate of its attack on silver by at least one order of magnitude (author’s measurements), because it forms a high-melting intermetallic compound with silver. With this particular type of ‘sweatsoldering’, the skin-forming tendency of Cd-containing solders was no serious impediment. Aluminium Aluminium is the most virulent skin former: above 0.0005% it will cause the skin eﬀect, but there are few circumstances under which it could ever get into a solderbath. Some caps of milk bottles are made of aluminium foil, as is the metal foil in many cigarette packs. Any of those found ﬂoating on a solderbath are, in any case, signs of bad works discipline and lack of supervision. Fortunately, aluminium is diﬃcult to tin under normal circumstances, and if removed within the working day the above items will not have caused any harm.

job:LAY03 page:18 colour:1

black–text

36 Soldering

3. Harmless impurities and deliberate additions Silver Silver cannot be regarded as a harmful impurity unless it exceeds the silver content of the ternary tin–lead–silver eutectic (1.35% Ag) by a signiﬁcant amount (‘hypereutectic’ silver content). Even then, it will not form high-melting intermetallic crystals, which make the molten solder gritty, because it is very soluble in solder above its melting point. Hyper-eutectic silver aﬀects only the microstructure of the solidiﬁed solder: with two or more per cent of silver, as speciﬁed in some standard speciﬁcations (Table 3.2), there is the possibility of large, plate-shaped crystals of Ag Sn appearing in soldered joints which have solidiﬁed rather slowly, as can occur in vapourphase soldering. Though these crystals are supposed not to be brittle, their presence is undesirable, and it is advisable to use solders with less than 2% Ag unless speciﬁcally requested by the customer. The presence of silver in its correct eutectic proportion confers several advantages: for one, it lowers the melting point of the solder from that of the binary eutectic (183 °C/361 °F) to that of the ternary (178 °C/352 °F). In many diﬃcult soldering situations, that gain of 5 °C/9 °F can be useful. For another, silver has been found to improve the strength and fatigue resistance of soldered joints. Finally, the silver addition slows down the rate of attack of the molten solder on silver-based substrates such as the metallized faces of certain chips (Section 5.2.3). Gold Gold dissolves extremely quickly in molten solder, which can hold 16% gold in solution at 250 °C/480 °F. On solidifying, most of the dissolved gold precipitates out in the form of large, brittle crystals of AuSn , which weaken the joint structure and cause cracks, even at slight loads.

The solubility of gold in solid eutectic solder is 3%, which would therefore be the safe limit for gold contamination in a wave solderbath. In practice, this would mean a gold content of 3000 g/97 oz troy in a solderbath of 100 kg/220 lb, representing a value many times that of the soldering machine. Normally, it will be worthwhile to empty a solderbath when its gold content has risen to 0.2%, and oﬀer it to a metal reﬁner for sale. Gold contamination arises from the wavesoldering of circuit boards with partially unprotected gold-plated edge contacts, or gold-plated footprints or component leads. The latter are more frequently encountered with military or space contracts in the US than in Europe. Reﬂowsoldering of gold-plated footprints or component leads can result in dangerously embrittled joints. With reﬂowsoldering, the products of the solder– substrate reaction remain trapped within the joint. Any gold carried on its surfaces turns into the brittle AuSn which, especially with narrow ﬁne-pitch impulse of the joint gap, with possibly dire long-term results. soldered joints, might ﬁll much Hence the frequently encountered prescription to remove the gold from gold-plated leads by brieﬂy dipping them in a small solderbath, which can be disposed of when it has become suﬃciently loaded with gold. With gold-plated footprints, the only recourse may be local de-plating, equipment for which is commercially available.

job:LAY03 page:19 colour:1

black–text

Soldering 37

Indium Indium, like Cd, forms a high-melting intermetallic phase not only with silver, but also with gold. It is therefore sometimes added to eutectic tin–lead solder to prevent the leach-out of gold-plated joint surfaces. A binary alloy of the composition 70% In/30% Pb has a melting range of 165 °C/329 °F to 173 °C/343 °F, and makes good, strong joints, not only on gold-plated but also on copper surfaces. Several of the proposed lead-free solders contain indium as an alloying constituent (Section 3.2.3).

3.3 The soldered joint 3.3.1 Soldering as a surface reaction between a molten and a solid metal Preconditions for the reaction A soldered joint is the result of a reaction between a molten metal, the solder alloy, and a solid metal surface, the substrate. This reaction can only start and proceed if the solid and the liquid can directly touch one another, without any intervening obstacle. As has been mentioned already, a non-metallic surface ﬁlm forms on all metallic surfaces, except on gold and platinum, when they are exposed to the normal atmosphere. In perfectly clean air this ﬁlm will be an oxide, but under many circumstances sulﬁdes can form as well, and some water vapour also may have been adsorbed. Before they come to be soldered, most substrates will have passed through a number of manufacturing operations. These leave their mark in the form of solid organic or metallic particles, or ﬁlms such as left-over processing chemicals or ﬁngerprints. All these must be cleaned oﬀ before any soldering operation (Section 8.1.1), but no normal precleaning can remove the oxides and sulﬁdes; only a chemical reaction can remove these. Dealing with them is the task of the soldering ﬂux, which is the subject of Section 3.4. For the present, we will assume that that task has been accomplished, and that the molten solder and the substrate touch one another without any intervening non-metallic ﬁlm.

The solder/substrate reaction Several things matter here: on the one hand, the surface temperature of the substrate must be above the melting point of the solder; if it is not, the reaction cannot start because the solder will set solid at the interface. The joint members and their immediate environment must receive enough soldering heat to achieve this. On the other hand, the substrate must of course never melt, and the soldering temperature must always keep well below its melting point. If it approaches it too closely, the solder/substrate reaction will get out of control and the solder will alloy with it and very likely destroy it, instead of reacting with it. This is unlikely to happen in normal soldering practice, except perhaps when soldering with laser energy.

job:LAY03 page:20 colour:1

black–text

38 Soldering

Because the reaction between the tin in the solder and the substrate is exothermic, it occurs spontaneously as soon as the molten solder and the clean substrate touch one another. As a further consequence of its exothermic nature, the reaction will proceed and the solder will cover as large an area of the substrate as its available amount and its surface tension, which tries to prevent its spread, will allow. These matters will be dealt with under the aspect of ‘Wetting’ (Section 3.4.1). In the present context we are concerned with the events at the interface between the molten solder and the solid substrate, once wetting has been established. Furthermore, since copper is the most commonly encountered substrate in SMD soldering, we shall from now on deal with the interaction between solder and copper unless speciﬁcally stated otherwise.

3.3.2 Structure and characteristics of the soldered joint The reaction products The products of the molten-soldersubstrate, or more correctly the tin/copper reaction are the so-called ‘intermetallic compounds’. They appear as a solid layer on the interface between the two partners, which is commonly known as the ‘intermetallic layer’, or ‘diﬀusion zone’. The diﬀusion zone itself consists of two distinct layers of diﬀerent intermetallic compounds. Next to the copper comes a thin layer of Cu Sn, to which metallurgists have assigned the Greek letter ‘epsilon’ (). This layer is covered with a somewhat thicker one, with the composition Cu Sn , known as ‘eta‘ () (Figure 3.7). At normal are solid, but above 415 °C/959 °F they begin to soldering temperatures these layers dissolve in the molten solder. Substrates other than copper form their own speciﬁc diﬀusion zones, which are listed in Table 3.5. Though they diﬀer in their composition, they share their crystalline structure with that of the zone formed on copper, with the same consequences for the mechanical properties of the joint itself.

Intermetallic compounds The intermetallic copper–tin compound can appear in the soldered joint itself if the molten solder becomes oversaturated with copper during solidiﬁcation (see Figure 3.6). It forms hexagonal needles, which are sometimes hollow, embedded in the tin–lead crystal structure of the solder. Unless they have become excessively Table 3.6 Substrates and their speciﬁc diﬀusion zones Substrates

Intermetallic compounds

Cu Ni Fe Ag

Cu Sn () Cu Sn () , Ni Sn Ni Sn , Ni Sn FeSn, FeSn Ag Sn

job:LAY03 page:21 colour:1

black–text

Soldering 39

Figure 3.7 Cross-section through a soldered joint, made with eutectic solder

large, due to the soldered joint having solidiﬁed very slowly, they do no harm. On the contrary, they may well have a strengthening eﬀect, since crystals were an intentional constituent of tin- and lead-base bearing metals when these alloys were still a common engineering material. The same applies to the crystals of NiSn which form on the interface between the solder and the nickel diﬀusion barrier on certain component leads (Section 3.6.6). Other intermetallic compounds are less innocuous interlopers in a soldered joint. Plate-shaped crystals of Ag Sn form in solder which is supersaturated with silver reach considerable size in a slowly solidiﬁed joint, but (Section 3.2.3). They too can are taken to be harmless because they possess a certain ductility (private communication, International Tin Research Institute). On the other hand, the ﬂaky crystals of AuSn , which are liable to form in a soldered joint made on gold, or any gold deposit, which is too thick (Section 3.6.6) are decidedly fatal: they are brittle and very weak. Any soldered joint in which they have formed is liable to crack.

Reflowsoldering versus wavesoldering: the metallurgical consequences There is an important diﬀerence between the metallurgical features of wavesoldered and reﬂow-soldered joints: with wavesoldering, most of the reaction products between solder and substrate, apart from those anchored in the intermetallic layer, are washed back into the large volume of the solder bath where they dissolve and very gradually add to its copper content (Section 3.2.3). By contrast, every reﬂowsoldered joint forms a closed system, with a very small solder volume, in which all the products of the solder/substrate reaction stay trapped. As the solder solidiﬁes, they precipitate out from solution and form crystallites which are dispersed through the joint. Their size depends on the speed at which the joint solidiﬁes, and this varies widely between the diﬀerent reﬂowsoldering methods. The relevant parameter here is the solidiﬁcation interval, which can be deﬁned as the time elapsed between the point when the joint temperature falls away from its maximum and the point when it passes through 183 °C/361 °F.

With laser soldering, the solidiﬁcation interval is measured in milliseconds; with wavesoldering it is below 0.5 seconds, with infrared soldering it is about one to two seconds, and with vapourphase soldering it may be up to ﬁve seconds, depending on the design of the plant. The longer the solidiﬁcation interval, the coarser will be the

job:LAY03 page:22 colour:1

black–text

40 Soldering

grain structure of the joint, and the larger will be the intermetallic crystals dispersed in it. This factor has a measurable eﬀect on the long-term behaviour of a joint. In the longer term, the microstructure of a soldered joint slowly changes after soldering: due to a process of slow diﬀusion in the solid state, the ﬁne lamellar structure of the tin–lead eutectic becomes coarser. Also, because the energy level of the intermetallic phases and is lower than that of both copper and solder, the phase change which led to their formation slowly continues in the solid state. These phenomena, and their consequences, will be discussed in Section 3.3.3.

Factors which determine the microstructure of a joint The thickness of the diﬀusion zone depends on several factors: ﬁrst of all on the maximum temperature reached during soldering, and secondly on the length of time during which the substrate was exposed to the molten solder, i.e. the time which it spent above 183 °C/361 °F. The latter will be termed ‘confrontation period’ from now on. The higher the temperature reached during soldering, and the longer the confrontation period, the thicker will be the diﬀusion zone. Both the confrontation period and the maximum temperature reached during soldering vary widely between diﬀerent soldering methods. So does the thickness of the diﬀusion zone (Table 3.6). What also matters is the speed at which a joint solidiﬁes, i.e. its rate of cooling between its maximum temperature and the point at which its temperature drops below 183 °C/361 °F. The higher the speed of solidiﬁcation, the ﬁner is the grain structure of the solder in the joint.

3.3.3 Mechanical properties of soldered joints The mechanical behaviour of the typical soldered joint is a consequence of its layered structure. The solder in the middle of the sandwich is comparatively yielding and ductile. This means that it can absorb stresses which may occur, for example, through a thermal expansion mismatch between a component and the Table 3.7 Relationship between soldering parameters and zone thickness

Soldering method

Wavesoldering Reﬂow: Laser Vapour phase Infrared and/or convection Impulse

Confrontation period 2–5 sec 0.02–0.04 sec 25–40 sec 15–30 sec 0.5–3 sec

Temperature °C °F 250

480

250–350 215 250–300 250–300

480–900 419 480–570 480–570

Zone thickness m 0.3–0.8 O0.1 0.7–1.5 0.5–1.5 0.1–1.0

job:LAY03 page:23 colour:1

black–text

Soldering 41

substrate on which it is mounted. On the other hand, the diﬀusion zone on either side of the solder consists of crystals which are strong, hard and brittle. Their response to any deformation is to crack. From this it follows that a soldered joint is strong in shear and tension, but relatively easy to peel apart provided at least one of the joint members is ﬂexible (as anyone knows who has managed to open a sardine tin by rolling back its soldered lid) (Figure 3.8). The numerical values of the mechanical strength of solders and soldered joints under various manners of loading are given in Table 3.8. Some interesting facts emerge from these data, which result from early pioneering work on the properties of soldered joints. Joints made with lead between copper members have a remarkably high tear strength. A strong ﬂux or a strongly reducing atmosphere are needed to persuade lead to ‘tin’ copper, but the adhesion between the two metals is very strong once it has been achieved. There is no intermetallic layer at the interface, but there is a certain, very slight mutual solubility between the two metals. The bonding between them is not exothermic as is the case with tin-containing solders. This means that in contrast to a soft-soldered joint, there is no long-term change in the microstructure of a Pb/Cu joint, which therefore has an excellent long-term stability (Section 3.3.4). Furthermore, the small amount of Cu dissolved in the lead which ﬁlls the joint adds to its strength. In this context, a nickel substrate behaves in a manner very similar to that of copper.

3.3.4 Soldering on surfaces other than copper Many SMDs confront the solder with substrates other than copper. Naturally, the molten solder interacts with them in quite a diﬀerent way (Table 3.9). The high leach-out speeds of gold and silver mean that thin layers of them will disappear in molten solder almost instantaneously. Additions of palladium to silver (on chipcapacitors’ metallized faces) or platinum to gold (on LCCC metallized surfaces) slow down this rapid leach-out without reducing the solderability too much, but considerably raising the cost. Nickel dissolves in molten solder by two orders of magnitude more slowly than silver. For that reason, it is often used as a barrier layer to protect the leachable noble metal from the solder. Because the solderability of nickel requires highly activated ﬂuxes, it is often given a galvanic topcoat of copper and/or tin or tin/lead solder. One point needs mentioning here. This topcoat of tin or solder will of course disappear immediately as the molten solder ﬂows over it. The molten solder will then have to confront whatever metal surface it ﬁnds underneath. This surface must be absolutely clean, otherwise the solder will ‘dewet’ (Section 3.6.1). If it is not inherently solderable, like for example iron or stainless steel (Section 3.6.4), it must be copper plated before the topcoat of solder or tin is applied. The solderability aspects of component terminals are dealt with speciﬁcally in Section 3.6.6 and those of circuit board surfaces in Section 6.4. The lack of solderability of a surface covered with a layer, however thin, of the intermetallic compound Cu Sn () is dealt with under ‘solderability’, Section 3.6.5.

job:LAY03 page:24 colour:1

black–text

42 Soldering

Figure 3.8 The mechanical behaviour of soldered joints under stress Table 3.8 The mechanical properties of solder and soldered joints Solder Bulk strength* tons/sq. in N/sq. mm Shear joint strength on copper* tons/sq. in N/sq. mm Max. sustained shear load on copper** tons/sq. in N/sq. mm Tear strength on copper (Cadwick)** N/mm width of joint

100% Pb

60 Sn/40 Pb

60 Sn/40 Pb+Ag

100% Sn

0.9 140

4.0 620

4.5 700

1.1 170

— —

2.8 430

— —

— —

— —

0.5 77

0.6 93

7.6

7.1

14

— — 8

*Derived from data given by Nightingale, S. J. (1929) The Jointing of Metals, Part 1: Soft Solders and Soldered Joints. Res. Report No. 3, Brit. Nonf. Met. Res. Assoc., Wantage, UK. **Derived from data given by McKeown, J. (1956) Properties of Soft Solders and Soldered Joints. Res. Monograph No. 5, Brit. Nonf. Met. Res. Assoc., Wantage, UK.

job:LAY03 page:25 colour:1

black–text

Soldering 43

Table 3.9 Solderable terminals of diﬀerent SMDs. (Tabular form of the data given in Section 2.3) Component

Nature of terminal

Melf resistors

Caps of Fe, Cu-plated (1 m), galvanic surface coating of 90 Sn/10 Pb (1–3 m) End-caps of 89 Cu/9 Ni/2 Sn; hot-tinned with 60 Sn/40 Pb (2–8 m) Thick-ﬁlm Ag (80–90)/Pd (20–10), 30–100 m thick, or Thick-ﬁlm Ag, galv. coated with 1–5 m Ni (barrier layer), top cover of galv. 3–10 m Sn Thick-ﬁlm Au (62–87)/Pt (38–13) Gullwing leads of 42 Ni/58 Fe sheet, often galv. coated Cu (1–5 m), top-coat hot-tinned 60 Sn/40 Pb, or 98 Cu/2 Fe sheet, galv. or hot-tinned Sn (3–10 m) Ditto, made from thinner-gauge sheet

TA and MKT condensers Chip resistors and ceramic condensers LCCCs SOTs, SOICs, PLCCs QFPs, TABs

Based on verbal communication, W. Richly, Siemens, Germany. Table 3.10 Solder interaction with substrates other than copper

Substrate

Intermet. phase adjacent to the solder

Speed of solder/substrate reaction

Speed of substrate leach-out at 250 °C/480 °F

Cu Au Ag Ni

Cu Sn AuSn Ag Sn NiSn

fast very fast very fast slow

0.15 m/sec 5.25 m/sec 1.6 m/sec 0.01 m/sec

3.3.5 Long-term behaviour of soldered joints The microstructure of a soldered joint changes slowly with time, in two respects: 1. The ﬁne lamellar structure of the eutectic gets coarser, because there is a certain amount of energy tied up at any grain boundary; a soldered joint populated by a small number of coarse grains of lead and tin has a lower energy content than one consisting of many small tin and lead crystals. This energy diﬀerence is the driving force for the grain coarsening, which proceeds through the mechanism of solid diﬀusion. 2. The intermetallic crystals and , which have formed at the solder/substrate interface, continue to grow. This growth, the result of a solid-state reaction, is also driven by an energy diﬀerential, because the tin/copper reaction is exothermic. This means that the tin–copper compounds have a lower energy content than the reaction partners by themselves. Like all reactions, the speed of both grain coarsening and the thickening of the intermetallic layer increase rapidly at higher temperatures. Since at room temperature a soldered joint is already within 34% of its melting point in terms of absolute temperature (Section 3.2.1), it is not surprising that at, for example, 100 °C/212 °F the tin

job:LAY03 page:26 colour:1

black–text

44 Soldering

and lead atoms can move through the crystal lattice of the solder with about twice their room-temperature mobility. Ageing and the consequent grain coarsening lower the mechanical strength and the ductility of a soldered joint. The thickening of the brittle intermetallic layer does not weaken a joint, but it reduces its ability to absorb repeated deformation without cracking. The mechanism of joint failure in service has been the subject of many investigations. A recent important contribution examines in detail the metallurgical features of the various types of joints between SMDs and their footprints, the mechanics of their failure, and the possibility of predicting their fatigue life under the conditions of practical operation. It is worth noting that the paper’s conclusions end with the sentence ‘Further work is needed.’

3.3.6 Long-term reliability of soldered joints The meaning of ‘reliability’ The expression ‘long-term reliability’ of an electronic assembly, or of any soldered joint in it, can be given a precise meaning in this context: it represents its ability to function as expected, for an expected period of time, within an expected failure level. In a recent study, it has been stated: ‘a solder joint in isolation is neither reliable nor unreliable: it becomes so only in the context of the electronic components that are connected via the solder joints to the printed wiring board. The characteristics of these three elements, together with the conditions of use, the design life, and the acceptable failure probability for the complete assembly determine the reliability of the surface mount attachment.

An important factor in the reliability consideration are the anticipated conditions of service. Tables have been drawn up which list ‘worst-case use environments’ ranging from consumer electronics (temperature range 0 °C/32 °F–60 °C/140 °F, 12 hrs daily running, 365 operating cycles per year) to automotive under-hood electronics (temperature range −55 °C/−67 °F to 125 °C/257 °F, with up to 1000 one-hour operating cycles per year). These scenarios form the basis for accelerated test programs to assess the reliability of a given electronic assembly.

The mechanics of joint failure If a soldered joint on an SMD populated board fails in service, it is through fatigue damage (unless is was so badly soldered that it came apart at the ﬁrst provocation). The stresses which produce fatigue failure can be caused by a mismatch between the thermal expansion of the board and the component, or by a temperature diﬀerence between the two at the beginning or after the end of a cycle of operation. There are some mitigating factors: if the component is small, the lateral joint displacement is small. If the temperature cycle is relatively short, the elastic deformation of the solder in the joint can take care of the strain before the solder begins to creep. The same is true for low operating temperatures, where the elastic limit of

job:LAY03 page:27 colour:1

black–text

Soldering 45

solder is higher. If the component leads are compliant, they can absorb the strain. Conversely, there can be aggravating circumstances: if, for some reason, the intermetallic zone ﬁlls a large part of the joint gap, the solder left in it is less capable of yielding to strain and the joint is likely to fail earlier. The stiﬀ gullwing legs of SOTs or SOs are less compliant than the thin leads of multilead components. The fatigue aspects in the life of a soldered joint have been extensively investigated and described. \

Design for joint reliability Given certain constraints, such as the operational environment and operational cycles, some factors are in the hands of the designer. For example, components with compliant leads should be a preferred choice, while melfs and chips with their stiﬀ joints should be as short as possible to minimize the eﬀect of the thermal expansion mismatch between them and the FR4 board. The leadless ceramic chipcarrier, soldered to an epoxy board, has suﬀered an unlamented extinction because of its large size. There is no serious thermal expansion mismatch problem between the polymer body of a BGA and an FR4 board. ‘Controlled-collapse’ bumps, formed from a lead-rich alloy which can accommodate thermal stresses better than a eutectic tin–lead solder (see Section 2.1.3) can provide a way out if such is required.

3.4 The flux 3.4.1 Tasks and action of the soldering flux Removing oxide skins The success of any soldering operation depends critically on the condition and behaviour of two surfaces: that of the substrate and that of the molten solder. The ﬂux has to deal with both of them (Section 3.1.1). By the time the molten solder encounters the substrate, the ﬂux should have completely removed all surface oxides from both the molten solder and the substrate, so that nothing prevents or interferes with the reaction between the two: this is the precondition for the formation of a soldered joint (Figure 3.9).

Figure 3.9 The function of the ﬂux in soldering

job:LAY03 page:28 colour:1

black–text

46 Soldering

During the solder/substrate reaction, which takes place at a temperature above 183 °C/361 °F, the ﬂux must prevent the formation of fresh oxide on both solder and substrate. Soldering methods which exclude or at least drastically reduce the presence of oxygen from the scene of joint formation are a help with the second task: wave soldering under nitrogen falls into that class. It can of course not remove any oxide which is already there before soldering starts, because nitrogen is purely protective and will not actively reduce oxides (Section 4.6). With reﬂowsoldering under nitrogen or in a vapour phase, using a solder paste, the situation is not so clear-cut: it could be argued that the ﬂux portion of the solder paste not only precleans both the substrate and the solderparticles in the paste, but when the solder melts, it is on hand to promote the union between the two, while at the same time excluding the atmospheric oxygen from the scene of action. Whatever the truth of this may be, practice conﬁrms that, when reﬂowsoldering with no-clean solder paste in the absence of oxygen, whether in a nitrogen-ﬁlled reﬂow oven or in a vapourphase (Section 5.6.4), there are decidedly fewer soldering faults than when soldering with normally activated pastes in a normal atmosphere (Chapter 3.4.3).

The oxide skin on molten solder In a normal atmosphere, a thin skin of oxide forms almost immediately on the surface of molten solder as soon as it is exposed to atmospheric oxygen. This skin acts like a tough, somewhat rigid envelope on the liquid solder and restricts its free movement. A simple but instructive experiment, which anyone can (and probably should) repeat on a benchtop, demonstrates this action. Place a short piece – about 2 cm/1 in long – of solid solder wire (without a core of ﬂux) on an untinnable surface, e.g. a small piece of stainless steel sheet or a ceramic wafer, and heat it on a hotplate or over a gas burner until the solder melts. You will ﬁnd that as the solder wire melts, it retains its shape, looking very much like a small sausage in a somewhat crinkly skin. Now let one drop of soldering ﬂux (e.g. an RMA or RA ﬂux) fall on that sausage: the skin will disappear in an instant and the sausage turns into a shiny, perfectly spherical ball of liquid solder (Figure 3.10). This experiment demonstrates two things:

Figure 3.10 The solderwire/ﬂux experiment

job:LAY03 page:29 colour:1

black–text

Soldering 47

1. Even a mild ﬂux removes the oxide skin from molten solder by dissolving or dispersing it. It is mainly the tin oxide which contributes to the stiﬀ nature of this skin. Lead oxide is more powdery. 2. The molten solder, as soon as it is free to move, forms a round sphere, this being the shape with the smallest surface area which a given volume of liquid can assume. The molten solder assumes that shape under the inﬂuence of its ‘surface tension’, which it can follow without restraint as soon as the oxide skin has disappeared. Surface tension is the result of the force with which every atom or molecule in a liquid attracts its neighbours. Any such particle which is well inside a given volume of liquid is attracted equally from all sides, so that the forces acting on it cancel out. The particles at the surface have neighbours only on the inwards-facing side, so that they are all being pulled inwards. Consequently, the liquid tries to make its surface as small as possible, and forms a sphere: in eﬀect, the surface behaves like a tensioned skin which encloses the molten solder, hence the term ‘surface tension’ (Figure 3.11). Surface tension, tending to reduce the surface of a given volume of molten solder to a minimum, is responsible for the suppression of icicles and bridges in wavesoldering (Section 4.4.3), and for the suppression of ‘solderballing’ and bridging in reﬂowsoldering with solder pastes. Hence the need for some ﬂux to survive on the underside of the board during its passage over the solderwave, so as to be available to prevent bridges and icicles forming on the exit side (Section 5.2.3) (Figure 3.12). If the solderwire/ﬂux experiment were repeated in an oxygen-free atmosphere, the mobility of the molten wire would not be impeded by an oxide skin: on melting, it would pull together into a near spherical shape, and even a very weak ﬂux would let it form a perfect globule.

3.4.2 Wetting and interfacial tension It is sometimes asserted that the ﬂux lowers the surface tension of molten solder, thus helping it to spread over a substrate or penetrate into a joint. This is not correct. All the ﬂux does to the molten solder is to let it move freely, so that it can follow the forces which act upon it. These forces are not only its own surface tension, but also the so-called ‘interfacial tension’ or wetting force, which pulls the solder across the surface of the substrate.

Figure 3.11 Surface tension and the molten solder wire

job:LAY03 page:30 colour:1

black–text

48 Soldering

Figure 3.12 Icicles, bridges, and surface tension

The chemical aﬃnity between the substrate and the tin in the solder is the driving force behind the formation of the intermetallic crystals. The energy set free, as the solder reacts with the copper (or nickel or silver) substrate, pulls it sideways into a ﬂat coating or into a joint gap. (There is some evidence, though, that some ﬂuxes initiate chemical reactions, which actively pull the molten solder across the substrate – Dr W. Rubin, verbal communication.) This wetting force overcomes the inwards pull of the surface tension of the solderglobule, forcing it to give up its spherical shape and to ﬂow where it is needed. The wetting force is the same as the interfacial tension. What matters is that the interfacial tension is higher than the surface tension of the solder (Figure 3.13). It is worth stating here once again that the ﬂux has nothing to do with the strength or quality of the resulting bond. All it does is to clear the path for the solder to advance across the substrate, and to give it the mobility to do so.

3.4.3 Properties required in a flux The essential function of a ﬂux is of a chemical nature: it must remove a surface layer of a metallic oxide or tarnish, in most cases from copper, tin and lead, less frequently from nickel. It does this by reducing the solid oxide skin to a soluble metallic salt, which means that the ﬂux must be of an acidic nature. To deal with copper, tin and lead oxides, even very mild organic acids such as natural rosin will do. When other metallic surfaces are involved, or when the reaction must be fast, like in industrial soldering, the ﬂux has to be more reactive, which generally means more acidic. Apart from this chemical reaction, a ﬂux must be capable of physically lifting the freshly formed metallic salts from the surface to be soldered, by taking them into solution or by dispersing them. The physical requirements which the ﬂux must meet depend on the soldering method used: 1. With wavesoldering, the ﬂux must be suitable for being applied to the entire surface of a circuit board by an automatic and reproducible method (Section 4.2). A liquid ﬂux is best suited for this purpose. For reasons discussed in the

job:LAY03 page:31 colour:1

black–text

Soldering 49

Figure 3.13 The wetting process as a balance between surface tension and interfacial tension. : Wetting angle

2. 3.

4.

5.

relevant chapter, gaseous ﬂuxes are not entirely satisfactory, at least not at the present state of the art. The liquid ﬂux must wet the board evenly, and well enough to penetrate into narrow gaps and ﬁll the vertical holes in throughplated double-sided boards. Given a liquid ﬂux cover of up to 0.5 mm/20 mil thick, its volatile constituents should be capable of being driven oﬀ by heating to about 100 °C/ 210 °F within not much more than 10 sec. Suﬃcient of the thickened ﬂux left after this must be able to physically survive the passage through a double wave, if one is employed, so as to stop the solder on the exit side from oxidizing and thus to prevent bridges, icicles, ‘spider’s web’ or ‘snails’ trails’ and solder balls. At the soldering temperature, the ﬂux must be a mobile liquid, and form a coherent cover for the front of the molten solder as it advances across the substrate, as shown in Figure 3.13. In addition to this, the oxide-reducing capability of the ﬂux must survive exposure to the soldering heat for as long as the soldering method demands: with a double wave in wavesoldering, this heat exposure may last up to ﬁve seconds at 250 °C/480 °F. In an infrared oven, the temperature may rise above 183 °C/361 °F for over 30 sec, with a peak of about 300 °C/390 °F. Physically, the ﬂux, having lost much of its solvent portion, must remain suﬃciently mobile to make way for the molten solder, allowing it to ﬂow across footprints and component leads, to rise up through every through-plated hole, and to penetrate into every joint gap. Therefore, it must not polymerize, become sticky, carbonize, or cake up during the temperature excursions of the soldering process. It must retain its mobility during soldering, and not become diﬃcult or impossible to remove after soldering. In the last few years, the removal of ﬂux residues from soldered assemblies has become a dominating topic. There are a number of reasons why cleaning after soldering may be necessary, and these are fully discussed in Section 8.1.1. The

job:LAY03 page:32 colour:1

black–text

50 Soldering

need to consider cleaning has become a dominating factor when choosing a ﬂux.

3.4.4 Rosin fluxes Until the seventies, only rosin-based ﬂuxes were considered suitable for electronic soldering. In their liquid form, rosin ﬂuxes are, or were, solutions of rosin in alcohol, with solids contents of up to 25% or more. Their residue could safely be left on the ﬁnished board, where it formed a hard, protective coating. Indeed, up to 60 °C/140 °F, pure rosin has a bulk resistivity of the same order of, if not better than, FR4. Therefore, in the early days of wavesoldering, one liked to see the soldered boards coated with a hard, shiny and continuous varnish-like coating of solidiﬁed rosin. If considered necessary, this residue could easily be removed with an azeotropic mixture of CFC113 and an alcohol. Since the existing or impending banishment of the CFCs, this situation has changed drastically (Sections 8.3.5 and 8.3.6). Natural rosin is a distillation product of the sap of pine trees. Chemically, it is a mixture of several organic acids, such as abietic and pimaric acid and their close relatives. Its composition depends very much on its place of origin and is also seasonally variable, so that buying good rosin is a matter of skill and judgement. Instead of a pH value, the acidity and hence the ﬂuxing power of a rosin is deﬁned as its ‘acid value’, which is measured in mg KOH per g, this being the amount of KOH required to neutralize a rosin solution in alcohol, per gram of dissolved rosin. An acid value of 160–180 would be considered adequate for a good rosin. The variable nature and the ﬂuctuating price of natural rosin were a strong incentive to search for synthetic alternatives. Pentaerythritol tetrabenzoate, a proprietary product, was the ﬁrst synthetic alternative to natural rosin to be used in a range of synthetic resin ﬂuxes. By now, it has been followed by a number of other synthetic resins with physical properties resembling those of natural rosin, which are used as alternatives to it in soldering ﬂuxes. In recognition of this, ISO 94S4-1 in its classiﬁcation of soldering ﬂuxes distinguishes between rosin- and resin-ﬂuxes (see Table 3.11). At room temperature, solid rosin is chemically inert, and as a ﬂux residue it protects the soldered board against dirt and moisture. At temperatures exceeding 50 °C/120 °F, rosin becomes sticky and attracts dust and ﬂuﬀ, and is then no longer an attractive ﬂux residue. In the molten state, above about 80 °C/180 °F, and as a solution in alcohol, rosin reacts with copper like a mild acid, and acts as a ﬂux. Because its ﬂuxing action on untinned copper is not particularly eﬃcient, so-called activators which enhance its eﬃciency are normally added to the rosin. These will be dealt with presently.

Problems with rosin fluxes 1. Rosin softens and becomes chemically active above about 70 °C/160 °F. This may happen if the assembly has to operate in a hostile environment: inside vehicles and aircraft parked in full tropical sun, and under the hood of motor

job:LAY03 page:33 colour:1

black–text

Soldering 51

vehicles anywhere, ambient temperatures can rise above 120 °C/250 °F (Section 3.3.4). In a warm and humid environment, rosin, left as residue on a board, can hydrolyze and lose its insulating character. 2. Rosin ﬂux residue, being hard and highly insulating, obstructs the contact between ATE test probes and the test pads on the board, and it also tends to gum up the tips of the probes. This problem is more serious with wavesoldered boards, which are fully covered with ﬂux residue, than with reﬂowsoldered boards, where the ﬂux residue from the solder paste is conﬁned to the footprints and their immediate neighbourhood. 3. The residue compromises the adhesion of protective conformal coatings. 4. The interaction between the rosin ﬂux and the substrate during soldering produces complex metallic reaction products, which are not fully soluble in many of the solvent systems employed in cleaning. They form the so-called ‘white residue’, which is the subject of a large volume of investigative work. A detailed account of it has been given by C. Lea.

Activators Because rosin and its syntheic resin alternatives are not very eﬃcient ﬂuxes, so-called activators have to be added.

Activators are polar, mostly high-molecular organic compounds, which may or may not contain a halogen atom. It is important that within the percentage added, the activator is fully soluble in the rosin and does not separate out when the rosin solidiﬁes. This is intended to ensure that after soldering, the polar activator stays safely locked up in the solidiﬁed rosin residue, unable to make it conductive or form local centres of corrosive action. Test procedures which ensure that this requirement is met are laid down in most national ﬂux standards (Section 3.4.6). The activator should of course also be soluble in the ﬂux solvent, which is usually isopropyl alcohol. Finally, if the ﬂux residue must be removed after soldering, the solvent used must be able to cope with the activator as well as with the rosin.

The role of halogen Activators are ﬂuxes in their own right, and by themselves they are more eﬃcient than the rosin or its synthetic resin equivalent. Activators fall into two classes, halogen-containing and halogen-free. Dibasic organic acids, such as adipic or succinic acid, have been found particularly useful as halogen-free activators. The latter vaporizes at 235 °C/455 °F, which makes it attractive as an additive in wavesoldering ﬂuxes. At the normal soldering temperature of 250 °C/480 °F, it forms a cloud of gaseous ﬂux, which surrounds the solderwave and reduces bridging on the exit side. Adipic acid, which melts at 153 °C/307 °F is a useful ﬂux for wavesoldering in a controlled atmosphere (Section 4.6). The choice of acids suitable for rosin activation is wide, and often more than one are added together. Most of the halogenated activators are either chlorides or bromides of nitrogencontaining compounds such as amines. The choice between Cl and Br depends

job:LAY03 page:34 colour:1

black–text

52 Soldering

largely on the idiosyncrasies of a ﬂux manufacturer; often, bromides are considered less corrosive at a given ﬂuxing eﬃciency than chlorides, but there is no concrete proof. There is a general belief in the industry that a halogen-activated rosin ﬂux poses a higher risk of corrosion and of lowered surface insulation resistance (SIR) than a halogen-free one, and some soldering documentations speciﬁcally outlaw the use of halide-activated ﬂuxes. This seems to be largely due to historical reasons.

Some halide-free modern activators are more corrosive by themselves than halidecontaining ones.

3.4.5 Low-solids and no-clean fluxes Wavesoldering applications In common usage, ﬂuxes with a solids content of 2% to 4% are called ‘low-solids’ ﬂuxes. Recently, ultra-low-solids ﬂuxes with about 0.5% solids content have appeared on the market: these are tailored for use in wavesoldering machines which operate in a nitrogen atmosphere with extremely low oxygen content (50 ppm oxygen). Low-solids ﬂuxes are preferably applied to the circuit boards by a sprayﬂuxer. Their behaviour in a foamﬂuxer (Section 4.2.1) is erratic, if not unsatisfactory. The demarcation between low-solids ﬂuxes and no-clean ﬂuxes is blurred. Low-solids ﬂuxes are the response to the ATE test-probe problem faced by wavesoldered boards. The recent advance of alternative test concepts has had no eﬀect on the continuing popularity of low-solids ﬂuxes. The decisive merit of a no-clean ﬂux is the fact that its residue can be left on the board without causing corrosion and without interfering with its functioning under normal circumstances. Its compliance with both these requirements can be tested, the ﬁrst with one of the corrosion tests covered by, for example, the copper-mirror test (ISO 9455–5), the second by a surface insulation-resistance test covered by ISO 9455–17 (see Section 5.2.4). Put crudely, low-solids ﬂuxes are activated rosin ﬂuxes with most or all of the rosin taken out but all of the activator left in. This results in a ﬂux with a total solids content from 5 per cent down to less than 2. The proportion of rosin or its resin substitute in the solids portion of the ﬂux can be well below one-half. Naturally, the only activators suitable for this stratagem are those which are by themselves not corrosive, and which form a thin, dry residue. The above-mentioned class of organic acids is one of the most popular candidates for this role. Initially, the main concern was that the ﬂux residue left on the test pads should be easily penetrated by the ATE test probes, without raising their contact resistance or gumming them up too quickly, but with changing test strategies, that motive has largely disappeared. A minimum of rosin, resin, or a low-volatility additive is necessary to give the ﬂux the required ‘body’ and staying power, so that some of it makes it to the far side of the second solderwave. This is necessary to keep the ‘peel-back’ of the wave in check and prevent it from ﬂying apart in a shower of small droplets, some of which may adhere to the underside of the board in the form of ‘solderballs’, one of the problems of wavesoldering under nitrogen (Section 4.6). Naturally, it can no longer be expected that the rosin in the ﬂux residue will retain the activator safely locked up in solid solution. Therefore, having become the main constituent of the ﬂux and its residue, the activator must be strictly non-

job:LAY03 page:35 colour:1

black–text

Soldering 53

corrosive and non-conductive under the service conditions for which the soldered assembly is intended. Consequently, low-solids ﬂuxes are normally halogen-free. Wavesoldering in a controlled atmosphere is an ideal method for getting the best results from low-solids ﬂuxes. For wavesoldering, the description ‘low-solids ﬂux’ can normally be equated with ‘no-clean ﬂux’. Nevertheless, it is advisable to carry out environmental testing of some soldered sample boards before deciding on a low-solids ﬂux for a given application.

Use in solder paste and solderwire Reﬂowsoldering with a solder paste presents quite a diﬀerent situation. ATE test probes are not the problem they are with wavesoldering, because care is in fact taken to ensure that the solder paste does not invade a neighbouring test pad, so starving the joint of solder. Low-solids ﬂuxes for the sake of just leaving less residue are uninteresting. On the other hand, formulating a paste which really needs no cleaning oﬀers worthwhile rewards: cleaning of densely-packed SMD boards is diﬃcult; boards have to be designed and components must be speciﬁed for cleanability (Section 8.1.2). The task is not an easy one. The ﬂux portion of a paste must have enough ‘body’ to provide the thixotropic properties which hold the solderpowder in suspension and make the paste printable without slump. So as not to cause solderballing, paste squeezed away from a footprint must remain moist and mobile until all the solder has been fetched back into the joint. Without cleaning, stray solderballs become vagrant and liable to cause damage with ﬁne-pitch and ultraﬁne-pitch layouts. Many ‘no-clean’ solder pastes are now on the market. Most of them require reﬂowing in a low-oxygen atmosphere. With all of them, there is very little apparent ﬂux residue left after soldering, but what is important is that whatever there is sits on the pads or leads, and not in the spaces between them. Solderwire with a rosin-free no-clean ﬂux has recently become available. Its inconspicuous residue makes cleaning after corrective soldering unnecessary (see Section 10.4.5).

3.4.6 Watersoluble fluxes If cleaning after soldering is obligatory, however non-corrosive the ﬂux residue may be, it is sensible to choose a ﬂux which can be removed as simply as possible (Section 8.7). The watersoluble ﬂuxes fall in that class. Water, and the recently introduced polar solvents like the modiﬁed alcohols, oﬀer the possibility of a greatly simpliﬁed and environmentally acceptable cleaning technology. Any completely rosin- or resin-free ﬂux would consist of polar substances only, and is consequently soluble in polar solvents like water or any of the alcohols. The choice of such ﬂuxes is large, and again it depends largely on whether the ﬂux is to be used for wavesoldering or for incorporation in a ﬂuxpaste. For wavesoldering, any of the activators discussed previously, in alcoholic solution and with the addition of a longer-chain polar compound such as a glycol to give the ﬂux ‘body’ and staying power in the wave (see Section 3.4.5), will be suitable. The presence of a halide is no requirement, but no disqualiﬁcation either. What matters is that, after soldering, the board must not be wet or sticky.

job:LAY03 page:36 colour:1

black–text

54 Soldering

3.4.7 Solvents used in fluxes Generally, and until recently, isopropyl alcohol (isopropanol) was used almost universally as the solvent in every soldering ﬂux. With some formulations, a portion of a higher-boiling alcohol was added; with others, water of up to 10% or more was added to improve their performance in a foamﬂuxer and reduce the ‘climbthrough’ of the ﬂux from the underside of the circuit board through the holes to the top, where it might interfere with the function of relays or contacts. Those latter ﬂuxes would of course have to be free from rosin. In 1992, isopropanol came under attack from two sides: ﬁrst, isopropanol falls in the class of ‘volatile organic compounds’ (VOCs, Section 8.3.5), which are implicated in the creation of urban and industrial smog. In several American states (e.g. California), the use of VOCs is already severely restricted. Secondly, though the soldering industry has been using ﬂammable isopropanolbased ﬂuxes for decades without any great qualms, observing of course all reasonable precautions, the recent emphasis on environmental aspects of industrial practices, together with stricter regulations concerning the storage of ﬂammable liquids on manufacturing premises, has brought the use of any of the lower alcohols, known as ‘Class I liquids’, under renewed scrutiny as ﬂux solvents in wavesoldering machines. As a result, waterbased wavesoldering ﬂuxes have been introduced to the market. Their ingredients must of course be fully watersoluble, and hence they cannot contain rosin. Secondly, since the heat of evaporation of water is over three times that of isopropanol, and its boiling point is 20 °C/36 °F higher, a waterbased ﬂux must be predried with a more powerful heater and to a higher temperature than an alcoholic one (Section 4.3.1). To assist predrying, these ﬂuxes are applied by sprayﬂuxers, as a very thin coating. Finally, water is heavier and has a higher viscosity than alcohol. Therefore, atomizing a waterbased ﬂux needs more energy than an alcoholic one. Not all ultrasonic atomizers have enough power to cope with a waterbased ﬂux, a factor which must not be forgotten when considering changing the type of ﬂux (see Section 4.2.1).

3.4.8 Flux standards Problems of formulating flux standards The main function of a standard speciﬁcation of an industrial product is to provide a formal framework of requirements which the product has to meet, so that in principle it could form the basis of a contract between the seller and the buyer. With an engineering product, for example a screw, a standard speciﬁcation will consist of set of physical dimensions and permissible tolerances. Compliance with the standard can be veriﬁed by a set of relatively simple measurements. With a chemical product like a solder, a standard speciﬁcation will state the composition of the solder, with permissible tolerances, and limits for a number of impurities. Compliance can be veriﬁed by chemical analysis. Soldering ﬂuxes for use by the electronics industry are also chemical products, but with them the situation is far less simple, for several reasons:

job:LAY03 page:37 colour:1

black–text

Soldering 55

1. The technology of electronic packaging, including soldering, is far from static. Methods and requirements change constantly, often rapidly, and with them the tasks which soldering ﬂuxes have to fulﬁl. 2. A number of ﬂux formulations are patented and are thus the property of the manufacturer; others are closely guarded industrial secrets, being the result of much research and development and company-speciﬁc expertise. 3. Veriﬁcation of the composition of electronic ﬂuxes is largely beyond the scope of most users except the large corporations. The standards institutions of the various industrial nations have chosen several ways out of these diﬃculties. In principle it is possible to frame two sets of requirement for a ﬂux: 1. Set down what a ﬂux must or may contain (for example rosin), and what it must not contain (for example a halide). 2. Set down what a ﬂux must do (for example possess a given minimum ﬂuxing activity), and what it must never do (for example cause corrosion or leakage currents). Starting from these premises, various international committees have been formulating standard speciﬁcations since the early 1990s which are intended to replace national standards existing until then. In Europe, ISO 9454–1 speciﬁcation for soldering ﬂuxes is now valid. However, in the USA, ISO 9454–1 is considered a European document, and J-STD-004 is generally used in industry. Other standards are also being referred to in the States, such as Bellcore TR-NWT-00078, ANSI/ IPC-SF-818, Fed.Spec.QQ-S-571 E, and several MIL Specs. Table 3.11a & b coordinates J-STD-004 classiﬁcations with the old QQ-S-571 E (1986) classiﬁcation of ﬂuxes into the rosin ﬂuxes R, RMA and RA, and the non-rosin ﬂuxes AC.

USA Federal speciﬁcation QQ-S-571 E (1986) This speciﬁcation divides ﬂuxes into four classes: R RMA RA AC

Rosin ﬂux Mildly activated rosin ﬂux Activated rosin or resin ﬂux Non-rosin ﬂux. Includes acids, organic chlorides, inorganic chlorides, etc.

The speciﬁcation names the type of rosin to be used for the ‘R’ ﬂuxes, but does not name the acids or salts contained in AC. For the rosin-based ﬂuxes, the resistivity of a water extract, prepared from the ﬂuxes by a described method, is speciﬁed. The speciﬁcation does not pronounce on the suitability of a given ﬂux for electronic soldering.

job:LAY03 page:38 colour:1

black–text

56 Soldering

Table 3.11 Flux classiﬁcations which are now in force: (a) J-STD-004 Type L0 L1 M0 M1 H0 H1

Former class of ﬂux

% Halide

All R ﬂuxes, some MRA, some ‘no-clean’ low solids ﬂuxes. Most RMA, some RA ﬂuxes. Some RA, some low-solids ‘no-clean’ ﬂuxes. Most RA, some RSA ﬂuxes. Some watersoluble ﬂuxes. Most of the watersoluble ﬂuxes.

0 0.5 0 0.5–2 0 2

(b) ISO 9454–1 Flux type

Flux basis

Flux activation

Flux form

1. Resin

1. Colophony (rosin) 2. Non-colophony (resin) 1. Water soluble 2. Non-water soluble 1. Salts

1. No activator added 2. Halide-activated*

A: Liquid

3. Non-halide activated

C: Paste

2. Organic 3. Inorganic

2. Acids 3. Alkalis

B: Solid

1. With ammonium chloride 2. Without ammonium chloride 1. Phosphoric acid 2. Other acids Amines and/or ammonia

*Other activators may be present. (c) ISO 9454–1: codes for halide levels Category

% halide

Activity

W:

0.01 (non-activated) 0.05 (activated 0.15 1.0 1.0

Low Low Mild Medium High

X: Y: Z:

Example: A halide-activated liquid resin ﬂux containing 1.0% halide would have the code 1.2.2.A.Y.

Military speciﬁcation MIL-F-14256 This speciﬁcation relates to liquid ﬂuxes, which are arranged in two classes: R Rosin, non-activated RMA Rosin, mildly activated These ﬂuids are based on the requirements listed in QQ-S-571E.

job:LAY03 page:39 colour:1

black–text

Soldering 57

For military applications, all ﬂuxes which are activated need to have their residues removed by a suitable cleaning agent. J-STD-004 classiﬁes ﬂuxes according to the nature of their main constituent: RO: natural rosin; RE: synthetic resin; OR: an organic substance; IN: an inorganic substance. A further code (Table 3.11c) indicates the halide level of halide-activated ﬂuxes. It is deﬁned as the weight percentage of halide ions (calculated as chlorine ions) in relation to the solid portion of the ﬂux.

3.4.9 Testing soldering fluxes The prospective user of a soldering ﬂux wants to be assured of two things: 1. Will it work as I expect it to, in my particular manufacturing situation? 2. Will it be safe to use, and not cause corrosion or malfunctioning of my particular product? Industrial (and military) standard speciﬁcations can give the user some guidance in these problems, but will not give a quantitative answer if he wants to know how eﬀectively an individual ﬂux will solder the components he is using to his circuit boards, and whether its residue will cause any damage. The wetting tests described in Section 3.6.8 will answer the ﬁrst question, corrosion tests and the insulation tests described in Section 8.6.3 the second one. The tests listed by the various standard speciﬁcations are designed to decide whether a given ﬂux conforms to their requirements. Most of them are beyond the expertise and the facilities available to the average ﬂux user; they appear to be designed mainly for use by the manufacturer or for arbitration purposes.

Soldering efficiency and the spreading test If the eﬃciency of a ﬂux needs to be measured, the ‘spreading test’ is an old established, simple method. A pellet of 60% tin solder, mostly weighing 0.2 g, is placed on a coupon of copper sheet, which has been cleaned by a prescribed method. A measured quantity of the ﬂux under test is applied to it, and the coupon is heated to 235 °C/455 °F. This can be done conveniently by ﬂoating the coupon on a thermostatically controlled small solderbath. The solder melts and after a speciﬁed time the coupon is lifted oﬀ, allowed to cool, and the mean diameter of the area covered by the solder is measured and compared with the value laid down in the speciﬁcation, for instance ISO/CD 9455–10. Other speciﬁcaions do not indicate the area of spread, but simply demand a sharp, ‘feathered’ wetting angle. The wetting balance (see Section 3.6.8, Figures 3.23 and 3.24) has now been accepted as a method for quantifying the wetting power of a ﬂux (ISO 9455–16). A copper specimen is subjected to a speciﬁed surface treatment to give it a standard and reproducible degree of wettability by molten solder. It is then covered with the ﬂux under test, dried, and immersed in the solderbath of the wetting balance. The

job:LAY03 page:40 colour:1

black–text

58 Soldering

eﬃciency of the ﬂux is derived from the resulting wetting curve. The solderbath contains a 63% Sn solder (for instance to JSTD-006, Sn63Pb37C), held at a temperature of 250 °C/480 °F.

Corrosive action The test for corrosive action is again conﬁned to observing what a ﬂux will do to copper during soldering, or what the residue which is left on the copper will do in a moist atmosphere. In ISO 9455–13 ﬂux residue, left on a copper coupon after having melted a small amount of 60% tin solder together with the ﬂux under test, is stored in a humid atmosphere, at 40 °C/645 °F and 91% to 95% relative humidity, for three days. Corrosion is deemed to have occurred if the ﬂux residue has changed colour, or if white spots have appeared in it. In ISO 9455–5, a drop of the ﬂux to be tested is placed on a ﬂat glass slide, on to which a thin ﬁlm of copper, with a thickness of 0.05 m/0.002 mil (500 angstrom) has been deposited by an evaporation technique, a so-called ‘copper mirror’. Copper mirror slides are commercially available. The slide with the drop of ﬂux on it is kept in a humidity chamber at 23 °C/73 °F and 50% relative humidity for 24 hours, and then examined. If the copper mirror has disappeared underneath the ﬂux, it is deemed to have failed the test. A ﬂux which passes the copper mirror test is an ‘L-type’ (low activity) ﬂux, which group comprises all R-type ﬂuxes, most RMA, and some R. If some of the copper mirror has gone, it is an ‘M-type’ (medium activity) ﬂux, which may still be an RMA, but is mostly RA and sometimes a watersoluble or a synthetic activated ﬂux. If the copper mirror has disappeared completely, the ﬂux is an ‘H-type’ (high activity). Watersoluble and synthetic activated ﬂuxes fall in that group. An important aspect of ﬂux classiﬁcation relates to the surface–insulation–resistance (SIR) properties of a ﬂux (ISO 9455–17, not yet issued).

Halide content Determination by analysis If a halide-free ﬂux is speciﬁed, some standards give a detailed analytical procedure for quantitatively determining the halide content of the ﬂux. If this exceeds 0.05% by weight of the rosin content of the ﬂux, calculated as Cl, the ﬂux does not conform to, for example, a BS 5625 halide-free ﬂux. If it exceeds 0.5% calculated Cl on the solids content of the ﬂux, it does not conform to an ANSI/J-STD-004 ﬂux of type LI. Silver-chromate test This is a qualitative yes/no test, and does not indicate a speciﬁc halide percentage. Silver chromate (AgCrO ) is a brick-red substance, which turns white or yellow in the presence of a halide. Silver-chromate impregnated testpaper is commercially available. If such a piece of paper turns white or yellow when a drop of the ﬂux under test is placed on it, halide is deemed to be present, and the ﬂux cannot be

job:LAY03 page:41 colour:1

black–text

Soldering 59

classed as ‘L0’ or ‘L1’ to J-STD-004. There is a problem, though: certain acids and amines (which may well be free of halide) are also capable of causing the colour of silver-chromate paper to change. Because this test is relatively insensitive, a ﬂux with up to 0.05% halide will still pass it as ‘halide-free’. Beilstein test This test, which is mentioned in ANSI/J-STD-004, is more sensitive than the silver-chromate test, but it is a qualitative test and gives no indication of the actual quantity of halogen present. Its drawback is that it will also respond to any non-ionic halogen in a halogenated solvent, should any such be contained in the ﬂux. The Beilstein test detects the presence of halogen in an organic compound. It requires a small piece of ﬁne copperwire gauze, which is heated in an oxidizing ﬂame (e.g. the blue part of a bunsen-burner ﬂame) until it ceases to turn the ﬂame green. It is withdrawn, allowed to cool, and a small amount of the ﬂux under test is placed on it. It is then put back into the ﬂame. If the ﬂame turns blue-green, the ﬂux contains traces of halide. If not, it is deemed to be halide-free. The Beilstein eﬀect depends on the formation of a volatile copper halide. (F. K. Beilstein, RussoGerman chemist, 1838–1906.)

Solubility of flux residues The average ﬂux user needs guidance on how to assess the ease with which the residue of the ﬂux he is using, or wants to use, responds to the cleaning method he is using or intends to use. The international standard ISO 9455–11: 1991 (E) is relevant to this problem. This standard describes a method of heating a sample of the ﬂux on a dish-shaped piece of brass sheet up to 300 °C/570 °F for a given time, placing the sample in a humidity chamber for 24 hours and then immersing it in the solvent which is to be used for cleaning. The presence of any residual ﬂux left after cleaning is indicated by the ability of the cleaned test specimen to form an electrolytic cell.

Surface insulation resistance (SIR) of the flux residue By deﬁnition, the residue from a ‘no-clean’ ﬂux remains on the board. Obviously, not only must it cause no corrosion, but its presence must not interfere with the functioning of the circuitry by lowering the surface insulation resistance (SIR) of the board between adjacent conductors: a leakage current of 10\ A between neighbouring IOs of a high-impedance microprocessor is enough to cause it to malfunction (see Section 8.1.1). A number of tests to measure the SIR after various soldering and cleaning procedures have been devised over the years. They are described in Section 8.6.3. J-STD-004 includes a method for testing the ﬂux residue for its moisture- and surface-insulation resistance. The relevant ISO working group is expected to complete its deliberations on the same subject in about three years’ time (information from BSI, London, April 1997).

job:LAY03 page:42 colour:1

black–text

60 Soldering

Tackiness of the flux residue Finally, the residue from a no-clean ﬂux must be dry and not sticky or ‘tacky’ under normal temperature and moisture conditions. Tackiness is tested by applying powdered chalk to a ﬂuxed coupon which has undergone a speciﬁed temperature regime. If the powder can be removed with a soft brush, the ﬂux has passed the test.

3.5 Soldering heat Conventional soldered joints are made with molten solder. Hence, the soldering temperature must always be at least above the melting point of the solder, i.e. above 183 °C/361 °F. The immediate environment of the joint, and sometimes the whole assembly, must be brought up to the soldering temperature too. The exact temperature needed depends entirely on the soldering method used. It is rarely less than 215 °C/420 °F and is often much higher.

3.5.1 Heat requirements and heat flow Heat is a form of energy, which is usually measured in one of the following ways. One calorie (1 cal) raises the temperature of one gram of water by 1 K (which is the same temperature diﬀerence as 1 °C, Section 5.4.2). One calorie equals 4.187 joule, or in units which are meaningful in the context of soldering, 4.18 watt.seconds (W.sec). Table 3.12 indicates the amounts of heat required in some common soldering situations. In this context, it is useful to know the heat conductivity of the various materials involved, so as to be able to gauge the speed with which the heat input spreads within an assembly (Table 3.13). The ﬁgures given in Tables 3.12 and 3.13 are worth studying. Table 3.12 shows that organic substances like FR4 have a much higher speciﬁc heat than metals. This has an important bearing on most soldering situations. The greater part of the soldering heat expended in making a joint is not used to heat the metallic joint partners, but to heat the FR4 epoxy board on which the copper laminate sits. Hence the need to preheat the boards before they pass through the solderwave (Section 4.3), but also the beneﬁt of preheating the circuit board, at least locally, when soldering single multilead components (Section 5.7), or before carrying out repair work, i.e. desoldering and resoldering single components (Section 10.3). The list of heat conductivities is equally illuminating. The heat conductivity of epoxy is two orders of magnitude lower than that of the ceramic substrate of a hybrid assembly. Hence the need for taking the thermal management of SMDs, which are mounted on an epoxy board, much more seriously than that of hybrid constructions, which were initially the beginnings of SMD technology. The ﬁgures also show how even the narrowest air gap prevents the ﬂow of heat between two hot bodies. Hence the need to have a drop of molten solder on the tip of a soldering iron or thermode, or at least some ﬂux on the joint to bridge that gap (Section 5.7).

job:LAY03 page:43 colour:1

black–text

Soldering 61

Table 3.12 Heat required to raise the temperature of a substance from 20 °C/68 °F to a soldering heat of 250 °C/482 °F 1 g copper 1 g solder 1 g FR4 A soldered joint (volume 1 cub. mm) A circuit board 23.3 cm ; 16 cm 9.2 in ; 6.3 in (‘Europa’ format) 1.2 mm/47 mil thick

88 watt. sec 102 watt. sec (including heat of melting) 338 watt. sec 0.7 watt. sec 27 kw sec

Table 3.13 Some heat conductivities in watt/cm °C Copper Aluminium Brass Steel Solder Ceramic (alumina) FR4, rosin Air

3.9 2.2 1.2 0.5 0.5 0.25 0.002 0.000 000 002

3.5.2 Heating options Equilibrium and non-equilibrium situations The basic aim of every heating process is the transfer of heat from a heat source to the heat recipient, i.e. from a hot body to a colder one via a heat transfer medium. There are two basic heating situations: equilibrium and non-equilibrium systems. In equilibrium situations, the temperature of the heat source is the same as the soldering temperature which must be reached. The time within which the joint reaches its soldering temperature depends on the eﬃciency of the thermal coupling between source and joint. The joint cannot be overheated, i.e. it cannot get too hot, but it can be ‘overcooked’, i.e. it can be heated for too long a time. The latter carries the risk of excessive growth of the brittle intermetallic compound, and thus an unsatisfactory joint structure and the risk of a shortened joint life-expectancy. In non-equilibrium situations, the temperature of the heat source is higher, often very much so, than the soldering temperature itself. Whether the correct soldering temperature is reached or exceeded is a matter of timing the heat exposure. The higher the temperature of the heat source, the steeper is the temperature rise of the solder joint, and the more critical becomes the precise control of the duration of its heat exposure. Overheating may not only endanger the joint and its properties, but in severe cases it can damage the assembly itself (Figure 3.14). Wavesoldering, vapourphase soldering, hot air or gas convection soldering, impulse soldering and handsoldering with a soldering iron present equilibrium

job:LAY03 page:44 colour:1

black–text

62 Soldering

Figure 3.14 Equilibrium and non-equilibrium heating situations

heating conditions. Infrared soldering, laser soldering and ﬂame soldering are non-equilibrium systems.

Heat sources A thermostatically controlled electrical resistance heater is the most common primary heat source. This transmits its heat to the heat-transfer medium, whether it

job:LAY03 page:45 colour:1

black–text

Soldering 63

be the drop of solder on a soldering iron or the solderwave in a wavesoldering machine. The reader may be amused to learn, though, that the ﬁrst few wavesoldering machines were gas heated. Small, pointed butane- or propane-gas ﬂames are used for soldering individual joints in awkward locations. Equipment using a very hot, needle-shaped hydrogen– oxygen ﬂame is also commercially available. These ﬂames, which represent extreme cases of non-equilibrium heating, may be hand-held, but more often are manipulated by programmed robots, and then of course equipped with controls which prevent overheating. Laser beams present the ultimate in non-equilibrium heating. To speak of the ‘temperature’ of a laser source makes no real sense; what matters is the extreme energy density of the spot of laser light, which impinges on the joint surface, and which may reach 10 kw per square millimetre (Section 5.6). A very precise energy dosage is of the essence, to avoid destruction of the joint and burning a hole into the substrate. Exposure times are measured in milliseconds.

Heat transfer mechanisms The soldering heat can be transmitted from the heat source to the joint by any one of three basic mechanisms: conduction, convection and radiation. Conduction relies on a direct physical contact between a hot solid body or liquid and the surface of one of the joint members. The eﬃciency of heat transfer depends critically on the close ﬁt between the heating and the heated surface. Any airgaps between them fatally aﬀect the heat transfer. Molten solder is the best heat-transfer medium available: being a liquid, it conforms perfectly to whatever surface it has to heat. This is the virtue of the solderwave, as well as of the drop of molten solder on the tip of a soldering iron, which will come in very useful with repair soldering (Sections 10.2 and 10.3). Strictly speaking, convection comes into the heat-transfer mechanism of wavesoldering as well, because the solderwave consists of a body of moving solder. By contrast, dipsoldering in a stationary bath relies on heat transfer by conduction only, like a soldering iron.

3.6 Solderability 3.6.1 Wetting and dewetting Wetting The term ‘wetting’ describes the behaviour of a liquid towards a solid surface with which it comes into contact. In our case, we are naturally concerned with the way the molten solder behaves toward the substrate. Though everyone knows instinctively what is meant by ‘wetting’, it will be useful to examine in detail what is involved in wetting in the context of soldering, and how it can be quantiﬁed and measured. Section 3.3.1 described the soldered joint as the result of a surface reaction between molten solder and a solid metallic substrate, and it was explained why an intimate contact between the two is a precondition for the joint to form. We must now amplify this by saying that wetting is the precondition for this intimate contact.

job:LAY03 page:46 colour:1

black–text

64 Soldering

Wetting is not a ‘yes or no’ situation; there is a scale of wetting quality between total non-wetting and complete wetting. The yardstick for measuring the quality of wetting is the ‘wetting angle’, which is formed between the surface of the solid and that of the liquid along the line where they meet (Fig. 3.13 and 3.15). A wetting angle of 180° is a sign of total non-wetting, while an angle towards zero denotes complete wetting. In the context of soldering, a wetting angle of less than 60–75° is normally, but arbitrarily, considered acceptable; anything up to 90° is doubtful, and beyond 90° deﬁnitely bad. Whether and when ‘bad’ can or should be equated with ‘non-acceptable’ will be discussed in Section 9.3. The wetting or contact angle between the molten solder and the substrate is the result of the opposing forces of the surface tension of the solder, which tries to pull it together into a globule (somewhat ﬂattened by gravity), and the interfacial tension between the solder and the substrate, which tries to pull the solder across its surface, so that as much of the solder as possible can come in contact and react with it. The wetting angle can be interpreted in terms of the three surface energies involved: that of the molten solder, of the solid, and of the interface between the two. Klein Wassink provides a detailed discussion of this aspect. In practical terms, the signiﬁcance of wetting can be stated very simply. Good wetting helps the solder to get to all the places where it ought to be; doubtful and bad wetting prevent the solder from entering a joint.

Dewetting ‘Dewetting’ is not the same as ‘non-wetting’. As the term implies, in a dewetting situation the molten solder did get to where it ought to be, but it does not stay there. Instead, it pulls back and forms separate islands of solder, with areas of exposed intermetallic compound in between. This situation can occur in dip-tinning, e.g. in the hot-air levelling process for circuit boards (HAL), or in wavesoldering, but only rarely in reﬂowsoldering. Dewetting is caused by local, untinnable spots of surface contamination, such as oxide particles, or surface dirt like traces of silicones or ﬁngerprints. Non-metallic inclusions in galvanic coatings, for instance embedded colloids caused by unsuitable or badly controlled plating baths for copper, nickel or gold, can cause dewetting too. Surfaces which dewet are at ﬁrst completely covered with molten solder, which

Figure 3.15 The wetting angle

job:LAY03 page:47 colour:1

black–text

Soldering 65

bridges the untinnable spots. Before it can solidify, its surface tension pulls the still liquid soldercoating apart, and away from the discontinuities (Figure 3.16).

3.6.2 Capillarity and its effects A capillary is a very thin hole or a narrow gap (from capillus, Latin for ‘hair’). If the surfaces of the hole or gap are wettable, interfacial tension quickly pulls the liquid solder into it with considerable force, often against the force of gravity. On the other hand, if the inner walls of the gap are untinnable, the surface tension of the solder prevents it from entering it. If one of the members forming the gap is movable, like the gullwing legs of an SMD during reﬂowsoldering, the interfacial tension pulls the walls of the gap towards one another, which means it pulls the ﬂat end of the leg into the middle of its footprint. If, on the other hand, one or both are untinnable, the surface tension of the solder pushes them apart (Figure 3.17). The consequences of capillarity for soldering are important: 1. If the joint surfaces are wettable, capillarity pulls the solder into the joint, against the force of gravity if necessary. If they wet badly or not at all, the solder cannot get into the joint, even if gravity would tend to pull it into the gap. 2. If one of the joint members is mobile, as is the case in reﬂowsoldering, and if both are wettable, interfacial and surface tension pull the joint members together. If one of them is unwettable, they are pushed apart. In reﬂowsoldering, capillary forces are the cause for the self-alignment of BGAs and small SMDs, but also for ‘tombstoning’ and the ﬂoating of chips or melfs on badly designed layout patterns (Sections 6.4.2 and 11.2.2; also Figure 3.18).

3.6.3 Capillarity and joint configuration Capillary joints and open joints The way in which the solder ﬂows into a wettable joint depends on the soldering method and on the shape of the joint itself. Basically, there are two types of joint: ‘capillary joints’ and ‘open joints’ (Figure 3.19). With a capillary joint, or lap joint, two ﬂat and essentially parallel surfaces face one another, and the joint forms a

Figure 3.16 Dewetting and non-wetting

job:LAY03 page:48 colour:1

black–text

66 Soldering

Figure 3.17

two-dimensional gap. Tubular joints, like through-plated holes, are a special form of capillary joint, where the gap is cylindrical. With an open joint, or butt joint, one or both of the joint members are not ﬂat, and they touch one another along a line or just in one spot. With capillary joints, the escape route for the air and ﬂux in the joint can get blocked if the molten solder closes all the edges around the joint gap before all the air and ﬂux inside the gap have been pushed out by an orderly, frontal advance of molten solder into the gap from one (or at most two) sides only. With an open joint, there is no such problem: from whichever direction the solder enters an open joint, the escape routes for air and ﬂux cannot be blocked. With wavesoldering, all capillary joints, ﬂat and tubular, ﬁll from one side only. Both types will normally be sound, especially the latter, unless air or water vapour escape from the walls into the hole after the solder has entered it (blowholing), which is a matter dealt with in Sections 9.5.3 and 11.2.2.

job:LAY03 page:49 colour:1

black–text

Soldering 67

Figure 3.18 The effects of capillarity in reﬂowsoldering. (a) Self-alignment of components; (b) tombstoning

Figure 3.19 (a) Capillary joints and (b) open joints

job:LAY03 page:50 colour:1

black–text

68 Soldering

The penetrating speed of molten solder into a ﬂat capillary gap between two copper surfaces, 0.09 mm/3.5 mil apart, has been measured for various solders and at various temperatures by McKeown (see Reference 2). At 243 °C/470 °F, using a 63% tin solder and a concentrated zinc–ammonium chloride ﬂux, McKeown measured a penetration speed of 3.5 sec over a gap length of 10 cm/4 in, which equals about 2 m/6 ft per minute, the average travelling speed of a circuit board across a solderwave. When reﬂowsoldering a capillary joint with solder paste, solder and a partially volatile ﬂux are already in the gap before soldering starts, and entrapment of gas and ﬂux in the ﬂat joint is almost impossible to avoid. The same is true for a reﬂowed capillary joint, where solid solder is preplaced on one of the joint members, because the molten solder tends to advance more quickly along the edges of a joint than in the middle (Figure 3.20). Only with impulse soldering, where the joint members are pressed together during soldering, are joints less likely to be porous. Internal porosity in a capillary joint is almost undetectable by external inspection and only shows up under X-ray examination (Section 9.4.3). However, whether a porous capillary joint, even if it contains up to 50% voids by volume, is really inferior to a completely solid one is very debatable; this will be dealt with in Section 9.3. Open joints, as which one can count not only the end-joints of melfs and chips, but also the joints of all SOs, because their horizontal legs are short and the joint gap is wedge-shaped, do not trap air. The few airbubbles found in such joints, if they are sectioned, are no cause for worry. On the contrary, they are more likely to arrest incipient internal cracks rather than starting them.

Open joints versus capillary joints Open joints have several advantages over capillary joints in both wavesoldering and reﬂowsoldering. The solder gets into them more easily, and they are much more inspectable by optical means, unless they are partially or completely hidden under the component housing like the J-legs of a PLCC, or underneath a BGA or a ﬂip-chip. The presence of solder in the joint and its wetting angle with the joint

Figure 3.20 How molten solder ﬁlls a capillary joint

job:LAY03 page:51 colour:1

black–text

Soldering 69

members are both readily veriﬁed. With capillary joints, the only external evidence for adequate wetting and penetration is the continuity and the wetting angle of its circumferential solder ﬁllet. Thus, a good case can be made for avoiding parallel capillary gaps and for designing wedge-shaped, open ones instead, unless the joints are to be soldered by impulse soldering under the mechanical pressure of a thermode. Here too, it may be worth while considering giving the faces of the thermodes a slant, thus making the impulse-soldered joints wedge-shaped, with any trapped ﬂux and vapour pushed towards one end.

3.6.4 The importance of solderability The ease with which molten solder wets a metallic surface is called ‘solderability’. It has a decisive inﬂuence on the achievement of both soldering success and soldering quality, and thus on the fault rate of a soldering operation and its cost eﬃciency. It is therefore important to choose joint surfaces which are inherently solderable and to make sure that they remain in a solderable condition. To this end, one must be able to measure, or at least to assess, their solderability.

The inherent solderability of a metal The solderability of a metal depends on two factors: ﬁrst, on the nature and the chemical stability of the oxide layer on its surface; secondly, on the chemical aﬃnity between the metal and the solder, in other words on the readiness of the solder to form a diﬀusion zone at its interface with the substrate. The ﬁrst factor determines whether a mild ﬂux will do, or whether an active, highly polar and corrosive ﬂux is needed to remove the oxide. The chemical aﬃnity is based on the amount of energy set free by the reaction between the tin, more rarely by the lead in the solder, and the substrate. The inherent solderability of a number of common metals is shown in Table 3.14. This listing assumes clean, though not oxide-free, surfaces. Solderability is governed by several factors, among them the following: 1. The ease with which surface oxides or sulﬁdes are dissolved by a ﬂux. 2. The surface energy of the metal surface (which means its readiness to react with whatever comes in contact with it), metals with low surface energies being more diﬃcult to solder. 3. The metallurgical aﬃnity between the metal to be soldered and the constituents of the solder. For example, lead is more compatible with nickel than tin, therefore lead-rich solders are better on nickel than pure tin or a eutectic tin–lead solder.

3.6.5 Oxide layers The chemical stability of the various metal oxides diﬀers widely. Gold and platinum do not form oxides under normal circumstances, so their chemical behaviour is

job:LAY03 page:52 colour:1

black–text

70 Soldering

Table 3.14 The solderability of common metals, listed in order of descending solderability A. Readily solderable with mild ﬂuxes (R and RMA) Gold and its alloys Tin–lead solder Tin B.

Solderable with mild ﬂuxes (RMA) Copper Silver Copper + 2% iron Silver/palladium (as thick-ﬁlm on chips and melfs) Gold/platinum (as thick-ﬁlm on LCCCs)

C. Solderable with activated ﬂuxes (RA) Brass Nickel Cadmium D. Solderable with active ﬂuxes (OA etc.) Zinc Tin/bronze Nickel/copper alloys Nickel/iron alloys (Alloy 42) Nickel/iron/cobalt alloys (Kovar) Mild steel Alloy steels Beryllium bronze E.

Only solderable with special ﬂuxes Aluminium bronze (ﬂuxes based on phosphoric acid) Stainless steel (ditto) Aluminium and its alloys (ﬂuxes containing zinc compounds) Cast iron (not solderable but tinnable with ﬂuxes consisting of fused chlorides)

F.

Unsolderable Chromium Silicon Titanium Manganese

irrelevant. Silver does not oxidize at room temperature, but ozone, an ingredient of urban smog, attacks and blackens it. It readily reacts with sulfur which is always present in our normal industrial atmosphere. The familiar brown tarnish of silver sulﬁde which results from this is resistant to mild ﬂuxes, which on the other hand deal readily with copper oxide and zinc oxide. Iron oxide is more diﬃcult, and cast iron, because of the non-metallic graphite particles on its surface, is untinnable and unsolderable by the methods admissible in electronic soldering. Chromium and its alloys owe their resistance against tarnish to a transparent, but stable and tough, oxide layer which makes them almost unsolderable. The oxide layer on aluminium

job:LAY03 page:53 colour:1

black–text

Soldering 71

and its alloys is equally transparent, but can be dealt with by special, though corrosive, ﬂuxes. On the other hand, surface oxides and sulﬁdes of copper are readily removed, even by mild ﬂuxes. A particularly obnoxious and almost unsolderable oxide layer forms if the intermetallic compound , which is the top layer of the diﬀusion zone between a copper surface and the molten solder (see Section 3.3.2, Figure 3.7), is exposed to air. This can happen when desoldering a faulty joint or component, if the exposed footprint is wiped clean of the solder remaining on it (Section 10.4.2). How to guard against this mishap, and what to do if it has happened, is discussed in the relevant section.

3.6.6 Solderability-enhancing surface coatings Uncoated soldering surfaces, like bare copper footprints or Alloy-42 gullwings, have become rare. Most surfaces intended to be soldered are coated with tin or a tin–lead alloy to improve and preserve their solderability. Silver or gold are also used sometimes, but their value as solderability preservers is doubtful. Silver is liable to tarnish, and the presence of gold in a soldered joint can lead to embrittlement if there is too much of it (see below).

Tin and tin–lead coatings It is true to say that nothing is more solderable than solder itself. It is even more solderable than pure tin, because the lead in the solder makes it more resistant to atmospheric moisture and to corrosive environments. For that reason, a coating with a 50% or even a 40% tin solder is often preferred to one with 60% tin. As soon as the molten solder encounters a tin or tin–lead coating, it melts and dissolves it. Provided the coating is thick enough, above about 25 m/0.1 mil, the molten solder will lift oﬀ any surface contamination which might sit on the surface of the coating, and ﬂow underneath it. This is called the ‘lift-oﬀ eﬀect’ (Figure 3.21). Galvanically deposited tin–lead coatings have their problems. They consist of discrete particles of tin and lead, and are therefore porous. All the damaging ingredients of the atmosphere, especially an industrial one, can and will slowly

Figure 3.21 The lift-off effect

job:LAY03 page:54 colour:1

black–text

72 Soldering

penetrate between the particles down to the base metal. The tin–lead deposit dissolves on contact with the molten solder, which is then confronted with the bare base metal, which was originally quite clean of course, otherwise the galvanic deposit would not have adhered to it. But after a period of unsuitable storage, contamination might have penetrated down to it, and its solderability will have suﬀered, if not disappeared. The remedy is to fuse, i.e. to reﬂow, galvanic tin or tin–lead deposits in the presence of a ﬂux cover, and turn them into a coherent layer of tin or tin–lead solder (Section 6.3). As a bonus, this creates a layer of intermetallic compound between the coating and the base metal. If the substrate base is not readily solderable with an RMA ﬂux (like iron or an iron–nickel alloy), a thin galvanic coating of nickel, possibly with a topcoat of copper, must be provided between the base metal and the tin or solder topcoat. Nickel dissolves only slowly in molten solder. While the topcoat disappears immediately in the molten solder once soldering starts, the nickel survives long enough to protect the possibly badly solderable base underneath. With a pre-fused coating, the solder will ﬁnd a ready-made intermetallic layer already in place when soldering starts. The alternative to a fused galvanic tin–lead coating is one produced by hot tinning, by one of the processes of roller-tinning, immersion tinning or the HAL hot-air-levelling process (Section 6.3.1).

Silver coatings Once popular, silver is now used less frequently, for several reasons. One is its low resistance to unsuitable storage conditions, as described above. Another is the danger of migration of silver between neighbouring conductors under the inﬂuence of an electrical DC potential between them. This leads to the formation of ﬁbrous dendrites, which cause short circuits.

Silver dissolves relatively quickly in molten solder. If it has to serve as a solderable coating on an otherwise unsolderable substrate, measures which are described below must be taken in order to prevent it from disappearing before soldering is completed.

Gold coatings Gold as such is superbly solderable, with excellent storage properties. In spite of this, it is rarely used because it is associated with several problems, apart from its cost. Galvanic gold deposits, mostly 1 m/0.04 mil thick, can be almost unsolderable if they were produced by an unsuitable plating technique. Shiny gold deposits, such as are used in jewellery, contain colloid additions and fall into that class. Gold coatings thinner than 1 m/0.04 mil are liable to be porous and soon become unsolderable. Gold rapidly dissolves in molten solder and with 3% Au present in a joint, large, brittle ﬂakes of the intermetallic compound AuSn form in the joint gap when the solder solidiﬁes. This situation can easily arise in a reﬂowsoldered joint.

For this reason, gold-coated joint surfaces should only be considered if there is a

job:LAY03 page:55 colour:1

black–text

Soldering 73

compelling technical reason for them, or if the customer, often a military one, insists. The rule, established in the seventies by the European Space Agency (ESO), that the thickness of any gold deposit on a solderable surface should bear a relation to the width of the joint gap seems to have been forgotten, since the outerlead bonding surfaces of TABs, which are meant to be soldered, are occasionally goldplated (see Reference 15).

3.6.7 Leaching effect of molten solder The rate at which a substrate dissolves in the molten solder is called the leaching rate, and it diﬀers from metal to metal. It depends on the rate at which substrate and solder react with one another, on the solubility of the reaction products in the solder, and of course on the soldering temperature. Table 3.15 lists the leaching rates of some substrates, in descending order. The ﬁgures show that silver disappears in the molten solder ten times and gold up to thirty times as fast as copper, and that the leaching rate rises quickly with the soldering temperature. The leaching eﬀect can have serious consequences, for instance if the thick-ﬁlm solderable metallized surfaces on chips, melfs and the (now obsolescent) LCCCs disappear, making them unsolderable. There are two ways of reducing a high leaching rate: 1. An alloying addition. About one per cent of indium added to the solder slows down the solution of Au in the solder. The 1.65% to 2% of Ag added to electronic solders (Section 3.2.2) does the same for a silver substrate, but this eﬀect is small. 2. Modifying the substrate. An addition of up to 35% platinum to the thick-ﬁlm gold on LCCCs signiﬁcantly slows down the leaching rate. Up to 20% palladium does the same for thick-ﬁlm Ag on resistors and condensers. Cheaper and more eﬀective, however, is a galvanically applied, leach-resistant nickel layer, topped with a tin or solder coating for optimal solderability. The leach resistance of components can be tested by the immersion solderability test, described in the following section. Table 3.15 Leaching rates of some substrates

Substrate

Leaching rate in 60% Sn/40% Pb solder (m/sec) at 215 °C/420 °F at 250 °C/480 °F

Au Ag Cu Pd Ni, Pt

1.7 0.75 0.075 0.025 0.01

5.25 1.6 0.15 0.075 0.01

job:LAY03 page:56 colour:1

black–text

74 Soldering

3.6.8 Measuring solderability The solderability of a surface is based on the speed and reliability with which it is wetted by the molten solder using a given ﬂux. Naturally, the milder the ﬂux which one wants to or must use, the higher must be the solderability of all the surfaces involved. Solderability is one of the most important parameters in all soldering processes, especially the mechanized and automated ones which are used in mass soldering. The soldering success, and with it the reject rate and the economics of the whole operation, depends on a consistently good solderability of all footprints, lands, throughplated holes, and component wires, leads, and sintered surfaces. It is therefore essential to have a meaningful and reproducible method for measuring it. In the age of handsoldering, it was mainly the ﬂux vendors who measured solderability in order to assess the ability of their activated ﬂuxes to cope with the often indiﬀerent solderability of component wires and soldering lands. With the advent of the mechanized soldering of large numbers of joints, where soldering times must be as short as possible, and with no-clean soldering, where ﬂuxes should be as mild as possible, the emphasis shifted to the soldering surfaces involved in the process: verifying and monitoring their optimal and consistent solderability became of paramount importance.

Uses of solderability measurement Solderability measurement has several uses. The main one is the assessment of the solderability of a substrate, using a ﬂux of known and standard eﬃciency. The other one is the assessment of the eﬃciency of a ﬂux, using a substrate of standard and reproducible solderability. This latter requirement is not an easy one to fulﬁl and it has engaged the attention of ﬂux manufacturers and drafting committees of standard speciﬁcations for quite some time (Section 3.4.7). Comparing the eﬃciency of an alternative ﬂux with that of a ﬂux with a proven performance, using components of known and consistent solderability for reference, is a simpler proposition, and is frequently practised in the industry.

Surfaces which need testing Circuit boards Given the present state of the art, the solderability of almost all commercially available circuit boards, that is their lands and footprints, can be assumed to be good, unless they are bare copper. In that case, a simple dipping test, which is described later, will verify solderability. With HAL pretinned boards and reﬂowed galvanic coatings, smooth and fully tinned footprints are a safe indicator of perfect solderability. Any defects in this respect can be assumed to have been spotted by the quality control of a competent board manufacturer. Component leads and metallized surfaces The solderability of components is not necessarily visually obvious. Only with Ag/Pd sintered thick-ﬁlm faces on melfs and chips, a dark grey or brown tarnish

job:LAY03 page:57 colour:1

black–text

Soldering 75

means that sulﬁde has formed on them because of unsuitable storage and that they have become unsolderable. Should that have happened with a batch of loose, not belted, components, they can be saved by a short immersion in a photographic ﬁxing bath (known as ‘hypo’), or its equivalent, a 10% sodium thiosulfate solution in water, followed by a rinse ﬁrst in de-ionized water, then in clean isopropanol, and drying oﬀ in air. Hypo is an eﬃcient solvent for silver compounds, including the brown sulﬁde.

Wetting tests Observing the solder meniscus The contour of the surface of the molten solder along the line where it touches an immersed metallic body is called the ‘meniscus’. The shape of the meniscus is an indicator of whether and how well the solder wets the metal (Figure 3.22). For a visual check of whether all is well with a doubtful leadwire or component, looking at the meniscus is a quick, simple test. The component lead or wire is dipped in an MRA ﬂux, conveniently the one which is used in production, allowed to dry for a short while, and dipped in a small bath of 63% Sn solder held at 250 °C/480 °F (it is useful to have such a bath handy in the quality control or production department; see below). The meniscus formed by the solder against the immersed body is observed visually. Opto-electronic equipment for measuring the deﬂection of a beam of light focused on the meniscus has been described.

The wetting balance The wetting balance has become the standard instrument for measuring the solderability of a metal surface, using a ﬂux of standardized ﬂuxing power, or the ﬂuxing eﬃciency of a ﬂux, using a copper specimen with a surface of standardized solderability, coated with the ﬂux under test (see Section 3.4.9). By now, it has reached a

Figure 3.22 The solder meniscus and its assessment

job:LAY03 page:58 colour:1

black–text

76 Soldering

high degree of technical perfection and is capable of measuring, recording and evaluating the wetting behaviour of almost any metallic surface involved in soldering. This includes the leads of all types of SMDs and the solderable endfaces of melfs and chips. Several makes of wetting balance are commercially available. Speciﬁed values derived from a wetting curve, produced with a ﬂux under test, are given in ISO 9455–16. In principle, the test procedure is as follows. The lead, or surface to be tested, is ﬂuxed with a standard RMA ﬂux and brieﬂy dried. The test specimen is then suspended from a sensitive balance or sensor, and immersed in an oxide-free surface of molten solder, mostly by raising a small, thermostatically controlled solder bath upwards against the suspended specimen (Figure 3.23), at a controlled speed. The sensor measures the vertical force acting on the specimen. A system of microprocessors plots this force during the test, and evaluates, prints and stores the result. The graph of the force measured by the sensor is known as the wetting curve (Figure 3.24). It is convenient to disregard the weight of the specimen itself, as well as its buoyancy in the molten solder when fully immersed, which of course equals the weight of the solder it displaces on full immersion. What is left is a curve which ﬁrst dips downwards, showing a negative weight. This is the eﬀect of the negative meniscus, which lasts until the specimen is warm enough to be wetted by the solder and for the ﬂux to begin its work. The curve then begins to climb at a rate which is governed by the eﬃciency with which the ﬂux cleans the surface of the specimen, and thus the speed at which the solder meniscus climbs upwards. The meniscus stops climbing, and the wetting curve ﬂattens out, as the ﬁnal wetting angle is reached, or asymptotically approached. The force recorded at this point, reduced to a unit of length of the meniscus, is called the wetting force. Obviously, the blunter the ﬁnal wetting angle, the lower the wetting force.

Figure 3.23 The wetting balance

job:LAY03 page:59 colour:1

black–text

Soldering 77

Figure 3.24 The wetting curve

What the wetting balance really measures is not a mysterious force but simply the weight of the solder meniscus, which has climbed upwards on the specimen under the inﬂuence of the interfacial tension between solder and specimen, minus the upwards buoyancy of that part of the specimen which is immersed in the solder. The outer contour of the meniscus, and with it its volume and weight, are governed by the surface tension of the solder. The mathematical law which the contour of the meniscus follows has been calculated and described by Klein Wassink. If the specimen tends to dewet, the meniscus will start to descend after a time, and the wetting curve begins to drop after it has reached its maximum. Deciding on the best method for deriving a numerical value of solderability from a given wetting curve has been the subject of much discussion over the years. Account must be taken of the rate of rise of the wetting curve once wetting has set in, of its shape, of its maximum value and of the time taken to reach it. The computer of a wetting balance is programmed to deal with it all; a detailed account of the evaluation of wetting curves is outside the scope of this book. The globule test With chips, melfs, and SMDs like PLCCs, the small size and shape of the solderable surfaces makes the measurement of the meniscus force diﬃcult. The surfaces concerned are small, often of complex geometry, and their buoyancy in molten

job:LAY03 page:60 colour:1

black–text

78 Soldering

solder is greater than the wetting force which must be measured. To cope with this situation, the ‘globule test’ (Figure 3.25) has been evolved as an alternative to the immersion method described above. The specimen is ﬂuxed, dried and suspended from the measuring head of the wetting balance. A heated anvil, normally held at a temperature of 235 °C/455 °F, which carries a small globule of 60% Sn solder, weighing 200 mg, replaces the solderbath. It is raised against the specimen from below until it touches the specimen. As soon as the globule begins to tin it, the surface tension of the bridge of molten solder, which forms between anvil and specimen, pulls it downwards. The solderability index is calculated from the time within which the resultant wetting curve reaches two-thirds of its maximum value (normally one-half to one second). With chips and melfs, the solderability of both ends must be measured, because an asymmetrical solderability can be the cause of ‘tombstoning’ (Section 3.6.2). Normally, about ten specimens, taken from a batch or belt of SMDs, are tested in this

Figure 3.25 The globule test

job:LAY03 page:61 colour:1

black–text

Soldering 79

manner. The solderability of single leads of PLCCs, QFPs, etc., can be measured in the same way. A commercially available computerized wetting balance (Multicore) calls up the correct testing procedure and parameters once a test specimen has been identiﬁed and placed in the machine, and automatically produces and records its solderability value within about one minute. The dipping test A wetting balance is a sophisticated laboratory instrument, which represents a considerable investment. It is used mainly by vendors of components or ﬂuxes, and by major users of either. The dipping test is a simple, but useful, alternative. It is often called the ‘dip and look’ test. It does not provide a quantiﬁable numerical result, but it enables the user to make a reasonably objective, unambiguous judgement of the solderability of a component. It requires an electrically heated, thermostatically controlled solderbath of about 2 kg/4 lb capacity, ﬁlled with 60% Sn/40% Pb solder. This solderbath might well be the same as the one used in the solderballing test for solder paste (Section 5.2.3). The best procedure for a dipping test is as follows. At least three components from a batch or belt are selected. The component to be tested is gripped with stainless steel tweezers, and dipped in the ﬂux which is used in production or, in the case of reﬂowsoldering with solder paste, in an RMA ﬂux. Excess drops of ﬂux are removed with a piece of ﬁlter paper, and the ﬂuxed component is allowed to dry at room temperature. Immediately before the test, the surface of the solder bath is cleaned of oxide by skimming it with a dry, clean stainless steel spatula. The ﬂuxed test specimen is then dipped vertically in the bath, in the manner shown in Figure 3.26. It is lowered

Figure 3.26 The dipping test for SMDs

job:LAY03 page:62 colour:1

black–text

80 Soldering

into the bath steadily and slowly, at a speed of about 25 mm/1 in per second. It is kept immersed under the solder for about two seconds, and then withdrawn without jerking at about the same speed at which it had been lowered. With a little practice, this procedure is easy to carry out. It is equally easy to mechanize the procedure with a simple motorized device. In some countries, simple dipping test equipment is commercially available. Table 3.16 Dipping test parameters

Purpose of test

Temperature of solderbath

Solderability in vapourphase soldering Solderability in wavesoldering Tendency to dewet

215 °C+/−3 °C 420 °F+/−5 °F 250 °C+/−5 °C 480 °F+/−10 °F 260 °C+/−5 °C 500 °F+/−10 °F 260 °C+/−5 °C 500 °F+/−10 °F

Leach resistance of chip metallization

Figure 3.27 Judging a dipping test result

Dwell time in solderbath 3 sec 2 sec 5 sec 30 sec

job:LAY03 page:63 colour:1

black–text

Soldering 81

The test parameters depend on the soldering method by which the components are to be used. They are tabulated in Table 3.16. Having been dipped, every specimen is examined for signs of dewetting, under a magniﬁcation of about ;5. If more than 95% of the surfaces of every specimen are covered with a smooth continuous solder coating, the batch of SMDs from which the set of specimens has been taken can be assumed to be suitable for soldering. If more than ﬁve per cent of surface area has dewetted, the suitability of the batch of SMDs represented by the specimens is doubtful. It will be wise to repeat the test with a further three or more specimens. If the majority of those fail too, the batch should not be used. It is relatively easy to estimate visually whether a dewetted area represents above or below ﬁve per cent of the total, as Figure 3.27 shows.

3.7 References 1. Strauss, R. (1992) The Diﬀerence between Soldering Success and Soldering Quality; its Signiﬁcance for Quality Control and Corrective Soldering. Proc. 6th Intern. Conf. Interconnect. Technology in Electronics, DVS Rep. 141, Duesseldorf, Germany (in German). 2. McKeown, J. (1948) The Properties of Soft Solders and Soldered Joints. Brit. Nonf. Metals Res. Assoc., Research Monograph No. 5, Wantage, UK. 3. Raynor, G. V. (1947) The Pb–Sn Equilibrium Diagram. Met. Abstr. (London), 19, p. 150. 4. Earle, L. G. (1946) The Pb–Sn–Ag Equilibrium Diagram. J. Inst. Met. (London), 72, p. 403. 5. Smernos, S. and Strauss, R. (1984) Low Temperature Soldering, Circuit World (Ayr, Scotland), 10(3), pp. 23–25. 6. Vianco, P. T. and Frear, D. R. (1993) Issues in the replacement of Pb-bearing Solders. Journal of Materials, July 93, pp. 14–19. 7. Glazer, J. (1995) Metallurgy of low-temperature Pb-free solders for electronic assembly. Internat. Materials Review, 40, No. 2, pp. 65–93 (139 references). 8. ITRI Ltd, Uxbridge UB8 3PJ, UK (from 1995 onwards) ‘Leadfree Solders & Coatings Survey’, ‘Lead-Free Solders – References and Abstracts’, ‘Lead-Free Solder Patents’. On-going issues of publications. 9. Fukuda, A. (1995) Eliminating Lead from PCB Solder. Nikkei Electronics Asia, July, pp. 51–57. 10. Strauss, R. (1989) SMD Surface Mounted Devices, Verlag Technische Texte, Bonn, Germany, p. 47 (in German). 11. Thwaites, C. J. (1986) Some Metallurgical Aspects of SMD Technology, Brazing & Soldering (UK), Spring 1986. 12. Bader, W. G. (1969) Dissolution of Au, Ag, Pd, Pt, Cu and Ni in a molten Tin–Lead Solder. Welding J., 12, 48, pp. 551–557. 13. Steen, H. A. H. and Becker, G. (1986) The Eﬀect of Impurity Elements on the Soldering Properties of Eutectic and Near Eutectic Tin–Lead Solders. Brazing & Soldering (UK), No. 11, pp. 4–11.

job:LAY03 page:64 colour:1

black–text

82 Soldering

14. Campbell, A. N., Screaton, A. M. and Schaefer, T. P. (1955) Canad. J. Chem., 33, p. 511. 15. Schmitt-Thomas, K. G., Lang, H.-P. and Moedl, A. (1993) Metallurgical Examination of Thermally Stressed TAB Outer-lead Bonds. Conference on ‘Soldering, Science and Practice’, Techn. Univ. Munich, March 1993. DVS Rep. 153, Duesseldorf, Germany (in German). 16. Strauss, R. (1988) Wavesoldering v. Reﬂowsoldering – The metallurgical consequences of the Choice of Method. Brazing & Soldering, 14, pp. 5–8. 17. Tanner, C. G. (1987) Reliability of Surface Mounted Component Soldered Joints produced by Vapour Phase, Infrared, and Wavesoldering Techniques. BABS Intern. Conf., Nov. 87, paper 29. 18. Ashby, F. A. and Jones, D. R. H. (1988) Engineering Materials 2. Pergamon Press, Oxford. 19. Derived from data established by Knott, U. C. (1981) Dissertation, Structure of Soft-soldered Joints, Techn. Univ. Munich, Germany (in German). 20. Hofmann, W. (1962) Lead & Lead Alloys. Berlin, Springer Verlag. (In German, English translation available through Brit. Nonf. Met. Res. Assoc., Wantage, UK.) 21. Ashby, M. F. and Jones, D. R. H. (1988) Engineering Materials 2. Pergamon Press, Oxford, UK. 22. de Kluizenaar, E. E. (1990) Reliability of Soldered Joints: A Description of the State of the Art. Soldering & SMT (Ayr, Scotland), No. 4, pp. 27–38, No. 5, pp. 56–66, No. 6, pp. 18–27. 23. Engelmaier, W. (1993) Reliability of Surface Mount Solder Joints; Physics and Statistics of Failure. Proc. Intern. Conf. Softsoldering, Munich. DVS Report 153, Duesseldorf, Germany, pp. 149–160. 24. IPC (1992) Guidelines for Accelerated Reliability Testing of Surface Mount Solder Attachments. IPC Document IPC-SM-785. 25. Engelmaier, W. (1989) Performance Considerations, Thermal-Mechanical Eﬀects. Electron. Mats. Handbook, Vol. 1, ASM Intern., Materials Park, OH, p. 740. 26. Wild, R. N. (1973) Some Fatigue Properties of Solders & Soldered Joints. IBM Techn. Report 73Z000421. 27. Solomon, H. D. and Sartell, J. A. (eds) (1986) Electronic Packaging: Materials & Processes, ASM. 28. Rubin, W. (1990) A No-Clean Review, Proc. Conf. Electron. Manufact. & the Environment, Bournemouth, UK, pp. 36–43. 29. Lea, C. (1992) After CFCs? Electrochemical Publications, Ayr, Scotland, pp. 94–98. 30. Zado, F. M. (1983) Increasing the Soldering Eﬃciency of Noncorrosive Rosin Fluxes. Western Electric Eng., 27(1), pp. 22–29. 31. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Ch. 5.5.3. Electrochemical Publications, Ayr, Scotland. 32. Lea, C. (1992) After CFCs? loc. cit., p. 301. 33. Manko, H. H. (1979) Solders and Soldering, McGraw-Hill, NY, p. 313.

job:LAY03 page:65 colour:1

black–text

Soldering 83

34. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Ch. 2. Electrochem. Publ., Ayr, Scotland. 35. Wise, E. M. (1948) Metals Handbook, ASTM, Cleveland, Ohio, p. 1111. 36. Klein Wassink, R. J. (1989) loc. cit., pp. 217–218. 37. Strauss, R. (1988) Wavesoldering v. Reﬂow-soldering: Metallurgical Consequences of the Choice between them. Proc. 4th Intern. Conference, DVS (German Welding Soc.), Report 110, Duesseldorf, Germany, pp. 174–176 (in German). 38. Albrecht, H.-J. Scheel, T. and Freund, T. (1985) The Wetting Angle Measuring Unit. Soldering & Brazing, No. 8, pp. 8–15. 39. Klein Wassink, R. J. (1989) loc. cit., pp. 46–49. 40. Lea, C. (1989) Solderability Measurement of SMDs, Report DMA (D) 648, Nat. Phys. Lab., Teddington, UK.

job:LAY04 page:2 colour:1

black–text

4 Wavesoldering

4.1 The wave concept 4.1.1 Wavesoldering before SMDs Wavesoldering of printed circuit boards was conceived in 1956 at a time when circuit board technology was re-introduced from the USA into Europe, where it had originated in 1941 but had failed to gain a foothold after the war. SMDs had not yet appeared, and all solderjoints were of the push-through type, disposed on the ﬂat, unobstructed underside of the board. Initially, they were all soldered by hand; joint-by-joint soldering was diﬃcult and expensive to mechanize. The idea of pumping molten solder upwards through a nozzle, and passing the ﬂuxed underside of a circuit board through the crest of the resulting wave, proved to be a practicable and comparatively simple method for soldering all the joints on a board in one operation. It opened the door to economical mass-soldering of printed circuit boards. With all the joints disposed on a plane, unobstructed surface, the molten solder can readily reach and ﬁll every joint and, with the smallest distance between joints at 2.5 mm/100 mil, bridging is easy to avoid. The early introduction of soldermasks made clean soldering and visual inspection still easier.

4.1.2 Wavesoldering after SMDs The situation changed drastically with the introduction of SMDs, which had begun to be used in hybrid technology in the early and mid sixties, spreading to epoxy circuit boards from the early seventies onwards. Initially, the designers of SMDs had only the reﬂowsoldering of hybrids in mind, and probably did not consider wavesoldering. SMDs carry their soldering surfaces on or very close to their bodies, sometimes in awkward corners and diﬃcult for the molten solder to reach, often close together and diﬃcult for the solder not to bridge. The two-dimensional open plain of the wired circuit board became a three-dimensional landscape with the soldered joints hidden in the valleys. The problems and the limitations of wavesoldering SMDs stem from this. Moreover, SMDs must be glued to the soldering side of the circuit board before they can be passed through the solderwave, which adds a further operation and an additional technology to be mastered.

job:LAY04 page:3 colour:1

black–text

Wavesoldering 85

The conclusion seems obvious: don’t wavesolder unless you must. Until recently, there was no alternative to wavesoldering, if a board carried inserted wired components as well as SMDs, because it had always been thought that inserted through-joints cannot be satisfactorily reﬂowsoldered by conventional methods. This is no longer necessarily true: early in 1997, a method has been described which allows wired components to be reﬂowsoldered alongside the SMDs on the same board (see ‘Through-hole reﬂowsoldering’ in Section 5.1.1). However, until this technique has been proved viable under all conditions, it would be wise to regard the remarks in the next paragraphs, which relate to boards with a mixed population of SMDs and wired components, as still valid. Since the introduction of wavesoldering in a nitrogen atmosphere low in oxygen, which improves the surface tension of the molten solder and reduces the risk of bridging (Section 4.5), and with components becoming much ﬂatter than they used to be (Section 2.1), and ﬁnally with the printing of solder paste onto ﬁne-pitch circuit boards having become an exacting task, the above advice can no longer be given without reservation. Nevertheless, it is still generally true for conventional wavesoldering machines. If there are only a few push-through joints on a board, it may be cheaper and simpler ﬁrst to reﬂowsolder all the SMDs on the board by one of the methods outlined in Chapter 5 and then insert and solder the few remaining wired components by hand, or with one of the now available soldering robots. The diﬃculty can be overcome by adopting a design and manufacturing strategy in which the SMDs and the inserted components on a board are soldered in two separate operations. For example, a board can be so designed that the SMDs are ﬁrst placed and reﬂowsoldered on the side of the board which subsequently receives the wired components. These are then inserted, and the board is reversed and wavesoldered on a simple solderwave, which need not be a double or special chipwave (see Section 2.2). During that second operation, the structure and the properties of the SMD joints, which ride over the solderwave on the top surface of the board, are in no way degraded. Soldering demands that every joint be supplied with ﬂux, solder and heat. In wavesoldering, these tasks are carried out in three distinct and consecutive stages: the ﬂuxer applies an even, thin coat of ﬂux solution to the joints on the underside of the board. The subsequent preheating stage raises the temperature of the board to between 80 °C/175 °F and 110 °C/230 °F and removes the bulk of the solvent from the ﬂux coating. Finally, the solderwave supplies the solder in molten form, and at the same time the rest of the required soldering heat (Figure 4.1). Most wavesoldering machines are still constructed as ‘monobloc’ systems. Recently and especially with the growing popularity of wavesoldering under nitrogen, the advantages of modular construction of wavesoldering installations are beginning to be realized.

4.2 Applying the flux The importance of applying a coating of ﬂux to the underside of a circuit board in a reliable, consistent and reproducible manner, before drying oﬀ the ﬂux solvent and

job:LAY04 page:4 colour:1

black–text

86 Wavesoldering

Figure 4.1 The operational sequence of a wavesoldering machine

passing the board over the solderwave, cannot be overstated. If the ﬂux cover is uneven, patchy or variable, even the best of all possible ﬂuxes and carefully optimized soldering parameters are of no use, and faulty joints are bound to result. Wherever the ﬂux cover is too thin, there is a danger of incompletely ﬁlled joints, and bridges, icicles and ‘spider’s webs’ of solder adhesions are likely to form. Local lack of ﬂux leads to massive adhesions of solder in the aﬀected areas. For this reason, the technology of ﬂuxing has reached a high level of sophistication and mechanization over the years. The ﬂuxer has become an essential part of today’s complex, costly, automated and computer-controlled wavesoldering line. Attempts have been made in the past to coat circuit boards with a layer of solid ﬂux in the form of a lacquer, before inserting or placing the components. So far, none have been successful because this method does not allow suﬃcient ﬂux to reach the soldering surfaces of the components during the short time available when the board enters the solderwave. For this reason joint formation is erratic. On the other hand, ﬂuxing need not necessarily always be directly integrated with a soldering machine. Several vendors oﬀer ﬂuxers as independent modules, which can be ﬁtted into an existing soldering line. With few exceptions, until recently isopropyl alcohol (isopropanol) was the universal solvent for all wavesoldering ﬂuxes. Isopropanol has a ﬂashpoint of 12 °C/53.6 °F and is therefore a ﬂammable liquid of Class I, its ﬂashpoint being below 38 °C/200 °F (see Section 8.3.1 under ‘Flammability’). Concern is sometimes expressed about whether a ﬂuxer, which contains and dispenses a ﬂammable liquid, often in the form of an aerosol, constitutes a serious ﬁre risk when in close proximity to the infrared heaters of the preheating stage. This is not the case, provided a few sensible constructional and operational measures are taken. Nevertheless, towards the end of 1992 more stringent regulations concerning the storage of ﬂammable liquids on manufacturing premises, and the classiﬁcation of isopropanol as one of the volatile organic compounds (VOCs), which contribute to the formation of industrial and urban smog, and which have come under severe restriction in some states in the USA, have led to the development of alternative ﬂuxes based on water (Section 3.4.7). However, at the time of writing (1993), the vast majority of soldering ﬂuxes continue to be based on isopropanol. As is explained in Section 8.3 it is not the ﬂammable liquid itself, but its vapour, which burns. If the vapour concentration in air lies within the ﬂammability limits, a ﬂame or a glowing surface will ignite it.

job:LAY04 page:5 colour:1

black–text

Wavesoldering 87

Provided the preheating stage is ﬁtted with an air blower to expel the alcohol vapour given oﬀ by the drying ﬂux, its concentration will remain below the lower ﬂammability limit. In an ill-ventilated preheater, the ﬂux vapour can, and occasionally does, ignite with a puﬀ, without causing any harm. With foamﬂuxed boards, a ﬁre may start if the ﬂuxer is ill-adjusted and not ﬁtted with a brush (or, better, with an airknife) which removes clusters of foam hanging underneath the boards before they enter the heater. If such a foam cluster falls onto a heating element, especially if it is operated in the near infrared, high temperature mode, the foam is liable to ignite as it hits the heater. Hence, with foamﬂuxers, especially when a high-solids ﬂux with good foamstability is used, some means of preventing foam clusters from entering the preheater must be used. With an installation of this kind, especially with a not constantly supervised or processor-controlled installation, it is as well to ﬁt a ﬂameguard, which causes the preheating stage to be ﬂooded with CO and stops the air compressor of the foamﬂuxer (but not the conveyor). Needless tosay, with sprayﬂuxed boards this contingency cannot arise. In principle it is not necessary that soldering should follow immediately after ﬂuxing and drying of the ﬂux cover. There may be situations, especially with short or experimental runs of complex or costly boards, where ﬂuxing and drying, maybe in air, is more satisfactory and safer than ﬂuxing which is immediately followed by forced drying and soldering. This procedure allows inspection and maybe corrections or additions to a board before the irrevocable step of soldering it is undertaken. Gently predried boards can be stored safely in a dry environment for periods up to a few days without any deterioration in their soldering behaviour. Such preﬂuxed and dried boards require, if at all, only a gentle warming before entering the solderwave. It is of course important to test a given ﬂux for its suitability for this procedure before embarking on it.

4.2.1 Types of fluxer There are three basic types of ﬂuxer to choose from: waveﬂuxers, foamﬂuxers and sprayﬂuxers.

Wavefluxers Waveﬂuxers coat the underside of the circuit board with the help of a pumped wave of ﬂux solution, analogous to a solderwave. This method has generally become obsolescent, and for SMD populated boards it is not recommended at all. Waveﬂuxers are liable to apply too much ﬂux and in uncontrollable amounts, which needs an excessive intensity of preheating and leads to spitting in the solderwave and to problems with postcleaning.

Foamfluxers With foamﬂuxers, the circuit board travels across the crest of a wave of foamed ﬂux issuing from an elongated nozzle which straddles the path of the circuit board. The

job:LAY04 page:6 colour:1

black–text

88 Wavesoldering

foam is created by forcing air through a cylindrical porous body (foaming stone) which is immersed in the ﬂux, at the bottom end of a vertical elongated chimney which guides the foam upwards towards the foam nozzle (Figure 4.2). Foamﬂuxers are constructed of either high-density polythene or stainless steel. The working principle of the foamﬂuxer is simple and elegant; above all there are no moving parts. Nevertheless, its correct and reliable functioning depends on a few vital parameters, relating both to the ﬂux and the design of the ﬂuxer. The height and stability of the head of foam depend above all on the foaming behaviour of the ﬂux. Generally, rosin containing ﬂuxes foam better than rosin-free ones, as do ﬂuxes with high solids content compared with low-solids ﬂuxes. For this reason, many low-solids ﬂuxes contain small amounts of foam promoters (Section 3.4.1). The foam itself should preferably consist of ﬁne bubbles rather than large ones, because the smaller the bubbles the larger will be the amount of ﬂux carried in a given volume of foam. This quality of the foam depends not only on the size of the pores in the foamstone, but also on the foaming behaviour of the ﬂux itself. Apart from foamability, the stability of the foam is another critical property of a ﬂux. The foam should not get coarser through the merging of bubbles as it rises towards the nozzle aperture. On the other hand, once the foam touches the board surface, the bubbles ought to burst quickly so as to form a thin liquid cover on the board. An excessive stability of the foam, caused perhaps by an unsuitable or excessive foaming additive in the ﬂux, is undesirable: clusters of bubbles hanging from the underside of the board are liable to drop down on to the heaters where they could ignite as the board travels through the preheating stage, as has been mentioned already. To prevent this from happening, foamﬂuxers should be ﬁtted with a brush or, better, an airknife behind the foam nozzle to burst the bubbles and blow bubble clusters back into the ﬂuxer. Some design features of the ﬂuxer are of help in getting diﬃcult ﬂuxes to produce a stable, suﬃciently high crown of foam (Figure 4.3):

Figure 4.2 Working principle of a foamﬂuxer

job:LAY04 page:7 colour:1

black–text

Wavesoldering 89

Figure 4.3 Critical design features of a foamﬂuxer

1. The aperture of the foam nozzle should not be wider than 10–15 mm/0.4– 0.6 in and the top edges of the foam chimney should be sharply inclined towards one another. 2. Two foam-supporting strips, about 10–15 mm/0.4–0.6 in wide and ﬁtted to the outside of the foam chimney slightly below its upper edge will help to stabilize the foamwave and raise its height. Attaching a row of vertical bristles to either side of the foam nozzle with the aim of raising the foamwave is an obsolete practice which is not recommended: it is not very eﬀective and it can interfere with loosely inserted wired components. 3. The pores in the foaming stones should be small (approximately 10–20 m/ 0.5–1 mil) and of course as numerous as possible. The diameter of the foaming stone is normally 3–4 cm/0.25–0.3 in. With diﬃcult ﬂuxes, two smaller foamstones side by side are better than a single, larger one. Foaming stones are normally made from sintered ceramic or a polymer. 4. The distance between the foamstone and the top of the foaming chimney is a critical dimension. The shorter it is, the less is the danger of the bubbles bursting and the foam collapsing before it reaches the nozzle. The amount of ﬂux deposited by a foamﬂuxer depends primarily on the travelling speed of the board, more ﬂux being deposited at lower speeds. However, it cannot be controlled directly by the operating parameters of the ﬂuxer itself. A good head of ﬁne foam will put down suﬃcient ﬂux, even with low-solids ﬂuxes. Flooding the board with too much ﬂux is undesirable: the board should be fully wetted with ﬂux, but not ‘swimming’ with it. Otherwise, the upwards tilt of the board on the inclined conveyor will cause the ﬂux to ﬂow towards the trailing edge of the board, which leads to uneven drying and consequently to uneven soldering behaviour along the length of the board. The absence of moving parts makes the operation of a foamﬂuxer comparatively simple, but a few points require attention. In principle, the compressed air required for operating a foamﬂuxer may be drawn from the works’ compressed air supply if one is available, via a reducing

job:LAY04 page:8 colour:1

black–text

90 Wavesoldering

valve. Unless that air is strictly free from moisture, oil and dust, eﬃcient ﬁlters and a desiccator must be provided. Even traces of oil will cause the foam to collapse. Moisture will be absorbed in the hygroscopic ﬂux solvent. Though small amounts of water in the ﬂux do not aﬀect its soldering behaviour and may even make it foam better, they increase its density and thus distort the relationship between the density and the solids content of the ﬂux. This in turn complicates the monitoring of ﬂux quality (Section 4.2.2). With low-solids ﬂuxes in particular, misinterpretation of the ﬂux density can lead to lowering of the solids content below the danger limit and trigger a steep rise in soldering defects. Pickup of moisture should therefore be avoided. Dust will gradually clog the pores of the foamstone and in consequence reduce the head of foam. This in turn can cause local gaps in the ﬂux cover, with dire consequences for the soldering result. Usually, therefore, the required compressed air is supplied to a foamﬂuxer from an external dedicated small compressor, or through an integral airpump. Either must be ﬁtted with both dust ﬁlters and a desiccator, the latter speciﬁcally when operating in a humid environment. A foamstone, once it is saturated with ﬂux, must not be allowed to dry unless the absorbed ﬂux has been thoroughly ﬂushed out with a suitable solvent, such as hot, slightly acidiﬁed water in the case of rosin-free ﬂuxes, or in the case of rosincontaining ﬂuxes with one of the solvents mentioned in Section 8.3. As a rule it is good policy to keep the foamstone always immersed in the ﬂux. That means that the ﬂuxer is not emptied during normal working. Should this become necessary, for cleaning or servicing, when changing the ﬂux or during longer breaks in production, the foamstone is kept immersed in isopropyl alcohol, in a container with a well-ﬁtting lid. Once a ﬂux-soaked foamstone has been allowed to dry, it may be diﬃcult to clear the pores. Boiling in water to which a dishwashing detergent or sodium metaphosphate has been added can be tried as a last resort, though foamstones made from certain polymers may not survive this treatment. Contact with a hot surface causes an immediate collapse of the head of foam, which will then take some time to re-establish itself. This circumstance can arise if a soldering carriage or a template which is still hot from its previous passage through the solderwave is sent through the conveyor with a fresh board. The pressure and rate of ﬂow of the foaming air depend very much on the dimensions and the porosity of the foamstone, and it would be unsafe to give precise data. However, a pressure indicator is an essential requirement with every foamﬂuxer. The pressure of the foaming air is the principal operating parameter of a foamﬂuxer, and for this reason it must be monitored and controlled. With processor-controlled soldering lines in particular, loss of pressure in the foaming air should trip an alarm signal and stop the feed of further boards to the ﬂuxer. Obviously, the conveyor must not stop while boards are still travelling through the preheater and across the solder wave. Some foamﬂuxers are ﬁtted with sensors which turn on the foaming air when a board approaches and switch it oﬀ after it has passed, but this facility must be used with caution: some low-solids ﬂuxes, and also some ﬂuxers, may need quite some time to build up a suﬃcient head of foam after the air is turned on. Foamﬂuxers are less popular than they used to be, for several good reasons.

job:LAY04 page:9 colour:1

black–text

Wavesoldering 91

Firstly, because the ﬂux is constantly recirculated, it picks up contaminants from the boards which pass over it, as is explained in Section 4.2.2. Secondly, foamﬂuxing does not lend itself well to soldering SMD-populated boards (Section 4.5.2).

Sprayfluxers Since the introduction of SMDs, sprayﬂuxing has gained in popularity, because ﬂux droplets can be propelled into the narrow gaps between closely-spaced SMD components, whereas foam bubbles may burst before they reach the joints at the base of the component housings. With sprayﬂuxing, the foaming behaviour of the ﬂux is irrelevant, an important point in view of the present tendency towards ever-lower solids contents and increasing foaming problems. With modern sprayﬂuxers, the amount of ﬂux deposited per unit of board area can be controlled. Finally, and this is its main advantage, a sprayﬂuxer always delivers virgin ﬂux to the board, since there is no run-back of ﬂux into the ﬂux reservoir, as is the case with foamﬂuxers. Thus, there is no need for the constant monitoring and adjustment of the ﬂux density, either manually or by an automatic ﬂux monitor, nor the regular check of the water content of the ﬂux, which is so critical with low-solids ﬂuxes. Because the ﬂux is not constantly aerated, as is the case with foamﬂuxers, the ﬂux does not pick up water from the blowing air. Water contamination not only falsiﬁes the density/solids-content equation, but can also seriously reduce the solubility of the ﬂux residue, making cleaning more diﬃcult. The ﬂux in a sprayﬂuxer can be used to the last drop. There is no need to discard exhausted or contaminated ﬂux, which would have to be disposed of safely and professionally. Users of sprayﬂuxers report this as an important ﬁnancial saving. With sprayﬂuxing, the user is confronted with a choice between several systems, each of which have their speciﬁc virtues. Several vendors of wavesoldering machines oﬀer more than one type of sprayﬂuxer, which may be supplied integral with the machine or as separate units for retroﬁtting to an existing soldering line. A few constructional and operational features are common to all sprayﬂuxers: almost all of them operate in an enclosure, which is ﬁtted with an exhaust. Without this precaution, an aerosol of ﬂux droplets is liable to spread in the neighbourhood of the ﬂuxer and the soldering line, with obvious and undesirable consequences. Also, measures must be taken to avoid overspray beyond the width and length of the boards, as they travel across the spray zone. This involves sensor-operated controls for starting and cutting oﬀ the spray action to coincide with the arrival of the leading edge of a board and the departure of its trailing edge, and provision for suiting the width of spraycover to the width of the board. Common to all sprayﬂuxers is the need for an eﬃcient exhaust system, which gathers overspray and the aerosol of small ﬂux droplets which unavoidably forms wherever ﬂux is atomized. This airborne ﬂux must not be allowed to settle on the top surface of boards or on the soldering equipment at large, where it could obviously cause a great deal of trouble. By now, most makers of sprayﬂuxers provide their machines with exhaust systems of suﬃcient size and suction power to prevent the escape of airborne ﬂux from the unit. It is important that such exhaust systems

job:LAY04 page:10 colour:1

black–text

92 Wavesoldering

are ﬁtted with eﬃcient ﬁlters which retain the ﬂux droplets, and that these ﬁlters are easy to reach and to service. In particular, when rosin-based ﬂuxes are used, regular servicing and cleaning of the whole exhaust system is of the essence: suction fans and conduits dripping with rosin constitute a serious and well-known ﬁre hazard. Compressed-air sprayﬂuxers With this type of ﬂuxer, the ﬂux solution is fed to the spraynozzles by a metering pump, so that the rate of ﬂux delivery can be controlled (Figure 4.4). The ability to control the rate of ﬂux delivery and the thickness of the ﬂux cover on the board has become very important with the growing use of ﬂuxes with low solids contents and the existence of water-based ﬂuxes (Sections 3.4.5 and 3.4.6). Obviously, at a given rate of ﬂux delivery, the amount of ﬂux deposited per unit of board area is inversely proportional to the travelling speed of the board. The spraynozzles are arranged in a row which spans the width of the solderwave. The width of the spraypattern can be adjusted to match the width of the boards passing through a line by cutting oﬀ the air and ﬂux supply from the appropriate nozzles at either end of the row. Before the advent of low-solids ﬂuxes, a problem with compressed-air sprayﬂuxers arose from the need for time-consuming cleaning of nozzles, which tended to clog during rest periods because of the drying of resinous ﬂuxes. Since the introduction of low-solids ﬂuxes, compressed-air sprayﬂuxers have become more popular again. Many vendors oﬀer sprayﬂuxers with a single nozzle which traverses the width of the circuit boards in a zig-zag pattern. Flux is fed to the nozzle by a metering pump, preferably at a pressure suﬃcient to ensure atomization without the use of compressed air. The width of the traverse is adjustable to match the dimensions of the

Figure 4.4 Working principle of a compressed-air sprayﬂuxer

job:LAY04 page:11 colour:1

black–text

Wavesoldering 93

circuit boards being soldered. It is essential that the pitch of the traverse is close enough so as not to leave any unﬂuxed areas. Users will be well advised to check at regular intervals that the spray pattern reliably and reproducibly covers all of the surface of the boards passing through the machine. A certain double coverage at the return points of the pattern is unavoidable and does no harm, but on no account must there be any unﬂuxed or poorly ﬂuxed areas elsewhere. If there are, reject rates will rise disastrously: solid construction, good maintenance and constant process control are of the essence with these ﬂuxers, as indeed with all aspects of a wavesoldering installation.

Rotating-drum sprayﬂuxer This is a simple and very eﬀective method of projecting a spray of ﬁne ﬂux droplets against the underside of a circuit board. A cylinder, formed from a woven closemesh stainless steel sieve, rotates in a shallow bath of ﬂux, with its lower portion immersed in the ﬂux to a depth of 1–2 cm/0.5–1 in (Figure 4.5). The diameter of the cylinder may be 5–10 cm/2–4 in, and its length corresponds to the width of the solderwave. An airknife, located inside the cylinder near its apex, directs a jet of compressed air upwards against the inside of the cylinder, either through a line of closely-set small holes or a longitudinal narrow slit. This airstream blows the ﬂux from the wiremesh, on which it has been carried out of the ﬂuxbath, against the underside of the circuit board which travels a short distance above the cylinder. The rate of ﬂux delivery depends on the speed of rotation of the cylinder, which is driven by a variable-speed motor. The onset and the cutoﬀ times of the spray are controlled by sensors so as to coincide with the arrival and departure of a board above the line of spray and to avoid overspray. The width of the sprayed area can be set by blanking oﬀ the ends of the airknife by, for example, movable sleeves, so as to match the width of the boards travelling across. The setting of this parameter can also be mechanized and controlled by sensors.

Figure 4.5 Working principle of a rotating-drum sprayﬂuxer

job:LAY04 page:12 colour:1

black–text

94 Wavesoldering

The cylinder need not be removed during rest periods and overnight. The ﬂux on it will of course dry, but rotating the cylinder for about 15 minutes before starting work again will clear it. For longer breaks in production, the cylinder is removed from the ﬂuxer and cleared of ﬂux with an appropriate thinner, which as a rule is supplied by the ﬂux vendor. Rotating-brush sprinklers Figure 4.6 explains the working principle: a rotating cylindrical brush, carrying fairly stiﬀ nylon bristles, and of a length corresponding to the width of the solderwave, is arranged at right angles to the travel of the circuit board conveyor. The lower portion of the brush dips in a container of ﬂux. The sense of rotation is contrary to the direction of travel of the board conveyor. Somewhat before the bristles reach the apex of their rotation, they pass the straight edge of a blade, which can be pushed into the path of the bristles so as to bend them backwards. Having passed the blade, the bristles spring forward and ﬂing the ﬂux they have picked up from the reservoir upwards against the underside of the circuit board which passes overhead. A sensor-actuated mechanism pushes the blade against the brush when a board arrives above the aperture of the sprinkler and retracts it as soon as the board has passed. The width of the spray is governed by the length of the blade, which is adjustable to match the width of the boards to be ﬂuxed. The amount of ﬂux delivered is governed by the controllable speed of rotation of the brush, while the depth of immersion of the bristles in the ﬂux determines the size of the ﬂux droplets to some extent. It is customary to keep the brush rotating during short breaks in production. During longer breaks, the brush is removed and stored in a container ﬁlled with thinners, and provided with a well-ﬁtting lid. Should the bristles harden by being left to dry in air, a brief period of rotation in the ﬂuxer will soften them again.

Figure 4.6 Working principle of a sprinkling ﬂuxer

job:LAY04 page:13 colour:1

black–text

Wavesoldering 95

Sprayﬂuxers, which propel the ﬂux droplets in a straight path and at some speed against a circuit board, have occasionally met with some objections. Because of their straight line of ﬂight, some droplets may reach the upper surface of the circuit board through apertures such as unoccupied through-holes, vias, or milled slots in boards which are to be broken into separate units after soldering. Stray ﬂux on the upper side of a board is undesirable. It can cause problems with relays, trimmers, or any other component which is sensitive to physical contamination. Directing the ﬂight of the drops against the board at an angle reduces the problem, but does not entirely eliminate it. Another diﬃculty arose with the introduction of wavesoldering in an oxygenfree atmosphere (Section 4.4). Blowing atomizing air into the oxygen-free machine interior runs contrary to the concept, and atomizing with compressed nitrogen is costly. Ultrasonic spray ﬂuxers The development of ultrasonically driven ﬂuxing systems was motivated by these problems. With ultrasonic atomization, a metered supply of ﬂux is fed to the vibrating surface of an ultrasonic generator. The vibrational energy is transmitted to the ﬁlm of ﬂux which forms on that surface and breaks it up into an aerosol of very ﬁne droplets, which form a cloud of aerosol above the generator (Figure 4.7). With some ultrasonic ﬂuxers, a gentle stream of nitrogen (or air with a conventional wavesoldering machine) wafts that aerosol against the underside of the board as it traverses the sprayzone. With others, the atomizing surface of the ultrasound generator is so shaped as to gather the aerosol cloud and to propel it towards the circuit board. The ﬂuxing head of some ultrasound systems traverses the width of the board in a zig-zag pattern, as has already been described; with others the shape of the aerosol cloud is given a fanlike shape, so that one or two atomizing heads suﬃce to straddle

Figure 4.7 Working principle of ultrasonic atomization

job:LAY04 page:14 colour:1

black–text

96 Wavesoldering

the width of a board. Sensor-actuated control of the width and duration of ﬂux application are common to all ultrasound ﬂuxers. Ultrasonic sprayﬂuxers are suitable for use with ﬂuxes based on alcohol, but not for waterbased ﬂuxes. Water, being heavier and less mobile than alcohol, requires more kinetic energy for its dispersal into ﬁne drops than the normal ultrasonic sprayhead can supply, at least in its present state of development.

4.2.2 Monitoring and controlling flux quality The solids content of a ﬂux, given its type and formulation, is its most telling and decisive parameter. With the exception of one reservation which will be discussed presently, there is a direct relationship between the density of a ﬂux and its solids content. Every ﬂux has a characteristic density/solids-content curve, which ought to be given in the datasheet supplied by the vendor. As a rule, these curves are correct for a temperature of 20 °C/68 °F and, strictly speaking, the ﬂux sample should be warmed or cooled to that temperature before its density is measured. Vendors can save their customers a good deal of time and trouble if they provide ﬂux-density/solids-content curves for a range of test temperatures (Figure 4.8). Whether and how often the ﬂux density needs checking depends on the type of ﬂuxer used. Waveﬂuxers and foamﬂuxers, where excess ﬂux runs back from the circuit board into the ﬂux reservoir, demand a regular check of the quality and purity of the ﬂux. With these systems ﬂux is constantly exposed to the ambient air, if not actively aerated. Solvent may evaporate, ﬂux constituents may oxidize, moisture may be absorbed, impurities in the form of solids or contamination may be washed oﬀ the board surface back into the ﬂuxer.

Figure 4.8 Flux-densitySolids-content curve

job:LAY04 page:15 colour:1

black–text

Wavesoldering 97

Flux density is usually checked with a ﬂoating aerometer of a suitably chosen range, often supplied by the ﬂux vendor, together with a convenient measuring cylinder. It is important that the scale on the shaft of the instrument should be suﬃciently open so that the ﬂux density can be read accurately to the third digit after the decimal point. With the recirculating ﬂuxers described above, the ﬂux density should be checked every day before sending the ﬁrst boards through the soldering line and, depending on circumstances and the workload, a second time after the lunchbreak. Thickening of the ﬂux through loss of solvent does not in most cases aﬀect soldering quality, but it increases the amount of ﬂux residue left on a board, which in turn aﬀects appearance and testability on an adaptor bed, and makes higher demands on any subsequent cleaning procedure. Thickening is compensated by adding an appropriate amount of solvent or thinners, usually supplied by the ﬂux vendor. This addition of thinners is often taken care of by an automatic ﬂux-density controller, which can be retroﬁtted to a machine if necessary. That such density controllers must be temperature compensated goes without saying, because a drop of 1 °C/1.8 °F in temperature raises the density of a ﬂux by approximately 0.0008 g/ml. In this context, the distortion of the density/solids-content relationship through water picked up by the ﬂux has important consequences. One per cent of water added to a ﬂux based on isopropyl alcohol raises its density by 0.003 g/ml. Adding thinners to a low-solids ﬂux under the mistaken assumption that it has thickened, when in reality it has become heavier through water pickup, can have fatal results: the concentration of active ingredients in these ﬂuxes is delicately balanced at the minimum which will ensure satisfactory soldering. Lowering it by adding thinners is very likely to lead to a rapid rise in soldering defects and bridging. This is exactly what an automatic ﬂux-density control apparatus will do, if it is misled by water contaminated ﬂux into the assumption that the solids content of the ﬂux is too high. With low-solids ﬂuxes, which are being used on an ever-increasing scale (Section 3.4.5), density is no longer a reliable indicator of their solids content. With such ﬂuxes, even a slight drop below the correct solids concentration is fatal. For all these reasons, ﬂux control systems have been developed, and are increasingly being used, which estimate the solids content of the ﬂux by chemical means, such as by monitoring its pH value or some other chemical parameter which is a measure of the percentage of its active ingredient. Many of these instruments are speciﬁc for a given make of ﬂux, and their operating parameters must be adjusted to ﬁt the exact type of ﬂux in the foamﬂuxer or waveﬂuxer. It is worth noting at this point that, apart from its eﬀect on the ﬂux density, the presence of water in a ﬂux has no deleterious eﬀect on its performance. On a warm humid day, the water content of a ﬂux has been known to rise up to 10% with a foamﬂuxer, without any ill eﬀect on the soldering quality. Sometimes it is useful to know the water content of the ﬂux if only to correct the result of an aerometer reading. Several ﬂux vendors supply simple titrating kits complete with reagents which make it easy, even for an operator untrained in chemical analysis, to determine the water content of a ﬂux with suﬃcient accuracy. It needs no stressing that none of these complications arise with sprayﬂuxers, which always deliver virgin ﬂux to the circuit board. Nevertheless, this does not

job:LAY04 page:16 colour:1

black–text

98 Wavesoldering

relieve the user from the obligation to check a new canister of ﬂux for the identity and density of its contents, before charging it into the ﬂuxer. An error here can ruin a day’s production. Rosin-based ﬂuxes, more so than rosin-free types, are subject to a certain degradation through constant exposure to air, mainly by oxidation, which reduces their ﬂuxing power. The rate at which this happens depends largely on the type of rosin used. A visible eﬀect of this degradation is a progressive darkening of the ﬂux, which gradually changes from the pale yellow of the fresh solution to a dark brown. It may be useful to keep a sample of fresh ﬂux in a small, well-sealed bottle which is stored away from daylight as a reference specimen to check and judge the darkening. With waveﬂuxers and foamﬂuxers, only a fraction of the ﬂux circulating through the ﬂuxer remains on the board. The bulk returns and is constantly recirculated. This means that the underside of all boards passing through the soldering line is constantly being washed by the ﬂux, which thus removes and accumulates all the contaminants such as dust, drilling and cutting swarf, grease or oil, and possibly small pieces of copperwire, etc. which adhere to the board underside. It is therefore advisable to empty a waveﬂuxer or foamﬂuxer after about 1500–2000 sq. m/ 15 000–20 000 sq. ft of board area have passed through it. Some companies operate on a time basis and, depending on the workload and on the nature of the product, they replace the ﬁlling of such ﬂuxers after a certain number of weeks of continuous operation. However, even with discontinuous operation, after about two months’ use in a waveﬂuxer or foamﬂuxer, a wetting or spreading test should be carried out with the ﬂux (Section 3.6.1) to check its performance. After emptying a ﬂuxer, its interior must be cleaned and accumulated solids removed. The tank of some ﬂuxers is ﬁtted with a removable tray for this purpose. Discarded ﬂux must of course not be dumped, but must be handed to a qualiﬁed and registered disposal specialist. Some ﬂux vendors are prepared to take back discarded ﬂux when delivering fresh supplies.

General operating hints Most modern ﬂuxers are designed in such a way that solvent losses through evaporation are reduced to a minimum. Nevertheless, it is advisable to cover the ﬂuxer with a well-ﬁtting lid during stops in production. Many makers provide such lids as a matter of routine. During longer rest periods and holidays, it is best to empty the contents of the ﬂuxer into a closed container, while cleaning the interior of the ﬂuxer at the same time. Some ﬂuxers are ﬁtted with an integral reservoir, into which the contents of the ﬂuxbath can be drained during such intervals.

4.3 Preheating the board 4.3.1 Heat requirements A freshly ﬂuxed board cannot be wavesoldered successfully unless its underside has been heated to a temperature above about 80–100 °C/170–210 °F before it enters the solderwave. Many reasons have been put forward for this undisputed fact of life

job:LAY04 page:17 colour:1

black–text

Wavesoldering 99

at one time or another, but by now there is general agreement that there are mainly physical, but no chemical, reasons for the need to preheat: the solderwave must raise the temperature of the board together with the joints to the full soldering heat of 250 °C/480 °F within at most a second. It can only do this if it is relieved of the task of boiling oﬀ the solvent contained in the ﬂux, and of supplying some of the heat needed for raising the temperature of the board itself, which may be a heavy multilayer laminate, from room temperature to soldering temperature. Preheating cushions the thermal shock, which would hit the board and the components on it, if it had to confront the solderwave straight from cold. Instead, as the board travels through the preheating stage, its temperature rises at the relatively gentle rate of about 2 °C/4 °F per second to approximately 80–100 °C/175–210 °F with an alcohol-based ﬂux, and to 120 °C/250 °F with a water-based one. Preheat is particularly important with components which are sensitive to thermal shock, such as ceramic multilayer condensers. Tables 4.1 and 4.2 give the order of magnitude of the amounts of heat involved in the preheating and the soldering stages of wavesoldering. The data summarized in these tables underline the importance and quantify the function of the preheating stage: they show that the heat needed to boil oﬀ the ﬂux solvent represents a considerable portion of the total heat demand, and that preheating reduces the heat demanded from the solderwave during its few seconds of contact with the board by almost one-third. Without an eﬃcient preheating stage, conveyor speeds of up to 4 m/12 ft per minute would not be possible, nor could the molten solder be persuaded to rise through the plated holes in a multilayer board to form a meniscus on its top surface during the short time available for it. Should an excess amount of ﬂux solvent be left on a board through insuﬃcient preheat, a vapour blanket is liable to form between the board and the solderwave. This not only slows down the heat transfer between the molten solder and the board, but it can also cause the solder to spit and thus provide one of the causes of small globules adhering to the underside of a board (for others, see Section 4.6.1). Finally, the mobility of an insuﬃciently predried ﬂux coating renders it more Table 4.1 Thermal properties of substances involved in wavesoldering Air

Water

Speciﬁc heat cal/g/°C W. sec/g/°C

0.24 1.00

Heat of fusion W. sec/g

—

—

Heat of boiling W. sec/g

—

2254

Thermal conductivity W/cm/sec ; 10\

0.0058

1.0 4.19

5.4

Iso-propyl alcohol 0.57 2.39 — 681 1.7

FR4

0.35 1.47 333 — 0.3

Copper

0.092 0.385 205

Solder 60% Sn 0.042 0.186 46

— 390

— 52

job:LAY04 page:18 colour:1

black–text

100 Wavesoldering

Table 4.2 Thermal audit of wavesoldering The data below are calculated for a standard ‘Europa board’ (160 mm/6.3 in wide ; 233 mm/9.2 in long, surface area 373 sq. cm/58.0 sq. in). The board is assumed to be 1.2 mm/57 mil thick FR4 and to have been given a 0.1 mm/4 mil thick coating of rosin ﬂux in isopropyl alcohol as solvent. Volume of the board laminate Weight of the board laminate Volume of the ﬂux cover Weight of the ﬂux cover

44.7 ml 80 g 3.7 ml 3.2 g

Thermal input during preheating the board from 20 °C/68 °F to 100 °C/212 °F: Heating the laminate 9.4 kW sec Heating the ﬂuxcover to its boiling temperature 0.6 kW sec Evaporating the ﬂux solvent 2.2 kW sec* Total

12.2 kW sec = 27% of total

Thermal input from the solderwave (solder temperature 250 °C/482 °F): Heating the board from 100 °C/212 °F to 250 °C/482 °F 17.5 kW sec = 73% of total Total heat demand

29.7 kW sec

The heat demand from the circuit tracks, the leadwires and the SMDs has been neglected in this calculation because of their comparatively low speciﬁc heat. *The heat of evaporation of water is 3.3 times that of isopropyl alcohol. Should a ﬂux have absorbed 10% of water, e.g. in a foamﬂuxer, 2.7 kW sec would be needed to dry the ﬂux cover instead of 2.2 kW sec, a negligible diﬀerence in the context of the total heat requirement.

liable to be washed completely oﬀ the board by the solder, so that there is not enough left on the exit side of the wave. Some presence of ﬂux is, however, needed there to ensure the mobility and high surface tension of the solder in the region of the ‘peelback’ which prevents bridging and solder adhesions (see Sections 3.4.1 and 4.3.2). This aspect is particularly important with many low-solids ﬂuxes, especially the rosin-free ones, which demand a sharper preheat than conventional high-solid rosin-based ﬂuxes. By contrast, with the latter, too ﬁerce a preheat is liable to bake the ﬂux cover into a hard, partially polymerized lacquer which makes postcleaning more diﬃcult, if not impossible (see Section 8.1.2).

4.3.2 Heat emitters and their characteristics In practice, preheating is eﬀected by passing the ﬂuxed boards over a bank of infrared heaters, at a distance of approximately 5 cm/2 in. These heaters are backed by a heat-reﬂecting metal panel, which ought to be easy to withdraw for the periodical removal of ﬂux drippings. It has become customary to direct a gentle stream of warm air through the space between the heaters and the boards travelling above them (Figure 4.9). There are

job:LAY04 page:19 colour:1

black–text

Wavesoldering 101

Figure 4.9 The preheating section

several reasons for this. By removing the solvent-laden air from this space, drying is accelerated. Most importantly, this venting prevents the build-up of potentially explosive solvent/air mixtures. Naturally, with a wavesoldering machine operating in a nitrogen atmosphere (Section 4.6) this precaution is neither possible nor necessary. With most preheaters, a reﬂector, made from polished aluminium or stainless steel, is ﬁtted above the board conveyor. This not only conserves thermal energy, but reduces the temperature diﬀerence between the underside and the top side of the board. It reduces warping and helps the solder to rise to the top of throughplated holes. With very heavy or multilayer boards, especially if they carry massive internal copper layers, a top reﬂector is essential. In some cases, a few infrared heaters mounted above the board conveyor may be necessary to provide the necessary topheat to get the solder to rise to the surface of the board. This measure is preferable and kinder to the board and its components than raising the solder temperature or slowing down the conveyor. The heating elements of the majority of wavesoldering machines are internally heated metallic or ceramic infrared emitters, ﬁtted with a heat-reﬂecting backing. Most machines carry heat-sensors, which permit thermostatic control and the display of their temperature on the control panel of the machine. As a rule, the heaters operate in the temperature range between 300 °C/570 °F and 500 °C/770 °F, and thus in the middle and far infrared range of the spectrum. At these wavelengths, the radiated energy is readily absorbed by both the ﬂux and the epoxy laminate, which ensures an eﬃcient heat transfer. The thermal energy given oﬀ by the surface of an emitter rises from 0.6 W per sq. cm/3.75 W per sq. in at an emitter temperature of 300 °C/570 °F to 2.0 W per sq. cm/12.5 W per sq. in at 500 °C/930 °F. The details of the physical laws which govern infrared heating are covered more fully in Section 5.4.2. With some makes of machine, tubular resistance heaters are installed, either in a zig-zag pattern which straddles the maximum board width, or in straight lines at

job:LAY04 page:20 colour:1

black–text

102 Wavesoldering

right angles or parallel to the direction of board travel. In the latter case, the width of the irradiated area may be adjusted to match the width of the boards being soldered. Whatever the arrangement of the heaters, it is important that all parts of a board receive the same dose of thermal energy, because uneven preheating is a dangerous source of soldering faults. Most modern soldering lines give a warning if a heater in the preheating section should fail; some prevent further boards from entering the line in case of a heater failure. The boards still in the line must of course continue to travel forward, if they are not to be fried to a crisp or get stuck over the solderwave. Internally heated infrared emitters have necessarily a high thermal mass, and their response to changes in the heating current is correspondingly slow. Depending on its design, an element of this type may require up to 15 minutes to reach its full operating temperature after being switched on. For this reason, some processor-controlled soldering lines are ﬁtted with high-temperature tubular quartz heaters in their preheating section. These heaters consist of a spiral of tungsten wire located inside an evacuated quartz tube. Usually, these tubes are arranged in groups, at right angles to the direction of travel of the boards (Section 5.4.4). They operate at temperatures between 800 °C/1500 °F and 1100 °C/2000 °F, and their emitted thermal radiation is in the near-infrared part of the spectrum. They reach their full operating temperature within less than a second after being switched on, and they respond very quickly to changes in the operating current. Depending on the type of heater and its temperature, the energy emitted lies in the range 15–50 W per cm/ 38–125 W per in length of tube. Because of this high energy density and their fast response to changes in heating current, quartz-tube heaters operate in short bursts, which must be accurately and reliably controlled so as not to bake the ﬂux into a hard coating, or even burn the boards and damage expensive SMDs.

4.3.3 Temperature control When conventional rosin-based ﬂuxes used to have solids contents of upwards of 10%, it was customary to aim at a heating regime which raised the underside temperature of the boards to between 80 °C/180 °F and 90 °C/195 °F. For modern, low-solids ﬂuxes, which may contain only small amounts of rosin, or none at all, ﬂux vendors recommend higher underside temperatures, of up to 110 °C/230 °F with alcohol-based ﬂuxes or 120 °C/250 °F for water-based ones. The aim is to consolidate the thin ﬂux coating suﬃciently to ensure that enough of it survives underneath the board after it has passed through one or two solderwave crests. Otherwise, bridging or the appearance of a thin ‘spider’s web’ of solder, adhering to the surface of the soldermask, can become a real danger. A given setting of the heating power in a preheating line is of course only valid for the conveyor speed at which it was established: slowing down the conveyor means that the boards get too hot; speeding it up leaves them too cold. Balancing and optimizing such operational parameters is fully dealt with in Section 4.7. Temperature indicators in the form of self-adhesive labels are a very convenient method of ascertaining the temperature a board has reached on leaving the preheating stage. They are usually available from the vendors of ﬂuxes or soldering accessories. They record the exit temperature through an irreversible and distinct

job:LAY04 page:21 colour:1

black–text

Wavesoldering 103

colour change, from white to brown or black, or from one colour to another. Sets of labels with a convenient range of colour-change temperatures are on the market. A board of the same size and thickness as the production boards, but without components, is used for a trial run through ﬂuxer and heater. The temperature indicators are stuck to various strategic locations on the board. Having been read after the run, they are removed, and one board can be used many times over. On many processor-controlled wavesoldering lines the temperature of the board underside is scanned and monitored by remote sensing, which is linked to the machine control. As has already been said, low-temperature heaters respond only slowly to current adjustments, and this must be considered in the control software. High-temperature quartz heaters are more suitable for this technique. Compact, self-contained temperature logging equipment has been available for some time. These systems employ a temperature sensing and recording unit, which is housed in a heat-insulated casing. It can ride along with a sample board through the length of the wavesoldering machine, sampling and storing the output of a number of thermocouples, normally six. These are glued to strategic positions on the circuit board with a thermally conductive adhesive. The logged data can be transferred from the logging unit to a PC and stored, displayed or printed out, thus providing a complete temperature/time proﬁle of not only the preheating stage, but of the whole soldering process. A number of such logging systems are commercially available, mostly from the makers of soldering machines or from ﬂux vendors. Obviously, the same equipment can be used for establishing and recording the temperature proﬁle of any type of reﬂowsoldering installation as well (Sections 5.3, 5.4 and 5.5).

4.4 The solderwave 4.4.1 Construction of the soldering unit Solderwaves are produced by forcing molten solder upwards through a vertical conduit which ends in the so-called wavenozzle. Figure 4.10 shows the general principle of a widely used type of wavesoldering machine. Originally, the wavenozzle had the form of a narrow slot, arranged at right angles to the travelling direction of the board, with the emerging solder forming a hump of molten metal and falling in a symmetrical wave over both sides back into the main container. The symmetrical wave was soon replaced by the asymmetrical wave shown in the drawing, which gives tidier joints, reduces bridging and permits higher soldering speeds. With most types of wavemachines, an axial impeller pump, driven by a variable speed motor, propels the solder downward into a pressure chamber, from which it ﬂows through a vertical conduit upwards towards the wavenozzle. This arrangement keeps the movement of the solder towards and over the weirs at both sides of the nozzle as free from turbulence as possible. Before the advent of SMDs, this waveform, with the board skimming on an upwards inclined path over the crest of the overﬂow, was the best way to achieve clean, bridge-free soldering at conveyor speeds of up to and over 2 m/6 ft per minute. Waveforms and the way in which they

job:LAY04 page:22 colour:1

black–text

104 Wavesoldering

Figure 4.10 Working principle of a wavesoldering machine

had to be adapted to the demands of SMD soldering are discussed in Section 4.4.3. The capacity of the solder tank may vary from 20–40 kg/40–80 lb with small benchtop machines up to 700 kg/1400 lb for high-capacity soldering lines for large circuit boards. In most cases the solder is heated by external heaters clamped to the sides of the solder tank. Many wavesoldering machines are constructed from stainless steel sheet. Mild steel, suitably protected against the action of the molten solder, is equally satisfactory. The solderwave itself must fulﬁl two tasks. The ﬁrst one is to get the already preheated board hot enough to permit the solder to ﬁll every joint completely. The second one is to enable the solder to reach and to completely ﬁll every joint on the board, and afterwards to let it drain away from all the places where it must not remain.

4.4.2 Thermal role of the solderwave The reservoir of molten solder which supplies the solderwave is normally maintained at a temperature of 250 ± 5 °C (480 ± 10 °F). By general consent, this has been accepted worldwide as the most convenient temperature which meets almost all normal requirements of wavesoldering if the standard eutectic tin/lead solder (melting point 183 °C/361 °F) is being used. If the machine runs with one of the lead-free solders (Section 3.2.3), the temperature of the solder will obviously have to be adjusted. Because the eﬃciency of a ﬂux is strongly temperature-dependent, special ﬂuxes will have to be formulated for use with lead-free solders. Some work dealing with the problems posed by low-melting solders has been published.

With a standard eutectic solder, temperatures above 250 °C/480 °F are hardly ever used. Particularly heavy demands of soldering heat can almost always be met by slowing down the conveyor or intensifying the preheat. Molten solder is by far the best heat transfer medium in the soldering business: it provides conductive transfer of heat by metal-to-metal contact, with perfect con-

job:LAY04 page:23 colour:1

black–text

Wavesoldering 105

formity between the heating and the heated surface. Copper may have a higher heat capacity and thermal conductivity than solder (Table 4.1), but molten solder adapts to the shape of every surface it encounters. Both the ancient soldering iron and some of the latest techniques of desoldering and resoldering SMDs make use of this convenient fact, by always working with a soldering bit well covered with molten solder. Heating by metallic contact represents an equilibrium situation where the temperature of the heat source is the target temperature for the heat sink, with the temperature diﬀerence between the two quickly dropping to zero. This means that the duration of heating is not the critical factor it is with non-equilibrium systems such as infrared or laser soldering. The mechanism of heat transfer between the solderwave and the circuit board relies on a mixture of conduction and convection. The measured rate of heat transfer between the crest of a normal non-turbulent solderwave and the copper laminate bonded to an FR4 board has been determined at approx. 2 W/sec. mm (Pascoe, G. and Strauss, R., 1958 unpublished). With a turbulent wave the rate of heat transfer is somewhat higher. On this basis, the quantity of heat available to a normal solderpad and its inserted wire during its two seconds’ contact with the solderwave adds up to about 15 W sec. The actual heat required to raise the temperature of the copper lining of the hole together with the footprints at both ends and the inserted wire amount to no more than 2 W sec. In this calculation, the thermal needs of the FR4, which surrounds the hole, and of the soldermask which covers the board and the conductor tracks can be neglected: though the speciﬁc heat of FR4 is four times higher than that of copper, its thermal conductivity is lower by three orders of magnitude. These ﬁgures show that, thermally, the solderwave can cope with all likely heat demands. With SMDs, these are in any case lower than with wired components. The mass of the metallized surfaces on passive components, and of the legs of SOs, PLCCs or QFPs is measured in mg, whereas the surfaces available for contacting the solderwave are in the sq. mm order of magnitude. Thus, provided full contact between the molten solder and all solderable surfaces can be achieved, implying that the solder wets all these surfaces, the heatﬂow available is more than adequate to get them all hot enough within the time available: in short, the thermodynamics of wavesoldering SMDs are no problem. The diﬃculties of wavesoldering SMD-populated boards are of a diﬀerent nature: they arise ﬁrstly from the problem of physically getting the solder to every single joint, and secondly from ensuring that it does not stay behind in the wrong places after the board has emerged from the wave. In other words, it should not leave joints empty or form bridges, solder prills or ‘spider’s webs’ adhering to the board.

4.4.3 Interaction between molten solder and the circuit board Entry of the circuit board into the wave and the ‘shadow effect’ Whether or not the molten solder reaches every single joint on the board is decided at its point of entry into the wave. SMD-populated boards are three-dimensional

job:LAY04 page:24 colour:1

black–text

106 Wavesoldering

(see Section 4.1), with many SMD joints located in recesses at the sides of the components where the surface tension of the molten solder prevents it from reaching them. The air and ﬂux vapours which are trapped between component and solder increase its reluctance to enter such corners. This phenomenon has been named ‘shadow eﬀect’ (Figure 4.11). For instance, the outer ends of the component leads of SOs, e.g. SOT 23 or SOT 143, do not extend beyond an aspect angle of 60° below the top edge of the component body (Section 2.1). In a laminar, non-turbulent wave, the surface tension of the molten solder gives it a circular contour, which cannot reach the entry to the joint. The problem is even worse with PLCCs, where the ends are bent inwards and tucked away under the body of the component. The problem is made worse by the air and the ﬂux vapours which are trapped between the SMD and the advancing solder, without means of escape. The exact way in which the surface tension acts in the case of SMDs and prevents the solder from getting where it is needed has been quantitatively treated by Klein Wassink.

Figure 4.11 The shadow effect

job:LAY04 page:25 colour:1

black–text

Wavesoldering 107

With component leadwires inserted in through-plated holes these problems did not exist: the projecting wire end, once wetted by the solder, pulls it into the hole, and the ﬂux ﬂoating on the advancing meniscus helps it to rise to the top of the board (Figure 4.12). In order to propel the solder into shadow areas of SMDs, it must be given a mechanical impulse of suﬃcient momentum and in the right direction. A number of waves of speciﬁc conﬁgurations and ﬂow patterns, known as chipwaves, have been developed over the years to achieve this (Section 4.3.3). Adapting the layout of the board to the idiosyncrasies of wavesoldering also helps, as will be dealt with in Section 6.4.1.

Exit of the circuit board from the wave and the peelback As would be expected, the circumstances on the exit side of the solderwave determine whether any solder stays behind on a board in the wrong places, mainly in the form of bridges and, if so, where this is likely to happen. Along the line where the board parts from the wave, both surface tension and the cohesive forces within the body of the molten solder play a role. The solder which has wetted the joints and the metallic surfaces of uncoated tracks and the backs of component legs is carried along with the travelling board until its weight overcomes the cohesive forces within the melt and the surface tension which hold it together. This volume of solder which forms in the nip between the back of the wave and the departing board is called ‘peelback’ (Figure 4.13). Soon after the introduction of wavesoldering it was found that peelback, and its tendency to cause bridging and excessive solder pickup, can be minimized by letting the board travel slightly uphill. Over the years, a rising angle of 7 ± 1° has become established worldwide as a useful standard, and it is neither necessary nor advisable to depart from it except under special circumstances. The 7° angle is equally suitable for SMDs. If bridging becomes a problem with close-pitch SMDs which are near the limit of wavesolderability, e.g. 0.75 mm/30 mil, raising the angle to 8° or a little above

Figure 4.12 Wired joint entering the solderwave

job:LAY04 page:26 colour:1

black–text

108 Wavesoldering

Figure 4.13 Peelback

and slowing down the conveyor at the same time might help. With some computer-controlled soldering lines, the optimal conveyor angle, once experimentally determined, can be stored in the control processor and recalled for a given type of board, e.g. by a barcode carried by the board. All these measures aim to make it as easy as possible for the solder to ﬁnd its way back to the wave. The ﬂowpattern of the solder in the wave is an important factor in clean and eﬃcient joint formation. Before SMDs appeared, the so-called ‘asymmetrical’ wave (Figure 4.14) was the most widely used type of wave. On entering the wave, the board encounters the solder as it falls in a smooth, laminar, non-turbulent stream over a weir, moving in the opposite direction to the travelling board. Where the board leaves the wave a few centimetres further on, the solder forms a ﬂat horizontal surface, which ﬂows, again without any turbulence, in the same direction and ideally at the same speed as the board. This is achieved by placing an adjustable weir at the exit side of the wave. In this way, every joint on the board is lifted vertically out of a level pool of solder, the surface of which moves in the same direction and at the same speed as the board. This arrangement minimizes the pick-up of solder by the board. The horizontal ﬂow of the solder surface on the exit side has a further purpose: in the absence of ﬂux, a static surface of molten solder is soon covered by a thin but tough skin of oxide, which can cause bridges and icicles. Though such ﬂux as has survived the passage of the board on its underside can deal with most of the oxide skin, the slow constant movement of the solder surface prevents the oxide from forming a stationary skin. With wired, inserted components, where the distance between leads is normally 2.54 mm/0.1 in, bridging is no problem with a well-adjusted asymmetrical wave, even at conveyor speeds of 2 m/6 ft or more per minute. With SMDs and closely spaced solderpads, these considerations are irrelevant and the cohesive force of the molten solder in the peelback becomes the dominant factor. When the gaps between neighbouring pads are narrower than the pads themselves, the peelback will span a number of pads before the weight of the molten solder carried along with the board overcomes its internal cohesive force and lets most of the solder fall back into the wave (Figure 4.15).

job:LAY04 page:27 colour:1

black–text

Wavesoldering 109

Figure 4.14 The movements of board and solder in an asymmetrical solderwave

Figure 4.15 Peelback and solderthieves

job:LAY04 page:28 colour:1

black–text

110 Wavesoldering

Several eﬀects come into play under these circumstances. With a row of pads aligned parallel to the direction of travel, the peelback jumps from pad to pad until the last two are reached. There is no further pad to jump to and the peelback is reluctant to drain from the last two pads in the row, so a bridge is likely to form between them. This bridging can be prevented by lengthening the last pad in the row so that the suspended solder drains towards the trailing end of the pad, or by adding a blind or dummy pad, called a solderthief, to the end of the row. The thief serves no connecting purpose and renders the bridge, should it form, harmless. If a row of pads lies at a right angle to the direction of travel, the peelback reaches all pads in the row at the same time, and has nowhere to jump to. Therefore, bridging is diﬃcult to avoid between parallel pads which leave the solderwave simultaneously (Figure 4.16). This idiosyncrasy of the solderwave is the reason for the layout rules for SMDs, which are fully dealt with in Section 6.6.1. Placing a multilead component diagonally to the direction of travel of the board is a widely and successfully practised compromise. It is, however, wasteful of space, a serious consideration with the steadily-rising cost of board real estate. For this reason, several makers oﬀers a soldering machines with the solderwave placed at an angle to the direction of travel (Figure 4.17). As the peelback releases its grip on a land or pad, the suspended thread of solder may, as it parts, form one or more small globular droplets of solder. Normally, these drops fall back into the exit pool of the wave, but when soldering is carried out in an oxygen-free atmosphere and with a low-solids ﬂux, they can end up sticking to the solder resist on the underside of the board. This problem is dealt with more fully in Section 4.5.

4.4.4 Chipwaves Double waves As the preceding chapter explains, the way in which a board enters the wave decides whether the solder gets to all the places where it is needed. The manner in which the board leaves the wave on the exit side determines whether any solder remains in places where it is not wanted. The concept of the double chipwave is the logical embodiment of this truth: the ﬁrst or primary wave makes sure that the solder ﬁnds its way to every joint on the board; the second or secondary wave, which follows closely after the ﬁrst one, allows the solder to drain away from the board without leaving any bridges or other unwanted accumulations behind. The primary wave achieves its purpose by providing the solder with a good deal of kinetic energy at the point where it meets the board. Having passed through this wave, the board is somewhat untidy, with some bridging and unsightly joints. These blemishes are tidied up in the second wave, which as a rule is a standard asymmetrical wave as has been described in the preceding section. Its smooth exit conditions iron out the imperfections left by the primary wave. Both waves follow one another as closely as the construction of the soldering unit will allow. Two types of primary wave have by now become established. One is a ‘symmet-

job:LAY04 page:29 colour:1

black–text

Wavesoldering 111

Figure 4.16 Bridging in a row of footprints aligned at right angles to the direction of travel

Figure 4.17 Slanting solderwave

rical’ wave, with an intentionally turbulent wavecrest (Figure 4.18). Its aim is to provide a zone of high kinetic energy with a vigorous, multidirectional ﬂow of solder underneath the board, which propels it into every recess and at the same time ﬂushes out trapped air and solvent vapours. This turbulence is often created by narrowing the nozzle exit so as to accelerate the solder as it is propelled upwards against the board. Sometimes a rotating or pulsating mechanical element is located close to the nozzle exit. The alternative is the so-called jet or hollow wave. Here, the solder is projected obliquely upwards against the underside of the board. The path of the circuit board intersects the parabolic trajectory of molten solder somewhat below its crest. The momentum with which the solder hits the board and the SMDs which sit on it propels it into the recesses where the joints are located. There are two possible kinds of jetwave: with the unidirectional wave, the solderjet moves in the same direction as the board; with the counterﬂow wave, it moves in the opposite direction. It has become customary to use the unidirectional wave with all double-wave machines (Figure 4.19) and the counterﬂow wave on single-jet machines. With the unidirectional wave, where the leading edge of the board intercepts the jet as it travels forward and moves in the same direction as the board, there is no danger of the solder ﬂooding the top surface of the board at the point of entry. It can be advisable, however, to clip a low baﬄe to the trailing edge of the board to prevent the solder from washing over it as it leaves the wave. Many double-wave machines have two pumps, one for each wave, but both

job:LAY04 page:30 colour:1

black–text

112 Wavesoldering

Figure 4.18 Turbulent primary wave

Figure 4.19 Unidirectional jetwave as primary wave

drawing on a common solder reservoir. A jetwave requires a considerable hydrostatic pressure of solder to give the trajectory its required height, which must be maintained with reasonable accuracy. With some makes of chip-soldering machines the primary wave can be switched from turbulent to jet operation without having to ﬁt a new nozzle.

Single counterflow jetwaves A unidirectional wave has an irregular, uneven peelback zone. This leaves the joints well ﬁlled, but with an ill-deﬁned amount of solder, which makes the secondary asymmetrical wave necessary. A counterﬂow wave has one great advantage: there is no peelback, because on the exit side the solder is constantly driven back towards the joints, at a speed which is higher than the speed of forward travel of the board. Since there is no peelback, there is no danger of bridging or excess solder left under the board, and consequently no need for a secondary wave (Figure 4.20). However, provision must be made to prevent the solder from ﬂooding the top surface of the board as it cuts into the wave. This can be done by ﬁtting a deﬂector blade to the leading edge of the carriage which carries the board through the soldering line. The maximum conveyor speeds which can be achieved with a

job:LAY04 page:31 colour:1

black–text

Wavesoldering 113

Figure 4.20 Single-wave soldering with a counterﬂow jetwave

single contraﬂow jetwave are somewhat lower than the speeds of double-wave machines. With one well-known make of single-jet contraﬂow machine (Kirsten, Switzerland), the solder is propelled not by a mechanical impeller pump, but by a so-called Faraday pump, which has no moving parts: a strong magnetic ﬁeld is applied at right angles to the ﬂow of the solder, while an electric current is ﬂowing through the molten solder in its conduit at right angles to both the solderﬂow and to the magnetic ﬁeld. The resultant electrodynamic force propels the solder through the conduit and into the jet nozzle (Figure 4.21).

Combination waves Combination waves manage to combine the functions of both the primary and secondary wave into a single asymmetrical one. This is achieved by creating and conﬁning a zone of mechanically-generated multidirectional kinetic energy within the normally smooth, laminar overﬂow at the point where the board enters the wave. The exit side of the wave follows the normal asymmetrical pattern with a smoothly moving surface. One example is the ‘Omega Wave’© (Electrovert). Here, the energy ﬁeld in the entry zone is produced by a narrow vertical blade which is placed close below the surface of the overﬂow and extends over the full width of the wave (Figure 4.22(a)). This blade oscillates horizontally at 50 Hz/60 Hz at a controllable amplitude, driven by an electromagnetic vibrator. The oscillations create standing waves in the solder overﬂow with an adjustable vertical vector along the line where the board enters the wave. Another example is the ‘Smart Wave’© (Soltec). Here the solder is made to well up in a pulsating movement along the line of overﬂow where the board enters the wave. This movement is produced by a horizontal hexagonal bar which extends across the width of the wave and which rotates at an adjustable speed within a cylindrical baﬄe, just below the surface of the overﬂow. A slot in the baﬄe allows

job:LAY04 page:32 colour:1

black–text

114 Wavesoldering

Figure 4.21 Electrodynamic solder pump (Kirsten)

the solder to well upwards against the board. The speed of rotation of the hexagon determines the degree of turbulence in the wave overﬂow (Figure 4.22(b)). A third example of the combination-wave concept employs no moving elements at all: with the CMS© Wave (Blundell) the solderpump is driven by an electronically-controlled stop–start motor, so that the whole solderstream itself pulsates (Figure 4.22(c)). Both the frequency and the amplitude of the pulses can be varied. Practice shows that the salient parameter is the pulsing rate, which can be suited to the type of SMDs being soldered. As with the other two, the wave itself is of the classical asymmetrical conﬁguration, and with all three types of wave the board lifts oﬀ on the exit side from a smoothly moving stream of solder.

4.4.5 Formation and control of dross In a normal atmosphere, molten solder quickly acquires a tough surface ﬁlm of mixed tin and lead oxides. As soon as the solder is moved or disturbed, the oxide skin ruptures and tangles with the solder underneath. The resultant mix of oxides and clean solder is called dross. Since wavesoldering involves moving solder around and letting it fall back into a bath of molten solder from a certain height, the formation of dross is unavoidable unless measures, which will be discussed later, are taken to protect it from the atmosphere. Physically, dross is a grey, heavy metallic sludge which ﬂoats on top of the solderbath and sets into solid heavy lumps when it cools below 183 °C/361 °F. Chemically, dross consists of between two to ﬁve per cent metal oxide, the rest being clean solder. Normally, dross also contains a certain amount of ﬂux residue,

job:LAY04 page:33 colour:1

black–text

Wavesoldering 115

Figure 4.22 Three examples of combination waves. (a) Omega Wave ©; (b) Smart Wave ©; (c) CMS Wave ©

which results from the ﬂux washed oﬀ the boards as they pass through the solderwave. With rosin-based ﬂuxes of high solids content, ﬂux residues can form a considerable portion of the dross. With low-solids and/or rosin-free ﬂuxes, the ﬂux content of dross falls to insigniﬁcant proportions. On pump-driven units, a small accumulation of black powdery dross is liable to form where the pumpshaft enters the solderbath. This black powder, which consists largely of lower tin and lead oxides, may spontaneously begin to glow and turn into

job:LAY04 page:34 colour:1

black–text

116 Wavesoldering

a grey or yellow powdery mixture of higher oxides. This glowing need not alarm a machine operator; it does not mean that the solder is beginning to burn up and turn completely into dross. The amount of dross which forms on a wave machine depends on several factors: 1. Even minute amounts of zinc, aluminium and cadmium, the so-called ‘skinformers’, can lead to a serious increase in drossing. Copper or iron, if present above their safe limits, can also cause excessive drossing. The safe limits of all these impurities are fully dealt with in Section 3.2.3. If at any time, the formation of dross on a wave machine begins to rise above the usual level without an obvious reason, an immediate check analysis of the solderbath is strongly recommended. As a general rule, the lower the level of impurities in a given solder, the less is its tendency to form dross in a wave machine. Special grades of high-purity solder for wavesoldering are available from the main solder vendors. Some makes of solder are claimed to have special ‘low-dross’ characteristics, due to speciﬁc alloying and melting procedures. A miracle solder which does not dross at all in normal atmosphere is, and will probably remain, an unfulﬁlled dream. Small amounts of added phosphorus (about 0.002%) will reduce drossing to a minimum for a time, but the additive soon oxidizes and disappears. To maintain the eﬀect, regular additions of phosphorus in the shape of phosphor–tin pellets, which are available from some solder vendors, have to be made. This method is rarely practised in industry, because there is a suspicion, though unconﬁrmed, that phosphorus may encourage dewetting of solder on copper. 2. Constructional features of the wavenozzle assembly have a pronounced eﬀect on the drossing characteristics of a given soldering machine. If the solder which ﬂows over the weirs of an asymmetrical nozzle or through the apex of a jetwave is allowed fall back into the solder reservoir from its full height, a great deal of turbulence will arise at its point of impact. A large amount of dross is bound to form, and much of it will be dragged below the surface of the solder, together with some air. In a short time, a thick layer of drossy sludge would form on the bath surface, making soldering impossible. For this reason, the free falling solder is intercepted on most soldering machines by suitable baﬄes and catchment devices, which guide it back to the level of the solderbath with minimum turbulence. 3. Covering all or most of the exposed surfaces of the solderbath with a layer of oil, molten wax, or some other suitable organic substance which does not smoke, smell, oxidize, decompose, polymerize or otherwise misbehave at 250 °C/480 °F is an old-established method of dross control which is still practised. A number of suitable cover oils or waxes are available from most ﬂux vendors. Some of them are water soluble to facilitate their subsequent removal from the boards, should they have contaminated them. For many years, one machine maker (Hollis) provided his wave units with a facility to inject a measured amount of cover oil directly into the pump conduit, where it was dispersed in the solder and emerged in the form of small oil

job:LAY04 page:35 colour:1

black–text

Wavesoldering 117

droplets in the solderwave. This method was very eﬀective in suppressing the formation of dross, but it did leave a slight deposit of oil on the soldered board, which as a rule made cleaning obligatory. Since the advent of wavesoldering in controlled atmospheres (Section 4.5), the use of a cover oil on or in a solderwave is hardly practised any longer. 4. With almost all wave machines, baﬄes or bulkheads are provided at the level of the solder surface to prevent dross, which forms where the solder drops back into the bath, from getting near the intake of the solderpump. Any dross particles sucked into the solderpump are liable to cause trouble: they stick to the sides of the solder conduit and to the pump impeller, and disturb the smooth ﬂow of the solder. This reduces the eﬃciency of the pump, causing the solderwave to drop, ﬂutter or form a ragged crest. Above all, grey or black dross particles appear in the soldered joints, where they constitute a serious soldering defect. Allowing the level of the solderbath to drop below the value recommended by the maker will increase the danger of dross being sucked into the pump circuit. Even with machines ﬁtted with an automatic solderfeed, and with warning circuits to guard against a dangerous drop in solder level, it is worth while checking the solder level visually once a day. With many wave machines, a circular baﬄe surrounds the rotating pumpshaft to stop the dross from reaching the pump inlet. Machine operators sometimes cover the space between that baﬄe and the shaft with a special high-melting wax to prevent the formation of the incandescent powdery dross which has been mentioned above. The amount of dross which arises in the course of a day’s normal running of a wavemachine varies widely. On smaller machines, the daily take-oﬀ of dross can be kept below 1 kg/2 lb. Even on large installations, it should not rise above a few kg or lb per day. An oil cover will of course reduce the amount of dross considerably. A great deal depends on the way in which the machine is operated. If the wave is allowed to run ‘dry’, that is without ﬂuxed boards passing over it, for long periods, more dross will form. This is a good reason for ﬁtting wave machines with sensors, which turn on the wave only when a board approaches, and turn it oﬀ again after it has passed through the wave. Skimming the dross oﬀ the bath surface very frequently, so as to make it look clean and tidy (for example in order to impress passing management or visitors), is counterproductive: fresh dross will quickly form again. If the dross cover is left undisturbed, it protects the bath underneath from rapid further oxidation. As a rule, skimming the bath surface twice a day, e.g. before the midday break and before switching it oﬀ at the end of a shift, is suﬃcient. If within that period the layer of dross becomes so thick as to impede operation, it is time to check the impurity levels of the solder and its temperature. Questions concerning the removal, handling and disposal of dross are dealt with in Section 4.8. In conclusion, all the problems arising from the formation of dross disappear when the solderwave operates in an oxygen-free atmosphere (see Section 4.5).

job:LAY04 page:36 colour:1

black–text

118 Wavesoldering

4.5 Wavesoldering in an oxygen-free atmosphere 4.5.1 Origins and development Normal non-industrial air contains approximately 78 vol % nitrogen and 21 vol % oxygen, the remaining less than one per cent being taken up by the gases argon, carbon dioxide, hydrogen, neon, helium, krypton and xenon, listed in descending order. The habit of almost all metals of acquiring a skin of oxide in normal air, especially when they are molten, is the bane of the life of every practitioner of soldering. Without a ﬂux to free the surfaces of the joint partners and of the molten solder itself from the oxide which covers them, soldering would be impossible. In response to this problem, a large number of ﬂuxes have been developed over the years which cope admirably well with the needs of every conceivable soldering situation. However, during recent years, ﬂux has become an increasingly unwelcome ingredient of the electronic soldering process. The physical presence of ﬂux residues on a soldered circuit board is an impediment to ATE testing with needle probes where it can be a source of serious errors. It also interferes with subsequent coating or encapsulating of the soldered board. The chemical nature of ﬂux residues, being potential electrolytes, makes them unacceptable on boards populated with components of high impedance and close-pitch leads. Hence the growing need to remove the ﬂux residue from soldered boards by a cleaning process. Removing the ﬂux residues with solvents based on chloroﬂuorocarbons (CFCs) was an eﬃcient and relatively simple way of dealing with them, until in the late eighties their serious environmental eﬀects were recognized. Consequently, their use has been phased out (Sections 8.3.5 and 8.3.6). Several alternative cleaning methods have been and are still being developed (Sections 8.3.7 and 8.4), but nobody likes to clean a soldered board unless there is no alternative to it. Cleaning is beset with problems, and its costs continue to rise. Since oxygen is the culprit in this situation, it seemed logical to consider soldering in its absence, without any ﬂux or at least with so little that cleaning is no longer necessary. Soldering in a vacuum is not practicable, but leaving out the oxygen from normal air and soldering in nitrogen, either pure or with other gases added, has been proposed and practised for some time. Attempts to conduct the wavesoldering process in an oxygen-free environment go back several decades. Except for a few specialized soldering tasks, these attempts did not lead to practical and generally applicable methods of wavesoldering until the late eighties. Oxygen-free soldering entirely without ﬂux assumes that all joint surfaces are completely or almost free from oxide before they enter the oxygen-free soldering environment, or that all of them are suﬃciently heavily pretinned so that the molten solder can ﬂow underneath an existing oxide layer (Section 3.4.1). Reducing any existing tin-oxide or lead-oxide layers by adding between 5% and 25% vol hydrogen to the nitrogen soldering atmosphere requires temperatures above 350 °C/660 °F, which are not practicable with normal electronic circuitry. The method is practised with certain hybrid circuits which carry ceramic components only, using a high-melting lead-rich solder and working in an atmosphere consisting of 90% nitrogen and 10% hydrogen (forming gas).

job:LAY04 page:37 colour:1

black–text

Wavesoldering 119

In the recent past, various plasma treatments of assembled circuit boards in specially formulated atmospheres immediately prior to wavesoldering have been described as methods of ﬂuxless soldering. Equipment based on [10] has recently (1993) become commercially available. The term ‘plasma’ describes a volume of gas (which can be normal atmosphere), which is in a state of intense ionization. Plasma treatments have been used for some time for cleaning purposes in electronic manufacture, e.g. for the ‘desmearing’ of drilled holes in circuit boards prior to plating them.

4.5.2 Wavesoldering in nitrogen Machine designs The ﬁrst practical and generally acceptable wavesoldering line which operated in a nitrogen atmosphere was introduced to the market in 1988 (SEHO, Germany, Figure 4.23). It found immediate and wide acceptance. Since then, a number of other leading wavemachine makers have followed suit. The atmosphere in all these machines is practically pure nitrogen, with an oxygen level, often automatically monitored, ideally below 10 ppm. However, many users report that they ﬁnd oxygen levels of 50–100 ppm perfectly acceptable in normal practice, without leading to inferior soldering results, while noticeably reducing nitrogen consumption and consequently running costs. With the SEHO machine, as with several other makes, the complete soldering line, comprising the ﬂuxer, the preheating zone and the solderwave unit, operates in a nitrogen-ﬁlled tunnel. The ﬂuxer need not necessarily be located inside the nitrogen tunnel. Placing it upstream of the tunnel entrance allows a wider choice of ﬂuxer systems, for example standard sprayﬂuxers. However, the preheating stage, which follows the ﬂuxer, should, for reasons which will be explained later, always be accommodated within the nitrogen tunnel upstream of the wave or waves. Where the boards enter and leave the tunnel through horizontal slots at both ends, the nitrogen unavoidably leaks away through them and needs constant replenishment. Consequently, all nitrogen wave machines are provided with one or more strategically placed nitrogen inlets, which admit metered amounts of the gas. The amount of nitrogen loss can and is being minimized with many designs through

Figure 4.23 Wavesoldering under nitrogen (SEHO, Germany)

job:LAY04 page:38 colour:1

black–text

120 Wavesoldering

careful dimensioning of the ports and by controlling the pressure of the nitrogen feed. Reported or claimed nitrogen consumption is normally at about 20 cub. m/ 550 cub. ft per hour (SEHO). Some makers oﬀer conversion kits for retroﬁtting existing soldering lines to working with nitrogen. These conversions may take the form of installing a nitrogen tunnel to cover the whole length of the soldering line, or they provide a hood which covers the waveunit only. By ﬂooding the wave with nitrogen only when a board passes through the machine, gas consumption can be drastically reduced.

The advantages to be set against these costs are considerable. Several makers of nitrogen-ﬁlled wavesoldering machines claim that the additional investment necessary for the nitrogen facility can be written oﬀ in a comparatively short time through the saving gained by the elimination of dross and the consequent loss of solder. There is general agreement that dross formed on a wave running in nitrogen is only a small fraction of the dross created by the same solderwave in air. For one thing, this drastically reduces the solder consumption and thus the running costs of the soldering line. For another, weekly servicing can replace the twice-daily routine of dross removal and machine cleaning. The virtual absence of drossing means that oil cover is no longer needed when working in nitrogen; in fact if it were used, its vapours would severely contaminate the whole system. Many users report that they operate their nitrogen machines with a drastically pruned maintenance schedule and a consequent reduction in down time. The most valuable trade-oﬀ with nitrogen wavesoldering is the virtual elimination of bridging. This has extended wavesolderability to components with a pitch approaching 0.5 mm/20 mil and thus has shifted the balance of the wave-versusreﬂow decision to some extent back towards the solderwave (Sections 5.1.1 and 5.9).

The solderwaves There is evidence that the nitrogen atmosphere increases the surface tension of the molten solder, as witness its reduced tendency to form solder bridges. This means that more kinetic energy is needed to push the solder into the recesses of SMD populated boards than would be needed for soldering in normal air. In consequence, the double wave on some nitrogen machines comprises a primary turbulent wave followed by a composite wave with a vibrating wavecrest (Section 4.4.4). This arrangement is claimed to help the solder to rise through the full length of throughplated holes and form a good meniscus at the top end.

Fluxes and fluxers As was pointed out above, nitrogen does prevent the molten solder from oxidizing, but it cannot free the surfaces of component leads and solderpads from their existing and unavoidable cover of oxide. Only the above-mentioned plasma precleaning treatments may be able to do that and thus make truly ﬂuxless soldering possible. Meanwhile, ﬂux is still needed, but given the usually good solderability of both

job:LAY04 page:39 colour:1

black–text

Wavesoldering 121

components and circuit boards, ﬂuxes for soldering under nitrogen can be weaker and thinner than ﬂuxes for working in air. Initially it was hoped that formic acid, an organic acid with a very simple structure and a boiling point of 100.5 °C/212.9 °F would be ideal. It could even be injected into the soldering tunnel together with the nitrogen, and would form a ﬂuxing vapour in the hot atmosphere. Provided the boards are hotter than 100 °C/212 °F as they leave the tunnel, there would be no ﬂux residue at all. Unfortunately these hopes were not fulﬁlled: the formic acid vapour did not remove the oxide from all component leads, while it increased the surface tension of the molten solder to such an extent that its ﬂow into the joints was seriously aﬀected. Moreover, formic acid has a very sharp, penetrating odour, which can be unpleasant if too much of it escapes through the entry and exit ports. Finally, its health aspects have come under suspicion. For these reasons, formic acid has fallen into disfavour, even as an adjunct to more conventional ﬂuxes, and US speciﬁcation ANSI/J-STD 004 expressly excludes it from its list of possible soldering-ﬂux ingredients. For some time, adipic acid in a weak alcoholic solution was a favourite alternative to formic acid. Adipic acid is a slightly more complex organic acid, which forms white crystals with a melting point of 153 °C/307 °F. It is a popular activator of rosin ﬂuxes and also a frequently used ingredient of many low-solids ﬂuxes. Its ﬂuxing action is adequate, but in due course more complex ﬂuxes have been found which give better soldering results, while being less demanding as far as perfect solderability of all component leads was concerned. Ten years of experience have established that wavesoldering in a low-oxygen atmosphere with low-solids and no-clean ﬂuxes (see Section 3.4.5) can give consistently high quality joints and low reject rates on surfaces of average solderability. There is one proviso: while the ﬂuxer may be located outside the protective atmosphere, the preheating stage must be inside. Otherwise a potentially vulnerable surface, protected only by a thin coating of a weak ﬂux, may start to oxidize too much for the ﬂux to cope when the board reaches the wave. Operating the ﬂuxer within the nitrogen cover narrows the choice of the ﬂuxing system. Foamﬂuxers and compressed-gas atomizers would need nitrogen as their driving gas, in quantities which would aﬀect the economics of the machine. In consequence, most nitrogen wavesoldering machines use one of the ultrasonic atomizing systems which have been described in Section 4.2.1. Another option is a sprinkling ﬂuxer as described in Section 4.2.1, Figure 4.6.

The vices and virtues of wavesoldering under nitrogen One of the problems of wavesoldering in a nitrogen atmosphere is the appearance of small globules of solder, which adhere to the underside of the board. Why they appear and how they can be avoided has been and continues to be the subject of many technical papers and public discussions, but no ﬁrm conclusions or recommendations have emerged to date. It seems agreed that they originate at the point where the solder in the peelback on the exit from the second wave breaks up. As the last thread of molten solder parts, some of it tends to form one or more separate small drops (Figure 4.24).

job:LAY04 page:40 colour:1

black–text

122 Wavesoldering

Figure 4.24 Breakup of the peelback

It is now generally accepted that in a nitrogen atmosphere molten solder has a higher surface tension than in air. Also, because the absence of any oxide skin makes it more mobile, the kinetic energy released by the breakup of the peelback has a more pronounced eﬀect under nitrogen than it would have in air. Moreover, any ﬂux residue present at that moment would be in the form of ﬁne dust rather than of a coherent skin, and therefore would not impede the mobility of the solder either. The latter argument is supported by the observation that the more rosin a ﬂux contains, the less solderballing there is. This of course runs counter to the whole reason of nitrogen wavesoldering, which aims at a minimum of ﬂux with a minimum of rosin, if any at all. An explanation why these small drops should decide to ﬂy upwards towards the board has to assume an electrostatic charge, a not unreasonable assumption in a situation which is essentially an atomization process. Finally, why do they stick to the board once they hit it? It is an observed fact that solderballs are only found on the solder resist, be it lacquer or ﬁlm, but hardly ever on a bare board surface. Van der Waals forces furnish a plausible explanation for the following reasons. It is a known fact that, in the absence of ﬂux, molten solder wets the underside of a board and sticks ﬁrmly to it after it has set solid. Equally, it is known that molten solder wets clean glass and ﬁrmly adheres to it after solidiﬁcation. The same forces might very well be assumed to act in the case of a droplet of molten solder which hits the smooth solder resist, ﬂattens a little on impact before it solidiﬁes and is held fast on its small but equally smooth interface. Unlike the smooth, unstructured surface of glass or solder resist, both of which are basically undercooled melts, the surface of the board laminate is structured, consisting of a large number of microscopic peaks. The high surface tension of a droplet of solder which hits the laminate prevents it from conforming to the irregular surface of the laminate. A large number of point contacts replaces the smooth interface, and the van der Waals forces cannot act. A few countermeasures against solderballing can be derived from this hypothesis of its causes. Raising the rosin content of the ﬂux has proved to be helpful, but this expedient runs counter to the whole purpose of soldering under nitrogen. The abrupt tearing of the thread of solder in the peelback can be softened by replacing all straight edges of solderpads which run at right angles to the direction of board travel by pointed peaks. This measure require pre-knowledge of the board’s direction of travel, and it occupies valuable board real estate (Figure 4.25). Another measure which suggests itself would be a drastic reduction of the area covered by the solder resist. If the solder resist were to cover only the conductor

job:LAY04 page:41 colour:1

black–text

Wavesoldering 123

Figure 4.25 Shape of solderpads to minimize solderballing

tracks and any other metallic surface which must not be tinned by the solder, solderballing would be much reduced. Above all, it would be conﬁned to areas where solderballs do not pose a risk of short circuits or reduced insulation values, as is for example the case between closely spaced solderpads. Finally, accepting it as true that solderballs originate in the peelback, and considering that a counterﬂow jetwave has no peelback, why are there no nitrogen wavesoldering machines ﬁtted with a counterﬂow jetwave, at least as a secondary wave? How dangerous or undesirable solderballs really are is still a matter of debate. At all events, a motorized brushing unit for removing them mechanically is on the market (Ascom, Switzerland). This unit consists of sets of rotary brushes set both parallel and at right angles to the direction of board travel, and is ﬁtted with an exhaust to collect the loosened solderballs. The higher surface tension of the molten solder in the absence of atmospheric oxygen has a further consequence: a high surface tension means that more force is needed to overcome the ‘shadow-eﬀect’ and to push the molten solder into the awkward corners next to some SMDs like for example PLCCs (see Section 4.4.3, Figure 4.1.1). Therefore, the crest of a solderwave which works under nitrogen may require some extra kinetic energy to ensure that the solder reaches every joint. This must be borne in mind when retroﬁtting a nitrogen hood to an existing wave machine.

The virtues of wavesoldering under nitrogen are proven and can be precisely deﬁned. Because the boards are heated in a protective atmosphere after ﬂuxing, and because there is no oxide skin on the solderwave, ﬂuxes with low levels of activation and low solids-content give equally good if not better results, than strong ﬂuxes do in normal air. This means that ‘no-clean’ ﬂuxes (see Section 3.4.5) can be used without reservation on boards of normal solderability. For instance, it has been reported that when soldered in a low-oxygen atmosphere, plain copper lands, covered with one of the ‘organic solderability protection’ coatings (OSP, see Section 6.4), give soldering results at least equal to those obtained on hot-tinned copper soldered in normal air. Thus, the process window of the wavesoldering process is considerably widened by operating the wave under nitrogen. This means a considerable reduction in corrective post-soldering work, and in turn lower costs and a greater life expectancy of the product.

job:LAY04 page:42 colour:1

black–text

124 Wavesoldering

The residue from modern no-clean ﬂuxes fulﬁls the safety requirements of most users of electronics assemblies, with the exception of some military or medical equipment, or of circuitry exposed to extreme environmental conditions. This means that far fewer products need to be cleaned after soldering than previously. All users are agreed that with soldering under nitrogen, the incidence of faulty or skipped joints has been drastically reduced. The consequent saving in rework, together with the reduction of dross losses and the savings in maintenance costs and down-time,are reported to oﬀset the cost of the nitrogen and to enable the writing-oﬀ of the machine and installation investment within a reasonable time, depending of course on the usage of the equipment. As far as skipped joints are concerned, users as well as machine vendors agree on several points. The solderability of all joint surfaces must be impeccable, especially with leadwires, throughplated holes and vias. Also, the double-wavesystem must be ﬁnely tuned to suit the demands of the three dimensional board geometry for each particular board pattern to obtain the optimal results which the nitrogen concept as such is capable of achieving. Finally, as has been said already, users report that with soldering under nitrogen, the pitch of the component leads, which allows wavesoldering without the danger of bridging, has been extended downwards. When wavesoldering in normal atmosphere, bridging is diﬃcult to avoid with a footprint pitch below 0.65 mm/26 mil. In a nitrogen atmosphere, bridge-free soldering is no problem with that pitch, and good results have been reported with 0.5 mm/20 mil pitch.

Wavesoldering under a cover of hot glycerine flux An example of wavesoldering in a non-atmospheric oxygen-free environment, if not an atmosphere, merits mentioning here. In the 1960s, IBM conceived a method of wavesoldering under a cover of a high-boiling ﬂux based on glycerine (boiling point 290 °C/554 °F). The ﬂux is a 10 per cent solution of EDTA (ethylene diamine tetra-acetic acid) in glycerine, a reasonably eﬃcient, halide-free, waterwashable ﬂux. The solder chosen is the tin–bismuth eutectic (43% Sn, 57% Bi) which has a sharp melting point at 138 °C/281 °F, and forms strong joints on copper. An alloy with a lower melting point than that of the tin–lead eutectic has been chosen so as to be able to run the wave well under the boiling point of glycerine, which starts to decompose when it boils. The operation is in fact run at temperatures well below 250 °C/480 °F. It is used for the wavesoldering of a type of board which carries no SMDs. IBM have developed a dedicated type of wavesoldering machine in which the wave, complete with its metal pump and the board conveyor system, is fully immersed in the hot ﬂux. The company have made the information on which the system is based generally available.

Wavesoldering in a vapourphase atmosphere It is known that the amount of oxygen present within the saturated working vapour of a vapourphase soldering system is normally well below 5 ppm (private

job:LAY04 page:43 colour:1

black–text

Wavesoldering 125

communication from Mr Russ Wood, BNFL Fluorochemicals Ltd). The reason is the high speciﬁc density of the vapour, which displaces the normal atmosphere by its gravity. A patented wavesoldering process, jointly developed by IBL (Germany), Kirsten (Switzerland), and the Berlin Fraunhofer Gesellschaft, uses this fact to shield a solderwave from atmospheric oxygen, by operating it within the saturated vapour of a working ﬂuid instead of surrounding it with nitrogen. A prototype soldering system based on this concept was shown at the 1997 Productronica in Munich. According to a preliminary description, the circuit boards, carried on horizontal frames, pass through a ﬂuxing and preheating stage before entering a soldering chamber, where they are lowered into the saturated vapour of a normal working ﬂuid, with a boiling point of 215 °C/420 °F. Moving on a horizontal track through this vapour, they pass through the crest of a Kirsten counter-ﬂow solder-jet wave. They are then lifted clear of the vapour, and having left the soldering chamber pass through a cooling stage (Figure 4.26). The system as it is described should be capable of dealing with most of the usual board-soldering tasks with one single piece of equipment. With the solderwave in operation, boards with inserted components only, or with a mixed population of inserted components and SMDs, can be soldered in one single pass: SMDs sitting on the upper side of the board are being reﬂowsoldered, while the wired joints underneath the board pass through the wave. With mixed-population boards, carrying SMDs glued to the underside (boards of type Ia and Ic, Figure 5.2, Section 5.1.1), the contra-ﬂow Kirsten jet-wave is well capable of soldering their joints (Section 4.4.4). When soldering boards carrying SMDs only, the solderwave is switched oﬀ, and the machine operates as a simple in-line ‘new-generation’ vapourphase reﬂowsoldering system (Section 5.4.5). An added bonus is the fact that, when having to use a lead-free solder with a melting point other than 183 °C/361 °F, vapourphase soldering, as is pointed out in Section 3.2.2 (lead-free solders), is the least problematical strategy, oﬀering a choice of working ﬂuids with a range of diﬀerent boiling points.

Figure 4.26 Wave soldering in a vapourphase atmosphere: 1, spray ﬂuxer; 2, preheating; 3, solder wave; 4, working vapour; 5, cooling stage

job:LAY04 page:44 colour:1

black–text

126 Wavesoldering

4.6 Board conveyor systems 4.6.1 Functional requirements Boards must travel through a wavesoldering unit at a known, controllable and steady speed, without jolts or periodic ﬂutter. While they traverse the solderwave(s), their line of travel must be accurately deﬁned and reproducible from board to board. Unless these conditions are met, the quality of soldering is bound to be erratic, however eﬃcient and well controlled the ﬂuxer, the preheating unit and the solderwaves may be. Furthermore, jolts or a rough ride while the joints solidify after their passage through the wave will spoil their appearance and may cause incipient cracks within the joints themselves. The conveyor is an essential part of a wavesoldering unit, and it must be a carefully designed, sturdy piece of precision engineering. On most machines, boards travel on one single continuous conveyor from one end of the machine to the other. Because the depth of immersion of every part of the board surface in the wavecrest critically aﬀects the soldering result, geometrical precision matters most where the boards travel over the crest or crests of the wave. Here, the position of every board in the vertical axis must be deﬁned, in reference to both its longitudinal edges, to within ±0.3 mm/12 mil. Assuming the wavecrest to be straight and horizontal, any sideways tilt of the board relative to the wavecrest must also be held within these limits. They should not be exceeded, because some unsteadiness of the wave, and warping and bowing of the board itself, must also be accommodated. The travelling speed of the boards need not be numerically deﬁned or known to within less than a few per cent. What matters is that it should not drift upwards or downwards by more than those amounts without automatic correction or at least a warning. The conveyor speed must be reliably monitored and displayed. The preferably tachometrically controlled conveyor drive must be free from slip, and should not be aﬀected by variations in the mains voltage.

4.6.2 Board-handling systems Individual board carriages or pallets Board carriages which grip a single board, or at most two boards of equal width in tandem, between two opposed, sprung longitudinal clips have been around since the beginning of wavesoldering (Figure 4.27). Their evolutionary development since then has been conﬁned to reﬁning their design and making them lighter. The clips are made from an unsolderable metal, such as stainless steel, sometimes chromium-plated steel, rarely sheet-titanium. They grip the boards between V-shaped jaws. The adjustable distance between the clips is set manually, with the correct lateral pressure against the sides of the board being judged by the operator: if it is too loose, the vertical position of the board in the V-jaws is ill deﬁned; if it is too tight, the board, which softens and expands in the preheater and above all during its passage over the wave, is liable to bow, causing an uneven depth of immersion across its width. With particularly wide or heavily laden boards, this eﬀect can be mitigated by clipping temporary stiﬀening edges to the leading, and sometimes also to the

job:LAY04 page:45 colour:1

black–text

Wavesoldering 127

Figure 4.27 Board carriage

trailing, edge of each board. Every board is manually loaded into its carriage by snapping it into the jaws of the sprung clips. Unloading is manual too. Carriages which provide for quick-action loading and unloading are available with some high-performance equipment. This handling of individual boards on unloading after soldering has one very important point in its favour: every single board is seen by an operator before it leaves the soldering machine for storage or the next manufacturing step. This means that a malfunction of the soldering machine, which does not automatically set alarm bells, if any, ringing, such as a collapsed foamwave, a blocked sprayﬂuxer or an uneven solderwave is spotted at once, and not after a number of scrap boards arrive at the next workstation, which may be distant from the soldering machine in both space and time. The carriages may either glide along the conveyor on rails, being pulled on either side by an endless link chain, or else their sides rest on endless moving fabric belts. The latter arrangement avoids mechanical damage to carriage and drive should one or more carriages jam. A conveyor must of course have a fail-safe provision which prevents a board coming to rest in the preheating section or over the solderwave without immediately switching either of them oﬀ. Because of the close tolerance with which the board must travel over the wave, board carriages are pieces of precision engineering, which must sit securely on the guide rails without rocking. Should one be dropped accidentally, it must on no account be put back on the line before being closely checked for its correct alignment, preferably by the works’ toolmaking department. Since the holding clips pass constantly through the ﬂuxer and the wave, board carriages must be cleaned regularly to prevent buildup of ﬂux residues which, especially with rosin ﬂuxes, can become almost insoluble after a number of passages through the solderwave. Passing the carriages through the board-cleaning installation, if one is available, at regular intervals, will suﬃce. Alternatively, cleaning equipment for board carriages is on the market.

Finger conveyors Board carriages represent a considerable investment, especially on large soldering lines, and their manual loading and unloading interrupts the smooth ﬂow of an automatic production line. For this reason ﬁnger conveyors (Figure 4.28) have

job:LAY04 page:46 colour:1

black–text

128 Wavesoldering

Figure 4.28 Finger conveyor

become the dominant technique. By now they have evolved into sophisticated and ﬂexible systems, which ﬁt in easily with integrated automatic production lines. The boards are carried between sprung individual ﬁnger clips, which are mounted on two endless link chains running along either side of the conveyor. The distance between the chains can be varied, manually or mechanically, to suit the width of the boards passing through the machine. With computer-controlled machines, the conveyor width can be called up together with all the other preset operating parameters, to suit a given batch of boards. The ﬁngers themselves are almost always made from titanium, which is untinnable with any type of ﬂux. A good deal of development has gone into the shape of the ﬁngers themselves to ensure that the position of the underside of the board in relation to the chassis of the machine is accurately deﬁned, without undue pressure against the sides of the board. One maker (Sensbey) has designed the ﬁngers as chucks, which release their lateral hold as the board passes over the wave while still deﬁning their vertical position. This allows the board to expand in the soldering heat without warping. Chain conveyors are, or should be, equipped with a mechanical cleaning device for each chain, normally a rotary brush, to prevent buildup of ﬂux residue on the ﬁngers, which would interfere with their function and accuracy.

Soldering templates Soldering mixed batches or short runs of circuit boards may need frequent resetting of the holding clips in every board carriage, or changing the distance between the conveyor chains. Sets of templates or frames with a milled or sawed aperture which corresponds to the outline of a given type of board are frequently used to cope with this situation (Figure 4.29). These frames are conveniently made from thick FR4 (2–4 mm/100–200 mil thick), with holding clips and lugs, as illustrated, and with ﬁngerholes to facilitate the loading and unloading of the boards. They are also very useful for dealing with boards with irregular, non-rectangular contours. The ﬁt of a board in its template aperture should of course not be too tight, but must allow for the expansion of the board during preheating and soldering. A set of templates made from good-quality FR4 will last for a year or more, even with constant use, if not maltreated.

job:LAY04 page:47 colour:1

black–text

Wavesoldering 129

Figure 4.29 Soldering template

Board-handling robots and selective solderwaves Several vendors oﬀer handling robots which grip the edges of a board, and which can be programmed to move over the crest of a solderwave along a non-linear path and with a non-constant speed. The idea is to provide the optimum wavesoldering parameters for every section of a board with complex and non-uniform soldering requirements on diﬀerent parts of its surface. Such handling robots require a considerable investment in both hardware and programming, and the niche they may have found is a narrow one. Another niche technology is the selective solderwave. This is a small wave, up to perhaps 5 cm/2 in wide, which can be used to solder a group of wire-terminals or a small edge-connector to a board which has already gone through its soldering process. The board may be hand-held against a ﬁxture, or it may be oﬀered to the wave by a robot handling system. Soldering individual components to threedimensional substrates (Section 6.2) is a further potential use for selective wave soldering. A facility to ﬂood the wave with nitrogen during soldering is oﬀered by several specialist vendors.

job:LAY04 page:48 colour:1

black–text

130 Wavesoldering

4.7 Wavesoldering practice 4.7.1 Operating parameters and their role Wavesoldering has more variable parameters than any other soldering method. Furthermore, most of these parameters are interdependent in their eﬀect on the soldering result. Their list makes formidable reading: E E E E E E E E E E E E

Angle of the conveyor towards the horizontal Conveyor speed Type of ﬂux Density, water content and freshness of the ﬂux Amount of ﬂux deposited per unit of board area (provided the machine allows for the variation of this parameter) Intensity of preheat Composition of the solder Impurity level of the solder Solder temperature Height and stability of the solderwave, as governed by the speed and the running behaviour of the solderpump Proﬁle and ﬂowpattern of the solderwave, as governed by the setting of the wavenozzle weirs Depth of immersion of the board in the crest of the solderwave

Several of these parameters are best decided on once and for all, and not changed thereafter: 1. The standard conveyor angle of 7° towards the horizontal is the result of many years of wavesoldering experience, and it should not be altered except for some special reasons, which will be discussed later. The angle is best left alone, and several machine makers recognize this fact by selling their machines with a conveyor rigidly ﬁxed at 7° towards the horizontal. 2. Choosing the right type of ﬂux for a given production line, soldering task or type of board involves a great deal of eﬀort, time, and very often expense. The type, layout and solderability of the board, the standard and constancy of component solderability, the cleaning, testing and postsoldering treatments and circumstances, and the ﬁnal use of the soldered assembly all determine the choice of ﬂux. Once this choice has been made, with ﬂux vendors, production managers, purchasing and quality control all having cooperated in the task (or not, as the case may be), the ﬂux speciﬁcation should not be changed except under dire necessity. Even with a quite small company, changing the ﬂux involves much time, eﬀort and cost in checks on corrosion, performance and quality. With a large organization, changing a ﬂux speciﬁcation may take up to a year to ﬁnalize and can cost very large sums of money indeed. 3. The choice of solder is simpler than the choice of ﬂux. Over the years, a solder alloy of eutectic composition, containing 63% of tin and little if any antimony, has been found to be universally suitable for almost every soldering task (see Sections 3.3.1 and 3.3.2). Unless special circumstances or a speciﬁc customer

job:LAY04 page:49 colour:1

black–text

Wavesoldering 131

demand a solder with a diﬀerent melting point or maybe a certain percentage of silver, the user will be well advised never to change the speciﬁcation of his solder. The upheaval which would be caused by changing from the standard tin–lead solder to a lead-free one (Section 3.2.3) explains the general reluctance of the industry to adopt a lead-free technology, unless forced to do so. 4. The standard wavesoldering temperature of 250 °C/480 °F plus or minus a few degrees is, like the conveyor angle, the result of over four decades of practical wavesoldering experience. Without a compelling need, it is advisable not to depart from it.

4.7.2 Choosing and monitoring operating parameters Condition of the flux Given that the choice of ﬂux is settled, the contents of the ﬂuxer should at all times match the density and/or the acid value which is speciﬁed in the vendor’s data sheet. Section 4.2.2 discusses in detail how this requirement can be met, by automatic equipment if required. It is worth restating at this point that the success of wavesoldering depends critically on the consistent quality of the ﬂux, and that this constancy is assured more easily with sprayﬂuxers than with foamﬂuxers.

Amount of flux per unit of board area This parameter also aﬀects the soldering success, though to a lesser degree than the density and the activity of the ﬂux. Too much ﬂux means more solvent in the ﬂux cover and, unless the preheater is adjusted accordingly, a risk of boiling and solder-prill formation as the board passes through the solderwave. If boards have to be cleaned after soldering, too much ﬂux reduces the cleaning eﬃciency. Too little ﬂux, uneven ﬂuxcover or, worse, unﬂuxed patches inevitably cause soldering faults, such as bridges, icicles, solder adhering to the board and open joints, especially with low-solids ﬂuxes. With these, the margin of error is much narrower than with high-solids ﬂuxes. The thickness of the ﬂux cover can be controlled to some extent with the various types of sprayﬂuxer, but foamﬂuxers permit very little, if any, control over this parameter. At the time of writing (1997), there is no equipment on the market for automatically monitoring the thickness of the ﬂux cover. A frequent visual check of the overall appearance of the soldered boards is the best method of ensuring the stability of this important factor. Automatic video surveillance of the output of a soldering line should be capable of giving warning of a malfunction of the ﬂuxing unit.

Intensity of preheating Insuﬃcient preheat leaves too much solvent in the ﬂuxcover, which is therefore more liable to be washed oﬀ in the solderwave, leading to bridging or open joints. This factor is particularly critical with double waves, where a substantial portion of

job:LAY04 page:50 colour:1

black–text

132 Wavesoldering

the ﬂux cover must survive the passage through the ﬁrst, turbulent wave. Moreover, if the board is too cool, the solder may not rise through all plated holes and form the required solder meniscus on the upper board surface. Too sharp a preheat can cause trouble with rosin-based ﬂuxes: overbaking such a ﬂux will cause the rosin to polymerize. This reduces its mobility, so that it may obstruct the solder in tinning all solderpads or in rising to the top surface of the board. It will certainly make cleaning less eﬃcient. By contrast, ﬂuxes with a low solids content and very little rosin, and the so-called ‘no-clean’ ﬂuxes (Sections 3.5 and 8.1) which are mostly rosin-free, require more intense preheating to ensure that the ﬂux coating is not washed oﬀ in the double solderwave. With these ﬂuxes, most vendors suggest that the underside of the board should have a temperature of 120 °C/250 °F on emerging from the preheating stage. The methods of controlling the intensity of preheating are dealt with in Section 4.2.3.

Parameters of the solderbath and the wave The level of molten solder in the machine should at all times be kept strictly at the height recommended by the maker. Many machines are ﬁtted with an automatic solder feeder, which maintains the correct solder level. Failing an automatic level control, the solder level must be regularly checked at intervals depending on the usage of the machine, and if necessary topped up. Unless ﬁtted by the maker, it is advisable to install a simple solder-level sensor, which gives an audible or visible warning as soon as the solder level drops below the maker’s danger mark. If the solder level drops too low, dross and ﬂux-residues which ﬂoat on the solderbath can be sucked into the inlet of the solderpump. Once in the solder stream, they tend to deposit on the solder conduits and the pump impeller. These deposits interfere with the steady running of the solderwave, as will be discussed below. Particles of dross and ﬂux which reach the wave nozzle emerge in the wave as small, but conspicuous, black spots, which pop up in the wavecrest and ﬁnish up on the surface of the solderjoints. Such dross or ﬂux inclusions do not necessarily threaten the function or reliability of the aﬀected joints, but they are a legitimate cause of rejection by quality control or by the customer. The temperature of the solder is one of the most basic wavesoldering parameters. The general suitability of 250 °C/480 °F for most wavesoldering tasks has been mentioned already. Close adherence to this value is less critical than is often assumed, an accuracy of ±2–3 °C/4–6 °F being quite suﬃcient. It is much more important to guard against a slow, unnoticed upward or downward drift of the solder temperature away from its set value. The temperature readout on the control panel of the machine, together with its warning signals, may be misleading: software or functional errors are not unknown. The safest way to guard against this danger is to check the actual solder temperature halfway through every working shift by checking it with a reliable, preferably occasionally re-calibrated, handheld temperature measuring instrument, with its sensor placed in the solderwave about 5– 10 mm/0.25–0.5 in below the crest.

job:LAY04 page:51 colour:1

black–text

Wavesoldering 133

The height of a wavecrest is directly linked to the speed of the solder pump, which with most good machines has a slip-free, tachometrically controlled drive which is protected against variations in the supply voltage. The waveheight and its consistency across the whole width of the wave can be checked very simply by sliding a piece of plain FR4, with gradations marked on it, across the length of the wavenozzle while the pump is running (Figure 4.30). It is advisable to carry out this simple check at the beginning of every shift. Some computer-controlled machines are ﬁtted with a sensor-operated surveillance of the height and integrity of their solderwave(s). The depth of immersion of a board into the crest of the solderwave is normally equivalent to the thickness of the board. It is therefore important that the underside of the board is strictly parallel to the line of the wavecrest to well within this measure. This is easily checked by letting a piece of plain FR4 without copper lamination, as wide as the largest board, run across the wave and stop brieﬂy over the wavecrest. The ﬂattened wavecrest will be clearly visible through the translucent FR4. If the board is parallel to the wavecrest, the width of the band formed by the ﬂattened wave will be the same across the whole breadth of the testboard (Figure 4.31). If the board is not parallel to the wavecrest, the whole conveyor must be tilted sideways until a parallel position is achieved. Provisions for carrying out this adjustment are, or should be, a feature of every wavesoldering machine. As an alternative to the FR4 board, many machine vendors can supply a plate of heatresistant borosilicate glass which carries a pattern of parallel lines to make it easy to check the width of the wavecrest across the plate. To make sure that the glass plate does not crack during this manoeuvre, it is advisable to pass it over the ﬂuxer and the preheater before arresting it over the wave. With FR4, this is not necessary. Uneven or rough running of the solderwave, such as ﬂuttering of the

Figure 4.30 Checking the wave height. : Conveyor angle

job:LAY04 page:52 colour:1

black–text

134 Wavesoldering

Figure 4.31 Checking depth of immersion and horizontal alignment between wavecrest and board

waveheight, can be a sign that deposits of dross or ﬂux residues have formed on the pump impeller or the solder ducts, often as a consequence of an unduly low solder level in the machine (see above). With all jetwaves, even quite small accretions of dross or ﬂux residue in the exit slot of the wavenozzle can ruin the smooth proﬁle of the solderjet. The wavecrest becomes ragged. One big dross particle can depress it by quite large amounts, naturally leading to serious soldering defects. Regular cleaning of the nozzle aperture is an important requirement with all jetwaves. It is best carried out by drawing a scraping tool, made from soft steel or PTFE, along the whole length of the nozzle aperture. Most vendors can supply suitable implements for the purpose. A scraper made from aluminium, brass, copper or hardened steel should on no account be used. With all double-wave machines, the second wave is of the ‘asymmetrical’ type (see Section 4.4.4). On the exit side of this kind of wave, the board lifts oﬀ from a horizontal pool of solder, whose surface moves in the same direction and ideally at the same speed as the board on its conveyor for reasons which have been explained already (see Figure 4.14). The match between these two speeds can be checked simply by ﬂoating a small steel ball, for instance from a ball bearing, on the solder surface and comparing its movement with that of the board conveyor.

job:LAY04 page:53 colour:1

black–text

Wavesoldering 135

Conveyor speed The conveyor speed is a critical wavesoldering parameter. On the one hand, the heat received by a board is inversely proportional to the speed at which it travels through the preheating unit at a given setting of the heater panels. On the other hand, the maximum practicable soldering speed of a wave machine is governed not only by the ability of the solderwave to get the necessary amount of heat into the board within the time available for this, but also by the complexity of its pattern and the density of its population of components. Furthermore, multilayer boards with high heat capacity must travel more slowly than simple single-layer boards. Boards with closely set SMDs and ﬁne-pitch multilead components must travel over the wave more slowly to give the solder a chance to ﬂow into the narrow gaps between neighbouring components, and to drain away from the ﬁne pattern of leads. With most soldering machines, the set and the actual conveyor speed are displayed on the control panel. Nevertheless, it should be part of the machineminder’s task to check the actual against the displayed conveyor speed of the machine once every day, with the aid of a stopwatch and a simple marker, travelling on the chain conveyor over a measured distance marked on the conveyor rail. This very simple test can save hours of expensive rework of boards, should the conveyor speed have drifted from its set value, or should the machine control have started to malfunction.

Computer-controlled soldering machines The large number of interlinked operational parameters makes wavesoldering a natural subject for computer control, which generally has two tasks. The ﬁrst task is the monitoring and stabilizing of all parameters, which will have been established as optimal and stored in the program. It is worth saying again that this automatic pilot does not relieve the operating personnel from periodically verifying that the machine does in fact run correctly. The functions which must be watched are those which are diﬃcult if not impossible to monitor by sensors, such as the behaviour of the foamwave, the spraypattern of the ﬂuxer and the correct behaviour of the solderwave. The second task relates to parameters which can be adjusted to suit a given type of circuit board. The main parameter here is the conveyor speed, which can be raised with boards of simple pattern and modest thermal requirements, or which may need lowering for complex or multilayer boards. Linked to this is the intensity of preheat. Low-temperature emitters respond slowly to a change in heater current (see Section 4.3.2), and this factor must be considered in the program. Alternatively, the inclusion of one or more high-temperature emitters in the preheating unit will permit a much faster response to the commands of the computer. Some types of machine allow for a choice between foamﬂuxing and sprayﬂuxing to suit diﬀerent types of board. With computer-controlled soldering lines, each board normally carries a barcode which calls up the correct parameter as it enters the machine. Nevertheless, it is not

job:LAY04 page:54 colour:1

black–text

136 Wavesoldering

at all advisable to run a soldering line with a random mix of diﬀerent types of board. It is advisable to gather them in as large batches as possible.

4.7.3 Optimizing machine parameters The following strategy for starting up a new machine, or changing to a new type of board, has proved its worth in practice: 1. Check that the conveyor angle is near 7°, and that the conveyor is laterally horizontal. Place a plain piece of FR4, of the same thickness and size as the boards to be soldered, in a board carrier or into the chain conveyor and move it forward into the ﬂuxer. With a foamﬂuxer, adjust the air pressure so that the wave can hold the required height with a good margin. With a sprayﬂuxer, set the width of the spraypattern to suit the width of the board. 2. Move the board forward to the solderwave. With double-wave machines, set the primary wave, whether it is of the turbulent type or a jetwave, as high as is possible without causing the solder to push through apertures in the board and ﬂood the top surface. With a jetwave of the type where the solder ﬂows in the direction of the travelling board, make sure that the baﬄe at the trailing edge of the board ﬁxture is high enough to prevent the solder from ﬂooding the top of the board as it leaves the wave. Single jetwaves of the counterﬂow type need a safety baﬄe at the leading edge of the board. Again, set the wave as high as is possible without ﬂooding the board. The secondary wave is always of the asymmetrical laminar type. The board is moved forward so that its leading edge is just in front of the wavecrest. Adjust the waveheight so that the crest comes approximately level with the top surface of the board. This means that thicker multilayer boards dip deeper into the wave, spend more time in contact with it, and in consequence receive more heat. Having done this, move the board forward into the wave and check whether the board is parallel with the wavecrest, as shown in Figure 4.31. If you ﬁnd that the board is not parallel with the wavecrest, do not try to adjust the setting of the whole solderbath or of the wavenozzle, but tilt the conveyor, as has been described already. 3. Next, set the conveyor speed at half the value which the vendor gives as its maximum speed, unless operational requirements make it necessary to work faster than that. It is worth remembering that it is a fact of life in engineering that the failure-rate or fault-rate of any given equipment or process begins to rise exponentially as it is driven at a rate or speed approaching its designed maximum. (Compare the number of pit stops during an Indianapolis race with the service requirements of a family car.) Run a board of the pattern which is to be soldered on the machine, without components, through the ﬂuxer and the preheating stage and check its temperature on leaving the latter (Section 4.3.4). If it gets too hot, reduce the setting of the heaters. If on the other hand the heater, even at its maximum setting, does not get the underside of a heavy multilayer board hot enough, ﬁt a

job:LAY04 page:55 colour:1

black–text

Wavesoldering 137

top reﬂector to the preheater if none is provided. If the board is still too cool, reduce the distance between the heaters and the conveyor. Only if all else fails (and in this case the design of the machine must be at fault) lower the transport speed or, better, modify the heating stage yourself. 4. Having balanced the setting of the heating stage and the conveyor speed against each other, proceed to solder about ten fully assembled boards, and check the soldering quality of each carefully. If this is satisfactory, enter the set of working parameters into the machine computer or your production control manual. If faults persist in an erratic pattern, check the stability of the ﬂuxer and wave setting; as a last resort, lower the conveyor speed and reduce the setting of the heating stage accordingly. If faults persist systematically with one or more given components, check their solderability or the suitability of the layout. For details of the systematic analysis, interpretation and elimination of soldering faults and defects, see Chapter 9.

4.7.4 Machine maintenance Daily Clean the wavenozzle at the end of the shift, and if necessary also at the mid-shift break. Turn on the solderpump and check whether the wavecrest is level and stable. If you are not satisﬁed, switch oﬀ the pump and scrape the inner walls of the solder conduit with an annealed hacksaw blade. An annealed hacksaw blade will not snap and constitute a potential danger, nor will it damage the conduit. Restart the solderpump and skim dross and ﬂux residues, which may now be ﬂushed through the wavenozzle, from the solderbath. This maintenance is especially important with jet nozzles. At the end of the day, clean splashes of solder and ﬂux from the top of the machine and the rims of the solderbath. With endless-chain conveyors, check the condition and functioning of the automatic chain cleaners. With board carriages, remove excessive ﬂux buildup from the holding jaws. This schedule can be greatly relaxed with soldering units which work under a nitrogen atmosphere (Section 4.5.2).

Monthly Lift the wavenozzle assembly and the pump impeller from the solderbath and remove all adhering dross and ﬂux residue. With foamﬂuxers, renew the air ﬁlter and clean the foaming stone. With sprayﬂuxers, clean spraynozzles, if any, and remove buildup of dried ﬂux, if any. Renew ﬂux in ﬂuxer, unless in the case of a foamﬂuxer the scheduled ﬂux renewal has taken place earlier. Clean the exhaust system of the ﬂuxing unit. Clean and, if necessary, renew air ﬁlters.

Annually Carry out a complete overhaul of the soldering machine. Check all board carriages, if any, for correct setting and alignment.

job:LAY04 page:56 colour:1

black–text

138 Wavesoldering

This schedule applies for soldering lines which are in constant use. With machines which are used only sporadically the schedule will, of course, be stretched accordingly.

4.7.5 Check-analysis of the solderbath Depending on the utilization of the machine, the solderbath should be checked at least once a year for its tin content and its impurity levels. Most solder vendors are able to carry out this analysis for their customers. Unless your own organization maintains a central analytical laboratory, and sometimes even then, it is better and quicker to employ the services of an outside specialist. For the interpretation of the analytical report, and the measures to be taken if it is unsatisfactory, see Section 3.3.3. An analytical laboratory requires a sample of solder weighing 100–200 g/3–6 oz, in the form of a small ingot. In order for this sample to be meaningful and representative of the contents of the solderbath, the following sampling procedure should be followed. The wave is switched on and kept running for 1–2 minutes. The sample is then taken from the over-run of the wave with a small stainless steel ladle, which must be absolutely dry. This is best assured by preheating it in a blowﬂame. The sample is then poured into a simple mould fabricated from heavy steel or stainless steel sheet, as sketched in Figure 4.32. This mould too must be absolutely dry, but it ought not to be too hot because the sample should solidify reasonably quickly.

4.7.6 Dealing with dross The nature of dross and the manner of its formation are discussed in Section 4.4.5. The layer of dross which forms on the surface of the solderbath (unless the machine is run under nitrogen) must be removed periodically to prevent it from being sucked into the pump inlet. Skimming the dross twice daily is suﬃcient for this

Figure 4.32 Taking a solder sample

job:LAY04 page:57 colour:1

black–text

Wavesoldering 139

purpose (Section 4.4.5). The simplest and best method is to gather the dross into one corner of the bath surface with a simple stainless steel implement, and then to lift the lump of dross out of the bath with a ﬂat stainless steel spatula such as is obtainable in any hardware shop. Tilting the spatula after lifting the dross allows most of the clean solder trapped in it to drain back into the bath. The rest is then put into a steel container which is provided with a lid. Most solder vendors are prepared to take back solder dross from their customers once a suﬃcient quantity has accumulated, and will credit them for a portion of the clean solder contained in it. Depending on the circumstances, it may be advisable to demand an analysis of the returned dross for its metal content from the solder vendor. Compact, fully enclosed electrically heated melting pots for the in-house recovery of solder from dross are oﬀered by some equipment vendors. Skimming the dross from the solderbath twice a day should be enough. Frequent skimming in order to make the solderbath look attractive, and maybe to impress visitors or the management, is not only unnecessary but also increases the amount of dross which forms on the machine. An existing layer of dross helps to protect the bath from further oxidation.

4.7.7 Hygiene and safety Lead and its toxic nature Solder contains about 40% lead, and lead is toxic. However, if treated and handled with common sense, there need be no danger to any person working with solder in any of its many forms, such as solderwire, solder ingots, molten solder or solder paste, provided a few basic facts are recognized. Lead can be absorbed into the human body only through the digestive system, while skin contact is harmless. Put crudely, the basic rule is therefore ‘Do not eat lead, in any of its forms.’ In practice, this means strict observation of a number of simple rules. Don’t smoke, eat or consume drinks on the job. Having handled solder or dross, wash hands thoroughly before smoking, eating or drinking. The reasons for these rules are obvious: handling a cigarette or food with solder-contaminated ﬁngers carries the danger of ingesting lead-containing solder. Even small amounts matter, because lead is a cumulative poison which is not excreted by the normal bodily functions. Quite apart from that, soft drinks should not under any circumstances be consumed near any part of an electronic assembly line. Fruit juices and fruit sugar form reaction products on metallic surfaces which severely aﬀect solderability, and which are diﬃcult to remove. Aerosol, formed for example by a ﬁzzy soft drink, can be fatal for the solderability of a circuit board. An often neglected danger point is the habit of chewing ﬁngernails. The spaces under the ﬁngernails are notorious collectors of dirt and dust, picked up from everything that is being handled or touched (as any forensic scientist knows). Habitual nailbiters should therefore on no account be given jobs which involve the handling of solder in any of its forms. Dross must be handled with caution and common sense: it contains a proportion

job:LAY04 page:58 colour:1

black–text

140 Wavesoldering

of powdery lead oxide, which is more dangerous than metallic lead because it is absorbed more readily into the digestive system. Hence the rule of placing dross skimmings into a metal container which is ﬁtted with a lid. Dross must be handled gently, so that it does not form a cloud of dust. It is a sensible precaution to issue a dust mask to all operators who have to handle dross in larger quantities. On the other hand, there is no reason for wearing a dust mask when skimming dross from a soldering machine, because in this form the oxide is trapped within the bulk of the metal and its adhering ﬂux residues.

Handling molten solder Molten solder is quite hot and must be treated with respect. The main danger when handling it arises from the fact that it will spit and splatter violently when it comes in contact with a wet or even slightly damp surface. This spitting is caused by the explosive evaporation of any surface moisture trapped under the molten metal. Hence the strict rule, already mentioned, that every implement which comes into contact with molten solder must be meticulously dried by preheating. By contrast, small amounts of liquid spilled onto the surface of molten solder will hiss away quietly without spitting. Drops of molten solder on the skin can be painful, and cause small but relatively harmless local burns. To stop the pain quickly, touch a cold metal surface, or run cold water onto the burn. Never apply oil or grease, which will only make matters worse. Application of a small amount of burn-ointment, which normally contains picric acid, stops the pain, promotes quick healing and prevents blistering. It is useful to keep a tube or tin of it handy near any machine or bench where molten solder is handled. On the other hand, even a minute drop of molten solder which reaches the eye can fatally damage sight. It is therefore important to issue all operators who have to handle molten solder, for example when taking a sample of solder from the solderwave or when emptying a solderpot, with safety goggles. There is, however, no need to wear goggles when removing the safety screen to watch a board passing over the solderwave, or when skimming a solderpot (provided the skimming tool is dry). Wearing protective gloves is a wise precaution when sampling the solder or cleaning the wavenozzle. When handling larger amounts of molten solder, such as when emptying a solderpot, it is advisable to wear an apron or protective clothing. Solderdrops clinging to clothing are easily removed by touching them with a small soldering iron set at a low soldering temperature, provided the material is entirely of natural ﬁbre such as wool, cotton or linen. With synthetic ﬁbres, this method would not work, and scraping or plucking the solder oﬀ is the only way. When faced with the task of handling larger amounts of molten solder, it is best to plan one’s strategy in advance: decide what you want to do, and how best to do it, before you start. Have all implements and receptacles dry and ready in their proper places. Do not hurry, and move slowly and with deliberation.

job:LAY04 page:59 colour:1

black–text

Wavesoldering 141

4.8 The role of adhesives in wavesoldering SMDs must be anchored to the board before they are wavesoldered because they have no leadwires or legs with which to hang on to the substrate. Adhesive joints have been found to provide the best answer to the problem. Their mechanical properties are adequate for the task, and they can be broken without undue force if necessary.

4.8.1 Demands on the adhesive and the glued joint The glued joint must be strong enough to hold the component securely to the board during any handling operation which may precede the soldering process, for example the insertion of wired components with a ‘mixed’ board, and above all during the wavesoldering procedure itself. These mechanical loads are only modest, at most of a magnitude of a few newtons. It is important, however, that the joint does not distort or disintegrate under the inﬂuence of the ﬂux solvents during the preheating stage, and especially during the passage through one or two solderwaves. Should the removal of a glued and soldered component become necessary because on inspection it has been found to be faulty or wrongly placed (Section 10.2), the joint should be capable of being broken without undue force and consequent damage to the substrate (Section 4.8.5). Finally, during the life of the assembly, the glued joints should not give oﬀ or leak any substance, particularly not one of an ionic nature, which could lower the surface resistance of the board or interfere with the function of the assembly.

4.8.2 Storage and handling behaviour of adhesives Adhesives for SMDs are of the reactive, single-component epoxy or acrylic type. Solvent-containing adhesives and two-component reactive adhesives, which require mixing before use, are unsuitable for industrial SMD wavesoldering. Single-component adhesives are a mixture of two ingredients, a polymer-resin and a hardener, which are capable of reacting with one another, forming a rigid structure of crosslinked molecules. This reaction requires a trigger to set it oﬀ, which may be a rise in temperature, or exposure to light in the visible or the UV range, or both these triggering agents, acting simultaneously or in sequence. A good SMD adhesive must satisfy a number of speciﬁc requirements: 1. During storage, resin and hardener should not of course react with one another. With some adhesives, this may require storage in a refrigerator at about 5 °C/40 °F, to ensure a storage life of up to one year, which is what the industrial user expects. With many modern adhesives, refrigeration is no longer necessary, and storage times of up to one year at room temperature (say 25 °C/78 °F) are not unusual. 2. A drop of adhesive, as dispensedonto the board, may have to bridge a gap between 0.01 mm/0.4 mil and 0.3 mm/12 mil in height (the standoﬀ height of the component)while, depending on the geometry of the layout, its base may have to

job:LAY04 page:60 colour:1

black–text

142 Wavesoldering

ﬁt into a very narrow gap between two footprints (about 1 mm/40 mil with a micromelf) (Figure 4.33). As a general rule, the dot as put down on the board shouldbe about 0.05 mm/2 mil higher than the standoﬀ height of the component which it has to hold down. This requires the dispensed adhesive to retain its shape without sagging or ‘slumping’. Any sideways spread of the dispensed drop would not only lower its height, so that it might fail to contact and hold the component, but it could also spread over the adjacent solderpads, totally and possibly irreparably ruining their solderability, and thus the whole circuit board. The type of behaviour in which semiliquid substance retains its shape is called ‘thixotropy’. For similar reasons, the solder pastes which are used in reﬂowsoldering must also exhibit thixotropy, which is discussed fully in Section 5.2.1. Apart from a sideways slump of the adhesive drop, it would be equally fatal should one of the more mobile constituents of the adhesive leak out sideways from the drop and contaminate an adjacent solderpad. Finally, the adhesive must separate neatly from the dispensing nozzle or placement pin, without forming a tail or thread which might tip over and fall on a solderpad. The ﬂow behaviour of an adhesive is necessarily temperature dependent, making it more mobile at highter temperatures. Most manufacturers have succeeded in reducing this temperature dependence to a minimum. However, since a very precise dosage of the dispensed adhesive drop is of the essence, especially with very small melfs and chips, the dispensing ampoules on some placement systems are heated to a standard temperature. As a rule, the adhesive does not sit directly on the FR4 of the board, but on the solder resist. This places certain demands on the adhesion and the surface properties of the latter which are discussed in Section 6.1. Very often one or more conductors will pass between the solder pads of a

Figure 4.33 Demands on the adhesive spot

job:LAY04 page:61 colour:1

black–text

Wavesoldering 143

component. It is important that these conductor tracks are not covered with a layer of solder, as might be the case with boards made by a ‘subtractive’ process. If they are, the solder will melt underneath the solder resist as the board passes through the solderwave. Because the solder resist starts to crinkle as the solder on which it sits melts, the result is called the ‘orange peel eﬀect’. An SMD glued to the solder resist loses its safe anchorage when the solder underneath the resist melts, so that it is in danger of being washed oﬀ in the wave. For this reason, boards for wavesoldering SMDs should preferably be of the ‘solder mask over bare copper’ or ‘SMOBC’ type (see Section 6.1). 3. After an SMD has been placed on its adhesive dot, it must stick to it strongly enough to prevent it from shifting its position or falling oﬀ, while the board is handled between the placement of the components and the curing of the glued joints. This holding power of the uncured adhesive is called ‘green strength’. Furthermore, an adhesive must be able to maintain its thixotropic behaviour and its green strength for at least 24 hours between being taken from its container, or discharged from its dispenser, and its being hardened or cured prior to soldering (open time). 4. Last, but not least, the adhesive should have a distinctive and conspicuous, perhaps luminous, colour, so that missing or misplaced dots are easily spotted. Orange or bright red seem to be the preferred shades.

4.8.3 Applying the adhesive The precision of both the placement coordinates and the size of every individual dot of adhesive are critically important, especially with small melfs and chips: a misplaced dot, or one which is too large and becomes squeezed out during placement, is liable to cover a solderpad and make it unsolderable. Removing cured adhesive from a pad surface is one of the most costly and hazardous operations in corrective soldering (Section 10.1.1). On the other hand, a dot of insuﬃcient height may not connect with the component it is supposed to hold. In most situations adhesive dots have to be of varying height, for reasons explained above. There are several alternative methods to achieve this:

Sequential application of single dots Dispensing the adhesives from the nozzle of a cartridge or ampoule is widely practised. Most vendors oﬀer adhesives in air-pressure operated ampoules, which can discharge the content in a controllable manner. For manual placement, the pressure impulse in the hand-held ampoule is controlled by the operator through a footpedal or a press-button. The operation is simple, and misplaced adhesive can be wiped oﬀ, with solvents supplied by most vendors. Dispensing adhesive from ampoules can be mechanized in two ways: 1. For putting down dots of adhesive onto boards before the components are placed, automatic equipment, which is capable of being programmed, is on the market. With these machines, the dispensing ampoule is mounted on an xy

job:LAY04 page:62 colour:1

black–text

144 Wavesoldering

movable gantry (Figure 4.34). The precision and repeatability of dosage and placement are of a high enough order to meet the requirements of adhesive application to modern, closely populated boards. The distance between the nozzle tip and the board can be varied and programmed, not only to suit the size of individual dots, but also to enable two dots to be placed on top of one another (piggy-back) to cater for exceptionally high standoﬀs. A ‘suck-back’ at the end of a delivery impulse prevents the formation of a dangerous string of glue when the nozzle is lifted oﬀ. The dispensing program can be derived from the software of the board layout. The speed is limited by the various manoeuvres which have to be performed between discharges, such as starting and stopping the dispensing head, adjusting its position in the vertical z axis, actuating the displacement mechanism, and executing the ‘suck-back’. Within these limitations, vendors claim maximum achievable dispensing rates of up to 17 000 dots/hour, i.e. over 4 dots/second. Another technique for putting down individual, metered amounts of adhesive is derived from ink-jet printing. The duration of an individual discharge is as short as 0.001 seconds, which makes it possible to use ‘on-the-ﬂy’ dispensing, where the dispensing head does not stop moving. Thus, dispensing speeds of 20 dots/sec, i.e. 72 000 dots/hour, are possible. Jet dispensing units can be integrated in-line with high-speed pick-and-place equipment. The major adhesive vendors are able to supply adhesives suitable for jet-dispensing. 2. Many automatic sequential pick-and-place machines are or can be ﬁtted with an adhesive dispensing station, which puts down measured dots of adhesive and precedes the component placement station. The dispensing details are the same as with the dispensing gantry. With simultaneous pick-and-place machines, the adhesive is often placed directly on the underside of each component in the time interval between pickup and placement (see Section 7.3.2).

Stencilprinting the adhesive Some major vendors oﬀer equipment and adhesives, which by using specially developed plastic stencils, and by controlling the thixotropic behaviour of the

Figure 4.34 Dispensing gantry

job:LAY04 page:63 colour:1

black–text

Wavesoldering 145

adhesive, permit the print-down of adhesive dots of varying and controllable height on to a board in one single printing operation. By choosing the right aperture diameter, dots varying in height from 0.125 mm/5 mil to 1 mm/40 mil can be printed with a 0.3 mm/12 mil thick stencil onto a given board in one pass. Also, dots do not necessarily have to be round, but may be given other outlines if required. The advantages are obvious: apart from speeding up the process, parameters of the adhesive such as a tendency to form strings are no longer critical. Vendors of the printing equipment claim printdown rates of up to 14 4000 dots per hour.

4.8.4 Curing the adhesive joint After all components have been placed on the ‘green’ adhesive, the joints must be cured. Curing transforms the adhesive from a viscous mass into a ﬁrm, solid body. This is achieved by triggering a reaction between the two constituents of the adhesive, which crosslinks the individual mobile polymer molecules of the resin constituent into a coherent, semicrystalline mass. It is important that the joint does not shrink or crack during curing. With most epoxy and acrylic adhesives, heat provides the required trigger. As is natural with any chemical reaction, the higher the temperature, the shorter the time in which the crosslinking reaction proceeds throughout the joint (Figure 4.35). With a modern adhesive, all joints on a board are suﬃciently hard for wavesoldering after two to three minutes at a curing temperature of 120 °C/250 °F. Curing can be carried out in an infrared oven, similar to or identical with a reﬂowsoldering oven (Section 5.4.4). It must be remembered, however, that with

Figure 4.35 Hardening curve of an epoxy adhesive

job:LAY04 page:64 colour:1

black–text

146 Wavesoldering

the exception of small melfs and chips, the adhesive joint is shielded from the radiation by the sometimes large and thick component. For adhesive curing, therefore, an eﬃcient convection oven is best. There is no advantage in carrying out this curing operation in a nitrogen atmosphere. As an alternative to heating, or possibly in addition, exposure of the adhesive to ultraviolet light is also eﬀective in promoting the curing process. This mechanism will only work if the adhesive, or at least some of it, is ‘visible’ to the light source and not covered by the component (Figure 4.36). Simultaneous exposure to heat and light can shorten the curing time by up to 50 per cent. A type of adhesive is available which contains a light-sensitive initiator. This has the eﬀect of adding a ‘hairtrigger’ mechanism to the crosslinking reaction: exposure of the dots of adhesive to a dose of visible light for one-half to four minutes (depending on the intensity of the light source), before the components are placed, ﬁrms up the adhesive and increases its green strength without starting the crosslinking proper. Once the components are placed, which must be done within 30 minutes after the light exposure, full curing of the joints can be completed in a much shorter time or at a much lower temperature than is the case with conventional adhesives.

4.8.5 The glass transition temperature No assembly process is entirely free from faults, and occasionally glued and wavesoldered components must be removed from a board. However, while soldered joints can be unsoldered, a glued joint cannot be ‘unglued’ but must be broken. The so-called ‘glass transition’ mechanism of crosslinked polymers makes it possible to break cured joints without damaging the board. Above a certain temperature, which is called the glass-transition temperature (T ) the crosslinked bonds between neighbouring molecules begin to open and the% molecules start to regain their mobility. For a cured joint this means that the adhesive loses its rigidity and begins to behave like a highly viscous substance. Depending on the type of adhesive and on its curing history, its T lies between 35 °C/95 °F and 80 °C/175 °F. This means that after heating it to %its T , the joint can be separated without much force. In % 10.2) this is done by twisting the SMD. The resulting desoldering practice (Section

Figure 4.36 Location of adhesive spots for ultraviolet hardening

job:LAY04 page:65 colour:1

black–text

Wavesoldering 147

shearing force will readily break the joint. Pulling the joint apart would require a much greater force than twisting, and is liable to damage any conductor tracks which may pass underneath the glued joint.

References 1. Brit. Pat. 798 701, 1956, Fry’s Metals, Improvements Relating to Soldering Components to Printed Circuits. 2. Brit. Pat. 639 178, 1943, Eisler and Strong, Manufacture of Electric Circuits and Circuit Components. 3. Kirby, P. L. and Pagan, I. D. (1987) The Origin of Surface Mounting, Proc. Europ. Microelectronic Conference, Bournemouth, UK. 4. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Electrochemical Publications, Ayr, p. 489. 5. Smernos, S. and Strauss, R. (1988) Low Temperature Soldering. Electronic Communications, pp. 148–151. 6. Klein Wassink, R. J. (1989) loc. cit., pp. 498–500. 7. Oates, W. A., Todd, D. D. (1962) Kinetics of the Reduction of Oxides. J. Austral. Inst. Met., 7, pp. 109–114. 8. Leibfried, W. (1979) Soldering without Flux. German Min. for Res. & Technol. (BMFT ), Rep. T., pp. 79–164 (in German). 9. Keeler, R. (1990) New Fluxless Soldering Process. El. Pack & Prod., 30, 10, p. 15. 10. Albrecht, J., Scheel, W., John, W., Wittrich, H., Grasmann, K. H. and Liedke, V. (1992) Fluxless Wavesoldering. DVS Report 141, Duesseldorf, Germany, pp. 90–99 (in German). 11. Hendry, M. (1995) Is there a future for nitrogen? El. Manuf. and Test, 1995, pp. 11–12. 12. Ehrlich, M. et al. (1994) Investigations into the Reliability of Atmosphericand Inert-Wavesoldered Capacitors. Proc. Techn. Conf. Nepcon West. 13. German Patent DE 195 19 188 A1, 24.5.95 (Scheel, Ring, Hafner & Leicht). 14. Anon. (1997) Wavesoldering in a Vapourphase Protective Atmosphere. Productronic 5/6, p. 6 (in German).

job:LAY05 page:2 colour:1

black–text

5 Reflowsoldering

5.1 The reflow concept As has been said in Section 3.1, the making of a good soldered joint needs the right amount of solder, ﬂux and heat, in the right place, and at the right time. With wavesoldering as with handsoldering, the ﬂux always comes ﬁrst, and solder and heat together come afterwards. With all reﬂowsoldering methods, the heat always comes last. To begin with, solder and ﬂux are placed on one or both joint surfaces, either together in the form of a solder paste or separately, ﬁrst the solder in the form of a metallic coating and then the ﬂux at a later stage. Subsequently the joints are put together. The important point is that all this happens at room temperature though, with some procedures, the solder may have been predeposited on one or both joint surfaces by a hot-tinning method. With all reﬂow strategies, the assembled joints are ﬁnally heated to a temperature high enough to melt the solder, and for long enough to let it tin the joint surfaces and ﬁll all the joint gaps. As soon as this has been achieved, heating is discontinued and the solder is allowed to solidify, the faster the better.

5.1.1 SMDs and reflowsoldering Reﬂowsoldering is a much older process than wavesoldering, going far back into antiquity; under the name of ‘sweatsoldering’ it is used in plumbing to this day. With the advent of hybrid technology in the early 1960s sweatsoldering was recognized as the logical way of joining SMDs, which were speciﬁcally developed for hybrids, to the metallic conductor pattern of the ceramic substrate. Rosin-based soldercreams were already in existence, though not as yet screen-printable, and the assembled hybrid circuits were mostly soldered on simple hotplates. Professional reﬂowsoldering equipment and printable solder pastes became commercially available by the early seventies, when SMDs had begun to be used on conventional circuit boards. SMDs and reﬂowsoldering are ideal partners. With wavesoldering SMDs, the molten solder needs help to ﬁnd its way to the joints (Figure 4.14). With reﬂowsoldering, both solder and ﬂux are already in place before the joints are heated by one

job:LAY05 page:3 colour:1

black–text

Reflowsoldering 149

of the several options available. Thus, for a board surface populated entirely with SMDs, reﬂowsoldering is the natural choice. A leading vendor of both wave- and reﬂowsoldering equipment stated recently (1997) that 80% of all SMDs are now being reﬂowsoldered, because reﬂowsoldering is less complex and demanding than wavesoldering: fewer operational parameters need to be controlled, and therefore reject rates can be kept signiﬁcantly lower. Figure 5.1 shows the procedural options of reﬂowsoldering. Figure 5.2 shows the various ways of arranging SMDs and wired components on a board. The choices of possible soldering strategies for the diﬀerent types of board construction are shown in Table 5.1.

Through-hole reflowsoldering At the present state of the art, boards which carry both wired components and SMDs must be wavesoldered. However, if a recently introduced technique termed ‘through-hole reﬂowsoldering’ proves successful, the balance could shift still further towards reﬂowsoldering. With this technique, the through-plated holes, which are to receive the leads of wired components, are ﬁlled with solder paste in the same printing operation which deposits solder paste on the footprints for the SMD leads. The wired components are then inserted in such a way that their leads don’t push all of the paste out of the other end of the holes. Several requirements have to be met: the layout of the board and the location of the wired components must suit the speciﬁc requirements of the process and most importantly, the paste printdown must ﬁll at least 75% volume of each hole. The placement of the wired components demands an insertion machine, which is able to insert them, as well as SMDs. Most placement machines for SMDs do not possess this capability, and in that case two placement operations will have to follow one another.

Furthermore, the temperature proﬁle of the reﬂow process must take account of the thermal limitations of the wired components involved, most of which are not meant to withstand temperatures much above 250 °C/480 °F. Electrolytic capacitors will not survive temperatures above 100 °C/212 °F. They are therefore not even suitable for vapourphase-reﬂowsoldering, which usually involves a temperature of 215 °C/419 °F. One author states that with through-hole reﬂow, the temperature proﬁle of the reﬂow oven (see Section 5.5.4) must ensure that during the melting phase the temperature of the board is held above the melting point of the solder (183 °C/ 360 °F) for at least 50 seconds, and that afterwards the board should be cooled at a controlled rate of 3–4 K/sec. If this concept of through-hole reﬂow proves viable, it could form a serious threat to wavesoldering and its associated technologies of placing and curing SMD adhesives.

Overhead soldering Reﬂowsoldering boards with SMDs on both sides involves ‘overhead soldering’, for which two diﬀerent strategies are possible:

job:LAY05 page:4 colour:1

black–text

150 Reflowsoldering

Figure 5.1 The reﬂow soldering options

job:LAY05 page:5 colour:1

black–text

Reflowsoldering 151

Figure 5.2 Options of board construction

Two-pass soldering This strategy is the more common one. One side is dealt with ﬁrst, involving paste print-down, placement of the SMDs, and soldering by vapourphase, infrared, or hot-air/gas convection. The second side (side two) is then treated in the same way. With vapourphase soldering, the joints on side one, which are now underneath, will melt again, with the components hanging onto the board with the help of the surface tension of the molten solder. Practical experience shows that this can be done provided there are no particularly heavy SMDs on side one, which might drop oﬀ when their soldered joints melt again during pass two. However, the metallurgical properties of these joints, are bound to deteriorate by being melted twice. Therefore, two-pass soldering of double-sided boards in a vapourphase installation should only be carried out if there is no alternative.

job:LAY05 page:6 colour:1

black–text

152 Reflowsoldering

Table 5.1 Board constructions and their soldering strategy options Type I: Mixed component population Board construction I(a) – Strategy I (Recommended by the USA Surface Mount Council (SMC), 1988) Side 1:

Insert wired components, crimp lead ends (Visual inspection) Turn board over

Side 2:

Apply adhesive,* place SMDs (Visual inspection) Cure adhesive Turn board over Wavesolder side 2 (Inspect, clean, test)

Board construction I(a) – Strategy II Side 2:

Apply adhesive,** place SMDs (Visual inspection) Cure adhesive

Side 1:

Insert wired components, do not crimp leads†) (Visual inspection) Wavesolder side 2 (Inspect, clean, test)

Turn board over

Board construction I(b) – Strategy I (Recommended by USA SMC, 1988) Side 1:

Print solder paste (Visual inspection) Place SMDs (Visual inspection) Reﬂowsolder Insert wired components†† Wavesolder side 2 (Inspect, clean, test)

Board construction I(b) – Strategy II (If the board carries only a few QFPs or TABs) Side 1:

Insert wired components Wavesolder Impulse-solder SMDs to their previously and suitably pretinned solderpads (Section 5.9)

Board construction I(c) (Recommended by USA SMC, 1988) Side 1:

Print solder paste (Visual inspection) Place SMDs (Visual inspection) Reﬂowsolder Turn board over

job:LAY05 page:7 colour:1

black–text

Reflowsoldering 153

Table 5.1 Continued Side 2:

Apply adhesive,‡ place SMDs (Visual inspection) Cure adhesive

Side 1:

Insert wired components Wavesolder side 2 (Inspect, clean, test)

Turn board over

Type II: SMDs only Board construction II(a) (Recommended by USA SMC, 1988) Side 1: Print solder paste (Visual inspection) Place SMDs Reﬂowsolder (Inspect, clean, test) Board construction II(b) (Recommended by USA SMC, 1988) Side 1: Print solder paste (Visual inspection) Place SMDs Reﬂowsolder Turn board over Side 2:

Print solder paste (Visual inspection) Place SMDs Reﬂowsolder‡‡ (inspect, clean, test)

*Adhesive applied by gantry-mounted programmed syringe (Section 4.9.2). The crimped wire ends of the inserted components make screenprinting or stencilling of adhesive impracticable. **Screening or stencilling of adhesive practicable. †The underboard crimping tool of the insertion machine may knock neighbouring SMDs oﬀ the board. ††Leadwire ends may be crimped but take care that the head of the insertion machine does not knock neighbouring SMDs. ‡Any method may be used, including screening and stencilling. ‡‡Reﬂowsoldering a board a second time, with previously reﬂowsoldered SMDs underneath is preferably carried out in a convection reﬂow-oven with separate temperature management for the top and the bottom half of the oven (Section 5.6.3).

It is safer and simpler to solder double-sideded boards in the type of convection reﬂow oven which allows side one, to which SMDs have been soldered in the ﬁrst pass, to be kept below 183 °C/360°F, when it is upside-down while side two is being soldered (see Section 5.6.3). Two-pass soldering in nitrogen has the advantage that the solderability of the footprints of side two is not compromised by being oxidized, while side one is being soldered.

job:LAY05 page:8 colour:1

black–text

154 Reflowsoldering

Single-pass soldering The option, of putting the components on both sides and then soldering the whole board in one single pass through the vapourphase or oven, is practicable with boards which carry a deposit of solid solder on their footprints (Section 6.3.2). With such boards, the components on side two are anchored to the board by a dot of air-hardening or curable adhesive, which is applied prior to the placement of the components (Section 4.9.3). These glued joints need not be as strong as those which hold the SMDs to the board during wavesoldering since they only have to prevent them from falling oﬀ. This rather complex procedure is only chosen as a last resort. Single-pass reﬂowsoldering with solder paste joints on both sides is not often practised because of the problem of printing solder paste and placing components on both sides of a board before soldering the joints. Soldering itself is only possible if the components on side two are very light, and if the solder paste has suﬃcient ‘wet strength’ to stop them from falling oﬀ before the solder melts and its surface tension takes over. Feasibility trials will certainly be required, possibly with some benchtop equipment (Section 5.4.4) before using this strategy.

Visual inspection Visual inspection between the application of adhesive and placing SMDs, and between placing SMDs and curing the adhesive, is well worth while: it is easy to correct missing or misplaced adhesive spots, or misplaced, misaligned or missing SMDs before the adhesive is cured. Corrections after curing are diﬃcult, often time-consuming, may damage the board, and above all, can be very expensive.

5.1.2 Reflowsoldering versus wavesoldering The respective merits and disadvantages of wavesoldering and reﬂowsoldering, speciﬁcally of SMD joints, are best compared under two separate aspects of making soldered joints, the metallurgical and the operational ones.

Metallurgical aspects Wavesoldering With wavesoldering, all joints are ﬁlled from a solder reservoir which holds from 40 kg (90 lbs) up to over 700 kg (1400 lbs) of molten metal, held at an accurately controlled and monitored temperature (normally around 250 °C/480 °F). The composition of the solderbath changes slowly over the course of time: the solder can and will pick up copper from the solderpads and other metals from the component leads; its tin content will gradually drop, because tin oxidizes more quickly than lead, and because the joint surfaces pick up more tin than lead. This means that there is need for occasional check analyses of the metal bath (Sections 3.3.3 and 4.8.5). All SMD joints are fully exposed to the washing action of the solderwave, which removes the greater part of the intermetallic products of the reaction between the

job:LAY05 page:9 colour:1

black–text

Reflowsoldering 155

solder and the substrate and returns them to the solderbath, where they are greatly diluted. Thus the solder content of every joint can be regarded as a very small part of a very large metallurgical system. With wavesoldering, the ‘confrontation interval’, by which is meant the length of time during which the joint surfaces confront molten solder and react with it, is short, from two to ﬁve seconds (Sections 3.2 and 5.4.1). Therefore, the brittle intermetallic layer, which is the product if the reaction between the two, is thin (1 m/0.04 mil). A wavesoldered joint solidiﬁes quickly: its solidiﬁcation interval, i.e. the time span between its passage through the solderwave with its temperature of about 250 °C/480 °F and its reaching the solidiﬁcation temperature of 183 °C/361 °F, is short too, two seconds at most, and this makes for a ﬁne-grained structure. As a consequence of all this, a wavesoldered SMD joint, whether on the ends of a melf or chip, or under the lead of an IC, has a favourable metallurgical structure: it is ﬁnegrained with few, if any, intermetallic solids dispersed in it, and the brittle layer of intermetallic compound between the solder and the substrate (Section 3.2) is thin. The tubular joints in the throughplated holes do not concern us here; in any case, they are not washed by the solderwave directly, but are ﬁlled by capillary action. Reﬂowsoldering With reﬂowsoldering, matters are drastically diﬀerent: every individual joint forms a separate, closed metallurgical system with all the products of the solder/substrate reaction trapped in it. This has a pronounced eﬀect on the joint structure, particularly since a very small volume of solder interacts with a relatively large surface area of substrate.

Methods of supplying the soldering heat Equilibrium heating methods The various reﬂowsoldering methods diﬀer mainly in the manner in which the joints are heated. Some heating methods present a so-called equilibrium situation, in which all joints reach the well-deﬁned and constant temperature of the heating medium after a certain time. With vapourphase soldering, this is the temperature of the saturated vapour of the working ﬂuid, i.e. its boiling point or the temperature of the superheated unsaturated vapour (see Section 5.4.3). With convection soldering, in a convection oven or a hot gasjet, it is the temperature of the heating medium. With impulse soldering, it is the temperature of the soldering tool. In an equilibrium situation, overheating is impossible (Section 5.5.1). The rate of heating and cooling varies widely between the diﬀerent methods. With vapourphase soldering, the joints approach their end-temperature asymptotically, in a matter of minutes, but not all joints necessarily at the same time. Consequently the confrontation interval too is not the same for every joint; it may extend to between 30 seconds and one minute. The speed of the subsequent

job:LAY05 page:10 colour:1

black–text

156 Reflowsoldering

solidiﬁcation depends on the design of the equipment. With modern systems, it can be less than 5 to 10 seconds. With convection soldering, the rate of heating is more uniform and controllable depending on the type and the eﬃciency of the equipment, and the same is true of the solidiﬁcation speed. The confrontation interval can be kept from a few to up to 30 seconds, depending on the scale of the operation and the type of oven. With impulse-soldering, where only the joints themselves but not the whole board are heated, both the confrontation interval and the solidiﬁcation period can be controlled and kept within one or two seconds. Non-equilibrium heating methods Infrared and laser soldering present non-equilibrium situations: the temperature of the heat source is well above the intended soldering temperature, and the thermal energy is transferred to the joints by heat radiation. The temperature reached by the joints depends principally on the duration of their exposure to the heat source. The higher the temperature of the heat source, the more critical is the timing of that exposure. With infrared soldering, heating rates depend on the temperature of the emitters, and are mostly relatively slow; confrontation intervals range between 10 and 30 seconds. Solidiﬁcation periods can be kept within about ten seconds. By contrast, with laser soldering both confrontation intervals and solidiﬁcation periods are counted in milliseconds. Whatever the soldering method, the metallurgical structure of a joint determines its reliability and life expectancy. The ﬁner the microstructure, and the thinner the brittle intermetallic layer between the solder and the substrate, the better both of them will be. As long as confrontation intervals can be kept well below a minute, or better 30 seconds, and the solidiﬁcation periods below ten seconds or so, all will be well. Figure 5.32 gives a comparison between the temperature proﬁles of wavesoldering and all current reﬂowsoldering processes.

Operational aspects Any comparison between diﬀerent soldering methods ought to take the following requirements into consideration: 1. 2. 3. 4.

Minimum percentage of faulty joints, minimum rate of rework Joints with optimum metallurgical structure and operational reliability Lowest possible thermal and mechanical stress for boards and components Soldering results independent of complexity of the board, SMD-population density and component shape 5. Suitability both for integration in CIM in-line production, and for coping with lots-of-one short runs 6. Low production costs 7. Environmental acceptability.

job:LAY05 page:11 colour:1

black–text

Reflowsoldering 157

Wavesoldering A great advantage of wavesoldering is its status as a mature and well understood technology of more than thirty years’ standing. Its main drawback is the critical dependence of its soldering eﬃciency, as measured by a consistently low jointdefect rate, on the correct setting, high stability and consistent monitoring of a large number of operating parameters, many of them interlinked, and involving the management of a large mass of moving molten solder. The list of parameters is formidable: the density, the freshness and the water content of the ﬂux, and the nature of the ﬂux cover; the temperature of the solder and its purity; the speed of the solderpump; the shape and stability of the solderwave; the temperature of the preheating stage; and the speed of the conveyor, to name the main ones. The computer-control of a modern wavesoldering line takes care of many of these parameters, but a wave-machine demands frequent and expert supervision to spot those types of malfunctioning which are outside the scope of automatic monitoring, before too much damage is done. While these are aspects of wavesoldering in general, wavesoldering SMDs raises further problems: SMDs must be glued to the circuit board and the adhesive must be cured before soldering. The board layout must take the ‘shadow eﬀect’, which an SMD exerts on the wave, into consideration and many board conﬁgurations have only one optimal direction of travel over the wave. With wavesoldering, it is diﬃcult to inﬂuence the amount of solder in a joint, especially with melfs and chips; thus the control of the joint proﬁle becomes problematical. Multilead SMDs with a joint pitch of below 1.27 mm/50 mil become diﬃcult to wavesolder in a normal atmosphere without bridging. A pitch of 0.75 mm/30 mil is presently regarded as the ultimate limit of wavesolderability. Wavesoldering under a cover of nitrogen, and with less than 50 ppm of oxygen present, has pushed this limit to 0.5 mm/20 mil and below.

Reﬂowsoldering The great attraction of all reﬂowsoldering methods from the operational point of view is the relatively low number of soldering parameters which need to be set and monitored: with vapourphase soldering, it is the duration of dwell in the vapour chamber; with infrared and convection ovens, the temperature of the heating elements or the oven atmosphere, and the conveyor speed; with laser-soldering, the duration of the energy pulse, and with impulse-soldering the temperature of the soldering tool and the duration of its dwell. It is a general rule that the fewer the operational parameters of a manufacturing process, the smaller the chance of something going wrong, and the higher the probability of keeping the fault rate and the amount of corrective soldering down. The ideal ‘ﬁrst time right, every time right’ is easier to realize with one of the reﬂowsoldering methods than with wavesoldering. The great attraction of reﬂowsoldering is that in every deposit of solder paste, both ﬂux and solder are factory-fresh. A growing problem is the tendency of the footprints, which must be covered with solder paste, and the distance between them

job:LAY05 page:12 colour:1

black–text

158 Reflowsoldering

(their pitch) to get progressively smaller, especially narrower. This is beginning to push the technologies of solder pastes, and of printing them, towards the limits of technical and commercial feasibility. Systems by which depots of solid solder can be placed on SMD footprints by the board manufacturer (Section 6.4.3) instead of the board user may provide an answer to this particular problem. Until the advent of the nitrogen-ﬁlled wavesoldering machine, the answer to the wave-versus-reﬂow dilemma was simple: do not use wavesoldering, unless you must. Even then, if you are faced with a board construction of type I(a) (Figure 5.2), it may be worth considering changing the board architecture to type 1(b) and avoiding the need to wavesolder SMDs. Should ‘through-hole reﬂow’ prove viable, the need to wavesolder could disappear altogether. The trade-oﬀ of lower reject rates against costs of redesign, loss of board real estate and maybe having to buy a reﬂowsoldering installation may still be favourable. Since wavesoldering under nitrogen has pushed the limits of wavesolderability into a region where solder paste-printing is beginning to get problematical, the wave-or-reﬂow dilemma must be solved on its respective merits in each particular case. A checklist on which this choice could be based will be found in Section 5.9.

5.2 Solder paste Solder paste is still the most widely used medium for putting down both solder and ﬂux in one single operation on a footprint for subsequent reﬂowsoldering. The success of a reﬂow process which involves solder paste depends in the ﬁrst place, and critically so, on the quality of the paste which is used. It is essential that every footprint on every board of a production run receives without fail its solder paste deposit of an identical and predetermined outline and thickness. On each one of them, and on every board, the solder paste must be of known and unvarying composition, with a consistently satisfactory soldering behaviour. Otherwise, faulty or open joints or solder bridges between neighbouring joints are bound to result, and the soldered board will not be able to function. This means that ‘soldering success’ as deﬁned in Section 9.1.1 will not be achieved, with all the consequences in corrective soldering, additional costs and loss in quality which this failure entails.

5.2.1 Operational requirements It follows that the properties and the behaviour of the solder paste must be closely deﬁned, maintained, and monitored to ensure that at all times it meets the following long list of requirements: E The paste must be easily dispensable or printable in precisely predetermined and repeatable quantities. E It must be of a stable consistency, without variation from batch to batch. The paste must not separate out in storage nor during use. These properties should not be unduly sensitive to the working environment such as temperature and relative humidity.

job:LAY05 page:13 colour:1

black–text

Reflowsoldering 159

E The paste printdown or deposit must ﬁrmly remain where it was put down, retain its shape and have suﬃcient ‘tack’ to hold every component ﬁrmly in place between placement and soldering.‘High-tack’ is particularly important with high-speed placement equipment (‘Chip-Shooters’). E Its soldering behaviour must be impeccable: the solder in the paste must melt at the correct temperature, and instantly and perfectly wet solderpads and component connectors. E All the solder from the paste printdown or deposit must ﬁnish up in the soldered joint, even though some of the paste may have been squeezed out of the joint during placement. None must be allowed to stay behind outside a joint in the form of a bridge between neighbouring footprints, or as individual prills or globules. E Finally, the ﬂux residue which remains after soldering must, if necessary, be removable by one of the presently available and acceptable methods unless the paste is a no-clean one. This complex list of requirements has turned the formulation and the manufacture of solder pastes into a science, if not an art, which involves such diverse disciplines as metallurgy, physics, colloid chemistry and printing technology, to name just a few. The successful and economic running of any reﬂowsoldering line which employs solder paste depends critically on the correct, predictable and constantly repeatable performance of that paste. To assure the user of its quality and to enable him to check it, standard speciﬁcations have been formulated in cooperation between paste users and producers. The standardization of solder pastes, which are substances of a complex nature, having to fulﬁl a number of interlinked operational requirements and constantly being further developed, is not an easy undertaking, especially on an international basis. In Europe, the relevant standards ISO/CD 12226–1 and -2 have been under discussion since 1995, but they are not yet ﬁnalized (in 1997). Meanwhile, E-DIN 32513–100, based on the previous German standard for solder paste, is still valid in Europe. In the USA, industry works to ANSI J-STD 005. Japanese suppliers to Europe and the USA follow the same standard, though they have their own speciﬁcation JIS-Z-3284 (communication from Dr M. Warwick, Multicore).

5.2.2 Standard specifications Solder pastes contain ﬁnely powdered solder with particles of closely deﬁned shape and size-distribution. Their composition conforms to one of the standard speciﬁcations for solders for electronic use which are outlined in Table 5.2. The solder particles are dispersed in a viscous medium which contains soldering ﬂux, a solvent or carrier, and various additives which control the physical behaviour of the paste during storage, dispensing or printing, in the period between deposition and soldering, and ﬁnally during the exposure to the heat of soldering. The ﬂux portion of the liquid phase conforms to one of the standard speciﬁcations for soldering ﬂuxes for electronic assemblies, though recent and continuing developments in soldering and cleaning technology make it diﬃcult to ﬁt some

job:LAY05 page:14 colour:1

black–text

160 Reflowsoldering

Table 5.2 Solderpaste parameters covered by US and European standard speciﬁcations Parameter Solder: Composition Particle: size

shape surface Flux: Paste: Metal content Viscosity

ANSI/J-STD 005

E-DIN 32513–100

To J-STD 006

To ISO 9453

6 ranges Spherical or elliptical No ‘satellites’ To J-STD 004

3 ranges Only spherical Not speciﬁed To ISO 9454–1

65–96% weight In centipoises, As speciﬁed by user Measured to IPC-TM-650

Slump

Measured to IPC-TM-650

Wetting Tack test Solderballing

Complete and uniform wetting of copper coupon to IPC-TM-650 Max. 3 ‘satellites’a or small number of scattered balls 50 microns dia.

Not speciﬁed In centipoises Not speciﬁed Measured on Brookﬁeld or Malcolm viscometer Measured to DIN 32513–100 Not quantiﬁed No scattered balls Max. 3 ‘satellites’

aSatellites

are small, subsidiary solderprills, which adhere to the circumference of the main solderball (see Section 5.2.6, Figure 5.3).

ﬂuxes into existing standard speciﬁcations (see Sections 3.4.3 and 5.2.4). The standard speciﬁcations also inform the user how to measure and verify such parameters of consistency and printing behaviour which aﬀect him or her.

5.2.3 Solderpowder Metal percentage and its effects Standard speciﬁcations, as well as paste manufacturers, usually give the metal content of a solder paste in per cent weight. The user, on the other hand, is more interested in the volume percentage of the solder in his paste, because he has to ﬁll a joint gap or make a solder ﬁllet, and both these tasks demand a deﬁnite volume of solder. Therefore the user needs to know how thick the paste printdown has to be or how much paste the syringe dispenser must discharge to give the volume of solder needed. Table 5.3 converts the weight percentage of the solder content of a paste into volume percentage, using the density of 63% Sn solder (8.5) and assuming a density of the ﬂux portion of 0.9 g/ml. The table shows, for example, that in order to produce a solder depot 0.2 mm/ 8 mil thick, a paste with a metal content of 90% weight will need a printdown

job:LAY05 page:15 colour:1

black–text

Reflowsoldering 161

Table 5.3 Weight per cent versus volume per cent of solder Weight % solder

Volume % solder

Best suitable for

90 85 80 75

50 38 30 24

Stencil and screen printing Screen printing, Syringe dispensing Syringe dispensing Syringe, Pin transfer

thickness (wet-thickness) of 0.4 mm/16 mil, while with an 80% paste the wetthickness will have to be 0.6 mm/24 mil. Generally speaking, the higher the metal content of a solder paste, the higher is its viscosity, which in turn determines its suitability for a given method of application. However, other factors such as the particle-size distribution and the nature of the ﬂux also aﬀect the printing or dispensing behaviour of a solder paste. It is therefore advisable to follow the recommendations of the vendor regarding the best grade of paste for a speciﬁc method of application.

Solder composition Reﬂowsoldering, like all soldering methods used for electronic assemblies, demands tin/lead solders of eutectic or near-eutectic composition. The eutectic (Section 3.3.1) with 63% tin/37% lead melts at 183 °C/361 °F, the lowest melting point within the tin/lead series. A small addition of silver to the eutectic tin/lead solder shifts the composition towards the ternary tin/lead–silver eutectic and lowers its melting point to 178 °C/352 F. Apart from this obvious advantage, there are two more reasons why such tin–lead–silver solders ﬁnd increasing use in SMD soldering. First, the silver addition slows down the rate of attack of the molten solder on silver-based substrates such as the metallized faces of certain chips (Section 3.3.3). Secondly, silver has been found to improve the strength and fatigue resistance of soldered joints.

In general international practice, the choice of solder used in solderpaste has narrowed down to two preferred compositions, a eutectic tin–lead solder, either without or with the addition of silver (see Section 3.2.4, item 3, for the beneﬁcial eﬀect of silver in solder): Solders to ISO 9453: I. 62.5%–63.5% Sn II. 61.5%–62.5% Sn, 1.8%–2.2% Ag*

melting point 183 °C/361–361 °F melting point 178 °C/352 °F

*The old DIN 1707 speciﬁed an Ag content of 1.3–1.5%. This was based on the suspicion that with 2% Ag, which is slightly above the silver content of the ternary Sn/Pb/Ag eutectic, brittle crystals of Ag Sn may form in a slowly solidiﬁed joint, such as can occur with vapourphase soldering.

See also Section 3.2.3.

job:LAY05 page:16 colour:1

black–text

162 Reflowsoldering

All major vendors are now oﬀering pastes containing lead-free solders (see Section 3.2.3). Pastes with solders of melting points other than the Sn–Pb eutectic are available for special soldering tactics. For example, a sequence of pastes with graded melting points can be used for ‘sequential soldering’, where an assembly is reﬂowsoldered more than once: the ﬁrst joints are made with a high-melting solder, later ones with solders of progressively lower melting points. This prevents the de-soldering of the ﬁrst joints, while the later ones are being made. A typical sequence of alloys would be the following: 57% Sn, 43% Bi 63% Sn, 37% Pb 96.5% Sn, 3.5% Ag 10% Sn, 2% Ag, 88% Pb

melting point 139 °C/282 °F melting point 183 °C/361 °F melting point 221 °C/430 °F melting range 302–310 °C/576–590 °F

Sequential soldering has been proposed in the past for reﬂowsoldering boards of Type II(b) (Section 2.2), with SMDs on both sides, soldering the ﬁrst side with a higher-melting solder than the second one. This complicated and expensive procedure has become unnecessary with the advent of convection reﬂow-ovens which allow the temperature of the underside of a board to be kept below the melting point of the solder (Section 5.6.3). Normally, pastes are made with fully alloyed solder powder, which means that all particles have the same composition and melt at the same temperature. At times, the attempt has been made to slow down the melting of the solder by adding a mix of pure Sn and 20% Sn/80% Pb powder to 63% Sn/37% Pb powder, maintaining the overall 63/37 composition. The aim was to avoid the ‘tombstone’ or ‘Manhattan’ eﬀect, which causes chips to stand up vertically on one end during soldering. However, a far better way to avoid this inconvenient and costly soldering fault is to pay proper attention to the correct layout of the solderpads and to good solderability of the components while working with a standard solder paste (see Sections 6.2.3 and 9.1.1).

Shape and size of solder particles The shape and the size-distribution of the solder particles, as well as their surface condition, have a pronounced eﬀect on the behaviour of a solder paste during and after printing or dispensing, and during soldering. It is now generally agreed that all solder particles should be as nearly spherical as possible, though J-STD 005 admits elliptical shapes with a maximum mismatch between length and width of 1.5: 1.0. DIN 32513 is adamant about sphericity, though it does not quantify it. The problem with non-spherical particles is their tendency to block the apertures of dispenser nozzles and the ever-narrower slots in stencils for ﬁne-pitch work, or to clog ﬁne-mesh screens. A few non-spherical particles locked against one another can soon start a ‘traﬃc block’, even if individually they are small enough to pass through the critical aperture. As a rule, the diameter of the largest particles in a given paste should be less than one-third of the width of the narrowest aperture through which the paste has to pass.

job:LAY05 page:17 colour:1

black–text

Reflowsoldering 163

Another malformation of solder particles is known as ‘satellites’. These are very small solder globules which adhere to the surface of individual solder particles, and they are mainly caused by unfavourable working parameters of the powdering process. The circumstances under which they can form are known, and are avoidable. Satellites too can lead to blocking of nozzles or screens. On automatic production lines and with close-pitch layouts, a few blocked apertures can cause a large number of costly soldering faults. The solder particles themselves should be free from surface oxide: IPC-SP-JSTD 005 wants them to be bright and smooth, because there must be no impediment whatsoever which could prevent neighbouring solder globules from fusing together as soon as they have started to melt. Solder particles free from surface oxide demand powdering procedures which operate in an oxygen-free atmosphere, and which by now have become routine. If the particles do not unite, or are slow about it, they may be left behind as small prills or globules, while the bulk of the molten solder is drawn into the joints. This is the mechanism behind the so-called ‘solderballing’, a serious functional defect of a solder paste which can cause malfunction of soldered boards in service. It is a recognized cause of rejection of any batch of paste which, when tested by the user, is found to be aﬀected (see Section 5.3.3). The size distribution of the particles is very important. Particle sizes are always given in microns (m) diameter, one micron equalling 0.04 mil. J-STD names screening, microscopy or optical image analysis as suitable methods of size determination. DIN prescribes microscopic measurement. J-STD speciﬁes six types of powder: Type 1: 80% weight of the powder 75–150 microns Type 2: 80% weight of the powder 45–75 microns Type 3: 80% weight of the powder 25–45 microns Type 4: 90% weight of the powder 20–38 microns Type 5: 90% weight of the powder 15–25 microns Type 6: 90% weight of the powder 5–15 microns At the top end of the scale, a 1% weight overshoot of size is allowed. At the bottom end, a maximum of 10% weight of the particles may be below the smallest speciﬁed size. DIN speciﬁes three types of particle size distribution: Type 1: 85% in number 75–125 microns Type 2: 85% in number 45–75 microns Type 3: 85% in number 20–45 microns At the bottom end, a 10% overshoot is allowed for particles smaller by a deﬁned amount than the bottom limit for the bulk, and below that a further 3% allowance for still smaller particles. At the top end of the scale, there is a 3% allowance for particles larger by ﬁfteen microns for type 1 and ﬁve microns for types 2 and 3. No particles are allowed larger than that. While size measurement is mainly the province of the paste manufacturer, the

job:LAY05 page:18 colour:1

black–text

164 Reflowsoldering

practical user has two particular concerns: at the top end of the particle-size range, he does not want to ﬁnd any large ‘rocks’, even one of which could block the nozzle of his dispenser or the mesh of his screen. Of equal practical importance is the absence of ﬁne dust in the micron range, because this dust can be a dangerous contributor to the solderballing eﬀect. In this context, counting is better than weighing: a simple calculation shows that 28 000 solder particles of twenty micron diameter, 225 000 particles of ten microns, and 1.8 million particles of ﬁve microns all weigh one milligram. However, whatever standard speciﬁcations prescribe, in practice it will be found that manufacturers of quality solder pastes are fully alive to the signiﬁcance of these circumstances. Vendors realize the importance of supplying their customers with a product which will not let them down during printdown and soldering. The advent of ﬁne-pitch technology (FPT) has made new demands on the properties and the performance of solder pastes. In this context, pitch denotes the centre-to-centre distance between the leads of a component. It has been said that what surface-mounting technology (SMT) was to through-hole technology, FPT is now to SMT, as far as reduction in weight and size of the assembly, closer component placement and QFPs with ever more numerous, more closely spaced leads are concerned.

A spacing of 1.25 mm (50 mil) has by now assumed the role of ‘standard pitch’. Fine pitch starts with 0.875 mm (35 mil), progressing via 0.750 mm (30 mil) and 0.625 mm (25 mil) to 0.5 mm (20 mil) and 0.3 mm/12 mil (ultra-ﬁne pitch). With FPT, the gap between two neighbouring footprints is half the pitch distance, and so is the width of the footprints themselves. The impact of ﬁne-pitch technology on the task of printing the paste onto such closely spaced, narrow solderpads is discussed in Section 5.3.2. Remembering that IPC powder Type 4 allows particles of up to 38 micron (1.9 mil) diameter, and that the narrowest aperture through which such powder has to pass during printing should be at least three times as wide as the largest particle diameter, it becomes clear that with a footprint 150 m (6 mil), FPT powders of very small particle size are required to ensure printdowns with consistent solder contents. Hence the introduction of solder-powder types 5 and 6 in the current J-STD-005 standard. Obviously, such narrow size ranges make high demands on the technology of both powder and paste manufacturers. However, particle size is not the only parameter which characterizes an FPT paste. Other relevant factors will be discussed presently.

5.2.4 The flux and its residue In the context of the residue left by a solder paste, it is logical to consider the whole of its non-metallic portion, which contains one or several solvents, thickeners, thixotropic additives and possibly other ingredients, apart from the soldering ﬂux itself. When considering the residue left by a solder paste after soldering, it will be convenient to call this whole cocktail ‘ﬂux’, and its residue ‘ﬂux residue’. The changed attitude towards cleaning, which followed the elimination of the CFC solvents (Sections 8.3.4–8.3.6), the urge to avoid the cost of cleaning and the

job:LAY05 page:19 colour:1

black–text

Reflowsoldering 165

trend towards ﬁne pitch technology are behind the drive towards no-clean solder pastes. The residue left by such pastes must satisfy the same requirements as are demanded of a no-clean ﬂux (see Section 3.4.5). This is not an easy task: no-clean ﬂuxes have a low solids content and are naturally thin and mobile. By contrast, the ﬂux portion of a solder paste must possess ‘body’, to hold the solderpowder in suspension, to give the paste the required ‘thixotropic’ behaviour and the printdown the necessary rigidity to prevent ‘slump’ (see Section 5.2.5). Additives have been developed to enable modern no-clean pastes to meet these conﬂicting requirements. Since the residue from reﬂowsoldered solder paste is strictly localized, and not likely to interfere with ATE testing with needle adaptors, the physical presence of a coating of ﬂux residue is not very important. What matters is the eﬀect of the ﬂux residue on insulation resistance, especially with ﬁne pitch, high pin-count components, and on the conformal coating or lacquering of a ﬁnished board. As a result, new pastes have reached and continue to reach the market. They fall broadly into two classes. The ﬁrst class covers low-residue pastes, containing ﬂuxes, which belong to the same family as the low-solids ﬂuxes used in wavesoldering (Sections 4.2.1 and 4.2.2). They demand reﬂowsoldering in a similar atmosphere, either in a nitrogenﬁlled convection oven (Section 5.6.5 and 5.7.1) or by a vapourphase technique, where the vapour of the working ﬂuid is suitably low in oxygen. Secondly, rosin-free pastes with a fully water-soluble residue are on oﬀer. These permit simple water or modiﬁed-alcohol cleaning and are gaining favour in situations where a cleaning process is obligatory, irrespective of the type of ﬂux used.

5.2.5 Printing and dispensing properties The consistency of a solder paste determines its behaviour during and after printing or dispensing. Both methods of putting the paste down on a board make precise and quantiﬁable demands on the paste during its deposition, and on its immobility once it sits on its pad. The apparent contradiction between these two requirements is taken care of by a characteristic ﬂow behaviour, which solder paste shares with many dispensable substances from decorators’ paint to mayonnaise, known as ‘thixotropy’. Speciﬁcally as applied to solder paste, the term ‘pseudoplasticity’ has been proposed as more ﬁtting. In practice, both terms mean that the eﬀective viscosity of the solder paste depends on the rate of shear or the force of deformation which acts upon it. In simple terms, it moves easily when it is pushed: the harder it is pushed the more easily it moves. When left alone, it stiﬀens and retains its shape. In the terminology of solder paste usage the lack of the latter property is called ‘slump’ or ‘spread’. The slump behaviour of a given paste is naturally of great signiﬁcance with ﬁne-pitch work.

Viscosity and its measurement Viscosity is an often quoted and certainly important property of a given solder paste, but thixotropy makes its measurement diﬃcult. Viscosity is deﬁned as the resistance

job:LAY05 page:20 colour:1

black–text

166 Reflowsoldering

of the paste to movement. Measuring viscosity involves measuring the force needed to move a sample of paste in a deﬁned way. Thixotropy means that the force needed to move the paste depends on the rate of movement of the viscometer, a Catch 22 situation which can only be resolved by accurately deﬁning the test conditions. Even so, the viscosity of a solder paste is given by most vendors within very wide margins, hardly ever as a deﬁnite value. Generally speaking, the higher the metal content of a paste the highers its viscosity, other things being equal. In practice, they hardly ever are. With ﬁner solderpowder, the paste becomes more mobile and its viscosity is lower for a given metal content. At the same time, it shows less slump, which is not surprising: it is easier to make a good mudpie out of sand than out of gravel. The contribution of the ﬂux portion of the paste to its ﬂow behaviour and the shape-retention of the printdown plays an important part in its suitability for ﬁne-pitch work. It has been shown that, if a paste printdown remains immobile during the heating stage of reﬂowsoldering, lateral spread of the melting solder is much reduced, and with it the danger of bridging between closely spaced solderpads.

Federal speciﬁcation QQ-S-571E lists a range of solder paste viscosities set against their metal content and recommended methods of application (Table 5.4). ANSI-SP-J-SDT 005 does not prescribe or recommend viscosity ranges for a given method of paste application; it only speciﬁes how to measure the viscosity of pastes within a given viscosity range, using a Brookﬁeld RVTD Viscometer. DIN 32513, recognizing the complex nature of paste viscometry, prescribes measurement at three diﬀerent rates of shear, and gives a choice of test methods, including one using a Brookﬁeld RVTD and another one which simulates syringe dispensing. Again, no absolute viscosity values are suggested. The aim of standardizing viscometry is to enable vendors and purchasers to speak the same language. The man on the shopﬂoor, who has to produce consistently faultless prints without too much trial and error when he opens a fresh tin, wants to know whether today’s paste will behave in the same way on his printing frame or his machine as yesterday’s paste. Table 5.4 Solder paste viscosities and methods of application (according to Federal Speciﬁcation QQ-S-571E) Code no.

Nominal metal content (% weight)

Range of viscosities (centipoises)

Examples of application

2 2 3

90 88 86

800.000–1.000.000 600.000–800.000 400.000–800.000

4

81

300.000–400.000

5

75

200.000–300.000

Stencilling Screenprinting Screenprinting/Syringedispensing Screenprinting/Syringedispensing Pin-transfer

job:LAY05 page:21 colour:1

black–text

Reflowsoldering 167

A Brookﬁeld RVTD or the Malcolm spiral pump viscometer will tell him that, within a margin of ±10%. This instrument, operated in the ‘Helipath’ mode or one of its equivalents, is the best choice for bench viscometry: the test can be carried out without having to take any of the paste out of the tin as long as the tin is at least 5 cm/2 in high and wide. Thus, little if any of the expensive paste is wasted. Before the test, the tin is stirred with a clean stainless steel or plastic spatula to counteract any settling out of the metal – it is as well to do this in spite of the advertised antisettling properties of a paste. After stirring the paste, it is advisable to wait a few minutes to let the paste recover its true viscosity before measuring it. Viscometry requires a certain amount of skill and experience – but so do screen and stencil printing. The results are bound to show some scatter; in particular they are very operator-dependent, and it is therefore best to entrust viscometry always to one particular operator (Dr M. Warwick, Multicore, UK, private communication). A further ﬂow property of solder paste has recently been introduced in the form of a ‘yield limit’. This quantiﬁes the shear force above which a body of paste begins to move, and which appears to have no direct relation to the measured viscosity of the paste. A high yield limit is said to make the paste appear ‘gooey’ and stick to the squeegee, too low a yield limit causes the paste to form a ‘wave’ rather than a ‘roll’ in front of the squeegee, and to increase the slump of the paste printdown. Measuring the yield limit involves determining the shear force between a stationary and a rotating disc, the gap between them being ﬁlled with the solder paste.

5.2.6 The solderball test The success of a reﬂow process depends critically on the way in which the paste behaves during soldering. One important aspect of this is the capability of a paste printdown to gather all its individual solder particles into one coherent volume and into the joint which it is meant to ﬁll, without leaving any stray solder prills behind. This property can be readily checked with the ‘solderball test’, a simple procedure which was originated by Philips many years ago. It is now incorporated in every relevant standard speciﬁcation for solder paste (see Table 5.2). IPC-TM-650 Test Methods Manual and the still valid German DIN 32 153 prescribe the following procedures. Using a suitable metal stencil, three circular deposits of the paste to be tested, 6.5 mm (or 1.5 mm) in diameter, and 0.2 mm (or 0.1 mm) thick, (6.5 mm diameter and 0.2 mm thick in DIN 32 513) are produced on a non-tinnable support such as a thin sheet of stainless steel or a ceramic wafer. The specimen is then heated to a temperature 25 °C/45 °F above the liquidus temperature of the solder alloy in the paste (near enough 183 °C/361 °F for normal electronic solder pastes), which means a test temperature of 208 °C/406 °F. The simplest way of heating the support coupon is by ﬂoating it on a small, thermostatically controlled solderbath. After 20 seconds, the solder in all three deposits should have melted and each have formed a single ball of solder with perhaps a ‘halo’ of a few individual small balls of 75 microns/3 mil at some distance. The German speciﬁcation DIN 32513 is stricter, permitting 3 ‘satellites’ adhering to the solderball itself. IPC-TM-650 stipulates that one test is carried out within 15 minutes after stencilling the paste on to the test coupon, and a second one 4 hours later. As soon as

job:LAY05 page:22 colour:1

black–text

168 Reflowsoldering

the solder in the paste print-down has melted, but not later than 20 sec. after it has been launched on the solderbath, the test-coupon is lifted oﬀ and allowed to cool. DIN 32 513 stipulates a waiting period of 1 hour and another one of 72 hours between print-down and melting, and a solderbath temperature of 215 °C/420 °F. This test is so simple to perform that it can and should be used on the shopﬂoor every time a fresh tin of paste is opened, or before paste which has been recovered from the printing frame at the end of a run is used again for printing. Some vendors of paste can supply stencils for the solderball test. Alternatively, a stencil can be punched from a sheet of metal. More simply, punching a hole through a selfadhesive paper label folded double upon itself with a normal oﬃce paper-punch will produce a stencil aperture for a paste printdown with a diameter of 5.5 mm and a thickness of 0.2 mm, which is adequate for a reproducible practical test result (Figure 5.3). The test specimen can be heated by placing it on a hotplate, though for preference it should be ﬂoated on a small solderbath which is thermostatically held at the test temperature. In actual paste-printing and reﬂowsoldering practice, test temperatures tend to diﬀer somewhat from the prescriptions of ANSII/PC-SP-JSTD 005: if the paste is to be used for reﬂowsoldering in an infrared oven, a test temperature of 250 °C/452 °F is preferred. If reﬂowsoldering is carried out in a vapourphase installation, the test temperature will be the same as the vapour temperature, i.e. 215 °C/419 °F. It is normal practice to commence using the tested paste for production as soon as the solderball test has been carried out and proved satisfactory. It is wise, however, especially when starting with a new delivery of paste, or when testing an alternative product, to set some test specimens aside and heat them after the maximum time which will elapse between printing down the

Figure 5.3 The solderballing test. 1. Making the stencil from a self-adhesive label; the paste printdown made with it; 2. Results: (a) paste printdown; (b), (c) acceptable results; (d), (e) unacceptable results

job:LAY05 page:23 colour:1

black–text

Reflowsoldering 169

paste and soldering the fully assembled boards on a given production line. The German DIN standard prescribes waiting times of one and seventy-two hours as a regular test procedure. The solderball test checks whether the ﬂux in the paste is capable of retrieving all the solder particles from that portion of the printdown which has been squeezed out beyond the conﬁnes of the solderpad during the placement of an SMD, so that they do not form stray solder globules. Oxidized solderpowder, old or insuﬃciently active ﬂux, deterioration during storage, or loss of volatile but essential ﬂuxconstituents during previous use may all contribute to the formation of stray solder globules. As is discussed in Section 11.2.2, such globules are a disqualifying soldering fault with most classes of electronic assemblies.

Predrying At one time, it was considered necessary to predry circuit boards between placement of the components and reﬂowing by whatever process, at a temperature between 80 °C/176 °F and 100 °C/212 °F for about 30–60 minutes. This was in order to ‘precondition’ the paste so that it should not misbehave during soldering: spitting and causing solderballs, or allowing the components to ‘swim’ or to stand upright, forming tombstones, for example. Most modern pastes do not require circuit boards to be predried, and IPC-TM-650 does not prescribe predrying in its testing schedule, though the German DIN 32513 does.

5.3 Putting the solder paste on the board The basic task here is to put the right amount of paste into exactly the right place. There are two ways of doing this. With sequential placement or dispensing, machines, single or, with some methods twin, circular dots of paste of controlled size are deposited on their footprints, either manually or mechanically. More usually in present-day practice, printing, either through a screen or a stencil, puts paste on every footprint on a board simultaneously in one operation. With printing, the shape of the paste deposit matches the outline of the footprint on which it is placed, with certain provisos which will be discussed later. Printing requires a ﬂat board surface, free from any obstruction such as the projecting ends of connecting wires or leads of components inserted from the other side of the board (see Section 5.1.1). Whenever paste has to be put down on a board surface which is not strictly ﬂat, printing is impracticable and a dispensing method must be used.

5.3.1 Single-spot dispensing Repair work is one main ﬁeld for single-spot dispensing, when either an open joint has to be ﬁlled with solder or a replacement component has to be soldered in position. For these tasks, the paste is dispensed either from a hand-held syringe,

job:LAY05 page:24 colour:1

black–text

170 Reflowsoldering

which may be operated with compressed air controlled by footpedal or ﬁnger action, or from a hand-operated dispenser gun. With all of these methods, the dispensing tool can be set to discharge a ﬁxed, constant amount of paste at every stroke, or else every discharge can be operator-controlled. Many vendors supply dispensing tools or guns suitable for clip-on paste cartridges. Dispensing solder paste onto footprints on a three-dimensional substrate like the body of a mobile telephone is a novel ﬁeld of use for single/spot dispensing (see Section 6.2). With this technique, the dispensing syringe is usually positioned and actuated by a robot device. Some automatic pick-and-place machines are ﬁtted with twin syringe dispensers fed from paste cartridges. They put down metered amounts of solder paste on the solderpads of bipolar components like melfs and chips prior to their placement. Metered syringe dispensing demands a paste of constant viscosity. This means either a stable temperature in the workroom, or a paste with a reasonably temperatureinsensitive viscosity. For accurate dispensing, the paste in the cartridge must be absolutely free from trapped air bubbles. Otherwise, accurate metering becomes impossible and, what is worse, the sudden bursting of an airbubble, as it reaches the tip of the dispensing nozzle, scatters small drops of paste in the neighbourhood, leading inevitably to a multitude of solder prills. The exact put-down location for the paste depends on the type of joint. With melfs and chips, the paste deposit must touch the metallized ends of the component but it should not be squashed underneath its body, since this can cause stray solder globules left underneath. For components with ﬂat legs or leads, the paste is deposited in the middle of the footprint. The amount of paste put down should provide just enough solder to completely ﬁll the joint, while the edges of the lead remain visible, or to give the solderﬁllet at both ends of the melf or chip a concave proﬁle, but no more than that. Naturally, the metal content of the paste by volume (see Table 5.2) must be borne in mind when working out the dosage (Figure 5.4). Several vendors oﬀer equipment for the mechanized, processor-controlled and programmable placement of a pattern of paste dots of controlled size on one or a run of circuit boards. One suggested use is the placement of solder paste on short runs of boards, where the preparation of a special screen or stencil would be uneconomical or too slow. With these applicators, a mechanically or pneumatically actuated dispenser cartridge is mounted on a gantry-type xy plotter, which straddles the board (see Figure 4.33). The software which controls the location and size of the individual dots of paste can be derived from the board layout, or created by teach-in and stored. The lateral accuracy of the placement coordinates is reported to be within 0.2 mm/ 80 mil, using automatic sighting of a ﬁducial reference mark on the board. Metered dispensing with a screw-feed mechanism is the preferred method of discharge, to prevent settling-out of the solder from the paste and consequent nozzle blocking through repeated pneumatic or piston impulses during operation. Put-down rates of 13 000–16 000 dots/hour are quoted for single-nozzle applicators, and up to 25 000 dots for twin nozzles. A further ﬁeld of application for this type of equipment is the placement of solder paste on boards on which the joints are located on diﬀerent levels, or where obstructions on the board surface prevent the

job:LAY05 page:25 colour:1

black–text

Reflowsoldering 171

Figure 5.4 Placement of solder paste by dispensing. (a) Unsuitable nozzle shape; tends to block; (b) recommended nozzle shape; (c) nozzle too close to footprint; squashing of paste deposit

use of a screen-printing or stencil-printing method. To meet this need, the location of the paste discharge nozzle in the vertical z axis is variable and programmable. The same type of equipment can be used for putting down drops of adhesive for anchoring SMDs to a board prior to wavesoldering (Sections 4.9 and 5.1.1).

5.3.2 Stencilling and screen printing Stencil versus screen Stencilling and screen printing are the most widely used methods for putting solder paste on printed circuit boards. Both demand a free, unobstructed and ﬂat board surface. Flatness is important for a precise printdown without smudging or lateral squeezing out of the paste. The solder resist too should be of equal thickness over the whole board, because the surface of either acts as a gasket against the screen or stencil, and prevents lateral squeeze-out of the paste. As far as the choice between stencilling and screen printing is concerned, most industrial users tend to opt for stencilling unless the company concerned has in-house screenmaking facility and expertise. The distinctive virtue of screen printing is its ability to create ring-shaped patterns like an ‘O’, being able to support the central dot on the mesh of the screen. Since solder paste is almost always printed in solid squares and rectangles, there is no compelling need for a screen. High print quality and precision can be achieved with either method. Metal stencils generally cost less and making them requires less specialized skill. Stencils are easier to store, more forgiving towards mishandling and, if properly treated, will last longer than screens. The thickness of the printdown equals the thickness of the stencil, while with screen printing both the nature of the mask and of the screen determine the thickness of the printdown. Above all, with ﬁne-pitch technology,

job:LAY05 page:26 colour:1

black–text

172 Reflowsoldering

footprint dimensions and distances are getting ever smaller, pushing screenprintability to its limits, if not beyond. Stencilling allows local reduction of printdown thickness, by thinning the stencil by local reduction in thickness. This is useful when individual ﬁne-pitch components require less paste deposit than the rest of the board population. However, there is a penalty involved: to allow the squeegee to drop down to the lower level of the etched-back area, this area must extend by 3–5 mm (120–200 mil) beyond the ﬁne pitch footprints, which wastes valuable real estate. The preferred alternative is to make the apertures in the stencil shorter than their corresponding footprints in order to reduce the amount of paste on the ﬁne-pitch footprints.

Thickness and dimensions of the printdown From the soldering point of view, it is crucial that every pad receives the correct amount, i.e. volume, of solder needed to ﬁll the joint. What interests the printer is the thickness of solder paste deposit (called the wet-thickness) which must be put down on the board. The ratio wet-thickness/solder-thickness depends on the metal content of the paste and can be derived from Table 5.3. Table 5.5 is based on these values and lists the relationship between wet-thickness and solder-thickness for the two types of paste normally used for stencilling. When deciding on the amount of paste which footprints are to receive, it is perhaps wise to err, if at all, on the generous side. In subsequent inspection and correction it is easier to detect and remove the occasional solderbridge than to ﬁnd and ﬁll a solitary empty joint, especially with ﬁne-pitch work. Another problem with the thin deposits of ﬁne-pitch printing is the high degree of coplanarity of the legs of multilead components which a thin printdown demands. Typical coplanarity tolerances are 25–75 microns (1–3 mil). Lack of coplanarity obviously increases the risk of open joints. The above-mentioned shortening of the length of the printdown and use of a thicker stencil is a simple way out.

Stencils and stencil printing Stencils for paste printing are mostly made from sheet metal, usually hard-rolled brass. For demanding work and ﬁne-pitch printing, beryllium copper, nickelTable 5.5 Thickness of solder paste printdown and of soldercoating Stencil thickness = wet-thickness of paste

Thickness of solder cover with paste 90% wght/50% vol 95% wght/67% vol of solder of solder

mm

mil

mm

mil

mm

mil

0.30 0.25 0.20 0.15 0.10

12 10 8 6 4

0.15 0.125 0.10 0.07 0.05

6 5 4 3 2

0.2 0.17 0.13 0.10 0.07

8.0 6.7 5.4 4.0 2.7

job:LAY05 page:27 colour:1

black–text

Reflowsoldering 173

chromium or stainless steel are preferred. A more recent development are plastic stencils. The advantages claimed for them is their ﬂexibility, which accommodates slight surface irregularities of the substrate, easier cleaning, long life and a clean lift-oﬀ from the paste printdown. Stencil apertures are often cut to the design of the customer by the vendor or by specialist supply houses. Stencil thickness ranges from 0.75 mm/30 mil to 0.1 mm/4 mil for ultra-ﬁne pitch work. There are a number of ways of creating the printing apertures. For short runs or prototype work, the stencil openings can be produced by drilling instead of etching. Stencil thickness and hole diameters must of course be suitably chosen to provide the required amount of solder paste for each pad. Drilling requires a precision drilling machine with optical registration or a numerically controlled circuit board drilling machine. With the majority of metal stencils, the printing apertures are created by etching, normally from both sides. For that purpose, both sides are pre-coated with a photomechanical etch resist, often by the vendor of the stencil sheets. The stencil pattern can be derived from software for the artwork for the board. To allow for possible misregister between stencil and the circuit board pattern, it is customary with standard pitch work to make the linear dimensions of the openings in the stencil somewhat smaller than those of the corresponding footprints, but the etch resist pattern must also make allowance for the undercutting of the stencil sheet around the outline of the apertures during etching. Double-sided etching is often carried out in such a way that the apertures are wider towards the underside of the stencil, which faces the circuit board. This aims to reduce the risk of paste sticking to the sides of an aperture. This can be a danger with ﬁne-pitch work, where the area on the footprint to which the paste must stick comes close to the area of the sidewalls of the stencil aperture, which should neatly slide away from the printdown as the stencil is lifted from the board after printing. For this to happen without fail requires not only a correctly etched stencil, but also a solder paste with ﬁnely adjusted stickiness and drying behaviour. With ultraﬁne-pitch work, this measure is no longer enough. Stencils with laser-cut straight-walled apertures are available from several vendors. Obviously, the cost of a lasercut stencil is proportional to the number of apertures rather than the size and complexity of the pattern, as with etched stencils. Nickel-plated brass stencils or molybdenum stencils, available in the US, are said to give particularly clean lift-oﬀ from ultraﬁne pitch paste-prints.

Stencil printing Stencils in sizes of up to 170 mm–250 mm (7 in–10 in) can be used in simple hand-operated stencil printers. The stencil is held in a hinged frame which can be lowered onto the board, which itself is held on a vacuum table and located against movable locating pins. Within this size range, high-precision printing can be obtained. Larger formats should only be printed on such equipment if the print pattern is a simple one and high precision is not required. Because the stencil is held in the frame without being tensioned, larger formats tend to sag. This leads to

job:LAY05 page:28 colour:1

black–text

174 Reflowsoldering

inaccurate deposition and can cause smearing of the paste on the substrate. Larger stencils should be used on a regular screen-printing machine. The accurate register between the stencil and the footprint pattern on the board is critical. Whatever the pitch of the footprint pattern, all of a paste-print must be deposited within the conﬁnes of its respective footprint. With an ultraﬁne pitch of say 0.3 mm/12 mil, the footprints are only 1.5 mm/6 mil wide, which means that the stencil must be aligned relative to the print pattern on the board to an accuracy of within 0.1 mm/4 mil in the x and y axis. This makes high demands not only on the precision and repeatability of the board pattern, but also on the skill of the paste printer. With in-line printing machines, automatic alignment systems based on video recognition of ﬁduciary marks are used. With manual printing frames, alignment should be veriﬁed by setting up the stencil with a ;10 magniﬁer for every print.

An in-depth discussion of the operational details of stencil printing goes beyond the conﬁnes of this book. A number of excellent publications and books are available to the practitioners of paste printing. Printing solder paste to circuit boards on high-performance special-purpose screenprinting machines has grown into an important technology, catered for by several major vendors. Most practitioners of stencil printing agree that the stencil should be placed in direct contact with the circuit board, without the ‘snap-oﬀ’ which is used with screen printing. This measure ensures maximum precision and avoids smearing of the paste over the edges of the printed areas. A hard rubber squeegee within the range of 75–95 shore with a diamond cross-section is often recommended. The rigidity of the hard diamond edge reduces ‘scoop-out’ of paste from the larger stencil apertures. Where stencils with locally reduced thickness (see above) are used, a blade-shaped rubber squeegee instead of a diamond will provide the elasticity required for the blade edge to follow the contour of the stencil. An increasing number of practitioners, on the other hand, prefer a steel blade as a squeegee. With ﬁne-pitch work, it has been reported that narrow rectangular stencil apertures which are parallel with the direction of travel of the squeegee ﬁll well with solder paste, but right-angle ones ﬁll poorly. Since this situation arises with square components such as quadpacks, it may be preferable to place these diagonally on the board and accept the loss of valuable board surface rather than a low yield on soldering. In any case, with ﬁne-pitch work, a low squeegee speed is recommended. Speeds of 1 cm–4 cm (0.5 in–1.5 in) per second have been mentioned, while with standard pitch 5 cm–10 cm (2 in–4 in) per second are normal. With stencils, both the forward and the return travel of the squeegee are used for printing. At the end of a stroke, the squeegee is lifted over the remaining paste and travels back again, pushing the paste before it. The printing pressure should be such that the stencil surface is wiped clean by the advancing squeegee. Though stencil pastes are more viscous and stiﬀer than pastes for screening, the stencil apertures are not obstructed by the mesh of a screen and therefore pressures need not be higher than for screen printing. Excessive pressure leads to smudging under the stencil and to early wear or deformation, especially of the narrow bridges between neighbouring apertures in ﬁne-pitch work (coining). At the start of a stroke, the squeegee is set

job:LAY05 page:29 colour:1

black–text

Reflowsoldering 175

down on the stencil, not on the surrounding screen, and the same is true for the end of the stroke. Equally, the length of the squeegee should be less than the width of the stencil. Both measures ensure that the screen which supports the stencil is not damaged or strained, which would aﬀect the register between printdown and the circuit board. In conclusion, it can be said that stencilling, which can cope with practically every task of solder paste printing, is a technique which demands manual skill and a conscientious approach, but which can be mastered by in-house training.

Screens and screen printing In contrast to stencil printing, screen printing demands a good deal of experience and skill and requires the control of a considerable number of parameters which inﬂuence print quality. Silkscreen printing is a profession in its own right which demands an extended apprenticeship. The use of screen printing as a means of putting down solder paste on circuit boards is decreasing. Screen printing is not really suitable for ﬁne-pitch work: the presence of the screen wires in the printing apertures complicates their geometry and interferes with the clean transfer of the paste from the apertures to the footprints which is so essential with ﬁne-pitch and ultraﬁne-pitch technology. Therefore only some basic factors which distinguish screening from stencilling need be mentioned here. For a detailed account of the technique, one of the many excellent books on silkscreening should be consulted. Printing screens are fabrics, woven from a large variety of materials such as polyester or polyamide. Stainless steel fabrics are sometimes recommended for solder paste printing because of their superior wear resistance against the solder particles. They are, however, unforgiving towards mishandling such as kinking or creasing and should be used only by professionals. The fabric is tensioned and bonded to the screen frame so that the threads run diagonally across the frame. This is to ensure the required precision and deﬁnition of the contours of the apertures, which run normally parallel to the sides of the frame. Screen fabrics are characterized by their mesh number, that is the number of openings per linear inch (or cm), and by the thickness of the thread. Both of them taken together determine the width of the mesh opening, which can range from 400 micron/16 mil down to 72 micron/2.9 mil. As a rule, the diameter of the largest solder particles in a given solder paste should be not larger than one-third of the mesh opening of the screen with which the paste is being printed. The printing pattern on the screen is created by coating it with a light-sensitive layer of photopolymer emulsion or bonding a photopolymer-ﬁlm of a given thickness to it in such a manner that, in printing, the squeegee bears against the photopolymer, not against the screen fabric. The polymer is then exposed to strong ultraviolet light, using a pattern derived from the circuit board artwork as a mask in the same way as has been described above for the etch resist pattern of a stencil. The unexposed portions of the photopolymer are water soluble and are washed out in water. When no longer required, the photopolymer mask can be washed from the screen, which can be recoated and used again. In contrast to stencilling, the screen is held at a small distance (‘snap-oﬀ’) from

job:LAY05 page:30 colour:1

black–text

176 Reflowsoldering

the board which is being printed, 1.0 mm–1.5 mm (40 mil–60 mil) being normal. Because of the elasticity of the screen, the downwards pressure of the squeegee overcomes the snap-oﬀ and creates a line-contact between screen and board, which traverses the board. Along this line, the paste, having been pressed through mask and mesh, is deposited on the board. Behind the moving line of contact, the screen lifts oﬀ the board, leaving the paste printdown on the board (Figure 5.5). The thickness of the paste printdown does not have the simple relationship with the thickness of screen-plus-mask that it has with the thickness of the stencil in stencilling, because the threads of the screen take up some of the space in the printing apertures. Its exact value will have to be determined by trial. With screen printing of solder paste, as with stencil printing, the squeegee is lifted over the left-over paste, additional paste being added when necessary, and the next board is printed on the return stroke. The ‘ﬂooding stroke’ between two printing strokes, which is customary for screen-printing with ﬂuid inks and which serves to redistribute the ink after a printing stroke, is not normally practised with solder paste printing. Certain adjustments may have to be made to the register of the second board to accommodate the slight shift in the position of the screen mask due to its elasticity.

Care of stencils, screens and paste At the end of a printing run, the stencil or the screen must be cleaned at once. Dried paste in an aperture reduces its area and thus starves the corresponding footprint of paste and therefore solder, which puts the formation of the joint at risk. If this type of fault passes undetected during the next printing run, locating and correcting the fault may become very costly. For cleaning, the stencil or screen is taken from the machine and laid ﬂat on a

Figure 5.5 Screen printing by hand

job:LAY05 page:31 colour:1

black–text

Reflowsoldering 177

bench covered with paper. Cleaning the screen or stencil in situ is bad practice, because paste and/or solvent are liable to drop into the machine or on to the vacuum bed. The bulk of the left-over paste is removed from the stencil or screen with a ﬂexible, blunt spatula; the remainder can be removed by hand using a squeegee as a scraper. Much of the paste remaining in the apertures will be pulled out of them when the paper which covered the bench is peeled away. The stencil or screen is then washed with a solvent, often speciﬁc to a given paste and obtainable from the paste supplier. The use of stencil or screen washing equipment, a wide range of which is commercially available, is recommended, because stencils, especially thin ones, are delicate, easily damaged and diﬃcult if not impossible to repair. Their replacement costs not only money, but also valuable if not critical time. Paste left over after a printing run or a shift need not be dumped, but it should on no account be returned to the tin or jar it came from, which still contains fresh, unused paste. Left-over paste goes into a separate, marked container, and must undergo the ‘solderball’ test (Section 5.2.6) before re-use. As soon as possible, lids must be replaced on tins or jars, which must never be left standing around open, nor in sunlight even when closed. After removing paste from a tin, or after putting left-overs back into one, any paste adhering to the sides is scraped back into the bulk, which should sit neatly in one coherent mass. If necessary, the contents of a tin can be compacted by tapping it down against the benchtop. Thin smudges of paste spread around the inside of a container will dry, and having dropped back into the paste, can block a stencil or a screen. After opening a paste container, it is good and safe practice to brieﬂy and gently stir the contents for a few seconds with a clean spatula, preferably made of plastic, before loading the paste onto the stencil or screen. Even the best of pastes may form a thin layer of solvent, or at least of more dilute paste, on top of the bulk after prolonged standing. Long or violent stirring must be avoided: the thixotropic or pseudoplastic nature of the paste means that the shearing force of stirring it lowers its viscosity. A paste needs a certain recovery time, which varies from one to the other, before it regains its inherent ﬂow properties and printing behaviour. The stronger the shearing force, the longer will the loss of viscosity persist. Solder pastes which must be stored in a refrigerator, at, for example, 4 °C/39 °F, so as not to settle out or to deteriorate are becoming rare. In any case, a container taken from the refrigerator must never be opened before its contents have been given enough time to attain room temperature. Normally this means taking the next day’s supply of paste from cold storage on the evening before, and putting it on a bench in the printing shop. If a container is opened while still colder than the ambient air, atmospheric moisture will condense on the paste and as likely as not spoil its printing and soldering behaviour. Lastly, the label of every paste container carries, or should carry, a use-by date. This date is disregarded at the peril of a run’s, if not of a day’s, wasted production. One last warning: a solder paste should not be tampered with. Even if the printer feels that a few drops of thinner or a pinch of ﬁne solderpowder would make the print come out even better, there is every likelihood that the soldering behaviour is

job:LAY05 page:32 colour:1

black–text

178 Reflowsoldering

going to be worse. If the print does not come out as it should, alter the printing parameters, but do not ‘improve’ or ‘adjust’ the paste. Solder pastes are the result of a careful balance between the demands of printing and of soldering, and this balance is a delicate one.

5.3.3 Depots of solid solder As the distance between footprints drops below 0.5 mm/20 mil, putting down depots of solder paste with suﬃcient accuracy, and soldering without unacceptable numbers of bridges or misses, becomes progressively more diﬃcult and expensive. Separating solder and ﬂux from one another and applying ﬁrst the solder, then the ﬂux, may seem a retrograde step after the simple concept of applying both of them together: however, in recent years, several proposals have been made which emphasize the merits of this approach.

The essence of these proposals is the creation of ﬂat depots or pads of solder, each of controlled and even height and of predetermined volume, fused to every footprint. Flatness is important, because the domed proﬁle of the solder depots on hot-air levelled circuit boards is unacceptable for the safe and precise placement of the thin, ﬂexible legs of close-pitch multilead components (Figure 5.6). Creating the ﬂat solder depots is part of the manufacturing process of the circuit board, and thus the responsibility of the board manufacturer (Section 6.4.4). Boards with preplaced solder as described in that section have meanwhile become commercially available. The preplaced solder depots relieve the board assembler of the tasks of handling solder paste and of screen-printing or stencilling it on to the boards, with all the headaches that this technology implies. He has only to ﬂux the boards, or selectively the footprints, and then to place the components before reﬂowsoldering. The ﬂux must remain suﬃciently sticky after being applied to a board or footprint, so as to hold the placed component securely before soldering. For selective application to the individual footprints it must also be screen or stencil printable. Fluxes which meet these demands are on the market. For impulse-soldering or thermode-

Figure 5.6 Danger of domed solder depot

job:LAY05 page:33 colour:1

black–text

Reflowsoldering 179

soldering of individual multilead components on the other hand, the ﬂux, which should be quick drying, is normally applied by hand (Section 5.9).

5.4 Vapourphase soldering 5.4.1 The basic concept Vapourphase soldering (or condensation soldering, as it was called originally) makes use of an elegant concept of heating the joints. When a cold body is placed in the saturated vapour of a boiling liquid, the vapour instantly condenses on its surface, giving up its latent heat of condensation in the process. This continues until the body has reached the same temperature as the vapour. Very stable and chemically inert organic ﬂuids with boiling points above the melting temperature of electronic solders, i.e. above 183 °C/361 °F, are commercially available as ‘working ﬂuids’.

In the light of present knowledge they do not add to the depletion of stratospheric ozone, being free of chlorine. Their contribution to global warming is probably negligible because of their low volatility (Section 8.3.5). With the growing use of BGAs (Section 2.2) vapourphase soldering has gained in importance. When soldering a BGA to a circuit board, the board should be heated from above and below and must reach the full soldering temperature at the same time as the bumps underneath the BGA. With vapourphase soldering, this is achieved automatically; with infrared and convection ovens, the oven design and the manner of its operation must allow for this requirement to be met. The working principle of vapourphase soldering is delightfully simple and elegant, but its physics are somewhat complex. Also, the high-boiling working ﬂuids are not cheap, with prices in the neighbourhood of £70–80 or over $100 per kg. Vapourphase soldering represents an ‘equilibrium situation’ (Section 5.1.2): the items to be soldered attain the same temperature as the source of heat, i.e. the vapour in which they are immersed. With the usual working ﬂuids, this temperature is 215 °C/419 °F. There can be no overheating, and at the end of the soldering cycle all parts of the circuit board have reached more or less the same temperature. Furthermore, the working vapour is heavier than the normal atmosphere, which it displaces from the soldering chamber. Consequently, less than 5 ppm by volume of oxygen (private communication from Mr R. Wood, BNFL Fluorochemicals) is present during the heating and soldering cycle, which thus amounts to soldering in a controlled atmosphere with all the consequent advantages (Section 5.6): the absence of oxygen makes it possible to use no-clean solder pastes and beneﬁt from their many advantages (Section 5.2.4). Metallic surfaces do not oxidize while they are being heated to soldering temperature. This helps the solder paste to climb up the vertical end faces of chips and melfs and make joints with good, ‘lean’ proﬁles (Section 9.3) (Figure 5.7). The vapour in the working chamber of a standard vapourphase soldering installation is a so-called ‘saturated vapour’. By this is meant that the vapour is in direct contact with the boiling ﬂuid from which it is formed, and that its temperature is that of the boiling point of that ﬂuid. As soon as a cold body is introduced into a

job:LAY05 page:34 colour:1

black–text

180 Reflowsoldering

Figure 5.7 The working principle of vapourphase soldering. TB = TV = Boiling temperature of the working ﬂuid; TS = Temperature of the item to be soldered TV

saturated vapour, the vapour condenses on its surface, giving up its heat of evaporation. That is the reason for the rapid initial heating rate ( 4 K/sec), characteristic for conventional vapourphase soldering, which can have some undesirable consequences (see below).

5.4.2 Vapourphase working fluids At the time of writing (1997), vapourphase working ﬂuids are made and marketed by three vendors (Tables 5.6 and 5.7). While the ﬂuids themselves are non-toxic, certain precautions must be observed when using them in soldering installations. These will be discussed later.

5.4.3 The physics of vapourphase soldering The thermodynamics of heat transfer by condensation The rate at which thermal energy is transferred from the working vapour to the circuit board depends on the temperature diﬀerence between the two. The heat transfer at any given surface area on the board stops when it is as hot as the surrounding vapour. This fact has two consequences:

job:LAY05 page:35 colour:1

black–text

Reflowsoldering 181

Table 5.6 Description of working ﬂuids Vendor

Name

Description

Constituents

Boiling point or range

3M

Fluorinert FC-70 Fluorinert FC-5312

Perﬂuorotriamylamine

C, F, N

215 °C/ 419 °F

Monteﬂuos

Galden LS 230*

Perﬂuoroether

C, F, O

225 °C– 235 °C/ 437 °F– 455 °F

RhonePoulenc

Flutec PP11**

Fluorocarbon

not available

215 °C/ 419 °F

*Grades with higher boiling ranges are available. **Grades with lower and higher boiling points available. Table 5.7 Important properties of working ﬂuids and other relevant substances Substance

Speciﬁc gravity

Thermal conductivity watt/cm/°C

Density of vapour

FC 70 FC 5311 LS 162 Flutec PP1

1.94 2.03 1.82 2.03

0.0007 0.0005 0.0007 not available

not available 13 ; air 16 ; air not available

Freon (R113) SF-2–I

1.57

0.0007

6 ; air

Cu FR4

3.9 0.002

1. The rate of heating is initially high, up to 40 °C/70 °F per second, but it gets slower the nearer the surface temperature of the board, and the components and solder joints on it, get to the temperature of the vapour. 2. Solids with a good heat conductivity and low speciﬁc heat (for instance metals like copper or solder) heat up more quickly than substances with low heat conductivity and high speciﬁc heat, such as ceramics, FR4, rosin, and the working ﬂuid itself. A further factor to be considered is the thermal diﬀusivity of solid bodies, which governs the heat ﬂow from the surface into their interior. The thermal diﬀusivity behaviour of a body depends on its thermal conductivity, its speciﬁc heat and its density, and it determines how quickly the bulk of the body assumes the temperature of a hot medium in which is immersed.

job:LAY05 page:36 colour:1

black–text

182 Reflowsoldering

Table 5.8 shows the practical consequences of thermal diﬀusivity, as far as they are relevant to vapour phase soldering.

The condensation process The condensate from the working vapour, which collects on the surfaces of the board assemblies on entering the working vapour, is a bad conductor of heat. Since a board is in a roughly horizontal position during soldering, the condensate forms a ‘puddle’ on its upper surface, which impedes the transfer of further heat. Using plates made from copper, it could be shown that holding the plate vertically in the working vapour, the rate of heat transfer was 1.4 times better than with the plate in a horizontal position. Reﬂowsoldering circuit boards in a vertical position is of course a practical impossibility, but the experiment does demonstrate the puddle eﬀect. Designing the holding ﬁxtures of the boards so that they tilt slightly towards one corner can help the condensate to run oﬀ.

Practical consequences Not all joints on a board will reach full soldering temperature at the same time, for reasons of their diﬀerent thermal properties and their accessibility to the working vapour. A given board must stay in the vapour until the slowest joint has been properly soldered. This dwell time must be determined experimentally in preliminary soldering runs. Naturally, it should not be longer than necessary, because prolonged ‘confrontation’ times between molten solder and substrate aﬀect joint quality (see Section 3.2). Once the slowest joint is fully soldered, the whole assembly is cooled to below the solidiﬁcation temperature of the solder (183 °C/ 419 °F) as soon and as quickly as is practicable. The peculiarities of heat transfer by condensation can cause some operational problems. The initially fast rise in temperature ( 4 °K/sec) can put some components, such as ceramic condensers, at risk from internal cracking. It may also rupture the housings of large ICs through the ‘popcorn eﬀect’ (see Section 1.4). Finally, the ‘tombstone eﬀect’, which causes chips to stand upright, has been attributed to the fast heat-up in vapourphase soldering, though solderability problems and unsuitable layout are probably the main culprits here (see Sections 3.6.3 and 9.3). Table 5.8 Heat diﬀusion in vapourphase soldering. Lapse of time before the centre of a 1.6 mm/ 63 mil thick plate, immersed in a heated medium, has approached its end temperature to within 90%, calculated in Kelvin

Substance

Lapse of time

Copper Solder AlO (ceramic) Glass FR4

0.006 seconds 0.019 seconds 0.074 seconds 1.1 seconds 5.6 seconds

job:LAY05 page:37 colour:1

black–text

Reflowsoldering 183

The puddle-eﬀect, combined with the diﬀerent temperature rise of metallic and non-metallic surfaces, is responsible for another problem met with in vapourphase soldering, the so-called ‘wicking’ of PLCC legs. In wicking, the solder climbs up the legs of PLCCs, thus starving the bottom bend of solder, with the risk of an open joint (Figure 5.8). The mechanism of wicking is brieﬂy as follows. The J-legs of a PLCC, being vertical and made of metal, warm up more quickly than the solder paste on which they sit. The paste is a bad conductor of heat, and is soon covered with condensate, much of it having run down the J-leg. This puts the footprint underneath at a disadvantage as far as heat transfer is concerned, and it heats up more slowly than the J-leg. As soon as the solder begins to melt, it is attracted by the hottest available metal surface, which is the J-leg. The strong forces of interfacial tension (see Section 3.2) cause it to climb up the leg, and starve the joint between leg and footprint suﬃciently to cause an open joint. Recently developed vapourphase soldering systems, which combine infrared preheating with a vapourphase soldering station, and which will be described presently, have helped to overcome the consequences of the initial fast rise in temperature.

Working with unsaturated vapour A volume of vapour which is not in direct contact with its working ﬂuid is termed an unsaturated vapour; it is called ‘superheated’ vapour when it is heated to a temperature above the boiling point of the ﬂuid from which it is formed. Superheated vapour behaves like any of the gaseous heating media, which are used in convection reﬂowsoldering. By working with unsaturated superheated vapour, the steep initial temperature rise which is characteristic of normal vapourphase soldering can be avoided, provided the boards are preheated to above the boiling point of the working ﬂuid in the machine. Equipment based on this concept, for which other

Figure 5.8 Wicking

job:LAY05 page:38 colour:1

black–text

184 Reflowsoldering

advantages such as reduced loss of expensive working ﬂuid are claimed, is described in a recent patent. It is expected to become commercially available before the end of 1997.

Boiling behaviour and safety aspects of working fluids The heating arrangements for keeping the working ﬂuid on the boil must be engineered with great care, because perﬂuorinated liquids must on no account be overheated lest they form the very toxic decomposition product perﬂuoroisobutylene (PFIB), a colourless, odourless gas which can form at temperatures above 300 °C/572 °F. Its occupational exposure limit is one part in 108, which is very near its limit of detectability.

During boiling, local overheating could occur if a vapour blanket is allowed to form between a heating surface and the working ﬂuid. To prevent this from happening requires correctly designed and well maintained equipment, as well as reliable safety measures, such as the monitoring of local temperatures, the replenishment, ﬁltering and monitoring of the condition of the working ﬂuid, and periodic removal of paste particles and other foreign matter which might have dropped into the boiling sump.

5.4.4 Vapourphase soldering equipment Until the end of the nineties, industrial vapourphase soldering equipment was of two diﬀerent types: the batch immersion plant and the in-line continuous soldering plant. The batch immersion machine is basically an open-top vessel, with a boiling sump of the working ﬂuid carrying either internally or externally placed heaters (Figure 5.9). Since this type of equipment is in the process of being phased out, it needs only a brief description. Its principal feature is a ‘lid’ of secondary vapour, which ﬂoats on top of the heavier working vapour (for the vapour densities, see Table 5.7), and prevents the escape and loss of the vapour of the expensive working ﬂuid. Before the environmental danger of the chloro-ﬂuoro-carbons (CFCs) had been recognized (Sections 8.3.5 and 8.3.6), CFC 113 (e.g. Freon), which boils at 47.6 °C/ 117.7 °F, was universally used for the secondary vapour blanket. Since then, a safe alternative, chlorine-free perﬂuorocarbon, is marketed by 3M under the designation of SF-2–I. It boils between 38 °C/100 °F and 40 °C/104 °F, and has a zero ozone-depletion potential, though it does possess a small global-warming potential. The levels of working and secondary vapour are controlled by cooling coils, located at the appropriate levels on the inside walls of the vapour chamber. Sensors monitor the existing vapour levels and activate pumps to replenish the working or secondary liquid when required. The boards to be soldered are placed horizontally on trays, or stacks of trays, made of stainless steel wire. It is good practice to stack the boards on their carriers in such a way that the condensate from boards higher in the stack does not drip onto the

job:LAY05 page:39 colour:1

black–text

Reflowsoldering 185

Figure 5.9 Vapourphase batchsoldering principle

soldering areas of boards below. The board trays are mostly lowered and raised mechanically. As has been said already, their dwell time in the vapour must be established experimentally for each type of board. In descending into the vapour and on emerging from it, the boards pass through the blanket of secondary vapour. To minimize drag-out of the expensive working ﬂuid, the boards may rest in the secondary vapour blanket for a short-time during emerging to allow condensate from the working vapour to drain back into the sump. Like all vapourphase soldering equipment, batch-immersion plants must be ﬁtted with all manner of monitoring and fail-safe equipment. This guards against overheating, circulates, ﬁlters and replenishes the working ﬂuid, monitors its acidity (pick-up of water might cause the formation of HF in the liquid), monitors and maintains vapour levels, and guards against failure of the cooling-water supply, to name its main tasks. Recent batch-immersion machines no longer have an open top, but are ﬁtted with a lid, with the boards to be soldered entering the machine sideways. In-line vapourphase soldering systems are larger in size, but simpler in design and they need no vapour blanket. The boards travel on an endless stainless steel belt of open wiremesh or link-belt construction, entering and leaving the vapour chamber through downwards-sloping and upwards-sloping watercooled tunnels which prevent the escape of the heavy working vapour from the machine (Figure 5.10). Given the length of the vapour chamber, the conveyor speed is governed by the dwell time which the slowest joint on the board needs to solder properly. It follows that with mixed batches of board the slowest joint governs the rate of production.

job:LAY05 page:40 colour:1

black–text

186 Reflowsoldering

Figure 5.10 In-line vapourphase soldering system

5.4.5 ‘New-generation’ vapourphase soldering systems The preheat concept During the late eighties, a fresh concept of vapourphase soldering was introduced to the market, under the general name of ‘new-generation’ vapourphase soldering. Its main feature is a preheating stage, through which the boards pass before they enter the vapour chamber. The ‘pre-heat’ raises the board temperature to between approximately 125 °C/260 °F and 150 °C/300 °F, at a heating rate of not more than about 5 °C/9 °F, per second. The boards are then held at that temperature for one and a half to two minutes, before they enter the working vapour with its temperature of 215 °C/390 °F. The resulting heating proﬁle of the boards is shown in Figure 5.11. Raising the temperature of the boards up to soldering heat in two steps brings a number of advantages: 1. The initial sharp temperature rise of straight vapourphase heating is eliminated, together with its dangers of spluttering paste, tombstoning, and damaged components. Preheating is also reported to prevent wicking of the J-legs of PLCCs. When the preheated boards enter the vapour, their initial temperature rise is about 20 °C/36 °F per second, but by that time the volatile constituents of the solder paste have disappeared and the components are much less likely to suﬀer internal cracks or to burst, having been preconditioned and dried. 2. As a board enters the vapour, the whole assembly is at a uniform temperature, only about 30–60 °C/55–100 °F away from the melting point of the solder. This means that it melts soon afterwards at more or less the same time in all the joints. In consequence, the dwelltime of a board in the vapour can be considerably shortened. Confrontation periods between the molten solder and the joint surfaces down to 15–30 seconds have been reported, with a consequent improvement of the metallurgical structure of the joints. It might be held against the preheating concept that it heats the assembled board in the presence of atmospheric oxygen. This is probably not a serious impediment to

job:LAY05 page:41 colour:1

black–text

Reflowsoldering 187

Figure 5.11 Temperature proﬁle of vapourphase soldering with preheat

the soldering process which follows, the preheating temperature being too low to seriously oxidize the metal surfaces or to degrade the solder paste. Two schemes of operation of vapourphase machines with preheat are shown in Figure 5.12. Vapourphase soldering equipment of the new generation has reached a level of sophistication well above that of the machines based on the original concept. With most of the new machines, the boards are carried on pallets, which are lowered into the vapour space in such a manner that they remain horizontal at all times. With a batch system, this makes it possible to fully close the vapour chamber, for example with hinged ﬂaps, before and after a pallet has entered it, thus reducing vapour loss and ﬂuid consumption. With in-line systems, it does away with the sloping entry and exit tunnels, and thus shortens the length of the machine. Again, the vapour chamber can be ﬁtted with vapour locks to minimize the loss of working ﬂuid. Preheating is eﬀected by infrared emitters, such as internally heated ceramic panels, which of course must be operated below the decomposition temperature of the working vapour. One manufacturer has chosen to preheat the boards indirectly with hot air to pre-empt objections on that score. Postcooling with a forced airstream, to shorten the confrontation period and to speed up the solidiﬁcation of the solder in joints, has become universal practice. One make of machine is ﬁtted with an exhaust system, which draws air inward through the entry and exit ports of the board conveyor towards the space above the vapour chamber. In this way, any backward diﬀusion of working vapour into the preheating section and with it the risk of PFIB being formed is avoided. A water scrubber retrieves solvent from the vapour which may have been carried away with the exhaust.

job:LAY05 page:42 colour:1

black–text

188 Reflowsoldering

Figure 5.12 Vapourphase soldering with preheat. (a) Batch system; (b) in-line system

Depending on the type of machine, ﬂuid losses as low as 50 g/hour are claimed to be achievable. With large in-line machines the losses can be higher, but at least one vendor oﬀers vapour-recovery units which can be retroﬁtted to keep ﬂuid loss and operating costs within the acceptable limits of the smaller batch systems.

job:LAY05 page:43 colour:1

black–text

Reflowsoldering 189

5.5 Infrared soldering 5.5.1 Working principle At ﬁrst sight, infrared (or IR) soldering appears even simpler than the vapourphase concept: passing the boards through a tunnel ﬁtted with infrared emitters seems to be all that is required, and the early IR soldering ovens did just that. However, practical experience soon showed that a thorough understanding of the physical principles which form the basis of infrared soldering, together with sound engineering, were required to make infrared soldering the reliable and largely prevailing production method it now is. A multitude of parameters enter into infrared reﬂowsoldering. The heat input into the circuit board in a pure infrared oven is governed by several basic physical laws, to be dealt with presently. The temperature of the emitters, the wavelength distribution of the infrared radiation, the reﬂectivity and the radiation absorption of the board, the components and their terminations, and also of the solder paste, all aﬀect the rate of heat input into a board exposed to infrared radiation. Unlike vapourphase soldering, infrared soldering represents a ‘non-equilibrium situation’, because the temperature of the heat source is considerably higher than the temperature which the soldered joints are intended, and can in fact be allowed, to reach. It will be useful to restate at this point that every soldering method represents either an equilibrium or a non-equilibrium heat-transfer situation (Section 2.1), and to detail the implications of the diﬀerence between them. In an equilibrium situation: 1. The temperature of the heat source is identical to the soldering temperature which the joints must reach. 2. The speed with which the joints reach that temperature depends on their thermal coupling with the heat source. Process control regulates the duration of exposure of the joints to the heat source. 3. There is no danger of overheating the joints. Faulty process control can result in two possible faults: cold joints and overcooked joints. Cold joints happen when they are not given enough time to reach their full soldering temperature. In consequence, the joint is weak or non-existent. Overcooked joints happen when they remain at the soldering temperature too long (30 secs). This results in a thickened intermetallic layer, so that the joints are brittle, with lowered life expectancy. 4. Examples are wavesoldering, vapourphase soldering, hot-air or hot-gas convection soldering, impulse or thermode soldering. Non-equilibrium situation: 1. The temperature of the heat source is higher than the soldering temperature which the joints must reach, as well as the maximum temperature which they can be allowed to reach. In most cases, the heat source is not in direct physical contact with the joints, but transmits its thermal energy by radiation. 2. The rate of temperature rise of the joints depends on the temperature diﬀer-

job:LAY05 page:44 colour:1

black–text

190 Reflowsoldering

ence between the heat source and the joints, the power of the heat source, its distance from the joints, and the heat capacity of the joints themselves. Process control regulates the temperature of the heat source and the time of exposure of the joints to it. Depending on the intensity of the heat radiation, exposure times range from milliseconds to minutes. 3. The demands on the precision and reliability of process control are in direct proportion to the speed of the temperature rise of the joints. Cold joints occur when the exposure time is too short. Overcooked joints are the result of too long exposure to the heat source. The consequences are as in the equilibrium situation. 4. Examples are infrared soldering and laser soldering. It follows from this that precise control of the operating parameters is essential with infrared soldering. Confusion often arises from the fact that the oven interior itself has no deﬁned temperature of its own. It is traversed by a ﬁeld of infrared radiation which is on its way from the emitters to the circuit boards. A considerable part of this radiation, is absorbed by the oven atmosphere before it reaches its target. This absorption factor depends not only on the distance between the emitters and the boards, but also on the rate at which the oven atmosphere is circulated in the oven interior. Thus, it makes no real sense to speak of an oven temperature as such. The temperature of the emitters is known and controllable. So is the rate of circulation of the air in the oven, and with it the eﬃciency with which it passes the heat, which it has absorbed from the radiation, by convection to the boards. This is a complex state of aﬀairs, from which it follows that the success of an infrared soldering operation depends critically on the setting, the stability and the monitoring of the operating parameters, on a meaningful and accurate monitoring of the ﬂow of heat in the oven, and on a suﬃciently quick response of the system to automatic or manual controls. This aspect will be dealt with in Section 5.5.4. Most industrial IR soldering installations are in-line tunnel ovens, with arrays of infrared emitters placed above and below a conveyor on which the circuit boards travel (Figure 5.13). More rarely, a batch process is used with one or more boards being soldered in a front-loading oven which is ﬁtted with emitters and a circulating system for the oven atmosphere. Pure infrared reﬂow ovens, which rely entirely on radiated heat for achieving the required soldering temperature, have become practically extinct since the mid-1990s with the exception of some small laboratury ovens. The reason is the diﬃculty in ensuring that all joints on a board heat up at the same rate and reach the same end temperature. This is due to diﬀerences in their mass, their shape and the reﬂectivity of their surfaces. Forced circulation of the hot oven atmosphere overcomes these problems to a large extent. Therefore forced circulation has become an essential feature of practically all infrared reﬂow ovens now on the market. Thus today’s infrared reﬂowsoldering is no longer a pure non-equilibrium process, sharing some of the advantages of an equilibrium system (Section 5.1.2).

job:LAY05 page:45 colour:1

black–text

Reflowsoldering 191

Figure 5.13 Working principle of an infrared soldering oven.

5.5.2 The physics of heat transfer by radiation The three laws of radiation In order to understand what is going on in an infrared soldering oven, and how to run it in an eﬃcient manner, three physical laws which govern the transmission of heat by radiation, and some facts about heat transfer by convection, must be discussed. This can be done in quite simple language and practically without mathematics. The temperature of a body is a measure of the thermal energy which it contains. The greater its thermal energy, or heat content, the higher is its temperature. Heat emitters are of course so designed that the surfaces which face the circuit boards are as hot as the heat source inside them, while their back surfaces reﬂect as much heat as possible back in to the emitter body. In principle, there are three ways in which a hot body can transmit its heat to its cooler surroundings: conduction, convection and radiation. In a pure infrared oven, emitters do not lose much heat by convection; virtually all the electrical energy input is given oﬀ as radiation. This radiation is the main vehicle for transferring thermal energy from the emitters to the joints on the board. In the ﬁrst edition of this book (1994), it was stated that in an infrared oven, up to 50% of the thermal output of the emitters was absorbed by the oven atmosphere, which in turn transfers it to the circuit boards. This was a misconception. The path length between the emitters and the circuit boards is far too short for any signiﬁcant heat absorption to take place. The oven atmosphere warms up simply by picking up heat from the oven interior and the emitter surfaces. The radiation given oﬀ by the emitters is still the main vehicle for transferring the required thermal energy to the boards and the joints on them. The invisible infrared heat radiation diﬀers from visible light, and in fact from any other radiation, be it cosmic, X-ray or radio, only by its wavelength, taking like all radiation the form of electromagnetic waves. (For the purpose of this discussion we shall not go into quantum physics and photons.) Electromagnetic waves, like all waves, are characterized by their wavelength and their amplitude, i.e. their energy content. In principle, infrared radiation can be

job:LAY05 page:46 colour:1

black–text

192 Reflowsoldering

emitted not only by a solid body, but also by a hot gas (e.g. from a ﬂame) or a hot liquid. In infrared soldering, we are concerned with the radiation given oﬀ by the surfaces of hot solid bodies, our emitters. The spectrum of wavelengths and the intensity of the radiation given oﬀ by any hot body follow a number of physical laws, of which the following three are important for us. The Stefan–Boltzmann law* This law states that the energy emitted by a hot body is proportional to the fourth power of the absolute temperature** of its surface. In consequence, a small increase in the temperature of the heat source, i.e. the surface of the emitter, produces a large increase in emitted thermal energy, which means in its heating power. Table 5.9 gives the numerical values of heat emission per unit of surface area, within a range of temperatures which includes those in which emitters for IR soldering normally operate. These values assume that the emitter surface converts its thermal energy into radiation with 100% eﬃciency. In practice, most industrial emitters have an eﬃciency of 95%, the other 5% being reﬂected back into the emitter body (‘grey factor’). Table 5.9 Relationship between surface temperature and emitted thermal energy. Values taken from NASA Document TT-F-783

K

Surface temperature °C °F

Emitted thermal energy (watt/cm)

373 473 573 673 773 873 973 1073 1273

100 200 300 400 500 600 700 800 1000

0.1 0.3 0.6 1.2 2.0 3.4 5.1 7.7 15.0

212 392 572 752 932 1112 1292 1472 1832

*Josef Stefan (1835–1893), German physicist; Ludwig Boltzmann (1844–1906), German physicist. **Absolute temperatures are measured on the Kelvin scale, in which a temperature of x Kelvin is the same as (x − 273) °C. (The Kelvin scale is named after Sir William Thomson (1824–1907), later Lord Kelvin of Largs, British physicist.) For example 0 K, is the absolute zero, −273 °C (it makes no sense to convert this into °F). Reckoning in absolute temperatures means, for example, that at room temperature, say 20 °C/68 °F = 293 K, solder is within 36% of its melting point of 183 °C/331 °F = 456 K. Hence the comparative ductility and low mechanical strength of solder at normal temperatures (Section 3.3). At very low sub-zero temperatures, solder becomes quite strong and brittle.

job:LAY05 page:47 colour:1

black–text

Reflowsoldering 193

Planck’s law* Planck’s Law describes how the radiation energy given oﬀ by the surface of a body is distributed over the wavelength spectrum at any given surface temperature. Figure 5.14 shows how the maxima of these energy distribution curves, which are quite sharp at high temperatures, move towards longer wavelengths and get ﬂatter as emitter temperatures get lower. On the scale of wavelengths, the visible radiation, which could of course also be called thermal radiation, lies between 0.38 m (violet) and 0.76 m (red).

Figure 5.14 Distribution of emitted energy over the wavelength spectrum for different emitter temperatures *Max Planck (1858–1947), German physicist.

job:LAY05 page:48 colour:1

black–text

194 Reflowsoldering

Ultraviolet begins below 0.38 m, while above 0.76 lies the range of infrared (the preﬁx ‘infra-’, meaning ‘below’, refers to the wave frequency of the radiation, not its wavelength). (The surface temperature of the sun is approximately 5500 °C/9900 °F, at which temperature the Planck curve has its maximum at 0.52 m. The wavelengths of the visible range of thermal radiation, i.e. of the light which our eyes can see, is spread neatly on either side of that maximum. This is as it ought to be, since our retina which perceives this radiation had millions of years to evolve under the light of our sun. One might add that many animals, whose requirements for survival diﬀer from ours, can perceive radiation with rather diﬀerent ranges of wavelengths.) For practical convenience, infrared radiation has been subdivided into three wavebands: 0.76–1.5 m 1.5–5.5 m 5.5 m

Near infrared Middle infrared Far infrared

Wien’s law* Wien’s law gives a formula for the location of the maximum of the energy distribution curves as they shift towards longer wavelengths with lower emitter temperatures: the wavelength of the maximum is inversely proportional to the temperature of the emitting surface. As has been said already, these maxima get progressively ﬂatter with lower emitter temperatures. Below 500 °C/930 °F, the precise location of the energy maximum has no longer any practical signiﬁcance. Table 5.10 illustrates these relationships.

The significance of the temperature difference between emitter and board The emitters used in reﬂowsoldering ovens generally fall into two categories: 1. Low-temperature and medium-temperature emitters usually take the form of internally heated metal panels or ceramic bodies. Their operating temperatures range from 250 °C/480 °F to 400 °C/750 °F for the metal panels and 300 °C/ 570 °F to 500 °C/950 °F for the ceramic ones. Their operating characteristics can be compared to those of an electric hotplate: slow to get hot, and slow to respond to changes in the heating current. 2. High-temperature emitters are as a rule quartz tubes with a tungsten or tungsten alloy heating coil running down the middle. Quartz (SiO ) is chosen for this purpose because it is transparent to infrared. The back half of the tube may carry an external ﬁlm of gold to act as a reﬂector. High-temperature emitters operate at temperatures between 700 °C/1290 °F and 850 °C/ 1560 °F. Their operating characteristics are similar to those of an electric light bulb in their fast response to being switched on or oﬀ, or dimmed. *Wilhelm Wien (1864–1928), German physicist.

job:LAY05 page:49 colour:1

black–text

Reflowsoldering 195

Table 5.10 Emitter temperatures and wavelength pattern of the emitted radiation Temperature °C °F Emitted energy: watt/cm watt/in kw/m Wavelength of the energy maximum: max

250 452

300 572

350 662

500 932

700 1292

0.43 2.58 4.3 5.5 m

0.60 3.60 6.0 5.0 m

0.89 5.34 8.9 4.6 m

2.0 12.0 20 3.7 m

5.1 30.6 51 2.4 m

1.0

1.5

Emitted energy 0.6 at max/ in relation to energy at max300 °C

4.4

13.9

As would be expected, the temperature diﬀerence between an emitter, the heat source, and a circuit board, the heat sink, governs the rate at which thermal energy ﬂows from the one to the other. In fact, because Planck’s law is involved, the fourth power of the absolute temperatures of both source (T ) and sink (T ) enter into the heat-ﬂow formula: Q = C ¸[(T /100) \ (T /100)] in which C represents the emission and absorption characteristics of the surfaces radiating eﬃciency of most practical emitters is about 95% (see involved. The above). The heat absorption of the surfaces involved in reﬂowsoldering will be discussed later. Table 5.11 gives numerical values, computed from the formula, for the relative rates of heat ﬂow between a low-temperature and a medium-temperature emitter and a circuit board at diﬀerent points of its travel through an IR oven. Many emitters, for example gold-backed quartz tubes, are designed so that their back reﬂects the heat from the emitter interior back into it, in order to direct as much as possible of its thermal output towards the circuit boards and not the casing of the oven. Failing that, heat reﬂectors must be mounted between the emitters and the oven wall. Several important practical conclusions can be drawn from the ﬁgures computed in Table 5.11: 1. With a low-temperature emitter of 300 °C/572 °F, a temperature variation of ±50 °C/120 °F drastically aﬀects the rate of heat transfer from the emitter to the board, by up to ±40%. This demonstrates the importance of accurately controlling and monitoring the temperature of that type of emitter. 2. As the board gets warmer during its travel past an array of low-temperature emitters, the eﬃciency of heat transfer from emitter to board drops drastically:

job:LAY05 page:50 colour:1

black–text

196 Reflowsoldering

Table 5.11 Comparison between heat transfer eﬃciencies between low-temperature and hightemperature emitters and a circuit board at various stages of heating. T , Temperature of the emitter; T , Temperature of the circuit board and the solder joints Comparative heat-transfer eﬃciencies Q with a low-temperature or medium-temperature emitter T T 20 °C/68 °F 100 °C/212 °F 150 °C/302 °F 183 °C/361 °F

250 °C/482 °F

300 °C/572 °F

350 °C/662 °F

Q 0.64 0.49 0.31 0.21

Q 1.00 0.84 0.75 0.65

Q 1.47 1.27 1.14 1.08

Comparative heat-transfer eﬃciencies Q with a high-temperature emitter T T 20 °C/68 °F 100 °C/212 °F 150 °C/302 °F 183 °C/361 °F

750 °C/1382 °F

800 °C/1472 °F

850 °C/1562 °F

Q 0.82 0.81 0.80 0.80

Q 1.00 0.99 0.98 0.98

Q 1.21 1.20 1.19 1.18

by the time the board has reached soldering temperature (183 °C/361 °F), the rate of heat transfer has dropped by 35%. This factor obviously lengthens the time which a board must spend in the ﬁnal heating stage, where the solder melts. This in turn lengthens the confrontation interval during which the solder remains molten in the joint, with its consequent undesirable eﬀects on its metallurgical quality. 3. With a high-temperature emitter (800 °C/1472 °F), a variation of emitter temperature has less drastic consequences on the amount of heat emitted than with a low-temperature emitter. More importantly, the rate of heat transfer to the board is hardly aﬀected while the board warms up and approaches its soldering temperature. It follows that while there may be a case for low-temperature emitters in the preheating stage of an infrared oven, where the heating rate of the board should not exceed about 5 °C/10 °F per second, high-temperature emitters are certainly more suitable for the last stage of the soldering cycle, where a ﬁnal burst of thermal energy has to raise the board temperature from about 100 °C/210 °F–150 °C/300 °F quickly and brieﬂy beyond the melting point of the solder to between 220 °C/ 430 °F and 250 °C/480 °F. This time-span should be short and the maximum temperature be readily controllable for metallurgical and operational reasons which have been discussed already. By reason of their construction, the surface temperature of low-temperature emitters takes several minutes to respond to changes in the heating current and even longer for the emitters to reach their operating temperature when switched on from

job:LAY05 page:51 colour:1

black–text

Reflowsoldering 197

cold. By contrast, high-temperature emitters reach their full operating temperature and respond to heating-current changes in well under one second.

Directionality of the emitted radiation A hot body emits heat radiation in all directions, with a falling oﬀ at angles close to the tangent to the surface. This means that in the interior of an oven heated by low-temperature and medium-temperature emitter panels, the pattern of infrared radiation is diﬀuse so that there is no danger of sharp shadows. Nevertheless, any joint which is totally out of sight of any emitter surface can only rely on such heat as convection from the hot oven atmosphere can bring to it. This applies for example to badly placed PLCC J-legs. On smooth, heat-reﬂecting surfaces with gold-backed quartz tubes, IR radiation follows the laws of optics. The IR output is directional and this must be taken into account when designing the spatial disposition of quartz emitters.

Reflection and absorption of incoming heat by the board and the joints When thermal (or any other) radiation encounters the surface of a solid (or a liquid) body, three diﬀerent eﬀects occur: 1. Some radiation is reﬂected by the surface. 2. The rest passes into the body where some of it is absorbed as it passes through it. Depending on the transparency of the body towards the radiation, and if it is thin enough, part of the radiation will reach the other side. 3. At the exit surface, some of the radiation is reﬂected back into the body. The rest emerges and travels on. Since circuit boards, together with their components and metallic laminates, are too massive for any thermal radiation to pass through, only reﬂected and absorbed heat need to be considered, both of them adding up to 100% of the incoming radiation. Figure 5.15 shows the reﬂection/absorption behaviour of solder and FR4 polyester/glassﬁbre laminate in the infrared range. With solder, as with all metals, such absorption as does take place occur in a few top atomic layers. FR4, like all organic substances (including the human body, as users of infrared lamps know), is to some extent transparent to infrared radiation, and thus allows a part of it to penetrate to the inner layers. Generally, this is beneﬁcial, as it reduces warping of the boards from one-sided heating, though the virtue of heating the boards equally from above and below remains. The ﬂux portion of solder paste, being an organic substance, is also somewhat transparent to infrared radiation, and allows it to enter the paste deposit, where it bounces around between the solder grains and quickly gives up its thermal energy to them.

job:LAY05 page:52 colour:1

black–text

198 Reflowsoldering

Figure 5.15 Reﬂection and absorption behaviour of solder and FR4 in the IR range. * After Lusk, E. F. (1984) Electronic Packaging Prod., 24, 3, pp. 98–104. **After Dow, S. J. (1985) Brazing and Soldering, No. 8, pp. 16–19

Solder reﬂects visible light, but it is an eﬃcient absorber of heat radiation in the very near infrared. This is useful when soldering with a Nd: YAG laser which emits at a wavelength of 1.06 m (Section 5.7). Absorption drops to 50% and below within the range of wavelengths of high-temperature and low-temperature emitters, which is good enough for all practical purposes and a help with solder paste, as mentioned above. The steep drop in absorption beyond 8 m makes CO lasers (emitted wavelength 10 m) uninteresting for laser soldering.

Effect of the nature of the components on their heat absorption Ceramics are good conductors of heat and absorb infrared radiation near their surface. This means that there is no danger of thermal stresses and cracking with melfs and chips on that score. However, that does not diminish the risk of internal cracks in ceramic condensers when heating them too quickly from room temperature. On the other hand, the plastic housings of ICs, like FR4, are somewhat

job:LAY05 page:53 colour:1

black–text

Reflowsoldering 199

transparent to IR radiation. This warms their interior, not suﬃciently to put the embedded chips at risk but enough to turn any internally trapped moisture into steam, and thus to trigger the popcorn eﬀect, especially with large ICs. The colour of an IC housing is quite irrelevant as far as reﬂection or absorption of heat in an infrared oven, and getting hot or staying cool, are concerned, as has been proved experimentally. What the human eye can see is irrelevant to what happens to infrared radiation on a given surface, as has been explained earlier on. If overheating of an individual large IC should be a worry because of the popcorn eﬀect, a piece of self-adhesive aluminium foil applied to its surface will keep its temperature down. What does count is the mass of an irradiated component. As Figure 5.16 shows, there is a direct relationship between the mass of a component and its temperature at the end of its passage past the IR emitters: a component weighing 0.1 g may get 60 °C/108 °F hotter than one weighing 4.5 g. The temperature of a component aﬀects the temperature of the component leads and the joints themselves: by the time a board leaves the oven, every joint on every component, including the one with the slowest temperature rise, must have become hot enough for the solder to melt. That means that the board must get hot enough for the solder on the largest components to melt, which may make matters uncomfortable for the small ones.

Effect of the shape of a component Because of the low heat conductivity of non-metallic bodies, such as IC housings and also circuit boards themselves, their edges and especially their corners get hotter

Figure 5.16 Component peak temperature versus mass during IR soldering

job:LAY05 page:54 colour:1

black–text

200 Reflowsoldering

than their ﬂat surfaces. The reason for this is that in a diﬀuse, multidirectional heatﬂow, a given volume of material receives twice as much heat along an edge and three times as much in a corner than in the middle of a ﬂat surface (Figure 5.17).

5.5.3 The physics of heat transfer by convection Today’s industrial IR soldering ovens provide for the forced and eﬃcient circulation of the air in the oven in order to smooth out the previously mentioned local temperature diﬀerences between SMDs of diﬀering mass, and excess heat on edges and corners. Also, air circulation improves the heat supply to solder joints located in partial shade, like the J-legs of badly designed or very closely spaced PLCCs. The physics of convection heating, which governs transfer of heat from the oven atmosphere to the boards with their population of components, is complex. Two factors matter in the present context. The rate of heat transfer from a hot gas to a solid body is directly proportional to the temperature diﬀerence between that gas and the surface to be heated, and proportional to the square of the relative speed at which the gas ﬂows over the surface. Also, turbulent ﬂow improves the rate of heat transfer. For that reason, a growing number of atmosphere circulation systems in IR soldering ovens are designed for moving smaller volumes of air at higher speeds, without of course dislodging components from their footprints. Normal, sometimes termed ‘standard’, atmospheric air is a mixture of a number of gases, the principal ones being: Nitrogen Oxygen CO Hydrogen

78 % vol. 21 % vol 0.03% vol 0.01% vol

75.5 % weight 23.2 % weight 0.05 % weight 0.001% weight

Some relevant physical properties of these gases, such as their density, their speciﬁc heat content per unit volume and their heat conductivity, are given in Table 5.12.

Figure 5.17 Energy ﬂow into a solid body

job:LAY05 page:55 colour:1

black–text

Reflowsoldering 201

Table 5.12 Physical properties of atmospheric gases

Density (g/litre) Speciﬁc heat (cal/g K) Speciﬁc heat (cal/litre K) Heat conductivity (cal/g cm sec 10\)

Standard air

N

O

CO

1.3 0.24 0.31 5.8

1.25 0.25 0.38 5.8

1.43 0.22 0.31 5.9

1.98 0.20 0.40 3.4

As the table shows, nitrogen is a more attractive heat transfer medium than air since, at a given temperature, a litre of it carries 1.2 times as much heat as a litre of air. Carbon dioxide looks even more attractive, and some nuclear reactor designs make use of its good heat transfer properties. Unfortunately, its usefulness for soldering is marred by its tendency to decompose to some degree at elevated temperatures, which leads to the presence of some free oxygen, which ruins its properties as a protective atmosphere, and of some carbon monoxide, which is dangerous.

5.5.4 Operation of infrared ovens Temperature profile Deﬁnition The term ‘temperature proﬁle’ here describes the thermal experience of the solder joints themselves, as the board to which they belong travels through an IR oven. It has become a convention to plot temperature proﬁles along a time axis, as shown in Figure 5.18. The deﬁnition of a temperature proﬁle, as normally encountered in technical and vendors’ literature, varies. Often the temperature values represent the temperature of the various groups of emitters which are disposed along the oven, with the horizontal time scale derived from a given conveyor speed. However, the relationship between the temperature of an array of emitters and of the solder joints which travel past it is neither a direct or simple one. Achieving a given temperature proﬁle Therefore, with a growing amount of high quality reﬂow ovens, the temperature values fed to the oven controls and displayed on the control panel of an oven are measured values, determined by temperature sensors disposed along the conveyor track of the oven. Provided the receptor surfaces of the sensors approximate the reﬂectivity of solder joints, i.e. the soldering terminals of the components, their readings provide a suﬃciently realistic measure of the real temperature proﬁle as it has been deﬁned above, and a better basis for temperature control. When the only available data are the temperatures of the emitters, the true temperature proﬁle for a given setting of the emitter temperatures can only be

job:LAY05 page:56 colour:1

black–text

202 Reflowsoldering

Figure 5.18 Idealized temperature proﬁle of an infrared reﬂowsoldering operation

established experimentally. A trial board, preferably an assembled board of the type for which the temperature proﬁle has to be set, is sent through the oven, with thermo-elements attached to some typical or critical joints. Often, some sensors are also attached to the housings of some ICs, which may be temperature sensitive. Thermally conductive adhesives for the purpose are obtainable through the trade, if not from the vendors of solder paste. Various makes of temperature recorders suitable for travelling through an IR oven alongside the trial board are commercially available (see Section 4.3.3 under temperature control of wavesoldering machines). A recorder can usually accommodate up to six temperature/timetracks, which it can play back to a PC or a visual display after it has emerged from the oven. Others can transmit the temperature data in real time to an outside receiver as they travel through the oven. Such a measured temperature proﬁle, together with the set of emitter temperatures which produced it, forms a reliable basis for setting, controlling and, if necessary, adjusting the real temperature proﬁle not only of boards represented by the trial board, but also of others of a similar type. Once the relationship between a given setting of the emitter temperatures and the actually realized temperature proﬁle of the joints on a board has been established, it should of course be entered and stored in a databank. The shape of the temperature proﬁle By a tradition which has only recently been challenged, temperature proﬁles are subdivided into several separate temperature regions, each corresponding to a

job:LAY05 page:57 colour:1

black–text

Reflowsoldering 203

separately controlled group or array of emitters disposed along the oven. The number of emitter groups varies from vendor to vendor, but as a rule there are never less than three or more than ﬁve. Until the mid-1990s, it had been held that the ideal temperature proﬁle started with a preheating period of about one minute, during which the board temperature rises to a plateau of between 90 °C/195 °F and 110 °C/230 °F. This is intended to precondition the paste in the joints so that it does not spit or misbehave in other ways. A second preheating stage, lasting another minute, followed, raising the temperature to about 150 °C/300 °F. The heating rate leading to either plateau was aimed to stay below 4 °C/8 °F per second. At the end of the second plateau, a rather faster, ﬁnal spurt of heating, which might be as steep as 6–8 °C/11–14 °F per second, was to take the temperature beyond 183 °C/361 °F, the melting point of the solder. The ﬁnal temperature peak must be high enough to ensure that the solder has melted and wetted the joint surfaces in every joint. Recommended peak temperatures vary from 215 °C/ 390 °F–280 °C/540 °F and 230 °C/420 °F–260 °C/470 °F.

The time spent by the joints above the melting point of the solder should be as short as is compatible with assuring that every single joint has reached it, but preferably not longer than 30 seconds. As has been said before, this important parameter on any temperature proﬁle is the ‘confrontation period’ during which the molten solder in the joint is in contact with the metallic joint members. The shorter this confrontation time, the thinner will be the brittle intermetallic layer between solder and joint members and the better will be the joint (see Section 3.2). To keep it below 15 sec is practically impossible in IR reﬂowsoldering, but it should be the aim of good soldering practice to keep it within 30 sec or at most 45 sec. Hardly less important is the speed at which the joint cools from the peak temperature down to about 170 °C/340 °F. Cooling rates between 20 °C/35 °F and 30 °C/55 °F per second should be the aim, to give the joints the desirable closegrained structure. This can be readily achieved by an eﬃcient and correctly placed aircooling unit at the exit end of the reﬂow oven. Figure 5.18 shows an idealized version of such a temperature regime. Recent work has shown that, with today’s solderpastes, a simpliﬁed temperature proﬁle for the approach to the ﬁnal peak gives as good results as the stepped heating mode: this temperature proﬁle has now only one temperature plateau, sometimes called the ‘soaking’ stage. The recommended duration of the soak varies between 1 minute and 2 minutes, with a soaking temperature of about 150 °C/ 300 °F. The rates of temperature rise between the various heating stages are still within the limits as before (Figure 5.19).

5.5.5 Oven design Size of oven and position of emitters Once the physical principles of reﬂowsoldering by infrared radiation are established and understood, designing a suitable oven becomes a straightforward problem of production engineering.

job:LAY05 page:58 colour:1

black–text

204 Reflowsoldering

Figure 5.19 Realistic temperature proﬁle of an infrared reﬂowsoldering operation. *After Reithinger, M. (1991) Reﬂow Soldering Technology for Surface Mount Assembly, Electr. Productn., March 1991, pp. 27–37

The starting parameters of any oven design are the maximum dimensions of the boards to be soldered and the maximum demanded output. The former governs the width of the oven; the latter, together with the maximum achievable speed of the conveyor, its length. With industrial high-capacity ovens the conveyor speed may reach 0.7–1.0 mm/min (28–40 in/min). Such conveyor speeds demand soldering chambers ranging between 1.5 m/50 in to 2 m/80 inch in length, to which the charging platform at the entry end and the cooling zone and the discharging platform at the exit end must be added. At the time of writing (1993), a high-speed oven, operating with a nitrogen atmosphere, and operating in an integrated production line for domestic video equipment, has been reported as the longest unit to date with an overall length of 16 m/48 ft. Several vendors are oﬀering ovens which are constructed on a modular basis with each module representing one of the heating zones on the temperature proﬁle. This gives users more ﬂexibility in adjusting their soldering line to the needs of changing circumstances. Bench-type ovens for small-scale production and laboratory use are often quite short, from 50 cm/20 in to 75 cm/30 in length of chamber. Whether such short ovens are in fact able to put a circuit board through a deﬁnable temperature proﬁle is open to doubt, especially as far as the short ﬁnal melting peak is concerned. With the low conveyor speeds which are a necessary feature of such small ovens, the temperature proﬁle is likely to become blurred unless the boards are very short. It has become standard practice to place emitters both above and below the board

job:LAY05 page:59 colour:1

black–text

Reflowsoldering 205

conveyor, mostly with the same type and rating of emitter at both top and bottom. The emitters are controlled in separate groups, normally not less than three and often ﬁve or more. Within each group, the top and bottom emitters must be separately controlled, to enable the reﬂowsoldering of boards with SMDs on both sides (Section 5.1.1). With most makes of oven, emitter settings, once they have been established for a given type of board, can be stored and called up on demand.

Emitters There are three types of emitters: 1. Internally heated metal panels, mostly with an integral or externally ﬁtted thermocouple, for thermostatic control. They operate within a temperature range between 250 °C/480 °F and 350 °C/750 °F. Their temperature takes well over a minute to respond to a change in heating current. 2. Internally heated ceramic panels, equally ﬁtted with a thermocouple. Their operating temperature extends up to 550–600 °C/1020–1100 °F and their response to a change in heating current is somewhat faster, but still in the minute range. 3. Quartz tubes with an internal tungsten coil extending down their centre. They can be ﬁtted with an integral thermocouple, but seldom are. Tubular heaters are mostly installed at right angles to the direction of the boards. With some high-performance ovens, a number of quartz tubes are also arranged lengthwise along the sidewalls of the oven, to ﬂatten the transverse temperature proﬁle which tends to drop towards the sidewalls due to heat loss. The operating temperature of quartz tube heaters ranges from 700 °C/1300 °F upwards, and their response to a change in the heating current is fast, within less than one second.

Disposition of emitters With most types of oven, the ﬁrst two or three groups of emitters are of the metal-panel or preferably the ceramic type. Irrespective of the type and heat absorption characteristics of the boards which travel through the oven, the heatﬂow needs no ﬁne tuning during the run-up to the soaking plateau on the temperature proﬁle. What matters, though, is that the temperature of the emitters should be well above that of the boards which travel between them. As has been explained in Section 5.5.2, the eﬃciency of the transfer of heat from a hot to a cooler body is related to the fourth power of the temperature diﬀerence between them. With most industrial infrared ovens, the emitters in the narrow melting zone at the end of the oven are a closely spaced group of quartz tubes, because only this type of heater can provide the short zone of intense, but accurately controllable heat irradiation which is essential to keep the confrontation interval between molten solder and joint surfaces brief, and to avoid overheating.

job:LAY05 page:60 colour:1

black–text

206 Reflowsoldering

With some makes of high-performance oven, all emitters are high-temperature quartz tubes. There, the tubes are more widely spaced for the run-up to the soaking plateau, but closely set together in the zone of the melting peak.

Controlling the temperature profile The control panel of almost every make of reﬂow oven displays a temperature reading for every group of heaters. As long as this readout is taken for what it is, namely the temperature of the emitters and not of the boards themselves as they travel through the oven, then all is well. This is worth pointing out, because not all makes of oven make this clear. With almost all ovens, the displayed emitter temperature can be set, thermostatically controlled, and often called up from a stored program which has been established as suitable for a given type of board. With some ovens, a temperature sensor for each group of emitters is located at conveyor level, with a surface which matches the thermal absorption/reﬂection characteristics of a typical solder joint. The readout from these sensors gives a more realistic picture of the heat to which the boards are exposed as they travel through the oven, though it is not necessarily equal to their actual temperature. Nevertheless, it forms a good basis for a thermostatically maintained temperature proﬁle. Finally, with some high-performance ovens, an infrared-responsive remote temperature sensor is focused on the surface of the travelling boards themselves. This does indeed give a direct reading of the actual board temperature. This expensive method is normally used only for the ﬁnal melting zone, where its feedback controls the fast-response quartz emitters, allowing them to be run at high temperatures and consequently high eﬃciency. With most other types of oven, the optimum setting of the emitter groups must be established experimentally, preferably with the travelling temperature recorder which has been described already, and then related to the readout on the control panel, and recorded. It may be worth pointing out again that the ﬁne tuning of the temperature proﬁle of the run-up to the soaking plateau does not matter very much with modern solder pastes, as long as the melting zone is kept short and sharp, with its peak temperature between 200 °C/390 °F and 300 °C/570 °F. It has in fact been reported that a single temperature proﬁle is suitable for most types of board.

Cooling after soldering As soon as all the joints have been soldered, they ought to solidify as quickly as possible, with their temperature dropping from the peak to below 183 °C/361 °F, this being the melting point of the solder, within a few seconds, certainly not more than about ﬁve. This will ensure a ﬁne-grain structure and good mechanical strength. A stream of air of room temperature, produced by a blower and directed at the boards both from above and below, is enough to achieve this. Obviously, the air velocity should not be such as to cause the components to shift on their footprints

job:LAY05 page:61 colour:1

black–text

Reflowsoldering 207

before the solder has set. Cooling the emerging boards from both above and below is not always practised, but it does repay the extra eﬀort and cost by improved joint quality. This cooling section should be located as close to the exit from the melting zone as possible. Suitable baﬄes must prevent the cooling air from blowing back into the oven.

Circulating the oven atmosphere Recognizing that much of the heat produced by the emitters is picked up by the oven atmosphere, designers are giving much attention to eﬃcient systems of air re-circulation in their ovens to ensure that this heat is not lost, but transferred to the boards by convection. (The physical laws which govern the transfer of heat from a stream of hot air to the surface of a solid body such as a circuit board are dealt with in Section 5.5.3.) A small and controllable bleed-oﬀ must be provided to prevent a build-up of the volatile constituents given oﬀ by the solder paste, and the possible formation of an explosive solvent concentration in the oven. In order to ensure that the air circulating in the oven does not blur the contours of the temperature proﬁle, most ovens have separate circulation systems for the warm-up, the soaking and the soldering zone. In some designs, the diﬀerent zones are separated from one another by bulkheads with horizontal slots just high enough to accommodate the conveyor and the boards riding on it. On the other hand, doubts are beginning to appear in some quarters about whether it is essential to strictly separate the ﬁrst two zones. It is agreed, though, that the ﬁnal soldering zone, which may be relatively short, must have its separate, accurately controlled temperature regime. An eﬃcient air circulation system, together with a correct layout of the emitters, will ensure that the temperature proﬁle within an oven is level to within 5 °C/10 °F across the width of the oven. Some makes of oven subdivide the emitters into several separately controllable groups across the width of the oven. This is intended to ensure an even heat supply if the thermal requirements of a given type of board vary substantially from side to side.

Overhead soldering Many ovens provide for separately controlled heating and circulation systems for the underside of the boards. This is useful when reﬂowsoldering boards with SMDs on both sides. After placing and soldering the components ﬁrst on one side, the second side is populated with SMDs and passed through the oven again, with the SMDs soldered in the ﬁrst pass hanging on to the underside. In vapourphase soldering it cannot be helped that the solder holding them to the board melts again but, as has been pointed out in Section 5.3, the surface tension of the molten solder will not let them drop oﬀ unless they are too heavy. Infrared reﬂowsoldering avoids this risk, because the underside of the board can be kept below the melting point of the solder. Speciﬁcally cooling the underside would be counterproductive, because it would reduce the eﬃciency of the soldering process on the top surface. Keeping the

job:LAY05 page:62 colour:1

black–text

208 Reflowsoldering

temperature of the underside of the board at between 100 °C/210 °F and 120 °C250 °F does no harm to the joints on it and assists the soldering process on the top side. The importance of placing the cooling zone as closely as possible to the exit from the soldering zone has been pointed out already.

Conveyor systems Boards travel through the oven on a continuous conveyor, which can be either an endless, ﬂexible open-mesh stainless steel belt, or consist of two endless link-chains which support the two sides of each board. The distance between the chains must be adjustable, either manually or through a programmed servosystem, to suit the width of boards; a stainless steel wire may run between these side supports to prevent wide boards with heavy components from sagging. A side-chain conveyor is of course obligatory for soldering double-sided boards: the side which was soldered ﬁrst and carries components cannot be placed face down on a grid conveyor; with a chain conveyor, the central supporting wire must be lowered to clear the highest component. This too can be done either manually or through a programmed servo system. One vendor equips his ovens with two conveyors running at diﬀerent speeds. The boards ﬁrst travel on a relatively slow conveyor through a combined heatingup and soaking zone, where the boards are heated principally by convection. They are then picked up by a faster conveyor, which carries them quickly through the IR-heated soldering zone, keeping the high-temperature peak as short as possible.

5.5.6 Infrared soldering in a controlled atmosphere The merits of soldering in the absence of atmospheric oxygen have been pointed out already, for both wavesoldering and vapourphase soldering. It has been found that IR reﬂowsoldering too beneﬁts in several respects from a controlled atmos-

Figure 5.20 Principal features of an IR reﬂowsoldering oven

job:LAY05 page:63 colour:1

black–text

Reflowsoldering 209

phere, provided the oxygen level can be kept below 10 ppm. Soldering in an oxygen-free environment allows the use of no-clean solder pastes which contain less aggressive ﬂuxes. Their residues can be left on many types of board which would require cleaning when soldered with a paste based on a conventional ﬂux. Because metallic surfaces do not oxidize in an oxygen-free atmosphere, the metallized ends of melfs and chips are more readily wetted by the solder in the paste, the joints present a more attractive contour, and all solder surfaces have a clear and sparkling appearance. Some striking reductions in the fault rate have been reported following a change from IR reﬂowsoldering in air to soldering in nitrogen, especially as far as solderbridges, non-wetting and incompletely ﬁlled joints are concerned. As with vapourphase soldering, boards which have been IR-reﬂowsoldered in nitrogen are free from discolouration. Nitrogen protects the ﬂux portion of the paste from oxidizing and carbonizing, thus making its removal easier when cleaning is required. It also seems to have the eﬀect of promoting the wetting of FR4 epoxy-laminate or other organic surfaces by the ﬂux, especially if it contains rosin. This can mean that ﬂux residue may be found in places where normally it would not have ﬂowed. It has been reported that the addition of 5% H to the nitrogen prevents this from happening.

A ‘no-residue’ solder paste is commercially available which, when used for IR reﬂowsoldering in a reactive, nitrogen-based atmosphere (of unstated composition), is claimed to leave almost no ﬂux residue, the ﬂux portion having been volatilized in the process. This can thus be classed as a genuine ‘no-clean’ soldering method (Section 5.2.4). Ovens for IR reﬂowsoldering in an oxygen-free atmosphere must be designed in such a way as to minimize the loss of the costly atmosphere. A certain amount of ‘bleeding’ will always be needed to prevent the buildup of the volatile constituents of the solder paste, such as solvents and carrier substances. Once all the joints have been soldered, they can be allowed to solidify in ordinary air, since at that stage the presence of oxygen cannot do any harm. Therefore, on emerging from the oven, the boards are cooled by a stream of ordinary air. Equipment which incorporates all these features is commercially available.

5.6 Reflowsoldering with hot air or gas 5.6.1 Convection versus radiation With infrared heating, there is no simple answer to the plain question of every cook (or soldering engineer) ‘How hot is my oven?’ It all depends on such factors as emitter temperatures, the absorption properties and shape of the soldering goods and their travelling speeds. Reﬂowsoldering by infrared radiation is a non-equilibrium process, where the emitters are much hotter, often very much so, than the joints can be allowed to get. This demands precise and reproducible control of the length of their exposure to the heat ﬂow from the emitters. The higher the temperature of the emitters, the more

job:LAY05 page:64 colour:1

black–text

210 Reflowsoldering

sophisticated and ﬂexible must be the control system of the oven, with emitter parameters having to be adjusted for diﬀerent types of board to suit their speciﬁc heating requirements. Even so, smaller components get hotter than large ones, and in consequence, temperature diﬀerences of up to 30 °C/55 °F can occur between their respective joints, which results in widely diﬀering microstructures. A further cause of uneven heating under infrared radiation is the eﬀect of the geometry of a solid body on its heat take-up, through which edges and corners get hotter than ﬂat surfaces (see Figure 5.17, Section 5.5.2). This is a further reason why most of today’s reﬂow ovens operate with hot-air or hot-gas convection.

5.6.2 The physics of convection reflowsoldering Convection heating in a moving stream of hot air or gas is an equilibrium situation. The oven temperature is precisely deﬁned and measurable, being that of the circulating atmosphere. Whether the soldered goods fully attain the temperature of that heat transfer medium depends only on whether they remain in it for long enough. In practice, all the joints on a board reach the same end temperature to within ±5 °C/10 °F. The rate of heat transfer between a ﬂowing gas and a solid surface is mainly proportional to: E the temperature diﬀerence between the gas and the surface E the square of the speed at which the gas ﬂows across that surface. Other factors enter into it as well, such as the mode of ﬂow at the interface: the more turbulent it is, the higher is the eﬃciency of heat transfer. Thus, a densely populated board with a highly complex topography, which produces local turbulence in the hot air ﬂow over it, picks up the heat better than a plain one (the design of every heat exchanger is based on this principle). Thermal conductivity of the oven atmosphere, and its speciﬁc heat per volume, also matter (see Table 5.13), with nitrogen having a 20% edge over air as regards heat content per volume. Flame soldering is a particular embodiment of hot-gas convection heating, and at the same time an extreme example of a non-equilibrium system (Section 3.5.2). Sophisticated microﬂame soldering equipment is commercially available, with robot-mounted ﬂame heads and a controlled feed of ﬂuxed solderwire on to the solder spot.

5.6.3 Convection reflow ovens Design considerations Convection reﬂow ovens have many operational advantages over plain infrared ovens, such as the possibility of separate temperature management for the upper and the lower surfaces of the boards which pass through an oven. This is essential when soldering boards with components on both sides. However, in recent years doublesided boards are being used less frequently. In recognition of the rules of convective heat transfer, most oven designs prefer to

job:LAY05 page:65 colour:1

black–text

Reflowsoldering 211

circulate the oven atmosphere at higher speeds and in lower volumes rather than the other way round. The speed must of course not be so high as to dislodge any component from its footprint before the solder melts. With most oven designs, the hot atmosphere is directed at a right angle towards the board surface, but by the mid-1990s a ﬂow tangential to the board has become popular. The general aim is to produce maximum turbulence and an even temperature proﬁle across the width of the board. With most convection ovens, the heating arrangement underneath the board conveyor is symmetrical to that above, so that the boards can travel nose-totail, forming a horizontal dividing baﬄe along the oven without aﬀecting its eﬃciency. With second-pass soldering of double-sided boards (Section 5.1.1), this way of working makes it easy to keep the temperature of the underside of the boards below the melting point of the solder. When soldering boards carrying BGAs, it is essential that the temperature of the circuit board is high enough to ensure the full reﬂow of all solder bumps underneath the component. With double-sided boards, care must of course be taken to ensure that the joints on the underside of the board do not melt again. The oven atmosphere is heated by passing it through a system of heat exchangers, which follow the pattern of a well established technology. Because convectionoven soldering represents an equilibrium system, the temperature of the heating air or gas in a given zone is held not much above that which the boards are intended to reach as they pass through it. Most convection ovens are subdivided into zones, numbering from four up to ten, depending on the intended throughput of the oven. The ﬁnal soldering stage is, or ought to be, designed so as to generate a steep temperature rise, leading to a narrow peak of 250 °C/450 °F–300 °C/540 °F, followed by a quick temperature drop. Ideally, joints should spend no more than about thirty seconds above the melting point of the solder (183 °C/361 °F), for reasons which have been explained before (Figure 5.19, Section 5.5.4). As has been explained, separate temperature management for the top surface and the underside of a circuit board is essential with a number of soldering strategies. When both sides of the board require the same temperature and the same heat input, the oven design must provide the appropriate ﬂow pattern of the heating atmosphere on both sides of the board conveyor. When the underside of the boards must stay cooler than their top surface, the two air streams must be prevented from mixing. This may require that the boards travel on the conveyor ‘bumper-tobumper’ to separate the two temperature regimes from one another.

Controlled-atmosphere working Except for a controlled bleed-oﬀ to remove the volatile constituents given oﬀ by the solder paste, the oven atmosphere is recirculated to conserve heat. For the same reason, the entry and exit ports for the board conveyor are kept narrow. These features make it relatively easy to design convection-soldering equipment for ready convertibility between air and nitrogen operation. Several ingredients of the ﬂux portion of a solder paste are volatile and evaporate during soldering. A build-up of these substances in the oven atmosphere must be

job:LAY05 page:66 colour:1

black–text

212 Reflowsoldering

avoided, to prevent them from accumulation on the oven interior, the heaters and the conveyor. Therefore the atmosphere circulation system must include ﬁlters, which are readily accessible, cleanable and replaceable. Some vendors of solder paste make a feature of oﬀering pastes which give oﬀ less of the volatile substances which are apt to form deposits on ﬁlters and in the oven interior. The length of a convection oven must take the relatively low rate of heat transfer between atmosphere and boards into consideration. Overall lengths of between 3.5 m/10.5 ft and 4.5 m/13.5 ft are common. The conveyor systems of convection ovens are basically the same as with IR soldering ovens (Figure 5.21).

Operating features The temperature–time proﬁle of convection soldering operations is less sharply deﬁned and divided into zones than is the case with infrared soldering. In fact, it has been found possible to solder all but a few boards with unusual temperature requirements with the same temperature proﬁle, which begins with a steady slope of 2–4 °C/4–7 °F per second from room temperature to about 140 °C/280 °F– 160 °C/370 °F, followed by a sharp rise to the above-mentioned soldering peak. This obviates the need for creating and storing a large number of board-speciﬁc oven programmes.

5.6.4 Development potential of convection reflowsoldering

Adding an infrared melting stage The single unattractive feature of convection ovens is the ﬁnal melting stage, which must produce a steep and narrow temperature peak, rising from about 150 °C/300 °F up to or above 250 °C/480 °F and then quickly dropping below 183 °C/360 °F. To achieve this with hot air demands a narrowly conﬁned stream of

Figure 5.21 Working scheme of a convection soldering oven

job:LAY05 page:67 colour:1

black–text

Reflowsoldering 213

high-temperature air or gas, operating separately from the preceding gradual and more gentle heating regime of the preheating stages. It would be simpler, and perhaps cheaper, to replace this necessarily somewhat blurred high-temperature blast by a readily focused beam of heat radiation produced by one or two closelyspaced quartz emitters. Their ready response to current changes would make them well suited to automatic control by suitably placed sensors.

Oven atmospheres Compared with infrared reﬂowsoldering, the pure convection reﬂow oven seems attractive on several counts: 1. The infrared oven is by necessity a mixed system, using both radiation and convection for heating the boards, because of the unavoidable heat absorption in the oven atmosphere. The convection oven turns the non-equilibrium infrared system, with the subsidiary role of the hot oven atmosphere, into a controllable heating regime by means of a volume of air or gas raised to a deﬁned temperature by an array of purpose-designed heat exchangers. 2. Convection heating makes it tempting to consider a wider choice of oven atmospheres. What matters in an oven atmosphere for convection heating is its speciﬁc heat, i.e. the heat content of a given volume of hot gas, its heat conductivity, which determines how eﬃciently this heat can be transferred to a circuit board, and above all its chemical interaction with the surfaces of the joints and the molten solder. In normal air with 21% vol of oxygen, any soldering operation needs a soldering ﬂux. From a chemical point of view, soldering in the chemically inert nitrogen needs no ﬂux, though for physical reasons ﬂuxless soldering under nitrogen has its problems, as has been shown. Hydrogen starts to become able to reduce tin oxide and other metallic oxides above 350 °C/630 °F, an uncomfortably high temperature for electronic soldering. However, at lower temperatures it already actively assists the wetting of copper and other solderable surfaces by molten solder, but the extreme ﬂammability of pure hydrogen rules it out as an acceptable soldering atmosphere. ‘Forming gases’ on the other hand, which are mixtures of hydrogen and nitrogen, do not suﬀer from this disability. A forming gas consisting of 25% vol hydrogen and 75% vol nitrogen has been found to actively encourage wetting of copper and some of its alloys by molten solder.

Table 5.13 compares some relevant physical properties of normal air, nitrogen, hydrogen and 75 N /25 H forming gas. As has been said already, nitrogen carries board per volume than ordinary air, and protects it and the more heat to a circuit solder from oxidation. Forming gas carries somewhat less heat per volume, but gives up its heat to the board more readily. Above all, it has been shown to positively promote soldering. Thus, forming gas could be worth considering.

job:LAY05 page:68 colour:1

black–text

214 Reflowsoldering

Table 5.13 Physical properties of some convection-oven atmospheres

Air N H Forming gas 75 N /25 H

Density g/litre

Speciﬁc heat cal/(litre K)

Heat conductivity cal/(g cm sec)

1.3 1.25 0.09 0.96

0.31 0.38 0.31 0.36

5.8 5.8 41 6.27

Alternative oven designs Some vendors oﬀer reﬂow ovens based on a modular design, which allows the addition of further heating stages to cope with growing production needs, or to allow adding an infrared end-stage as an option. Accommodating a temperature proﬁle, which requires the boards to spend between 2[12–3 minutes in the oven, may lead to very long ovens, when in-line production and large throughputs demand high conveyor speeds. To save expensive ﬂoor area, a vendor has developed a vertical convection oven, based on the ‘tower’ concept: the boards, held on horizontal supports, travel in a ‘paternoster’ manner upwards through a preheating section, then horizontally through a shorter melting stage, and downwards again through a cooling section. The entry and exit ports of the oven are located at conveyor level (Figure 5.22). The same vendor has announced work on a concept to exclude atmospheric oxygen from the interior of the ‘tower’, which forms an inverted closed container, by ﬁlling it with the inert, lighter-than-air vapour of a working ﬂuid, which has a boiling point below the melting temperature of the solder. The marketing of this oven is scheduled for 1998.

5.6.5 Convection soldering of single components The process Hand-held and bench-mounted hot air/gas reﬂowsoldering tools also represent a form of convection soldering. A gas which could be used instead of air is mainly nitrogen. Whether the expense of nitrogen is justiﬁed must be decided in the context of the possibility of using a no-clean ﬂux, and thus avoiding or simplifying any subsequent cleaning, should that be called for. Hot air/gas soldering is used mainly for attaching individual components, such as large multilead ICs, to circuit boards which already carry the bulk of their SMDs, having been soldered by an in-line method, either by wave or reﬂow. Another major use of hot air/gas soldering is the de-soldering and re-soldering of SMDs in repair work (see Chapter 10). If solder paste is used as the solder/ﬂux depot, it is mostly applied with a hand-held dispenser gun, which may be manually or pneumatically operated (Section 5.3.1) Alternatively, if the footprints are already covered with a suﬃcient layer of solder from a preceding hot-air-levelling (HAL) operation or from having

job:LAY05 page:69 colour:1

black–text

Reflowsoldering 215 2

1

3

2 3

Figure 5.22 Vertical tower oven (SMT, Germany): 1, pre-heating section; 2, melting section; 3, cooling section

passed through a solderwave, a low-solids ﬂux, is suitable. Its choice will be governed by any postsoldering treatment which may be necessary or called for. Soldering individual components to three-dimensional substrates (MDs, see Section 6.2, item 4) is a recent newcomer to the technology of localized reﬂowsoldering. Soldering with these tools does not represent an equilibrium situation: the temperature of the hot air or gas is between 350 °C/650 °F and 450 °C/850 °F, and thus well above the ﬁnal joint temperature of about 250 °C/480 °F. These high gas temperatures are chosen because in this work speed is of the essence. The aim is to keep the confrontation period during which the solder in the joint is molten to within a few seconds, and not more than ﬁve if possible. Once the target temperature has been reached, heating is discontinued. Control is either visual, by programmed timing or with a temperature sensor. With both types of equipment, a coherent stream or jet of hot air or gas of moderate velocity is directed more or less vertically against an array of joints, with the solder paste deposit or the ﬂux in place. On impact, the stream becomes turbulent, which, as with convection-soldering ovens, is the basis of eﬀective heat transfer to the joints.

Hand-held tools These are normally in the form of hot-air guns, either ﬁtted with an integral air blower and heater or fed via a ﬂexible hose from a stationary small compressor and heat exchanger. The latter arrangement is preferable for close work, because the

job:LAY05 page:70 colour:1

black–text

216 Reflowsoldering

unencumbered airnozzle is more manouvrable. The controllable air temperature is normally set between 350 °C/650 °F and 450 °C/850 °F. This is well above the joint temperature aimed at: as has been said already, heating is discontinued as soon as the solder in the joints is seen to have melted and ﬁlled them. The jet is conveniently controlled with a footpedal, so as to keep the operator’s hand free. The component is placed on the prepared footprints, normally with a vacuum pipette, and held down while the joints are heated with the jet of hot air. It may be best to pin down larger components by ﬁrst soldering two diagonally opposed corners, and then work along the edges, moving the jet on as soon as a joint can be seen to have ﬁlled with molten solder.

Bench-mounted equipment A variety of bench hot-air or hot-gas soldering equipment of varying degrees of sophistication, automation and complexity is on the market. These machines are used for the soldering of single multilead components such as PLCCs, SOICs, QFPs, BGAs and ﬂip-chips to boards already populated with the bulk of their components. The stream of hot air or gas is guided to the array of joints through an interchangeable nozzle, shaped to ﬁt the footprint pattern. It is important that the nozzle should have a low heat capacity so as to heat up quickly and not chill the airblast unduly as soldering begins (Figure 5.23).

Figure 5.23 Hot-air nozzle for soldering a multilead component

job:LAY05 page:71 colour:1

black–text

Reflowsoldering 217

During soldering, and until the solder has solidiﬁed afterwards, the component must be held down against the board under gentle pressure. This ensures that all component legs sit ﬁrmly on their respective pads, even if their coplanarity is not ideal (see Section 7.1), and that the component does not move during soldering. It is advisable to plan the soldering strategy so as to create the solder depots for this operation during the preceding soldering stage, where the bulk of the components are soldered. Hot-air levelling or wavesoldering will leave enough solder on the pads for subsequent hot-air or hot-gas soldering. The same applies to the solder paste deposit on unoccupied footprints; the solder paste will have melted during a preceding normal reﬂow operation. In most cases the pretinned pads will have to be ﬂuxed again before the component is placed in position. This consideration applies generally to the area of ultraﬁne-pitch technology (pitch 0.3 mm/12 mil), where solder paste reaches the limits of its printability and its freedom from bridging. Hot-nitrogen reﬂow techniques for the soldering of the outer leads of TABs to their pretinned footprints (outer-lead bonding – OLB), which use a so-called hot-air thermode (HAT), have been developed by several companies ( e.g. IBM, Fuji and SRT).

With many bench-mounted hot-air soldering machines, visual or video aids are provided to assist with the precise placement of ﬁne-pitch multilead components. For quantity production, machines are on the market where a placement head and the hot-air nozzle operate sequentially, with the board remaining stationary during the operation, its correct position assured by ﬁduciary holes or markings. With this type of equipment, the temperature, timing and duration of the hot airblast and the hold-down of the component during and after soldering are all programmed.

Preheating In order to keep the duration of the molten-solder confrontation as short as possible, especially with heavy multilayer boards, many bench-mounted machines provide for locally preheating the circuit board from below, with a gentle ﬂow of hot air or a low-temperature infrared emitter. Preheating the board to 60 °C/140 °F–80 °C/ 180 °F should suﬃce. Large boards may warp if the local preheat is too sharp. With manual hot-air soldering, placing the board on a warm hotplate is helpful.

5.7 Laser soldering Laser soldering presents the ultimate non-equilibrium situation: the wavelengths emitted by the lasers used for soldering lie in the infrared region, but because of the mechanics of laser emission, it makes no sense to talk about the temperature of the radiation source, as will be explained in Section 5.7.1. However, controlling the laser dosage with great precision is essential if the joint is not to be vapourized. In contrast to IR oven-soldering, where the total surface of a board is ﬂooded with infrared radiation, its wavelengths spread over a wide spectrum, laser soldering

job:LAY05 page:72 colour:1

black–text

218 Reflowsoldering

targets each individual solder joint with a measured pulse of infrared energy, of a single wavelength, and gathered in an extremely narrow beam. The word ‘laser’ is formed from the initial letters of the term Light Ampliﬁcation by Stimulated Emission of Radiation. In 1957, the laser phenomenon as such was recognized as a possible practical application of quantum physics. Th. Maiman (USA) translated it into a practical piece of equipment in 1960. Several features make reﬂowsoldering with laser beams appear attractive. A beam of heat radiation can be targeted very accurately onto a joint. The high energy density at its point of impact allows for very short soldering times and quick solidiﬁcation, while the duration of a laser light pulse can be controlled to well within a millisecond. Finally, heating is strictly localized and both the components and the board remain cool.

5.7.1 How a laser works The working of a laser is based on the fact that certain so-called laser-active substances may, when exposed to a strong source of light (termed ‘pumping’), emit quite a special type of light themselves. The eﬀect is caused by the pumping light raising the atoms or molecules of the laser-active substance to a higher quantum level of energy, from which they return instantly to their original state. Matters can be so arranged that this secondary energy emerges from the laseractive substance in the form of laser light, which has some very special properties. Instead of being spread over a spectrum of wavelengths, it has one single wavelength only, which is speciﬁc for the ‘lasing’ substance. Also, it is composed of long ‘coherent’ trains of lightwaves, not of the very large number of separate brief energy pulses which make up the light emitted by a hot body or gas, or a gas discharge. A laser usually takes the form of an elongated cylindrical rod or, if the lasing substance is a gas, a transparent tube. To make it ‘lase’, its sides must be irradiated by the pumping light, an intense pulse usually produced from a powerful ﬂashlight or gas-discharge lamp with ratings in the kilowatt range. Both ends of a laser rod or cylinder are mirrored, the long wavetrains of laser light bouncing back and forth between them, while being constantly reinforced by the pumping light. Eventually they escape through small apertures in one or both of the end-mirrors in the form of monochromatic, coherent and almost perfectly parallel light beams. Lasing starts as soon as the primary light starts pumping, and stops as soon as pumping stops. This makes it possible to pulse laser light very accurately. The eﬃciency with which the pumping light is converted into laser light ranges from a few per cent up to 30%, depending on the type of laser. The diﬀerence between pumping energy and emitted laser energy takes the form of heat, which must be disposed of by eﬃcient cooling, otherwise the laser can destroy itself in a few seconds (Figure 5.24).

5.7.2 Nd: YAG and CO2 lasers Two types of lasers can be used for soldering purposes: the Nd: YAG laser and the CO laser.

job:LAY05 page:73 colour:1

black–text

Reflowsoldering 219

Figure 5.24 Working principle of a laser with emission at both ends

The Nd: YAG laser This is a solid laser. It uses a synthetic semiprecious stone, yttrium aluminium garnet, which is dosed with neodymium (a rare earth element) as a lasing substance. Its emitted light has a wavelength of 1.06 m, which is located in the near infrared range. It lases with an eﬃciency of a few per cent, which means it has to be pumped with light of near 1 kw energy to emit a laser beam of 10 watt. The rest of the energy must be removed by an eﬃcient and reliable cooling system. The light beam from a Nd: YAG laser can be gathered into a bundle of 10–20 m/0.4–0.8 mil diameter. For soldering, beam energies of 10–20 watt are normally used. Solder absorbs thermal radiation of a wavelength of 1 m well (see Figure 5.15), which means that the light from a Nd: YAG laser has a high heating eﬃciency. Though according to Wien’s law the energy maximum of light emitted by a body with a surface temperature of 2600 °C/4700 °F is located at the 1 m wavelength, it would be misleading to ascribe that temperature to the lasing substance. As has been said already, lasing is not a matter of heat and the chaotic oscillations of atoms and molecules associated with it, but of quantum jumps; that is why it is monochromatic. Therefore, the intense local heat created at the point where a laser beam meets a surface is due not to a high temperature of the lasing substance but to the high energy density at the point of impact: a laser beam of 20 watt, with a diameter of 50 m, produces an energy density of 10 kw/mm in the spot where it impinges on, for instance, a footprint. It will burn a hole through it in milliseconds, an extreme case of a non-equilibrium situation, which calls for high-precision timing and targeting. The Nd: YAG beam passes through glass and polymers, including the ﬂux portion of solder pastes, with little absorption. The transparency of glass towards the beam means that it can be manipulated and transmitted by normal optical means,

job:LAY05 page:74 colour:1

black–text

220 Reflowsoldering

such as ordinary glass lenses, mirrors and glass ﬁbres. It also means that safety goggles do not protect the human eye against it. In turn, this makes it mandatory to place all Nd: YAG laser soldering equipment in completely lightproof enclosures, so that no stray, direct or reﬂected, laser beam can escape. The beams, being coherent and parallel to a high degree, can traverse great distances without loss of intensity. The Nd: YAG laser beam passes through the cornea, lens and eyeﬂuid of the human eye with little attenuation, and will destroy the retina in milliseconds at the point of impact. Therefore, this type of laser soldering can only be monitored through an indirect video display.

The CO2 laser The CO gas laser is another type of laser used for soldering. Its laser-active substanceis CO gas, which lases at a wavelength of 10.6 m, i.e. in the far infrared. CO lasers havean eﬃciency of about 30%, and they are cooled by pumping the gas a heat exchanger. The beam from a CO laser can be bundled to a diameter through of 50–100 m2–4 mil. It is strongly absorbed in polymers, and especially normal glass. On the other hand, solder absorbs only about 20% of its energy (see Figure 5.16). If the beam has to be manipulated, the optics must be made from expensive special glasses. For these reasons, the development potential of the CO laser for soldering applications is limited.

5.7.3 Laser soldering in practice Points in favour Laser soldering oﬀers a number of tempting features. The confrontation period is measured in milliseconds instead of seconds or half-minutes, and solidiﬁcation after soldering is equally rapid. Therefore, the intermetallic layer in a laser-soldered joint is hardly visible under the microscope, and the microstructure of the solder is extremely ﬁne. In consequence, the mechanical properties and the life expectancy of laser-soldered joints are optimal. Also, the heat input during soldering is so short and so strictly localized that both the board and the components stay at room temperature. This avoid the stresses locked in the joints arising from the diﬀerent contraction behaviour of substrate and components, as the soldered assembly cools down from the soldering temperature. In fairness, it must be said that laser soldering shares this feature with impulse soldering (Section 5.8). The narrowly localized soldering spot invites the attempt to direct a ﬁne jet of nitrogen on it and to solder in a controlled atmosphere. The possibility of using this method for ﬂuxless soldering, and thus to avoid cleaning, has been mentioned in some of the literature on the subject.

Points against Several aspects take some of the shine oﬀ laser soldering. One is the one-by-one nature of soldering with a single beam, though double-beam laser machines (see

job:LAY05 page:75 colour:1

black–text

Reflowsoldering 221

below) reduce this handicap by half. Another problem arises from the extreme non-equilibrium nature of laser soldering. For a given laser-soldering task, every joint with its individual thermal mass and reﬂectivity demands a precisely deﬁned laser impulse. A slight deviation, such as a bent lead, or a slight change in the amount of solder paste, may mean a joint left open, or destroyed. To cope with this problem, the temperature of the joint can and should be monitored during soldering. A PbSe(Te) pyrometer focused on the joint is claimed to be able to control the irradiation time to within 0.001 sec. This is the basis of the so-called ‘smart lasers’.

5.7.4 Laser-soldering equipment A double-beam Nd: YAG laser-soldering machine has been commercially available for several years (Baasel Lasertechnik, Germany) (Figure 5.25). This machine operates with two jointly controlled 20 watt beams of 50 m diameter emitted by a double-ended Nd: YAG laser, which provides an energy density of about 10 kwmm in each soldering spot. The laser beams are manipulated by electromagnetically actuated galvanometer mirrors in such a manner that, with

Figure 5.25 A twin-beam Nd: YAG lasersoldering machine (Baasel, Germany)

job:LAY05 page:76 colour:1

black–text

222 Reflowsoldering

every SMD, two symmetrically opposed joints are irradiated. This symmetry prevents the tombstoning of chips. The duration of a given soldering impulse depends on the mass of the joint members, amounting for example to 0.02 sec for an SOIC gullwing leg. Soldering an SOIC with 28 joints takes approximately one second, half of which is needed to move the beams from joint to joint. During the soldering pulse, the beams oscillate across the joint area in circular or elliptical patterns in order to distribute the heat and prevent local overheating (Figure 5.26). Most good-quality solder pastes have been found to give good, sputter-free lasersoldered joints without the need for predrying. The movement of the laser spots from joint to joint on a given SMD, and their oscillation during soldering, is taken care of by the galvanometer mirrors. Individual SMDs are brought into soldering position by a servo-operated xy table, on which the board is mounted. The coordinates of the individual soldering points can be derived from the software which creates the solder paste printing stencil. The optimum exposure times for the individual joints must be established by a teach-in procedure. Laser soldering is an ideal heating system for soldering individual ICs or TABs with their small footprints, with ultraﬁne-pitch spacing. The introduction of the twin-beam concept for the soldering of a complete population of ordinary joints with standard pitch spacing was probably premature. It has to use expensive and time-wasting expedients, which may be one of the reasons for its lack of market penetration. With the spread of ﬁne-pitch and ultraﬁne-pitch technology, the niche which soldering with smart lasers has found in electronic assembly technology has begun to grow. Four makers of commercial OLB laser bonding equipment have recently been identiﬁed in the US and Japan (PanasonicMatsushita, Hughes Aircraft, Mitsubishi and Sony). Some problems still remain, however. While the ND: YAG laser provides accurately localized heating for densely spaced leads, uniform lead hold-down remains one of the challenges for this particular technique. In conclusion, it would be fair to say that at the time of writing (1997), lasersoldering still generates interest rather than enthusiasm amongst the assemblers of electronic products.

Figure 5.26 Oscillating laser spot

job:LAY05 page:77 colour:1

black–text

Reflowsoldering 223

5.8 Impulse soldering 5.8.1 Operating principle The concept of impulse soldering, also known as thermode or hot-bar soldering, derives from the ordinary soldering iron. This time-honoured tool brings a hot, suitably shaped piece of copper into close contact with one or both members of the intended joint, to which ﬂux and solder are either supplied at the same time, unless one or both have been pre-deposited in the joint (‘sweatsoldering’). Thermode soldering is a sophisticated derivative of sweatsoldering with a soldering iron. Prior to soldering, the pretinned footprints are ﬂuxed, the component is placed in position and the heated soldering tool (thermode) is brought down on all the joints simultaneously. It is held down under a slight, controllable pressure until the solder has melted and ﬁlled the joints. Heating is then discontinued, and aircooling is sometimes applied to speed up the solidiﬁcation of the solder. Once it is solid, the thermode is lifted clear of the assembly. The rate of heat-transfer between the thermode and the joint against which it is pressed is the arithmetical product of the following factors: E E E E

the area of contact between thermode and joint the thermal conductivity of the thermode material and the joint the time of contact the time-integral (the sum total) of the temperature diﬀerence between thermode and joint during the soldering process.

Impulse soldering is basically an equilibrium process, because the temperature of the joint equals that of the thermode at the end of the heating-up period, which usually lasts less than one second. Impulse soldering is used more and more frequently for attaching individual multilead, ﬁne-pitch components like SOICs, QFPs, ﬂatpacks, PLCCs and, particularly, the outer leads of TABs to boards which have already been populated with the bulk of their components. The fact that the thermode holds down all the legs of these components – and their lead-count may rise up to a hundred or more – against their respective footprints with a controllable pressure before, during and after soldering is the principal virtue of impulse soldering. Because of this, coplanarity of these legs (Section 1.4) is no longer the problem it is with other soldering methods. For obvious reasons, impulse soldering is equally useful for desoldering multilead components, should their removal become necessary for repair or corrective work, and of course equally for soldering the replacement component into place (Sections 10.2 and 10.3). There may be various reasons for choosing impulse soldering: the components concerned may not be suitable for overall heating because of their construction; equipment for their automatic placement may not be available or may be uneconomic to procure; or the component may be tailor-made for impulse soldering and unsuitable for any other reﬂowsoldering method, for example TABs. Most frequently its pitch may be too ﬁne to permit wavesoldering or a reliable printdown of solder paste; heat sensitivity of the component may be an added factor (see the popcorn eﬀect: Section 2.5, Figure 2.5).

job:LAY05 page:78 colour:1

black–text

224 Reflowsoldering

5.8.2 The solder depot Impulse soldering being a reﬂow method, a solder depot must be provided on one set of the joint members, usually the footprints. On ultraﬁne-pitch components the tin or solder coating on the component legs may be thick enough to provide enough solder to make the joints.

Principally, a solder-depot thickness of 10–30 m (0.5–1.5 mil) is suﬃcient to give well ﬁlled joints. The closer the pitch of the footprints, the thinner should be the depot: solder squeezed out from closely spaced footprints can cause bridging. The impulse soldering of a multilead IC is normally preceded by the wavesoldering or reﬂowsoldering of all the other SMDs to the board. Wavesoldering will have left a domed solder depot of up to 100 m/4 mil thickness on the empty pads, as will have hot-air levelling. Reﬂowing a printdown of solder paste leaves less solder on the unoccupied pads; with ﬁne-pitch layouts, the thickness of the melted down solder will be around 50 m/2 mil (Section 5.3.2), when doming is less pronounced. If a still thinner solder depot is called for, a galvanic solder depot can be used. Unless the preceding reﬂowsoldering of the other components on the board has fused this electrodeposited solder depot, it ought to be fused in a separate operation (most conveniently in a vapourphase soldering operation). This is advisable because an electrodeposited solder layer is not a coherent alloy coating, but a porous agglomeration of discrete tin and lead particles. After a certain time, oxygen and possibly water vapour penetrate down to the copper substrate and aﬀect its solderability, while the tin and lead particles themselves also oxidize, and are thus less likely to fuse together (Section 3.6.6). If a printdown of solder paste is used prior to impulse soldering, it must not be placed on that part of the footprints where the thermode will come down on them, even if the pitch would allow it, because the non-metallic portion of the paste (the previously mentioned mixture of ﬂux, thickeners and thixotropic additives (Section 5.2.4)) would carbonize and adhere to the hot surface of the soldering tool. This impairs its eﬃciency, and means frequent cleaning, which is costly and can damage the tool. Instead, the paste is printed near the ends of the footprints, away from the component legs. The heat from the thermode will ﬂow along the component legs and the footprints, melt the solder and draw it into the joints (Figure 5.27). The domed proﬁle of a thick solder depot may cause a thin lead to slip sideways under the pressure of the thermode. Such depots can be ﬂattened by bringing the thermode, whose temperature must be below the melting point of the solder, say 120 °C/250 °F to 150 °C/300 °F, down on the footprints with suﬃcient pressure (‘coining’ the footprints). Various options for creating ﬂat solder depots are described in Section 6.4.4. Before a component is placed, the pads are ﬂuxed with an electronic grade of ﬂux (Section 3.4.3), preferably with a low solids content. Its choice will depend on whatever circumstances govern the choice of ﬂux for the whole board. The ﬂux is normally applied as a narrow jet of ﬁne spray, either manually or with automated equipment, in a pattern which matches that of the footprints. It is good practice to put down the component while the ﬂux is still somewhat moist, so that the legs of the component receive some of it.

job:LAY05 page:79 colour:1

black–text

Reflowsoldering 225

Figure 5.27 Paste printdown for thermode soldering

The ﬂux itself is of course of a type suitable for use on electronic assemblies (see Section 3.4.3). The exact choice, e.g. whether low-solids or no-clean, will depend on any postsoldering treatment which the ﬁnished assembly will have to receive. Impulse-soldering under nitrogen considerably widens the choice of ﬂux, while improving soldering quality and reducing reject rates (see Sections 4.5.2 and 5.6.4).

5.8.3 The thermode and its heating cycle Thermodes are made from a strong, non-tinnable, heat resistant metal, such as titanium or, less frequently, molybdenum, or one of their alloys. A thermode is normally heated by passing a controlled pulse of current through it – hence the term ‘impulse soldering’ – less frequently by attached resistance heating elements. A thermocouple embedded in the thermode controls its time–temperature proﬁle. In order to keep the heat pulse short – within the range of a few seconds – the heat capacity of the thermode is kept low by slimming its cross section as far as the mechanical demands on it will allow. Its outline and dimensions must ﬁt the conﬁguration of the component leads, which implies that every type of component demands its speciﬁc thermode (Figure 5.28). PLCCs pose a special problem, because their solder joints are not directly accessible to the thermode: the soldering heat is transmitted to the vertical shanks of the J-leads, while the thermode tip heats the solderpads next to the joints (‘collet soldering’, Figure 5.29). During the heating cycle and until the solder has solidiﬁed, a pin holds the PLCC against the circuit board under slight pressure. With many thermode soldering machines, a hold-down pin is used with all types of component during soldering and postcooling. The heating current ﬂowing through the thermode necessarily creates a gradient of electric potential along its horizontal bars. Where the ICs to be soldered are of a type likely to suﬀer damage by such a potential diﬀerence between its leads, the underside of the thermode can be given a thin, electrically insulating but thermally conductive coating, e.g. a vitreous enamel or PTFE. Thermode soldering makes some speciﬁc demands on the board layout. Since each solderpad receives the same amount of heat, it is important that all pads have the same heat capacity, which means the same geometry. Potential heat sinks must

job:LAY05 page:80 colour:1

black–text

226 Reflowsoldering

Figure 5.28 Thermode for ICs with ﬂat leads

Figure 5.29 Thermode for PLCCs

not be integral with the pad areas, but should be separated from them by narrow bridges, which minimize parasitic heat ﬂow away from a pad (Figure 5.30). The time/temperature proﬁle of an impulse soldering operation must meet some speciﬁc demands: 1. The heat pulse must be kept short for several reasons. The joint gap between a footprint and a component leg is only 0.01 mm/0.4 mil to 0.1 mm/4 mil across, but the joint area may be as much as 1 mm/1600 mil. With such a joint

job:LAY05 page:81 colour:1

black–text

Reflowsoldering 227

Figure 5.30 Footprint layout for impulse soldering. After Soldering in SMD Technology, Siemens, Munich, Germany

geometry, there is real danger of ﬁlling much of the joint gap with brittle intermetallic compounds if the temperature is too high or heating unduly prolonged.

2. Another reason for a short heating pulse is the need to avoid weakening the bond between the footprints and the board laminate. In order to keep the heating pulse short, heavy multilayer boards may need local preheating of the board from underneath, in order to relieve the thermode of the task of heating a heavy substrate with massive internal copper conductors which form eﬀective heatsinks. This presupposes of course that the underside of the board does not carry its own population of SMDs. 3. The temperature gradients at the beginning and end of the heating cycle can be quite steep, up to 500 °C/900 °F per second, because the component itself stays cool during soldering and is not in danger from a sudden heat shock.

5.8.4 Impulse-soldering equipment With most of the commercially available equipment, the thermodes follow a similar design (Figure 5.31). Four horizontal bars, each with separate leads, follow the pattern of the footprints. The pulse of heating current is supplied from a common transformer. The temperature rise at the beginning of the pulse is steep, at 400 °C/ 700 °F to 500 °C/900 °F per second, and so is the temperature descent at the end of the 3–5 sec heating period. Fast cooling is normally assisted by a blast of cold air. The design of commercially available impulse-soldering equipment spans a wide range of sophistication. At one end of the scale, single components are placed by

job:LAY05 page:82 colour:1

black–text

228 Reflowsoldering

Figure 5.31 Four-bar thermode

hand, their manual alignment being assisted by a simple magniﬁer. This can be very eﬀective, and a reasonably skilled operator can manoeuvre an IC to within 0.1 mm/4 mil lateral accuracy with a vacuum pipette. Position having been eﬀected, the heating pulse of pre-set intensity and duration is triggered by pedal pressure. At the other end of the scale, automated production equipment may employ opto-electronic sighting on ﬁduciary markings or footprint patterns to position the component. Often the soldering equipment is integrated with a pick-and-place facility. If a variety of components is to be handled, thermode heads can be automatically changed. Heating periods, peak-temperature values and dwell periods are numerically controlled. If a number of components are soldered to one board, the board position is normally ﬁxed, with the thermode head mounted on a numerically controlled xy gantry. Before a component is placed, the correct pattern of ﬂux can be sprayed automatically on to its footprints. Most impulse-soldering equipment on the market is designed to allow soldering under nitrogen. Alternatively, the nitrogen option can be retroﬁtted (see Section 5.8.2).

5.9 SMD soldering methods – A survey See Figure 5.32 for temperature proﬁles of the diﬀerent soldering methods.

job:LAY05 page:83 colour:1

black–text

Reflowsoldering 229

Wavesoldering (Double waves, Combination waves, Jetwaves) Characteristics: A thermal equilibrium situation – all joints attain the same temperature as the heat source. Flux, preheat and hot solder supplied to all joints sequentially in an in-line process. Capable of being carried out in an oxygen-free atmosphere. Soldering temperature: As a rule 250 °C/450 °F. Rate of production: Medium to high. Duration of confrontation between molten solder and substrate: 2–5 seconds. Solidiﬁcation speed of joints: High. Field of application: Mandatory for boards with a mixed population of components, where SMDs share a board surface with wired-through joints, unless the ‘throughhole reﬂow’ technique is used with the latter (see Section 4.1.2). The SMDs must be glued to that board surface before wavesoldering. Limits of applicability in normal atmosphere: Suitable for passive components, SOTs, SOs, and all multilead components with a pitch down to 1.27 mm/50 mil. Possible, but more diﬃcult and requiring special layout provisions, at ﬁner pitches, down to 0.75 mm/30 mil, and PLCCs. Unsuitable for ultraﬁne-pitch components and closely spaced SMDs. Limits of applicability under nitrogen: Suitable for components down to 0.5 mm/20 mil pitch.

Reflowsoldering in general Characteristics: Creation of depot of solder paste [ = solder + ﬂux], or of solid solder, followed by ﬂuxing and placement of the SMDs, and subsequently the application of heat. The lapsed time between creating the depots, placing the components and applying the heat may be hours or days. Creation of depots footprint-by-footprint or simultaneously on all of them. Subsequent application of heat either joint-byjoint, component-by-component, or simultaneously to the whole board. Field of application: Suitable for all types of SMD, and for soldering wired components by ‘through-hole reﬂow’. Reﬂow methods diﬀer in the way the joints are heated. The diﬀerent methods of creating the solder/ﬂux depots are applicable to all of them, except to thermode soldering where the use of solder paste is not always advisable.

Vapourphase soldering Characteristics: A thermal equilibrium situation: all joints reach the temperature of the heat source, i.e. the working vapour, which is as a rule 215 °C/419 °F. All joints are heated simultaneously. Soldering takes place in an oxygen-free atmosphere. Soldering is carried out on a batch or an in-line basis. Rate of production: Low to medium. Duration of molten soldersubstrate confrontation: 20–40 sec.

job:LAY05 page:84 colour:1

black–text

230 Reflowsoldering

Solidiﬁcation speed of joints: Medium.

Infrared soldering Characteristics: A thermal non-equilibrium situation: the temperature of the heat source is higher than the soldering temperature reached by the joints, sometimes by 400 °C/750 °F. Soldering is carried out mostly on an in-line, more rarely on a batch, basis. Capable of being carried out in an oxygen-free atmosphere. Rate of production: Medium to high. Usual maximum soldering temperature: 250 °C/480 °F to 300 °C/540 °F. Duration of molten solder and substrate confrontation: 15–30 sec. Solidiﬁcation speed of joints: Medium.

Laser soldering Characteristics: A non-equilibrium situation: the high energy-density of the laser beam can destroy the joint unless precisely timed. Soldering on a joint-by-joint basis. Capable of being carried out in an oxygen-free atmosphere. Rate of production: Slow. Soldering temperature: 300 °C/540 °F–400 °C/750 °F. Duration of molten solder and substrate confrontation: 0.02–0.04 sec. Solidiﬁcation speed of joints: Very high.

Convection-oven soldering Characteristics: A thermal equilibrium situation: in the ﬁnal stage, all joints attain the same temperature as the heatsource. An in-line process. Capable of being carried out in an oxygen-free atmosphere. Rate of production: medium to high. Maximum soldering temperature: 250 °C/480 °F–350 °C/660 °F. Duration of molten solder and substrate confrontation: 20–40 sec. Solidiﬁcation speed of joints: Medium.

Convection soldering of single components Characteristics: thermal equilibrium or near-equilibrium situation. Capable of being carried out in an oxygen-free atmosphere. Rate of production: slow. Soldering temperature: 250 °C/480 °F–350 °C/660 °F. Duration of molten solder and substrate confrontation: 10–20 sec. Solidiﬁcation speed of joints: Medium.

job:LAY05 page:85 colour:1

black–text

Reflowsoldering 231

Impulse soldering of single components Characteristics: A thermal equilibrium situation. Oxygen-free option possible. Rate of production: Slow to medium. Soldering temperature: 250 °C/480 °F–300 °C/570 °F. Duration of molten solder and substrate confrontation: 0.5–3 sec. Solidiﬁcation speed: High.

Figure 5.32 Temperature proﬁles of the different soldering methods

job:LAY05 page:86 colour:1

black–text

232 Reflowsoldering

5.10 References 1. Beine, H. (1997) Reﬂowsoldering of Wired Components, Productronic 12, pp. 14–15 (in German). 2. Rutter, G. (1997) Through-Hole Reﬂowsoldering. EPP (UK), May, p. 28. 3. Strauss, R. (1987) BABS 5th Intern. Conf. Brighton, UK. Paper 28. 4. For a detailed discussion of the deﬁnition of particle size distribution, see Ruthardt, R. (1990). Die Verfahren zur Lotpulvererzeugung . . . SMT/ ASIC/Hybrid Int. Conf., Nuremberg, pp. 93–105 (in German). 5. Thwaites, C. J. (1986) Some Metallurgical Aspects of SMD Technology. Brazing & Soldering, (UK), Spring 1986. 6. Short, R. H. and Lee, N. C. (1989) Fine Pitch Technology: Optimizing the Role of Solder Paste. EXPO SMT ’89, Nashville, Techn. Proc., pp. 83–85. 7. Hobby, A. (1990) Practical Aspects of Printing Solderpaste. Surface Mount Intern., Vol. 4, Issues 4 and 5. 8. Chilton, A. C. and Gaugler, K. W. (1990) Fine Pitch Solder Creams. Soldering & Surface Mount Technology, Oct. 1990. 9. Scheuer, I. (1993) The Importance of Viscometry of Solderpastes for Quality Assurance. 6th Academic Soldering Colloquium, Munich, DVS Report 153, Duesseldorf, Germany, pp. 46–55. 10. Burke, J. (1992) Fine Pitch Screen Printing. Electron. Manuf. & Test, Nov. Dec., pp. 33–34. 11. Short, R. H. and Lee, N. C. (1989) loc. cit. 12. Burke, J. (1992) loc. cit. 13. Burke, J. (1992) loc. cit. 14. Short, R. H. and Lee, N. C. (1989) loc. cit. 15. Friedrich, D. (1990) Dip pretinning of printed circuit boards for reﬂow soldering. Interconnecting Technology for Electronics, DVS Berichte 129, Duesseldorf, Germany, pp. 164–168 (in German). 16. Maiwald, W. J. (1992) SMD Placement without Solderpaste. EPP, Leinfelden, Germany, March, 1992, pp. 56–62 (in German). 17. Chu, T. Y., Mollendorf, J. C. and Pfahl, R. C. (1974) Soldering using Condensation Heat Transfer. Proc. Nepcon West 74, Anaheim, Cal., pp. 101–104. 18. Lea, C. (1988) A Scientiﬁc Guide to Surface Mount Technology. Electrochem. Publ., Ayr, Scotland, p. 237. 19. Lea, C., Scient. Guide., p. 254. 20. Rahn, A., European Patent EP 0340275 B 1 (8.11.89). 21. Turbini, L. and Zado, F. (1980) Chemical and environmental aspects of condensation reﬂow soldering. Electr. Packaging & Prodctn., 20, No. 1, pp. 49–59. 22. Grikitis, K. (1991) A Renaissance for Vapourphase Soldering. Electr. Manuf. & Test, Feb. 1991, pp. 11–14. 23. Bjoerkloef, A. (1990) VPS with preheat, the key to troublefree production. Nepcon West, Anaheim, Cal., 26 Feb.–1 Mar. 24. Reithinger, M. (1991) Reﬂow Soldering Technology for Surface Mount Assembly. Electr. Prodctn., March 1991, pp. 27–37.

job:LAY05 page:87 colour:1

black–text

Reflowsoldering 233

25. Flattery, D. K. (1986) IR Reﬂow for the solder attachment of surface mounted devices. Hybrid Circuits, No. 9. 26. Kolsters, J. W. M. and Beelen-Hendrikx, C. C. M. (1991) Process Requirements for Infrared Reﬂow Soldering. Philips Report 52/9OEN, Jan. 1991. 27. Reithinger, M. (1991) loc. cit. 28. Volk, H. (1990) SMT soldering without changing the proﬁle. Productronic, 10, pp. 72–74. (in German) 29. Arslancan, A. N. (1990) IR Solder Reﬂow in Controlled Atmosphere of Air and Nitrogen. Proc. Nepcon West (90), Anaheim, Cal., pp. 170–178. 30. Ivankovits, J. C. and Jacobs, S. W. (1990) Atmosphere Eﬀects on IR Reﬂow Soldering. Proc. SMTCON, Atlantic City, NJ, pp. 283–300. 31. Gruss, A. and Flattery, D. (1985) Improved reﬂow oven for SMD technology. Productronic, 5, pp. 30–34 (in German). 32. Bandyopadhyay, N., Kirschner, M. and Marczi, M. (1990) Development of a ﬂuxless soldering process for surface mount technology. Soldering and Surface Mount Technology, No. 4, pp. 23–26. See also USP 4.960.236. 33. Nylen, M. and Norgren, S. (1990) Temperature Variations in Soldering and their Inﬂuence on Microstructure and Strength of Solder Joints. Soldering and Surface Mount Technology, No. 5, pp. 15–20. 34. Volk, H. (1990) loc. cit (in German). 35. Lenz, E. (1985) Automated Soldering of Electronic Assemblies, Siemens, Munich, Germany, pp. 113–118. ISBN 3–8009–1449–2 (in German). 36. Palmer, M. J. et al. (1991) HAT Tool for Fluxless OLB and TAB. Proc. Electronic Comps. and Technology Conf., pp. 507–510. 37. Lea, C. (1989) Lasersoldering – Production and Microstructural Beneﬁts for SMT. Soldering and Surface Mounting Technology, No. 2, pp. 13–21. 38. Lea, C. (1988) A Scientiﬁc Guide to Surface Mount Technology. Electrochemical Publications, Ayr, Scotland, p. 302. 39. Moeller, W. and Knoedler, D. (1992) Fine Pitch Laserbeam Soldering of TABs. Verbindungstechnik in der Elektronik, March 1992, pp. 14–18 (in German). 40. Vardaman, E. J. (1993) International Developments in Fine Pitch TABs. 6th Academic Colloquium on Soft Soldering, Research and Practice; Munich, March, 1993. DVS Report 153, Duesseldorf, Germany. 41. Zimmer, G. (1993) Soldering Ultraﬁne Pitch components, esp. TAB Outer Leads. 6th Soft-Soldering Colloquium, Munich. DVS Report 153, Duesseldorf, Germany, pp. 166–176 (in German). 42. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Electrochemical Publications, Ayr, Scotland, p. 587. 43. Strauss, R. (1988) loc. cit (in German).

job:LAY06 page:2 colour:1

black–text

6 The circuit board

6.1 The beginnings The printed circuit board has come a long way since Paul Eisler ﬁled his pioneering patent in 1943. The patent describes how to create a network of metallic conductors on a ﬂat insulating board by printing its pattern in acid-resisting ink on to a metal foil, which is bonded to the board, and etching away the unprotected area. The idea had to wait till the end of the war in Europe before it was taken up by the America Bureau of Standards and used in anti-aircraft proximity fuses in the Far East. In the early ﬁfties the printed circuit board concept ﬁltered back into Europe, and quickly spread throughout the industrial world. In 1987, the annual production of circuit boards worldwide was estimated as 140 sq. km/55 sq. miles, which is about twice the area of Manhattan Island.

6.2 SMD-specific demands on a circuit board Mounting SMDs on a circuit board makes quite speciﬁc demands on its characteristics and its quality requirements. 1. The board must be more rigid. With melfs, chips and SOs, the soldered link between component and board is rigid itself and cannot absorb stresses which arise if the board should warp after soldering. This was no problem with wired joints, and is no great problem with the more ﬂexible leads of PLCCs and multilead devices but it matters with BGAs and ﬂip chips. 2. The demands on the ﬂatness of the board are higher. Before the advent of SMDs, the permissible bowing of a board across its length was 1%. Over a length of 25 cm/10 in, this would mean a diﬀerence in level between edge and middle of 2.5 mm/100 mil, which is unacceptable for the printing down of solder paste by stencil or screen. 3. At the other end of the scale is the three-dimensional board or ‘moulded interconnect device’ (MID), which made its ﬁrst appearance in 1994. Examples of MIDs are the housings of some mobile phones, miniature video cameras, or

job:LAY06 page:3 colour:1

black–text

The circuit board 235

4.

5.

6.

7.

portable radios. With all these, the conductive circuit pattern is deposited on the inside of the moulding, which for example may be an injection-moulded polymer or a hot-moulded thermoplastic. There are a number of options for creating such a conductive circuit pattern on the surface of the moulding, as for instance tampon-printing a conductive ink, or metallization by chemical deposition. Dedicated methods for dispensing solder paste onto the footprints of the three-dimensional circuitry, for placing the components, often by robotics, and for applying the soldering heat, mostly locally, have been developed. MID, an upwardly mobile technology, has made its appearance in the early 1990s,

and has become the subject of ongoing research, promoted and discussed at dedicated international conferences. Fine-pitch technology demands a circuit pattern of very high dimensional precision and reproducibility. The same is true for the soldermask and its register with the circuit pattern. To meet these requirements, the board manufacturer must invest in more expensive production equipment, and use base material of a higher speciﬁcation. This in turn means more expensive boards. For wavesoldering, SMDs must be anchored to the circuit board by adhesive joints which are located between their footprints. If any conductor tracks which run between these footprints, as they often do, are coated with solder, this coating may melt as the board passes through the wave. If the soldermask is a thin lacquer, it will warp (orangepeel eﬀect) and the adhesive joint will lose its footing. For this reason, the conductor tracks of most boards for SMD technology are bare copper (often oxidized to improve the bond between soldermask and track) and only the footprints and the lands of the throughplated holes are tinned. This technique is known as ‘soldermask on bare copper’ (SMOBC). Boards made from paper-reinforced phenolic resin (FR2) or epoxy resin without glassﬁbre reinforcing (FR3) are no longer used for SMD technology, except for cheap and undemanding products, because of their low mechanical properties. Miniaturization, the increasing population-density on the board surface, and the array-pattern of BGA footprints make new demands on circuit board layout and construction. The increasing density of footprints calls for multilayer boards with more and thinner layers. Printed wiring has to be routed through the narrowing gaps between footprints, or taken through vias to one of the inner board layers. The vias themselves are getting smaller, with mechanical drilling nearing its limits at diameters of 0.25–0.30 mm/10–12 mil. Still smaller holes (‘microvias’) are created by photo-imaging, plasma-etching or laser-drilling. The vias themselves are so small and ‘rob’ so little solder from an adjacent joint (see Figure 6.11), that they can be directly incorporated into the component footprints.

These techniques demand boards with top layers consisting no longer of glassﬁbre-reinforced laminates, but of homogeneous layers of polymer, similar to solder resist. The boards themselves are taking over the functions of some of the passive components: resistors are embedded in some of the lower layers, and copper deposits separated by an inner layer function as capacitors. The printed

job:LAY06 page:4 colour:1

black–text

236 The circuit board

wiring board is no longer a mere interconnecting device, but has become an electronic package with built-in resistors and capacitors. Naturally, increasing complexity of board construction and circuitry is reﬂected in increased costs, not only of manufacture, but also of bare-board testing.

6.3 Thermal management As long as circuit boards carried only wired components, the heat which they might generate during operation posed no great problem: there was suﬃcient space between components and the board to prevent the board from getting hot, and the lead wires took care of any dimensional mismatch between a warm component and the cool board. With SMDs, the situation is diﬀerent: the rigid soldered joints between melfs, chips and LCCCs (if used) come under stress when these components get warmer than the board; even if there is no temperature diﬀerence between components and the board, there is a mismatch of the thermal expansion coeﬃcient between the board and components with a ceramic body, such as melfs and chips. The relatively stiﬀ legs of PLCCs and SOs can also pose a problem, only the gullwing legs of QFPs and similar components are suﬃciently pliable to shield the joints from such stresses (Figure 6.1).

Figure 6.1 Thermal expansion: the behaviour of SMDs and wired components

job:LAY06 page:5 colour:1

black–text

The circuit board 237

With densely populated boards, and ICs with a large number of switching functions, the heat generated during operation may rise to 0.5 W/sq. cm (1.25 W/sq. in) of board area. This heat must be disposed of, and the consequences of the temperature rise of components and board must be dealt with.

6.3.1 Thermal expansion mismatch With chips, melfs and LCCCs, the thermal expansion mismatch between component and board was a problem, before the passive components started to become ever smaller and LCCCs began to disappear. Until then, considerable eﬀorts were made to devise circuit board substrates whose thermal expansion (TCE) matched that of such ceramic bodies better than the polymer-based FR4 (Table 6.1). Most of these substrates are more expensive than FR4, and they are used only if there is a compelling reason for matching thermal expansion between component and substrate. Metal-cored substrates are sometimes used because of their high thermal conductivity, in situations where a copper layer inside a multilayer board is not enough to conduct the heat created on the board to its edges or the nearest heat sink.

6.3.2 Effects of temperature differences between components and board Matching the TCE of the component and the board does not solve everything: after an assembly is switched on, its components warm up more quickly than the substrate. After switching oﬀ, the board stays warm longer than the components. This temperature diﬀerence causes strains, which the joints are expected to accommodate and which are proportional to the size of the component. At a temperature Table 6.1 Substrates and their thermal expansion coeﬃcients (TCE) Material

TCE ;10\/°C

Alumina ceramic FR4 (epoxy/glassﬁbre)

5.5 16

0.26 0.0016

— 1

4–8 4–8 4–8

0.0012 0.0013 0.0013

8 5 11

6

164

1.5

9–12

60

0.6

Fibre-reinforced polymer laminates Epoxy/Kevlarﬁbre* Epoxy/Quartzﬁbre Polyimide/Kevlarﬁbre* Metal composites Cu-clad Invar** coated with epoxy Porcelain-enamelled steel

Thermal conductivity W/cm/°C

*Heat-resistant polymer: © DuPont. **Invar: Ni–Fe alloy (35–59% Ni) with closely controllable CTE. Data supplied by Dr S. Smernos, Alcatel, Stuttgart, Germany.

Relative cost

job:LAY06 page:6 colour:1

black–text

238 The circuit board

diﬀerence between component and board of 50 °C/90 °F, the dimensional diﬀerence between the distance between the footprints on an FR4 board and between the ends of the body of the component are as follows: Ceramic bodies Dimensions Dislocation Chip or melf 5 mm/0.2 in long 1.3 m/0.05 mil Chip or melf 2 mm/0.08 in long 0.5 m/0.02 mil LCCC 25 mm/1 in wide 6.7 m/0.27 mil Plastic bodies QFP, BGA 25 mm/1 in wide 15 m/0.6 mil These ﬁgures illustrate the stresses which joints can experience under a given operating regime, and the importance of creating thermal links between components and heat sinks on or in a board for certain types of circuit board assemblies, in order to reduce the temperature diﬀerences between components under load and the board. The ﬁgures also show that as passive components, especially melfs, get ever smaller, the thermally caused stresses on their soldered joints become negligible. The thermal expansion coeﬃcient of plastics is high, and components housed in plastic like microprocessors are getting larger. But then, their thin leads are suﬃciently compliant to take care of the resultant mutual movements. Depending on the soldering method used, the joints on a freshly soldered board may become stressed after soldering is completed. If the complete assembly is heated to soldering temperature, the board and the components are equally hot. As the assembly cools after soldering, all joints solidify as the temperature passes through 183 °C/361 °F. From then on, board and components cool down to room temperature, each contracting according to its own coeﬃcient of contraction (i.e. expansion). This leaves every joint with a locked-in stress as it starts its life. With wavesoldering, and vapourphase, infrared and convection reﬂowsoldering, board and components get equally hot, and therefore this consideration applies. With laser soldering and thermode reﬂowsoldering, both board and component remain more or less at room temperature. With multilayer boards, a continuous copper layer below the board surface, with provision of course to allow for the passage of vias leading to lower layers or the other side of the board, can serve to conduct the heat generated by the components to the edges of the board, where it can be suitably disposed of. Metal-ﬁlled, heat-conductive adhesive is often used as the thermal link between the underside of such components and the copper layer. The latter is made accessible to the heat-conductive medium by blind holes leading to it. With modern, battery operated handheld electronic assemblies, the dissipation of heat generated in the components is no longer a problem.

6.4 Solderable surfaces A consistently good solderability of lands and footprints is an essential precondition for soldering with a low reject rate. As a rule, the solderability of a circuit board is

job:LAY06 page:7 colour:1

black–text

The circuit board 239

enhanced and preserved by applying a coating of tin, or preferably solder to its copper surfaces (Section 3.6.3). Recently, several vendors of equipment for wavesoldering or reﬂowsoldering under nitrogen claim that pretinning of footprints is no longer necessary, and plain copper footprints, since they do not oxidize at soldering heat, will suﬃce. This presupposes that the copper is perfectly free from oxide to begin with, and has not deteriorated during storage or handling. Experience will have to show whether this practice can prevail.

6.4.1 Galvanic coatings Several manufacturing methods of circuit boards include an electroplating process whereby the pattern of the conductors and footprints is created by the so-called ‘patternplating’ of a tin–lead deposit onto the copper laminate. This plated pattern serves both as an etch resist in the next manufacturing stage and as a solderabilityenhancing and preserving coating afterwards. Because a galvanic tin–lead coating is a somewhat porous layer of discrete tin-rich and lead-rich particles, it must be reﬂowed in order to be able to preserve the solderability of the substrate beneath (Section 3.6.3). This reﬂow process serves at the same time as a quality check: if the solderability of the copper underneath the plating is unsatisfactory, the reﬂowed coating will show conspicuous signs of dewetting. A minimum coating thickness of 5 m/0.2 mil is considered necessary to ensure long-term solderability. In the mid-1990s, galvanic gold/nickel coatings have been introduced as protective and readily solderable coatings for copper surfaces. As mentioned in Section 3.6.6, gold is one of the most easily solderable surfaces, but too much of it can seriously weaken a joint. The AuNi galvanic coating which has been developed for preserving the solderability of footprints on circuit boards is reported to be safe in this respect. It consists of a galvanic nickel undercoat, covered with a gold deposit 0.005 mm/0.2 mil thick. At the time of writing (1997) it has been well received. A corrosion-resistant, solderable coating of palladium, one of the corrosion-resistant noble metals, is also being oﬀered, with thicknesses from 0.001–0.02 mm/0.04– 8 mil. It is said to be suitable for both wave and reﬂowsoldering (see also Section 2.3.2).

6.4.2 Hot tinning Hot-air levelling (HAL) This process was initially developed for enhancing the solderability of boards with through-plated holes. It involves vertical immersion of a ﬂuxed board in a bath of molten solder, or ﬂooding it with molten solder by passing it horizontally through a solderwave. Afterwards, the molten solder must be blown out of the holes by an array of high-pressure jets of hot air, before it solidiﬁes, hence the name of the process. HAL leaves the footprints with a domed coating of solder, which may reach a thickness of 25 m/1 mil in the middle of a footprint or land, but which tapers

job:LAY06 page:8 colour:1

black–text

240 The circuit board

down to as little as 1 m//0.04 mil towards its circumference. With through-plated holes, this happens at the shoulder between the barrel of the hole and its land (Figure 6.2). This phenomenon, which is called a ‘weak shoulder’, can be avoided by careful control of the operating parameters of the tinning machine. It can create a solderability problem. After a time, the steady growth of the intermetallic layer between the copper and the solder will cause the Cu Sn () to reach the surface. Once exposed, it soon oxidizes and becomes almost insolderable, even with strong ﬂuxes (Section 10.4.2, p. 353). The domed proﬁle of HAL-tinned footprints, on the other hand, may cause problems when multilead components are to be impulse soldered: the thin, ﬂexible leads may slip sideways under the pressure of the thermode and give a defective joint (Figure 6.3). For this reason, HAL tinning is only appropriate for boards with through-plated holes, i.e. for mixed SMD/leaded component technology. For pure SMD boards, especially with ﬁne-pitch footprints, other pretinning methods are more appropriate. Lately, HAL has come under the suspicion of lowering the surface insulationresistance (SIR) of a hot-tinned circuit board, because the process involves the use of a highly polar, halogenated tinning ﬂux. A lowered SIR would be a cause for concern with ﬁne-pitch technology.

Rollertinning Rollertinning is a cheaper alternative to HAL tinning, suitable mainly for the tinning of single-sided boards. It involves passing the circuit board between two horizontal rotating rollers, of which the lower one is made of steel, and half immersed in a bath of molten solder (Figure 6.4). Rollertinning gives a coating

Figure 6.2 ‘Weak shoulder’ of HAL-tinned through-hole

Figure 6.3 Domed HAL-solder coating on a footprint

job:LAY06 page:9 colour:1

black–text

The circuit board 241

Figure 6.4 Rollertinning

thickness of between 2 m/0.08 mil and 5 m/0.2 mil, which is thick enough to protect footprints for about one year’s storage before the layer comes to the surface. On the other hand, every footprint carries a small ‘blip’ of solder, which can be up to 100 m/4 mil high at its trailing edge, where the footprint emerged from the nip between the two rollers. It is caused by part of the peelback between the tinning roller and the board hanging on to the footprint. Some board users object to these blips on cosmetic grounds, while others report problems with component placement. Like HAL, rollertinning involves the use of acidic ﬂuxes with high halogen levels. Therefore, rollertinned boards are, or should, only be used on low-cost, low-technology products.

6.4.3 Organic coatings Coating circuit boards with a lacquer of rosin ﬂux was one of the earliest protective measures to preserve the solderability of a circuit board. It is eﬀective and cheap and still being used in low-cost manufacture. However, it has some obvious practical drawbacks, such as getting sticky at higher temperatures and being sub-

job:LAY06 page:10 colour:1

black–text

242 The circuit board

ject to age-hardening, like any rosin varnish. More sophisticated coatings are based on ‘complex-forming’ organic compounds (Benzotriazole or Imidazole), which provides a stable protective coating on copper surfaces under reasonable storage conditions. Though known for a long time, they have recently found wide acceptance under the generic name of ‘organic solderability protection’ (OSP). They give good results with wave and reﬂowsoldering under nitrogen.

6.4.4 Flat solder depots In recent years, methods for creating ﬂat solder depots which are fused to the copper laminate on every footprint have been proposed. The depots are in the form of a ﬂat pad of solder, 0.1 mm/40 mil to 0.2 mm/80 mil thick, which is fused to and fully covers every footprint. The thickness of the solderpads corresponds normally, but not necessarily, to the thickness of the surrounding soldermask (Figure 6.5). Two ways have been proposed to create these pads. In one of them, molten solder is applied to the circuit board in such a way that it tins the preﬂuxed footprints and covers them, while the surrounding ﬁlm of solder resist acts as a shim which deﬁnes the thickness of the solderpad. Its ﬂat surface is deﬁned by a plate pressed against the circuit board.

With the other system, solder paste (which need not be of ﬁne-pitch quality) is squeegeed over the footprints, with the surrounding soldermask acting as a stencil. Alternatively, a stencil is placed over the dry-ﬁlm resist, which allows a thicker paste printdown. Subsequently, the solder paste is reﬂowed, so that it forms a domed solderdepot on every footprint. Finally, these domed depots are ﬂattened by a heated platen, with the soldermask acting as a shim which deﬁnes their thickness (Figure 6.6).

Putting the solder depots on the boards is the task of the board manufacturer and the assembler is relieved of the complexities of printing or dispensing solder paste on to his circuit boards. All he has to do is to apply ﬂux, either to the whole board surface or selectively to the ﬂat solder depots, then to place the components on the board and to proceed to reﬂowsolder them. Fluxes which act as an adhesive to keep the components in place, while the boards are being handled between placement

Figure 6.5 Flat solder depot

job:LAY06 page:11 colour:1

black–text

The circuit board 243

Figure 6.6 Two options for creating ﬂat solder depots (the Sipad © process)

and soldering, are commercially available. Obviously, there has to be a trade-oﬀ between the necessarily high cost of boards with ﬂat solder depots, and the savings which the board assembler can realize by using them. At the time of writing (1997), ﬂat solderdepots have not yet swept the ﬁeld. The solder-jet technique, engineered by MPM, is a more recent arrival on the scene of ﬁne-pitch solder deposition. The general concept is not unlike an ink-jet printer: a vibrating plunger expels small droplets of molten solder from a liquidmetal reservoir. Their downward trajectory subsequently passes between two sets of electrostatic electrodes, which guide the solder droplets to their targets. With solder-jetting, the rate of deposition is said to match the production rate of paste-printing. Other uses of solder-jetting include the putting of solderbumps on the underside of BGAs and ﬂip-chips (Section 2.2), or creating solder depots on three-dimensional substrates (MIDs) which cannot be screenprinted (see Section 6.2). The pattern of the solder-jet deposition can be CAD controlled.

job:LAY06 page:12 colour:1

black–text

244 The circuit board

6.5 The soldermask The soldermask was originally introduced in the ﬁfties, primarily to reduce solder consumption by preventing the unnecessary tinning of every conductor line, and also in order to reduce the copper contamination of the solder in the wavesoldering machine. Its other advantages of improving joint quality and facilitating inspection by conﬁning the solder to the lands soon became apparent. By the time SMDs appeared, the use of the soldermask was universal. SMD technology does not place any speciﬁc requirements on a soldermask. With ﬁne-pitch boards, creating the very narrow strips of mask between adjacent footprints is becoming increasingly diﬃcult, and places high demands on process control. The necessity of separating the footprints by these strips of soldermask is beginning to be queried by several board makers and users, and no adverse eﬀects of their omission have been reported.

6.6 Layout A good board layout must be user-friendly, in the sense that the initial user of a ﬁnished circuit board is the person who must solder the components to it. The more diﬃcult this becomes, the greater the likelihood of something going wrong. Soldering faults mean rework and rework means increased costs, while reworked joints are likely to be less reliable. Naturally, the ﬁrst task of the layout designer is to create a circuit which functions electronically and which fulﬁls the tasks for which it is intended. But if the layout places excessive demands on its manufacture, the commercial success of the end product may be at risk. To make a layout user-friendly in the above sense, the circuit designer must know which soldering method is to be used. Some layout rules are speciﬁc for wavesoldering, others for reﬂow.

6.6.1 Layout for wavesoldering Avoiding skipped joints The main problem with wavesoldering SMDs is the ‘skipped joint’, the joint which the solderwave could not reach because of the ‘shadow eﬀect’ (Section 4.4.4), which even the best double wave cannot always overcome. A good wavesoldering layout helps the molten solder to ﬁnd its way to joints which are hidden behind or partly underneath a component (such as the legs of PLCCs). An extended footprint, or a short length of conduit which is not covered by the soldermask, helps to lead the solder to a joint close to a high component housing; footprints for melfs and chips should extend far enough to provide an aspect angle of about 60° (Figure 2.4). This allows for a slight misplacement of the component, so that in no circumstances does the angle get steeper than 45° (Figure 6.7). Setting diﬃcult components such as PLCCs at an angle of 45° against the direction of travel of the board is another way of helping the solder to reach the joints on the

job:LAY06 page:13 colour:1

black–text

The circuit board 245

Figure 6.7 Letting the conductor track lead the solder to the joint

Figure 6.8 Mitigating the shadow effect. (a) Favourable alignment; (b) unfavourable alignment

shadow side (Figure 6.8). Of course, this measure wastes valuable real estate on the board, and is therefore often unacceptable. As an alternative, the whole board, if it is small enough, can be set obliquely on the transport carriage. Some machine vendors provide a third alternative by oﬀering wavesoldering machines where the soldering wave is set at an angle towards the line of the conveyor belt. This makes it possible to solder full-size boards (see also 4.4.3 and 4.4.4 and Figure 4.17).

Avoiding solderbridges Solderbridges are the result of some idiosyncrasies of the peelback behind the solderwave (Section 4.4.3). With a row of footprints, provided the pitch is not below 1.25 mm/50 mil, it is easier to avoid bridges when they emerge from the wave in single ﬁle rather than all of them together in a broad front (Figure 6.9).

job:LAY06 page:14 colour:1

black–text

246 The circuit board

Figure 6.9 Preferred alignment relative to direction of travel. (a) Favourable alignment; (b) alignment resulting in the formation of bridges

Wavesoldering in a nitrogen atmosphere extends bridge-free soldering below that limit (Section 4.4.6). As a row of footprints leaves the wave in single ﬁle, the peelback seems to jump from print to print, until the last two emerge, when a bridge tends to form between them. Placing a somewhat larger dummy footprint, called a ‘solderthief’ (see Figure 4.15, Section 4.4.3), at the end of the row draws the bridge to a place where it does no harm. With the footprints for square multilead components, a solderthief is placed into each corner so as not to restrict the choice of the direction of travel. This expedient is often written into the software of the layout program.

Soldering in a nitrogen atmosphere: its effect on bridging Under the terms of surface tension, a solder bridge should not really exist, and it could be called a ‘metastable’ state: because it does not represent the smallest possible surface area of the molten solder, it ought to pull back onto the footprints, and the surplus should break up into drops of solder. This may not happen, either because there is no time for it before the solder solidiﬁes, or more likely because a thin skin of surface oxide reduces the mobility of the molten solder. Experience with soldering equipment working in a nitrogen atmosphere with roughly 20 ppm of oxygen, be it a wavesoldering machine or a reﬂow installation, conﬁrms that in the absence of oxygen, bridging is very much reduced. Some of the solderballs which are found on boards which are wavesoldered under nitrogen (Section 4.6), and which represent the trade-oﬀ for this advantage, are the debris of broken-up solder bridges.

job:LAY06 page:15 colour:1

black–text

The circuit board 247

Layout for boards with a mixed SMD/leaded component population With such mixed technology boards, the following contingencies must be borne in mind: 1. Should the SMDs have to be placed and glued to the board as the ﬁrst step, they must be spaced so as to allow enough room for the crimping tool of the machine which inserts the leaded components afterwards. If this is not done, some SMDs might get knocked oﬀ the board. It is advisable to know which type of insertion machine is to be used when the layout is drafted. 2. If the SMDs are placed after the leaded components, the space requirements of the placement head of the pick-and-place machine must be taken into account when the spacing of the SMDs is being decided.

6.6.2 Layout for reflowsoldering The layout rules for reﬂowsoldering are governed by three considerations: 1. The components must stay ﬁrmly in their allocated positions. Leaded components and wavesoldered SMDs are ﬁxed in their positions before soldering starts. In reﬂowsoldering, the SMDs ﬂoat on molten solder during a crucial period. They are then at the mercy of the forces of surface tension and of capillarity, which act between the footprints. These forces also act between the metallized endfaces in the case of melfs and chips and the component legs in the case of all the others. Depending on the geometry of the footprints, this can be a help or a cause of trouble. Impulse soldering and laser reﬂowsoldering are exceptions: with the former, the soldering tool ﬁrmly presses the legs down onto the footprints during soldering; with laser soldering the joints are soldered one-by-one, so the component is never free to ﬂoat. 2. All of the available solder depot must contribute to forming the joint; none of it must be tempted to ﬂow away from it. 3. With many reﬂowsoldering methods, both the amount of heat supplied to the joints, and the soldering time are limited. Because it is important that all joints of a component reach roughly the same temperature at the same time, the heat capacity of footprints should be uniform (see Figure 5.30).

Surface tension and capillarity Surface tension tries to make the free surface of a liquid as small as possible; capillarity pulls two ﬂat, wetted surfaces towards one another as closely as possible (Section 3.6.2). As long as all the footprints of a component have the same shape and size, surface tension and capillarity tend to pull every solderable surface towards the middle of its footprint (see Figure 3.17). This ‘self-alignment’ is eﬀective with chips, melfs and BGAs and ﬂip-chips.

job:LAY06 page:16 colour:1

black–text

248 The circuit board

If there is a lack of symmetry between the footprints of a component, the footprint which oﬀers more capillary force than the other, or the footprint on which the solder melts earlier, tries to pull the wetted surfaces of the component towards itself, while the component is free to move (Figure 6.10). Lack of symmetry is also behind the phenomenon of ‘tombstoning’ of chips (see Figure 3.18). There may be several reasons for this asymmetry. The solder may melt and wet the metallized face of the chip earlier or better at one end than at the other, because of a diﬀerence in heat capacity or because one end is more solderable than the other. A faulty paste printdown may also be to blame: there may be less solder paste on one footprint than on the other, or maybe none at all. Finally, yet another layout fault may be to blame: if there is a possibility of capillary action robbing a footprint of some of its solder, for example through the proximity of a via (Figure 6.11), the molten solder on the aﬀected footprint will exert less pull on the component than the solder at the other end. The better end wins, because its surface forces are stronger or start to act earlier, and so they pull the weaker end oﬀ its pad. As a consequence the aﬀected chip ﬁnishes by standing upright on its better end. Tombstoning aﬀects only bipolar SMDs, and among those mainly chips. It is rarely observed with melfs.

Figure 6.10 The dangers of asymmetry. (a) Floating caused by lack of symmetry between left and right footprint areas; (b) remedy

Figure 6.11 Footprint starved of solder by neighbouring via. Remedy: a bridge of solder resist between the via and the component footprint

job:LAY06 page:17 colour:1

black–text

The circuit board 249

Layout for impulse soldering With impulse soldering, equal heat capacity of all footprints of a component is important. Large footprints heat up more slowly than small ones, and since with impulse soldering the heat pulse is the same for all joints and must be as short as possible, the consequences of asymmetry are either badly soldered large joints or overheated small ones (see Figure 5.30).

Layout for BGAs The reworking of BGAs (Section 10.4.2) involves a regime of local heating and manipulation, which might aﬀect the health and safety of soldered joints in the immediate neighbourhood. It has been suggested that a 5 mm/0.2 mil in wide ‘keep out’ zone around the perimeter of the BGA would make its removal and replacement less risky, provided the demand for board ‘real estate’ will allow this luxury.

6.7 References 1. British Patent 639,178,02; 02 (1943) Strong and Eisler, Manufacture of Electric Circuits and Circuit Components. 2. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Electrochemical Publications, Ayr, (Scotland), p. 376. 3. Hunter, P. (1995) MIDs – PCBs move into the third dimension. El. Prod. (UK), June, pp. 10–13. 4. Research Assoc. Three-Dimensional Electronic Assemblies, University Erlangen, D-91058 Erlangen, Germany. 5. Puymbroek, J. V. et al. (1996) ‘MOV’-Technological Innovation in Circuitboard Technology. Productronic, December, pp. 12–16 (in German). 6. Friedrich, D. (1990) A Circuit board Surface which Optimises the Metallurgy and Processing Technology of Reﬂowsoldering. Proc. SMT/ASIC/Hybrid Internat. Conf., Nuremberg, Germany, June 1990 (in German). 7. Maiwald, W. J. (1993) Can SIPAD© Technology Provide Better and More Reliable Board Assemblies? DVS Report 153, Duesseldorf, Germany, pp. 124–130. (© Copyright, Siemens AG.) (In German.) 8. Hall, R. (1997) Solder Jetting: Mission accomplished. Electronic Production, February, pp. 10–12. 9. Peck, D. J. (1997) BGA Rework – Issues and Answers. Future Circuits International, 12, No. 1, pp. 111–118. 10. Woodley, D. (1997) The revolution in interconnection. Electronic Production, February, pp. 13–14.

job:LAY07 page:2 colour:1

black–text

7 Component placement

7.1 The task ‘Pick-and-place’, the common name for equipment which puts SMDs on circuit boards, is an apt description of its tasks: 1. The correct component must be selected from a magazine or feeder. 2. It must be placed on the correct footprints, in the correct orientation, and with the required precision. These two straightforward tasks are getting ever more demanding, as the diversity of components grows and as footprints continue to get smaller and more closely spaced. Some components, like melfs, are getting smaller, and others like QFPs and TABs get larger, with over a hundred closely spaced leads. Minimelfs 0204 (3.6 mm/142 mil ; 1.4 mm/56 mil dia.) have become common, and micromelfs 0102 (2.0 mm/80 mil ; 1.1 mm/44 mil dia.) have begun to appear in vendors’ catalogues. PLCCs and QFPs reach dimensions of 29.4 mm/1.16 in or above. These demands are the driving force for the increasing sophistication and specialization of the pick-and-place equipment which is on oﬀer. Depending on whether the boards are to be wavesoldered or reﬂowed, the placement operation is either preceded or followed by an additional process. For wavesoldering, placement of the components is preceded by putting down a metered amount of adhesive between the footprints. The components having been placed, the assembly is heated to cure the adhesive before soldering (Section 4.9). Placement for reﬂowsoldering is preceded by covering the footprints with a metered amount of solder paste, unless the footprints carry a solid solderdeposit. The placement of SMDs as such is simpler, and pick-and-place machines can handle a greater variety of components than insertion machines for leaded components, because insertion demands diﬀerent equipment for axial, radial and DIL components (Table 7.1). The various forms of packaging in which SMDs reach the user are given in Section 1.4. Normally, a user has a choice of packaging systems to suit his placement methods:

job:LAY07 page:3 colour:1

black–text

Component placement 251

Table 7.1 The diﬀerence between the tasks of placing SMDs and of inserting wired components Inserting wired components

Placing SMDs For wavesoldering For reﬂow

Placing components on tape* Sequencing components

Placing components in blistertape or magazines* Placing the Printing the adhesive solder paste Collect a component Place a component Cure the adhesive Solder on the Reﬂow wave

Preform the leadwires Insert a component Crimp leadwires Solder on the wave *Normally the task of the vendor

Chips Melfs SOs PLCCs QFPs TABs BGAs Flip Chips

Choice of packaging systems Paper or plastic blistertape; bulk package Paper or plastic blistertape; bulk package Plastic blistertape; linear magazine Plastic blistertape; linear magazine Waﬄe trays Film Waﬄe trays, linear magazine Waﬄe trays, linear magazine

Automated placement equipment places speciﬁc demands on paper and plastic blistertape: the coverfoil must peel away smoothly and without jerking from the tape, otherwise components are liable to jump out of the tape and jam the machine. Paper tape must not form ﬂuﬀ which might interfere with the placement mechanism.

7.2 Reliability of placement The automatic placement of SMDs introduces ﬁve potential defects: Missing components Wrong components Wrong polarity Misregistration with the footprints Mounting in the wrong place The ﬁrst three, which used to be the major sources of defect, are largely avoided by the now universally available ‘smart’ placement machines which check the presence, identity, polarity, and often the functional integrity of every component between picking it up and putting it down (see below). The elimination of the last two is the aim of the continuing reﬁnement of today’s placement equipment.

job:LAY07 page:4 colour:1

black–text

252 Component placement

Positional accuracy With ﬁne-pitch lead spacing, the width of the footprints is half their distance. Fine-pitch below 0.5 mm/20 mil and ultraﬁne-pitch with 0.25 mm/10 mil spacing have become real demands. This means footprints 0.125 mm/5 mil wide, and lateral placement accuracies of ±0.06 mm/2.5 mil. Pick-and-place equipment with a placement accuracy of ±0.05 mm/2 mil, and a repeatability of ±0.02 mm/0.8 mil is commercially available. Angular accuracy of placement also matters. With a QFP of dimensions 25 mm/ 1 in ; 25 mm/1 in, an angular twist of 1° means a lateral displacement of 0.22 mm/ 8 mil at every corner. As a result, with a ﬁne-pitch layout, about half the legs would sit on the wrong footprint (Figure 7.1). Therefore, with large ﬁne-pitch components, angular placement accuracy has to move into the ±0.1° bracket. Because BGAs and ﬂip-chips are able to correct even massive misplacement by self-alignment as soon as the solder melts (see section 2.2), the accuracy of their placement is less critical.

Component identity and functionality checks The number of placement errors is a measure of the reliability of a placement system. Until not so long ago, wrong-value chips and melfs in blistertape or bulk packages contributed signiﬁcantly to manufacturing reject rates. Smart placement systems, which detect and correct such errors during placement ‘on-the-ﬂy’ brought a drastic improvement and have become a common feature with most automatic placement machines.

Figure 7.1 Angular accuracy of placement

job:LAY07 page:5 colour:1

black–text

Component placement 253

7.3 Placement options A user must decide between two strategies of component placement: on the one side are the manual and semi-automatic manual methods, on the other the fully automatic ones, which also fall into two categories, the sequential and the simultaneous systems. The choice between them depends on several factors: 1. A newcomer to SMD technology who operates on a small-to-medium scale will tend to opt for a manual or semi-automatic system, unless he is part of an organization where in-house know-how and technical assistance with fully automatic systems are available. 2. The type of product and the volume of production are crucial factors. If there are no more than about 50, at most 100 components, on a board, however complex their function and the layout, and if the number of boards does not exceed a few hundred per working day, a manual, probably semi-automatic placement system may well be the best choice. As the number of boards to be processed per day rises, the cost eﬀectiveness of purely manual placement soon drops. Semi-automatic placement reaches its maximum cost eﬃciency in the middle range of production volume, particularly where full-time working is not always guaranteed. A further factor which aﬀects the choice of system is the product mix: if the boards are all customer-speciﬁc boards, each with a short or unpredictable length of run, and if production must be ﬂexible and capable of coping with frequent changes, semi-automatic manual placement may be best. It is worth noting, though, that recent years have seen the arrival of several fully automatic pick-and-place machines of great ﬂexibility, with facilities for a rapid change-over from one working program to another. In the last resort, the size of the necessary investment must be decisive. Naturally, manual and semi-automatic equipment is cheaper, and writing it oﬀ is less of a problem when faced with a ﬂuctuating and highly diﬀerentiated demand. On the other hand, where one or a number of soldering lines must be fed with assembled boards, without the risk of costly interruptions, one or more fully automatic pick-and-place installations are the best, if not the only choice.

7.3.1 Fully manual placement Like every placement system, placing SMDs by hand involves two steps: ﬁnding and fetching the component, and then putting it down on its footprints, having rotated it into its correct orientation (Figure 7.2). With boards to be wavesoldered, placement is preceded by putting down the spots of adhesive with a handheld syringe or by hand stencilling. The footprints of boards to be reﬂowsoldered are provided with solder paste, again from a syringe, a metering dispenser, or by manual stencilling. As with all manually operated processes, good ergonomic design of the work place is the precondition to get the best possible results with a minimum of errors. Even so, manual placement without any additional aids like assigning to each type of

job:LAY07 page:6 colour:1

black–text

254 Component placement

Figure 7.2 The basic tasks of manual placement

component its proper set of footprints, needs good housekeeping and unremitting concentration. It should be practised only for assembling small numbers of prototype boards, or very simple assemblies with few types of components. Even with entirely manual placement, no component should ever be touched with bare ﬁngers. As has been said several times already, however clean ﬁngers are, they will transfer fatty acids and salts to the components and their soldering surfaces. This aﬀects their solderability, especially if adhesive joints must be cured before soldering. The curing heat greatly intensiﬁes the damaging eﬀect of any surface contamination on a soldering surface. Tweezers can be used for handling the components, but a vacuum pipette with a ﬁnger-actuated rotatable head is much more convenient. The pipette may be handheld, or mounted on a gantry which is operated by a ‘joystick’. With both, the accuracy of placement depends on the normally very high degree of coordination between the human eye and the human hand. Most operators, with some training, have no problem in putting down components on ﬁne-pitch footprints without smudging the solder paste. It may be worth remarking here that, so far, no vendor seems to have found it worth his while to provide manual placement equipment which can be converted for left-handed operators. With manual placement, there are three kinds of possible errors: picking the wrong component, putting it in the wrong place and, with active components, placing it the wrong way round. Every manual placement system, however well conceived, which uses a bulk feed system of loose melfs or chips contains one further, and dangerous, source of placement error: one or more stray components may have found their way into the wrong compartment of a carousel or feeder box. If such an error is noticed, or maybe only suspected, it may be simpler and cheaper to discard the contents of the whole compartment than to try to ﬁnd the rogue components amongst several hundred correct ones. It is important to allow the operator regular intervals of rest, at least ﬁve to ten minutes every hour. It has been found that, depending on the complexity of the board and the number of component types, the error rate rises rapidly with less than that amount of rest time. With ten to twenty components per board and not more

job:LAY07 page:7 colour:1

black–text

Component placement 255

than ten diﬀerent types of components, placement rates of up to 500 or 600 components per hour can be realized with purely manual placing. This can drop to 300/hour with more complex boards. Components may be picked from a turntable (carousel) which is subdivided into a number of compartments holding loose components, from a row of horizontal feeders, which present the components from the open ends of blistertapes, from stick magazines or waﬄe trays. With purely manual placement, the error rate may drop below 0.1%, i.e. :1000 ppm. But errors there will be, and in order to avoid expensive rework it is strongly advisable to inspect every board for correct placement before soldering it. Corrections are made by lifting oﬀ the oﬀending component. Melfs and chips, unless valuable, are best discarded. SOs and gullwing-legged components can be re-used, after the legs have been cleaned with isopropanol. The footprints are wiped clean of solder paste with a small piece of cotton or linen soaked with isopropanol. Dots of adhesive are best left alone, lest they be smeared over a footprint, which will become unsolderable. Adhesive vendors may be able to recommend or supply a suitable solvent to clear oﬀ an adhesive spot. The place having been cleaned up, fresh solder paste (or adhesive) is put down and the component is replaced.

7.3.2 Semi-automatic placement Semi-automatic placement machines take over some of the tasks of manual placement. These are principally those where human error could creep in, such as picking the right component and putting it in its correct place. Moving the components from their feeders to their footprints, and putting them down with the necessary precision, is still left to the sensory and muscular feedback system between the human eye and hand, a system which can be replicated by electromechanical and opto-electronic means only at great expense. All semi-automatic manual placement machines are linked with a computer system, which can be either integral to the machine or operated by a separate PC. Such a system can be programmed to indicate by an LED or a spot of light the feeder from which the next component must be fetched. At the same time, the place where it has to be put down is illuminated by a beam of light, or indicated in some other way. These functions can be reﬁned and added to. Some semi-automatic placement machines make only the correct feeder accessible, while the others are covered. Feeders are mechanized to automatically present the next component after the preceding one has been collected. The vacuum pipette which handles the component can be mounted on a traversing mechanism which ﬁrst guides it to the correct feeder, and then to the correct location above its placement position. The operator then lowers the pipette and guides it to its exact position. As the component touches down, the vacuum in the pipette may be released automatically. Finally, the controlling computer can be programmed to work out the most economical placement sequence to save time-wasting movements. Depending on the complexity of the board and the mix of components, the capacity of semi-automatic placement systems with full computer support can rise to about 900 components per hour.

job:LAY07 page:8 colour:1

black–text

256 Component placement

7.3.3 Fully automatic sequential systems General features The term ‘sequential’ means that, as with the manual systems, the machine always places one component at a time (Figure 7.3). Apart from that, a fully automatic sequential placement system is like a semi-automatic manual system, with the human element replaced by opto-electronic and electromechanical means. Taking out the human element has several consequences: 1. Fully automatic equipment is more expensive, by one or more orders of magnitude. 2. Fully automated sequential placement is faster, with a capacity of up to 60 000 components per hour. 3. The high accuracy of placement demands a robust and stable platform on which the moving parts are mounted. This in turn means a design based on the technology of a precision machine tool rather than of a mechanical plotter.

Flexibility With most users of pick-and-place equipment, ﬂexibility of the system is a crucial requirement in order to reduce down-time of the expensive equipment to a minimum. In this context, ﬂexibility means the ease and speed with which a machine can be switched from one type of board to another. Such a change-over involves changing the array of feeders and the pick-and-place sequence. The latter needs little time if the operating software already exists. If it does not, it can often be created while the machine is still busy placing components on another board. Assembling the array of feeders and loading them with the required tapes and magazines takes more time. Many state-of-the-art machines have mobile feeder arrays which can be assembled away from the machine. An array can be fully loaded with the tapes and magazines for the next run while the machine is still busy on the preceding one. For the change-over, feeder arrays can be quickly exchanged against one another. Working out the best sequence of components in a feeder array,

Figure 7.3 Sequential placement

job:LAY07 page:9 colour:1

black–text

Component placement 257

together with the most economical pick-and-place sequence, is a matter of software and programming.

Additional functions Apart from picking and placing components, most automatic pick-and-place machines can put down single drops of adhesive for SMDs which are to be wavesoldered. When placing BGAs or ﬂip-chips on ‘bare’ footprints, which have not been provided with a deposit of solder paste, several placement machines have the facility to give the component a shallow dip in a tray of no-clean ﬂux between pick-up and placement.

‘Smart’ machines Smart machines observe and react to circumstances, and detect errors and take the appropriate action. In the context of component placement, this includes the following: E Feeder units identify the tapes or magazines loaded into them, and in the case of an error give a signal or prevent operation until the mistake is rectiﬁed. E Placement heads identify the components they have picked up, and check some of their basic functions (‘in-ﬂight testing’). Multilead components are checked for the coplanarity of the lead ends. E Vision centring systems align ﬁne-pitch components with their footprints before setting them down.

Grouping of placement units Placement lines can be assembled from individual automatic placement units, which are linked together and operated as a CIM system. This makes it possible to multiply the capacity of the placement section while still maintaining its ﬂexibility to respond quickly to changing production requirements.

7.3.4 Simultaneous placement systems Some types of electronic product like domestic audio and video equipment involve long runs of similar boards which are not particularly complex but which are produced in large volume. These boards are soldered on high-capacity lines, which may be wave machines or reﬂow ovens. They in turn must be fed by placement equipment of equally high output. For this task, simultaneous placement systems are better suited. As the name implies, a number of components are picked and placed at the same time at every working stroke of the machine (Figure 7.4). A number of placement arms, each of which can choose between several feeders, pick up components simultaneously. The length of the stroke of each arm determines where the component comes

job:LAY07 page:10 colour:1

black–text

258 Component placement

Figure 7.4 Simultaneous placement

down. If the boards are to be wavesoldered, a dot of adhesive is placed on the underside of each component as it moves forward to be placed.

7.4 The practice of automatic component placement 7.4.1 The range of choice One of the driving forces behind the development of automatic placement equipment is the evolution of the SMDs themselves. In some respects this seems to have reached a plateau, at least a temporary one: the miniaturization of melfs and chips (‘birdseed’ in the language of component users) has probably stopped with components 1 mm/40 mil wide and 2 mm/80 mil long. The size of multilead components may have reached a temporary limit with 55 mm/2.2 in square, which with a 0.5 mm/20 mil pitch gives a leadcount of about 400. The makers of automatic placement equipment have responded, many of them in collaboration with their customers. The advent of ﬂip-chips and BGAs posed no fresh problems; if anything, the accuracy of placement is less critical because of the capacity of these components for self-alignment, after the solder has melted (see Section 3.6.3). An essential requirement will all placement machines is a robust construction, resembling that of a machinetool rather than of a piece of oﬃce equipment, which needs frequent attention. The importance of a high placement speed depends very much on whether the machine is part of a high-output assembly line, soldering a limited number of types of board, or whether the user solders comparatively shorter runs of a larger variety of boards, as would be the case with a contract assembler for example. Common needs of most users are ease and storability of programming, a wide range of components which the machine can handle, and speed of changeover from one placement program to another. A recent survey lists 24 vendors in the USA, Europe, and Japan. The functional capabilities of the equipment which they oﬀer is classiﬁed in Table 7.2. Choosing a placement system poses formidable problems. In terms of size of investment, it may well equal if not exceed the cost of the soldering equipment.

job:LAY07 page:11 colour:1

black–text

Component placement 259

Table 7.2 Functional capabilities of commercially available automatic SMD placement equipment (1996) Capability

Percentage of available equipment oﬀering the capability

Capable of in-line integration Placing 910 000 SMDs/hour Machine vision to assist placement Handling SMDs with :0.4 mm/16 mil pitch Handling TABs and BGAs

100% 80% 95% 75% 60%

There is no single machine which is simultaneously the fastest, the most ﬂexible, the most accurate and the cheapest. All attributes must be traded oﬀ against one another. However, most of today’s automatic placement machines are conceived as modules which can be added to one another into an integrated line, and this makes the choice easier: a newcomer to automatic placement can start with a unit of comparatively modest capability and cost, without pre-empting his later options for expansion.

7.4.2 Classes of placement machines Entry-level and mid-range machines A buyers’ guide, already mentioned above, lists 66 diﬀerent models of placement machines, catering for a wide range of requirements. At what is sometimes termed the ‘entry-level’ and the ‘mid-range’ of placement machines, up to 100 feeder stations are provided with a changeable mix of bulk-feeders, feeder tape, and stick-tray and waﬄe-tray magazines. With many machines, sets of feeder stations are mounted on individual, interchangeable trolleys which can be quickly detached from, or linked to, the machine to increase ﬂexibility and speed up the change-over from one type of board to another. The feeder stations on each trolley are assembled according to a computer-generated sequence to suit a given type of board. This enables the machine to switch from one type of board to another very quickly. The single placement heads collect, centre, rotate and put down single components in sequence. Most of these single-head machines have a maximum theoretical placement rate of 4000 components per hour. In practice, the necessary allowance for travel time and stop-and-start movements reduces the practically achievable rate of placement to about 2400 components per hour. This type of operation is suitable for placing melfs, chips and SO components with standard pitches from 1.25 mm/50 mil down to 0.65 mm/26 mil. For placing components with ﬁner pitch, machines are either equipped, or can be retroﬁtted, with opto-electronic placement aids. Facilities for in-ﬂight veriﬁcation of component identity and functional integrity can also be provided.

job:LAY07 page:12 colour:1

black–text

260 Component placement

With single-head placers, putting down drops of adhesive on boards destined for wavesoldering would require a second placement station. For this reason, it is economical to feed this type of machine with boards to which the adhesive has been pre-applied by one of the methods described in Section 4.8.3.

Fine-pitch placement machines Next in line are ﬁne-pitch placement machines, which can cope with placement accuracies up to 0.4 mm/15 mil and component sizes up to 55 mm/2 in square, which means maximum xy and rotational accuracies. Such machines are fully equipped with opto-electronic sighting, veriﬁcation of the coplanarity of component legs, and automatic adjustment of placement pressure so as not to smudge or squeeze out the paste printdown on the narrow footprints. With a single head, the maximum output is as above.

High-speed ‘chip-shooters’ The next step in sophistication are the high-speed ‘chip-shooters’. Diﬀerent equipment makers have chosen diﬀerent paths to this end. With one system, for example, the placement head takes the form of a rotating disc (revolver head) with twelve circumferential stations, each of which grips one component. With a two-head machine, one disc loads up while the second one puts down its load of components on the board. Instead of the second revolver disc, a single placement head for very large multilead components can be substituted. A further head for pre-placing metered amounts of adhesive can also be ﬁtted. The placement rate of such machines is quoted at 13 000 components per hour.

Very high speed placement machines Three machines listed in the already mentioned guide have capacities of between 20 000–30 000 components/hour, two can place up to 40 000/hour, and one (Philips) up to 60 000/hour. The latter operates with six XY heads, each of them populating separate areas of the same board. Most of the other high-speed placers use turret systems for handling the components. One machine is capable of placing components simultaneously on both sides of a board.

7.5 Reference 1. SMD Placement Machines – Buyers’ Guide; Electronic Production, July/August 1996, p. 22–24.

job:LAY08 page:1 colour:1

black–text

8 Cleaning after soldering

8.1 Basic considerations If cleaning must be considered, its problems can be reduced to three questions: 1. What has to be removed? 2. Why? 3. How? The ﬁrst question has a simple answer: principally the residue from soldering ﬂuxes, and sometimes from wavesoldering oils. This is why cleaning is often called ‘deﬂuxing’. Sometimes, contaminants from manufacturing steps which precede soldering can also be present in amounts which aﬀect the need for cleaning and the choice of cleaning strategy, as well as the result of subsequent tests for cleanliness. These contaminants are listed alongside the principal ﬂux residues in Table 8.2. The answer to the ‘why?’ is less simple. It clariﬁes the issue to some extent to rephrase the question like this: ‘How clean has your circuit board got to be, considering who wants to use it, where, and for how long?’ Even then, at the present state of knowledge, it is not always possible to give a reasoned and quantiﬁable answer to this question. Generally it is true that any contamination on a soldered assembly can reduce its reliability. Impaired reliability means that the aﬀected assembly is likely to malfunction, or to stop functioning altogether before its designed, expected or guaranteed lifespan. ‘Contamination’ in this context means the presence of any foreign substance – either too much of it, or in the wrong place. Flux residues are the most common example of such contamination. The problems they cause can be electrical and/or chemical ones; if they are visible, they may also aﬀect the marketability of the product. All these aspects will be fully dealt with in the next chapter. Two important points must now be made before we go any further. First, unless there is a compelling and unanswerable reason for cleaning a soldered board, do not clean it. Cleaning is expensive, and a badly cleaned board is worse than it was before cleaning: ineﬃcient cleaning is liable to spread ﬂux residue to places where there was none before. Second, if you ﬁnd yourself compelled to clean, given the

job:LAY08 page:2 colour:1

black–text

262 Cleaning after soldering

soldering technique you are using, consider whether you can change that technique so that you don’t have to clean. This could mean choosing circuit boards and components which can be soldered with no-clean ﬂuxes or pastes, or using soldering methods which allow you to use no-clean products, such as wavesoldering or reﬂowsoldering under nitrogen, or vapourphase reﬂowsoldering. As growing numbers of manufacturers are taking this approach, cleaning after soldering is being practised less and less in recent years. The halogenated solvents, principally the CFCs and CHCs, which were until very recently the principal and most convenient cleaning solvents for the electronic industry, have now been recognized as posing severe environmental threats, and they have been phased out almost world-wide (see Section 8.3.5). Therefore, the whole technology of cleaning has been forced into diﬀerent cleaning media and strategies. Some of them, like cleaning with water, are already well established; others are opening up new approaches. At the time when the original CFCs and CHCs were facing extinction, several similar, but environmentally less objectionable alternative solvents like CHC 111 were introduced to the market. They showed much reduced levels of ‘ozone depletion potential’ and ‘global warming potential’, while being eﬃcient cleaning media (see Table 8.5). In this context, a warning was recently sounded: when choosing a cleaning process or a cleaning medium, do not base your decision on present environmental regulations. They will inevitably accelerate and become more restrictive in the near future (Colin Lea, Nat. Phys. Lab. Conf. on Cleaning Processes, 3.12.96). If with your given market or customer situation, and your present soldering strategy, cleaning is or seems to be obligatory or unavoidable, examine carefully whether you cannot solder in such a way that cleaning is no longer necessary. Possible solutions might be the use of low-solids or no-clean ﬂuxes or solder pastes (Section 3.4.3) or soldering in an oxygen-free atmosphere (Sections 4.6 and 5.4.5). A word of caution is necessary at this point: having changed your ﬂux and/or your procedure so that your product looks and is clean to your own satisfaction, check with your existing customers and test your market to ﬁnd out whether the product still meets their expectation of reliability and life expectancy before sending it out into the world. Once the need for cleaning has been recognized as deﬁnitely unavoidable, the ‘how?’, that is the strategy of cleaning, depends entirely on the choice of ﬂux. Here, a ﬂux with a fully watersoluble residue is well worth considering: with full watersolubility, there is no need to replace a soon inadmissible halogenated hydrocarbon with an alternative organic solvent, with potential problems of ﬂammability, regeneration or disposal, or a saponiﬁed waterwash. A plain waterwash and some semi-aqueous systems have far fewer environmental problems, and zero-eﬄuent cleaning systems are already available. Sections 8.3, 8.4 and 8.5 deal with these various cleaning options. Another important point: if you have to clean your boards after soldering, because your customer or your market deﬁnitely demand it, there is then no reason for chosing a ‘no-clean’ ﬂux. In fact it might be better not to use one. Some no-clean ﬂuxes leave a very thin, dry layer of residue which can be more diﬃcult to remove than residue left by more active ﬂuxes with higher solids content. There-

job:LAY08 page:3 colour:1

black–text

Cleaning after soldering 263

fore, before deciding on your manufacturing strategy, make sure that the residue left by the ﬂux you intend to use is fully removable by the cleaning process you have chosen. Most ﬂux vendors will be able to help you in your choice. It is worth noting here that soldering under nitrogen, whether by wave or reﬂow, retains its advantages irrespective of whether a no-clean or an ordinary ﬂux is used.

8.1.1 Reasons for cleaning Cleaning can become necessary for one or several of the following reasons:

Electrical problems Flux residues left on a soldered assembly can cause leakage currents, ionic migration between neighbouring conductors (formation of dendrites), or insulating deposits on contact surfaces such as pin-connectors, relays, or trimmer-tracks, but above all on the contact pads for testbed pins. Here, the insulating eﬀect of the ﬂux residue falsiﬁes the test results. If it is sticky it contaminates the contact points of the test needles, which then need expensive and time-consuming maintenance. This problem was the initial driving force behind the development of modern low-solids ﬂuxes. Though needle-adaptor testing may begin to reach its limits with the growing complexity and population density of modern circuitry, and other testing strategies are beginning to take its place, as long as needle testing is being practised any ﬂux residue on test pads must be such as not to interfere with it. Impaired surface insulation resistance is a serious defect with boards carrying ICs with closely spaced leads and impedances of 10 to 10 ohm. Leakage currents of 10\ amp may be suﬃcient to cause malfunctioning of binary gates.

Chemical problems Corrosion In hostile operating environments, ﬂux residues can cause corrosion or promote fungus growth. Electronic assemblies which have to operate in humid tropical climates are especially at risk from the latter (Figure 8.1). Polar, watersoluble components of residual ﬂux (e.g. activator residues, or indeed residues from any watersoluble ﬂux) can, in the presence of moisture, cause electrolytic corrosion between adjacent surfaces of dissimilar metals. For example, moist ionic ﬂux residue sitting on the dividing line between solder and the silver metallization on a chip can form an electrolytic cell with a potential of 2.5 V (see Figure 8.2).

Formation of dendrites All organic ﬁlms, including protective lacquers and conformal coatings, are permeable to water vapour. Residual activator, trapped under a coating of lacquer

job:LAY08 page:4 colour:1

black–text

264 Cleaning after soldering

Figure 8.1 Map of world climates. After Britten, R. and Matthews, G. W. (1988) Plessey Assessment Services; Electronic Production

job:LAY08 page:5 colour:1

black–text

Cleaning after soldering 265

Figure 8.2 Electrolytic corrosion

Figure 8.3 Formation of dendrites

between two adjacent metallic conductors with an electric potential between them, causes not only leakage currents, but can initiate the growth of dendrites between the conductors, which may lead to short circuits (see Figure 8.3). Under the conditions described above, the formation of dendrites is most frequently observed between surfaces of Ag, but it can also occur between Pb/Sn, Cu, AuPd and AuPt. Their rate of growth can be up to 0.1 mm/min.

Problems arising with follow-on processes Flux residue can be responsible for bad adhesion of conformal coatings, lacquers or potting compounds. The vendors of several low-solids or ‘no-clean’ ﬂuxes claim that the residues from their ﬂuxes do not cause such problems.

Reasons related to the nature of the product Some classes of electronic product require the highest possible degree of reliability, and hence cleanliness, which can only be achieved by a cleaning procedure after soldering, irrespective of the ﬂux or soldering method used. These classes include professional electronic equipment which falls under categories I, II and sometimes

job:LAY08 page:6 colour:1

black–text

266 Cleaning after soldering

III, set out in Chapter 9. Professional electronic equipment in categories IV to VI requires cleaning only in certain circumstances, e.g. for service in damp tropical climates or hostile environments. Products of the class ‘Consumer Electronics’ in category VII rarely need cleaning.

Reasons related to marketing considerations A number of non-technical considerations fall under this heading, such as: E the customer wants (and pays for) cleaning E the competitors clean E cleaning improves the appearance of the product and makes it more saleable in a competitive market.

8.1.2 Designing for cleanability Once cleaning has been accepted as unavoidable, designing the board and specifying the components in such a manner that successful cleaning does not become unnecessarily diﬃcult, expensive or even damaging becomes an important consideration. To be readily cleanable, high-proﬁle components should be spaced as far apart from one another as economic and functional considerations will allow. Braided wire should not be used for jumper connections, because ﬂux and cleaning solvents are likely to get trapped in them. Plastic sleeving on such wires must be tested for its compatibility with the cleaning process to be used. Shrinkable sleeves should not be used on boards which must be cleaned.

Components should be tested for their compatibility with the cleaning method chosen. Military Standard MIL-STD-202 demands the testing of component markings for their resistance to the cleaning solvent which is going to be used. British Standard BS 9003 provides also for the testing of component bodies, sealing materials, varnishes and encapsulating compounds. It has been proposed that components ought to be marked with a cleanability code in the same manner in which garments carry a code of appropriate cleaning and washing procedures. Detailed cleanability testing schedules for complete electronic assemblies are outlined by Lea.

The clearance between the underside of a soldered SMD and the surface of the board (its ‘stand-oﬀ height’) has a critical inﬂuence on the ease with which ﬂux residue trapped in this gap can be removed. The eﬀectiveness of removing such residues increases with the fourth power of the stand-oﬀ height. The problem of removing ﬂux residues from underneath multilead components has become acute with BGAs (Section 8.2.2), if such cleaning is required, which is not often the case. If it must be done, even high-pressure solvent jets are not always enough. A process of vapourphase assisted jet-cleaning has been developed to deal with this problem (see Section 8.3.3).

job:LAY08 page:7 colour:1

black–text

Cleaning after soldering 267

8.1.3 What must be removed? Flux types and their residues The nature of a ﬂux residue and its response to cleaning depend obviously and principally on the type of ﬂux used. The various ﬂuxes which are available to the industry are all subject to national and international standard speciﬁcations. As far as ﬂux composition is concerned, a standard speciﬁcation does not say what a given ﬂux actually contains, it only states what kind of substance might be found in it. On the other hand, it states precisely what a given ﬂux or class of ﬂuxes must not contain. Generally speaking, standard speciﬁcations classify ﬂuxes into various groups, though these groups do not fully overlap between diﬀerent countries. What matters in the present context is whether a ﬂux residue is watersoluble or not. Residues from ﬂuxes containing rosin or a synthetic resin are not watersoluble, but require an organic solvent, or water with an added saponiﬁer. Rosin-free ﬂuxes generally leave a watersoluble residue. If for technical or marketing reasons ‘deﬂuxing’ becomes mandatory, the noncorrosive nature of the residue from rosin-based ﬂuxes, which is their principal virtue, becomes irrelevant. Instead, they turn into a liability: their removal involves the use of solvents with all their problems, or the addition of saponiﬁers to the washing water. In the context of cleaning, rosin-free ﬂuxes are nowadays gathered under the collective description of ‘watersoluble ﬂuxes’. Solder pastes which are based on such ﬂuxes are also called ‘watersoluble’. This classiﬁcation relates to the residues they leave behind. With watersoluble ﬂuxes, cleaning after soldering used to be advisable, even if the soldered product as such did not demand cleaning, and if corrosion tests as speciﬁed in some ﬂux standards did not disclose any corrosive action.

In recent years, low-solids ﬂuxes and ‘no-clean’ ﬂuxes, where the vendor speciﬁcally guarantees that cleaning is not required, have become available. They leave a very thin layer of a dry, sometimes powdery residue (see Section 3.4.3) which is of obvious advantage when an assembly is subsequently tested on a pin adaptor or ‘bed of nails’. With ‘no-clean’ ﬂuxes, especially when they are used on assemblies of a critical nature, the buyer may be well advised to verify that the vendor’s claims apply to his speciﬁc product and its market. It must be remembered that the action of all ﬂuxes is based on their ability to react with metal oxides and that therefore all ﬂux residues contain traces of metallic compounds. For that reason, ﬂux residues ought to be removed whenever the service requirements of the ﬁnished assembly are at all critical (which applies for example to the Product Classes I, II and III as set out at the beginning of Chapter 9). The ﬂux residue from rosin-based soldercreams contains not only rosin, but also the remnants of various additives which such creams contain, such as stabilizers, thickening agents, etc., which control their ﬂow-properties during and after printing or dispensing. These substances are normally no more corrosive than the rosin itself, but they must be considered in the cleaning process.

job:LAY08 page:8 colour:1

black–text

268 Cleaning after soldering

The effect of the soldering method and its parameters Wavesoldering With wavesoldering, the whole underside of the circuit board is covered with ﬂux, not all of which is washed oﬀ when the board passes through the wave. On the other hand, with wavesoldering, SMDs have to be glued to the underside of the circuit board, and the adhesive takes up a considerable part of the gap between the component and the board. This can mean that there is less ﬂux residue to be removed from under wavesoldered SMDs, and such residue as is present is near the edge of the component and therefore more accessible (Figure 8.4). On the other hand, if cracks have opened in the adhesive joint during the preheat or the passage through the solderwave, they may harbour some ﬂux residue which can leak out during later service, even if the MIL test for cleanliness has given the board a clean bill of health. Exposure to heat causes rosin to polymerize and to become less soluble. Therefore, overheating the board in the pre-drying stage before it passes through the solderwave, and above all undue delay between soldering and cleaning, will make the cleaning process more diﬃcult. Reﬂowsoldering With all reﬂowsoldering methods, soldercream or ﬂux is applied only to the solderpads. Thus, the ﬂux-residue is conﬁned to the neighbourhood of the footprints, and consequently near to the outer edge of the components. It is therefore more accessible and easier to remove. Needle-adaptor testing is no problem with reﬂowsoldered boards, since testpads are, or ought to be, free from ﬂux residue.

Figure 8.4 Effect of the adhesive joint on the accessibility of the ﬂux residue

job:LAY08 page:9 colour:1

black–text

Cleaning after soldering 269

Vapourphase soldering and reﬂow soldering in a nitrogen atmosphere are claimed to leave rosin ﬂux residues in a more soluble condition, because they do not oxidize during soldering and should therefore be easier to remove. Recently, several solder pastes have become available which are claimed to leave no residue at all. One of them, containing a ﬂux based on a synthetic resin, requires infrared reﬂowing in a special reactive atmosphere. Another low-residue paste demands reﬂowing in a low-oxygen atmosphere such as nitrogen, or in a vapourphase system.

Other residues Wavesoldering methods where oil is injected into the wave (Hollis) or applied to the wave surface (Kirsten, Soltec Smartwave) can leave a certain amount of oil residue on the board. After prolonged use, such oils can polymerize and become less soluble, so that routine cleaning does not remove them fully. For this reason, it is important with such machines to follow the manufacturer’s operating instructions very carefully. In any case, wavesoldering in the presence of oil places an additional load on any subsequent cleaning process, and this factor has to be considered in the choice and the operation of a cleaning installation. Apart from ﬂux residues and perhaps soldering oil, a well conducted assembly process should not leave any other substances on the soldered boards. It has been pointed out, though, that markings made with certain felt-tipped pens during inspection may be diﬃcult to remove by normal cleaning methods, the marking ink having been speciﬁcally formulated to resist removal. Lea recommends the use of peelable stickers instead of marking with a pen.

Chemicals or surface contamination arising from preceding manufacturing processes of the board, or from handling the boards during assembly, can seriously aﬀect the performance of a board, its cleanliness as determined by the MIL test, or its surface insulation resistance after it has been soldered. It can therefore become advisable to write cleanliness requirements into purchasing contracts, or to subject incoming boards and sometimes components to cleanliness tests before assembling and soldering them.

8.2 The theory of cleaning 8.2.1 The physics of cleaning The removal of a ﬂux residue consists of two separate tasks: 1. The deposit of solidiﬁed ﬂux residue must be dissolved or at least made mobile in the cleaning medium or solvent. 2. The resultant solution or suspension of ﬂux residue must be ﬂushed away and replaced by fresh, clean solvent which soaks up or dislodges more ﬂux and which must be ﬂushed away in turn. Thus, every solvent-cleaning process is in principle a progressive dilution, and absolute cleanliness can only be approached asymptotically. Therefore, a rational

job:LAY08 page:10 colour:1

black–text

270 Cleaning after soldering

and economic cleaning process demands a sensible deﬁnition of the required degree of cleanliness, and often a precise measurement of the degree of cleanliness which has been achieved. SMD technology, with its complex geometry of densely populated boards, with joints hidden in narrow gaps between neighbouring components and with ﬂux residue trapped between SMDs and circuit board, has made cleaning more diﬃcult. It makes more stringent demands on the eﬃciency of cleaning equipment and solvents than did boards with simple, inserted components.

The ‘stand-off’ height The distance between the underside of an SMD and the board surface – the ‘stand-oﬀ height or gap’ – is a critical parameter as far as cleaning is concerned. With stand-oﬀ heights below 75 m/3 mil, cleaning with a liquid medium becomes practically impossible. This poses a problem with many modern multilead components, which sit close to the board, and still awaits a practicable solution. With greater stand-oﬀ heights, procedures which are supported by an input of hydrodynamic energy, such as ultrasonic vibrations or high-pressure jets, are generally successful. For simple bath-type cleaning systems, a stand-oﬀ height of at least 500 m/20 mil has been postulated.

With wavesoldered boards, the stand-oﬀ height is less critical than with reﬂowsoldered boards, because the adhesive which secures the SMDs to the board during wavesoldering occupies between ﬁfty and seventy-ﬁve per cent of the gap-volume. This means that the ﬂux residue is located mainly near the outer edge of wavesoldered components (see Figure 8.4). However, should the adhesive joint crack during or after hardening because of faulty formulation or processing, matters get worse instead of better: ﬂux residue is bound to enter the cracks, from where they may exude later and reach the soldered joints. The stand-oﬀ height itself is governed by a number of factors, including the structure of the board surface and the shape of the component legs (Figure 8.5). The dimensions given in Figure 8.5 must be understood as averages, and they can vary from one supplier to another. Further factors are the thicknesses of the copper laminate and of the solder resist on the circuit board (Figures 8.6 and 8.7).

Figure 8.5 Stand-off heights of various SMDs. (a) Chip resistors and ceramic condensers 25 m/1 mil; TA condensers 100 m/4 mil; (b) SOTs 125 m/5 mil; SOICs, QFPs 250 m/10 mil; (c) PLCCs 250 m/10 mil; (d) LCCCs and BGAs 25 m1 mil

job:LAY08 page:11 colour:1

black–text

Cleaning after soldering 271

Figure 8.6 Height of various surface features on a circuit board. Footprints and tracks 35–135 m/1.5–5.5 mil; soldermask lacquer 10–20 m/0.4–0.8 mil; soldermask dry-ﬁlm 50–100 m/2–4 mil

Figure 8.7 Effective stand-off height = SMD-speciﬁc stand-off −thickness of soldermask

As Figures 8.6 and 8.7 show, the thickness of the solderpads on which the components sit raises the stand-oﬀ height, while solder resist and conductor tracks, which run underneath a component, reduce it. Before deciding on the cleaning strategy for a given board, it is sometimes advisable to check the actual stand-oﬀ height of critical components with a feeler gauge. Obviously, components with a high proﬁle and dense packing make cleaning more diﬃcult. A further factor is the ‘picket-fence’ eﬀect of the legs of components like PLCCs or QFPs, which obstruct the ﬂow of the cleaning medium into the gap between component and circuit board.

The hydrodynamics of cleaning Clearly, ﬂux residue can only be removed from a crevice or from under a component if the cleaning medium penetrates into the gap ﬁrst. This penetration depends on the wetting behaviour of the medium towards the surfaces involved, which include the board laminate, the solder resist, the underside of the component and the solder. It also depends on its viscosity (Figure 8.8; Table 8.1). Compared with organic solvents, water penetrates faster into a given gap. Unfortunately, the same capillary force which pulls the medium quickly into a gap holds it there ﬁrmly once it has entered. Eﬀective cleaning demands that the solvent, having dissolved or loosened the contaminant, is expelled from the gap by a pressure

job:LAY08 page:12 colour:1

black–text

272 Cleaning after soldering

Table 8.1 Penetrating speeds of diﬀerent solvents

Solvent

Temperature

Penetrating speed cm/sec in/sec

CFC/alcohol azeotrope CHC/alcohol azeotrope Water

40 °C/104 °F 73 °C/163 °F 70 °C/158 °F

2 830 4 056 11 380

1130 1620 4550

Figure 8.8 The hydrodynamics of cleaning

diﬀerential between its opposing ends and replaced by fresh solvent. At a given pressure diﬀerential, the force which acts on a body lodged in a gap is proportional to: E the density of the cleaning medium and the square of its speed E the fourth power of the stand-oﬀ height and is inversely proportional to: E the square of the viscosity of the cleaning medium.

These relationships underline the decisive eﬀect of the stand-oﬀ height: with a stand-oﬀ height of 75 m/3 mil, the washing power of a ﬂuid medium is 81 times higher than with a stand-oﬀ of 25 m/1 mil, all other circumstances being the same.

Practical measures to improve the kinetics of washing Ultrasonics Ultrasonic energy introduced into a liquid creates a pattern of closely spaced wavefronts of high and low pressure which travel across its volume. If the pressure in the low-pressure regions drops below the vapour pressure of the liquid, small bubbles of near-vacuum form there. They collapse immediately with the arrival of the next high-pressure front. Where the wavefronts impinge upon a solid surface the collapsing bubbles act like innumerable small hammerblows against that surface (cavitation), loosening adherent contamination and thus assisting cleaning.

job:LAY08 page:13 colour:1

black–text

Cleaning after soldering 273

If the liquid is boiling, or near-boiling, the mechanism is a diﬀerent one. Because the vacuum would immediately ﬁll with vapour, no bubbles can form. Instead, the ultrasonic pressure waves exert a strong pumping action on gaps and crevices by creating local pressure diﬀerentials between opposite ends of a gap. The ultrasonic pressure applied to the circuit boards immersed in a cleaning bath is normally held at 2–4 bar, with the total power introduced into a cleaning bath amounting normally to about 10 watt per litre/38 watt per US gallon. With ultrasonically assisted cleaning, circuit boards must not be packed too tightly in ﬁxtures or cleaning baskets, and they should be oriented in such a way that the ultrasonic energy has unimpeded access to all surfaces where it is needed. The ultrasonic frequencies are normally in the range 35–40 kHz. There has been much argument in the past about the danger of damaging wirebonds or circuitry inside ICs by setting up a resonance between the bonding wires and the ultrasonic oscillations or their harmonics, thereby causing fatigue damage. Practical experience has shown that there is very little danger of this happening provided the frequency is kept within the above proven range. Safe ultrasonic cleaning regimes, in terms of ultrasonic power density and exposure times, have recently been established. On the other hand, cracks in outside gullwing legs, which are made from Fe-containing copper alloy, have sometimes been blamed on fatigue damage caused by vibrations induced during ultrasonic cleaning. However, no clear conclusions can be drawn so far, and research is continuing. High-pressure jets Ultrasonic cleaning requires full immersion in a solvent bath and it is therefore more suited for batch processes. With jet-cleaning, which is mostly used in conveyorized in-line installations, the soldered assemblies pass between arrays of high-pressure jets. The boards travel on a horizontal open-mesh conveyor, and the jets impinge on them from above and below, at a carefully balanced intensity so as not to make them ﬂip over. When working with a hot organic solvent, the jets have diameters in the range of 1–2 mm (0.04–0.08 in). Their operating pressure is governed by the lowest standoﬀ height of the various SMDs which populate a given board. Experiments with a CFC solvent have shown that with stand-oﬀs below 25 m (1 mil), jet pressures of 15–17 bar are required. With stand-oﬀs above that ﬁgure, jet pressures of 2–5 bar suﬃce to give a cleanliness to MIL standard within 10 seconds. With the new water cleaning systems, the hydrodynamics of the water jets have received a great deal of attention. These matters are discussed in Section 8.4.4.

The glass plate test for checking cleaning efficiency Two thin glass plates (e.g. microscope slides), separated from one another by metal shims and pressed together by clamps at both ends (e.g. ‘Bulldog’ paperclips) form a convenient and readily evaluated model of the stand-oﬀ gap underneath an SMD (Figure 8.9). The thickness of the shims is chosen to represent the minimum stand-oﬀ of the board’s population of SMDs.

job:LAY08 page:14 colour:1

black–text

274 Cleaning after soldering

Figure 8.9 The glass plate model for testing cleaning efﬁciency

For the test, a small amount of the same ﬂux or soldercream which is used on the boards to be cleaned is placed in the centre of the gap between the two glass plates. The model is then put through the same temperature cycle which the assembly will have to undergo before it reaches the cleaning stage. Afterwards, the model is put through the cleaning procedure which is to be assessed. The depth to which the ﬂux residue has been ﬂushed from the gap between the glass slides is readily visible and provides a measure of the eﬃciency of the cleaning treatment. The addition of a small amount of ﬂuorescent dye to the ﬂux or cream, and subsequent examination under UV light, makes the result even easier to observe. This method is very useful for evaluation tests when comparing diﬀerent cleaning solvents or diﬀerent cleaning procedures. It is also useful for comparing the response of diﬀerent ﬂuxes or soldercreams to a given cleaning procedure, in situations where a change of product or supplier is contemplated. However, for a safe prediction of cleaning results in an existing situation it must be regarded with some caution: the dimensions of the glassplates diﬀer too much from the actual components, and in addition the gap has a simple geometry and is not obstructed by a picket fence of component leads or by neighbouring components. A concluding thought for this section: in practice, the problem of removing ﬂux residue from under large, ﬂat components is not as daunting as it seems: for one thing, such components with their closely spaced leads are normally not wavesoldered, but are reﬂowsoldered by one of the various methods. This means that except with BGAs, the ﬂux residue is located near the perimeter of the component, close to the ‘picket fence’ which is formed by the component leads, so that it need not be fetched from far inside the stand-oﬀ gap. On the other hand, the capillary action of a low stand-oﬀ gap, which pulls the ﬂux from a solder paste underneath the component body, must not be forgotten.

8.2.2 The chemistry of cleaning The choice of the most suitable cleaning medium for a given cleaning task depends on the chemical nature of the substance which must be removed. Polar solvents are best for polar contaminants. Non-polar contaminants can be removed with nonpolar solvents, though there are polar solvents, for instance alcohols, which can remove most ﬂux residues and contaminants encountered in practice. Tables 8.2 and 8.3 list and classify the commonly encountered contaminants and cleaning

job:LAY08 page:15 colour:1

black–text

Cleaning after soldering 275

Table 8.2 The chemical nature of various contaminants Soldering residues Natural rosin Synthetic resin Flux activators Cover-oil for wavesoldering Regular Watersoluble Solder paste additives (stabilizers and ﬁllers) Hot-air levelling ﬂux Pre-soldering residues Plating and etching residues Swarf from drilling, sawing or scoring Fingerprints Protective handcream

non-polar when solid; slightly polar when molten or in solution non-polar polar non-polar polar slightly polar polar polar non-polar solids polar/non-polar mixture polar/non-polar mixture

Table 8.3 The chemical nature of some cleaning media Water Saponiﬁer Wetting agents Chloro-ﬂuoro-carbons (CFCs) Chloro-hydrocarbons (CHCs) Alcohols CFC- and CHC-azeotropes (see Section 8.3.1) Modiﬁed alcohols, esters Terpenes, ketones and hydrocarbon mixtures

polar polar polar non-polar non-polar polar polar polar non-polar

media. Most polar cleaning media are watersoluble or watermiscible, while nonpolar ones are not. This diﬀerence is important with semi-aquaeous cleaning (Section 8.5.5). It follows that residues from activated rosin-based or rosin-containing ﬂuxes can be removed with the (now doomed) CFC- or CHC-azeotropes (Section 8.3.1) and with their environmentally acceptable polar alternatives, such as plain and modiﬁed alcohols and esters (Section 8.3.7). Water with added saponiﬁers (Section 8.4) is another viable alternative. The cleaning eﬀect of a water/saponiﬁer mixture on these residues is based not on their solubility in these media, but on a chemical reaction which turns them into water-soluble soaps. Terpenes and ketones are excellent solvents for rosin, resin and oils, but not for the polar activators. Cleaning systems based on them need an added waterwash if residues from rosin-based or resin-based ﬂuxes have to be removed (semi-aqueous systems).

job:LAY08 page:16 colour:1

black–text

276 Cleaning after soldering

Residues from rosin-free ﬂuxes are soluble in plain water, as are the residues from watersoluble wavesoldering cover oils. Because all cover oils oxidize or polymerize after prolonged use, and so their residues become less soluble, suppliers’ instructions as to their conditions of use should be strictly followed. Temperature has a decisive inﬂuence on every cleaning process: as has been mentioned when ﬂuxes were discussed (Section 3.4), a temperature rise of 10 °C/18 °F roughly doubles the speed of a chemical reaction. The same is true for the speed with which a contaminant dissolves in a given solvent. For this reason, almost all cleaning methods operate with warm solvents. It must be remembered, however, that for reasons explained above ultrasonic energy loses its principal cleaning mechanism if it acts in a boiling or near-boiling solvent.

Time-interval between soldering and cleaning Cleaning should follow as soon as possible after soldering. The longer the time gap between the two, the greater is the eﬀort needed to remove the ﬂux residue. Resinous deposits, like any varnish, oxidize in air and become less soluble. Watersoluble residues can become dry and hard, and their solubility decreases. Experiments have shown that immediately after wavesoldering, rosin-residues could be removed completely by spraying with a CFC for 20 seconds. Thirty minutes later, even spraying for 50 seconds removed only 75% of the residues. For this reason, with in-line soldering installations, soldering and cleaning machines are placed as close together as possible. However, two provisos must be made: 1. If a board is immersed in a cleaning medium while it is still hot, the medium may be sucked into the interior of the components as they cool, thus damaging them. 2. Care must be taken that vapours from any solvent-cleaning equipment which is still operated with CHCs or CFCs cannot drift back into the hot zones of wavesoldering machines or IR heating ovens. Vapours of these solvents can generate highly toxic decomposition products at elevated temperatures, particularly in the presence of hot solder-dross (see Section 8.3.5).

8.3 The practice of cleaning The cleaning of a soldered electronic assembly involves, almost without exception, a chemical and physical interaction between a liquid medium – the solvent – and the ﬂux residue left on that assembly. In general practice, these liquid cleaning media are either organic solvents or water, with suitable additives if necessary. Mechanical cleaning with dry rotary brushes is only used for removing solderballs (Section 4.4.5). Cleaning in a plasma atmosphere has been proposed and is being investigated; at the time of writing (1997) a pilot plant, based on a combination between plasma treatment and water vapour absorption, is in operation. Wavesoldering machines incorporating a plasma pretreatment stage are commercially available.

job:LAY08 page:17 colour:1

black–text

Cleaning after soldering 277

Cleaning after soldering or ‘deﬂuxing’, in spite of the growing use of no-clean ﬂuxes, is still an important aspect of soldering technology. Early in 1997, a buyers’ guide to deﬂuxing media indicated the strong position of cleaning techniques involving water, but the presence of 11 solvent-cleaners amongst 35 listed products indicates that cleaning with organic solvents is far from extinct.

8.3.1 Organic solvents Ever since rosin-based ﬂuxes were introduced for wavesoldering in the ﬁfties, organic solvents have been used for removing their residues whenever that was necessary. The lower alcohols are excellent organic solvents for both rosin and its usual activators. Isopropyl alcohol (isopropanol) is in fact the standard solvent base in ﬂuxes containing rosin or synthetic rosin substitutes. The ﬂammability of these alcohols has in the past been to some extent a deterrent against their industrial use for cleaning soldered assemblies, but recent developments have helped to overcome this resistance against them (Section 8.3.7). It must also be remembered that large quantities of alcoholic ﬂux solutions are in daily use worldwide in soldering machines, in close proximity to the electric preheaters and to molten metal. Such mishaps as do occasionally occur are mainly due to some operational misjudgement. In contrast to the alcohols, halogenated hydrocarbons are only slightly ﬂammable or non-ﬂammable. They are therefore widely used as industrial solvents for organic substances such as rosins, oils, paints or rubbers. Halogenated hydrocarbon solvents are for the most part simple hydrocarbons such as ethane, or propane, with some or all of their hydrogen atoms replaced by a halogen, mostly chlorine and/or ﬂuorine. A CHC contains chlorine and hydrogen apart from carbon; CFCs contain only chlorine, ﬂuorine and carbon, but no hydrogen. Chlorinated hydrocarbons have been in use for a long time, while ﬂuorinated ones are relative newcomers. The attraction of the low or non-existent ﬂammability is outweighed by their pronounced health risk, especially of the chlorinated hydrocarbons. Most of them are either poisonous or narcotics, or both. A further problem is their ability to penetrate concrete, which can lead to groundwater contamination from leaks or spills.

The rise and fall of the CFCs About twenty years ago, the non-polar hydrogen-free chloro-ﬂuoro-carbons(CFCs) and in particular CFC 113* (C F Cl ), trichloro-triﬂuoro-ethane, which is known as Freon or Arklone, became industrially available. by a number of tradenames such CFC 113 in particular quickly became very popular for deﬂuxing, for a number of *This shorthand classiﬁcation was originated by the DuPont Chemical Company in the thirties for proprietary reasons, and it is now used worldwide. If the substance contains chlorine, the ﬁrst capital letter is C. The second is F, if ﬂuorine is present; the third is H, if any hydrogen is left in the molecule. The last C stands for carbon. Of the numerals, the ﬁrst is the number of carbon atoms minus one, the second the number of hydrogen atoms plus one, the last the number of ﬂuorine atoms.

job:LAY08 page:18 colour:1

black–text

278 Cleaning after soldering

reasons. It is non-ﬂammable, chemically very stable and not toxic, nor does it smell. It has a conveniently low boiling point, and the ﬂux-loaded solvent can easily be recovered on site by distillation, and recirculated. It does not attack the circuit board, the solder resist, the printing on the board nor the components. Its relatively high density improves the dynamics of ultrasonic or pressure-jet assisted cleaning. Above all, it is, or was, freely available at a reasonable cost. By itself, CFC 113 is not an especially good solvent for rosin, but adding a small amount of ethyl alcohol or methyl alcohol makes it into an eﬃcient cleaning solvent for removing the residue from activated rosin ﬂuxes. Its worldwide consumption in 1989 was estimated at 200 000 tonnes, ﬁfty per cent of which was used for deﬂuxing soldered electronic assemblies. Unfortunately, the chemical stability of CFC 113 and its relations turned out to be their undoing. They sooner or later evaporate, and their vapour eventually reaches the upper layers of the atmosphere. There it contributes to the global warming of our planet, and causes the depletion of the ozone layer, both of them eﬀects of the utmost environmental menace (Section 8.3.5). For that reason, the use of CFCs and related solvents, not only for cleaning but for refrigeration and as propellants in aerosol packages, has come under severe attack. Their use has now been largely phased out in most industrialized countries (Section 8.3.6). Nevertheless, the CFCs and their less virulent, but still in the long run unacceptable, cousins have to be considered here, together with the various types of cleaning equipment in which they are used and the operating precautions which must be observed with them. The reason for their inclusion in this book is their continued, if restricted use in some developing countries, the large investment which existing solvent cleaning installations represent, and the possibility of their continuing use with one of the more innocuous ‘drop-in’ replacement solvents, which are beginning to be oﬀered to industry (see Table 8.12). In the countries where CFCs are still being used, industry will have to live with them and use them for the time being, while taking every possible precaution to prevent or at least minimize the escape of these solvents into the environment by observing certain rules and practices of handling CFCs, which are outlined later. Table 8.4 lists some important properties of the two main halogenated hydrocarbons which were important cleaning solvents in the electronics industry, together with the properties of ethyl alcohol and isopropyl alcohol, which are both ﬂammable but are very good solvents for ﬂux residues. Water is added to the list for comparison, since it forms the basis for a growing range of cleaning processes. There are many other halogenated hydrocarbon solvents, some of them with very interesting properties and excellent solvent power, but most of them are disqualiﬁed from industrial use in the electronics industry. Examples of these are methylene chloride, which attacks many polymers and marking inks, and trichlorethylene, which poses severe health risks.

Flammability Flammability of a given substance implies that a ﬁre risk is involved in using or storing it. Once a substance catches ﬁre, it is not the solid or the liquid itself which

job:LAY08 page:19 colour:1

black–text

Cleaning after soldering 279

Table 8.4 Some solvents and their main properties Solvent

Density

Boiling point

Flash point*

MAC ppm**

Polarity

113–Trichloro-Triﬂuoro-Ethane (CFC 113, ‘Freon‘, ‘Arklone’) 111–Trichloro-Ethane (CHC 111, Methyl-Chloroform, ‘Genklene’, ‘Inhibisol’)

1.56

47.6 °C 117.7 °F 74.1 °C

n.a.

1000

non-polar

n.a.

350

non-polar

Water

1.0

100 °C 212 °F

n.a.

Methyl alcohol (methanol)

0.791

Ethyl alcohol (ethanol)

0.789

Isopropyl alcohol (isopropanol)

0.786

65.1 °C 149.2 °F 78.5 °C 173.3 °F 82.4 °C 180.3 °F

12 °C 54 °F 14 °C 57 °F 13 °C 55 °F

1.46 165.4 °F

n.a.

polar

200

polar

1000

polar

400

polar

*Tag closed cup ﬂashpoint **MAC = Maximum allowable concentration (see Section 8.3.4)

burns but its vapour. Combustion needs oxygen to start and to proceed. Hence there are so-called ﬂammability limits for any vapour: with too much vapour in a given space there is not enough oxygen to start and sustain combustion; with too little vapour there is not enough of it to start and maintain combustion. The ‘ﬂashpoint’ of a substance gives a measure of the ﬁre risk involved in using it. It is the lowest temperature at which the combustible liquid (or solid) gives oﬀ enough vapour to enable an air–vapour mixture within the combustibility limits to ignite on the application of a ﬂame. The ‘Tag Closed Cup’ test is designed to determine that temperature. A sample of the substance is placed in a closed container with an aperture in its lid. The temperature is raised slowly until a small ﬂame which is applied to the aperture at regular intervals manages to ignite the vapour which issues from that aperture. Liquids with a ﬂashpoint below 37.8 °C/200 °F are commonly classed as ‘ﬂammable’; with a ﬂashpoint above that limit they are classed as ‘combustible’. Flammable liquids are known as class I liquids, combustible ones fall into classes such as II, IIIA and IIIB. Regulations concerning handling and working with ﬂammable or combustible liquids vary from country to country. In the US they fall within the competence of the US National Fire Protection Association. If a ﬂammable or combustible liquid is present in the form of a spray or mist, i.e. an aerosol, there is the risk of an explosion, that is of a very rapidly spreading combustion, if that aerosol is ignited locally, even if its bulk is below the ﬂashpoint of the liquid involved. The temperature of each individual droplet can rise very rapidly to above the ﬂashpoint, and the ﬂame, once started, travels quickly through the aerosol. The working of the internal combustion engine, aptly called ‘explosions-motor’ in the German language, is based on this phenomenon.

job:LAY08 page:20 colour:1

black–text

280 Cleaning after soldering

In the context of solvent cleaning, jets or sprays of non-ﬂammable but combustible liquids with ﬂashpoints above 37.8 °C/200 °F, such as terpenes, pose an explosion risk. Equipment using such liquids in the form of jets or sprays must be made explosion-proof, or the jet-cleaning section of the machine must be ﬁlled with nitrogen (see Section 8.5).

Solvent power CFC 113 and CHC 111, both of them non-polar, are useful solvents for rosin and synthetic resin, but not for the polar additives which all activated rosin ﬂuxes contain. However, unless these activators are removed together with the rosin, they or a portion of them will remain on the cleaned circuit board, usually in the form of a whitish deposit. This not only makes the board look unattractive and sometimes unsaleable, but the polar activators, now no longer safely encapsulated in the neutral rosin, can cause corrosion and leakage currents in the presence of moisture. Thus, a board cleaned in an unsuitable CFC or CHC is worse oﬀ than it was before cleaning. Alcohols, being polar, are excellent solvents for all activators (see Section 8.2.1) and one or another of the alcohols given in the list is therefore added to the above non-polar solvents to enable them to remove all of the ﬂux residue. The ratio in which the alcohol is added to the non-polar solvent must be such that during boiling the composition of the mixture does not change, and this means that the vapour must have the same composition as the boiling liquid. For a given solvent and a given alcohol there is just one such ratio, and mixtures of this type are called ‘azeotropes’. In all solvent-cleaning processes which involve heating or boiling, only azeotropes should be used. Otherwise, the composition of the solvent would have to be constantly monitored and corrected. Table 8.5 lists some commonly used azeotropes together with their solvent power for rosin.

The kauri–butanol value The kauri–butanol (K ) value given in Table 8.5 is a commonly used indicator for the solvent power of a given solvent for resinous substances. It is an arbitrary unit, measured with the aid of a standard solution of kauri-gum in butyl alcohol, hence its name. The higher the K value of a given solvent, the greater is its solvent power against not only rosin as used in ﬂuxes, but also other resinous substances. For this reason, solvents with high K values like CHC 111 must be tested before being used sure that they do not damage the circuit board, its on a given assembly, to make printed markings, or any component housings. The relevance of the K value as a yardstick for the deﬂuxing eﬃciency of a given solvent is open to doubt. It was originally conceived as a measure of the solvent power of hydrocarbon solvents for gums and rosins in comparison with that of butyl alcohol (butanol) for kauri-gum. This gum is a hard, fossil rosin totally diﬀerent from the rosins or their synthetic substitutes as used in soldering ﬂuxes. More relevant for deﬂuxing eﬃciency are various solubility parameters, which take,

job:LAY08 page:21 colour:1

black–text

Cleaning after soldering 281

Table 8.5 Some commonly used azeotropes and their solvent power for rosin Solvent

Boiling point

CFC 113 CHC 111** CFC 113/Methanol azeotrope CFC 113/Isopropanol azeotrope CFC 113/Methanol/Dichloroethylene azeotrope* CFC 113/Ethanol/Dichloroethane azeotrope* CHC 111/Isopropanol azeotrope** Isopropanol

47.6 °C/117.7 °F 74.1 °C/165.4 °F 39.6 °C/103.3 °F 46.4 °C/115.5 °F 38.4 °C/101.1 °F 45.0 °C/113.0 °F 72.0 °C/161.6 °F 82.4 °C/180.3 °F

Solvent power K value 27 124 45 47 not reported not reported 126 inﬁnite

*Reduced ozone depletion potential **Very low ozone depletion potential See Section 8.3.5

amongst other things, the speed of ﬂux removal into consideration. Nevertheless, the K value continues to be used as the main indicator of the deﬂuxing eﬃciency of agiven solvent.

Environmental acceptability When judging the environmental acceptability of a cleaning solvent for industrial use, its potential to cause damage can be quantiﬁed by four principal parameters. Its maximum allowable concentration (MAC) quantiﬁes the harm which it might cause to the persons working with it. This aspect will be discussed in Section 8.3.4. Its ozone depletion potential (ODP) and its global warming potential (GWP), or in popular parlance its ‘greenhouse eﬀect’, quantify the threat which the substance poses to life on our planet if it escapes into the atmosphere. Its photochemical ozone creation potential (POCP), a relative newcomer to the list of environmental villains, relates to the threat to the quality of life in our cities and industrial areas from the phenomenon of man-made ‘photochemical smog’. The ODP, the GWP and the POCP form the subject of Section 8.3.5. Table 8.6 lists the environmental risk parameters of the main solvents discussed so far. The MAC is deﬁned as the peak concentration, in parts per million, of the potentially noxious vapour in the atmosphere at the workplace to which a person may be exposed, based on an eight-hour day and a ﬁve-day week. High levels of MAC indicate a low level of health risk. The ODP relates the ozone depletion potential of the solvent to that of trichloroﬂuoromethane (CFC 11), an until-now widely used refrigerant and foamblowing agent, which is taken as 1.00. The GWP compares the global warming potential of the solvent against that of carbon dioxide, the universally known ‘greenhouse gas’, which is taken as 1.0. The POCP relates the photochemical ozone creation potential of a given solvent to that of isoprene, a naturally occurring volatile organic compound (VOC), which is arbitrarily taken as 100.

job:LAY08 page:22 colour:1

black–text

282 Cleaning after soldering

Table 8.6 Environmental risk parameters of the principal CFCs Solvent Methanol Ethanol Isopropanol CFC 113 CFC 113/Methanol azeotrope CFC 113/Ethanol azeotrope CHC 111

MAC (in ppm) 300 900 800 1000 300 900 350

ODP

GWP

POCP

zero zero zero

zero zero zero

12 27 15

0.85 0.75 not reported

2100 not reported not reported

zero not reported not reported

0.13

37

zero

Solvents based on CHC 111 have the great attraction of having a much lower ODP than CFC 113. The GWP of CHC 111 and its azeotropes, which is a measure of their contribution to the ‘greenhouse eﬀect’, is by more than one order of magnitude lower than that of CFC 113. Nevertheless, neither of them is zero, and therefore they are under notice of restriction or phase-out. The POCP of the CFCs, as well of the other non-ﬂammable halogenated solvents, none of which contain oxygen, is zero. On the other hand, the otherwise environmentally safe alternative solvents, like the terpenes and the modiﬁed alcohols which replace them, do have non-zero POCPs. Whether these are at all signiﬁcant in practical terms is however far from certain. These aspects will be dealt with more fully in Section 8.3.5.

8.3.2 Solvent-cleaning installations Manual cleaning Before describing the various mechanized cleaning processes with their more or less elaborate capital equipment, it may be useful to mention a simple manual cleaning method which is based on an old-establish practice of watch- and clockmakers. This method has its legitimate uses in small establishments, for short or laboratory runs, or in touching-up work, whenever not more than 6–12 boards have to be cleaned at a time. Its main virtue lies in the important fact that it uses none of the halogenated hydrocarbons, but plain isopropyl alcohol (isopropanol). Isopropanol is inﬂammable, and sensible precautions must therefore be taken, such as the avoidance of open ﬂames, and especially a strict prohibition of smoking (which should not be allowed in any case wherever a cleaning process is carried out). It is worth remembering that most rosin-based ﬂuxes contain isopropanol as a solvent and are therefore just as inﬂammable as the plain solvent. Handled sensibly, they do not represent a dangerous ﬁre risk, as normal wavesoldering practice proves. In order to minimize the risk, a mixture of 75% vol isopropanol and 25% vol demineralizedwatercan be used, which is a very good solvent for rosin-ﬂux residues at room temperature. It is used for that reason in the MIL test for checking the cleanliness

job:LAY08 page:23 colour:1

black–text

Cleaning after soldering 283

of circuit boards after a given cleaning treatment (Section 8.6.2). As with all manual cleaning procedures, polythene gloves should be worn. The equipment required consists of three ﬂat dishes, large enough to take 1–3 boards at a time (photographers’ developing dishes will serve very well), and three brushes with long, fairly stiﬀ bristles. For small boards, a toothbrush is quite suitable; bigger industrial brushes for larger boards are obtainable from most equipment suppliers. The board to be cleaned is allowed to soak for a while in dish no. 1. It is then scrubbed with the brush, using a circular motion. The procedure is repeated in dish no. 2, with a second brush, and the ﬁnal wash is given in dish no. 3, with brush no. 3. If after a while dish no. 1 becomes visibly contaminated, the solvent in it is discarded (which means it is emptied into the appropriate drum provided for the disposal of contaminated solvents by an accredited disposal company, which should be obligatory in every cleaning department).The dish is cleaned, ﬁlled with fresh solvent and becomes dish no. 3. The former no. 3 is demoted to no. 2, and no. 2 becomes no. 1. This procedure is repeated whenever it becomes necessary. To assist with the removal of ﬂux residue from underneath large components like PLCCs, the use of a dental jet-cleaner operated with the solvent instead of water has been favourably reported. Again, it must be ascertained beforehand that the solvent does not damage the apparatus. If operated with due care and given the right circumstances, manual cleaning can be very eﬃcient and cost eﬀective.

Mechanized cleaning processes The cleaning equipment which will be described in this section is designed to operate with non-ﬂammable halogenated hydrocarbons, principally CFC 113 and CHC 111, and their azeotropes. The phasing-out of these solvents in the industrialized countries does not mean that these machines are already irrelevant. One of the former major vendors of CFC 113 has recently launched a subsitute product with very similar handling and solvent properties, having a zero ozone depletion potential and a ‘very low’ global warming potential. At the time of writing (1997) it is awaiting general clearance (see Section 8.3.7, Table 8.12). It can be used with the equipment described in this chapter. Also, large numbers of cleaning installations which operate with CFCs and CHCs are still in daily use in several developing countries. It is important that their users are not only familiar with their working principles, but that they operate them in such a way that the escape of these solvents into the environment is reduced to an absolute minimum (see Section 8.3.4). Also, the working principles, if not the actual design, of cleaning installations which operate with the alternative solvents discussed in Section 8.3.7 are the same as those on which the machines for halogenated solvents are based. Rotary-brush cleaning This is a simple cleaning method, often employed for deﬂuxing the underside of wavesoldered boards which carry no SMDs. The soldered board passes over a number of successive cylindrical brushes, which are partly immersed in a bath of

job:LAY08 page:24 colour:1

black–text

284 Cleaning after soldering

solvent, and which rotate against the direction of travel of the board. This so called ‘kiss-cleaning’ method is unacceptable for working with halogenated organic solvents because of its high vapour loss to the atmosphere. Apart from that, it is unsuitable for the cleaning of boards which carry SMDs: it does not remove ﬂux residue from spaces close to or underneath SMDs, and in fact it could brush ﬂux residues into dead corners.

Batch cleaning by immersion, twin-tank method Immersion methods employ a combination of full immersion and vapourphase cleaning. A ‘twin-tank cleaner’ contains two adjoining solvent tanks, which are surrounded by a high-walled enclosure ﬁtted with condensing coils well below its upper rim (Figure 8.10). The solvent in the ﬁrst tank, which is heated, is kept boiling. Consequently, the space above this boiling sump is ﬁlled with saturated, heavier-than-air solvent vapour up to the level of the cooling coils which surround the freeboard of the twin-tanks at a safe distance below their top rim. Solvent which condenses on these coils ﬂows via a water separator into the second tank, which is

Figure 8.10 Twin-tank solvent cleaning unit

job:LAY08 page:25 colour:1

black–text

Cleaning after soldering 285

not heated but is ﬁtted with ultrasonic generators which are normally located on the tank bottom. The water separator removes moisture which might have condensed on the cooling coils along with the solvent. Though halogenated solvents like CFC 113 or CHC 111 contain stabilizers which reduce decomposition, the presence of water may cause the formation of hydrochloric or hydroﬂuoric acid, with fatal consequences for the cleaning plant. For this reason, it is best to maintain the temperature of the cooling water in the condensing coils at room temperature. To refrigerate the cooling water is risky: drops of dew, which form on the chilled coils, can collect HCl or HF from the solvent vapour and cause perforation. From the bottom of the boiling sump, contaminated solvent is continuously or periodically withdrawn and returned to the second tank via a distillation unit, which separates out the dissolved ﬂux residues. The plant is operated as follows. The circuits to be cleaned are loaded into a stainless steel basket and lowered ﬁrst into the solvent-vapour space above the boiling sump. Clean solvent condenses on the cold circuit boards and drains back into the sump, carrying the bulk of the ﬂux contamination with it. For this to happen eﬃciently, the boards should be stacked in the basket vertically and not too close together. Once the boards have reached the vapour temperature, the basket is moved across to the second tank and immersed in the clean, cold solvent, where the boards are exposed to the eﬀects of the ultrasonic agitation and cavitation. After a suitable interval, normally a minute or two, the basket is raised out of the solvent and allowed to remain in the vapour space for a further short period to allow dragged-out solvent to drain back into the tank and to evaporate into the surrounding vapour, thus reducing solvent drag-out. This type of twin-tank installation has proved its worth over many years, while wavesoldered boards were populated with inserted components only. It is still suﬃciently eﬀective with SMD-populated boards of simple design, with components not too closely spaced, and above all wavesoldered boards, where the stand-oﬀ gap is to a large extent ﬁlled with adhesive. For closely populated and speciﬁcally reﬂowsoldered boards, a three-tank installation like the one shown in Figure 8.11 is a better choice. Three-tank method After the initial condensation-cleaning stage above the boiling sump, the circuits are lowered into the boiling sump of tank I, which is optionally ﬁtted with ultrasonic agitation. As has been explained in Section 8.2.2, in a boiling medium ultrasonic impulses produce a strong rinsing eﬀect in the space between SMD and the board surface. From the boiling sump, the boards move to the second tank, which is ﬁlled with clean, cold solvent. This tank too can be ﬁtted with ultrasonic agitation, in order to remove ﬂux adhesions from the free board surfaces between the components. It is fed with clean solvent condensate from the cooling coils, again via a water separator. After a short dwelling period, the boards move to a third tank, which contains clean, boiling solvent and is ﬁtted with ultrasonic agitation for a ﬁnal cleaning stage. From here, the circuits are lifted into the vapour space where any adhering solvent is allowed to steam oﬀ in order to reduce solvent loss.

job:LAY08 page:26 colour:1

black–text

286 Cleaning after soldering

Figure 8.11 Three-tank solvent cleaning unit

Typical dwelling times in the various stages are reported as one minute for the ﬁrst stop in the vapour volume, two minutes in the boiling sump, one minute each in tanks II and III, and a ﬁnal half-minute dwell in the vapour volume before lifting the basket clear of the cleaning plant. Energy requirements To turn, for example, CFC 113 azeotrope into vapour, starting from room temperature, requires approximately 0.08 kW/hr per litre (0.3 kW/hr per US gallon). In actual cleaning practice, this means an installed heating power of 0.1 kW for each distilled litre of solvent per hour (0.4 kW for each US gallon distilled per hour). Depending on the size and the type of a given installation, the complete solvent content of a machine may be turned over as distillate between one to ten times every hour. Therefore, with a large plant, ﬁtting the plant with a heat pump which cools the condensing coils and helps to drive the evaporators or to heat one of the tanks may be a sensible investment. With a small plant, it could take years to write it oﬀ, longer than the normal lifespan of the machine.

job:LAY08 page:27 colour:1

black–text

Cleaning after soldering 287

Environmental safety rules for the operation of immersion cleaning installations Strict observance of the safety rules outlined below has become even more important in those countries where the use of CFCs is still permitted, because on-going surveillance of the ozone situation indicates that ozone depletion is still proceeding at a dangerous rate. 1. For both environmental and economic reasons, a number of measures must be taken to prevent solvent or its vapour from escaping into the working environment. (i) Circuit boards must be stacked vertically and not too tight in the holding basket, so that they can drain readily. This prevents not only carry-over of contaminated solvent from a dirty bath into a clean one, but also drag-out of solvent from the plant. (ii) The freeboard of the tank-surround must be at least three-quarters of the width of the tank, to prevent vapour from ‘sloshing’ over the edge of the tank when a transport basket is lowered into or raised out of the tank (Figure 8.12). Edge exhausts must on no account be ﬁtted. (iii) Baskets must be lowered and raised slowly, no faster than 3 m/min (9 ft/min), in order to minimize the ‘piston eﬀect’ (Figure 8.12). Programmed mechanical handling of the baskets is a main factor in reducing solvent loss and thus environmental damage.

Figure 8.12 Safety measures for immersion-cleaning tanks. (a) h 0.75w; (b) avoiding the ‘piston effect’ when lowering a working basket

job:LAY08 page:28 colour:1

black–text

288 Cleaning after soldering

(iv)

2. 3. 4. 5.

6.

Draughts of air in the workroom must be rigorously guarded against. When a tank or an installation is not in actual use, it must be covered. Permanently ﬁtted sliding lids are best. All solvent-cleaning installations must be ﬁtted with sensors which monitor and limit the bath temperature and the height of the vapour blanket above the solvent. All heated solvent tanks must be ﬁtted with cooling coils, which are turned on as soon as the plant is shut down. Cooling is continued until the solvent has reached room temperature in every tank. Solvent must never be poured from a bucket (it should not be in a bucket in the ﬁrst place) or a canister. To move solvent from one container into another, a pump, manual or motorized, must be used at all times. The formation of acid in the solvent must be monitored, and if necessary corrected. With a small installation this can be done periodically and manually, but larger installations should be ﬁtted with automatic acid-control. In ﬂuorinated or chlorinated solvents, ingress of water causes the formation of HF or HCl (see above) with grave consequences for the plant. Each solvent tank should be provided with a well ﬁtting stainless steel mesh, held in a frame slightly above the bottom of the tank, so that it can be lifted out. This screen intercepts any metallic or non-metallic items which may occasionally drop into the tank. Though almost all solvents are stabilized, a number of metals like copper, aluminium or brass are attacked when in contact with stainless steel in the presence of solvent. Tramp-metal parts can lead to local attack or perforation of the tank bottom if left there for any length of time.

8.3.3 In-line cleaning plants An integrated soldering line is best served by an in-line cleaning machine. The relatively long dwell times which a circuit board must spend in a static or even an ultrasonically energized tank ﬁlled with solvent would make an in-line cleaning plant too long. Therefore, in-line cleaning must be assisted by more powerful means than ultrasonic energy. High-pressure solvent jets are used to shorten both the washing and the rinsing stages of the cleaning process. In this context, it is worth remembering that the required jet pressure is determined by the SMD with the lowest stand-oﬀ height on a given board, and that doubling the stand-oﬀ height reduces the kinetic energy needed to ﬂush a contaminant from under the SMD by a factor of eight (Section 8.2.2). Table 8.7 shows the relationship between stand-oﬀ height and solvent jet pressure. In all in-line cleaning plants, the boards travel on a stainless steel belt of open mesh construction through successive arrays of jets, which impinge on the boards both from above and below. The pressure and volume delivery of the upper and lower jet arrays must be accurately balanced, so as not to dislodge the boards as they travel through the cleaner. The in-line cleaners at present on the market are either pure jet cleaners or combined jet and immersion cleaners.

job:LAY08 page:29 colour:1

black–text

Cleaning after soldering 289

Table 8.7 Relationship between stand-oﬀ height and solvent jet pressure m 25 25

Stand-oﬀ height mil 1 1

Jet pressure bar

lb/sq. in

15–17 2–5

220–250 30–75

The data were established with a CFC 113 azeotrope solvent

Pure jet in-line cleaning An example of such a system is shown in Figure 8.13. The circuit boards travel through the cleaner on an open-mesh endless stainless steel belt. Cooled, inwardly sloping entry and exit tunnels minimize the escape of the heavier-than-air solvent vapour. The conveyor carries the boards through a cooled, downwards sloping tunnel into the machine. There they pass through three successive arrays of hot, nearboiling solvent jets, each of which is fed from a tank beneath, with the boards moving in an atmosphere of practically saturated solvent vapour. Tank I is supplied with clean solvent, derived from the cooling coils of the downward sloping entry tunnel. It is followed by a boiling sump which provides the vapour atmosphere for the whole unit. A pump withdraws soiled solvent from this sump and feeds it to the exit tank III and its jets via a water separator and distillation unit. The solvent cascades from the exit tank via tank II back to the boiling sump. The boards leave the machine through a cooled, upwardly sloping tunnel. If a machine of this type is ﬁtted with a forced draught exhaust in order to prevent any solvent diﬀusing into the workroom, the exhaust duct must of course be ﬁtted with a cooled heat exchanger to prevent solvent escaping to the outside air.

Combined immersion and jet cleaning Again, the cooled entry and exit tunnels slope inwardly. On entering the machine, the boards dip into a ﬂat tank ﬁlled with warm solvent and ﬁtted with optional ultrasonic agitation. Halfway along the tank, boards pass underneath a vertical bulkhead, which forms an airlock to contain the saturated solvent vapour in the interior of the machine. The central cleaning stage consists of two jet arrays in series, which are fed with hot solvent from two boiling sumps in the bottom of this section. Having passed the jets, the boards enter a ﬂat exit tank, containing hot, clean solvent. They dive underneath a second bulkhead and leave the machine through the upwardly sloping, cooled exit tunnel. The solvent ﬂows through the machine from tank to tank in a direction opposite to the travel of the boards, which leave the cleaner through a bath of clean, freshly distilled solvent. Solvent from the entry tank is pumped via a water separator into a distillation unit, which removes the dissolved ﬂux residues and returns the clean distillate to the exit tank. With in-line solvent cleaning machines, the drag-out of solvent by the boards

job:LAY08 page:30 colour:1

black–text

Figure 8.13 An in-line pure jet cleaning plant (OSL)

job:LAY08 page:31 colour:1

black–text

Cleaning after soldering 291

which leave the machine could be a problem with closely spaced SMDs on a board. The combined immersion and jet cleaning machine shows an advantage here: the solvent in the exit tank is hot and so are the boards on leaving it. This gives the boards a chance to dry as they travel through the exit tunnel. Warming the exit spray of the pure jet cleaning machine might bring a similar improvement.

Vapourphase jet-cleaning Though a batch and not an in-line process, the following description of a cleaning process for boards populated with BGAs, which does not use a halogenated solvent, should be included in this section: BGAs with their very narrow stand-oﬀ clearance between component and board pose a particularly diﬃcult problem when for some reason the ﬂux residue must be removed from underneath the component (see Section 2.1.3). A recently introduced cleaning process, named ‘EVD’ (ecological vapour deﬂuxing) by its vendors, oﬀers a solution.

The procedure involves two basic steps: the board to be cleaned is placed in a closed chamber, where high pressure jets of a halogen-free, water-immiscible, non-ﬂammable solvent, at a temperature of about 45 °C/113 °F, impinge tangentially on the board with suﬃcient force to ﬂush ﬂux residue from underneath the components. Subsequently, the pressure in the chamber is reduced, while superheated solvent vapour of a temperature of 70 °C/158 °F is introduced into it. The vapour condenses on the circuit board which is still at about 45 °C/113 °F, and ﬂoods it with clean solvent. Subsequently, the board is dried under vacuum, while still in the chamber. Equipment for carrying out this process on a batch basis is commercially available. The solvent used in the EVD process is a halogen-free mix of organic solvents, with zero ODP, GWP and POCP values (see Section 8.3.5).

8.3.4 Halogenated solvents: safety and health Technical aspects Most chlorinated and ﬂuorinated solvents intended for industrial use contain stabilizing additives, which are designed to protect them against thermal or chemical decomposition. Nevertheless, a number of safety precautions are mandatory when working with these solvents in an industrial environment. Water contamination of the solvent – for instance through water condensate formed on cooling coils – causes the formation of hydrochloric or hydroﬂuoric acid in the system, with dire consequences for the installation. For that reason, the solvent circulation loops of both batch and in-line installations must be ﬁtted with reliable and regularly serviced desiccators of suﬃcient capacity, which should be located upstream of the distillation unit. Either molecular sieves (zeolite) or silica gel can be used, and manufacturers’ instructions must be carefully followed as to their regular regeneration or replacement. Gravity water separators must not be used on installations which work with azeotropic solvents: the alcoholic component of an azeotropic mixture is watersoluble, and would be removed together with the

job:LAY08 page:32 colour:1

black–text

292 Cleaning after soldering

separated water. Most equipment vendors can supply simple test kits for the detection and measurement of water contamination of a CFC or CHC. Alternatively, a simple test for excessive water content of the solvent works as follows. A test tube is half ﬁlled with the solvent to be examined, and a few grains of anhydrous cobalt chloride are added. If, on shaking, the colour of the solvent changes from blue to red, it is time to replace the zeolite or the silica gel in the desiccator. Any undue accumulation of ﬂux residues in the boiling sump must be avoided. If the rosin content of this sump rises above 3%, the solvent could begin to decompose, forming injurious decomposition products.

All metallic components of a solvent cleaning installation should be made of stainless steel. Metals like aluminium, magnesium, zinc, copper or brass are not resistant to long-time exposure to chlorinated or ﬂuorinated solvents. Therefore, any ﬁttings or components added by the user to a solvent cleaning installation must be made of stainless steel.

Health aspects The occupational exposure limit (OEL) is a measure of the health risk of a substance to a person using it, and the deﬁnition of an OEL varies from country to country and from industry to industry. With volatile substances such as solvents, the normally used OEL is the ‘maximum allowable concentration’ (MAC) of the solvent vapour in the working atmosphere, expressed in volume parts per million (ppm). The MAC of a volatile substance is the maximum concentration (in ppm) of its vapour in air to which a worker may be regularly exposed, on the basis of a 40 hour working week. Thus, the concentration of the vapour may be at or near its MAC during the whole working week, but the OEL must never be exceeded, for however short a time. MAC values may vary to some extent from country to country. Generally speaking, the lower the MAC value of a given substance, the higher is its toxicity. Table 8.8 shows MAC values for some common solvents. As the table shows, CFC 113 has the same low toxicity as ethyl alcohol. Its Table 8.8 MAC values of some common solvents Solvent

MAC in ppm

Methanol Ethanol Isopropanol

200 1000 400

CFC 113 CHC 111

1000 350

CFC 113/Methanol azeotrope CFC 113/Ethanol azeotrope CFC 113/Ethanol/Methanol azeotrope

300 900 800

job:LAY08 page:33 colour:1

black–text

Cleaning after soldering 293

azeotrope with ethyl alcohol is slightly more toxic than either, while the addition of the toxic methyl alcohol drastically increases the toxicity of the azeotrope. Good ventilation of the working premises is in any case essential, preferably both at ﬂoor level, because CFC 113 vapour is heavier than air, and above the normal working height. Above all, as has been said already, smoking must be strictly prohibited in any room where CFC or CHC solvents are used or handled. Both form extremely poisonous decomposition products at temperatures above 350 °C/662 °F, which means that inhaling their vapour through a burning cigarette can be very dangerous, if not fatal. Equally, neither food nor drink should be consumed in rooms where solvents are employed. Furthermore, Ellis mentions a physiological eﬀect of exposure to the vapour of isopropanol over a full working day. Absorption of this vapour is cumulative and additive to the eﬀect of ethyl alcohol in terms of slowing physiological reaction times. This means that just one aperitif at the end of a full working day which has been spent in an atmosphere containing isopropanol vapour can have a pronounced eﬀect, and he advises drivers to be aware of that. He also recommends that anybody suﬀering from a drink problem should not take on a job which involves the handling of organic solvents or exposure to their vapours.

8.3.5 The three environmental threats Today, scientists, industrialists and politicians are critically aware of the eﬀects of our industrial activities on the living environment of our planet. The organic solvents which concern us here are just a few amongst a very large number of environmentally damaging substances. Being volatile, their vapours enter the atmosphere, where they make their eﬀects felt. Some of these eﬀects have recently been recognized as potentially disastrous. All halogenated solvents are potentially dangerous, the CFCs more so than the rest. The tonnages in which they have been used until recently were considerable. The average annual global consumption of halogenated hydrocarbons in the late eighties amounted to approximately ﬁve million tonnes, which is 1 kg/2 lb for every person on this planet. Amongst these, the CFCs accounted for about one million tonnes in 1986, with seventy-ﬁve per cent consumed in Europe and the United States. Twenty per cent of this tonnage was used as solvents, while the rest went into refrigerating and airconditioning plant, aerosol cans and foamed plastics, in roughly equal parts.

Eventually, all of this tonnage ﬁnishes up in the atmosphere.

The ozone layer Ozone (O ) is a colourless gas with a distinctive, sharp odour (its name derives from the Greek word for ‘smelly’). It is highly toxic, causing damage to mucous membranes when above 10 ppm in air. At ground level, ozone is present in the atmosphere in minute quantities, but its concentration increases at higher levels until in the stratosphere, at about 28 km/92 000 ft above ground level, it reaches a maximum of approximately 8 ppm by volume. At greater heights, the concentration tails oﬀ again.

job:LAY08 page:34 colour:1

black–text

294 Cleaning after soldering

To speak of an ozone ‘layer’ is therefore not quite accurate, but in the public mind the term has created a powerful image of its concrete existence and of the threat to it; thus the term serves a useful purpose. The ozone layer’s crucial importance for life upon earth is its function as a powerful ﬁlter for UV radiation below the wavelength of 320 m. Radiation within that range has many diﬀerent eﬀects on humans, animals, plants and also man-made materials. Most of them are harmful and some of the damage that can be caused will be discussed presently. Ozone owes its presence in the stratosphere to a delicate balance between the processes of its formation and of its depletion. Ozone is formed from oxygen present in the stratosphere through a photochemical reaction, under the inﬂuence of the intense UV radiation which prevails at those heights. Its depletion is due to a breakdown of two ozone molecules into three oxygen molecules through a series of steps, initiated by the catalytic eﬀect of certain ‘free radicals’ like Cl or NO, which are naturally present in the stratosphere. These free radicals have diﬀused upwards as products of naturally occurring processes down at ground level, such as the decomposition of organic matter. The arrival in the stratosphere of additional amounts of man-made free radicals, like Cl, NO, and also Br, has now tipped the balance towards the decomposition of ozone. Measurable overall depletion has set in. It is particularly severe in the Arctic regions, and especially in the Antarctic where the ozone layer periodically disappears completely (ozone hole). In the latitude of the UK too, the ozone loss since 1969 has been estimated at approximately 7%. By now, public awareness of the ozone problem has risen to a level where ozone ﬁgures are given in the daily press. The situation is aggravated by the catalytic nature of the depletion process, which means that the oﬀending radicals remain in the stratosphere for a long time. It has been estimated that one Cl radical in the stratosphere can destroy 10 to 10 ozone molecules before diﬀusing back to the troposphere, where ‘the weather happens’. Once down there, at a height below 12 000 metres/36 000 feet, it eventually comes back to earth as acid rain. At this point is must be emphasized that the account given here of the mechanisms of ozone depletion is a highly simpliﬁed and by no means authoritative summary of very complex chemical and physical processes. A more detailed and authoritative overview of the subject has been written speciﬁcally for the solventusing electronic industry by Dr Colin Lea (see Reference 1). Table 8.9 shows the ozone depletion potential of some solvents. The damage potential of the more intense UV radiation which will reach the surface of the earth as the ozone ﬁlter gets weaker is very great, as can be seen from the following. Primitive life forms are endangered, especially plankton in the surface layer of the oceans. Fewer plankton not only aﬀects the whole marine food chain, but also restricts the role of the oceans as a global sink for CO , which the plankton normally assembles into organic matter. The loss of this mopping-up mechanism for CO increases in turn the threat of the ‘greenhouse eﬀect’ which will be dealt with presently. Meanwhile, further problems due to increased UV exposure include a higher risk of skin cancer for people with light coloured skin, suppression of the body’s immune system and increased damage to the eyes.

job:LAY08 page:35 colour:1

black–text

Cleaning after soldering 295

Table 8.9 Ozone depletion potential of some solvents Solvent

Ozone depletion potential (ODP)

Stratospheric lifetime

Alcohols CFC 11 (Freon 11) CFC 113 CHC 111 (Methyl chloroform)

nil 1.00 0.85 0.13

nil 281 years 138 years 6.3 years

CFC 11 was a widely used low-boiling solvent, though not used for cleaning soldered electronic assemblies. Its ODP = 1.00 has been chosen as an arbitrary reference point

Global warming The presence of CFCs in the atmosphere poses a further environmental problem. The radiation received on earth from the sun extends from the UV part of the spectrum over the visible light into the near infrared wavebands. The radiation re-emitted from the surface of the earth lies in the middle and far infrared. Much of this outgoing infrared is absorbed in the atmosphere, which thus forms a warming blanket, maintaining the more or less comfortable temperature to which life on the planet has adjusted itself (except for glacial periods, the last one of which ended about 10 000 years ago).

Like the maintenance of the ozone layer, the thermostatic control of the annual average global temperature is a matter of delicately balancing several parameters, in this case the transmission and retention of infrared, that is warmth, which is reﬂected back from earth into space. The main naturally occurring infrared absorbing gases, now termed ‘greenhouse gases’, are water vapour and CO . Since the start of the industrial revolution, steadily growing amounts of carbon dioxide have been added to the atmosphere, most but not all of which can still be absorbed by the naturally occurring sinks like the oceans. The rise in the average surface temperature of the earth by 0.5 °C/0.9 °F over the last century has been attributed to the rising level of CO . are newcomers of deadly eﬃciency upon this scene. On a tonne-for-tonne CFCs basis, CFCs have 6000 times the warming potential of CO , because just within the wavelength window between 8 and 13 m, where the carbon dioxide allows the infrared radiation to pass through, the atomic bonds of C-Cl and C-F absorb it.

All ﬂuorinated and chlorinated solvents have been given ratings to indicate their potential to inﬂict damage on the environment, based on experimental evidence. The rating ﬁgures refer to their respective ozone depletion potential (ODP) and their global warming potential (GWP), both potentials being rated against those of CFC 11 (Trichloroﬂuoro-Methane) arbitrarily taken as 1.0. CFC 11 is a lowboiling CFC solvent which is not normally used in the electronics industry (Table 8.10). The projected eﬀects of global warming, like all projections, are still a subject of debate, as is also the question whether the recent apparent changes in the weather

job:LAY08 page:36 colour:1

black–text

296 Cleaning after soldering

Table 8.10 GWP values of some solvents Solvent

Emission (1985) in kilo tonnes/yr

GWP

CFC 11

280

1.00

CFC 113 CHC 111

138 8

1.35 0.024

pattern are the beginning of a trend or due to statistical scatter. The rise of the mean sea level through thermal expansion of the oceans, as they get warmer, could be an early eﬀect. On the other hand, a melting of the polar ice caps is thought to take a long time. Moreover, according to a recent study, a rise in the average annual temperature leads in fact to thicker polar ice caps. This is explained by the increase in precipitation and a consequently increased snowfall in the polar regions, with the Greenland icecap thickening by 0.45 mm and the Antarctic one by 0.75 mm.

What seems certain is that a shift in climatic behaviour over large land areas will have early and serious consequences for farming and crops on a global scale. All this has strengthened the arguments which motivated the delegates at the London Conference 1990 in hastening the regulatory process concerning the halogenated solvents.

Photochemical smog The ‘photochemical ozone creation potential’ (POCP) of the vapour of a volatile organic compound is a further worry of environmentalists, for the following reason. In contrast to the stratospheric ozone, which protects life down below, ozone at street level is a noxious poison. Exposure to more than 0.1 ppm of ozone in the breathing air for longer than one hour is considered dangerous to a healthy adult, while 10 ppm in air are positively poisonous. Ozone concentrations at 10\ to 10\ levels are one of the constituents of so-called photochemical smog, a noxious cocktail of ozone together with organic peroxides, nitrates and other unpleasant chemicals. The smog and its ozone constituent are termed ‘photochemical’ because they are formed from otherwise less harmful, if not innocuous, vapours of organic compounds by the photochemical action of sunlight upon them. Photochemical smog is mainly an urban and local industrial problem, aﬀecting cities such as Los Angeles, Mexico City and Athens, or areas of dense industrial conglomerations. The principal man-made culprits are the exhaust gases from cars not ﬁtted with catalysers, the emissions from petrol reﬁning and from the ineﬃcient burning of coal or oil, but there are many other minor ones as well. Recently, even isopropanol, the most commonly used solvent in soldering ﬂuxes, has come under attack (Section 3.4.4). The compounds whose vapours are liable to be aﬀected in this manner are collectively known as ‘volatile organic compounds’ (VOCs). Their POCP is measured in arbitrary units, from zero to 100, the latter being the POCP of

job:LAY08 page:37 colour:1

black–text

Cleaning after soldering 297

isoprene, a constituent of natural and synthetic rubber. At the present state of the art, there is no general agreement on the method of determining or computing the POCP of a given volatile organic compound. What is certain is that the POCP of all CFCs and their relatives is zero. Unfortunately, on the other hand, isoprene with its POCP of 100 is a building block of most terpene molecules, the terpenes being one of the classes of organic solvents which at present are among the most favoured substitutes for the CFCs. So far, no POCP values for commercial deﬂuxing terpenes have been published. Alcohols, too, some of which are as promising as the terpenes for the purpose of deﬂuxing, are classed as VOCs, and have their speciﬁc POCPs (Section 8.5.3). In judging the environmental risk posed by a given VOC, its volatility is a decisive factor. In this context, the sparingly volatile deﬂuxing terpenes and modiﬁed alcohols, which are such promising alternative deﬂuxing solvents, seem fairly innocuous. To put the situation further into perspective, the quantities of other VOCs with non-zero POCPs which enter the atmosphere on a global scale ought to be considered. All plants release terpenes into the atmosphere, and their global annual terpene emission amounts to probably gigatons, admittedly much of it far from urban habitations. Furthermore, the vapour emitted by VOCs used for deﬂuxing in electronic manufacture, most of which is carried out in enclosed plant, is inﬁnitesimally small compared with that given oﬀ by non-catalysed car exhausts and the ineﬃcient burning of coal and oil reﬁning. Nevertheless, the VOCs have attracted the attention of the various international bodies concerned with the protection of the global environment, and along with them the terpenes and alcohols, as will be discussed in the next chapter.

8.3.6 Restrictions on solvent usage The nature and size of the environmental damage caused by the emissions from the various halogenated solvents have now been recognized as global concerns. The United Nations Environmental Program (UNEP) in 1981 set up a cooperative framework for monitoring, research and information exchange on all matters concerning the ozone layer and related global topics. In September 1987, UNEP called a convention in Montreal, Canada, with the aim of agreeing on regulatory measures concerning the production and use of halogenated solvents. The outcome was the ‘Montreal Protocol’, signed by the EC countries, the USA, Japan and 21 other countries. The then USSR and six further countries signed later. The Protocol relates to the present and future use of, amongst other substances, ﬁve CFCs (some of which are not only used as solvents but also as aerosol propellants, blowing agents for plastics and refrigerants). As far as solvents are concerned, the Protocol and its successors directly aﬀect the cleaning practices of the entire electronic assembling industry. In June 1990, representatives from 92 countries met in London under the auspices of UNEP for a ten-day conference to agree on a redrafting of the ‘Montreal Protocol’. As a result, all fully halogenated CFCs will be phased out by the year 2000, while the consumption level of not fully halogenated solvents such as methyl

job:LAY08 page:38 colour:1

black–text

298 Cleaning after soldering

chloroform (CHC 111) is to be reduced by seventy per cent by that date, before being fully phased out by the year 2005. Not the least problem of the conference was the need to persuade industrially developing countries like China and India, who between them account for forty per cent of the world’s population, to agree to these costly environmental measures, and for the developed nations to ﬁnd ways to internationally fund them. Regulatory measures to be taken concerning the VOCs are still being vigorously debated within the UNEP committees. The VOCs have been classiﬁed into four classes, graded according to their POCP values, with most of the alternative deﬂuxing solvents within the lower categories. Solvents may come under restriction according to their area of use rather than as speciﬁc solvents. Such areas are for instance car painting, printing, industrial painting, wood preservation and dry cleaning. Deﬂuxing is not among them. A full, though by now (1997) partially out-of-date, account of these developments is found in Reference 1.

8.3.7 Non-flammable organic solvents with reduced environmental risks Two features combine to give the CFC molecules their high environmental damage potential: their chlorine content and the high stability of their structure. The chlorine causes the destruction of the ozone in the stratosphere, and the high stability of the molecule helps the chlorine to get there and to stay around for a very long time. Replacing one or more of the halogens by a hydrogen atom destabilizes the molecule to some extent, so that it decomposes in the troposphere, at a height below 12 000 metres/36 000 feet, before reaching the stratosphere. On the other hand, any halogen set free in the troposphere will eventually come back to earth in the form of acid rain (or something worse, see below). To avoid confusion among the various alternatives to fully halogenated solvents, Table 8.11 lists the elements present in the diﬀerent classes of halogenated organic compounds. Though the CHC 111 molecule has a shorter life in the atmosphere than the CFCs, the behaviour of the Arctic and Antarctic ozone holes has become more alarming and the Cl content of 111 posed a suﬃciently serious threat at the 1992 London Conference to reduce its use to zero by the end of 1995. Table 8.11 Nomenclature of halogenated organic solvents Class Hydrogen FC CC CFC HCFC HCC HFC

− − − + + +

Elements present in the molecule Chlorine Fluorine − + + + + −

+ − + + − +

Carbon + + + + + +

job:LAY08 page:39 colour:1

black–text

Cleaning after soldering 299

Of the large number of possible non-ﬂammable HFCs and HCFCs, only a few have been evaluated so far for their use in deﬂuxing. These are given in Table 8.12. The new HCFCs such as HCFC 123 and azeotropes of HCFC 141b have lower ODPs and GWPs than CHC 111, and the parties to the revised Montreal Protocol have agreed to describe them as ‘transitional’ substances. They called for their ‘prudent and responsible use’, prior to their phasing out between 2020 and 2040, by which time the CFCs and CHCs will already have disappeared. Furthermore, some academics are suspicious of the HCFCs. Not only do they fear an intensiﬁcation of acid rain, but also the potential formation of triﬂuoroacetic acid (TFA), a possible byproduct of the breakup of the HCFC molecule, which the rain could bring down to earth. The fear is that TFA could enter the food chain through the roots of plants, and thus endanger health. Pentaﬂuoro-propanol (tradename Pefol) is in a diﬀerent category: it is a ﬂuorinated, non-ﬂammable propyl-alcohol, which is produced in Japan. At the time of writing (1993) the commercial availability of these solvents is limited, and evaluation is still proceeding. Once these CFC 113 substitutes have proved their worth and are fully commercially available, they could be used as drop-in substitutes for CFC 113 in existing cleaning installations, thus extending the useful life of sometimes large investments for a limited number of years.

8.3.8 Flammable solvents Isopropyl alcohol (isopropanol) is one of the best solvents for all ﬂux residues, with a clean environmental bill (except for its POCP, Section 8.3.4). As with all lower Table 8.12 Nonﬂammable alternatives to CFC 113 and CHC 111 Solvent

Boiling point

K value

Atmospheric life (years)

ODP

GWP (CFC 11 = 1.0)

CFC 113 CHC 111

47.6 °C/117.7 °F 74.1 °C/165.4 °F

27 124

90 6.3

0.85 0.13

1.3 0.02

HCFC 123 HCFC 141b 123/141bMethanol azeotrope ‘Pefol’* Vertrel XF** Cirozane***

28.0 °C/82.4 °F 32.0 °C/89.6 °F 30.0 °C/80.0 °F

68 61 85

1.6 12 —

0.02 0.15 —

0.02 0.18 —

80.7 °C/177.3 °F 54 °C/130 °F 47 °C/115 °F

36 — 40

— — —

0 0 0

— ‘low’ not stated

*‘Pefol’ is the tradename of pentaﬂuoro-propanol, a propyl alcohol with ﬁve of its hydrogen atoms replaced by ﬂuorine **Dupont (approvals pending, May 1997) ***3M

job:LAY08 page:40 colour:1

black–text

300 Cleaning after soldering

alcohols (Table 8.13), its ODP is zero, its vapour is not listed under the greenhouse gases and its health risk is low. However, it is ﬂammable, and therefore it requires specially designed ﬂame-proof and explosion-proof, and consequently more expensive, cleaning equipment. Amongst the lower alcohols, isopropanol is the normal choice not only as a solvent for liquid ﬂuxes, whether rosin-based or rosin-free, but also for deﬂuxing. Methyl alcohol is toxic and can cause blindness. Ethanol, which is the alcohol contained in wine and liquor, carries a high tax in most countries, unless made unpalatable. There is also the risk of addiction in operators. n-Propanol is more toxic and more expensive than isopropanol; it is mainly used in countries where isopropanol carries a tax. One way of rendering explosion-proof a deﬂuxing line which runs with isopropanol is to ﬁll its interior with nitrogen. With a conveyorized in-line machine (Figure 8.14) with immersion in a cold, ultrasonically agitated bath, this is a practical possibility. The oxygen level in the nitrogen atmosphere need not be as low as in a nitrogen-ﬁlled wavesoldering machine. On the other hand, the electrical side of the machine must be fully ﬂame- and explosion-proof, which adds to the cost of the installation. Another method of rendering boiling isopropanol explosion-proof by adding to it a high-boiling perﬂuorocarbon (tradename Flutec) has been proposed. The name ‘perﬂuorocarbon’ implies that the molecule contains only carbon and ﬂuorine, but no hydrogen. The ozone depletion potential of Flutec is zero, though its vapour is a greenhouse gas. Flutec itself is not miscible with isopropanol, but the vapours of the two ﬂuids are, and the vapour mixture is not ﬂammable. Plant for putting this process into practice is commercially available. Because of the GWP of the perﬂuorocarbon and its high cost, the design of the plant aims at minimum vapour loss. The low boiling points of the lower alcohols and their low heat of evaporation make it easy to incorporate a re-distilling facility into any cleaning plant working with alcohol. This avoids disposal problems of spent solvent, and adds to the environmental attraction of alcohol cleaning. Table 8.13 The lower alcohols Boiling point

Flash point

MAC (ppm)

Methyl alcohol (Methanol)

64.5 °C/ 148 °F

11 °C/ 52 °F

200

Ethyl alcohol (Ethanol)

78.2 °C/ 172.8 °F

14 °C/ 57 °F

1000

Isopropyl alcohol (Isopropanol, IPA)

82.3 °C/ 180.1 °F

17 °C/ 33 °F

400

n-propyl alcohol (n-propanol)

97.2°C/ 207.0 °F

22°C/ 42 °F

220

job:LAY08 page:41 colour:1

black–text

Figure 8.14 Combined jet and immersion cleaning machine (Electrovert)

job:LAY08 page:42 colour:1

black–text

302 Cleaning after soldering

8.4 Cleaning with water 8.4.1 Chemical and physical aspects Water is the universal and most readily available inorganic polar solvent. Using water instead of an organic solvent for deﬂuxing soldered circuit boards solves the problems of ozone destruction, global warming and ﬂammability, but raises several others.

Chemical aspects Rosin and residues from most wavesoldering oils are practically insoluble in water. Therefore, alkaline additives, so called saponiﬁers, must be added to the washing water to render these residues soluble. Rosin-free, fully watersoluble ﬂuxes, instead of rosin-containing ones, and watersoluble wavesoldering oils avoid this problem: the washing water needs no saponiﬁers and, as a further bonus, the dissolved residue of a watersoluble ﬂux is more mobile and ﬂushed away more readily than that from a saponiﬁed rosin. This means less rinsing eﬀort, cleaner boards, possibly a smaller washing unit with a lower energy consumption, and fewer eﬄuent problems. Therefore, there is a strong case for choosing a rosin-free ﬂux, though not necessarily one of the ‘no-clean’ ﬂuxes, with a fully watersoluble residue for soldering boards which for some good and unanswerable reason must be cleaned. Removing such residues with plain water is simpler, and a high degree of cleanliness can be achieved with less trouble and expense. As an added bonus, a more active watersoluble ﬂux can be used than would be admissible with a rosin-containing ﬂux, and this means fewer faulty joints, less expensive rework and a more reliable product.

Physical aspects Table 8.14 lists the values of some physical constants which are relevant to cleaning for water, isopropanol, CHC 111 and CFC 113. Their signiﬁcance, as far as cleaning is concerned, is as follows: 1. Water has a higher surface tension than the organic solvents. Therefore, it is retained more ﬁrmly in a given gap, such as under an SMD, and it requires more eﬀort to push it out in order to achieve eﬃcient rinsing. 2. Chlorinated and ﬂuorinated solvents have a higher density, hence a solvent jet of a given pressure and diameter has a higher kinetic energy than an equivalent water jet. Therefore, water-jet cleaning machines must operate at higher pressures than solvent-jet cleaners. 3. Water has a much higher heat of evaporation and is much less volatile than organic solvents. This means that drying a circuit board washed with water needs much more energy, and therefore costs more, than drying a solventcleaned board. In fact, drying the latter is mostly taken care of by the stray heat present in a solvent cleaning installation, so that normally no special drying stage is needed.

job:LAY08 page:43 colour:1

black–text

Cleaning after soldering 303

Table 8.14 Comparison between the physical properties of water, isopropanol, CHC 111 and CFC 113 Parameter

Water

Isopropanol

CHC 111

Boiling point

100 °C/ 212 °F 1.0 72 0.40 70 °C/ 158 °F 539

82.3 °C/ 180.1 °F 0.79 22.6 0.91 20 °C/ 68 °F 163

74.1 °C/ 47.6 °C/ 165.4 °F 117.7 °F 1.46 1.56 26 19 0.42 0.52 73 °C/ 40°C/ 163 °F 104 °F 35 53

Density at 20 °C/68 °F Surface tension (N m\) Viscosity (mPA sec) at Heat of evaporation (cal/g)

CFC 113

For these reasons, an in-line water washing machine consumes more energy and must be longer than a solvent-cleaning one with comparable output. At a given travelling speed, a board must receive a higher amount of kinetic and thermal energy for the same cleaning and drying eﬀect. A large in-line water washing installation may be rated at 25 kW or more. Alternatively, a batch operating water washing machine demands a longer dwelling time per charge than an equivalent solvent plant. Both aspects imply a higher demand on expensive factory space compared with solvent cleaning. All this adds up to the fact that running a water cleaning plant needs more thermal and kinetic energy, and thus costs more money than running a solvent-based one. A good deal of kinetic energy is dissipated when the high-pressure water jets, and the blasts of hot air issuing from the air-knives in the drying stage hit the circuit boards and the surrounding machinery. This means that a water washing line can be quite noisy unless soundprooﬁng measures, which may be expensive, are taken. Recently, the makers of water washing equipment have paid closer attention to the hydrodynamics of cleaning with water. Sprays consisting of individual drops of water, however intense, have been recognized as ineﬃcient. The aim now is to devise coherent, fast-moving water jets which, on hitting the board surface, convert their kinetic energy into equally fast-moving sheets of water which ﬂow tangentially across the board surface and penetrate into the spaces underneath and between the components, and around and behind the soldered joints, instead of shattering into a chaotic, multidirectional spray which may leave puddles of stagnant water between closely-set components. Fan-shaped jets which impinge on the boards at an angle are amongst the designs aimed at improving cleaning eﬃciency.

8.4.2 Water quality The degree of cleanliness achieved in any water cleaning procedure depends on the quality, that is the purity, of the water employed. ‘Hard’ water contains salts of calcium and magnesium. A distinction must be made, however, between ‘temporary’ and ‘permanent’ hardness. The former, which is due to the presence of calcium bicarbonate and/or magnesium bicarbonate or calcium hydroxide (lime) can be

job:LAY08 page:44 colour:1

black–text

304 Cleaning after soldering

removed by heating or boiling (thermal softening). The latter, due to calcium carbonate or magnesium carbonate or sulphate, must be removed by more elaborate methods. The degree of hardness of a water supply is usually given in mg calcium carbonate (or its chemical equivalent) in one litre of water.

Methods of water purification Should the hardness of a given water supply be entirely of the temporary kind (which is unlikely), simple heating will be suﬃcient to remove it by thermal ‘decalciﬁcation’. Heating such water from 20 °C/68 °F to 90 °C/194 °F precipitates more than half the dissolved solids. Heating it in a large boiler ﬁtted with an exit ﬁlter is a cheap method, but not recommended for producing by itself water of a quality suitable for the cleaning of electronic assemblies. Chemical water softeners, which are based on an ion exchange mechanism using sodium chloride, are worse than useless for treating water for cleaning circuit boards: they replace calcium carbonate with strongly ionic sodium carbonate, a very unwelcome substance to ﬁnd on a cleaned circuit board.

In practice, water purity suitable for the cleaning of electronic assemblies can be achieved by one of two methods: 1. De-ionization with ion exchange resins gives good results. Mixed-bed deionization involves passing ﬁltered water through one or more cartridges containing mixed anionic and cationic exchange resins. The dimensions and the number of the cartridges or columns of exchange resin needed for a given cleaning installation depend on the water consumption of the plant concerned. Regular and professional regeneration of the resins is essential. Normally, the cartridges are returned to the supplier for regeneration. Alternatively, some makers supply low-cost throw-away resins, where local regeneration facilities do not exist. The alternative to a mixed-bed system is separate-bed deionization, where anionic and cationic exchange resins are contained in separate columns, and the water passes through them in sequence. This system has a slightly lower eﬃciency than mixed bed de-ionization, but for all except the most demanding requirements it is good enough. Its advantage is its low running cost, because the resins can be regenerated by the user with hydrochloric acid. 2. Reverse osmosis (RO) is another option of water puriﬁcation. In this method, the raw water passes under high pressure through a semipermeable membrane or ‘permeator’, which allows the water to pass through but which retains all dissolved substances, whether they are ionic or not. The principle involved is not a plain physical ﬁltration. Put crudely, water is squeezed out of an electrolyte against the osmotic pressure of the solution. The puriﬁcation ratio is between 10: 1 and 20: 1, depending on the design of the RO puriﬁer. Any suspended solids in the raw water must be ﬁltered out ﬁrst, otherwise they clog the membrane of the RO ﬁlter. Excessive lime, giving a hardness 8°, and free Fe or Cl also render a feedwater unsuitable for RO. Thermal softening might be an answer to this problem, unless the initial contamination is high.

job:LAY08 page:45 colour:1

black–text

Cleaning after soldering 305

Degrees of water purity The best yardstick for assessing the suitability of a given water supply for board cleaning is its conductivity, measured in micro-Siemens/cm (S/cm= megohm\ cm\ (S = Siemens = Ohm\). The various water qualities encountered in cleaning processes can be roughly classiﬁed as follows: E Normal mains water: 100–1000 S/cm Suitable for cleaning circuit boards for industrial applications with no excessive cleanliness requirements. However, after the last cleaning stage, the rinsing water clinging to the boards must be blown oﬀ in a hot-air high-pressure drying stage (see Section 8.4.5). E Puriﬁed water: 10–100 S/cm For cleaning boards for domestic and industrial applications, with normal drying after washing. For more demanding applications, high-pressure drying is required. E High-purity water: 1–10 S/cm For military and avionic electronics. E Extreme-purity water: 0.8–1 S/cm For highly critical circuitry, carrying ICs with high lead counts.

8.4.3 Water recycling and effluent problems The higher the purity requirements of the water, the more it costs to meet them. For this reason, the ﬁrst stages of a water washing process are often carried out with mains water, provided it is of reasonable quality. Before the boards enter the last washing stage, adhering washing water is blown oﬀ, and only the last washing stage operates with puriﬁed water. Cleaning systems built on a module basis have the necessary ﬂexibility to meet such situations. The high-purity water of the ﬁnishing stage can be reconditioned by ion exchange or RO, either continuously or when a conductivity monitor indicates that the cleanliness has fallen below a preset value. Some soldering residues left on wavesoldered boards may cause problems here: certain watersoluble soldering oils are based on or contain non-ionic poly-alcohols which an ion exchange bed will not remove. RO ﬁltering is suitable for dealing with these contaminants. The quality requirements and the permissible concentration of contaminants in the eﬄuent water, which is run to waste from a washing installation, vary not only from country to country, but also between diﬀerent local authorities. Most organic constituents of soldering ﬂuxes and their residues are bio-degradable, and since the amounts involved are small, their biological oxygen demand is modest. However, because the action of every soldering ﬂux is based on its ability to dissolve metal oxides, all ﬂux residues contain metal salts. Therefore, washing water run to waste contains not only organic contaminants but also some metal compounds. The most likely metals to be found in deﬂuxing waste water are Pb, Sn and Cu. The limits are set normally in mg/litre, for example, 0.5 mg Pb/litre and 1.5 mg Cu/litre and, in the USA, no limits for Sn. One of the most demanding

job:LAY08 page:46 colour:1

black–text

306 Cleaning after soldering

countries in this respect appears to be Switzerland, which sets a limit of 2 mg/litre for tin in the eﬄuent water. Should the waste water exceed one of these limits, the eﬄuent is often diluted with mains water till the required limit is met. This practice is rightly beginning to be frowned upon, since what matters is not only the concentration of a pollutant in the eﬄuent, but also its total tonnage over a given period. With the growing importance of the environmental impact of every industrial activity, it is very likely that an ion exchange treatment instead of simple dilution will be required by the various authorities at some future date with consequent increases in the cost of waterwashing. The acceptable pH value of waste water lies normally in the range 6–9 and, therefore, some water-washing eﬄuent may need pH adjustment before being discharged. Finally, most authorities object to foam and, if necessary, foam suppressants must be added before such water is run to waste.

8.4.4 Removal of residue from watersoluble fluxes Residues from these ﬂuxes consist mainly of their solids content, e.g. various amines or organic acids, together with thickeners, wetting agents, etc., partly in their original form and partly as pyrolytic decomposition products which have formed during soldering. Small amounts of metallic compounds are also present (see above). Most of these substances dissolve in hot water (in normal cleaning practice 60– 80 °C/140–175 °F) reasonably quickly. Some Pb compounds may occasionally cause solubility problems, as can some soldering oils used in wavesoldering, which may polymerize and lose their solubility if they have been overheated or not renewed in good time (Section 8.2.1). Though plain water without additives will remove all residues from watersoluble ﬂuxes, for physical rather than chemical reasons the addition of 5–10% of highpurity (99.9%) isopropanol to the rinsing water of the last cleaning stage has been found to give several beneﬁts. The isopropanol halves the surface tension of the water, and this assists rinsing. Also, on emerging from the rinsing stage, the boards are covered by a thin ﬁlm of water instead of discrete drops. Therefore, they dry more readily, which saves thermal energy. Finally, the alcohol acts as a foam suppressant, and helps to dissolve remaining organics. In many cases, these advantages outweigh the cost of the isopropanol.

8.4.5 Removal of residue from resinous fluxes Since the introduction of no-clean ﬂuxes, the use of resinous ﬂuxes has been shrinking steadily. Nevertheless, it is still worth knowing how to remove their residues. Resinous ﬂuxes leave a heterogeneous residue: the rosin itself is non-polar and water-insoluble; the ﬂux activators are polar and watersoluble; the metallic reaction products which are the result of the interaction between ﬂux, metallic substrate and solder are partly watersoluble metal salts and partly water-insoluble metal resinates. This is true both for ﬂuxes based on natural rosin, and on synthetic rosin substitutes.

job:LAY08 page:47 colour:1

black–text

Cleaning after soldering 307

To cope with this mixture the washing water requires an additive. This may be one of the above-mentioned saponiﬁers, for example monoethanolamine, which converts the insoluble rosin into soluble resinous soaps. The reaction takes a certain time, especially if the rosin has polymerized because of overheating during the soldering process, or prolonged delay between soldering and cleaning. The resulting resin–soap solution is somewhat viscous, hence the need for high-pressure water jets. Alternatives which have recently become available contain surfactants (i.e. wetting agents) together with phosphates and silicates, or alternatively an alcohol which assists the solution of the rosin residue. The additives are claimed to be biodegradable within the deﬁnitions of the legal requirements of the EU. Resinous ﬂuxes with low solids content, which have become popular in the last few years, are more amenable to water cleaning than the classic high-rosin ﬂuxes: their residue contains a high proportion of the watersoluble activators, and therefore the washing water needs less saponiﬁer to deal with them. Because of the preponderance of polar compounds in the residue from these ﬂuxes, they are in fact more readily removed by water washing, with a surfactant (wetting agent) added to the water, than by solvent cleaning, should their removal be required. The need to add a saponiﬁer to the washing water has to be considered in the design of the washing plant. With batch cleaners, which work on the ‘dishwasher’ principle, the watertank has to be large enough to accommodate the saponiﬁer addition. With in-line washing plants the saponiﬁer addition must be metered so as to match the requirements of the boards in transit through the machine. With these machines, saponiﬁer is added only to the ﬁrst and the main wash, both of which must provide a transit time long enough to allow for complete saponiﬁcation. The ﬁnal wash operates with a separate clean-water circuit. Saponiﬁed washing water has a pH of around 10. It should be buﬀered in order to prevent it from attacking light metals, such as certain component housings, or some board laminates or solder resists. Therefore, before using a given saponiﬁer in a cleaning plant, it is advisable to test it at the maximum concentration which is likely to be encountered, and at the normal washing temperature, against all circuit board materials and components which will come in contact with the washing water. Because of its high pH, saponifying washing water must be neutralized, mostly with dilute HCl, down to a pH acceptable by the local authority before it is discharged as waste. Most saponiﬁers are themselves biodegradable.

8.4.6 Water washing installations Batch-cleaning systems Batch-type water cleaning is sometimes known as ‘dishwasher’ cleaning. The name ‘dishwasher’ must not be allowed to mislead here: some makes of batch water cleaning machines are indeed made by well-known manufacturers of domestic and industrial washing and dish-washing equipment, but batch cleaners are dedicated machines, designed for the speciﬁc purpose of deﬂuxing soldered circuit boards and, as a class, they have reached a high degree of technical sophistication. A batch cleaner needs provision for adding measured amounts of saponiﬁer to the water of the ﬁrst washing

job:LAY08 page:48 colour:1

black–text

308 Cleaning after soldering

cycles, when the boards were soldered with a resinousﬂux, and for carrying out the last rinsing cycle with fresh, clean water. With this type of equipment, the circuit boards are vertically arranged in ﬁxtures or baskets, and placed at bench-level in a mostly front-loading washing chamber. They are then washed in an array of high pressure hot-waterjets, of a temperature of 60 °C/140 °F–70 °C/160 °F, which are projected from rotating or reciprocating spray arms. The cleaning sequence normally follows a program, which can be called up from a store, either supplied by the vendor or created by the user. The water for the ﬁrst washing cycle is pumped from a heated sump or tank. For the removal of rosin-free, fully watersoluble residue, a small amount of surfactant (wetting agent), sometimes together with a certain amount of alcohol, is often added to the water in order to speed up the solution of the residue. The removal of rosin-containing residue needs the addition of an alkaline ‘saponiﬁer’, which converts the water-insoluble rosin into a watersoluble soap. A number of saponiﬁers are on oﬀer from specialist vendors or from the machine vendor, and they raise the pH of the washing water up to 9–10. Some of them are in the form of concentrated solutions, which may contain a certain amount of alcohol. With some machines, the water from the washing cycle is run to waste and replaced with the spent water from the rinsing cycle which follows. With others it is returned to the sump or tank, from which it is discharged to waste when it has reached a preset level of contamination. The tank may then be reﬁlled with clean mains water and heated, or reﬁlled with the run-oﬀ from a rinsing cycle. The rinsing cycle normally operates with hot, demineralized and/or de-ionized water, of a quality governed by the cleanliness required from the ﬁnished board (see Section 8.4.2). Untreated mains water can sometimes be used if it is of high quality and if the cleanliness requirements of the product are modest. In all cases, the rinsing water is held in a separate tank, and often piped and sprayed through a separate plumbing system in order to avoid cross-contamination from the washing water. Some makers oﬀer dishwasher-type machines operating with recirculated rinsing water which has passed through a de-ionizing column, and which is being monitored for its quality. Zero-discharge batch washing machines are a relatively new concept. Here, spent rinsing water is used for the prewash, and then recycled through a set of activated charcoal ﬁlters, which remove non-ionic contaminants such as rosin residue, followed by a set of de-ionizing columns. Having been washed and rinsed, the boards must be dried in a stream of hot air, sometimes created by an array of reciprocating hot-air knives. With some machines, the washing unit doubles as a drier, with a stream of hot air passing through the washing chamber. It is more economical, however, both in energy consumption and in time, to transfer the boards in their holding basket from the washing unit to a dedicated drying unit, in which the boards are subjected to a strong blast of hot air. It saves energy not to have to dry the interior of the washing unit and its spray-nozzles, as well as its load of boards, after every cycle. Time is saved and the capacity of the installation is doubled, because the next charge is being washed while the preceding one is dried. A modern batch water washing system can handle boards with up to a total area of

job:LAY08 page:49 colour:1

black–text

Cleaning after soldering 309

about 2.5 sq. m/22.5 sq. ft per batch. With two cycles per hour, a batch water washing system with separate washing and drying units can handle up to 5 sq. m/45 sq. ft board area per hour, suﬃcient to keep up with a small or medium sized soldering line.

Dishwasher systems can give excellent cleanliness, at a capital cost and with space requirements which are both modest in comparison with in-line waterwashing plants. Their throughput, however, is limited and cannot be expected to keep pace with a continuously running large wavesoldering or reﬂowsoldering line. Moreover, the boards must be placed by hand in their holding baskets, which means that batch washers cannot be integrated into a continuous soldering line.

In-line water washing systems The output from one or more integrated full-sized soldering lines is best handled in an in-line washing plant, with the boards travelling on a continuous conveyor. For dealing with boards soldered with a watersoluble ﬂux, the in-line cleaner need not be very long, at most three metres/nine feet, because of the ready solubility of the ﬂux residue. The removal of resinous residues requires longer washing machines, because the rosin in the residue must be saponiﬁed and washed away before the subsequent rinsing stage. The nature of the process favours washing lines built up from modules. Modular design, oﬀered by several makers, makes the process more ﬂexible and allows the user to change from one soldering strategy to another without the capital investment for a complete new cleaning plant. A high-capacity modular water washing installation may be up to 9 m/27 ft in length. Figure 8.15 shows the basic layout of an in-line water cleaner. Plants constructed from stainless steel have a long life, but are expensive and, being inherently more

Figure 8.15 In-line water washing machine

job:LAY08 page:50 colour:1

black–text

310 Cleaning after soldering

noisy, may need soundprooﬁng. Polythene is cheaper and quite safe as a constructional material, provided the water temperature is reliably controlled so as not to exceed 70–80 °C/160–180 °F. At higher temperatures, polythene softens and may sag or crack under stress. The boards travel on a horizontal, open-mesh stainless steel conveyor belt through successive arrays of high-pressure waterjets, which impinge on the boards from above and below. Because the boards lie loosely on the belt, the pressure and the ﬂow rate of the upper and lower jet arrays must be precisely balanced, so as not to cause the boards to ﬂip over. The kinetics of modern washing jets have been discussed already in Section 8.4.1. With the system shown, washing proceeds in several stages. The prewash and the main-wash compartments are linked, with the feed-water entering the main-wash at its exit end, and cascading from tank to tank towards the inlet end of the machine, ﬂowing against the direction of the conveyor belt. Saponiﬁer, if needed, is added in metered amounts to the main-wash, either to the water tank or to the feed-water of the cleaning jets. The cleaning jets, which operate as a rule at about 2 bar (30 lb/sq. in), can be fed from the hot-water sump or with fresh, preheated water. Both main-wash and prewash can be fed with mains water, provided this is of reasonable quality and free from suspended or organic matter. From the main-wash, the boards pass into the rinsing wash, through a curtain of high-pressure hot-air jets which blow the water from the wet boards back into the main-wash. This prevents contamination of the clean (and maybe expensive) rinsing water by carry-over of dirty washing water. Any plastic ﬂaps which separate the two washing sections must be kept scrupulously clean so as not to redeposit dirt on the boards. The water quality of the rinsing wash is chosen to suit the cleanliness and service requirements of the end product. Part or all of the rinsing water can be cascaded into the main-wash tank. Alternatively, the rinsing water can be recycled through an ion exchange column. Monitoring the water quality in the rinsing stage with conductivity meters can save water. Assuming the rinsing stage is subdivided into three modules, the conductivity can be set at, for example, 300 S/cm in the ﬁrst tank, 30 S/cm in the next, and 3 S/cm in the exit tank. If these values are exceeded, either the water ﬂow can be increased or the board conveyor can be slowed down. From the rinsing stage the boards enter a drying chamber. Here they pass through one or more curtains of high-pressure hot-air jets, which blow away most of the adhering water. Finally a bank of infrared heaters warms the boards so that they lose any remaining surface moisture by natural drying after emerging from the machine.

8.5 Semi-aqueous cleaning 8.5.1 The concept The phasing out of the non-ﬂammable fully or partly halogenated solvents and the problems associated with the ﬂammability of the lower alcohols have led to the development of organic solvents for the removal of ﬂux residues, both water- and not watersoluble, and of equipment for their use. At the beginning of 1997, a

job:LAY08 page:51 colour:1

black–text

Cleaning after soldering 311

European market survey listed some 30 products, oﬀered by 18 vendors. They are all halogen-free and not ﬂammable, but with some exceptions combustible. The solvents should have zero ODP and GWP and ﬂashpoints above 37.8 °C/100 °F. So far, a number of solvents which come under the broad classes of the terpenes, ketones, the modiﬁed alcohols and the so-called hydrocarbon mixtures have emerged (see Table 8.3 in Section 8.2.2). Since none of them contain halides, their ozone depletion potential is zero. Any global warming potential they may possess is claimed to be very low because of their low volatility. Being organic substances, they are combustible because their molecules contain carbon. They do not present a high ﬁre-risk, but some precautions must be observed in their use, as will be discussed presently. Their chemical constitution makes them good solvents for rosin and its synthetic equivalents, but they are equally suitable for the removal of rosin-free ﬂux residues. However, because their molecules are larger than those of the halogenated solvents and the lower alcohols, they are less mobile, i.e. more viscous. Once they have dissolved the ﬂux residue, they are often, but not necessarily, rinsed oﬀ with water. A hydrocarbon mixture for example can be rinsed oﬀ with a similar, lower boiling one. What is then left on the board after that rinse can be allowed to dry in air.

The solvent cleaning and water cleaning systems described so far employ one single cleaning medium, which fulﬁls two functions: ﬁrst it dissolves the ﬂux residue, and then it ﬂushes away the resultant ﬂux solution in the rinsing stage. The highly mobile halogenated solvents and the alcohols fulﬁl both functions very well, but they either endanger the environment or they are ﬂammable. Water is slightly less mobile, but it needs additives to help it to dissolve the residue from rosin-based ﬂuxes and oils. The semi-aqueous cleaning process closely resembles the action of a cleansing cream, which is ﬁrst applied to dirty hands and is then rinsed oﬀ with warm water: semi-aqueous cleaning systems separate the tasks of solubilizing and of rinsing. The task of dissolving the ﬂux residue is taken by an organic, non-ﬂammable, slightly viscous medium, which is miscible with or emulsiﬁable in water. Its principal function is to penetrate to all the places where ﬂux residue lodges, and to interact with it. The subsequent rinsing task is taken over by water, very often warm or even hot, which ﬂushes out and carries away the organic solubilizing medium together with the ﬂux residue which it has absorbed. In the last few years, a variety of cleaning machines which are designed speciﬁcally for the semi-aqueous process have become commercially available. They are now established in a wide and diverse range of applications.

8.5.2 The cleaning solvents The organic cleaning media which are used in semi-aqueous cleaning fall into several classes (see Table 8.3, Section 8.2.2). They may be polar like saponiﬁers, wetting agents, modiﬁed alcohols and esters, or non-polar terpenes, ketones or hydrocarbon mixtures. The terpenes together with the so-called ‘hydrocarbon mixtures’ are non-polar compounds; they are not miscible with water, but they readily emulsify in it, which means that a water rinse will remove them, together

job:LAY08 page:52 colour:1

black–text

312 Cleaning after soldering

with the ﬂux residue which they have dissolved. The ‘modiﬁed alcohols’ are a somewhat later development: being alcohols, they are polar compounds and miscible with water. Thus, a water rinsing stage will remove them together with the ﬂux residue which they have absorbed. Terpenes are a rather loosely deﬁned, but very large, class of organic compounds, many of them liquids at room temperature. Most of them are derived from vegetable matter such as wood or fruit, and they have a distinctive, often not unpleasant, fruity smell. While over 10 000 naturally occurring terpenes are known, only a few of them, which have a molecular structure similar to that of rosin, are used for deﬂuxing. Synthetic terpene-like cleaning media, known as hydrocarbon mixtures, with tailor-made, purpose-dedicated properties are oﬀered by many vendors. They are often mixtures of a number of hydrocarbons with properties taylored to the requirements of deﬂuxing. Terpene-like media used for deﬂuxing share several common features. Because of their molecular similarity to rosin they are very eﬃcient rosin solvents, but their solvent power for inorganic or ionic ﬂux activators is limited. Most commercially available deﬂuxing terpenes contain an added surfactant (wetting agent) which assists them to penetrate into the recesses of the board and to be ﬂushed out by the water in the rinsing stage. Terpenes can hold up to 60% vol of rosin in solution before they become saturated. The rosin-loading of the terpene can be estimated by checking its speciﬁc gravity against a calibration curve, supplied by some vendors. Once it has become saturated with rosin and recovered from the deﬂuxing line, it must either be disposed of, which is best entrusted to a specialist ﬁrm, or returned to the vendor if suitable arrangements exist. Most terpene-like media are not miscible with water, so that solvent carried over into the water-rinsing stage must be separated out in a so called ‘decanter’ or settling tank. On the other hand, terpenes are soluble in alcohol, e.g. isopropanol. They are more viscous than water, but still reasonably mobile. A terpene can be separated from the rosin it has dissolved only by distillation. However, at normal atmospheric pressure, its boiling point is above its ﬂashpoint, so that it must be vacuum-distilled at a pressure low enough to depress the boiling point to below the ﬂashpoint. For this reason, reconditioning of ﬂux-saturated terpene is best left to the vendor. Small amounts of terpene which enter the water of the ﬁnal cleaning or ‘polishing’ stage which follows the rinsing are biodegradable. The so-called modiﬁed alcohols are a class of water-miscible organic solvents, or a mixture of such solvents, which are derived from non-linear alcohols or glycols, sometimes with added ethers or amines. They have been formulated to possess good solvent power for both rosin and its synthetic equivalents, and for ionic or inorganic activators. Their ﬂashpoints are in the region between 80 °C/180 °F and 100 °C/ 215 °F. They are mostly colourless ﬂuids, and like the terpenes slightly viscous. With most of these solvents, the percentage of accumulated dissolved ﬂux residue can be determined by a analytical method.Many vendors of solvents are able to give advice, and often can provide reagents and equipment to carry out the analysis. The methods of disposing of the spent cleaning solvent depend on its nature, the location of the user and the local environmental regulations. Some solvents can be

job:LAY08 page:53 colour:1

black–text

Cleaning after soldering 313

regenerated by the user, many are biodegradable, some can be burnt in a suitable disposal installation, while spent modiﬁed alcohols can be regarded as secondary industrial fuels. For some other cleaning media, collection can be arranged with the vendor. It cannot be too strongly stressed that, before deciding on a particular cleaning medium, it is essential to discuss the method of its disposal, and above all the associated costs, with the vendor or his agent.

8.5.3 Semi-aqueous washing installations for water-immiscible solvents General features Common to all semi-aqueous cleaning systems is a ﬁrst washing stage which ensures thorough penetration of the solvent into all the spaces and crevices of the soldered boards. Though the wetting behaviour of both terpenes and modiﬁed alcohols towards the surfaces of boards, components and joints is good, and with some of them assisted by added surfactants, their viscosity means that they need some mechanical push to get to where they have to act. Section 8.2.1 describes the diﬀerent methods which can be used to propel a solvent to where it is needed. It is common practice to warm the cleaning medium in the washing stage, in order to reduce its viscosity and to speed up the solvent action. An operating temperature of 40 °C/100 °F to 50 °C/120 °F is normal, but in no case should this temperature approach the ﬂashpoint of the medium closer than to within 20 °C/35 °F. Even when this precaution is observed, there is a problem when one of these organic solvents is applied by a jet or spray. A mist or aerosol of a combustible ﬂuid may spontaneously ignite and cause an explosion at temperatures below its ﬂashpoint. To guard against this danger, spray chambers of semiaqueous washing machines must be ﬁlled with nitrogen or carbon dioxide. This complication can be avoided if the boards, instead of being sprayed, are fully immersed in the cleaning medium, while the kinetic energy for propelling it into the crevices of the circuit board is provided by strong jets below the surface (jacuzzi eﬀect) or by ultrasonic energy. An ultrasonic energy input into the liquid in the cleaning tank of about 20 W/litre (90 W/gal) is normal, where the energy is taken as the rated electrical power consumption of the ultrasonic transducers.

Conveyorized in-line systems With an in-line system, the boards travel on a ﬂat, straight open-mesh conveyor. They ﬁrst enter a washing module, where they pass between successive arrays of solvent jets, which impinge on the boards with equal force from above and below, as with an in-line water washing machine. The explosion risk requires that the spray chamber is ﬁlled with nitrogen or carbon dioxide. If the boards travel fully immersed through an elongated jacuzzi tank on a conveyor which enters and leaves the bath at an angle, as is the case with some designs on the market, this complication is avoided. Before leaving the washing unit, an array of warm-air knives reduces the drag-out of solvent.

job:LAY08 page:54 colour:1

black–text

314 Cleaning after soldering

The boards then enter a rinsing or ‘polishing’ module via an intermediate conveyor, which prevents undue carry-over of solvent into the rinsing water. The rinsing stage is very similar in concept and operation to that of the rinsing stage of an in-line water washing system. The same considerations as to operational strategy, water purity and ﬁnal drying apply (Figure 8.16). As with all in-line systems, the boards travel through the machine in single, or at most double, ﬁle. This means that these machines are necessarily rather long. With washing and polishing modules having lengths of between 4 m/12 ft and 6 m/18 ft, and with an intermediate conveyor connecting them, overall lengths of 10 m/39 ft or more are not uncommon.

Batch systems With the batch concept, the boards are placed in baskets or carriers, which are immersed in a succession of treatment tanks. With most installations on the market, the baskets are moved by mechanized, often automated and programmable, handling systems. The design details of a cleaning installation depend on whether a water-insoluble terpene or a watersoluble modiﬁed alcohol is used, but basically all batch cleaning systems are similar. With more viscous water-immiscible solvents like terpenes, the washing stage comprises two tanks. The ﬁrst one contains warm solvent (40 °C/100 °F to 60 °C/ 140 °F, depending on its ﬂashpoint). The solvent in the tank may be agitated ultrasonically by arrays of transducers which are so placed that their energy can reach the surface of all the boards in the holding ﬁxture with adequate intensity. Alternatively, an array of strategically placed sub-surface jets of solvent provide the necessary kinetic energy in the solvent to penetrate into the recesses of the board assembly. With some installations, this tank is equipped with a heat pump, which extracts heat and recycles it, so that the temperature of the solvent may be maintained at its optimum, both for cleaning eﬃciency and for safety.

Figure 8.16 In-line semi-aqueous cleaning (water-immiscible solvent)

job:LAY08 page:55 colour:1

black–text

Cleaning after soldering 315

The dwell time of the boards in this tank depends on the complexity and the population density of their layout, on the type of ﬂux used, on the soldering parameters, and on the time interval between soldering and cleaning. Normally it is no more than a few minutes. The board is then transferred to the second tank of the washing module. This tank contains warm water (40 °C/104 °F to 60 °C/140 °F), with which the waterimmiscible, rosin-loaded terpene forms an emulsion. Ultrasonic agitation or subsurface jets ﬂush this emulsion from the recesses of the board, removing the bulk of the ﬂux residue. The surfactant in the terpene assists this rinsing process. The emulsion which forms in the cleaning tank is constantly pumped through a settling tank, called a ‘decanter’. In the decanter, the water, which is heavier than the solvent–water solvent settles to the bottom, from where it is returned to the cleaning tank. The ﬂux-loaded solvent–water solvent rises to the top, where it is creamed oﬀ and transferred to containers for subsequent disposal by a specialist contractor, while the water is recycled. The carry-over of terpene on the boards passing from the solution tank into the emulsion tank ensures that the concentration of ﬂux residue in the terpene in the emulsion tank remains roughly at the same level, normally about 50%. The carry-over is constantly made good by further solvent being added, which therefore must be considered as a consumable. After leaving the emulsion tank, the boards in their baskets enter the rinsing stages, where they pass through a succession of water-rinsing tanks. The successive washes follow the same pattern as applies to an in-line water washing installation (Section 8.4.6). Depending on the degree of cleanliness required, the boards then pass through several hot-water rinsing stages, of which the ﬁnal ones may operate with de-ionized water if the product requires it. Finally, the baskets enter a hot-air drying chamber before they leave the machine. In principle, there is little diﬀerence between the back-end of a semi-aqueous cleaning system and that of a water cleaning one. Several processing options and conﬁgurations of this procedure, one of which is shown diagrammatically in Figure 8.17, are on oﬀer to the market.

8.5.4 Semi-aqueous washing installations for water-miscible solvents The ﬁrst immersion cleaning stage will always consist of either one tank or two tanks in sequence with either ultrasonic or sub-surface jet agitation. They operate at temperatures between 40 °C/100 °F and 60 °C/140 °F, and the dwell time in the tank or tanks depends, apart from the characteristics of the solvent, on the bath temperature and the intensity of the agitation. The dwell time is counted in minutes, normally well below ﬁve. Most solvent vendors recommend that the dissolved ﬂux residue is stripped continuously from the solvent by circulating the contents of the tank or tanks through a carbon ﬁlter to remove the rosin and an ion exchange ﬁlter to remove the ionic ﬂux activators. If a rosin-free watersoluble ﬂux is used, only the latter is needed. The recycled clean solvent cascades from the second tank into the ﬁrst. A number of options exist for the rest of the cleaning line.

job:LAY08 page:56 colour:1

black–text

316 Cleaning after soldering

Figure 8.17 Batch-type semi-aqueous cleaning (water-immiscible solvent)

The semi-aqueous option If the normal semi-aqueous path is followed, the washing stage is followed by one or more water rinses, which in layout resemble a standard batch water cleaning sequence. For example, the ﬁrst rinse may be fed with tap water, which is run to waste via a carbon absorption ﬁlter to strip any rosin carry-over (most modiﬁed alcohols are rated as biodegradable), or else is recycled in a closed loop. Alternatively, the rinsing or polishing stage may be a cascade system, with recycled demineralized water entering the exit end of the last stage. The choice of layout of the rinsing stage will be determined by the cleanliness which is required of the product. After leaving the ﬁnal rinsing stage, the boards must be dried by forced circulation of hot air. Depending on the dimensions of the plant, the hourly throughput of a semiaqueous batch cleaning installation can be reckoned between 5 sq. m to 25sq. m/ 45 sq. ft to 225 sq. ft of board area, occupying lengths from 5 m/15 ft to 6.5 m/20 ft. A simple, compact and low-cost but very eﬀective installation for small throughputs, coping with up to 20 sq. m (180 sq. ft) board area per day, consists of just two adjacent tanks, one for cleaning and one for rinsing, which can be run concurrently. It occupies a ﬂoor area of 1.5 m ; 0.75 m (60 in ; 30 in).

The solvent-only option With this option, both the cleaning and the rinsing stages operate with the same modiﬁed alcohol or similar solvent. With both stages, the solvent is recirculated through carbon and ion exchange ﬁlters to remove dissolved rosin and activator. The advantages are the convenience of operating a single-chemical system and the absence of an eﬄuent problem. The disadvantages stem from the low volatility of the solvent, which means a longer drying time. On the other hand, energy

job:LAY08 page:57 colour:1

black–text

Cleaning after soldering 317

Figure 8.18 Strategy options for cleaning with a water-miscible solvent. (a)(i) Semi-aqueous, (ii) semi-aqueous, zero efﬂuent; (b) solvent only; (c) mixed solvents – rinsing and drying in isopropanol

job:LAY08 page:58 colour:1

black–text

318 Cleaning after soldering

consumption is low: though the boiling points of the modiﬁed alcohols are well above 100 °C/212 °F, their heat of evaporation is lower than that of water.

The solvent–alcohol option Several equipment manufacturers oﬀer a layout in which the rinsing stages operate with one of the lower alcohols, normally isopropanol, with which the modiﬁed alcohols are fully miscible. The ﬁrst rinsing stage or stages operate with cold alcohol. The alcohol in the last stage boils, and the boards dwell for a short while in the vapour space in order to dry before they emerge. Naturally, the construction of such a plant must be explosion-proof, e.g. with Flutec©. which raises the cost. On the other hand, there is no eﬄuent problem and drying is rapid and consumes no extra energy.

8.6 Testing for cleanliness 8.6.1 The meaning of cleanliness Before entering the complex ﬁeld of testing circuit boards for cleanliness and of monitoring the eﬀectiveness of a given cleaning treatment, a few concepts should perhaps be clariﬁed. The ﬁrst one is the meaning of ‘clean’ in the context of a soldered printed circuit board. Absolute cleanliness of an object or a surface cannot be achieved except in a hard vacuum or in outer space. Under normal circumstances, it can only be approached asymptotically. At which point on this asymptotic curve a given object is declared as clean depends on the context: for example, ‘clean hands’, when referring to a surgeon, means something quite diﬀerent from when applied to a schoolboy. Neither cleanliness standard is arbitrary, both are purposerelated: the surgeon must not infect his patient, the schoolboy must not smudge his exercise book. The same is true for circuit boards; the link between the degree of cleanliness required from a circuit board and its function in service has been outlined in Section 8.1.1. Testing or measuring the cleanliness of a circuit board involves a further concept. Here, cleanliness means compliance with a set of quantiﬁed requirements, which are deﬁned in such a way that compliance with them can be objectively and accurately measured. As matters stand at present, two parameters have been chosen to serve as yardsticks for cleanliness. The ﬁrst one is the amount of ionizable matter per unit area which is present on a circuit board. This is a sensible choice, because under moist conditions ionizable deposits on a soldered board are liable to cause corrosion or they provide conductive paths between adjacent conductors. Leakage paths threaten the function of any electronic assembly, particularly when components with high impedance are involved. Detection of ionizable contamination is the object of the so-called MIL test, which will be discussed presently. The MIL-test method seeks out ionizable contamination only, disregarding non-ionic substances like drilling debris, oils or silicones. While these latter contaminants may not endanger the function of an aﬀected circuit board, they may well prevent the adhesion of a conformal coating which is applied to the board after cleaning.

job:LAY08 page:59 colour:1

black–text

Cleaning after soldering 319

The second parameter chosen for testing the cleanliness of a circuit board is its surface insulation resistance (SIR) over a given distance, measured with the aid of one of the several standard interlacing-comb patterns. The SIR test requires separate, dedicated test boards: these can serve to assess the cleanability of a ﬂux, the eﬀectiveness of a cleaning solvent or a cleaning system, or the eﬃcient working of a particular cleaning line in actual operation. Unless a production circuit board carries a test comb-pattern somewhere on its surface, for instance in a corner or under a component, its SIR cannot be directly determined.

8.6.2 Measuring ionic contamination (MIL test) A test procedure, known by its abbreviated name as the MIL test and now (1997) no longer oﬃcially binding, was contained in an American military speciﬁcation, issued by Naval Electronic Systems Command, Washington DC. The full speciﬁcation, with the title ‘Printed Wiring Assemblies’, last issued in 1981 under the number MIL-P-28809 A, deals with a large number of requirements which soldered and conformally coated circuit boards have to meet, one of them being the absence of ionic contamination. The speciﬁcation describes a test method which involves rinsing both sides of the circuit board to be tested with a mixture of 75% high-purity isopropanol and 25% demineralized water which has been de-ionized until its conductivity is below 0.04 S/cm. Rinsing is carried out with the aid of a polythene wash-bottle for at least one minute, and the run-oﬀ is collected in a beaker. The conductivity of the run-oﬀ, which in total should amount to 10 ml for each sq. in of circuit board washed, is measured. From this, the amount of ionizable contamination which has been washed oﬀ the board is deduced. MIL-P-28809 requires that not more than 10.0 g/sq. in (1.56 g/cm) of ionizable matter, calculated as NaCl, should be found on a board, taking all board surfaces and an estimate of the component surfaces into account. Returning to the image of the dirty hands, the MIL test is equivalent to judging the cleanliness of a pair of hands by measuring the amount of dirt in the washing water. On reﬂection it would seem that there is no reasonable or practicable alternative to this approach. The ﬁgure of 10.0 g/sq. in is of course arbitrary. A provisional British Ministry of Defence Standard (Def. St. 34, Part 6, sect. 1, 1986) sets the soluble ionic impurity limit at 1.5 g/cm (9.6 g/in) and adds the cut edges of the board to its calculated surface, together with a 10% allowance for the component surfaces. A number of commercial instruments for the measurement of ionic contamination of printed circuit assemblies are still on the market. They all share the same basic construction. The board to be tested is placed in a cuvette or cell where it is exposed to a stream of the propanol/water rinsing mixture under controlled conditions. The rinsing solvent circulates via a conductivity measuring sensor in a closed loop through the cell, and after the completion of a test cycle through a regenerating ion exchange column, to be stripped of the accumulated ionic contamination. The test cycle continues until the monitored rise in the conductivity of the rinsing solvent ﬂattens out, indicating that all of the soluble contamination has been absorbed in the solvent (Figure 8.19). While the basic construction of most contamination meters

job:LAY08 page:60 colour:1

black–text

320 Cleaning after soldering

follows this general outline, they diﬀer in their testing and evaluation strategy. Most of them are controlled by microprocessors which automatically run the tests and evaluate and record the results. The MIL test concept raises several issues: 1. It assumes that cold rinsing solvent is capable of dissolving all of the resinous residue, rendering the ionic activators which are embedded in it accessible and soluble. This is not always the case, and therefore with some instruments the solvent can be heated up to 50 °C/120 °F. 2. Non-polar impurities like the rosin itself, oil residues and some of the constituents of soldercreams or of ﬂuxes with low solids content remain ‘invisible’. 3. Many locations on SMD-populated boards are not readily accessible to the rinsing solvent. This means that the conductivity of the solvent takes a long time to reach its asymptotic maximum. The standard mixture of isopropanol and demineralized water fails to remove any of the residue from a rosin-based solder paste from a 0.15 mm/6 mil high gap, after 30 minutes immersion, at room temperature and without agitation. For this reason, several makers of MIL-test instruments have ﬁtted the test cuvette with underwater jets, which produce a ‘jacuzzi’ eﬀect. Since these modiﬁed contamination meters are more searching, but in diﬀerent degrees, cleanliness requirements ought to specify the instrument with which compliance should be veriﬁed in order to be meaningful. 4. The limiting value of 10 g/sq. in (1.56 g/cm) is arbitrary and does not reﬂect the end use of the printed circuit assembly. A graded scale of contamination limits has therefore been proposed (Table 8.15).

Figure 8.19 Working principle of a MIL contamination meter

job:LAY08 page:61 colour:1

black–text

Cleaning after soldering 321

Table 8.15 Proposal for grading MIL-test values End use Industrial electronics: no SMDs on board with SMDs Military, avionics, with high-impedance component: no SMDs on board with SMDs Ultracritical SMD assemblies, hybrids

NaCl g/cm

NaCl g/in

2.0 1.5

13 10

1.5 1.0 0.5

10 6.5 3.5

ANSI/J-STD-001B covers rquirements for cleaning and cleanliness assessment in section 8. It speciﬁes that the cleaning process must be capable of removing ionic and non-ionic contamination, and must be compatible with the materials to be cleaned. It also sets down allowable levels of surface contamination, and lists cleanliness veriﬁcation methods. Agreement on the standard has been reached in the USA, and it is being circulated internationally at the time of writing (1997).

8.6.3 Measuring surface insulation resistance (SIR) The determination of SIR requires a dedicated test-board which carries a standardized comb-pattern (Figure 8.20), unless a corner or a proportion of every production board is set aside for a test comb-pattern. The length of the tracks and the spacing between them diﬀers between the various speciﬁcations. The IPC-B-25 comb-pattern for instance prescribes spacings of 0.16, 0.25 or 0.31 mm (6.5, 10.0 or 12.5 mil). Further standards for such patterns, as well as for SIR testing in general, are for example MIL-STD-202, IPC-TM-A-600 or BELLCORE TR-TSY000078. SIR testing is normally carried out to evaluate the response of ﬂux residues to a cleaning treatment, the need for cleaning in a given manufacturing situation, the eﬀectiveness of a given cleaning treatment, or for monitoring the performance of a cleaning installation during a production run. It can of course also be used to check whether and to what degree the residue left by a ‘no-clean’ ﬂux will aﬀect the SIR of a board which has been soldered with it and not been cleaned. A SIR test can take

Figure 8.20 Comb pattern for a SIR test

job:LAY08 page:62 colour:1

black–text

322 Cleaning after soldering

considerable time and, for that reason, it is unsuitable for giving a quick alarm if things should go wrong or are suspected to be going wrong in an ongoing production. A number of commercial SIR testing instruments are on the market. Since the test programmes prescribed by the various standards require the exposure of the test boards to a variety of climatic environments, sometimes for prolonged periods, and repeated and intermittent testing, most testing instruments are provided with climatic test chambers, programmable and microprocessor controlled. Moreover, they must be capable of measuring high resistances, with orders of magnitude of up to 10 ohm. Finally, test schedules are long and complex, involving a large number of measurements which must be evaluated and recorded. For all these reasons, SIR test equipment is of a high degree of sophistication, and expensive, as is SIR testing in itself.

8.7 The future of cleaning and of fluxing The future of economic and environmentally acceptable cleaning depends on a rational and organized cooperation of several industries. Involved are principally the formulators and suppliers of solvents, and they have already come up with many useful and promising alternatives to the environmentally destructive and the ﬂammable solvents. Second in line are the suppliers of cleaning plant, who have to design and supply installations for using these solvents, and they have already put a good choice of such equipment into the hands of the user. Finally, and above all, the future of successful and economic cleaning, and perhaps the eventual abolition of cleaning, lies in the hands of the soldering industry, its customers and the suppliers of ﬂuxes and soldering equipment: 1. Both the soldering industry and its customers have started to overcome their obsession with the need to use rosin-containing ﬂuxes. Once rosin-free ﬂuxes and solder pastes can be shown convincingly to leave truly innocuous residues which are acceptable to all except justiﬁably fastidious users, and once the electronics industry accepts them as such, there will be less cleaning, and such cleaning as must still be practised will be simpler and cheaper. For many years in the past, boards soldered with resinous ﬂuxes were occasionally disﬁgured by the so-called ‘white stain’, a grey haze which covered parts or whole circuit boards after solvent-cleaning. It was never quite clear why it happened, whether it was due to the type of rosin, or the activator, the soldering conditions or faulty cleaning parameters. There were also many suggestions of how to avoid it, or how to remove it when it occurred. In any case, the ‘white stain’ disappeared together with resinous ﬂuxes. 2. Flux manufacturers are striving and will continue to strive to produce ﬂuxes which satisfy the no-clean requirements of all but the most fastidious classes of users of electronic equipment. 3. The makers of soldering machines are equally striving to perfect soldering equipment which permits soldering with minimum-residue non-corrosive

job:LAY08 page:63 colour:1

black–text

Cleaning after soldering 323

ﬂuxes. Systems, which permit soldering without any ﬂux at all in a plasma atmosphere still have to prove their commercial viability at the time of writing (1997).

8.8 References 1. Lea, C. (1992) After CFCs? Electrochemical Publications, Ayr, Scotland, p. 102 and (1993) Report to Soldering Science and Technology Club, 9 December, Teddington, England. 2. Lea, C. (1988) A Scientiﬁc Guide to Surface Mount Technology, Electrochemical Publications, Ayr, Scotland, p. 436. 3. Lea, C. (1988) loc. cit., p. 438. 4. Lea, C. (1992) loc. cit., p. 131. 5. Ellis, B. N. (1986) Cleaning and Contamination of Electronics Components and Assemblies. Electrochemical Publications, Ayr, Scotland, Appendix 1. 6. Lea, C. (1992) loc. cit., p. 132. 7. Zado, M. F. (1983) Eﬀects of Non-Ionic Watersoluble Flux Residues. Western Electric Engineer, 27, 1, pp. 41–48. 8. US Patent 4.960.236. 9. Lea, C. (1992) loc. cit., p. 88. 10. Richards, B. P., Prichard, D. J. and Footner, P. K. (1990) Assessing Cleaning Options. Electronic Production, London, Dec. 1990, 19, 12, pp. 25–26. 11. Boswell, D. (1990) Surface Mount Components and the Ozone Layer Depletion Problem. Proc. SMTCON, Atlantic City, NJ, pp. 103–106. 12. Lea, C. (1988) loc. cit., p. 449. 13. Lea, C. (1988) loc. cit., p. 447. 14. Richard, B. P., Burton, P. and Footner, P. K. (1990) The Eﬀects of Ultrasonic Cleaning on Device Degradation. Circuit World, 16, 3, pp. 20–25. 15. Beine, H. (1993) Entirely without Flux (in German). Productronic (Germany), 6, pp. 28–29. 16. Turbini, L. J., Eagle, J. G. and Stark, T. J. (1979) A comparison of removal of activated rosin ﬂux by selected solvents. Proc. IPC Fall Meeting, San Francisco, CA, Techn. Paper IPC-TP-305. 17. Cabelka, T. D. and Archer, W. L. (1985) Cleaning, What Really Counts. Proc. ISM Intern. Microel. Symposium, Anaheim, CA, pp. 520–528. 18. Ellis, B. N. (1986) loc. cit., p. 187. 19. Lessmann, K. (1996) Cleaning of Boards with BGAs, ﬂip-chips and SMDs. Productronic 12/96, pp. 22–24 (in German). 20. Ellis, B. N. (1986) loc. cit., p. 188. 21. Ellis, B. N. (1986) loc. cit., pp. 170, 182. 22. Lea, C. (1992) loc. cit., Chapters 1 and 2. 23. Seinfeld, J. H. (1986) Atmospheric Chemistry and Physics of Air Pollution, Wiley, New York. 24. UK Stratospheric Ozone Review Group (1988) Stratospheric Ozone, HMSO, London.

job:LAY08 page:64 colour:1

black–text

324 Cleaning after soldering

25. 26. 27. 28. 29. 30. 31. 32. 33. 34. 35. 36. 37. 38. 39. 40. 41.

Polar Ozone Workshop (1988) NASA Conference Publication 10014. Jones, R. R. (1987) Ozone Depletion and Cancer Risk. Lancet, pp. 443–446. New Scientist, London, 22 Oct. 1988. Lea, C. (1992) loc. cit., Chapter 4. Davidson, G. (1992) Icy Prospects for a Warmer World. New Scientist, 8 August 1992, pp. 23–26. Murphy, K. P. (1990) The HCFC Alternative for CFC-113. Proc. First CFC Alternatives Conference, San Francisco, CA. Tickell, O. Up in the Air. New Scientist, 20 October 1990, pp. 41–43. Slinn, D. S. L. and Baxter, B. H. (1990) Alcohol Cleaning under a Nonﬂammable Perﬂuorocarbon Vapour Blanket. Proc. Nepcon West ’90, Anaheim, CA, pp. 1810–1819. Ellis, B. N. (1986) loc. cit., pp. 205–206. Andrus, J. J. (1991) PWA Aqueous and Semi-Aqueous Cleaning. Proc. Nepcon West 91, Anaheim, CA, pp. 281–291. Ellis, B. N. (1986) loc. cit., p. 211. Ellis, B. N. (1986) loc. cit., pp. 220–225. Dishart, K. T. and Wolﬀ, M. C. (1990) Advantages and Process Options of Hydrocarbon Based Formulations in Semi-queous Cleaning. Proc. NEPCON West ’90, Anaheim, CA, pp. 513–527. Bodhurta (1980) Industrial Explosion Prevention and Protection, McGraw-Hill, New York. Dishart, K. T. and Wolf, M. C. (1990) Circuit Assemblers can have a Reliable Future with New Cleaning Techniques. Proc. Electronics Manufacturing and the Environment, Bournemouth, UK. Ellis, B. N. (1986) loc. cit., p. 260. Hymes, L. (1997) ANSIJ-STD-001B: Process and Acceptance Requirements, Circuits Assembly, January, p. 38.

job:LAY09 page:1 colour:1

black–text

9 Quality control and inspection

9.1 The meaning of ‘quality’ The term ‘quality’, when applied to a technical product, can mean a number of diﬀerent things, depending on the context in which the word is used. Some of them are listed below: 1. It can be used as a yardstick when comparing the same type of product made by diﬀerent manufacturers, or a number of products in the same class. In this context, ‘quality’ expresses how closely the product approaches perfection of functioning, material speciﬁcation, ﬁnish, appearance and so on. 2. It can be used for quantifying the working eﬃciency of a technical product, or the relationship between its cost and its performance. 3. It can be a measure of the capability of a technical product to meet a set of functional requirements, which may have been formulated by the maker, or which the purchaser can justiﬁably expect. In simple terms: Does it work as I expect it, or have been led to expect, and for how long will it work? In this chapter, the word ‘quality’ will be used in this last sense.

9.1.1 Product quality and product reliability The quality which a ﬁnished technical product must possess is only meaningful, and can only be achieved, if all the tasks which it will have to fulﬁl, the eﬃciency and perhaps the speed at which it must work, the circumstances under which it will have to function, and its reliability are precisely speciﬁed. The formulation of these demands will depend on several factors: 1. Company-speciﬁc considerations like: Product or market philosophy Product or quality image What does the competition oﬀer?

job:LAY09 page:2 colour:1

black–text

326 Quality control and inspection

2. Application-speciﬁc considerations. Here, quality demands can be split into ‘ability to function’ and ‘reliability’, both of them in the environment in which the product will be used.

9.1.2 Classification according to reliability requirements The following classiﬁcation groups electronic products according to their reliability demands, and to some extent the consequences of a premature or unforeseen failure: I

Professional equipment, highest demands Space and satellite technology Avionics, commercial and military Telecom, submarine Telecom, military and weapons systems Medical, life support systems

II

Professional and commercial equipment, very high demands Automotive, under hood, engine management, ABS, air-bag Telecom, commercial

III

Professional equipment, high demands Industrial electronics, high quality Computers Telecom, private

IV

Professional equipment, medium demands Industrial electronics, general Medical electronics, general Computer peripherals, medium price range

V

Professional equipment, low demands Oﬃce equipment Measuring instruments, general use

VI

Semi-professional equipment Professional audio and video Automobile, passenger compartment Entertainment electronics, high-quality Desktop and laptop electronics Consumer electronics, high quality

VII Consumer electronics, general Entertainment electronics, domestic Household equipment Calculators Toys

job:LAY09 page:3 colour:1

black–text

Quality control and inspection 327

‘Ability to function’ in the context of deﬁned quality requirements means that the equipment must be capable of working, not only at the time when it reaches the customer (‘zero hour quality’ or ‘acceptance quality level’) but also under its speciﬁed worst-case operating conditions. ‘Reliability’ in the context of quality can be deﬁned as ‘the ability of a product to function as expected for an expected period of time, without exceeding an expected failure level’. A discussion of the reliability of an electronic assembly as such goes beyond the purpose of this book. The importance of deﬁning, measuring and safeguarding the quality and reliability of technical products has been recognized in recent years, as witnessed by the large number of relevant national and international standards speciﬁcations (e.g. ISO 9001–9003, and MIL-Q-9858A). Quality and reliability in the context of industrial manufacture have become the subjects of academic teaching and research, and of a growing number of publications.

What interests us here are the quality and reliability of the soldered joints of an electronic assembly. If just one of its joints is not soldered, or if one bridge between neighbouring conductors causes a short circuit, the whole assembly malfunctions or does not work at all. If one of the joints fails in service, the assembly begins to malfunction or stops working altogether. The reliability of soldered joints is dealt with in detail in Section 3.3.5. See also References 22 and 23 of Chapter 3.

9.2 Soldering success and soldering perfection 9.2.1 Soldering success and soldering faults In soldering, two things matter before all others, as has been said several times already: 1. The solder must reach all the places where it is required, and it must stay there: there must be no open joints. 2. Solder must not remain anywhere where its presence causes a short circuit. Soldering success shall be considered to have been achieved if both requirements have been met. If one or both remain unfulﬁlled, success has not been achieved and a ‘soldering fault’ has occurred: the circuit board cannot function. In practical terms, a soldering fault is caused by one or more of the following.

Open joints The electrical continuity of the circuit requires that no joint remains open. With wavesoldering, ﬁlling of every joint can be diﬃcult, and it requires the optimization of both the board layout (Section 6.4) and of the ﬂowpattern of the solderwave (Section 4.4.4) to persuade the solder to reach every joint. With reﬂowsoldering, every footprint must receive the correct solder depot and enough ﬂux, be it as paste printdown or as a depot of solid solder. Also, every joint must have reached the

job:LAY09 page:4 colour:1

black–text

328 Quality control and inspection

required minimum temperature needed to melt the solder, and to connect the joint members. Brieﬂy, there must not be a single skipped or open joint on any one board. Thus, for example, a footprint without paste or solder depot must be considered a soldering fault even before the board is soldered: the solder never got to where it is required. If there was insuﬃcient solder paste on a footprint to reach the bent leg of a multilead device (lack of coplanarity), the joint will remain open. With a reﬂowed joint on a PLCC where wicking has occurred, the solder did not remain in its appointed place and the joint opens during soldering. In all cases, soldering success has not been achieved (Figure 9.1). The correct position of every component belongs in the same category of soldering success. With SMDs, every component must sit and stay in its correct place. Seriously misaligned components, or components which have ‘ﬂoated’ or ‘tombstoned’, constitute soldering faults. It is convenient to include the placement of the components here, so that their correct identity, and in the case of active components their correct orientation, also counts under ‘soldering success’ (Figure 9.2). It has been estimated that on average, 50% of all soldering faults are due to faulty joints, such as bridging or open joints, while about 30% are due to components having been misplaced (wrong polarity of an active component, wrong identity, or missing), with another 10% being due to faulty passive components.

Figure 9.1 Open joints caused by: (a) lack of coplanarity; (b) wicking

Figure 9.2 Displaced and misplaced components

job:LAY09 page:5 colour:1

black–text

Quality control and inspection 329

Bridges and solderballs A circuit board cannot function if it contains a short circuit, i.e. a solder bridge. Wavesoldering without bridging demands special techniques, such as optimizing the conﬁguration of the wave (Section 4.4.4) and the board layout (Section 6.4.1). Boards with a pitch below 1 mm40/mil are diﬃcult to wavesolder without faults, unless soldered in a nitrogen atmosphere. With reﬂowsoldering, especially of ﬁne-pitch boards, the type of paste and its quality and the precision of the printing of it are key factors in achieving soldering success (Section 5.2.3). Solderballs need not necessarily be classed as soldering faults. If a solderball sits between two neighbouring footprints on a ﬁne-pitch board, it can constitute a shortcircuit, and prevents the board from functioning. Elsewhere, solderballs represent potential shortcircuits, and as such reduce the reliability to an extent which is diﬃcult to quantify. How solderballs are to be regarded is very much a matter of individual company policy. Even a single soldering fault on a board prevents it from functioning, and there are only two options: correct it or scrap the board. The choice between them depends on several factors, which will be discussed in Section 10.1. What must be stressed here is the following.

The nature of the soldering fault The existence of a soldering fault is an objective fact. A joint is either soldered or it is not soldered. A bridge is either there or else there is none. The soldering fault presents a ‘yes/no situation’ (Figure 9.3). To pronounce upon it is in the nature of a verdict upon an observed fact, and two or more inspectors must necessarily reach the same verdict. Because of its objective ‘yes/no’ nature, the success/fault verdict can be entrusted to an automatic quality assessment system, which may be based on opto-electronic inspection or functional electronic testing (Section 9.5.5).

Figure 9.3 The yes/no nature of soldering success

job:LAY09 page:6 colour:1

black–text

330 Quality control and inspection

9.2.2 Soldering perfection and soldering imperfections Assessing soldering perfection presents an inspector with a fundamentally diﬀerent situation: imperfect soldering does not prevent the aﬀected circuit board from functioning, but it can be seen as endangering or reducing its reliability. It may also aﬀect its saleability where the buyer has speciﬁed precise criteria. Criteria for perfection may include the following features (Figure 9.4): Wetting angle Joint proﬁle and amount of solder on a joint Alignment or displacement of components If an imperfection disqualiﬁes the product in the eyes of the customer, it becomes a soldering fault, because it makes the product unsaleable. A product which is unsaleable does not work as far as the vendor is concerned. Being saleable is the ﬁrst function any manufactured product must fulﬁl. A product which is not saleable in the market for which it has been made does not function from the point of view of its maker (unless it is still saleable elsewhere for less proﬁt or at a loss). The oﬀending feature must be corrected, or else the product must be scrapped. In contrast to the unequivocal yes/no verdict upon the veriﬁable fact of soldering success or fault, a pronouncement upon the soldering perfection of a joint represents a judgement, which is necessarily subjective. The judgements arrived at by diﬀerent inspectors represent points along a scale, which separate the ‘perfect’ or ‘acceptable’ from the ‘imperfect’ or ‘non-acceptable’ (Figure 9.5). On either side of the accept/reject divide are areas of doubtful acceptability and false alarm. It has been found that only 44% of the quality judgements on the same set of soldered boards, made on two diﬀerent days by the same inspector, agree with one another. The quality judgements of the same boards made by two diﬀerent inspectors overlap by only 25%, while those made by three inspectors overlap by 14% (A. T. & T. Bell, Burlington, N. Carolina). To sum up: deciding between soldering success and a soldering fault amounts to a verdict. Deciding whether soldering perfection has been approached suﬃciently is a matter of judgement, and the making of this decision can be automated only with great diﬃculty.

The blowhole problem Blowholes in wavesoldered throughplated joints, caused by ‘gassing’ of the walls of the hole, are a special form of imperfection (Figure 9.6).

Figure 9.4 Some soldering imperfections

job:LAY09 page:7 colour:1

black–text

Quality control and inspection 331

Figure 9.5 The perfect/imperfect judgement scale

Figure 9.6 Blowholes in a throughplated wavesoldered joint

The causes of gassing of throughplated holes, and the measures which are needed in order to avoid it, are by now well understood. Gassing can be prevented by ensuring the smoothness of the drilled holes and the continuity and adequate thickness of the copper plating on their walls. It can be cured by a suitable heat treatment of boards which are liable to form blowholes before using them.

job:LAY09 page:8 colour:1

black–text

332 Quality control and inspection

Because blowholes do not interfere with the functioning of a circuit board, they are soldering imperfections rather than soldering faults, though their presence or absence is an unequivocal yes/no situation. Searching investigations have shown that they do not aﬀect the life expectancy of joints or their reliability, in any way. Corrective soldering can only mask, but not ﬁll, a porous hole, and it is bound to shorten the life expectancy of the joint.

9.3 Practical examples of soldering faults The nature of a soldering fault means that a circuit board is faulty and cannot function until every single fault on it has been corrected. Therefore, the most important task of any quality-control system is to ﬁnd every one of them. In Tables 9.1–9.3, the various types of soldering faults are listed and illustrated. For completeness’ sake, faulty throughplated joints are included.

9.4 The ideal and the imperfect joint The criteria of perfection in a soldered joint go back to the days of handsoldering. They have to do with two parameters: ﬁrst, the wetting angle between the solder and the substrate; and secondly the amount of solder in or on the joint. Together, they determine the so-called joint proﬁle. The ideal handsoldered joint has a ‘lean’ proﬁle: the solder meniscus has a concave shape, so that the sharp wetting angle can be seen clearly. Also, the contours of the ends of the joint members must be visible, so that an inspector can be sure that, in the case of the leadwires of inserted components, the wires do in fact project through the hole and that all leads have been properly tinned (Figure 9.7). The criteria of perfection of wavesoldered and reﬂowsoldered joints on circuit boards go back to these early days. They deal with surface contours, surface areas, the relationships between distances. It is possible to base judgements like good/bad, acceptable/unacceptable or beautiful/ugly on these criteria, provided every inspector can refer to a set of pictures or samples of ‘perfect’ and ‘imperfect’ joints. It is diﬃcult and certainly expensive to derive a clear yes/no verdict unless precise, time-consuming and therefore expensive measurements of individual joints are made. It is equally diﬃcult, if not impossible, to base an automatic, opto-electronic inspection system on a ‘good/bad’ or ‘beautiful/ugly’ situation instead of a ‘yes/no’ one. Tables 9.4 and 9.5 illustrate practical examples of perfect and imperfect joints. There is one instance where an imperfection can become a fault: ‘fat’ joints with too much solder at the ends of a melf or chip-capacitor can cause the ceramic body of the component to crack under the mechanical stresses caused by temperature ﬂuctuations during service. Fat joints hold the component as in a vice, lean joints can yield.

9.5 Inspection No circuit board should leave its soldering stage without having been inspected. To inspect means to view or examine closely and critically. This implies that inspection is

job:LAY09 page:9 colour:1

black–text

Quality control and inspection 333

Table 9.1 Soldering faults I: Open joints Soldering method

Fault (C, if correction is possible)

Possible cause

Wave

No solder on both footprint and wire or lead (C)

Solderwave did not reach the joint. (If the joint was not ﬂuxed, it is covered by lumps of solder); or the solderwave did not overcome the shadow eﬀect, because either layout or waveshape was unsuitable. Remedy: improve waveshape or layout, or change orientation of the board towards the direction of travel. No paste on footprint. Check screen or stencil for blockage

Reﬂow

Solder on wire or lead, but not on land or footprint (C, but diﬃcult and costly) Defect unlikely

With wired components: land unsolderable through faulty solermask or misplaced marking With SMDs, as above or misplaced adhesive

Reﬂow

Wicking (C)

Gap between leg and footprint, due to lack of coplanarity of leads. Remedy: quality control before placement.

Reﬂow

Wave

Unsuitable soldering parameters. Remedy: put right, or choose paste with higher-melting solder

more than ‘just having a look’. To be meaningful and cost eﬀective, every inspection procedure must have a set of well-deﬁned targets or criteria, preferably in the form of written, and sometimes illustrated, lists, or explicit software when automatic image analysis is used. The distinction between ‘soldering success’ and ‘soldering perfection’ (Section 9.2) simpliﬁes the task of inspection, in the same way that it is easier to umpire a horse race than a beauty contest. Without an umpire, both race and contest are pointless. Without inspection, a manufacturing process like the soldering of electronic circuit boards is incomplete. There is a basic diﬀerence between the inspection of engineering products like a crankshaft and the inspection of a soldered circuit board. The dimensions of the

job:LAY09 page:10 colour:1

black–text

334 Quality control and inspection

Table 9.2 Soldering faults II: Bridging and solderballs Soldering method

Fault

Possible cause

Wave

Bridging between neighbouring lands or footprints (C)

Solderballs under melfs or chips (C: de-solder and resolder aﬀected SMDs)

Conveyor speed too high; unsuitable wave geometry. Flux too thin or too weak. Remedy: check (and change) ﬂux, or soldering parameters; if layout unsuitable for wavesoldering, change orientation of board in carriage (does not always work) As above, or add solderthieves to layout. Change direction of travel by 90° Paste tends to form solderballs. Remedy: carry out solderballing test, and if necessary use fresh paste. Paste-printdown too thick: check and if necessary, correct Can happen with controlled atmosphere machines. Remedy: change to diﬀerent or slightly thicker ﬂux. Slow down conveyor Paste forms solderballs or spits. Remedy: if solderballing test conﬁrms, use fresh paste Printdown too large or too thick. Remedy: check and correct screen or stencil

Wave

Scattered solderballs, or ‘spider’s webs’. (C: pick up with tip of soldering iron)

Flux too thin, or insuﬃciently pre-dried. Remedy: check and, if necessary, adjust

Reﬂow

Scattered solderballs. (C: as above)

Paste spits because it has picked up moisture, or temperature proﬁle too steep. Remedy: check and, if necessary, use fresh paste or adjust temperature proﬁle of reﬂow oven Note: As pointed out above, solderballs do not necessarily constitute a soldering fault, unless they are loose, or are liable to become loose, and can roll about on the board

Ditto, with ﬁne-pitch multileads Reﬂow

As above (C)

Wave

Solderballs near footprints (C)

Reﬂow

job:LAY09 page:11 colour:1

black–text

Quality control and inspection 335

Table 9.3 Soldering faults III: Displaced components Soldering method

Fault

Possible cause

Reﬂow

One or more leads or faces fail to connect with their footprints (C: desolder and resolder by hand)

Serious misplacement or ﬂoating. Remedies: check pick-and-place equipment; with chips or melfs, lack of solderability at one end, or lack of symmetry between footprints

Floating or tombstoning (C): desolder and resolder

One end less solderable than the other. One end solders later than the other because of asymmetry of size or thermal behaviour of footprints. Remedy: check quality of components or correct layout fault

Figure 9.7 The ideal handsoldered joint

former can be expressed numerically, and readily and automatically compared against prescribed standards, within a given set of tolerances. It is very diﬃcult, and certainly expensive, to ascribe numerical values to a soldered joint. Hence the need for visual, optical or functional inspection of soldered circuit boards.

9.5.1 When to inspect Inspecting every soldered board when it has reached the end of the production line is certainly necessary, but it is not enough. Unless intermediate inspections are carried out after various stages of production, errors or defects which are carried over into the next production stage can be very expensive to correct later. The printdown of the adhesive which ﬁxes SMDs to the board before wavesoldering must be checked for completeness and correct placement. Missing adhesive means a lost SMD; misplaced adhesive can make adjacent footprints unsolderable. Mistakes in adhesive printdown are very diﬃcult and expensive to correct once the joints have been cured. Most adhesives are given conspicuous, sometimes luminescent, colouring to make visual or opto-electronic automatic inspection easier. Similarly, the correct printdown of solder paste must be checked before the

job:LAY09 page:12 colour:1

black–text

336 Quality control and inspection

Table 9.4 Too much or too little solder Soldering method

Defect

Judgement and possible remedy

Wave or Reﬂow Wave

None H H +H 1 much ! solder % Too H 9H +H 1 ! %

The ideal joint

Wave Reﬂow

Too little solder H : 30%(H + H ) 1 ! %

Wave Reﬂow

Too little solder W : 75%W 1 !

Reﬂow

Too little solder on PLCC J-leg W : 50%W 1 !

Acceptability depends on the product category and the customer. Remedy: change machine parameters, lower the wave, speed up the conveyor Acceptability as above. Remedy: raise wave, slow down conveyor, more paste in case of reﬂow Acceptability as above. Remedy: check solderability of footprint and component Acceptability as above. Remedy: see ‘wicking’

Table 9.5 Unsatisfactory wetting angle; displaced components Wave Reﬂow

Angle 990°

Acceptability depends on product category and customer

D 9 50%W

May be unacceptable with ﬁne-pitch layout. In that case, count as soldering fault

SMDs are placed on the board. Faults are easily corrected at this stage. If detected after soldering in the form of empty joints or bridges, the cost of correction rises by at least one order of magnitude. With hand-placed components, a ﬁnal check before the soldering stage is advisable. Much mechanized pick-and-place equipment is equipped with integrated checks for correct identity, polarity and placement of the components (Section 7.4). If it is not, a ﬁnal visual or optical check before soldering is worth while.

job:LAY09 page:13 colour:1

black–text

Quality control and inspection 337

9.5.2 Visual inspection It is useful to distinguish between two basic types of visual inspection, which one could call the ‘general picture’ and the ‘detailed inspection’.

The general picture In small-scale production, where boards are soldered individually, by hand or on benchtop equipment, the operator will naturally look at every single board before it leaves his workstation. If there is an obvious fault due to a malfunctioning of his equipment, or a defective board, he or she will put matters right before carrying on soldering. With in-line soldering, the operator, or supervisor in charge of the soldering line, whether wave or reﬂow, should have a brief look at the boards leaving the line at regular intervals, perhaps at one board in every ten, in order to ensure that the line is running normally. Obvious major faults might be unﬂuxed areas or uneven soldering because of an unsteady solderwave, or reﬂowed boards which are scorched, or did not get hot enough for the paste to melt on all joints. Unless such disasters are spotted before many boards reach the next inspection station, the line may have been producing a good deal of expensive scrap.

The detailed inspection The manner of the detailed visual inspection and the equipment used for it depend very much on the type and volume of production and the size of the boards. The type and speciﬁcation of optical inspection equipment ranges from simple or illuminated magniﬁers with a power of about ﬁve times, to sophisticated apparatus with zoom optics, binocular operation, stereoscopic vision, and facilities to look at the J-legs of PLCCs at an angle. The advent of low-priced, small, readily manipulated video systems has added a new dimension to visual inspection. As a general rule, optical systems where the operator has to look into a single eyepiece, or a binocular, which forces him to keep his head in a ﬁxed position, are more fatiguing to operate than systems which show the object of observation on a screen. A good and ﬂexible system of illumination is essential with all optical inspection methods. An easily operated handling system of the boards under test is equally important. With a number of systems, boards are mounted on a movable xy table, which allows for overall scanning, or indexing into preset positions where certain recurring faults tend to occur. Recent studies pinpoint the problems of visual inspection: operators, often female, are under increasing stress, mental rather than physical, as boards get more complex and the pitch gets ﬁner. They rate their stress factors in descending order as intense concentration, burden of responsibility and time pressure. Faulty ergonomics and noise can be additional problems. With ﬁne-pitch layouts and components, the rate of inspection falls dramatically, and the stress is greater. The solution is seen in systems where automated opto-electronic inspection precedes, and is linked with, inspection by a closely integrated team of about three operators, who visually inspect and manually correct faulty joints at the same time.

job:LAY09 page:14 colour:1

black–text

338 Quality control and inspection

The value of linking visual inspection with corrective soldering is increasingly recognized and practised (Section 10.1).

9.5.3 Automated opto-electronic inspection Unless the distinction between ‘soldering success’ and ‘soldering perfection’ is made, automatic inspection must recognize both of them and be able to evaluate features like joint contours. This demands expensive systems of great complexity. If the judgement on soldering perfection is omitted, existing technology, which is constantly being reﬁned, permits relatively straightforward practical solutions for automatically recognizing footprints without solder paste, empty joints or the presence of bridges or solderballs. These systems are based on video scanning of a board surface, combined with an automatic comparison between the actual image and the ideal image of a faultless board. Equipment which operates fast enough to keep up with in-line soldering machines and reﬂow installations is commercially available. Opto-electronic systems are able to recognize the following soldering failures: Missing, misplaced or defective printdown of solder paste Missing or misplaced adhesive Missing, misplaced or displaced components Bridges, ‘spider’s webs’ and solderballs A recently developed automatic opto-electronic inspection system does not require a pre-programmed ‘ideal’ image of a faultless board, but creates its own ‘learning curve’ by evaluating parameters such as shape of solder-ﬁllet, identity and dislocation of components, bridges etc. ‘Self-learning’ automated visual inspection equipment is expected to become commercially available before the end of 1997.

9.5.4 X-ray inspection X-ray inspection represents an optical system, which operates at two levels. The board with its joints is scanned by penetrating X-ray radiation, which is absorbed most strongly by the lead-containing solder in either joints or paste printdown, less so by metallic conductors, ICs and other semiconductor devices, and least of all by organic substances like FR4 and ceramic or plastic component housings. The resulting X-ray image is converted to a monochrome image in the visible range, which can be evaluated visually by an operator, or processed photo-electronically as described above, and compared with the image of a faultless board. One of the problems which might perhaps be encountered in this context with lead-free solders (Section 3.2.3) is the reduced contrast between such a solder and its surroundings in an X-ray image, unless the solder contains bismuth. X-ray images are shadowgraphs. In the last decade, X-ray sources have been developed with emitter-spots small enough to provide shadows of suﬃcient sharpness to allow even micrographic evaluation. By controlling the voltage applied to

job:LAY09 page:15 colour:1

black–text

Quality control and inspection 339

the X-ray tube, the penetrating characteristics of the radiation can be adjusted to suit the features which need to be examined. X-rays show up the solder in the joint itself, which is a great advantage, but the image must be sensibly interpreted: as has been explained in Section 3.6.3 (Figure 3.19), almost all capillary joints contain voids. A distinction must be made here between two kinds of joint porosity. If the porosity appears as voids which are surrounded by solder, it is safe to conclude that the solder has wetted the joint surfaces with a satisfactory, sharp wetting angle. This type of porous joint will be as reliable as a completely ﬁlled one. If, however, the solder in the joint gap appears as an archipelago of separate islands, one of the joint surfaces is likely to have dewetted (Figure 9.8), and reliability of the joint is impaired. Image processing software might well be devised to be able to distinguish between these two types of porosity, where the solder forms either a continuous or a discontinuous phase, and raise the alarm with dewetted capillary joints. X-ray inspection is the only option for inspecting joints underneath BGAs and ﬂip-chips (see Section 2.2). To spot an open joint between a solderbump and the paste print-down on the board is diﬃcult, because the bump itself will produce a circular shadow. A strategy to overcome this problem has been proposed by N. Manson. The pads on the board and the paste print-down are both given diamond-shaped or square outlines. A square shadow means that the paste has been melted, but has not been drawn into the joint. A round X-ray shadow indicates a correctly formed joint. It should not be diﬃcult to program an automatic optoelectronic X-ray inspection system to recognize this type of defect. The discovery of an open joint underneath a ﬂip-chip poses a problem: once the underﬁll underneath the chip has set, the chip cannot be removed without damaging the board, and the cost of scrapping the board must be balanced against the costly and delicate microsurgery needed to clear away the underﬁll. There is no reason why the adhesive for ﬁxing SMDs prior to wavesoldering should not be made opaque to X-rays by the addition of a ﬁller like a barium compound. Thus, X-ray scanning could be used for the intermediate scanning of boards for the correct presence of either adhesive or solder paste before placing the components. X-rays are equally suitable for checking the correct placement of components before the boards enter their soldering stage. The virtues of such intermediate inspections between successive manufacturing stages are obvious.

Figure 9.8 X-ray images of capillary joints. (a) Innocuous cavities caused by trapped air or vapour; (b) pattern of unsoundness indicating a wetting or solderability problem. Solder, void

job:LAY09 page:16 colour:1

black–text

340 Quality control and inspection

9.5.5 Electronic inspection Testing the correct functioning of a circuit board by electronic means has developed into a complex technology which is outside the scope of this book. ATE testing with an array of probes, not so long ago a cause of concern for solder paste formulators, is still being practised but on a declining scale. The growing number of functions, crowded not only on to a board, but also into individual components and MCMs, demand that the board itself is designed for testability – for example by methods such as ‘boundary scanning’. Dedicated contact points are designed into the board circuitry, from which the board can be interrogated for its functions, as well as for the existence and location of soldering faults. Functional testing of soldered boards has become an important capital- and cost-intensive part of electronic production. It is still in a state of constant further development.

9.5.6 Thermographic inspection For the sake of completeness, the so-called thermographic methods of sequentially checking all the joints on a board for their quality by measuring their thermal capacity must be mentioned here. The basic idea is to ﬁnd out whether there is too much or too little solder on any given joint, or whether the joint is open, by measuring its thermal capacity and comparing it with an ideal value. In order to do this, a short, accurately dosed pulse of Nd: YAG laser energy is focused onto the joint, and its temperature rise is picked up by a fast-response pyrometer and recorded. Naturally, the reﬂective properties of the solder ﬁllet on which the laser beam is focused also enter into the result and the evaluation of the test. The method requires a laser scan of great accuracy and, for a start, a board with every joint of an adequate degree of perfection – a so-called golden board – so that for every type of board, a library of ideal thermal capacities can be established. The Vanzetti method was and still is used, especially with military and space electronics. Other, similar, thermographic testing systems have been developed in Europe, but are not commercially available at the time of writing (1997).

9.6 References 1. Birolini, A. (1992) Guidelines for the development and design for quality, reliability and maintainability. Report Z4, 10 January 1992, Swiss Fed. Inst. Technology, Zurich. 2. Lea, C. et al. (1987) The Scientiﬁc Framework leading to the recommendations for the elimination of Blowholing in PTH Solder Fillets. Circuit World, 13, No. 3, pp. 11–20. 3. Lea, C. (1990) The harmfulness of reworking cosmetically defective joints. Soldering and SMT, No. 5, pp. 4–9. 4. Strauss, R. (1992) The Diﬀerence between ‘Soldering Success’ and ‘Soldering Quality’; Its Signiﬁcance for Quality Control and Corrective Soldering. Proc. 6th Intern. Conf. Interconnection Technol. in Electronics, Fellbach, DVS Report 141, Duesseldorf, Germany (in German).

job:LAY09 page:17 colour:1

black–text

Quality control and inspection 341

5. Vanzetti, R. (1984) Automatic Laser Inspection System for Solder-Joint Integrity Evaluation. Proc. 3rd PC World Convention, Washington DC, Paper WC III-44. 6. Geiler, H. D., Karge, H. and Kowalski, P. (1992) Possibilities and Limits of Modulated Thermographic Spectroscopy for the Nondestructive Testing of Joints. 6th International Conference on Interconnection Technology in Electronics, Fellbach. D.V.S. Report 141, Duesseldorf, Germany, pp. 111–112. 7. Graumueller, B. et al. (1997) Non-destructive Examination of Soldered Joints, VTE (3) June, pp. 145–149 (in German). 8. Manson, N. (1996) Qualiﬁcation Requires Keen Vision. Electronic Production, July/August, pp. 15–16.

job:LAY10 page:2 colour:1

black–text

10 Rework

10.1 The unavoidability of rework 10.1.1 Rework in the production process In our imperfect world, zero-fault soldering does not exist. Soldering faults will occur, and because even one single fault makes a board unusable, each must be corrected by rework or corrective soldering. It would be a mistake to regard rework as an unavoidable, tedious adjunct to electronic production. On the contrary, it is an essential link in the production chain. Unless it is taken seriously, properly organized, managed, monitored and integrated into production, reworking the soldered boards may well cost more than soldering them in the ﬁrst place. On the other hand, if rework is monitored systematically, so as to lead to a learning curve and a fault catalogue for each type of board, its cost can be reduced to its unavoidable minimum. At the same time, the fault catalogue will form a valuable tool, for use by management, designers, buying departments and quality managers. This applies equally to a large organization or manufacturing unit with many soldering lines as to a small manufacturer with a handful of employees. Every rework operation must involve three steps: 1. Diagnosis Having located a fault which must be put right, try to ﬁnd out ﬁrst why it has occurred. Don’t start working on it, until you have satisﬁed yourself that you have found the answer, and have made a record of it. Otherwise, you may destroy vital evidence, which could have helped to prevent the fault recurring again. 2. Remedy Put the fault right. 3. Prevention Make sure that whoever in the organization could or should have prevented the fault from occurring, knows what you have found and done about it, and if possible that this information is recorded. Procedures and information technologies to take care of that are commercially available (Section 10.5.2). The rework rate can be regarded as the fever thermometer of a manufacturing line. If nobody cares to read it, the patient may well be moribund before anybody has noticed that he is sick.

job:LAY10 page:3 colour:1

black–text

Rework 343

10.1.2 Desoldering and resoldering Rework itself often involves two closely linked operations: if the correction of a fault requires the removal of a faulty, misplaced or dislodged component and its replacement, the desoldering and resoldering operations which this implies should follow closely upon one another. Removing bridges and, if necessary, solderballs, are simple desoldering operations. Desoldering leaded components from throughplated holes requires soldering irons which can suck the solder out of the hole. With SMDs, the removal of a defective component and its replacement with a new one can often be carried out with one and the same tool. With the desoldering of wavesoldered SMDs, separating the glued joint underneath the component is an additional operation. Open joints are normally ﬁlled with a small temperature-controlled handsoldering iron.

10.2 Basic considerations 10.2.1 Metallurgical and mechanical consequences of rework A reworked joint is never as good as the ﬁrst joint would have been had it not needed to be replaced or corrected. The reasons are found principally in the metallurgy of joint formation. Furthermore, the additional thermal, and sometimes mechanical, stresses of resoldering may easily weaken the bond between footprint and board. A lifted footprint is one of the most serious types of damage, caused by getting a joint too hot or heating it for too long during desoldering. Repairing a lifted footprint is possible, but it is expensive, takes time, and the board will never be as good again as it was in the ﬁrst place.

Industrial experience conﬁrms the damaging eﬀect of corrective soldering. So did a cooperative research project carried out by a number of industrial companies in the UK under the auspices of the National Physical Laboratory.

The latter counted the number of through-hole joints on standardized sample boards with 2000 joints each which showed visible cracks after they had been reworked with a soldering iron under controlled conditions and then exposed to up to 1000 temperature cycles between −20 °C/−4 °F and 100 °C/212 °F. For comparison, boards which had not been reworked were given the same thermal treatment. Some of the results are given in Table 10.1. Two conclusions are clear: 1. The longer the rework contact time of the soldering-iron bit, the more soldered joints are visibly cracked after a given number of thermal fatigue cycles. 2. The higher the rework temperature, the more heat is supplied to the solder joint and the greater is the degradation of its performance under thermal fatigue, i.e. the loss of reliability. The metallurgical reason for this degradation is the growth of the brittle intermetallic layer between solder and substrate. Its thickness is a function of the confrontation time between the molten solder and the substrate, and of its temperature.

job:LAY10 page:4 colour:1

black–text

344 Rework

Table 10.1 The degradation of soldered jonts caused by rework Rework time at soldering temperature of 400 °C/750 °F

Number of joints out of 2000 cracked after 2000 cycles between −20 °C/−4 °F and 100 °C/212 °F

No rework 2 sec 6 sec

100 160 180

Rework temperature using rework time 4 sec

Number of cracked joints after cycles as above

350 °C/660 °F 400 °C/750 °F 450 °C/840 °F

130 170 200

A further factor is the depletion of tin in the immediate neighbourhood of the solder/copper interface because it migrates to augment the intermetallic layer. This leaves a predominance of lead in the area next to that layer. Lead being weaker than solder, this circumstance further promotes cracking under thermal fatigue loads.

10.2.2 The cost of rework Rework is a joint-by-joint procedure, and necessarily time-consuming and expensive. Reworking a single joint costs on average as much as did the ﬁrst-time soldering of the complete circuit board on which it sits, and often considerably more. Depending on the type of product and its sale value, it may sometimes be cheaper to scrap a faulty circuit than to rework it. Some low-cost products like pocket calculators, cheap electronic watches and toys fall in that class. In small-scale production in particular, where visual inspection and rework are carried out by the same operator or operators, it is important to keep this cost aspect in mind. It is tempting to say ‘I might as well touch up this joint while I am looking at it.’ Not only do joint quality and reliability suﬀer through this practice, but costs are liable to rise in an uncontrollable manner.

10.2.3 Lessons to be learned The lessons to be drawn from these considerations are plain: 1. Whatever the method used for rework, choose only the best equipment available, and maintain it in top condition. 2. Complete every joint quickly. The solder should be molten for not longer than a few seconds. 3. Keep the working temperature as low as is compatible with this requirement. 4. Preheating the board, either locally or overall, before carrying out any rework on it brings two beneﬁts. First, the speciﬁc heat of the FR4 substrate is almost

job:LAY10 page:5 colour:1

black–text

Rework 345

four times that of copper or solder. This means that four times as much heat energy is needed to bring the board up to soldering temperature than to heat the joint itself. Preheating considerably shortens the heating time necessary to complete a joint, particularly with heavy multilayer boards. Secondly, with wavesoldered boards where the SMDs are glued to the board surface, preheating softens the adhesive joint and makes it easier to break when desoldering becomes necessary (Section 4.9.5). A preheating temperature of about 60 °C/140 °F to 100 °C/210 °F is usually enough for this purpose. A stream of warm air directed against the underside of the board is the usual method of preheating. This avoids the danger of a sharply localized hot spot, which could distort the board. 5. Rework for cosmetic reasons alone is an expensive and damaging luxury, and it should only be carried out if the customer or the market demands it and pays for it.

10.3 Rework equipment 10.3.1 Heat sources Almost every heat source which is employed in production soldering ﬁnds its use in rework: soldering irons in various forms, thermodes, solderwaves in miniature form, infrared radiation, hot air or gas, and in recent years also the vapour of a vapourphase soldering machine. With all of them, eﬃciency of the heat transfer from source to joint is of the essence, together with precise temperature control.

Soldering irons Molten solder is the ideal heat transfer medium: its heat conductivity is high and, being molten, it adapts perfectly to the surface contours of the joint and the joint members. For this reason, a soldering iron used for rework must have a well tinned tip, preferably with a drop of molten solder on it, to establish instant and good thermal contact with the joint. The best solder to use for rework, not only with an iron but with any method, is the silver-containing 63% tin solder (Section 3.3.1). The size of the iron and the shape of the tip must suit the type and the conﬁguration of the joint, as will be shown in Section 10.3.2. Naturally, the ergonomic aspects of the hand-held soldering iron must not be neglected. Precise control of the tip temperature, and a fast response to changes in the amount of heat demanded from it, are very important. Recent years have seen rapid advances in the technology of the soldering iron, which had remained static through several decades. Above all, methods of heating the soldering tip, and of shortening the path from the heat source to the end of the tip, have improved it greatly. Many handsoldering work stations include a fast response temperature indicator of the soldering tip itself. Bearing in mind what is at risk if rework is carried out badly, it is worth stressing the importance, not only of choosing a state-of-the-art soldering tool with antistatic

job:LAY10 page:6 colour:1

black–text

346 Rework

protection and a quick response to sudden heat-demands or changes in thermostat setting, but also of maintaining it well and periodically checking the accuracy of its temperature control.

Heated tweezers and thermodes Resistance-heated tweezers are a convenient tool for desoldering the two endjoints of a melf or chip simultaneously. PLCCs can be removed with a shaped tweezer, which grips the vertical shanks of the J-legs on all four sides of the components simultaneously. Tweezers are particularly useful for removing and resoldering these components on a crowded board, where the neighbours of the aﬀected component must be protected from the soldering heat of the site of the repair (see below). Tweezers, like thermodes, are made from an untinnable metal like tungsten. The thermodes used for desoldering are the same as those which are used for the impulse-soldering individual multilead SMDs (Section 5.7). Because their soldering surfaces are untinnable, they cannot be pretinned like a soldering iron, and molten solder cannot be used as a thermal link between the tool and the joints. A thin coating of a low-solids RMA ﬂux, brushed over the row of leads on all four sides, will have to serve as a substitute for the molten solder in establishing a thermal link between the soldering tool and the joint. Once the thermode sits ﬁrmly on the ﬂat leads, the heat transfer between the soldering tool and the joints takes place by conduction, as with a tinned soldering iron.

Miniature solderwaves Miniature solderwaves were developed in the sixties for the desoldering and resoldering of inserted multipin devices, like DILs. With this method, the board is placed over the nozzle of a dedicated small wavemachine, so that the leads which have to be desoldered sit closely above it. As soon as the wave is switched on and touches the underside of the board, the solder in the joints melts and the DIL can be lifted oﬀ. A replacement DIL can then immediately be soldered into the empty holes, its legs having been ﬂuxed ﬁrst. Alternatively, the molten solder can be sucked out of the holes, an operation for which this type of machine is equipped, and the replacement part can be soldered in position, on the same wave, at a later stage.

Hot air or gas Jets of hot air or gas, of a controlled temperature, are widely used for desoldering SMDs. Because they transfer their heat to the joints by convection, which is much less eﬃcient than conduction through molten solder or contact with a thermode (Section 5.5), it takes longer to melt the solder in the joints, and this must be taken into account when deciding on the reworking procedure. Single jets from hand-held nozzles can be used for desoldering and resoldering

job:LAY10 page:7 colour:1

black–text

Rework 347

melfs, chips, SOs and multilead devices. For the latter, however, many vendors oﬀer equipment with interchangeable arrays of jet nozzles, which direct the hot air or gas towards the joints on all four sides of the SMD at the same time. These jet arrays are useful for the desoldering and resoldering of PLCCs, where the joints are not directly accessible to a plain thermode. The hot air stream from a hand-held nozzle is usually controlled by the operator via a pedal, while multijet soldering heads are operated by a timer, the correct duration of heating having been determined empirically for a given board and component. With most hot-air desoldering machines, the board is preheated locally from underneath, for reasons already mentioned. Preheating is especially important with heavy multilayer boards.

Infrared radiation Beams of infrared radiation, focused on the joints of a multilead device, are another option for supplying the heat for desoldering and resoldering. Similar to the jet nozzles, the IR desoldering heads are interchangeable to suit speciﬁc component dimensions. Heating by radiation represents a non-equilibrium system (Section 5.8) where the temperature of the heat source is much higher than the target temperature of the joint. For this reason, such systems demand precise dosage of the radiation input, and ideally a feedback from the joint temperature to the heatsource. Infrared desoldering heads normally operate with medium wavelength emitters, operating in the 300 °C/550 °F to 500 °C/950 °F range.

10.3.2 Rework stations The workplace or work station for carrying out desoldering and resoldering must be user-friendly. Reworking can be a stressful task, and requires constant concentration and decision making. The workplace must therefore be well lit, provided with an exhaust which removes the ﬂux fumes, and the equipment must be ergonomically designed so that it can be operated with a minimum of fatigue. For manual rework, adjustable inclined frames which hold the board are standard. Wide-ﬁeld magniﬁers with a power which need not exceed ﬁve, or at most ten, times are also standard. Often, provision is made for a set of soldering irons of diﬀerent size to be readily at hand. In addition to soldering irons, workstations may provide sets of hot air or gas jets, vacuum pipettes for handling components, and heated tweezers for desoldering and resoldering them. Small mechanical tools like rotary drills and reamers to clean or remove footprints are also often part of a rework station. More elaborate manual stations are ﬁtted with an overhead illuminator, which direct a pencil of light in sequence to the several joints or components which require rework. This sequence can be created by the inspection station and stored on software in cases where visual inspection and manual rework are carried out separately from one another. From simple manual workstations, the market oﬀers a gradual succession of

job:LAY10 page:8 colour:1

black–text

348 Rework

increasingly complex and sophisticated equipment for rework, particularly for use with multilead SDMs. Most of them use sets of quickly interchangeable hot-air nozzles or thermodes, together with placement systems for aligning the component to be dealt with accurately with the soldering tool, visually or by opto-electronic means. Notwithstanding these electromechanical aids, the accuracy of feedback between the human eye and hand must not be underestimated. It has been shown that a trained operator, aided by a low-power magniﬁer, can place a multilead device with a 0.5 mm/20 mil pitch on its footprints with suﬃcient accuracy by hand. This means a lateral accuracy of ±0.125 mm/5 mil, since the maximum permissible lateral misplacement of ﬁne-pitch components is one quarter of the pitch distance (M. Cannon, Pace Europe Ltd, verbal communication).

10.4 Rework tasks and procedures Most of the published information and know-how in this ﬁeld can be found in the voluminous vendors’ literature. A few comprehensive accounts have appeared in the technical press. –

10.4.1 Removing bridges and solderballs A solder bridge is removed by touching it brieﬂy, for not more than a few seconds, with the well-tinned tip of a small soldering iron, with a rated output of about 40 W, and set to a temperature of about 250 °C/480 °F. For de-bridging ﬁne-pitch leads, a conical 20 W soldering bit is best. All that is necessary is to disrupt the bridge. Do not try to ‘tidy up’ the joints on either side, and do not use ﬂux. A solder wick (see below) should not be used either, because it is likely to suck out too much solder from the joints themselves and thus weaken them. Solderballs are removed in the same way. As soon as the tip of the iron touches one, it will disappear. The same will happen with ‘spiders’ webs’. Because a web covers more ground than a solderball, a chisel-shaped soldering tip is more convenient for removing them. Excess solder is removed from the tip of a soldering iron by wiping it with a piece of linen or cotton, but never with fabric made from synthetic or mixed ﬁbre. Many handsoldering stations are equipped with a heat resistant sponge for cleaning the soldering tip.

10.4.2 Desoldering SMDs Any of the following circumstances makes desoldering of an SMD obligatory: E Melfs and chips, if one or both of their metallized faces are seen to be badly solderable or unsolderable, or if the metallization has been leached oﬀ by the molten solder. The desoldered components are discarded. E Chips which have ‘tombstoned’. The desoldered components are discarded, because their solderability is doubtful.

job:LAY10 page:9 colour:1

black–text

Rework 349

E Melfs, chips and SOs which have ﬂoated away from their footprints. The desoldered components are discarded, unless there is a desperate need for their re-use. E Any SMD which is in the wrong place, or wrongly orientated. If carefully desoldered, the component can be reused. If X-ray inspection or functional testing reveal an open joint underneath a BGA, the oﬀending component must be desoldered, because the joints underneath are inaccessible, and cannot be corrected with the component in position. The BGA itself should be discarded, unless it is irreplaceable. To put fresh solderbumps on the underside of a desoldered BGA is a delicate and laborious operation, though solder pre-forms for putting down a fresh array of bumps are on the market. Unless the temperature is carefully controlled, the operation could easily ruin the IC inside the component, or cause the housing to crack due to the ‘popcorn’ eﬀect (see Section 2.6). Flip-chips pose another problem: once the underﬁll has been applied and hardened, it is almost impossible to remove a ﬂip-chip without damaging the board. Delicate microsurgery with special tools would be required to cut away the hardened underﬁll without damaging the board. The cost of this operation, which may put the board at risk in any case, must be balanced against the cost of scrapping the board (see Section 9.5.4).

Desoldering melfs and chips with a solder-wick Melfs and chips are joined to their footprints by butt joints. The joints of the larger ones contain too much solder to be sucked up by the tip of the hot soldering iron. Instead, a device called a ‘solder-wick’ is used to remove it. A solder-wick is a tape of closely braided ﬁne copper wire, a few millimetres wide, which is impregnated with an RMA ﬂux. Recently, solder-wick impregnated with a no-clean ﬂux has become available. The wick acts towards molten solder like blotting paper against ink: for desoldering, it is pressed into the corner between the endface of the component and the footprint (Figure 10.1) with the end of a chisel-shaped soldering

Figure 10.1 Desoldering a melf or chip with a solder-wick

job:LAY10 page:10 colour:1

black–text

350 Rework

tip held at a temperature of about 250 °C/480 °F–300 °C/570 °F. As soon as the heat has travelled from the tip through the wick of the solder, the latter melts and is sucked by capillarity into the ﬂuxed wire braid. Tip and wick are lifted oﬀ, and the solder-ﬁlled end of the wick is discarded. This operation should take no longer than a few seconds, but the wick should be pressed into the corner for long enough to let the heat travel into the gap underneath the component so that all the solder is sucked out of it. With wavesoldered components, the glued joint between component and board must now be broken. To make this possible without undue force, the adhesive must be heated to above its ‘glass-transition temperature’, which is normally about 60 °C/140 °F to 80 °C/180 °F. Above that temperature, the adhesive changes from a rigid body to a soft pliable substance (Section 8.5). This makes it possible to break the glued joint by twisting the component (Figure 10.2). If the temperature is not high enough and the adhesive still too stiﬀ, the board might get damaged. If there are any conductor tracks running underneath the component, between its footprints, the glued joint sits on top of the soldermask which covers them: twisting the joint apart with too much force can damage the soldermask and expose the tracks underneath. Local preheating of the board will raise the temperature enough to soften the adhesive. The heat of the desoldering will do the rest. If this is not enough, further heat from a hand-held hot-air nozzle will have to be applied to the component.

Desoldering melfs, chips and PLCCs with heated tweezers A simpler method of removal employs a pair of tweezers, heated in the same manner as a thermode to about 220 °C/400 °F. In this way, the joints at both ends of a component are desoldered simultaneously. The jaws of the tweezers are pressed against the ends of the component until the solder can be seen to melt. As soon as this happens, the component is lifted oﬀ or, in the case of a wavesoldered one, twisted from its adhesive joint (Figure 10.3).

Figure 10.2 Twisting a glued joint apart

job:LAY10 page:11 colour:1

black–text

Rework 351

Figure 10.3 Desoldering with heated tweezers

The same principle, using tweezers with interchangeable heated jaws which enclose the sides of a PLCC, is a useful option. The jaws press against the sides of the J-legs, and the component is lifted or twisted oﬀ as soon as the solder melts.

Desoldering SOs, SOICs and multilead components With these components, the leads cannot be gripped with a sideways pressure without damaging them, which would be undesirable where removed components may have to be re-used. Here, a heated tool of a shape which conforms to the pattern of the footprints, in other words a thermode as it is used in impulse soldering (Section 5.7), is pressed downwards against the horizontal ends of the gullwing legs (see Section 5.8.3). The hot jaws only heat the joints, but do not grip the leads. Lift-oﬀ is eﬀected by a vacuum pipette, which is located between the jaws and seats against the top of the component housing. It is activated by the operator when the joints are seen to have melted and the component is ready to be lifted. With thermode desoldering, a thin coating of RMA ﬂux brushed over the component leads improves the thermal contact between them and the face of the thermode. The presence of ﬂux also reduces to some extent the sharp spikes of solder which are likely to remain on the footprints after the component has been lifted clear. Failing desoldering equipment which allows the use of a thermode, multilead components can be desoldered joint by joint, with a temperature-controlled soldering iron (about 220 °C/430 °F). The well-tinned tip of the chisel-shaped iron is pressed against the joint: as soon as the solder is seen to melt, the iron is lifted oﬀ and the gullwing leg is lifted clear of the footprint with a pair of tweezers. Another way is to thread a thin stainless steel wire underneath the component: as soon as the joint has started to melt, the legs are pulled upwards with the wire, one after the other (Figure 10.4). After desoldering operations such as these, the component is mostly a write-oﬀ because of its bent legs. Also, unless skilfully executed, these methods put the footprints in danger of lifting oﬀ the board because of overheating. For all these reasons, it is best to invest in a thermode desoldering tool.

job:LAY10 page:12 colour:1

black–text

352 Rework

Figure 10.4 Desoldering a SOIC leg by leg (courtesy Edsyn Corp.)

Desoldering BGAs Several vendors oﬀer special equipment for desoldering a BGA if it must be removed because one of its joints is defective, because it is wrongly orientated or because it malfunctions. These desoldering tools or stations are of varying degrees of sophistication, working with hot air or hot nitrogen (230–250 °C/420–480 °F), which is directed against the upper surface of the component, less frequently with infrared heat. When desoldering, the underside of the board is heated to about 100 °C/210 °F to assist the melting of the soldered joints. As soon as the correct desoldering temperature has been reached and the joints have melted, the device is lifted oﬀ with a vacuum pipette. After the lift-oﬀ, the vacated footprints are cleaned up as described below. A small amount of no-clean ﬂux, applied to the edge of the BGA and allowed to penetrate into the gap underneath by capillarity, will reduce the amount of ‘spiking’ of the solder which is left on the footprints after the BGA is lifted clear.

These soldering stations are designed not only to remove an oﬀending BGA, but also to solder its replacement on to the board. With some of them, the solder-bumps underneath the replacement BGA can be accurately aligned with their footprints by optical means. With others, ﬁduciary markings on the board have to be relied upon. It has been suggested that reworking BGAs will be facilitated if a 5 mm/0.2 in wide ‘keep-out’ zone around the BGA site can be kept free of neighbouring footprints – provided the board designer can be persuaded of its merits.

job:LAY10 page:13 colour:1

black–text

Rework 353

Desoldering in a vapourphase machine Equipment has been described recently which allows the desoldering of multilead devices and BGAs in a standard vapourphase installation. The top surface of the component to be removed is fastened to the arm of a small lift-oﬀ device, which is placed next to it on the board. The board is then put in the vapourphase chamber. As soon as it has reached a pre-set temperature, say 190 °C/375 °F, the lift-oﬀ mechanism is actuated and pulls the component away from the board. Advantages claimed are the absence of spikes on the footprints, and of any surface oxydation. A possible drawback could be the fact that with this procedure all the joints on the board, not only those to be desoldered, are heated to above the melting point of the solder.

Cleaning the empty footprints Before the replacement component is put into place, the footprints must be cleared of remaining blobs or spikes of solder. This is done by lightly ﬂuxing them again and then passing the tip of a soldering iron, preferably chisel-shaped, across all of them. After that, they are ﬂuxed once more, and the replacement SMD is soldered into place as soon as possible. Caution! Any footprint cleared of solder must be given a coating of ﬂux as soon as possible, for the following reason: if the soldercoating is removed from a footprint, or for that matter from any soldered copper surface, the top layer of the diﬀusion zone formed by the intermetallic compound ‘eta’ (, Cu Sn ) (Section 3.1) should be exposed to to oxidize and become unsolderthe air. This compound will immediately begin able, even with a strong ﬂux, unless it is quickly protected from the atmosphere by a thin coating of ﬂux. All the same, a replacement component could be soldered to its footprints as soon as possible. Should this compound by any chance have begun to oxidize and made the footprint unsolderable, the situation can be retrieved by rubbing it with a piece of ﬁne emerypaper, folded over the end of a small screwdriver, until the pink copper surface becomes visible.

10.4.3 Filling empty joints Finding the empty joint An empty butt joint or open joint is easily recognized provided it is fully visible. PLCCs are the exception, because they are half hidden under the component edge. With a little practice and the right optical aid this problem is easily overcome. With BGAs, the joints are underneath the component and faults can only be identiﬁed by X-ray inspection (see Section 9.5.4). With empty capillary joints, only the top surface of the component lead is directly visible. A bent lead or a footprint without solder is immediately apparent. If the footprint is covered with solder, but the solder along the edge of the lead looks doubtful or if there is none at all, the joint can be tested by lifting the end of the lead

job:LAY10 page:14 colour:1

black–text

354 Rework

with a sharp probe. If it lifts, the joint must be corrected. If it stays ﬁrm, it is best left alone. For non-visual methods of inspection, see Section 9.4.3.

Finding the cause of the defect Before a joint which on inspection has been found to be empty is repaired and ﬁlled with solder, it is essential to ﬁnd out why the fault happened, and that the ﬁnding be recorded. If this is not done, and the reason remains undetected, and the repair unrecorded, the fault may recur again and again throughout the complete batch of boards. If a joint at the end of a melf or chip has remained empty because the metallization was unsolderable, has dewetted or leached away (as the evidence will clearly show) it is useless to try resoldering. The component must be desoldered, discarded and replaced. If there are several similar open joints, it is advisable to query the whole batch of components, and meanwhile to continue production with a fresh batch, having checked its solderability. If the footprint did not accept the solder, the reason for it must be discovered before an attempt is made to patch up the joint. The soldermask may have been faulty, and have partially or completely covered the footprint. Again, ﬁrst check whether this is a single occurrence or whether several boards show the same defect in the same place. If the latter, production management must be informed at once. If the former, a decision must be made whether to desolder the component and repair the aﬀected footprint, or whether to scrap the board. Removing cured soldermask from a footprint is a specialized and time-consuming task, which requires either a special solvent or mechanical removal with a rotating miniature burr or milling cutter, similar to a dentist’s drill (many vendors of rework equipment supply such equipment). Alternatively, the printed marking ink on the board may have partially covered the footprint. Misplaced ink can be removed with a suitable solvent, but it is as well to check whether this is a recurrent fault. If it is, action must be taken as above. If the board was wavesoldered, adhesive which has spread across one or both footprints may be responsible for an open joint. This can happen if too much adhesive has been put down between the footprints, and was squeezed out as the component was placed on the board. The closely spaced footprints of small melfs and chips are especially at risk from this cause. The fault can be readily spotted by the distinctive colour of the adhesive. If the board is to be saved, the components must be desoldered and the adhesive joint must be parted. The cured adhesive can be removed from the pad only by mechanical means, with one of the rotating tools described above. This should only be done by trained operators, because at this stage the board carries a high investment of production eﬀort, which a mistake at this stage puts at risk. On wavesoldered boards, an unsuitable layout, or an unfavourable orientation of the board towards the direction of travel over the wave, may have made it diﬃcult for the solder to reach some joints. The result will be a ‘skipped joint’. What has happened will be obvious from the evidence which such joints present. It is not diﬃcult to ﬁll them with a ﬁne soldering iron with a chisel tip, having lightly ﬂuxed

job:LAY10 page:15 colour:1

black–text

Rework 355

them ﬁrst with a low-solids ﬂux and using a thin, ﬂux-cored solder wire preferably ﬁlled with no-clean ﬂux which is now commercially available. The occasional empty joint on a multilead component on a reﬂowed board is often due to the gullwing leg having been bent upwards for some reason. This fault is called ‘lack of coplanarity’ (Section 1.4). It can be caused by unsuitable packaging or handling. Coplanarity should normally be within ±0.1 mm/4 mil, but even within these limits a thin paste printdown may not be able to reach the occasional lifted leg.

Filling the open joint Soldering iron The correct way of soldering open joints with a soldering iron is shown in Figure 10.5. In all cases, the chisel-shaped soldering tip is placed against the joint in such a way that the transfer of heat from tip to joint is as eﬃcient as possible. The end of the solderwire is always placed close to the tip of the iron, but never on it: if that were done, contact with the hot iron would have killed the ﬂux by the time it reached the joint. Placing the solderwire close to both tip and joint lets the heat travel to it, and it will begin to melt as soon as the joint has reached the correct temperature. As soon as the solder is seen to have ﬂowed into the joint, both the solderwire and the iron are lifted oﬀ. The temperature of the soldering iron is set at about 210 °C/410 °F to 220 °C/ 440 °F. Joints on thick multilayer boards may need a higher soldering temperature. In any case, the operation should be completed in not much more than three seconds. Solder paste can of course be used instead of solderwire for the ﬁlling of such joints. A small spot of paste is placed into, or next to, the joint before heating it. Generally it is found that handsoldering with paste instead of wire leaves more ﬂux

Figure 10.5 Filling an open joint with a soldering iron. Place the end of the solderwire on the footprint in spot (1). Then place the ﬂat side of the soldering iron against the footprint or component leg as shown

job:LAY10 page:16 colour:1

black–text

356 Rework

residue on the soldering iron and on the joint, and needs more cleaning up after soldering. Hot air or gas Being a convection method of heating, ﬁlling an empty joint with a hot air or gas jet (about 300 °C/570 °F) may take more time than soldering with an iron, maybe from ﬁve up to ten seconds. It may be advisable to use local preheat from below, to speed things up. On the other hand, handling a hot air jet requires less skill than the simultaneous handling of a soldering iron and solder wire; also, the progress of the soldering operation is easier to observe. With hot air or gas soldering, a small spot of solder paste is preplaced into or near the joint, and ﬁlling the joint becomes a one-hand operation. Thermode Filling an open joint with a thermode is not often practised because it involves all joints on a multipin component for the sake of correcting one single joint.

10.4.4 Resoldering SMDs Resoldering in this context means replacing a component which has been desoldered for one of the reasons discussed above, mostly by a new one. Soldering a component which has been desoldered back into its place should only be done for the compelling reason of its value or irreplaceability, and after its correct functioning has been checked. Desoldered passive components like melfs and chips, particularly ceramic condensers, should always be discarded if the situation allows it.

Handling and placing the component Here, the ﬁrst rule is never to touch a component with the ﬁngers. However clean the operators’ hands are (and they should be clean of course), some sweat or contamination is bound to transfer to the soldering surfaces and reduce their solderability. Components are handled with tweezers or preferably a vacuum pipette. The latter have reached a high level of ergonomic perfection and all of them allow the component to be rotated into its correct orientation after having been picked up. Most operators ﬁnd it more convenient to manipulate components directly with a hand-held pipette, instead of via ‘joystick’ like manipulator, which is manoeuvrable in the x, y and z directions, and rotatable round the vertical z axis. As has been said already, the coordination between the human eye and the human hand is remarkably precise, to within 0.125 mm/5 mil.

Handsoldering with an iron Using the conductive method of heating, handsoldering is fast. Melfs, chips and SOs are placed and held in position so that their leads sit correctly on their footprints. A

job:LAY10 page:17 colour:1

black–text

Rework 357

little L0 or L1 ﬂux is then applied to the joints with a small brush, and the joints are touched with the tip of the soldering iron, which is preferably chisel shaped and held at a temperature of about 220 °C/430 °F. Before this, the tip of the iron has been touched brieﬂy with the end of a thin ﬂux-cored solder wire, so that it carries a small drop of molten solder at its end. Most low-solids ﬂuxes are suitable for handsoldering, but some no-clean ﬂuxes may prove inadequate for the task. On the other hand, a proprietary no-clean cored solderwire has been speciﬁcally designed for repair work, and can safely be used. A ‘half-chisel’ shape of soldering iron tip has been specially developed for the handsoldering of SMDs: the endface of the cylindrical bit is ﬂat and set at an angle so that it has an oval surface (Figure 10.6). This enables it to hold a fair amount of solder, which can be run into the joint very quickly while presenting a sharp, horizontal edge to the joint. The butt joints of melfs or chips are touched at the corner where the metallization and the footprint meet; capillary joints are touched at the joint entry. The whole operation should not take longer than a few seconds – three at most. With multilead components with gullwing legs, the component is placed carefully on its preﬂuxed footprints by hand. That this is perfectly feasible even with ﬁne-pitch components as has already been explained. Once in place, the component is tacked to the board by touching one joint each at two diagonally opposed corners. After that, the component need not be held down any longer, and the rest of the joints can be soldered by running the tip with its reservoir of solder along each row of joints, letting the solder run into them. The J-legs of PLCCs are dealt with similarly. The edge of the tip is run along the line where the legs sit on their footprints.

Resoldering with a hot airgas jet Resoldering with a hand-held jet of hot air or gas needs only simple equipment, but it requires skill and experience. The temperature of the air or gas is about 300 °C/

Figure 10.6 Soldering bit with an oblique endface (courtesy Pace Inc.)

job:LAY10 page:18 colour:1

black–text

358 Rework

540 °F to 350 °C/630 °F, and the force of the jet can be controlled with a footpedal. The footprints are thinly covered with solder paste, which can be put down with a hand- or air-operated syringe. The method demands skill because the heating rate is slower than a soldering iron, and therefore soldering takes longer. With densely populated boards, particular care must be taken to avoid getting neighbouring joints too hot, so that they start to melt. Nevertheless, this method is very useful for boards with a simple layout, and it requires little investment.

Resoldering BGAs After the footprints have been cleaned up, as has been described above, they are lightly ﬂuxed with a no-clean ﬂux, applied with a ﬁne brush (in spite of the comments made above about using a no-clean ﬂux for repairwork, in this instance it must be used because the joints cannot be cleaned after soldering). The component is then placed into position, which can be done quite easily by hand, using a vacuum pipette with a rotatable head, as has been described in Section 7.3.1. The accuracy of positioning is not very critical, because a certain amount of misplacement is readily corrected by the phenomenon of self-alignment under the inﬂuence of the surface tension, once the solder has melted. This has been described in Section 3.6.3 (Figure 3.18). Nevertheless, a number of tools for de- and resoldering BGAs and ﬂip-chips are on the market which allow for accurate alignment (see Section 10.4.2). When soldering a replacement BGA into position, the board, at least in the vicinity of the replacement, must be preheated from underneath, preferably by hot air, or with single-sided boards on a hotplate, to between 100 °C/210 °F–120 °C/ 250 °F, for reasons which have been discussed in Section 10.2.3. The replacement component is heated from above, preferably by a focused stream of hot air or nitrogen, rather than by infrared radiation. The latter, being a non-equilibrium method, is diﬃcult to control and subject to many unpredictable parameters such as the surface reﬂectivity of the component to be soldered (see Section 10.3.1). With a certain amount of skill, a hand-held nozzle, providing a gentle stream of hot air or nitrogen, is quite adequate. During this operation, the component is lightly held in place by a thin probe or a piece of stiﬀ wire. If a dedicated BGA soldering tool is used, it is of course simplest to solder the replacement component into position immediately after desoldering the defective one. If it is found necessary to apply solder paste to the vacated footprints before putting down the replacement BGA, a miniature template for stencilling on the paste will save a great deal of tedious and delicate work.

10.4.5 Cleaning after rework Cleaning after rework is often neglected or forgotten. There are several tell-tale marks which indicate, or betray, where a joint has been reworked: the usual sign is a conspicuous ﬂux residue on an otherwise clean board; less frequently, and perhaps

job:LAY10 page:19 colour:1

black–text

Rework 359

less excusably, an uneven or maybe clumsy dot of solder. If rework is carried out before the boards are cleaned, all ﬂux traces of any rework will of course disappear. If there is no cleaning after soldering, or if rework is carried out after cleaning, the question of cleaning up after rework must be addressed. Unless it is the deliberate policy of quality inspection to show where correction has taken place, traces of rework should be eliminated for the sake of appearance and customer satisfaction. If the ﬁnished board is to be lacquered or has to receive a conformal coating, there is a technical reason for a clean-up after rework. Solderwire with a core of no-clean ﬂux is commercially available, and there may therefore be no technical reason for its removal. The residue left by some of these wires is very inconspicuous, and whether it can be left as it is must be a matter of individual judgement. If the ﬂux residue is plainly visible, it ought to be removed. Any cleaning method must of course be environmentally acceptable. Spray dispensers of non-ﬂammable ﬂux solvent are commercially available. A sprayed-on solvent will disperse the ﬂux residue and make it less conspicuous, but it will not remove it. The best method of local ﬂux removal is dabbing with a small swab of linen or cotton, soaked in isopropanol and held with a tweezer. With some practice, this method gives perfectly adequate results. Here are a few ‘don’ts’: E Don’t use a very volatile solvent such as methylene chloride (Section 8.3.1), which is often the basis of nail-varnish remover or of the ﬂuid used for removing adhesive plaster: it dries so quickly that it does not remove the ﬂux residue but only spreads it around. E Don’t use cotton wool, or natural wool, for a swab. Both will leave ﬂuﬀ behind, which is as bad if not worse than the ﬂux residue you want to remove. E Don’t use synthetic ﬁbre fabric for a swab, because it does not soak up liquids very well.

10.4.6 Semi-mechanized work stations A variety of semi-mechanized, multi-purpose workstations are commercially available. These can be used not only for rework such as desoldering and resoldering multilead components, but also for soldering them individually to a circuit board during normal production. Some work with thermodes, but most of them use hot air or gas as the heating medium. Their design spans a wide range of technical sophistication: 1. Most of them embody means for optically checking the correct positioning of the component on its footprints. This may be done visually through stereoscopic or vertical sighting, or through video observation on a screen. 2. A set of hot air/gas nozzles of various sizes to match the component to be soldered is normally carried. On some stations, the nozzles are carried on a rotating turret. The design of the nozzles conﬁnes the stream of heating gas to the joints of the component, and prevents it from aﬀecting neighbouring components.

job:LAY10 page:20 colour:1

black–text

360 Rework

3. The correct heating cycle for a given component is empirically determined, and can be stored in a databank. 4. Postcooling with room-temperature air, before the pipette which holds down the component is lifted oﬀ, is often provided. 5. Depending on the type of reworkstation, a complex range of data storage and processing can be incorporated. So-called ‘paperless rework stations’ can fulﬁl the following tasks: E identify (mostly with the aid of a bar code) and record the type of board that is being reworked, the identity of the reworked component and the type of fault that caused the rework E record the rework parameters and the identity of the operator E process the recorded data, so as to integrate them into a CIM system and to make them available for statistical process control (see also Section 10.5.1).

10.5 Integrating rework into the production process Rework, together with inspection, must be seen not only as a process in itself, but also as an essential part of the whole manufacturing activity. The links between rework and product design, materials selection and control, and the manufacturing parameters in general, must be understood, established and maintained, and above all acted upon. Unless this is the case, inspection and rework, while preventing faulty products from leaving the factory and reaching the customer, will be unproductive and unnecessarily expensive.

10.5.1 Rework personnel Rework is entirely a personal matter. The decision whether rework is necessary may have been made by a quality inspector, or by automatic inspection equipment, but the rework itself is done by a person, not a machine. As has been shown in the preceding sections,the question whetherto reworkor not is very often the responsibility,and the result of an on-the-spot decision, of the same person. Inspectors and reworking personnel, like policemen, lawyers and doctors, only go into action when things have gone wrong. It is natural that they are tempted to take a jaundiced view of the work of their colleagues further back along the production line, from the designers and the purchasing departments down through all the manufacturing sections. It is important that this problem is appreciated by management, and that every eﬀort is made to prevent the resulting attitude from taking root and hardening. Inspectors and the reworking teams must be made familiar not only with the manufacturing steps upstream of their own place in the chain, but they must also be given the opportunity to establish some personal contacts with the people who work there. It is important not to leave these links entirely to some bureaucracy or an impersonal CIM system. Thus, the training of rework personnel must include familiarizing visits to these

job:LAY10 page:21 colour:1

black–text

Rework 361

departments, and occasional renewal of contacts, as well as being kept informed of what goes on and what is new.

10.5.2 Closed-loop soldering The term ‘closed-loop soldering’ is an apt formulation of the concept of which the above integration of inspection and rework into the entire manufacturing chain is only a part. In a closed-loop production, inspection and rework have two functions: ﬁrst, they must ensure product integrity; secondly, they must identify design problems and provide the background for material and process control. Practising closed-loop soldering without computerized data processing is possible, but with medium and large organizations it involves much paperwork and administrative eﬀort. A number of individuals and companies have begun to develop and market both software and hardware which are designed to take over where the human operator would be swamped with recording and evaluating what he is doing. Inspection verdicts and rework operations can be entered into data stores, where they are classiﬁed and evaluated. Paperless rework stations are able to log their operations automatically. Programs are already in existence which can be interrogated to relate fault rates of a speciﬁc board or a component to suppliers, storage time or any of the manufacturing parameters relating to the assembly being repaired. Statistical process control can be added to such a program, so that warnings are sounded as soon as the rates of faults, rejects or rework exceed an empirically established standard ﬂuctuation. To use an image introduced earlier, closed-loop soldering automatically checks the fever thermometer, which signals the state of health of the manufacturing unit, and it sounds a warning as soon as it begins to drift beyond its normal reading. 10.6 References 1. Strauss, R. (1990) The Metallurgical Aspects of Corrective Soldering of Printed Circuit Boards. Proc. 5th Intern. Conference Interconnection Technology in Electronics, DVS Report 129, Duesseldorf, Germany, pp. 155–157 (in German). 2. Keller, J. (1989) Solder Joint Failure Detection: Does Inspection ensure Reliability? Soldering and SMT, No. 3, October 1989, pp. 56–57. 3. Lea, C. (1990) The Harmfulness of Touching up of Cosmetically Defective Solderjoints. Soldering and SMT, No. 5, June 1990, pp. 4–9. 4. London, J. and Ashall, D. W. (1986) Compound Growth and Fracture at Copper/Tin–Silver Solder Interfaces. Brazing and Soldering (UK), No. 11, pp. 49–55. 5. Verguld, M. M. F. and Leenaerts, M. H. W. (1988) Repair of Printed Circuit Boards carrying SMDs. Circ. World (UK), No. 2, January 1988, pp. 11–15. 6. Klein Wassink, R. J. (1989) Soldering in Electronics, 2nd ed., Electrochem. Publ., Ayr, Scotland, pp. 631–641.

job:LAY10 page:22 colour:1

black–text

362 Rework

7. Morris, B. (1993) Rework and Repair of SMD Assemblies. Electronic Mats. & Packages (Elsevier), March/April, pp. 27–32. 8. Leicht, H. W. (1996) Vapourphase soldering. DVS Reports, 182, pp. 182–195 (in German). 9. Abbagnaro, L. (1993) Manual Operations take the Heat out of Rework, Electronic Manuf. (UK), June, pp. 8–10. 10. Davy, J. G. (1990) Closed-Loop Soldering, Proc. 14th Electronics Manufacturing Seminar, Naval Weapons Centre, China Lake, CAL, February 1990. 11. Habenicht, G., Janker, A. and Wuermseher, H. (1992) Automatic Registration of Quality Data, Proc. 6th Intern. Conf., Interconnection Technol. in Electronics, Fellbach (Germany), DVS Report 141, Duesseldorf, Germany (in German). 12. Willis, B. (1996) Electronic Production Yearbook 1996, pp. 15–23. 13. Peck, D. J. (1997) BGA Rework – Issues and Answers. Future Circuits International, 1.1, pp. 111–118.

job:LAYIND page:1 colour:1

black–text

Index

Accuracy of component placement, 252, 260 Activators for rosin/resin ﬂuxes, 51 Adhesive joints for wavesoldering SMDs: breaking when desoldering, 350 curing, 145, 146 eﬀect on post-cleaning, 268 glass-transition temperature, 146, 147, 350 properties, 141 Adhesives for wavesoldering SMDs: dispensing during component placement, 257 properties required, 141, 142 single-shot dispensing, 141–144 slump, 142 stencilling, 145 storage and handling, 141 Alcohols: as ﬂux solvents, 54 ﬂammability, 86, 300 health aspects, 292, 293 modiﬁed, for semi-aqueous cleaning, 312, 313 used for cleaning, 299, 300 Aluminium as an impurity in solder, 35 Angle of aspect of SMDs, 16, 17 Area-arrays of IOs:, 11 Asymmetry: of footprint areas (impulse soldering), 277

of surface tension (tombstone eﬀect, ﬂoating during reﬂow), 248 ATE test probes (aﬀected by ﬂux residues), 52, 340 Atmosphere, oxygen-free: for reﬂowsoldering, 208, 211, 213, 214 for wavesoldering, 118–125 in vapourphase soldering Automated component placement, 256–258 Automated inspection, 338, 340 Azeotropic cleaning solvents, 280, 281 Ball-grid arrays (BGAs):, 11–13 board lay-out considerations, 249 controlled-collapse bumps, 45 de-soldering, 349 ﬂuxing during automatic placement, 257 lead-free solders, suitability of, 31 placement on circuitboard, 251, 252 re-soldering, 358 self-alignment on footprints, 65 vapour-jet cleaning underneath BGA, 291 vapourphase soldering, 179 X-ray joint inspection, 339 Batch-cleaning systems: aquaeous, 307 semi-aqueous, 314 solvent cleaning, 284–287 waterwashing, 307–309

job:LAYIND page:2 colour:1

black–text

364 Index

Beilstein Test for ﬂuxes, 59 Blistertape for SMD placement, 251 Blowholes: as soldering imperfection, 330 causes, 331 inadvisability of correction, 332, 343, 344 Board conveyors: reﬂow ovens, 208 wavesoldering machines, 126–128 Board-handling robots, 129 Board templates for wavesoldering, 129 Boundary-scan electronic testing, 340 Bridging: as a soldering fault, 00 measures for avoiding it in reﬂow soldering, 245 in wave soldering, 108–112 removing bridges, 348 roles of surface tension, 48 Cadmium as an impurity in solder, 35 Capillarity, 65 Capillary joints, 65–69 CFCs: chemical nature, 275 environmental risks involved, 278, 293–296 reduced-risk substitutes, 299 restrictions on usage, 297, 298 CHCs, 277, 279, 281 Chip-shooters, 260 Chips: 6–8 chip-on-board (COB), 5 solderability, 14 Circuit-board: conveyors for reﬂowsoldering, 208, 214, 215 conveyors for wavesoldering, 126–128 robot-handling, 129 SMD-speciﬁc aspects, 234, 235 thermal management, 236–238 Circuitboard layout: for BGAs, 249 for mixed component boards, 247 for reﬂow soldering, 247–249

for wavesoldering, 244–246 Clean-up after rework, 358, 359 Cleanability: designing for, 266–269 of residue from low-solids ﬂux, 52, 53 Cleaning: by high-pressure jets, 273, 289, 303, 309 by ultrasonics, 272, 273 by vapour jet, 291 chemistry of, 274, 274 contaminants to be removed, 267–269 hydrodynamic apects, 269–273 Cleaning eﬃciency: eﬀect of delay between soldering and cleaning, 276 Cleaning eﬃciency checks: glass-plate test, 273 MIL test, 318–321 SIR test, 321, 322 Cleaning installations: solvent-cleaning, batch operation, 284–288 solvent-cleaning, in-line, 288–290 water-washing, batch operation, 307–309 water-washing, in-line, 309, 310 Cleaning solvents: alcohols, 299, 300 CFCs, 278, 293–299 CHCs, 277, 279, 281 modiﬁed alcohols, 312, 313 terpenes, 275, 311–313 water, 302–310 Cleaning – Yes or No, inﬂuenced by: corrosion aspects, 263, 265 general considerations, 261–263 its operating environment, 263, 264 the marketplace, 266 the nature of the endproduct, 265–266 Cleanliness after cleaning: deﬁnition, 318, 319 measuring cleanliness, 319–322 Closed-loop soldering, 361 Combustibility, 279, 280 Component placement:

job:LAYIND page:3 colour:1

black–text

Index 365

accuracy, 252 fully automatic, 256–260 manual, 253–255 semi-automatic, 255–256 Confrontation period (oven soldering), 203, 204 Convention reﬂow-soldering, 209–212 Cooling after IR soldering, 206, 207 Copper as an impurity in solder, 33, 34 Corrective soldering see Rework Corrosion, see Flux corrosion Dendrite formation (corrosion), 265 Design for joint reliability, 45 De-soldering tools, 350–352 De-soldering wick, 349, 350 De-soldering: BGAs, 352–353 bridges and solderballs, 348 cleaning up vacated footprints, 353 multi-lead components, 351, 352 SMDs, 348–353 Dewetting, 64, 65 Diﬀusion zone, see Intermetallic layer DIL, 4 Dipping Test for solderability: 79–81 contributory factors to dross formation, 116 dealing with dross, 138 hygiene and safety, 139 its origin and nature, 114–116 preventive measures against dross formation, 116, 117 Dispensing: adhesive for wavesoldering, 143 solderpaste, 165, 169 Disposal of electronic scrap, 31 Double-waves, 110–112 Dross-free wavesoldering see Wavesoldering under nitrogen Eisler, Paul, 2, 234 Electrolytic corrosion, 265 Electronic inspection methods of soldered circuitboards, 340 Empty joints, see Open joints

Environmental acceptability aspects: of cleaning solvents, 278, 281, 293–297 of water-washing eﬄuents, 305, 306 Environmental risk parameters: of ﬂux- and cleaning solvents, 282 Equilibrium/non-equilibrium heating methods, 155, 156, 189, 190 Errors in namual component placement, 254, 255 Eta-phase – its unsolderability, 72, 353 Eutectic, 25, 27 Expansion, see Thermal expansion Explosion risks (in cleaning), 280 Fine pitch: 9 and component placement, 260 and solderpaste printing, 174, 175 limits for wavesoldering, 9 Flammability, 278–280 Flip-chip: concept, 11, 12 desoldering problem, 12 glob-top, 12 underﬁll, 12 X-ray joint inspection, 339 Flux corrosion, 58 Flux in solderpaste, 164, 165 Flux solvents, 54 Fluxers for wavesoldering: 85, 86 avoiding ﬁre hazard, 86 foamﬂuxers, 87–91 monitoring ﬂux quality, 96–98 sprayﬂuxers, 91 compressed air, 92, 93 rotating brush, 94, 95 rotating drum, 93 ultrasonic, 95, 96 waveﬂuxers, 87 Fluxes, see Soldering ﬂuxes Fluxless soldering, see Plasma soldering Floating of chips during reﬂow, 248, 328 Forced circulation in reﬂow ovens, 207 Galvanic coatings on circuitboards, 239 Glass-transition temperature of adhesive joints, 146, 147, 350

job:LAYIND page:4 colour:1

black–text

366 Index

Glassplate test (cleaning eﬃciency), 273, 274 Glob-top, 12 Global warming potential of solvents, 281, 295, 296 Glycerine as wavesoldering cover, 124 Gold: embrittlement of soldered joints, 36, 39, 72, 73 impurity in solder, 36 Gold-nickel coatings on circuitboards, 239 Greenhouse eﬀect, see Global warming Gritty solder, 33, 34 Halogenated solvents: environmental threats, 293–297 health aspects, 292, 293 less harmful replacements, 298, 299 non-ﬂammability, 277–279 restrictions on use, 297, 298 technical aspects, 291, 292 Handling of SMDs, 254, 255 Handling of circuitboards, 126–129, 208, 214, 215 Handsoldering, 21–23, 355–357 Heat absorption under IR radiation, 198, 199 Heat conductivity data, 61 Heat requirements for soldering, 60, 61 Heat sources: electrical resitance heaters, 63 ﬂames, 63 hot air or gas, 346, 347 infrared emitters, 100, 205, 206 laser, 218–220 molten solder, 104, 105 soldering iron, 355 solderwave, 104, 105, 346 thermodes, 225–228 Heat-sinks, 238 Heat-transfer mechanisms: conduction, 61, 63 convection, 210 radiation, 191–199 Heating situations:

equilibrium, 155, 156 non-equilibrium, 156 Hot-air levelling (HAL), 239, 240 Hot-air soldering, 214–217 Hybrid technology, 3 Hygiene and safety: solvent cleaning, 292, 293 wavesoldering, 139, 140 Icicles, 48 Imperfection, soldering, 330, 331 Impulse soldering: 68, 223 equipment, 227, 228 footprint layout for, 227, 249 solder depots for, 224, 225 thermodes for, 225, 226 Impurities in solder: grit-forming impurities, 33, 34 harmless impurities, 36, 37 impurity limits, 31, 32 skin-forming impurities, 35 Impurity limits in solders, 31, 32 Indium-containing solders, 37 Infrared radiation, physical laws, 191–194 Infrared reﬂow soldering: working principles, 189, 190, 191 Infrared soldering ovens, 201–209 infrared heaters, 205, 206 temperature proﬁle, 201, 206, 189, 190 with oxygen-free atmosphere, 211, 212 Inspection: 333–340 automated, 338 electronic, 340 indispensability of, 335 thermographic, 340 visual, 338, 339 X-ray, 338, 339 Interfacial tension, 47, 48 Intermetallic compounds, 38, 39 Intermetallic layer, 21 Intermetallic solder-substrate reaction, 37 IO, 9, 11 Ionic contamination (MIL Test), 319–321 Iron as an impurity in solder, 34 Isopropyl alcohol (isopropanol, IPA):

job:LAYIND page:5 colour:1

black–text

Index 367

as cleaning solvent, 299, 300 as a ﬂux solvent, 54 ﬂammability, 86, 300 photochemical smog hazard, 296, 297 J-legs of PLCCs, 9 their angle-of-aspect problem, 17 their ‘wicking’ problem, 183, 328 Jacuzzi eﬀect: used in semi-aqueous cleaning, 313 used in the MIL test, 320 Jet solderwaves, 112–114 Joints, see Soldered joints Kauri-Butan value of a solvent, 280 KOH value of a rosin, 50 Laser soldering: 217–222 how a laser works, 218 laser soldering equipment, 221, 222 lasers suitable for soldering, 218–220 practical aspects, 220, 221 Layout for circuitboards: for BGAs, 249 for mixed SMD/TMD-populated boards, 247 for reﬂow soldering, 247–249 for wavesoldering, 244–246 Leaching of substrate by molten solder, 73 Lead-free solders, 29–31 disposal of scrapped electronic equipment as reason for their development, 30 practical aspects of their use, 30, 31 Leakage currents, 263 Lift-oﬀ eﬀect, 71 Low-solids ﬂuxes, 52, 53 MAC – maximum allowable concentration of a solvent vapour, 281 Manual component placement, 253–255 Manual cleaning, 282 Melfs, 6–8 Melting points of solders, 27–30 Meniscus, 75

Metals, solderability of, 70 Metallurgical structure, soldered joint, 38, 39 MID – three dimensional substrates, 234, 235 MIL test, 319–321 Montreal Protocol on solvent use, 297 Multichip modules, 13, 14 Multilayer circuitboards, 235, 236 Nd:YAG laser, 218–230 Nitrogen atmosphere for soldering see Oxygen-free soldering No-clean ﬂuxes, 52, 53 No-clean solderpaste, 164, 165 Open soldered joints: causes, 327, 354, 355 examples, 333, 335 Opto-electronic inspection, 338 Orange-peel eﬀect, 143 Organic solderability protection (OSP), 241, 242 Overhead reﬂowsoldering, 149, 207 Oxide skin: on molten solder, 46 on solid metallic surfaces, 69–71 Oxygen-free wavesoldering: beneﬁts – less dross and bridging, 120 drawbacks – solderballs, 121–123 wavesoldering under a vapourphase, 124, 125 wavesoldering under forming gas, 118 wavesoldering under glycerine, 124 wavesoldering under nitrogen, 119–121 Oxygen-free reﬂowsoldering: reﬂowsoldering under nitrogen, 208, 211–214 vapourphase soldering, 179–187 Ozone: 293 in stratosphere, 293–295 in photochemical smog, 281, 296, 297 Ozone-depletion potential of solvents, 281, 194, 295 Ozone-hole: 294, 295

job:LAYIND page:6 colour:1

black–text

368 Index

Packaging systems for SMDs, 251 Peelback of solderwave, 107–110, 122, 123 Photochemical ozone creation potential (POCP), 281, 296, 297 Photochemical smog, 281, 296, 297 Pin-count, 3, 9 Pin-grid arrays, 11 Pitch (see also Fine pitch), 7, 9, 12 Placement: accuracy angular, 252 linear, 252 faults, 251, 252, 254 ﬁne-pitch, 260 options, 253 speeds, 259, 260 Planck’s law of radiation, 193 PLCC, 4, 237 Popcorn eﬀect, 16–18 Porosity in capillary joints, 339 Preheating in vapourphase soldering, 186–188 Preheating in wavesoldering: constructional features, 100–102 heating elements, 100, 101 operational features, 102, 103 purpose and heat requirements, 98–100 Printed circuit-board see Circuitboard Protective-atmospheres soldering see Oxygen-free soldering QFP, 3, 15 Quality: deﬁnitions, 325, 327 linked with reliability, 325, 326 linked with type of product, 326, 327 monitoring, 361 standard speciﬁcations, 327 Reﬂowsoldering: heating methods, 155–158 operating options, 150–154 overhead soldering, 149, 207 principle, 23 reﬂow versus wavesoldering, 154–157 Reliability:

deﬁnition, 327 of a ﬁnished product, 327 of soldered joints, 43–45 product-related requirements, 326 Repairing open joints, 355, 356 Resoldering: BGAs, 358 multilead SMDs, 357, 358 Rework: as part of the production process, 342, 360 by handsoldering, 349, 355–358 cost aspects, 344 desoldering and resoldering, 343 equipment, 345–348 its three basic elements, 342 metallurgical consequences, 343, 344 using hot air or gas, 346 using infrared radiation, 347 using miniature solderwaves, 346 Robots for board handling, 129 Role of rework personnel, 360, 361 rollertinning of circuitboards, 240–241 Rosin as a ﬂux ingredient, 50, 51 Rotary-brush cleaning of circuitboards, 283 Saponiﬁers for water-washing systems, 307, 308 Self-alignment of SMDs during reﬂow, 65, 67, 247 Semi-aqueous cleaning: cleaning media, 311–313 cleaning plant water-immiscible media, 313–315 water-miscible media, 316, 317 concept, 310, 311 disposal of spent solvent, 312, 313 Silver as an additive to solder, 27, 28, 36 Skipped joints (in wavesoldering), 244, 245 SO, 3, 7 SOD (SO diode), 7 Solder: mechanical strength, 26, 27 melting behaviour, 25, 27 Solder-bridges see Bridging Solder bumps, 11–13, 45

job:LAYIND page:7 colour:1

black–text

Index 369

Solder powder: compositions, 161 particle shape, 162, 163 particle size, 163, 164 Solder-substrate interaction (leaching), 73 Solder-substrate intermetallic reaction, 36, 154, 155 Solder-substrate reaction, 20, 21 Solderability, 63, 69–71 Solderability-enhancing surface coatings, 71–73 Solderability measurement methods, 74–78 Solderability testing, 79, 80 Solderable component leads, 10, 14–16, 41, 43 Solderable surfaces on circuitboards, 238–243 ﬂat solder depots on footprints, 178, 179, 242, 243 galvanic coatings, 239 gold-nickel, 239 hot-air levelling (HAL), 239, 240 organic solderability protection, 241, 242 rollertinning, 240, 241 solder depots for impulse soldering, 224, 225 solder-jet depots on footprints, 243 Solderball-test of solderpastes, 167–169 Solderballing in reﬂowsoldering, 53 Solderballing in wavesoldering: countermeasures, 121, 122 explanations, 121 observed facts, 121 Solderballs: as soldering faults, 329, 334 removing them, 56, 348 Soldered joints: factors aﬀecting microstructure, 39, 40 failure, 44, 45 long-term behaviour, 40, 43 mechanical properties, 40, 42 microstructure, 39, 40 reliability, 44, 45 solidiﬁcation range, 39 solidiﬁcation time-interval, 39 Soldering faults, deﬁnition of, 327, 329

examples, 328, 329, 333–335 Soldering ﬂux residues: corrosive action, 58 solubility, 59 surface insulation resistance, 59, 321 tackiness, 60 Soldering ﬂux tests: Beilstein test for halide presence, 59 corrosion test, 58 halide test, 58 silver-chromate test, 58 spreading test, 57, 58 Soldering ﬂuxes: activators for rosin/resin ﬂuxes, 51 alcohol-based ﬂuxes, 54 demands to be met, 48, 49 functions, 45–47 low-solids ﬂuxes, 52 no-clean ﬂuxes, 52, 53 rosin/resin ﬂuxes, 50, 51 watersoluble ﬂuxes, 53 Soldering imperfections and defects, 330, 331, 336 soldering irons, 22 Soldering irons for rework, 345, 346 Soldering methods, comparison between, 228–231 Soldering perfection, criteria of, 327, 330 its acceptable/unacceptable nature, 330, 331 Soldering robots, 22 Soldering success, 24, 327 Soldering success, deﬁnition of, 327 its yes/no nature, 329 Soldering tools for rework, 346 Solderjet technique, 243 Soldermask, 244 Solderpaste: ﬂux protion, 164, 165 metal content, 160, 161 operational requirements, 158, 159, 165 print-down thickness, 172, 173 screen printing, 175, 176 single-spot dispensing, 169–171 solderball test, 167–169 standard speciﬁcations, 159, 160

job:LAYIND page:8 colour:1

black–text

370 Index

Solderpaste (cont.) stencil printing, 172–175 storage and handling, 176–178 thixotropy, 165 viscosity and its measurement, 165–167 Solderwaves: asymmetrical wave, 108–110, 112 bridging, 108, 110 chip waves, 110–115 combination waves, 113–115 design features of wavemachines, 103, 104 double waves, 110–112 electrodynamic waves, 113 jet-waves, 111, 112 peelback, 107–110 shadow eﬀect, 105–107 slanting wave, 111 solderthieves, 109, 110, 246 thermal role of solderwave, 104, 105 Solderwaves for rework, 346 Solderwire, 22 with no-clean ﬂux core, 359 Solvent cleaning: batch systems, 284–288 environmental precautions, 287, 288 immersion systems, 284–289 in-line systems, 288–291 Solvent-power of cleaning media, 280 Solvents used in ﬂuxes see Flux solvents Solvents used for cleaning see Cleaning solvents Standard speciﬁcations: for solder, 28 for soldering ﬂuxes, 54, 57 Starved joints, 248 Stefan-Boltzmann law of radiation, 192 Surface insulation resistance (SIR) measurement, 321, 322 signiﬁcance 263, 321 Surface-tension of molten solder, 47 TAB, 3, 10, 11 Temperature proﬁle in reﬂow ovens, 201–203 Terpenes, 275, 311–313

Thermal expansion coeﬃcients, 237 Thermal expansion stresses, 236, 237 Thermodes for impulse soldering, 225, 226 Thermographic inspection (Vanzetti), 340 Thixotropy, 142, 165 Through-hole reﬂow method, 85, 149 Tinning: hot-air levelling, 239 rollertinning, 240, 241 Tombstone eﬀect, 67, 248, 328, 335 Two-pass reﬂowsoldering, 151 Ultrasonic sprayﬂuxers, 95, 96 Ultrasonically assisted cleaning, 272, 273, 313, 315–317 Underﬁll (ﬂip-chips), 12 Vanzetti thermographic inspection, 340 Vapour-jet cleaning, 291 Vapourphase desoldering, 353 Vapourphase soldering: equipment, batch operation, 184, 185, 188 in-line operation, 185–188 physical aspects, 179–183 safety aspects, 184 use of preheating, 186–188 using unsaturated vapour, 183, 184 working ﬂuids, 181 Viscosity of solderpaste, 165–167 Visual inspection, 337 Volatile organic compounds (VOC), 281 Waﬄe trays (for component handling), 251 Water as a cleaning medium: chemical and physical aspects, 302, 303 eﬄuent problems, 305, 306 removing resin-free ﬂux residues, 306 removing resinous ﬂux residues, 306, 307 water quality, 303–305 water recycling, 305 Water as a solvent in soldering ﬂuxes, 54, 96 Water-washing equipment:

job:LAYIND page:9 colour:1

black–text

Index 371

batch systems, 307–309 in-line systems, 309, 310 Wavesoldering: selective soldering, 129 general features of wave-machines, 103, 104 Principle, 23 SMD – speciﬁc aspects, 84, 85 Wavesoldering in oxygen-free atmosphere: beneﬁts gained, 123, 124 concepts of working under nitrogen, 119 solderballing, 121–123 working in a vapourphase, 125 working under hot glycerine, 124 Wavesoldering practice: chemical analysis of solder-bath, 138 computerised machine management, 135 dross management and -handling, 138, 139 hygiene and safety, 139, 140 machine mainteance, 137

optimising operating parameters, 130–137 Weak shoulder, of through-plated holes: on HAL-tinned circuitboards, 240 Wetting, 63 Wetting angle, 64 Wetting balance, 75–79 White stain on cleaned circuitboards, 280, 322 Wicking of vapourphase soldered J-legs, 183, 328 Wien’s law of radiation, 194 Workstations for rework, 359, 360 World climates, 264 X-ray inspection of solderedboards, 13, 338, 339 Zero-eﬄuent: semi-aqueous cleaning, 316, 317 water-washing systems, 305, 308 Zinc as a solder impurity, 35